FERROUS ALLOYS
BACK
ALLOYING
ADDITIONS
IRON & STEEL
ir G HENDERIECKX
GIETECH BV
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
CONTENT
1. GRAIN SIZE
2. CONTENT OF SPECIFICATIONS
1. GRAIN SIZE
Alloy
FeB
FeCr
FeCrSi
FeMn
FeMnSi
FeMo
FeNb(Ta)
FeP
FeSi
FeTi
FeV
FeW
+
x
0 – 3,15
+
+
+
+
+
+
+
+
+
+
+
X
0,6 – 6,3
X
+
+
X
X
+
+
X
Size in mm
3,15 - 25
X
X
X
X
X
X
X
X
X
X
X
3,15 - 50
X
X
X
X
X
X
X
X
X
X
X
10 - 100
Suitable for metalstream and ladle addition
Suitable for furnace adition
ir G Henderieckx
GIETECH BV
September 2004
X
X
X
X
X
X
FERROUS ALLOYS
2. CONTENT OF SPECIFICATIONS
FeSi75
FeSi10
FeSi25
FeSi45
FeSi75-Al1
FeSi90
FeSi90-Al1
Si98
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
FeCr70C01
FeCr70C02
FeCr70C04
FeCr70C06
FeCr70C08
FeCr70C10
FeCr70C50
FeCr70NC10
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
CaSi
CaSiC50
FeSi75 (inoc)
FeMn85C01
FeMn85C01P015
FeMn85NC01
FeMn85NC01P015
FeMn80C1
FeMn80NC1
FeMn75C7
FeMn75C7P015
FeMn65Si
FeMn70Si
Mn97
FeMo70
FeMo62
Al
Ni
Cu
FeV60
FeV80
FeB16
FeB18
FeB12C
FeB17C
SiC90
FeW1C
FeW0,1C
Sn
Graphite electrod
Petroleum cokes
High sulphur PET cokes
Metallurgical cokes
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
FeCr70C1
FeCr70C1,5
FeCr70C2
FeCr70C4
FeCr70C5
FeCr70C8
FeCr70C6Si
FeCr40Si
FeCr60Si
Cr99
FeNi25
FeNi25C
FeNi25CS
FeNi55
Mg
Mg15Ni85
Mg15Ni69Fe15
Mg5Si47Fe45
Mg10Si45Fe42
Mg30Si55Fe12
Mg10Si55Ca39
FeTi30
FeTi40
FeTi50
FeTi70
FeP24
FeNb65
FeNb60Ta
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
Go to
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO SILICON for alloying
STANDARD
STANDARD
NAME
DIN 17560 (DEC 1965)
WERKSTOFFNUMMER
FeSi 75
0.3375
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX
0,1
Si
%
75
73,0
79,0
Fe
%
24
P
%
S
%
Al
%
0,05
0,04
1,0
2,0
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
2,8 kg / dm
3,15 to 35 mm
8 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1210 - 1315 °C
+ 4,9 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves very easy with increase of temperature
+ Does not evaporate, putting it in the metal bath
+ Melting with a :
Acid Lining : Si-content will increase if C, Cr, Mn, Al and or Ti is present.
The more oxygen in the metal, the lower the increase
Basic Lining : small decrease of Si-content due to the deoxidising effect (SiO2),
which will stick to the lining.
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
:
: FERRO SILICON for alloying
NAME
STANDARD
STANDARD
NAME
DIN 17560 (DEC 1965)
WERKSTOFFNUMMER
FeSi 10
0.3310
COMPOSITION
NOMINAL
RANGE
MIN
MAX
C
%
2,5
Si
%
10
8,0
15,0
Fe
%
87
P
%
S
%
Al
%
0,15
0,04
0,8
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
kg / dm
3,15 to 35 mm
8 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
°C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves very easy with increase of temperature
+ Does not evaporate, putting it in the metal bath
+ Melting with a :
Acid Lining : Si-content will increase if C, Cr, Mn, Al and or Ti is present.
The more oxygen in the metal, the lower the increase
Basic Lining : small decrease of Si-content due to the deoxidising effect (SiO2),
which will stick to the lining.
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
:
: FERRO SILICON for alloying
NAME
STANDARD
STANDARD
NAME
DIN 17560 (DEC 1965)
WERKSTOFFNUMMER
FeSi 25
0.3325
COMPOSITION
NOMINAL
RANGE
MIN
MAX
C
%
0,8
Si
%
25
20,0
30,0
Fe
%
74
P
%
S
%
Al
%
0,08
0,04
0,8
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
kg / dm
3,15 to 35 mm
8 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
°C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves very easy with increase of temperature
+ Does not evaporate, putting it in the metal bath
+ Melting with a :
Acid Lining : Si-content will increase if C, Cr, Mn, Al and or Ti is present.
The more oxygen in the metal, the lower the increase
Basic Lining : small decrease of Si-content due to the deoxidising effect (SiO2),
which will stick to the lining.
