Stainless Steel Electrode
ANAND ARC
TECHNICAL DATA
Description
Typical Applications
Classifications
Welding Current (Amps.)
AC / DC (+)
Typical Weld
Metal Analysis (%)
Typical Mechanical
Properties
A rutile coated, all position electrode capable of depositing 316 type of
weld metal with normal carbon content. The weld has excellent
resistance to corrosive agents of reducing nature and also has good
creep strength. The weld metal is of radiographic quality.
For welding ANSI 316, 317 types of stainless steel. It finds application in
a p e r, t e x t i l e , p a i n t a n d c h e m i c a l p r o c e s s i n d u s t r i e s .
AWS : A 5.4 E 316 - 16
IS
: 5206 E 19.12 - 2 R 26
2.50 mm
40 - 60
4.0 mm
95 - 135
5.0 mm
135 - 175
C
Mn
Si
Cr
Ni
Mo
S
P
0.045
1.5
0.45
18.0
12.0
2.30
0.010
0.030
UTS
Elonation % (I=4d)
Ferrite %
Size (mm)
Packing Specifications
3.15 mm
60 - 95
2.50 x 350
3.15 x 350
4.00 x 350
5.00 x 350
: 590 mpa (N/mm2)
: 38.0
: 6.5
Pcs. Per
Carton
110
70
50
30
Pcs. Per
Box
440
280
200
120
Pcs. Per Kg.
47
30
19
12
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
Approved by
Engineers India Ltd.
Projects & Development (I) Ltd.
Nuclear Power Corporation
Toyo Engineering (I) Ltd.
BPCL
ANAND ARC
ANAND - 1A
Stainless Steel Electrode
TECHNICAL DATA
Description
A rutile coated, all position electrode capable of depositing 308 type of
weld metal with normal carbon content. The bead finish is good and slag
removal is easy. The weld metal has excellent resistance to corrosion
and cracking and it has good creep strength. The weld metal is of
radiographic quality.
Typical Applications
For welding ANSI 301, 302 ans 304 types of stainless steel. It finds
application in food and chemical process industries. It can be used to
weld steel with poor weldability.
Classifications
Welding Current (Amps.)
AC/DC (+)
Typical Weld
Metal Analysis (%)
Typical Mechanical
Properties
AWS : A 5.4 E 316 - 16
IS
: 5206 E 19.9 - R 26
2.50 mm
40 - 60
3.15 mm
60 - 95
5.0 mm
135 - 175
C
Mn
Si
S
P
Cr
Ni
0.045
1.50
0.45
0.015
0.030
19.5
10.0
UTS
Elonation % (I=4d)
Ferrite %
Size (mm)
Packing Specifications
4.0 mm
95 - 135
2.50 x 350
3.15 x 350
4.00 x 350
5.00 x 350
: 590 mpa (N/mm2)
: 40.0
: 6.5
Pcs. Per
Carton
110
70
50
30
Pcs. Per
Box
440
280
200
120
Pcs. Per Kg.
47
30
19
11
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
Approved by
Bureau of Indian Standards
Indian Register of Shipping - Gr.2
Uhde India Ltd.
L&T
ANAND ARC
ANAND PLUS
All Purpose
M.S. Electrode
IS 814
CM/L 2007327
TECHNICAL DATA
Description
A medium rutile coated, all position electrodes with smooth operating
characteristics. The electrode gives medium penetration and east
spatter. The electrode has uniform weld bead easily detachable slag and
radiographic quality weld metal. The electrode is ideally suited for
structural work and general fabrication.
Typical Applications
For fabrication of tanks, barges ships, railway wagons boilers etc. And for
structural work, grill work and general fabrication.
Classifications
Welding Current (Amps.)
AC/DC (-)
Weld
Metal Analysis (%)
Typical Mechanical
Properties
AWS : A 5.1 E 6013
IS
: 814 ER 4222 X
2.50 mm
3.15 mm
4.0 mm
5.0 mm
6.3 mm
60 - 90
90 - 140
140 - 175
175 - 210
210 - 270
C
Mn
Si
S
P
0.10 Max
0.15 - 0.40
0.08 - 0.30
0.030 Max
0.030 Max
Size (mm)
Packing Specifications
:
:
:
:
500 mpa (N/mm2)
420 mpa (N/mm2)
24.0
60 Joules
Pcs. Per
Carton
275
150
150
105
70
40
Pcs. Per
Box
1100
600
600
420
280
160
UTS
YS
Elonation % (I=4d)
o
ZCVN Impact at 0 C
2.50 x 350
3.15 x 350
3.15 x 450
4.00 x 350
5.00 x 350
6.30 x 450
Pcs. Per Kg.
60
36
28
18
11
7
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
Approved by
R. D. S. O
IRS CLASS - I
L&T
ANAND ARC
ANAND MIG-1
Copper Coated
MIG Welding Wire
TECHNICAL DATA
Description
ANAND MIG-1 is a double deoxidised Copper Coated MIG Welding Wire
for general engineering and structural applications. The cast, helix
tensile strength and chemistry of the wire are controlled to yield high
quality welds with least spatter.
Typical Applications
It is ideally suited for continuous welding of unalloyed and structural
steels. Finds extensive use in the automobile and container industry.
Also used for welding bicycle frames. Railways bogies earth moving
equipments etc.
Classifications
Welding Current (Amps.)
DC (+)
Weld
Metal Analysis (%)
Typical Mechanical
Properties
Packing Specifications
AWS : A 5.18 ER 70S - 6
IS
: 6419
Size (mm)
0.8
1.0
1.2
1.6
Amps
50 - 160
80 - 200
110 - 250
200 - 400
C
Mn
Si
S
P
0.08
1.50
0.80
0.016
0.018
UTS
2
(mpa (N/mm )
585
YS
2
(mpa (N/mm )
455
EL
%
o
CVN Impact at - 30 C
(Kg/m )
26.0
5.0
Spool of 12.5 Kg. Nett. Wt. In Moisture resistant packing
Drum Packing available.
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND MELT-1
Submerged
Arc Welding Flux
ANAND ARC
Description
Typical Applications
Classifications
Typical weld metal Analysis (%)
When Used With
ANAND SAW-1(EL8) Wire
Typical Weld Metal
Mechanical Properties
When Used With
ANAND SAW-1 (EL8) Wire
Packing Specifications
Redrying Instructions
TECHNICAL DATA
ANAND MELT-1 is an agglomerated Flux designed for Submerged Arc
Welding of mild, medium and high tensile steels in combination with
ANAND SAW-1 (EL8) Grade wire, to yield weld metal with excellent
chemical and mechanical properties. The slag removal is easy and weld
metal has a smooth and shiny finish. Weld metal also of a radiographic
quality.
ANAND MELT-1 Flux in a combination with ANAND SAW-1 Wire is
suitable for welding mild, medium and high strength steels. Extensively
used in welding of thick plates. S.A.W Pipes, Girders, off shore Platforms
and Machines Building applications etc.
AWS/SFA 5.17 F7AZEL8
C
Mn
Si
S
P
0.07
1.10
0.40
0.015
0.020
UTS
YS
Elongation (%) (I-4xd)
CVN Impact
:
:
:
:
525 N/mm2
425 N/mm2
26.0
at RT 80 J
25 Kgs. Net. Packed in Kraft Paper Bags with HDPE Lining from inside.
0
It is recommended to redry the Flux at 350 C for 2 hours before use for
best results..
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND MELT-2
Submerged
Arc Welding Flux
ANAND ARC
Description
Typical Applications
Classifications
Typical weld metal Analysis (%)
When Used With
ANAND SAW-2(EH14) Wire
Typical Weld Metal
Mechanical Properties
When Used With
ANAND SAW-2 (EH14) Wire
Packing Specifications
Redrying Instructions
TECHNICAL DATA
ANAND MELT-2 is an agglomerated Flux designed for Submerged Arc
Welding of mild, medium and high tensile steels in combination with
ANAND SAW-2 (EH14) Grade wire, to give excellent mechanical
0
properties and impacts down to -20 C with extreme resistance to
cracking. Owing to insensitivity to rust, scale, primer on the surface to be
welded, has excellent x-ray characteristics and slag removal.
ANAND MELT-2 Flux in a combination with ANAND SAW-2 Wire is
suitable for welding medium and high strength steel. Extensively used in
welding of Pressure Vessels, Ships Building, Earthmoving Equipments,
Machines Building Applications etc.
AWS/SFA 5.17 F7A2EH14
C
Mn
Si
S
P
0.10
1.40
0.50
0.03
0.03
UTS
YS
Elongation (%) (I-4xd)
CVN Impact
:
:
:
:
530 N/mm2
440 N/mm2
27
0
27 J at-20 C
25 Kgs. Net. Packed in Kraft Paper Bags with HDPE Lining from inside.
0
It is recommended to redry the Flux at 350 C for 2 hours before use for
best results..
