Ancorloy HP-1 ®

advertisement
0715-ALHP1-D-2
Pg 1 of 2
Ancorloy® HP-1
Ancorloy HP-1 is a new press-ready,
engineered binder-treated premixed ferrous
P/M material designed for enhanced
as-sintered mechanical properties. It has
comparable performance to a diffusion
alloyed product of the same composition.
Ancorloy HP-1 is a hybrid alloy based on
Ancorsteel 150 HP to which 4 w/o nickel
and 2 w/o copper have been added during a
binder-treated premixing operation. It is
more highly alloyed than the hybrid alloy
Ancorloy 4. Tempering as-sintered compacts
made from Ancorloy HP-1 improves
their tensile strength and tensile ductility.
Typical Analysis and Properties
Composition (weight %)
Fe
Mo
Mn
Balance
1.4
0.15
Ni
4.0
Cu
2.0
Apparent Density
Flow
3.19 g/cm3
30 s/50 g
Green and Sintered Density vs Compaction Pressure
30
7.3
Compaction Pressure ( tsi )
40
50
0.6 w/o graphite + 0.75 w/o Acrawax C
Density ( g/cm3 )
7.2
7.1
7.0
6.9
6.8
6.7
350
450
550
650
Compaction Pressure (MPa)
Green
Sintered
NORTH AMERICA Cinnaminson, NJ: +1-856-829-2220, tim.hale@hoeganaes.com
EUROPE Meerbusch, Germany: +49-2132-6598-20, klaus.vossen@hoeganaes.com
ASIA Seoul, Korea: +82-2-3486-4471, jongsik.na@hoeganaes.com
Pudong Shanghai, China: +86-21-2037-3950, oliver.he@hoeganaes.com
0715-ALHP1-D-2
Data Sheet
Pg 2 of 2
Ancorloy HP-1
Tensile Strength
50
Tempered at 175ºC (350ºF)
130
800
110
90
600
70
350
450
550
Compaction Pressure (MPa)
650
Dimensional Change (%)
Tensile Elongation
50
0.1
0.05
0
-0.05
350
450
550
650
Compaction Pressure (MPa)
Elongation [% in 25.4 mm (1 inch)]
Dimensional Change
Compaction Pressure (tsi)
30
40
0.15
Compaction Pressure (tsi)
30
40
2.5
1.5
350
450
550
650
Compaction Pressure (MPa)
Compaction Pressure (tsi)
30
40
25
Impact Energy (Joules)
Apparent Hardness (HRA)
50
60
350
450
550
650
Compaction Pressure (MPa)
Impact Energy
Tempered at 175ºC (350ºF)
55
50
2.0
Apparent Hardness
Compaction Pressure (tsi)
30
40
65
UTS
Yield
50
Tempered at 175ºC (350ºF)
15
20
15
10
10
350
Impact Energy (ft. lbf)
400
Tensile Strength (103 psi)
30
1000
Tensile Strength (MPa)
Compaction Pressure (tsi)
40
450
550
650
Compaction Pressure (MPa)
Specimens were compacted from a premix that contained 0.6 w/o graphite and 0.75 w/o Acrawax C lubricant.
Test specimens were sintered for 30 minutes at 1120ºC (2050ºF) in a 75 v/o hydrogen; 25 v/o nitrogen atmosphere.
All as-sintered test specimens were tempered at 175ºC (350ºF) prior to mechanical property testing.
IMPORTANT NOTICE: The data shown are based on laboratory processing standard test specimens. Results may vary from that obtained in production processing.
NORTH AMERICA Cinnaminson, NJ: +1-856-829-2220, tim.hale@hoeganaes.com
EUROPE Meerbusch, Germany: +49-2132-6598-20, klaus.vossen@hoeganaes.com
ASIA Seoul, Korea: +82-2-3486-4471, jongsik.na@hoeganaes.com
Pudong Shanghai, China: +86-21-2037-3950, oliver.he@hoeganaes.com
Download