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
:
: FERRO SILICON for alloying
NAME
STANDARD
STANDARD
NAME
DIN 17560 (DEC 1965)
WERKSTOFFNUMMER
FeSi 45
0.3345
COMPOSITION
NOMINAL
RANGE
MIN
MAX
C
%
0,2
Si
%
45
42,0
48,0
Fe
%
54
P
%
S
%
Al
%
0,05
0,04
1,5
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
5,1 kg / dm
3,15 to 35 mm
8 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1215 - 1300 °C
- 10,0 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves very easy with increase of temperature
+ Does not evaporate, putting it in the metal bath
+ Melting with a :
Acid Lining : Si-content will increase if C, Cr, Mn, Al and or Ti is present.
The more oxygen in the metal, the lower the increase
Basic Lining : small decrease of Si-content due to the deoxidising effect (SiO2),
which will stick to the lining.
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
:
: FERRO SILICON for alloying
NAME
STANDARD
STANDARD
NAME
DIN 17560 (DEC 1965)
WERKSTOFFNUMMER
FeSi 75-Al1
0.3376
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX
0,1
Si
%
75
73,0
79,0
Fe
%
24
P
%
S
%
Al
%
0,05
0,04
1,0
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
2,8 kg / dm
3,15 to 35 mm
8 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1210 - 1315 °C
+ 4,9 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves very easy with increase of temperature
+ Does not evaporate, putting it in the metal bath
+ Melting with a :
Acid Lining : Si-content will increase if C, Cr, Mn, Al and or Ti is present.
The more oxygen in the metal, the lower the increase
Basic Lining : small decrease of Si-content due to the deoxidising effect (SiO2),
which will stick to the lining.
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
:
: FERRO SILICON for alloying
NAME
STANDARD
STANDARD
NAME
DIN 17560 (DEC 1965)
WERKSTOFFNUMMER
FeSi 90
0.3390
COMPOSITION
NOMINAL
RANGE
MIN
MAX
C
%
0,1
0,1
Si
%
90
87,0
95,0
Fe
%
9
P
%
S
%
Al
%
0,04
0,04
1,0
2,5
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
2,4 kg / dm
3,15 to 35 mm
8 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1210 - 1280 °C
+ 12,4 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves very easy with increase of temperature
+ Does not evaporate, putting it in the metal bath
+ Melting with a :
Acid Lining : Si-content will increase if C, Cr, Mn, Al and or Ti is present.
The more oxygen in the metal, the lower the increase
Basic Lining : small decrease of Si-content due to the deoxidising effect (SiO2),
which will stick to the lining.
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
:
: FERRO SILICON for alloying
NAME
STANDARD
STANDARD
NAME
DIN 17560 (DEC 1965)
WERKSTOFFNUMMER
FeSi 90-Al1
0.3391
COMPOSITION
NOMINAL
RANGE
MIN
MAX
C
%
0,1
0,1
Si
%
90
87,0
95,0
Fe
%
9
P
%
S
%
Al
%
0,04
0,04
1,0
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
2,4 kg / dm
3,15 to 35 mm
8 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1210 - 1280 °C
+ 12,4 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves very easy with increase of temperature
+ Does not evaporate, putting it in the metal bath
+ Melting with a :
Acid Lining : Si-content will increase if C, Cr, Mn, Al and or Ti is present.
The more oxygen in the metal, the lower the increase
Basic Lining : small decrease of Si-content due to the deoxidising effect (SiO2),
which will stick to the lining.
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
:
: SILICON for alloying
NAME
STANDARD
STANDARD
NAME
DIN 17560 (DEC 1965)
WERKSTOFFNUMMER
Si 98
0.3398
COMPOSITION
Ca
%
NOMINAL
RANGE
MIN
MAX
0,35
Si
%
98
97,0
99,0
Fe
%
P
%
0,5
S
%
Al
%
1,5
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
2,3 kg / dm
3,15 to 35 mm
8 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1410 - 1440 °C
+ 17,0 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves very easy with increase of temperature
+ Does not evaporate, putting it in the metal bath
+ Melting with a :
Acid Lining : Si-content will increase if C, Cr, Mn, Al and or Ti is present.
The more oxygen in the metal, the lower the increase
Basic Lining : small decrease of Si-content due to the deoxidising effect (SiO2),
which will stick to the lining.
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
:
: SILICON for alloying
NAME
STANDARD
STANDARD
NAME
DIN 17560 (DEC 1965)
WERKSTOFFNUMMER
SiC 90
COMPOSITION
NOMINAL
RANGE
MIN
MAX
C
%
30
Si
%
67
Fe
%
0,2
P
%
S
%
Al
%
0,3
0,06
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
3,0 kg / dm
3,15 to 35 mm
8 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
> 1500 °C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves very slowly
+ Does not evaporate, putting it in the metal bath
+ Melting with a :
Acid Lining : Si-content will increase if C, Cr, Mn, Al and or Ti is present.