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND MELT-3
Submerged
Arc Welding Flux
ANAND ARC
Description
Typical Applications
TECHNICAL DATA
ANAND MELT-3 is an agglomerated aluminate rutile type flux. Relatively
High Silicon pick up is achieved with the flux, when used with EL8 wire
average Manganese pick up also results. ANAND MELT-3 enables the
use of very high speed welding with twin, tandom, and multiwire
technique. The weld metal is not susceptible to porosity when welded on
work place contaminated by rust, scale etc. It is particularly resistant to
arc burn through.
It is used for welding general Structural Steels, Pressure Vessels, Pipe
Steels as well as Fine Grain Steels, Boiler Drums etc. On account of its
good slag detachability ANAND MELT-3 is very commonly used for
welding fillets. ANAND MELT-3 is particularly suited for pipe welding with
high speeds. This Flux can be welded on AC or DC up 1000 Amps (with
single wire process).
General
Classifications
Basicity Index
Granulometry
Classifications
AWS/SFA F7AZEL8
Typical weld metal Analysis (%)
When Used With
ANAND SAW-1(EL8) Wire
Typical Weld Metal
Mechanical Properties
When Used With
ANAND SAW-1 (EL8) Wire
Packing Specifications
Redrying Instructions
0.6
10X150 B.S.S.
C
Mn
Si
S
P
0.070
1.30
0.45
0.018
0.018
UTS
YS
Elongation (%) (I-4xd)
CVN Impact
:
:
:
:
560 N/mm2
460 N/mm2
25.0
at RT 80 J
25 Kgs. Net. Packed in Kraft Paper Bags with HDPE Lining from inside.
o
Flux should be kept dry. It is recommended to redry the Flux at 350 C for 2
hours before use for best results.
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND MELT-4
Submerged
Arc Welding Flux
ANAND ARC
TECHNICAL DATA
Description
Typical Applications
ANAND MELT-4 is an agglomerated aluminate basic type flux.Silicon
pick up is achieved from the flux when used with EL8 wire adequate
Manganese pick up also results.
It is used for welding general Structural Steels, Pressure Vessels, Pipe
Steels as well as Fine Grain Steels, Boiler Drums etc. This flux is
particularly well suited for twin, tandom, multi wire welding at high speed.
ANAND MELT-4 is most suitable for Narrow Gap Welding Applications.
Production of large pipes especially spiral pipes is a typical application of
ANAND MELT-4. On account of its good detachability ANAND MELT-4 is
very commonly used in welding fillets.
General
Classifications
Basicity Index
Granulometry
Classifications
AWS/SFA F7A4EL8
Typical weld metal Analysis (%)
When Used With
ANAND SAW-1(EL8) Wire
Typical Weld Metal
Mechanical Properties
When Used With
ANAND SAW-1 (EL8) Wire
Packing Specifications
Redrying Instructions
1.6
10X150 B.S.S.
C
Mn
Si
S
P
0.07
1.60
0.40
0.019
0.020
UTS
YS
Elongation (%) (I-4xd)
CVN Impact
:
:
:
:
540 N/mm2
430 N/mm2
28
o
at - 40 C 40 J
25 Kgs. Net. Packed in Kraft Paper Bags with HDPE Lining from inside.
o
Flux should be kept dry. It is recommended to redry the Flux at 350 C for 2
hours before use for best results.
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND MELT-5
Submerged
Arc Welding Flux
ANAND ARC
Description
TECHNICAL DATA
ANAND MELT-5 is a basic aluminate type flux which has very good
welding characteristics both in single and multi wire system. It is
weldable on both AC & DC and can carry reasonably high currents. The
flux being basic gives very low Hydrogen and Oxygen contents in weld
o
o
metal and gives excellent impact values down to -40 C, -50 C. The
required weld metal strength is achieved by selection of suitable
unalloyed (plain) and alloyed wires and the alloying elements are
obtained mainly from the wire.
General
Classifications
Basicity Index
Granulometry
Current
Classifications
AWS 5.17 F6A4EL8
F7A4EM12K, F7A5EH14
AWS 5.23 F11A4EG
Typical Weld Metal
Analysis (%)
With Wire
EL8
EM12K
EH14
EF5
With Wire
Typical Weld Metal
Mechanical Properties
Packing Specifications
EL8
EM12K
EH14
EF5
1.6
10X150 B.S.S.
DC or AC
C
0.070
0.082
0.100
0.090
Mn
1.10
1.40
1.50
1.60
Si
0.36
0.38
0.40
0.36
S
0.016
0.017
0.017
0.016
Mo
P
Cr
Ni
0.17
0.16
0.16
0.16 0.60 2.30 0.50
TS
YS
Elong CVN Impact in J
o
o
o
2
2
N/mm N/mm (L=4xd) -30 C -40 C -50 C
440
520
560
820
370
420
470
730
29
28
28
23
-
60
54
35
25 Kgs. Net. Packed in Kraft Paper Bags laminated from inside.
o
Recommendations
30
0
It is recommended to re-dry the Flux at 350 C for 2 hours before use for
best results.
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND MELT-6
Submerged
Arc Welding Flux
ANAND ARC
Description
Typical Applications
Classifications
Typical weld metal Analysis (%)
When Used With
ANAND SAW-1(EL8) Wire
ANAND SAW-3 (EM12K) Wire
Typical Weld Metal
Mechanical Properties
When Used with
ANAND SAW-1 (EL8) Wire
ANAND SAW-3 (EM12K) Wire
Packing Specifications
Redrying Instructions
TECHNICAL DATA
ANAND MELT-6 is an agglomerated Flux designed for submerged arc
welding of medium and high tensile in combination with ANAND SAW-1
(EL8). Grade Wire ANAND SAW-3 (EM12K) wire to yield weld metal with
excellent chemical and mechanical properties with respect with impact
o
values down to -20 C. The slag removal is easy and weld metal has
smooth and shiny finish,is also of radiograhic quality.
ANAND MELT-6 Flux is combination with ANAND SAW-1 / ANAND
SAW-3. Wire suitable for welding medium and high strength steels.
Extensively used in welding of thick plates, S.A.W. Pipes. Grinders, Off
Shore Platforms, Penstock Shells and Machine Building applications
etc.
AWS : SFA 5.17 F7AOEL8/F7A2EM12K
C
Mn
Si
S
P
0.07
1.40
0.40
0.015
0.020
0.08
1.70
0.50
0.018
0.018
UTS
N/mm 2
YS
N.mm 2
EL(%)
1=4xd)
CVN Impact
InJ
515
410
24
At 0 C 50
575
492
25
At -20 C 31
o
o
25 Kgs. Net. Packed in Kraft Paper Bags with HDPE Lining from inside.
o
It is recommended to redry the Flux at 350 C for 2 hours before use for
best results.
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND MELT-7
Submerged
Arc Welding Flux
ANAND ARC
TECHNICAL DATA
Description
Typical Applications
General
Classifications
ANAND MELT-7 is an Aluminate Rutile based acidic type aggiomerated
Submerged Arc Welding Flux.
Its is the most common choice of operators for variety of applications.
This flux is most suitable for single pass weld. It may be used for
multipass welds for the material below 25mm thickness with Anand
SAW-8 (EL12) wire. This prevents cracking sensitivity due to excessive
built-up.
Basicity Index
Granulometry
0.6
10X150 B.S.S.
Classifications
AWS/SFA 5 17 F7AOEL12
Typical weld metal Analysis (%)
When Used with
ANAND SAW-8(EL12) Wire
Typical Weld Metal
Mechanical Properties
When Used with
ANAND SAW-8 (EL12) Wire
Packing Specifications
Redrying Instructions
C
Mn
Si
S
P
0.070
1.22
0.45
0.010
0.012
UTS
YS
Elongation (%) (I-4xd)
CVN Impact
:
:
:
:
560 N/mm2
470 N/mm2
28 o
At 0 C 27 J
25 Kgs. Net. Packed in HDPE Lined Kraft Paper Bags.
o
It is recommended to redry the Flux at 350 C for 2 hours before use for
best results.
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND MELT-03M
Submerged
Arc Welding Flux
ANAND ARC
Description
Typical Applications
General
Classifications
Chemical
Composition (wt. %)
Typical Weld Metal
Mechanical Properties
Packing Specifications
TECHNICAL DATA
ANAND MELT-03M is basic type non-alloyed agglomerated flux for
Submerged Arc Welding of Stainless Steel.
It is ideal for butt & fillet welding at current upto 900 Amp on a single wire.
Slag detachability is excellent leaving a good smooth, bright bead
surface finish. Basicity level produces a low content of micro slag
inclusions and ensures very good low temperature fracture toughness
properties. Flux contains appropriate quantity of elements leads to good
crack resistibiilty of weld metal having appropriate ferrite content.
Basicity Index
Granulometry
Current
With Wire
ER308L
ER316
ER316L
ER347
1.80
12X100 B.S.S.
DC or AC
C
<0.030
<0.06
<0.03
<0.07
Cr
Ni
19.20 9.60
18.60 11.10
19.00 11.30
20.00 9.30
Mo
2.20
2.30
-
Nb
o
>8 C
Tenisle Charpy “V” Notch Ferrite No.
