Ancorsteel 150 HP

advertisement
0715-AS150HP-D-2
Pg 1 of 3
Ancorsteel 150 HP
®
Ancorsteel 150 HP is a water atomized
low-alloy steel powder for high performance
applications. The prealloyed 1.5 w/o
molybdenum addition permits extremely good
compressibility and provides good response to
heat treatment. Ancorsteel 150 HP is a good
base powder for a wide range of hybrid alloy
systems.
Typical Analysis and Properties
Composition (weight %) (w/o)
C
<0.01
Mn
Mo
O
0.12
1.5
0.08
Flow Rate
Apparent Density
25 s/50g
2.95 g/cm3
Sieve Distribution (w/o)
Micrometers
+250
U.S. Standard Mesh
(+60)
Trace
-250 /+150
-150 /+45
(-60 /+100 ) (-100 /+325)
66
11
-45
(-325)
23
The Effect of Compaction Pressure on Ancorsteel 150 HP with 0.5 w/o Zinc Stearate
Green Density
Green Strength
Compaction Pressure (tsi)
35
40
45
50
28
7.1
Green Strength (MPa)
Green Density (g/cm3 )
Compaction Pressure (tsi)
35
40
45
50
4000
26
7.2
7.0
6.9
6.8
6.7
6.6
24
22
3000
20
18
16
14
2000
12
10
6.5
6.4
30
Green Strength (psi)
7.3
30
8
400
500
600
Compaction Pressure (MPa)
700
Ancorsteel 85 HP
Ancorsteel 150 HP
NORTH AMERICA Cinnaminson, NJ: +1-856-829-2220, tim.hale@hoeganaes.com
EUROPE Meerbusch, Germany: +49-2132-6598-20, klaus.vossen@hoeganaes.com
400
500
600
700
Compaction Pressure (MPa)
Ancorsteel 2000
Ancorsteel 4600 V
ASIA Seoul, Korea: +82-2-3486-4471, jongsik.na@hoeganaes.com
Pudong Shanghai, China: +86-21-2037-3950, oliver.he@hoeganaes.com
0715-AS150HP-D-2
Data Sheet
Pg 2 of 3
Ancorsteel 150 HP
Properties of Sintered Compacts with Various Graphite Additions
10
8
6
4
2
0
0.2
0.4
0.6
Graphite (w/o)
UTS
Yield (0.2% offset)
0
1.0
0.8
Dimensional Change
Dimensional Change (% from die size)
550
500
450
400
350
300
250
200
150
100
Elongation [% in 25.4 mm (1 inch)]
Tensile Strength (MPa)
Tensile Properties
0.30
0.25
0.20
0.15
0.10
0.05
0
0
0.2
0.4
0.6
Graphite (w/o)
0.8
1.0
% Elongation
Ancorsteel 150 HP plus various amounts of graphite. All specimens were compacted at 620 MPa (45 tsi)
and sintered at 1120˚C (2050˚F) for 30 minutes in dissociated ammonia.
Tensile Properties
1000
A
C
F
900
Nickel (w/o)
2
2
4
800
Copper (w/o)
0
1
1
Graphite (w/o)
0.5
0.5
0.5
Tensile Strength (MPa)
Material
120
700
100
600
80
500
60
400
300
40
200
Ultimate Tensile Strength
20
100
0
Impact Energy
20
1.5
1.0
0.5
0
A
C
Material
F
15
15
10
10
5
5
0
Impact Energy (ft. lbf)
2.0
Impact Energy (Joules)
Elongation [% in 25.4 mm (1 inch)]
Tensile Elongation
A
A
C
Material
A
C
F
0
Dimensional Change (%from die size)
Yield (0.2% offset)
140
Tensile Strength (103psi)
Properties of Sintered Compacts of Ancorsteel 150 HP
C
Material
0.20
F
0
Dimensional Change
0.15
0.10
0.05
0
-0.05
-0.10
A
C
Material
F
F
All specimens were compacted at 620 MPa (45 tsi) and sintered at 1120˚C (2050˚F) for 30 minutes in dissociated ammonia.
NORTH AMERICA Cinnaminson, NJ: +1-856-829-2220, tim.hale@hoeganaes.com
EUROPE Meerbusch, Germany: +49-2132-6598-20, klaus.vossen@hoeganaes.com
ASIA Seoul, Korea: +82-2-3486-4471, jongsik.na@hoeganaes.com
Pudong Shanghai, China: +86-21-2037-3950, oliver.he@hoeganaes.com
0715-AS150HP-D-2
Data Sheet
Pg 3 of 3
Ancorsteel 150 HP
Sinter-hardening (Effects of Accelerated Furnace Cooling)
Material
A
C
F
Nickel (w/o)
2
2
4
Copper (w/o)
0
1
1
Graphite (w/o)
0.5
0.5
0.5
Apparent Hardness
1300
180
1200
1100
160
1000
140
900
120
800
700
6.7 6.8
6.9
7.0
7.1
7.2
7.3
7.4
100
7.5
40
Apparent Hardness (HRC)
200
Ultimate Tensile Strength (103 psi)
Ultimate Tensile Strength (MPa)
Tensile Strength
1400
35
30
25
20
6.7 6.8
Sintered Density (g/cm3)
6.9
7.0
7.1
7.2
7.3
7.4
7.5
Sintered Density (g/cm3)
A
C
F
Impact Energy
15
20
15
10
10
5
6.7 6.8
6.9
7.0
7.1
7.2
7.3
7.4
Impact Energy (ft. lbf))
Impact Energy (Joules)
25
5
7.5
Sintered Density (g/cm3)
All compacts were prepared with 0.5 w/o graphite and 0.5 w/o zinc stearate They were compacted at 620 MPa (45 tsi)
and sintered at 1120˚C (2050˚F) for 30 minutes in dissociated ammonia followed by accelerated cooling
in the water jacketed cooling zone.
IMPORTANT NOTICE: The data shown are based on laboratory processing standard test specimens. Results may vary from those obtained in production processing.
NORTH AMERICA Cinnaminson, NJ: +1-856-829-2220, tim.hale@hoeganaes.com
EUROPE Meerbusch, Germany: +49-2132-6598-20, klaus.vossen@hoeganaes.com
ASIA Seoul, Korea: +82-2-3486-4471, jongsik.na@hoeganaes.com
Pudong Shanghai, China: +86-21-2037-3950, oliver.he@hoeganaes.com
Download