The more oxygen in the metal, the lower the increase
Basic Lining : small decrease of Si-content due to the de-oxidising effect (SiO2),
which will stick to the lining.
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
:
: CALCIUM SILICON for alloying
NAME
STANDARD
STANDARD
NAME
DIN 17580 (DEC 1968)
WERKSTOFFNUMMER
CaSi
0.3650
COMPOSITION
NOMINAL
RANGE
MIN
MAX
C
%
Si + Ca
%
90
1,20
90,0
Ca
%
30
29,0
33,0
P
%
S
%
Al
%
0,070
0,060
1,80
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
2,5 kg / dm
3,15 to 35 mm
8 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
980 - 1200 °C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves very slowly
+ Does not evaporate, putting it in the metal bath; creates liquid slag
+ Melting with a :
Acid Lining : Si-content will increase if C, Cr, Mn, Al and or Ti is present.
The more oxygen in the metal, the lower the increase
Basic Lining : small decrease of Si-content due to the deoxidising effect (SiO2),
which will stick to the lining.
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
:
: CALCIUM SILICON, low carbon
NAME
STANDARD
STANDARD
NAME
DIN 17580 (DEC 1968)
WERKSTOFFNUMMER
CaSiC50
0.3655
COMPOSITION
NOMINAL
RANGE
MIN
MAX
C
%
Si + Ca
%
90
0,50
90,0
Ca
%
30
29,0
33,0
P
%
S
%
Al
%
0,070
0,060
1,80
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
2,5 kg / dm3
3,15 to 35 mm
8 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
980 - 1200 °C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves very slowly
+ Does not evaporate, putting it in the metal bath; creates liquid slag
+ Melting with a :
Acid Lining : Si-content will increase if C, Cr, Mn, Al and or Ti is present.
The more oxygen in the metal, the lower the increase
Basic Lining : small decrease of Si-content due to the deoxidising effect (SiO2),
which will stick to the lining.
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
:
: FERRO SILICON for inocculation
NAME
STANDARD
STANDARD
NAME
DIN 17560 (DEC 1965)
WERKSTOFFNUMMER
FeSi 75
0.3375
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX
0,1
Si
%
75
73,0
79,0
Fe
%
24
P
%
S
%
Al
%
0,05
0,04
1,0
2,0
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
2,8 kg / dm
3,15 to 10 mm
8 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1210 - 1315 °C
+ 4,9 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves very easy with increase of temperature
+ Does not evaporate, putting it in the metal bath
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO CHROMIUM low carbon
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 70 C 01
0.4010
COMPOSITION
C
%
0,010
NOMINAL
RANGE
MIN
MAX 0,010
Si
%
0,60
1,50
Cr
%
72
65
75
Fe
%
26
P
%
S
%
N
%
0,030
0,010
0,050
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,35 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1600 - 1650 °C
- 19,4 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO CHROMIUM low carbon
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 70 C 02
0.4011
COMPOSITION
C
%
0,010
NOMINAL
RANGE
MIN
MAX 0,020
Si
%
0,60
1,50
Cr
%
72
65
75
Fe
%
26
P
%
S
%
N
%
0,030
0,010
0,050
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,35 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1600 - 1650 °C
- 19,4 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO CHROMIUM low carbon
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 70 C 04
0.4012
COMPOSITION
C
%
0,010
NOMINAL
RANGE
MIN
MAX 0,040
Si
%
0,60
1,50
Cr
%
72
65
75
Fe
%
26
P
%
S
%
N
%
0,030
0,010
0,050
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,35 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1600 - 1650 °C
- 19,4 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO CHROMIUM low carbon
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 70 C 06
0.4013
COMPOSITION
C
%
0,010
NOMINAL
RANGE
MIN
MAX 0,060
Si
%
0,60
1,50
Cr
%
72
65
75
Fe
%
26
P
%
S
%
N
%
0,030
0,010
0,050
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,35 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1600 - 1650 °C
- 19,4 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO CHROMIUM low carbon
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 70 C 08
0.4015
COMPOSITION
C
%
0,010
NOMINAL
RANGE
MIN
MAX 0,080
Si
%
0,60
1,50
Cr
%
72
65
75
Fe
%
26
P
%
S
%
N
%
0,030
0,010
0,050
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,35 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1600 - 1650 °C
- 19,4 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO CHROMIUM low carbon
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 70 C 10
0.4016
COMPOSITION
C
%
0,010
NOMINAL
RANGE
MIN
MAX 0,10
Si
%
0,60
1,50
Cr
%
72
65
75
Fe
%
26
P
%
S
%
N
%
0,030
0,010
0,050
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,35 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1600 - 1650 °C
- 19,4 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO CHROMIUM low carbon
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 70 C 50
0.4017
COMPOSITION
C
%
0,010
NOMINAL
RANGE
MIN
MAX 0,50
Si
%
0,60
1,50
Cr
%
72
65
75
Fe
%
26
P
%
S
%
N
%
0,030
0,010
0,050