%
Wire Grade Sr
Strength Impact Test Absobed
AWS
Status Elongation
N.mm2 Energy in Joules
o
ER308L
AW
34.0
520
>70 (20 C)
10-11
o
ER316
>70 (20 C)
AW
30.0
560
o
ER316L
>70 (20 C)
AW
32.0
540
o
>65 (20 C)
AW
30.0
580
ER347
Packed in Kraft Paper Bags with HDPE Lining from inside.
Net. Wt. 25 Kgs.
o
Redrying Instructions
Flux should be kept dry. It is recommended to redry the Flux at 350 C for 2
hour before use for best results.
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND MELT-SS3
Submerged
Arc Welding Flux
ANAND ARC
Description
Typical Applications
General
Classifications
Chemical
Composition (wt. %)
Typical Weld Metal
Mechanical Properties
Packing Specifications
TECHNICAL DATA
ANAND MELT-SS3 is basic type non-alloyed agglomerated flux for
Submerged Arc Welding of Stainless Steel.
It is ideal for butt & fillet welding at current upto 900 Amp on a single wire.
Slag detachability is excellent leaving a good smooth, bright bead
surface finish. Basicity level produces a low content of micro slag
inclusions and ensures very good low temperature fracture toughness
properties. Flux contains appropriate quantity of elements leads to good
crack resistibiilty, good mechanical properties and good corrosion
resistibility of weld metal having appropriate ferrite content.
Basicity Index
Granulometry
Current
With Wire
ER308L
ER316
ER316L
ER347
1.40
12X100 B.S.S.
DC or AC
C
<0.030
<0.06
<0.03
<0.07
Cr
20.60
18.60
19.20
20.10
Ni
9.41
11.00
11.15
9.25
Mo
2.60
2.60
-
Tenisle Charpy “V” Notch Ferrite No.
%
Wire Grade Sr
Strength Impact Test Absobed
AWS
Status Elongation
N.mm2 Energy in Joules
o
ER308L
AW
34.0
520
>70 (20 C)
12.-13
o
ER316
>70 (20 C)
AW
30.0
560
o
ER316L
>70 (20 C)
AW
32.0
540
o
>65 (20 C)
AW
30.0
580
ER347
Packed in Kraft Paper Bags with HDPE Lining from inside.
Net. Wt. 25 Kgs.
o
Redrying Instructions
Flux should be kept dry. It is recommended to redry the Flux at 350 C for 2
hour before use for best results.
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
Approved by
ANAND ARC
Description
Typical Applications
Classifications
Welding Current (Amps.)
AC/DC (-)
Weld
Metal Analysis ( %)
Typical
Mechanical Properties
General Purpose
Mild Steel Electrode
IS 814
CM/L 2007327
TECHNICAL DATA
A medium heavy rutile coated, all position mild steel electrode with excellent welding
characteristics producing finely rippled weld metal It is easy to operate even in vertical
down position The weld metal is of radiographic quality.
General fabrication, steel structures, pressure vessels, ship building, boilers, Auto
bodies etc.
AWS : A 5.1 E 6013
IS
: 814 ER 4212 X
2.00 mm
2.50 mm
3.15 mm
4.0 mm
5.0 mm
6.3 mm
40 - 60
60 - 90
90 - 140
140 - 180
180- 230
230 - 300
C
Mn
Si
S
P
0.10 Max
0.30 - 0.60
0.12 - 0.40
0.030 Max
0.030 Max
UTS
YS
Elonation % (I=4d)
ZCVN Impact at 0 Co
% R.A
Size (mm)
Packing Specifications
ANAND - S
Lloyds Register of Shipping - Gr 2
American Bureau of Shipping - Gr 2
Indian Register of Shipping Gr 2
Bureau Veritas - Gr 2
Det Norske Veritas - Gr 2
Engineers India Ltd
Projects & Development (I) Ltd
Bureau of Indian Standards
Nuclear Power Corporation
Directorate of Steam Boilers (IBR)
Toyo Engineering (I) Ltd
Essar Projects Ltd
Uhde India Ltd
M N. Dastur & Co
BPCL. HPCL. IOCL. BHEL
L&T
:
:
:
:
:
2
510 mpa (N/mm )
450 mpa (N/mm2)
26.0
70 Joules
50-70
Pcs. Per
Carton
Pcs. Per
Box
Pcs. Per Kg.
2.00 x 300
2.50 x 350
3.15 x 350
3.15 x 450
360
250
150
150
1440
1000
600
600
103
57
35
27
4.00 x 450
5.00 x 450
6.30 x 450
100
60
30
400
240
120
17
11
7
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND ARC
Description
Approved by
BHEL
Lloyds Register of Shipping - Gr 3YH
American Bureau of Shipping - Gr 3YH
Indian Register of Shipping - Gr 3YH
- Gr 3YH
Bureau Ventas
- Gr 3YH
Det Norske Veritas
Engineers India Ltd
Projects & Development (I) Ltd
Bureau of Indian Standards
Nuclear Power Corporation
Directorate of Steam Boilers (IBR)
Toyo Engineering (I) Ltd
Essar Projects Ltd
BPCL
L&T
HPCL
IOCL
ANANDTHERME
Low Hydrogen
on Powder Electrode
IS 814
CM/L 2007327
TECHNICAL DATA
A heavy basic coated, all positions, low hydrogen electrode having excellent
welding characteristics such as good penetration easy slag removal and low
spatter.
The weld metal is of radiographic quality and has excellent notch toughness
even at - 30°C Weld metal recovery is approx. 115%
Typical Applications
Classifications
Welding Current (Amps.)
AC/DC (+)
Weld
Metal Analysis ( %)
Typical
Mechanical Properties
Pressure Vessels. Boilers, Pipe line Tanks and for welding of restrained
joints and structures designed for service down to -30°C
AWS : A 5.1 E 7018
IS
: 814 EB5426 H,JX / E85426 H3JX
2.50 mm
3.15 mm
4.0 mm
5.0 mm
6.3 mm
65 - 90
100 - 140
150 - 200
200- 250
250 - 320
S
P
0.030 Max
0.030 Max
C
Mn
Si
0.10 Max
0.90 - 1.60
0.25 - 0.65
UTS
YS
Elonation % (I=4d)
o
CVN Impact at -30 C
% R.A
Size (mm)
Packing Specifications
2.50 x 350
3.15 x 350
4.00 x 450
5.00 x 450
6.30 x 450
:
:
:
:
:
2
590 mpa (N/mm )
2
500 mpa (N/mm )
26.0
80 Joules
70
Pcs. Per
Carton
Pcs. Per
Box
250
150
100
60
30
1000
600
400
240
120
Pcs. Per Kg.
57
35
17
11
7
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND SAW-1
Copper Coated
Solid Wire for
SA Welding
ANAND ARC
TECHNICAL DATA
Description
ANAND SAW-1 is a copper coated continuous solid wire for Submerged
Arc Welding (SAW)
Typical Applications
It is ideally suited for continuous welding of Unalloyed, Mild and Medium
Tensile Steels, in combination with agglomerated Submerged Arc
Welding Fluxes. Finds application in the welding of continuously welded
pipes, thicker steel sections, LPG cylinders etc.
Classifications
Standard Wire
Dia (mm)
Wire Analysis (%)
Packing Specifications
AWS/SFA A5.17 EL8
5.0, 4.0, 3.15, 2.5, 2.0 & 1.6
C
Mn
Si
S
P
Cu
0.10 Max
0.25 - 0.60
0.07 Max
0.030 Max
0.030 Max
0.35 Max
Normally supplied as spools on Mild Steel Former with Nett. with 25 Kgs.
wire can also supplied in steel bubbins & in sealed drums of approx. 500
kgs.
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND SAW-2
Copper Coated
Solid Wire for
SA Welding
ANAND ARC
TECHNICAL DATA
Description
Typical Applications
Classifications
Standard Wire
Dia (mm)
Wire Analysis (%)
Packing Specifications
ANAND SAW - 2 is a copper coated continuous solid wire for Submerged
Arc Welding (SAW).
It is ideally suited for continuous welding of Medium and High Tensile
Steels, In combination with agglomerated Submerged Arc Welding
Fluxes. Finds application in the welding of LPG/LNG Storage Tanks, Low
Temperature Service Equipments, Ships Building, Pressure Vessels
etc.
AWS/SFA A5 17 EH14
5.0, 4.0, 3.15, 2.5
C
Mn
0.10 - 0.20 1.70 - 2.20
Si
S
P
Cu
0.10 Max
0.030 Max
0.030 Max
0.35 Max
Normally supplied as spools on Mild Steel Former with Nett. wt. 25 Kgs.
Wire can also supplied in sealed drums of approx. 500 kgs.
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND SAW-3
Copper Coated
Solid Wire for
SA Welding
ANAND ARC
TECHNICAL DATA
Description
Typical Applications
Classifications
Standard Wire
Dia (mm)
Wire Analysis (%)
Packing Specifications
ANAND SAW - 3 is a copper coated continuous solid wire for Submerged
Arc Welding (SAW)
It is ideally suited for continuous welding of all range of thickness of
plates in combination with agglomerated Submerged Arc Welding fluxes
giving excellent impact properties and crack resistibility of welded metal.
