IR measurements were recorded on a Jasco FTIR spectrometer 460

advertisement
Supplementary Material for Chemical Communications
This journal is © The Royal Society of Chemistry 2002
Supplementary data
100
T ransmitance (% )
90
80
70
60
50
40
4000
S2
S3
S1
M C M -4 1
3200
2400
W a v en u m b e r ( c m - 1)
Figure 1. IR spectra of the pure MCM-41 silica material and the different MCM-41
functionalized supports (S1, S2 and S3) in the OH and CH stretching vibration region.
Spectra were recorded on KBr diluted pellets.
Figure 2. SEM image of the functionalized material S1(the bar represents 1 m).
Macroporous system (from 20 to 70 nm) can be appreciated. Similar SEM images were
obtained for S2 and S3 solids.
Supplementary Material for Chemical Communications
This journal is © The Royal Society of Chemistry 2002
2 (degrees)
Figure 3. X-ray diffraction pattern of S1 solid. Similar X-ray diffraction patterns were
obtained for S2 and S3 solids.
Analysis of the functionalised content of the three solids were carried out by
means of TG analysis of the solids obtained in each step of the synthesis process. From
the registered differences the molar content of the active molecules per gram of
functionalised solid can be calculated. The result obtained for the three solids are as
follows:
TG/TD analysis:
S1: 0.81 mmol antracene/g solid
S2: 0.57 mmol methyl orange/g solid
S3: 0.41 mmol rhodamine/g solid.