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,35 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1590 - 1650 °C
- 19,7 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO CHROMIUM low carbon,
nitrogen
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 70N C 10
0.4020
COMPOSITION
C
%
0,05
NOMINAL
RANGE
MIN
MAX 0,10
Si
%
0,60
1,50
Cr
%
70
60
72
Fe
%
26
P
%
S
%
0,030
0,010
N
%
3,0
2,50
4,0
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,35 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1600 - 1650 °C
- 19,4 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO CHROMIUM medium carbon
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 70 C 1
0.4030
COMPOSITION
C
%
NOMINAL
RANGE
MIN 0,50
MAX 1,00
Si
%
0,60
1,50
Cr
%
70
65
72
Fe
%
27
P
%
S
%
0,030
0,050
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,34 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1580 - 1610 °C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO CHROMIUM medium carbon
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 70 C 1,5
0.4032
COMPOSITION
C
%
NOMINAL
RANGE
MIN 1,00
MAX 1,50
Si
%
0,60
1,50
Cr
%
70
65
72
Fe
%
27
P
%
S
%
0,030
0,050
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,34 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1580 - 1610 °C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO CHROMIUM medium carbon
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 70 C 2
0.4036
COMPOSITION
C
%
NOMINAL
RANGE
MIN 1,50
MAX 2,00
Si
%
0,60
1,50
Cr
%
70
65
72
Fe
%
26
P
%
S
%
0,030
0,050
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,31 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1400 - 1500 °C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO CHROMIUM medium carbon
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 70 C 4
0.4038
COMPOSITION
C
%
NOMINAL
RANGE
MIN 2,00
MAX 4,00
Si
%
0,60
1,50
Cr
%
69
65
72
Fe
%
25
P
%
S
%
0,030
0,050
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,20 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1360 - 1420 °C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO CHROMIUM high carbon
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 70 C 5
0.4052
COMPOSITION
C
%
NOMINAL
6
RANGE
MIN 4,0
MAX 6,0
Si
%
0,60
1,50
Cr
%
64
60
72
Fe
%
28
P
%
S
%
0,030
0,050
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,10 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1350 - 1500 °C
- 24,9 °C (+/- 4°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO CHROMIUM high carbon
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 70 C 8
0.4056
COMPOSITION
C
%
NOMINAL
8
RANGE
MIN 7,0
MAX 10,0
Si
%
0,60
1,50
Cr
%
64
60
72
Fe
%
28
P
%
S
%
0,030
0,030
0,050
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,10 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1350 - 1400 °C
- 24,9 °C (+/- 4°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO CHROMIUM high carbon, silicon
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 70 C 6Si
0.4058
COMPOSITION
C
%
NOMINAL
6
RANGE
MIN 4,0
MAX 8,0
Si
%
1,50
10,0
Cr
%
64
60
72
Fe
%
28
P
%
S
%
0,030
0,030
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
6,70 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1400 - 1500 °C
°C (+/- 4°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
SILICO CHROMIUM
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 40 Si
0.4070
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,050
Si
%
40
35
45
Cr
%
42
40
45
Fe
%
16
P
%
S
%
0,020
0,010
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
5,30 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1300 - 1400 °C
- 16,9 °C (+/- 4°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
SILICO CHROMIUM
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
FeCr 60 Si
0.4072
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,050
Si
%
30
20
35
Cr
%
60
55
65
Fe
%
16
P
%
S
%
0,020
0,010
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
5,80 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1500 - 1600 °C
- 22,7 °C (+/- 4°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
CHROME METAL
STANDARD
STANDARD
NAME
DIN 17565 (DEC 1968)
WERKSTOFFNUMMER
Cr 99
0.4090
COMPOSITION
C
%
Si
%
NOMINAL
RANGE
MIN
MAX 0,030
0,10
Cr
%
99
99,0
99,3
Fe
%
0,020
P
%
0,020
S
%
Al
%
0,035
0,10
0,30
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,20 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1850 °C
- 21,5 °C (+/- 2°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves best if temperature is TL + (100 – 150) °C and quick and good mixing
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon or ferromanganese
+ Melting in furnace with :
Acid Lining : will go in the slag, recovery 98 to 96 %
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO MANGANESE low carbon
STANDARD
STANDARD
NAME
DIN 17564 (DEC 1968)
WERKSTOFFNUMMER
FeMn 85 C 01
0.3185
COMPOSITION
C
%
NOMINAL
0,50
RANGE
MIN 0,05
MAX 0,50
Si
%
1,50
1,00
1,50
Mn
%
85
80
92
Fe
%
13,5
P
%
S
%
0,25
0,030
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
7,30 kg / dm
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1240 °C