Finds application in the welding of single and multi layer welding of
Structural Steels, Ships Building, Offshore Structures thick Pressure
AWS/SFA A5.17 EM12K
5.0, 4.0, 3.15, 2.50
C
Mn
Si
S
0.05 - 0.15 0.80 - 1.25 0.10 - 0.35 0.030 Max
P
Cu
0.030 Max
0.35 Max
Normally supplied as spools on Mild Steel Former with Nett. wt. 25 Kgs.
Wire can also supplied in sealed drums of approx. 500 kgs.
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND SAW-4
Copper Coated
Solid Wire for
SA Welding
ANAND ARC
TECHNICAL DATA
Description
ANAND SAW - 4 is a copper coated continuous solid wire for Submerged
Arc Welding (SAW)
Typical Applications
It is low carbon and medium manganese 0.5 Molybdenum wire for
submerged arc welding. It is to be used with agglomerated submerged
arc welding fluxes. It is suitable for single or multipass weld.
Classifications
Standard Wire
DIA (mm)
Wire Analysis (%)
Packing Specifications
AWS/SFA A5.23 EA2
5.0, 4.0, 3.15, 2.5
C
Mn
Si
S
P
Cu
MO
0.05
to
0.17
0.95
to
1.35
0.20
Max
0.025
Max
0.025
Max
0.35
Max
0.45
to
0.65
Normally supplied as spools on Mild Steel Former with Nett. wt. 25 Kgs.
Wire can also supplied in sealed drums of approx. 500 kgs.
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND SAW-5
Copper Coated
Solid Wire for
SA Welding
ANAND ARC
TECHNICAL DATA
Description
ANAND SAW - 5 is a copper coated continuous solid wire for Submerged
Arc Welding (SAW)
Typical Applications
It is low carbon and high manganese 0.5 Molybdenum wire for
submerged arc welding. It is to be used with agglomerated submerged
arc welding fluxes. It is suitable for single or multipass weld.
Classifications
Standard Wire
DIA (mm)
Wire Analysis (%)
Packing Specifications
AWS/SFA A5.23 Ea3
5.0, 4.0, 3.15, 2.50
C
Mn
Si
S
P
Cu
MO
0.05
to
0.17
1.65
to
2.20
0.20
Max
0.025
Max
0.025
Max
0.35
Max
0.45
to
0.65
Normally supplied as spools on Mild Steel Former with Nett. Wt. 25 Kgs.
Wire can also supplied in sealed drums of approx. 500 kgs.
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND SAW-7
Copper Coated
Solid Wire for
SA Welding
ANAND ARC
TECHNICAL DATA
Description
Typical Applications
Classifications
Standard Wire
Dia (mm)
Wire Analysis (%)
Packing Specifications
ANAND SAW-7 is a copper coated continuous solid wire for Submerged
Arc Welding (SAW)
It is ideally suited for continuous welding of Non- alloyed Construction
Steels, Boiler Plates, Fine Grained Steels, Ship Building Steels, Pipe
Steels etc.
AWS : SFA A 5.17 EH10K
5.0, 4.0, 3.15, 2.50
C
Mn
Si
S
0.07 - 0.15 1.30 - 1.70 0.05 - 0.25 0.025 Max
P
Cu
0.025 Max
0.35 Max
Normally supplied as spools on Mild Steel Former with Nett. Wt. 25 Kgs..
Wire can also supplied in sealed drums of approx. 500 kgs.
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ANAND SAW-8
Copper Coated
Solid Wire for
SA Welding
ANAND ARC
TECHNICAL DATA
Description
Typical Applications
Classifications
Standard Wire
Dia (mm)
Wire Analysis (%)
Packing Specifications
ANAND SAW-8 is a Copper coaled continuous solid wire for Submerged
Arc Welding (SAW)
It is a low carbon and low manganese general purpose wire for
submerged arc welding. It is to be used with agglomerated submerged
arc welding fluxes. It is suitable for single or multipass weld.
AWS/SFA A5.17 EL12
5.0, 4.0, 3.15, 2.5, 2.0 AND 1.6
C
Mn
0.04 - 0.14 0.25 - 0.60
Si
S
P
Cu
0.10 Max
0.030 Max
0.030 Max
0.35 Max
Normally supplied as spools on Mild Steel Former with Nett. Wt. 25 Kgs..
Wires can also supplied in sealed drums of approx. 500 kgs.
ANAND ARC LTD.
(AN ISO 9001 COMPANY)
30, Kala Udyog, L.B.S. Marg, Bhandup, Mumbai-400 078
Tel. : 2566 1853 / 2566 1788 / 2566 4340 / 2566 4321
Fax : 2566 2833
Email : sales@anandarc.com / anandarc@bom5.vsnl.net.in
Site : www.anandarc.com
ANAND ARC PRODUCTS
More than a Source, a Solution
ELECTRODE DETAILS
ANAND ARC
Typical Weld
Properties
Mn
ANANDPLUS
Classification: AWS E 6013 IS ER 4222X
Approved by: IRSGR2, UHDE, L&T, BIS
ANAND PLUS is an all purpose mild steel electrode ideally suited for
welding in all positions using AC and DC power Sources. High rutile
content ensures soft arc, easily detachable slag, and uniform weld
bead and the weld metal is of radiographic quality. Recommended
for welding of tanks, barges, wagons, autobodies etc. and general
fabrication.
C
0.090
Sizes
(mm)
0.12
2
500mpa(N/mn )
2
YS
420mpa(N/mm )
El
24.0%
(l=4d)
CVN impact
at 0°C
Pieces
Per Carton
Pieces metal
Per Box
Si
0.30
UTS
Current Range
Amps
60Joules
2.00x300
40-60
375
1500
2.50x350
60-90
275
1100
3.15x350
90-140
150
600
3.15x450
90-130
150
600
4.00x450
140-170
105
420
5.00x450
170-200
70
280
6.30x450
210-270
AC/DC (-)
40
160
40-60
360
1440
ANAND - S
Classification : AWS E 6013 IS ER 4212X
Approved by : LRS-Gr2, ABS-Gr2, IRS-Gr2, BV-Gr2, DNV-Gr2, EIL,
PDIL, BIS, NPC, IBR, CRL, BPCL, TOYO ENGG., UHDE INDIA, ICB,
MNDASTUR&CO.,ESSARPROJECTSLTD.,IOCL,L&T.
A medium heavy rutile coated, all position electrode for general fabrication
and structural work- The welding characteristics include smooth arc, easy
slag removal, minimum spatter and well rippled bead. Weld metal is of
radiographicquality.RecommendedforweldingofShips,PressureVessels,
Pipe lines, storage tanks, Boilers, Automobile bodies, railway wagon and
generalfabrication.
C
Mn
%0.080
0.45
Si
0.20
2.50x350
60-90
250
1000
2
3.15x350
100-140
150
600
UTS 510mpa(N/mn )
YS 450mpa(N/mm )
El
24.0%
(l=4d)
CVN impact
at 0°C
2.00x300
2
70Joules
3.15x450
100-130
150
600
4.00x450
140-180
100
400
5.00x450
180-230
60
240
6.30x450
230-300
AC/DC (-)
30
120
60-90
175
700
ANAND - SS
Classification : AWS E 6013 IS : ERR 4222X / ERR 4222X
Approved by : BIS, IBR
A heavy coated, rutile type, all position electrode with excellent welding
characteristics. The welding speeds are higher and the weld metal is of
radiographic quality. The electrode can be used for "touch welding".
Application includes Welding of Boilers, Bridges, Ships, Compressors,
Automobilepartsetc.andrapidfillingofgaps.
C
Mn
%0.080
Si
0.45
0.20
2
2.50x350
UTS
510mpa(N/mn )
3.15x450
100-140
105
420
YS
450mpa(N/mm2)
4.00x450
140-190
65
260
190-250
40
160
El
26.0%
5.00x450
(l=4d)
AC/DC(-)
CVN impact
at 0°C
70Juoles
ANAND - 714
C
Classification : AWS E 7014 IS : ERR 5222JX
A medium heavy coated, all position electrode, containing iron powder in the
coating. The electrode is capable of taking higher currents and thus gives
higher welding output. The weld metal is of radiographic quality and the
depositionefficiencyisapprox.110%.Recommendedforgeneralfabrication,
welding of thicker sections, making corner joints, and any other applications
requiringhigherweldingoutputandfastdepositionrate.
%0.090
Mn
Si
0.5
2.50x350
70-100
175
700
2
0.4
3.15x450
100-150
105
420
2
4.00x450
150-200
65
260
5.00x450
200-250
AC/DC(-)
40
160
UTS 510mpa(N/mn )
YS 420mpa(N/mm )
El
(l=4d)
26.0%
CVN impact
at 0° C
60Joules
ELECTRODE DETAILS
ANAND ARC
ANAND-724
Typical Weld
metal Properties
C
Mn
Si
Sizes
(mm)
Current Range
Amps
Pieces
Per Carton
Pieces
Per Box
Classification :AWSE7024IS:ERR5235KX
%0.07
Aheavycoatedironpowder,electrodewithadepositionefficiencyofapprox.