- 18,3 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves ver good
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon
+ Melting in furnace with :
Acid Lining : will go in the slag
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO MANGANESE low carbon &
low phosphor
STANDARD
STANDARD
NAME
DIN 17564 (DEC 1968)
WERKSTOFFNUMMER
FeMn 85 C 01P015
0.3186
COMPOSITION
C
%
NOMINAL
0,50
RANGE
MIN 0,05
MAX 0,50
Si
%
1,50
1,00
1,50
Mn
%
85
80
92
Fe
%
13,5
P
%
S
%
0,15
0,030
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,30 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1240 °C
- 18,3 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves ver good
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon
+ Melting in furnace with :
Acid Lining : will go in the slag
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO MANGANESE low carbon &
nitrogen
STANDARD
STANDARD
NAME
DIN 17564 (DEC 1968)
WERKSTOFFNUMMER
FeMn 85 NC 01
0.3187
COMPOSITION
C
%
NOMINAL
0,50
RANGE
MIN 0,05
MAX 0,50
Si
%
1,50
1,00
1,50
Mn
%
85
80
92
Fe
%
13,5
P
%
S
%
0,25
0,030
N
%
2,5
2,0
2,5
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,30 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1240 °C
- 18,3 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves ver good
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon
+ Melting in furnace with :
Acid Lining : will go in the slag
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO MANGANESE low carbon &
low phosphor & nitrogen
STANDARD
STANDARD
NAME
DIN 17564 (DEC 1968)
WERKSTOFFNUMMER
FeMn 85NC 01P015
0.3188
COMPOSITION
C
%
NOMINAL
0,50
RANGE
MIN 0,05
MAX 0,50
Si
%
1,50
1,00
1,50
Mn
%
85
80
92
Fe
%
13,5
P
%
S
%
0,15
0,030
N
%
2,50
2,00
2,50
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,30 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1240 °C
- 18,3 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves ver good
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon
+ Melting in furnace with :
Acid Lining : will go in the slag
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO MANGANESE medium
carbon
STANDARD
STANDARD
NAME
DIN 17564 (DEC 1968)
WERKSTOFFNUMMER
FeMn 80 C 1
0.3180
COMPOSITION
C
%
NOMINAL
2,00
RANGE
MIN 0,50
MAX 2,00
Si
%
1,00
0,50
1,50
Mn
%
80
75
85
Fe
%
17
P
%
S
%
0,25
0,030
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,40 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1150 – 1190 °C
- 18,7 °C (+/- 2°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves ver good
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon
+ Melting in furnace with :
Acid Lining : will go in the slag
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO MANGANESE medium
carbon & nitrogen
STANDARD
STANDARD
NAME
DIN 17564 (DEC 1968)
WERKSTOFFNUMMER
FeMn 85 NC1
0.3181
COMPOSITION
C
%
NOMINAL
2,00
RANGE
MIN 0,50
MAX 2,00
Si
%
1,00
0,50
1,50
Mn
%
85
80
90
Fe
%
17
P
%
S
%
0,25
0,030
N
%
2,0
1,0
2,0
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,40 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1150 - 1190 °C
- 18,7 °C (+/- 2°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves ver good
+ Does not evaporate, putting it in the metal bath
+ It oxydies very easy, especially if no other deoxidising elements are present,
therefore bring it in after partly deoxidising with ferro-silicon
+ Melting in furnace with :
Acid Lining : will go in the slag
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO MANGANESE high carbon
STANDARD
STANDARD
NAME
DIN 17564 (DEC 1968)
WERKSTOFFNUMMER
FeMn 75 C 7
0.3175
COMPOSITION
C
%
NOMINAL
7,0
RANGE
MIN 6,0
MAX 8,0
Si
%
1,00
1,50
Mn
%
78
75
80
Fe
%
14
P
%
S
%
0,35
0,030
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,30 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1070 - 1260 °C
- 18,7 °C (+/- 2°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+
+
+
+
Dissolves ver good
Strong tendency to evaporate, putting it on top of the liquid metal bath
It oxydies in contact with the air
Melting in furnace with :
Acid Lining : Enters easily in the slag
Increasing C and Cr does increase the recovery (stainless steel:
95 %, high manganese steel: 50 – 60 %)
High tendency to react with SiO2
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO MANGANESE high carbon,
low posphorus
STANDARD
STANDARD
NAME
DIN 17564 (DEC 1968)
WERKSTOFFNUMMER
FeMn 75 C 7P015
0.3177
COMPOSITION
C
%
NOMINAL
7,0
RANGE
MIN 6,0
MAX 8,0
Si
%
1,00
1,50
Mn
%
78
75
80
Fe
%
14
P
%
S
%
0,15
0,030
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
7,30 kg / dm
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1070 - 1260 °C
- 18,7 °C (+/- 2°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+
+
+
+
Dissolves ver good
Strong tendency to evaporate, putting it on top of the liquid metal bath
It oxydies in contact with the air
Melting in furnace with :
Acid Lining : Enters easily in the slag
Increasing C and Cr does increase the recovery (stainless steel:
95 %, high manganese steel: 50 – 60 %)
High tendency to react with SiO2
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
SILICO MANGANESE
STANDARD