140%. The electrodes can take high currents, thereby increasing welding
productivity.Idealfortouchweldinginflatandhorizontalpositions.Theweldis
of radiographic quality. Suitable for heavy machine parts, heavy structural
worklikeweldingofcolumnsandgirders,shipbuildingetc.
0.55
2.50x350
80-120
2
0.35
3.15x450
130-170
75
300
2
YS 420mpa(N/mn )
4.00x450
80-240
45
180
El
5.00x450
250-290
35
120
UTS 510mpa(N/mm )
25.0%
(L=4d)
CVN impact
at 0°C
LOW HYDROGEN ELECTRODE
ANAND SUPER PLUS
Classification : AWS E 7016 IS : EB5426H2X
Approvedby:BIS,BPCL,EIL,PDIL
A medium heavy coated, all position, low hydrogen electrode for welding of
Carbon Steels. It is also suitable for joining mild steel to cast steel, for
depositing non-machinable welds on Cast iron and as a buffer layer before
hardfacing.RecommendedforfabricationofBoilers,PressureVessels,ships
etc.andforweldingcaststeel,castiron,mildandlow-alloysteels.
AC/DC(-)
70Joules
C
Mn
%0.08
1.0
Si
2.50x350
60-90
225
900
2
0.40
3.15x450
95-140
130
520
2
YS 500mpa(N/mm )
4.00x450
140-180
85
340
El
5.00x450
180-240
55
220
6.30x450
240-310
30
120
UTS 590mpa(N/mm )
26.0%
(l=4d)
CVN impact
at - 30° C
AC/DC(+)
80Joules
ANANDTHERME
Classification :AWSE7018IS:EB5426H,JX/ EB5426H3X
Approved by: LRS-Gr3YH, ABS-Gr3YH, IRS-Gr3YH, BV-Gr3YH,
DNV-Gr3YH, EIL, PDIL, BIS, NPC, IBR, UHDE INDIA, TOYO ENGG.,
ICB,BPCL,MNDASTUR&CO.,ESSARPROJECTSLTD.,I0CL,L&T.
A heavy basic coated, low hydrogen iron powder type of electrode with
excellent welding characteristics. The weld metal is ductile, crack resistant
and is of radiographic quality, Easy to operate in all position efficiency is
approx. 115%. Suitable for welding of pressure vessels, Restrained joints,
Penstocks,shipconstruction,Boilers,Bridgesetc.
C
Mn
%0.080
Si
0.12
0.40
2.50x350
60-90
150
600
UTS 590mpa(N/mn )
3.15x450
100-140
105
420
YS 500mpa(N/mm2)
4.00x450
150-200
70
280
5.00x450
200-240
45
180
6.30x450
250-320
30
12 0
2
El
26.0%
(L=4d)
CVN impact
AC/DC(+)
at -30°C
70Juoles
ANANDTHERME (SPL)
Classification : AWSE 7018-1 IS : EB5626H,JX
Approved by : UHDE, EIL, NPC, TOYO ENGG.
A heavy coated, low hydrogen iron powder type of electrode, specially
designed for high CVN impact values down to - 50° C. The weld metal is
resistant to cracking and is of radiographic quality. Metal recovery approx.
110% Suitable for welding of pressure vessels & Equipments, subjected
to severe stress and low temperatures down to - 50° C, Ammonia Storage
tanks, Hortonspheres etc.
C
Mn
%0.08
1.3
Si
2.50x350
60-90
150
600
2
0.30
3.15x450
100-140
105
420
2
YS 500mpa(N/mm )
4.00x450
150-200
70
280
El
5.00x450
200-240
45
180
6.30x450
250-320
UTS 590mpa(N/mn )
26.0%
(l=4d)
CVN impact
at - 45° C
AC/DC(+)
60Joules
30
1 20
ELECTRODE DETAILS
ANAND ARC
LOW ALLOY, HIGH TENSILE ELECTRODES
Typical Weld
metal Properties
Mn
Si
ANANDTMERME-Ni
Classification :AWSE7018-GIS:EB5626H2JX
A medium heavy coated iron powder, low hydrogen type of electrode,
yielding0.5%Niintheweldmetal.Theweldmetalisofradiograpicqualityand
hasgoodnotchtoughnessdownto-60° C.Thedepositionefficiencyis115%
approx. Recommended for welding heavy sections, restrained joints,
requiring good notch toughness down to - 50° C and for welding fine grained
steelcontainingNiupto1%.
ANANDTHERME - Ni (X)
C
%0.07
1.4
0.30
Ni
0.60
2
UTS 550mpa(N/mn )
YS 480mpa(N/mm2)
El(l=4d) 27.0%
CVN impact
50Joules
at -50° C
C
Mn
Si
Ni
Classification : AWS E 8018-G IS : E55BG129Fe
Approved by: EIL
Abasiccoated,lowhydrogen,ironpowdertypeofelectrodeyielding1.5%Mn
and0.7%Niintheweldmetal.Recommndedforweldingoffinegrained,high
strength Q & T steels, Penstocks, Pressure vessels etc., where a
combination of high strength and sub-zero impact toughness are called for.
Also recommended for welding of low alloy steels, containing Ni upto 1 %.
Theweldsareofradiographicqualityandhasgoodnotchtoughnessdownto
-60° C.Thedepositionefficiencyisapprox.115%.
%0.07
1.6
0.20
0.75
ANAND-818W
C
%0.06
Classification : AWS E 8018-W2 IS : E55BG 129 Fe
A basic coated all position electrode, designed for welding of weathering
steels such as Corten A, Corten B etc. The weld metal has excellent
resistancetoatmosphericcorrosionandisofradiographicquality.Suitablefor
welding of weathering steel used in the construction of Railway wagons,
Bridgesetc.andalsohightensilesteels..
2
Sizes
(mm)
Current Range
Pieces
Amps
Per Carton
Pieces
Per Box
2.50x350
3.15x450
4.00x450
5.00x450
6.30x450
70-100
100-140
140-180
180-250
250-320
AC/DC(+)
150
105
70
45
30
600
420
280
180
120
2.50x350
70-100
150
600
UTS
580mpa(N/mm )
3.15x450
100-140
105
420
YS
500mpa(N/mm2)
4.00x450
140-180
70
280
El
26.0%
(l = 4d)
5.00x450
180-250
45
180
6.30x450
250-320
30
120
60-90
150
600
420
CVN impact
at-60°C
AC/DC(+)
70Joules
Mn
0.7
Si
0.4
Cr
Ni
Cu
0.6
0.7
0.5
2.50x350
3.15x450
100-140
105
UTS 580mpa(N/mn2)
4.00x450
140-180
70
280
500mpa(N/mn2)
5.00x450
180-230
45
180
6.30x450
240-310
30
120
600
YS
El(l=4d)
25.0%
CVN impact
60Joules
AC/DC(+)
at- 20° C
ANAND-918
Classification : AWS E 9018 - M IS : E63BM 129 Fe
Hydrogen controlled, Iron powder type of electrode for all position welding of
high tensile, low alloy structural steels. The weld metal has good notch
toughness down to - 51 C and is of radiographic quality. Ideal for welding
penstocks, machinery parts, heavy duty structures, Pressure vessels,
Pipingsetc.
C
Mn
Si
%0.05
1.0
0.5
2.50x350
60-90
150
Ni
Mo
3.15x450
100-140
105
420
1.7
0.3
4.00x450
140-180
70
280
UTS 650mpa(N/mm2)
5.00x450
180-250
45
180
580mpa(N/mm2)
6.30x450
240-310
30
120
YS
El(l=4d) 24.0%
AC/DC(+)
CVN impact
at - 50° C
ANAND-918W
Classification :AWSA5.5E9018-GIS:E63B-D124J
Alowhydrogen,LowAlloySteel,Ironpowderelectrodespeciallydesignedfor
welding of high strengh Railway/Concor wagons. The electrode is also
suitable for welding of High Tensile Steels, Pen stocks, Machinery Parts and
heavydutystructures.
50Joules
C
Mn
Si
Mo
%0.06
1.30
0.20
0.25
2.50x350
60-90
150
600
to 0.10 to 1.75
0.45
0.45
3.15x450
100-140
105
420
280
4.00x450
140-180
70
UTS 630-670mpa(N/mn2)
5.00x450
180-250
45
180
530-570mpa(N/mn2)
6.30x450
240-310
30
120
YS
El(l=4d) 20-25%
RA
48-60%
CVN impact
at - 50°C
: 30-65 Joules
at R.T.
: 90-140 Joules
AC/DC(+)
ELECTRODE DETAILS
ANAND ARC
ANAND MONICHROM
Classification :AWSE10016GIS:E68BG126Fe
Anand Monichrom is a low hydrogen, low alloy all position electrode. The
weldmetalhasveryhightensilestrengthandisresistanttohightemperature
abrasion, Recommended for welding high strength steels, earth moving
equipment etc. and repair welding of hot forging dies, mould, steam turbine
rotorsetc.