STANDARD
NAME
DIN 17564 (DEC 1968)
WERKSTOFFNUMMER
FeMn 65 Si
0.3160
COMPOSITION
C
%
NOMINAL
0,5
RANGE
MIN 0,1
MAX 0,5
Si
%
30
23
35
Mn
%
65
58
72
Fe
%
3
P
%
S
%
0,20
0,010
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
6,10 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1270 - 1280 °C
- 16,9 °C (+/- 2°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+
+
+
+
Dissolves ver good
Strong tendency to evaporate, putting it on top of the liquid metal bath
It oxydies in contact with the air
Melting in furnace with :
Acid Lining : Enters easily in the slag
Increasing C and Cr does increase the recovery (stainless steel:
95 %, high manganese steel: 50 – 60 %)
High tendency to react with SiO2
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
SILICO MANGANESE
STANDARD
STANDARD
NAME
DIN 17564 (DEC 1968)
WERKSTOFFNUMMER
FeMn 70 Si
0.3162
COMPOSITION
C
%
NOMINAL
2,0
RANGE
MIN 0,5
MAX 2,0
Si
%
20
15
25
Mn
%
70
65
75
Fe
%
3
P
%
S
%
0,20
0,010
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
6,30 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1130 - 1240 °C
- 17,4 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+
+
+
+
Dissolves ver good
Strong tendency to evaporate, putting it on top of the liquid metal bath
It oxydies in contact with the air
Melting in furnace with :
Acid Lining : Enters easily in the slag
Increasing C and Cr does increase the recovery (stainless steel:
95 %, high manganese steel: 50 – 60 %)
High tendency to react with SiO2
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
MANGANESE METAL
STANDARD
STANDARD
NAME
DIN 17564 (DEC 1968)
WERKSTOFFNUMMER
Mn 97
0.3197
COMPOSITION
C
%
Si
%
NOMINAL
RANGE
MIN
MAX 0,030
0?50
Mn
%
97
95
98
Fe
%
3
P
%
S
%
0,050
0,008
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
7,80 kg / dm3
3,15 to 50 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1220 - 1240 °C
- 18,3 °C (+/- 1°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+
+
+
+
Dissolves ver good
Strong tendency to evaporate, putting it on top of the liquid metal bath
It oxydies in contact with the air
Melting in furnace with :
Acid Lining : Enters easily in the slag
Increasing C and Cr does increase the recovery (stainless steel:
95 %, high manganese steel: 50 – 60 %)
High tendency to react with SiO2
Basic Lining : recovery nearly 100 %
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO MOLYBDENUM
STANDARD
STANDARD
NAME
DIN 17561 (DEC 1965)
WERKSTOFFNUMMER
FeMo 70
0.4270
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,10
Si
%
0,5
1,00
Mo
%
70
60
75
Fe
%
29
P
%
S
%
Cu
%
0,10
0,10
0,50
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
9,40 kg / dm
3,15 to 25 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1800 - 1900 °C
- 10,8 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO MOLYBDENUM
STANDARD
STANDARD
NAME
DIN 17561 (DEC 1965)
WERKSTOFFNUMMER
FeMo 62
0.4262
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,50
Si
%
2,0
2,0
Mo
%
62
58
65
Fe
%
36
P
%
S
%
Cu
%
0,10
0,10
1,00
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
9,00 kg / dm
3,15 to 25 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1800 - 1900 °C
- 10,8 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO NICKEL
STANDARD
STANDARD
NAME
DIN 17561 (DEC 1965)
WERKSTOFFNUMMER
FeNi 25
0.4425
COMPOSITION
C
%
Si
%
NOMINAL
RANGE
MIN
MAX 0,030
0,05
Ni + Co
%
25
20
30
Fe
%
P
%
S
%
Cr
%
0,030
0,040
0,10
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
kg / dm
3,15 to 25 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
°C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO NICKEL, high carbon
STANDARD
STANDARD
NAME
DIN 17561 (DEC 1965)
WERKSTOFFNUMMER
FeNi 25C
0.4427
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 2,0
Si
%
4,0
Ni + Co
%
25
20
28
Fe
%
P
%
S
%
Cr
%
0,040
0,040
2,0
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
kg / dm
3,15 to 25 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
°C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO NICKEL, high carbon &
sulphur
STANDARD
STANDARD
NAME
DIN 17561 (DEC 1965)
WERKSTOFFNUMMER
FeNi 25CS
0.4429
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 2,0
Si
%
4,0
Ni + Co
%
25
20
28
Fe
%
P
%
S
%
Cr
%
0,040
0,30
2,0
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
kg / dm3
3,15 to 25 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
°C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO NICKEL
STANDARD
STANDARD
NAME
DIN 17561 (DEC 1965)
WERKSTOFFNUMMER
FeNi 55
0.4455
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,05
Si
%
1,0
Ni + Co
%
55
50
60
Fe
%
44
P
%
S
%
Cr
%
0,020
0,010
0,050
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
8,3 kg / dm
3,15 to 25 mm
5 % can be smaller, 10 % can be larger but never
exceeding 1,5 x dimension in 2 or 3 directions
1425 - 1435 °C
- 15 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
ALUMINIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
Al
COMPOSITION
C
%
Si
%
NOMINAL
RANGE
MIN
MAX
Al
%
100
99,5
Fe
%
P
%
S
%
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
2,70 kg / dm
Special shape
650 - 675 °C