ANAND 1118
Classification : AWS : E 11018-M IS : E76BM329Fe
A low hydrogen, low alloy, iron powder electrode for all position welding of
high tensile, fully killed, fine grained, quenched and tempered steels. The
weld metal has good notch toughness down to -51° C and is of radiographic
quality. Ideal for welding of penstocks, heavy duty structures, earth moving
equipmentandhighstrengthsteelssuchasHY80andSA517grades.
Typical Weld
metal Properties
C
Mn
Si
%0.06
1.3
0.3
Cr
Ni
Mo
1.0
2.5
0.7
UTS 800mpa(N/mm2)
YS 700mpa(N/mm2)
El(l = 4d) 20.0%
CVN impact
at 50Joules
at-50° C
Sizes
(mm)
2.5x350
3.15x450
4.0x450
5.0x450
6.3x450
Current Range
Pieces
Amps
Per Carton
60-90
100-140
140-180
190-240
250-320
AC/DC(+)
Pieces
Per Box
225
130
85
55
30
900
520
340
220
120
600
C
%0.06
Mn
1.5
Si
0.45
2.50x350
60-90
150
Cr
Ni
Mo
3.15x450
100-140
105
420
0.3
2.1
0.4
4.00x450
140-180
70
280
UTS 800mpa(N/mm2)
5.00x450
180-240
45
180
740mpa(N/mm2)
6.30x450
250-320
30
120
YS
El(l=4d) 24.0%
AC/DC(+)
CVN impact
55Joules
at - 50° C
ANAND MOLY
Classification : AWS : E 7018 -A1 IS : E49BA126Fe
Alowhydrogen,ironpowdertype,allpositionelectrodeyieldingaductileand
creep resistant weld metal containing 0.5% Mo. The weld metal is of
radiographicquality.Suitableforwelding1/2Moand1Cr-1/2Mosteels,boiler
tubesandplates,andforotherhightemperatureapplicationsupto525° C.
C
Mn
Si
%0.07
0.75
0.35
2.5x350
Mo
3.15x450
60-90
145
580
100-140
105
420
280
0.5
4.0x450
140-180
70
UTS 550mpa(N/mm2)
5.0x450
180-250
50
200
460mpa(N/mm2)
6.3x450
250-320
30
120
580
YS
El(l=4d)
26.0%
CVN impact
AC/DC(+)
150Joules
at R.T
ANAND CHROM -1
Classification : AWS : E 8018 - B2 IS : E55B-B2 26 Fe
Approved by : EIL
A low hydrogen, iron powder type, all position electrode yielding a creep
resistantweldmetalcontaining1.25%Cr.and0.5%Mo.Theweldmetalisof
radiographic quality and has creep resistance upto 550° C. Recommended
for welding 1 Cr 0.5 Mo and 0.5 Cr- 0.5 Mo steels, used in Boilers, super
heaters,pipelines,oilrefineriesetc.
ANAND CHROM - 2
Classification : AWS : E9018 - B3 IS : E63B-B3 26Fe
Approved by : EIL
A low hydrogen, iron powder type, ail position electrode yielding a creep
resistant weld metal containing 2.25% Cr. and 1% Mo. The weld metal is of
radiographic quality and has creep resistance upto 600° C. Recommended
for welding 2.25% Cr. 1 % Mo steels, used in Boilers, oil refineries power
plantsetc.atservicetemp.upto600° C.
C
%0.06
Mn
0.80
Si
0.45
2.5x350
60-90
145
Cr
Mo
3.15x450
100-140
105
420
1.35
0.55
4.0x450
140-180
70
280
UTS 600mpa(N/mm2)
YS
5.0x450
500mpa(N/mm2)
El(l=4d)
6.3x450
25.0%
Creep Strength
180-240
50
200
240-320
30
120
AC/DC(+)
120Joules
at 550° C
C
%0.06
Mn
0.80
Cr
Mo
2.2
1.1
Si
0.45
2.5x350
60-90
145
580
3.15x450
100-140
105
420
4.0x450
140-180
70
280
UTS 650mpa(N/mm2)
5.0x450
180-240
50
200
560mpa(N/mm2)
6.3x450
240-320
30
120
YS
El(l=4d)
23.0%
Creep Strength
at 575° C
AC/DC(+)
90Joules
ELECTRODE DETAILS
ANAND ARC
ANAND CHROM - 5
Classification : AWS : E 8018 - B6 IS:41BB626Fe
Approved by : EIL
A low hydrogen, Iron powder type, all position electrode yielding a creep
resistant weld metal containing 5% Cr. and 0.5% Mo. The weld metal is of
radiographic quality and has excellent creep resistance upto 550° C.
Recommended for welding of 5 Cr 0.5% Mo steels for high temperature
applications in oil refineries, power plants, fertilizer and pharmaceutical
industries.
Typical Weld
metal Properties
C
Mn
Si
%0.07
0.80
0.4
Cr
Mo
5.0
0.5
2
UTS
580mpa(N/mn )
2
YS
500mpa(N/mn )
El(l=4d) 23.0%
Creep Strenth
80Joules
at 575° C
Sizes
(mm)
2.5x350
3.15x450
4.0x450
5.0x450
6.3x450
Current Range
Pieces
Amps
Per Carton
Pieces
Per Box
60-90
100-140
140-180
180-240
240-320
AC/DC(+)
145
105
70
50
30
580
420
280
200
120
HARDFACING ELECTRODES
ANAND C -1
A medium heavy coated, rutile type of electrode, depositing an air hardening
type of weld metal of appro. 250 BHN hardness. The weld metal is
machinable. Recommended for Gears, Shafts, Axles, Pinion teeth and
Machinery parts where moderate hardness and toughness combined with
easymachinabilityisdesired.
Hardness 250 BHN
on 3rd Layer
3.15x450
4.0x450
5.0x450
100-140
140-180
180-220
AC/DC(-)
130
85
55
520
340
220
Hardness 400 BHN
on 3rd Layer
3.15x450
4.0x450
5.0x450
6.3x450
100-140
140-180
180-220
220-290
AC/DC(-)
130
85
55
30
520
340
220
120
Hardness 600 BHN
on 3rd Layer
3.15x450
4.0x450
5.0x450
100-140
140-180
180-220
AC/DC(-)
130
85
55
520
340
220
Hardness 600 BHN
3.15x450
100-140
110
440
ANAND C - II
A medium heavy coated, rutile type of electrode, depositing an air hardening
type of weld metal of appro. 350 BHN hardness. A buffer layer of ANAND
SUPER PLUS is recommended on hard base materials. The weld metal is
machinable. Suitable for Shear blades, shafts, axles, pulleys, brake shoes,
couplings,conveyorparts,steelcastingsetc.
ANAND C- III
A medium heavy coated, rutile type of electrode, depositing an air hardening
typeofweldmetalofapprox.600BHNhardness.Theweldmetalconsistsof
hardchromiumcarbidesinamartensiticmatrix.Itisnonmachinableandcan
onlybeground.Theelectrodeisrecommendedforhardfacingwheresevere
conditions of abrasion, friction, accompanied by moderate impact exist.
Suitable for Shear blades, Shafts, axles, pulleys, brake shoes, couplings,
conveyorparts,steelcastingsetc.
ANAND C -III(LH)
Amediumheavycoated,lowhydrogenelectrodedepositinganairhardening
type of weld metal of approx. 600 BHN hardness. The low hydrogen coating
enables the electrode to be used on high carbon and high sulphur steels
without the risk of underbead cracking or porosity. The electrode is
recommended for hardfacing where severe conditions of abrasion, friction,
accompaniedbymoderateimpactexist.Theweldisnotmachinableandcan
only be ground. Recommended for parts of earth-moving equipments, oil
expellers,crusherhammers,shears,cranewheels,scraperblades,punching
diesetc.
on 3rd Layer
4.0x450
140-180
70
280
5.0x450
180-220
40
160
AC/DC(+)
ELECTRODE DETAILS
ANAND ARC
ANAND C - V
A medium heavy coated, low hydrogen type, hardfacing electrode
depositing alloyed cast iron type of weld metal. The weld metal is
hard and extremely resistant to abrasion and metal to metal wear,
has a hardness of approx. 600 BHN. Suitable for concrete mixer
blades, excavator teeth, bucket lips, scarper blades, cement die
rings, plough shares, oil expellers etc.
ANANDC-VI
A heavy coated hard facing electrode yielding weld metal, resistant to
abrasion, corrosion, erosion, heat and impact. The weld metal has an asdeposited hardness of approx. 250 BHN, which increase to 500 BHN under
impactinservice.ForhardfacingMillhammers.Crushermantles.Ingotlifting
tongs, Industrial valves, coal minimg cutters etc. and other applications
involvingabrasion,corrosionheatandimpact.
ANANDMANGAN
A basic coated, low hydrogen type of electrode, depositing austenitic weld
metal of 12% Mn composition. The weld metal is tough and work hardens to
more than 500 BHN in service under severe impact. Reconditioning of
medium Manganese steel rail points and crossings, rock crusher jaws,
crusher hammers, bulldozer teeth, dredger bucket, austenitic manganese
steelcastingsetc.