+ 18,0 °C (+/- 2°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves ver good
+ It oxydies in contact with the air
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
NICKEL
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
Ni
COMPOSITION
C
%
Si
%
NOMINAL
RANGE
MIN
MAX
Ni
%
100
99,9
Fe
%
P
%
S
%
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
8,90 kg / dm
Special shape
1450 - 1475 °C
- 12,3 °C (+/- 1°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
COPPER, electrolytic
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
Cu
COMPOSITION
C
%
Si
%
NOMINAL
RANGE
MIN
MAX
Al
%
100
99,9
Fe
%
P
%
S
%
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
8,96 kg / dm
Special shape
1080 - 1095 °C
- 10 °C (+/- 2°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
+ Dissolves very good
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
MAGNESIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
Mg
COMPOSITION
C
%
Si
%
NOMINAL
RANGE
MIN
MAX
Mg
%
100
99,9
Fe
%
P
%
S
%
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
1,74 kg / dm
Special shape
650 °C
°C (+/- 2°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
NICKEL MAGNESIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
15 Mg 85 Ni
COMPOSITION
C
%
Si
%
NOMINAL
RANGE
MIN
MAX
Mg
%
15
Ni
%
85
P
%
S
%
N
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
6,10 kg / dm
Special shape
1050 - 1130 °C
°C (+/- 2°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO NICKEL MAGNESIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
15 Mg 69 Ni 15 Fe
COMPOSITION
C
%
Si
%
NOMINAL
RANGE
MIN
MAX
Mg
%
15
Fe
%
15
P
%
S
%
Ni
%
69
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
6,0 kg / dm
Special shape
1050 - 1070 °C
°C (+/- 2°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO SILICON MAGNESIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
5 Mg 47 Si 45 Fe
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX
Si
%
47
Mg
%
5
Fe
%
45
P
%
S
%
Ni
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
4,3 kg / dm
Special shape
950 - 1275 °C
°C (+/- 2°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO SILICON MAGNESIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
10 Mg 45 Si 42 Fe
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX
Si
%
45
Mg
%
10
Fe
%
42
P
%
S
%
Ni
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
3,8 kg / dm
Special shape
950 - 1245 °C
°C (+/- 2°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRO SILICON MAGNESIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
30 Mg 55 Si 12 Fe
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX
Si
%
55
Mg
%
30
Fe
%
12
P
%
S
%
Ni
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
2,5 kg / dm
Special shape
900 - 1000 °C
°C (+/- 2°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
CALCIUM SILICON MAGNESIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
10 Mg 55 Si 39 Ca
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX
Si
%
55
Mg
%
10
Fe
%
P
%
S
%
Ca
%
39
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
2,2 kg / dm
Special shape
900 - 1100 °C
°C (+/- 2°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERROBOR
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
FeB16
0.4816
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,10
Si
%
1,0
B
%
16
15
18
Al
%
% Mn
%
P
%
S
%
Co
%
4,0
0,50
0,005 0,001 0,005
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
6,7 kg / dm
Special shape
1450 - 1500 °C
-16,2 °C (+/- 6°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERROBOR
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
FeB18
0.4818
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,10
Si
%
2,0
B
%
18
18
20
Al
%
% Mn
%
P
%
S
%
Co
%
2,0
0,50
0,005 0,001 0,005
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
6,5 kg / dm
Special shape
1450 - 1500 °C
-16,9 °C (+/- 5°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERROBOR
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
FeB12C
0.4812
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 2,0
Si
%
4,0
B
%
12
10
14
Al
%
% Mn
%
P
%
S
%
0,50
0,50
0,005 0,1
Co
%
0,005
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
6,7 kg / dm
Special shape
1450 - 1500 °C
-16,2 °C (+/- 6°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERROBOR
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
FeB17C
0.4817
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 2,0
Si
%
4,0
B
%
17
14
19
Al
%
% Mn
%
P
%
S
%
0,50
0,50
0,005 0,1
Co
%
0,005
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
6,6 kg / dm
Special shape
1450 - 1500 °C
-14,2 °C (+/- 6°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERROTITANIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
FeTi30
0.4530
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,10
Si
%
4,0
Ti
%
30
28
32
Al
%
% Mn
%
P
%
S
%
4,5
1,50
0,050 0,060
Co
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
6,2 kg / dm
Special shape
1315 - 1500 °C
-16,4 °C (+/- 4°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERROTITANIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
FeTi40
0.4540
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,10
Si
%
4,5
Ti
%
40
36
40
Al
%
% Mn
%
P
%
S
%
6,0
1,50
0,10
0,060
Co
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
5,9 kg / dm
Special shape
1335 - 1480 °C
-16,3 °C (+/- 4°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERROTITANIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
FeTi50
0.4550
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,10
Si
%
4,0
Ti
%
50
46
50
Al
%
% Mn
%
P
%
S
%
7,5
1,0
0,10
0,060
Co
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
5,6 kg / dm
Special shape
1270 - 1350 °C
-15,4 °C (+/- 4°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERROTITANIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
FeTi70
0.4570
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,20
Si
%
0,20
Ti
%
70
65
75
Al
%
% Mn
%
P
%
S
%
2,0
1,0
0,040 0,030
Co
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
5,4 kg / dm
Special shape
1070 - 1135 °C
-12,3 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERROVANADIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
FeV60
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,15
Si
%
1,5
V
%
60
50
65
Al
%
As
%
P
%
S
%
Cu
%
2,0
0,06
0,06
0,05
0,10
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
6,9 kg / dm
Special shape
1550 - 1600 °C
-18,1 °C (+/- 5°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERROVANADIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
FeV80
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,15
Si
%
1,5
V
%
80
78
82
Al
%
As
%
P
%
S
%
Cu
%
1,5
0,06
0,06
0,05
0,10
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
6,4 kg / dm
Special shape
1690 - 1770 °C
-17,7 °C (+/- 5°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERROPOSPHORUS
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
FeP24
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,10
Si
%
V
%
Al
%
As
%
1,0
3,0
P
%
S
%
23
25
0,01
Cu
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
6,4 kg / dm
Special shape
1250 - 1350 °C
°C (+/- 5°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERROWOLFRAM (TUNGSTEN)
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
FeW1C
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX
Si
%
W
%
Mn
%
0,6
75
85
0,6
As
%
P
%
S
%
Cu
%
0,05
0,05
0,2
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
15,4 kg / dm
Special shape
1650 - 2100 °C
- 8 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERROWOLFRAM (TUNGSTEN)
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
FeW0,1C
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX
Si
%
W
%
Mn
%
0,6
75
85
0,6
As
%
P
%
S
%
Cu
%
0,05
0,05
0,2
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
15,4 kg / dm
Special shape
1650 - 2100 °C
- 8 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRONIOBIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
FeNb65
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,15
Si
%
Nb
%
Ta
%
Al
%
2,0
62
68
1,0
2,5
P
%
S
%
Cu
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
8,1 kg / dm
Special shape
1530 - 1580 °C
- 12 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
FERRONIOBIUM
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
FeNbTa
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX 0,15
Si
%
Nb
%
Ta
%
Al
%
1,5
60
65
6
8
2,0
P
%
S
%
Cu
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
8,4 kg / dm
Special shape
1550 - 1600 °C
- 12 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
TIN
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
Sn
COMPOSITION
C
%
NOMINAL
RANGE
MIN
MAX
Sb
%
Sn
%
Bi
%
As
%
0,02
0,05
P
%
S
%
Pb
%
99,75
0,08
0,08
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
3
7,4 kg / dm
Special shape
230 - 240 °C
- 5 °C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
GRAPHITE
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
C
Electrod cokes
COMPOSITION
C
%
S
%
NOMINAL
RANGE
MIN 99,10
MAX
0,02
N
%
H
%
Ash
%
Volatile
%
%
0,01
0,02
0,30
0,30
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
kg / dm
3
°C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
GRAPHITE
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
C
Petroleum cokes
COMPOSITION
C
%
S
%
NOMINAL
RANGE
MIN 99,00
MAX
0,80
N
%
H
%
Ash
%
Volatile
%
%
0,40
0,60
0,20
0,60
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
kg / dm
3
°C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
GRAPHITE
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
C
High sulphur PET cokes
COMPOSITION
C
%
S
%
NOMINAL
RANGE
MIN 97,00
MAX
2,50
N
%
H
%
Ash
%
Volatile
%
%
0,20
0,11
0,20
0,80
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
kg / dm
3
°C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004
FERROUS ALLOYS
MATERIAL NR
NAME
:
:
GRAPHITE
STANDARD
STANDARD
NAME
DIN
WERKSTOFFNUMMER
C
Metallurgical cokes
COMPOSITION
C
%
S
%
NOMINAL
RANGE
MIN 90,00
MAX
0,80
N
%
H
%
Ash
%
Volatary
%
%
1,00
0,25
9,50
1,50
%
OTHER PROPERTIES
SPECIFIC WEIGHT
SIZE
MELT RANGE
COOLING INDEX
kg / dm
3
°C
°C (+/- 3°)
Temperature change if 1 % of the element is added to a
steel (bath) at 1600 °C
REMARKS
Go to Menu
ir G Henderieckx
GIETECH BV
September 2004