ANAND HSS
Sizes
(mm)
Hardness 600 BHN
on 3rd Layer
ANAND - IA
Classification : AWS : E 308-16 IS : E19.9R 26
Approved by : EIL, PDIL, CRL, NPC, BPCL, TOYO ENGG.
Anormalcarbon19/10typeofstainlesssteelelectrodewithcontrolledferrite.
The weld metal has good resistance to cracking, corrosion, and scaling upto
800° C. The weld metal is of radiographic quality. Suitable for welding
stainlesssteelsofAISI301,302,304and308composition.Forfabricationof
equipments used in food industry. Hospital apparatus, Pharmaceutical
equipmentetc.
ANAND - IA - 15 conforming to AWS E 308-15 can also be
manufacturedonrequest..
Pieces
Per Box
3.15x450
100-140
130
4.0x450
140-180
85
520
340
5.0x450
180-220
55
220
AC/DC(+)
Hardness
A.W. 250 BHN
W.H. 500 BHN
2.5x350
3.15x350
4.0x350
5.0x350
60-80
90-130
140-180
180-220
AC/DC(+)
150
95
60
35
600
380
240
140
Hardness
A.W. 200 BHN
W.H. 500 BHN
3.15x450
4.0x450
5.0x450
100-140
140-180
180-220
AC/DC(+)
105
65
40
420
260
160
Hardness (A.W.) 600 BHN
2.5x350
3.15x350
4.0x350
5.0x350
Anand HSS, deposits high speed steel type of weld metal, corrosponding to
steelusedforhotworkingandtoolsteels.Theweldmetalhasan"Aswelded"
hardnessofapprox.600BHNwhichisretaineduptoabout600° C.Theweld
metal also has resistance to "metal to metal wear", abrasion and impact.
Recommended for surfacing of hot trimming tools. Hot shear blades, ingot
liftingtongs,Rollingmillguides,punchingandformingdiesetc.
STAINLESS STEEL ELECTRODES
Current Range
Pieces
Amps
Per Carton
Typical Weld
metal Properties
C
Mn
Si
%0.045 1.55
0.45
Cr
Ni
19.0
0.0
2
UTS 590mpa(N/m )
El(l=4d) 40.0%
Ferrite
5.0%
Sizes
(mm)
2.0x300
2.5x350
3.15x350
4.0x350
5.0x350
60-90
100-140
140-180
180-220
AC/DC(+)
Current Range
Amps
35-45
40-60
60-95
95-135
130-175
AC/DC(+)
200
115
75
45
Pieces
Per Carton
210
110
70
50
30
800
460
300
180
Pieces
Per Box
840
440
280
200
120
ELECTRODE DETAILS
ANAND ARC
ANAND -1B
Classification :AWSE347-16IS:E19.9NbR26
A normal Carbon 19/10 stabilised stainless steel electrode with controlled
ferrite, Niobium in the weld metal prevents Chromium Carbide precipitation
and provides resistance to inter-grannular corrosion. The weld metal has
excellent creep strength and is of radiographic quality. Recommended for
welding of AISI 304, 308, 321 and 347 composition, in application where the
materialhastowithstandhotexhaustgasesorhightemperatures.
ANAND-IB-15 conforming to AWS E 347 - 15 can also be
manufacturedonrequest.
Typical Weld
metal Properties
C
Mn
Si
%0.045 1.55
0.45
Cr
Ni
Cb
19.0
10.0
0.45
2
UTS 590mpa(N/mm )
El(l=4d) 40.0%
Ferrite
6.0%
Sizes
(mm)
2.5x350
3.15x350
4.0x350
5.0x350
Current Range
Pieces
Amps
Per Carton
Pieces
Per Box
40-60
60-95
95-135
135-175
AC/DC(+)
110
70
50
30
440
280
200
120
440
ANAND - 1C
Classification : AWS E 308L-16 IS : E 19.9 Lr26
Approved by : PDIL, EIL, NPC.
Anextralowcarbon19/10typestainlesssteelelectrodewithcontrolledferrite.
Extra low Carbon content, in the weld metal, eliminates the chances of
intergrannular corrosion at elevated temperatures. The weld metal has
excellent creep strength and is of radiographic quality. Suitable for welding
stainless steels of AISI 301, 302, 304, 304L and 308 composition. Finds
applicationinNuclearPlant,Foodstuffsandchemicalprocessindustries.
ANAND-IB-15 Conforming to AWS E 347-15 can also be
manufacturedonrequest.
C
Mn
Si
%0.030
1.55
0.45
Cr
Ni
19.0
0.0
UTS
580mpa(N/mm2)
El(l=4d)
40.0%
Ferrite
6.0
2.5x350
40-60
110
3.15x350
60-95
70
280
4.0x350
95-135
50
200
5.0x350
135-175
30
120
210
110
70
50
30
840
440
280
200
120
110
70
50
30
440
280
200
120
AC/DC(+)
ANAND - 2A
Classification : AWS E 316-16 IS : E 19.12.2 R 26
Approvedby:EIL,PDIL,BPCL,TOYOENGG.
A normal carbon 19/12/Mo type of stainless steel electrode with controlled
ferrite. The weld metal has excellent resistance to corrosion agents of
reducingnatureandalsohasgoodresistancetopittingandisofradiographic
quality. Suitable for welding AISI 316 and 317 type of stainless steels. It finds
applicationinPaper,Textile,paintsandchemicalprocessindustries.
C
Mn
Si
%0.045
1.5
0.45
Cr
Ni
Mo
18.0
12.0
2.3
2
UTS 590mpa(N/mm )
El(l=4d) 38.0%
Ferrite
6.5%
2.0x300
2.5x350
3.15x350
4.0x350
5.0x350
35-45
40-60
60-95
95-135
135-175
AC/DC(+)
ANAND-2A-15 Conforming to AWS E 316-15 can also be
manufacturedonrequest.
ANAND - 2B
Classification : AWS E 318-16 IS : E 19.19.2 Nb R 26
Approved by : EIL.
A normal carbon 18/13/Mo, stabilised stainless steel electode with controlled
ferrite. It can be used in all positions to deposit weld metal resistant to pitting,
stress corrosion cracking, chemical corrosion and intergrannular corrosion.
Theweldmetalhasexcellentcreepstrengthupto850° andisofradiographic
quality. Recommended for welding AISI 316, 317 and 318 types of stainless
steels.Forthefabricationofchemicalplants,papermillequipment,bleaching
equipment,picklingplantetc.
C
Mn
Si
%0.045
1.5
0.45
Cr
Ni
Mo Cb
18.0
12.0
2.3 0.45
UTS 590mpa(N/mm2)
El(l=4d) 38.0%
Ferrite 6.5%
2.5x350
3.15x350
4.0x350
5.0x350
40-60
60-95
95-135
135-175
AC/DC(+)
ELECTRODE DETAILS
ANAND ARC
ANAND -2C
Approvedby:EIL,NPC
Classification :AWSE316L-16IS:E19.12.2Lr26
A extra low carbon 18/13/Mo type of stainless steel electrode with controlled
ferrite. The weld metal has excellent resistance to intergrannular corrosion
even at elevated temperature. It also has good resistance to stress corrosion
cracking&hotcrackingandisofradiographicquality.SuitableforweldingAISl
316Land317Ltypesofstainlesssteels.Findsapplicationinchemicalplants,
paint,paperandtextileindustries.
ANAND -2D Conforming to AWS E 317- L-16 can also be
manufacturedonrequest.
Typical Weld
metal Properties
C
Mn
Si
%0.030
1.5
0.45
Cr
Ni
Mo
18.0
12.0
2.3
2
UTS 580mpa(N/mm )
El(l=4d)
38.0%
Ferrite
6.0%
Sizes
(mm)
2.5x350
3.15x350
4.0x350
5.0x350
Current Range
Pieces
Amps
Per Carton
40-60
60-95
95-135
135-175
AC/DC(+)
Pieces
Per Box
110
70
50
30
440
280
200
120
440
ANAND-D2
Classification :AWSE309-16IS:E23.12R26
Approvedby:PDIL,BPCL
A medium heavy coated rutile type all position electrode, depositing 23Cr/12
Ni type of weld metal. The weld metal has excellent resistance to chemical
corrosion and oxidation upto 1100° C. The electrode has good welding
characteristics. Recommended for AISl 309 grade of stainless steel and
straight chrome steel. For joining clad steels, stainless steels to low alloy
steelsandcarbonsteels.
ANAND-D2-15 Conforming to AWS E 309 -15 can also be
manufacturedonrequest.
C
Mn
Si
%0.05
1.75
0.45
2.5x350
40-60
110
Cr
Ni
3.15x350
60-95
70
280
23.5
13.0
4.0x350
95-135
50
200
135-175
30
120
UTS 590mpa(N/mm2)
El(l=4d)
38.0%
Ferrite
8.0%
5.0x350
AC/DC(+)
ANAND-D2-M0
Classification :AWSE309Mo-16IS:E23.12.2R26
A medium heavy coated rutile type all position stainless steel electrode,
depositing 23Cr/12 Ni/2.5 Mo type of weld metal. The weld has excellent
resistance to chemical corrosion and oxidation upto 1100° C. The electrode
has good welding characteristics. Suitable for welding clad side of 316 type
cladsteels,316typeofsteelstocarbonsteelsandlowalloysteels.Alsoused
asabufferlayerforweldingdissimilarsteels.
C
Mn
Si
%0.045 1.5
0.45
Cr
Ni
Mo
23.5
13.0
2.4
2
UTS 600mpa(N/mm )
El(l=4d) 38.0%
Ferrite
12.0%
2.5x350
3.15x350
4.0x350
5.0x350
40-60
60-95
95-135
135-175
AC/DC(+)
110
70
50
30
440
280
200
120
2.5x350
3.15x350
4.0x350
5.0x350
40-60
60-95
95-135
135-175
AC/DC(+)
110
70
50
30
440
280
200
120
ANAND - D2 + Cb
Classification :AWSE309Cb-16IS:E23.12NbR26
A medium heavy coated, rutile type, all position stainless steel electrode,
depositing 23 Cr/12 Ni type of weld metal, stabilised with columblum. The
weld metal withstands temperatures upto 1100° C in continous service and
has excellent resistance to chemical corrosion. Recommended for welding
AISl 309, 309 Cb steels and straight chrome steels. For joining stainless
steels to low alloy steels and carbon steels. Suitable for over laying on ferritic
steels.
ANAND - D2-Cb-15 Conforming to AWS E 309-15 can
alsobemanufacturedonrequest.
C
Mn
Si
%0.05
1.75
0.45
Cr
Ni
Cb
23.5
13.0
0.8
UTS 600mpa(N/mm2)
El(l=4d) 38.0%
Ferrite
8.5%
ELECTRODE DETAILS
ANAND ARC
ANAND - CW
Approvedby:BPCL
Classification :AWSE310-16IS:E25.20R26
A rutile coated all position stainless steel electrode with excellent welding
characteristic,manufacturedusing25Cr/20Nitypeofcorewire,depositinga
weld metal of Identical chemistry. The weld metal has excellent resistance to
oxidation and scaling upto 1200° C in continuous service. Weld metal is fully
austentic and is of radiographic quality. Suitable for welding AISI 310 type of
stainless steel, straight chrome steels, clad steels, C-Mo and and Cr-Mo
steels, Also suited for joining dissimilar steels. High temperature furnace
parts,brokendies,non-magneticinsertsinelectricalequipmentetc.
ANAND - CW-15 Conforming to AWS E 310-15 can also be
manufacturedonrequest.
Typical Weld
metal Properties
C
Mn
Si
%0.09
1.9
0.45
Cr
Ni
27.0
21.0
2
UTS 600mpa(N/mm )
El(l=4d)
40.0%
Ferrite
0%
Sizes
(mm)
2.5x350
3.15x350
4.0x350
5.0x350
Current Range
Pieces
Amps
Per Carton
40-60
60-95
95-135
135-175
AC/DC(+)
110
70
50
30
Pieces
Per Box
440
280
200
120
ANAND-CHROM-13
Classification :AWSE410-15
A heavy coated, low hydrogen, stainless steel electrode, depositing 13% Cr.
typeofweldmetal.Theelectrodeoperatesinallpositionsandtheweldmetal
is of radiographic quality. Suited for surfacing of turbine blades, valve seats,
pump parts etc. For welding straight chrome steels and for general corrosion
andheatresistingapplications.
C
Mn
Si
%0.05
0.75
0.35
Cr
Ni
2.5x350
55-75
130
520
3.15x350
75-125
105
420
4.0x350
125-160
65
260
5.0x350
160-220
40
160
C
Mn
Si
0.070% 0.70%
0.35%
Cr
Ni
17.0
0.5
UTS 560mpa(N/mm2)
Z El(l=4d) 40.0%
2.5x350
3.15x350
4.0x350
5.0x350
55-75
75-125
125-160
160-220
130
105
65
40
520
420
260
160
C
Mn
%0.08
5.0
Cr
Ni
19.0
8.5
UTS 600mpa(N/mm2)
El(l=4d)
35.0%
2.5x350
3.15x350
4.0x350
5.0x350
100-120
130-170
180-220
230-280
150
100
60
35
600
400
240
140
13.0
UTS
El(l=4d)
0.4
2
560mpa(N/mm )
40.0%
ANAND - CHROM-17
Classification : AWS E 430-15
A heavy coated, low hydrogen, stainless steel electrode, depositing 17% Cr.
type of weld metal. The electrode can be used be in all positions. The weld
metal has good resistance to corrosion and heat and is of radiographic
quality. Suitable for surfacing and welding of straight chrome steels, such as
AISI430.
ANAND18.8.5(S)
Classification :IS:E:18.8MnR14036
A heavy coated and highly alloyed, mild steel cored electrode producing 18
Cr, 8 Ni, 5 Mn type of austenitic stainless steel deposit. The weld metal has
excellentheatresistantandcrackresistantproperties.Italsohasresistanceto
corrosionfromweakacids,seawaterandatmosphere.Depositionefficiency
is approx. 140%. Recommended for welding austenitic manganese steel,
hardenable steels, armour steels etc. Also recommended for repair of
manganesesteelcastingsandasabufferlayerbeforehardfacing.
Si
0.50
ELECTRODE DETAILS
ANAND ARC
ANAND - 18.8.5
Classification : AWS E 307-15 (Nearest) IS: 18.8 Mn B26
Anand 18.8.5 is a medium coated stainless steel electrode depositing low
hydrogen type o weld metal with 18 Cr, 8 Ni, 5 Mn composition. The weld
metal has excellent crack resistance, corrosion resistance and heat
resistanceupto900° C.Theelectrodeissuitableforpositionalwelding.Highly
recommended for welding dissimilar steels. Armour steels and austenitic
manganesesteels.
Typical Weld
metal Properties
C
Mn
Si
%0.07
5.5
0.35
Cr
Ni
19.0
8.5
UTS 620mpa(N/mm2)
El(l = 4d) 38.0%
Sizes
(mm)
Current Range
Pieces
Amps
Per Carton
110
70
50
30
Pieces
Per Box
2.5x350
3.15x350
4.0x350
5.0x350
50-80
80-110
110-160
160-200
AC/DC(+)
440
280
200
120
2.5x350
3.15x350
4.0x350
5.0x350
55-70
70-110
110-140
140-180
AC/DC(+)
All sizes in 1 Kg
packaging
2.5x350
3.15x350
4.0x350
5.0x350
55-70
70-110
110-140
140-180
AC/DC(+)
All sizes in 1 Kg
packaging
CAST IRON ELECTRODES
ANAND CAST-1
Classification :AWSENiFeCIIS:EMNiFe214
ANAND CAST - 1 is a light coated graphite based electrode, depositing
Ferro-Nickel type of weld metal. The weld metal has good ductility and
adequate strength and is machinable. The electrode is suitable for welding
cast iron without preheat. The deposit is free of defects such as cracks.,
porosityetc.anditgivesgoodcolourmatchwithcastiron.
ANANDCAST-2
Classification :AWSENiCuIS:EMNiCu2/214
ANAND CAST - 2 is a light coated graphite based electrode, depositing
'Monel' type of weld metal. The weld metal is machinable and the electrode
can be used for welding cast iron without preheat and for rectification of
castingdefects.
ANANDCAST-3
Classification :AWSENiClIS:EMNi241
ANANDCAST-3isalightcoatedgraphitebasedelectrode,depositingpure
Nickel type of weld metal. The weld metal has good ductility and is easily
machinable. The electrode is suitable for welding cast iron without preheat
andtheweldmetalisfreefromdefects.
%C
1.3
Ni
5.5
Fe
Bal.
2
UTS 450mpa(N/mm )
Hardness 175 BHN
%C
0.75
Ni
68
Fe
Bal.
UTS 450mpa(N/mm2)
Hardness 170 BHN
%C
1.3
Ni
98
Fe
Bal.
UTS 420mpa(N/mm2)
Hardness 165 BHN
2.5x350
3.15x350
4.0x350
5.0x350
55-70
70-110
110-140
140-180
AC/DC(+)
2.5x350
3.15x350
4.0x350
5.0x350
DC(+)
50-70
70-110
120-160
160-200
All sizes in 1 Kg
packaging
NON FERROUS ELECTRODES
ANAND MONEL
Classification : AWS E NiCu-7
A medium heavy coated, low hydrogen type of electrode depositing 'Monel'
type of weld metal. The metal has good corrosion resistance to sea water,
sulphuricacidandalkalies.IdealforweldingmonelandsimilarNi-Cualloysto
themselvesandtosteels.Alsorecommendedforsurfacingofsteelforservice
inCorrosiveatmosphere.
%C
0.05
Ni
65
Cu
Bal.
Ti
0.5
All sizes in 1 Kg.
packging