Araldite CY 1300 GB 100 pbw Hardener HY 2918 85 pbw

advertisement
Ciba Specialty Chemicals
Performance
Polymers
Electro & Electronic
Encapsulating
®
Araldite Casting Resin System
Araldite
CY 1300 GB
Hardener
HY 2918
Accelerator DY 062
100 pbw
85 pbw
Casting systems for multi purpose processing at
room temperature or slightly higher temperatures.
Curing at high temperatures.
By addition of accelerator DY 062 the casting resin
system may be optimally adjusted to particular
applications
Encapsulating or potting of low voltage and electronic components
Casting, impregnating or vacuum impregnating
Good mechanical and dielectric properties
Good ageing resistance
Edition:
June 1998
Replaces edition: December 1996
Applications
Processing
Properties
Product data
(Guideline values)
Medium viscosity, solvent free epoxy resin
Araldite
CY 1300 GB
Viscosity (Hoeppler)
Specific gravity
Flash point
Epoxy content
at 25°C
at 25°C
DIN 51 758
As supplied form
Hazardous decomposition products
Disposal
mPa s
g/cm³
°C
Eq/kg
13 000
1.16
>200
5.35
Pale yellow to amber liquid
Carbon monoxide, carbon dioxide and
other toxic gases and vapours if burned
Regular procedures approved by national
and/or local authorities
Low viscosity anhydride hardener
Hardener HY 2918
Viscosity (Hoeppler)
Specific gravity
Flash point
at 25°C
at 25°C
DIN 51 758
As supplied form
Hazardous decomposition products
Disposal
mPa s
g/cm³
°C
65
1.2
>140
Clear, pale yellow to yellow liquid
Carbon monoxide, carbon dioxide and
other toxic gases and vapours if burned
Regular procedures approved by national
and/or local authorities
Tertiary amine
Accelerator DY 062 Viscosity (Epprecht TV) at 25°C
Specific gravity
at 25°C
Flash point
As supplied form
Hazardous decomposition products
Disposal
Araldite CY 1300 GB/HY 2918/DY 062
June 1998
DIN 51 758
mPa s
g/cm³
°C
< 10
0.9
59
Colourless or pale yellow liquid
Carbon monoxide, carbon dioxide and
other toxic gases and vapours if burned
Regular procedures approved by national
and/or local authorities
2
Product data
(Guideline values)
Storage
Store the components in a dry place at 18-25°C, in tightly sealed original containers.
Under these conditions, the shelf life will correspond to the expiry date stated on the
label. After this date, the product may be processed only after reanalysis. Partly emptied
containers should be tightly closed immediately after use.
For information on waste disposal and hazardous products of decomposition in the event
of a fire, refer to the Material Safety Data Sheets (MSDS) for these particular products.
Araldite CY 1300 GB/HY 2918/DY 062
June 1998
3
Processing
The resin component should be stirred and homogenized in the original container before
use.
The casting mix is best prepared by heating the resin up to 40-50°C before stirring in the
hardener. Brief degassing of the mix under 5-10 mbar vacuum improves the mixture
homogeneity and enhances the dielectric properties of the castings.
Dosing of accelerator DY 062 can be adapted in betwen 0.5 and 2.5 pbw for 100 bbw of
resin.
Mix ratio
Araldite CY 1300 GB
Hardener HY 2918
Accelerator DY 062
Processing data
(Guideline values)
Initial viscosity (Hoeppler)
Pot life (Hoeppler)
to 1500 mPa s
to 15 000 mPa s
parts by weight
parts by weight
parts by weight
100
85
0.5 - 2.5
at 25°C
at 60°C
mPa s
mPa s
1050
90
at 60°C
at 25°C
h
h
31/4
>50
h/°C
2/80 + 2/120
Minimum curing time
Properties achieved by addition of 1.3 pbw accelerator DY 062 to the resin.
Araldite CY 1300 GB/HY 2918/DY 062
June 1998
4
Properties
Guideline values determined on standard test specimens cured for 2 h/80°C+2 h/120°C
Shore D hardness (4 mm plate)
at 25°C
Glass transition temperature
(DSC, Mettler TA 4000)
DIN 53 505
76
DIN 51 005
°C
123
Tensile strength
max. tensile stress
elongation at break
at 25°C
at 25°C
ISO/R 527
ISO/R 527
MPa
%
61
2
Elastic modulus from tensile test
at 25°C
ISO/R 527
MPa
3637
Water absorption
10 days
30 min
at 23°C
at 100°C
ISO 62
ISO 62
%
%
0.28
0.05
Dielectric constant εr (50 Hz)
at 23°C
at 60°C
at 80°C
at 100°C
DIN 53 483
Dissipation factor tan δ (50 Hz)
at 23°C
at 60°C
at 80°C
at 100°C
DIN 53 483
%
0.1
0.1
0.1
0.3
Volume resistivity ρ
at 23°C
at 60°C
at 80°C
at 100°C
DIN 53 482
Ω⋅cm
3x10
16
2x10
16
1x10
16
1x10
Electrolytic corrosion
DIN 53 489
grade
A-1
Tracking resistance
IEC 112
Electric strength
20 s for 2 mm plate (50 Hz)
Araldite CY 1300 GB/HY 2918/DY 062
at 23°C
June 1998
IEC 243
3.3
3.3
3.3
3.4
16
CTI >600
- 0.2
kV/mm
19
5
Industrial hygiene
Mandatory and recommended industrial hygiene procedures should be followed whenever our products are being handled and processed. For additional information please
consult the corresponding Safety Data Sheets and the brochure "Hygienic precautions for
handling plastics products of Ciba (Publ. No. 24264/e).
Handling
precautions
Safety precautions at workplace:
protective clothing
gloves
arm protectors
goggles/safety glasses
respirator/dust mask
yes
essential
recommended when skin contact likely
yes
recommended
Skin protection
before starting work
after washing
Apply barrier cream to exposed skin
Apply barrier or nourishing cream
Cleaning of contaminated skin
Dab off with absorbent paper, wash with
warm water and alkali-free soap, then dry with
disposable towels. Do not use solvents
Clean shop requirements
Cover workbenches, etc. with light coloured
paper. Use disposable beakers, etc.
Disposal of spillage
Soak up with sawdust or cotton waste and
deposit in plastic-lined bin
Ventilation:
of workshop
of workplace
Renew air 3 to 5 times an hour
Exhaust fans. Operatives should avoid inhaling
vapours.
First Aid
Contamination of the eyes by resin, hardener or casting mix should be treated
immediately by flushing with clean, running water for 10 to 15 minutes. A doctor should
then be consulted.
Material smeared or splashed on the skin should be dabbed off, and the contaminated
area then washed and treated with a cleansing cream (see above). A doctor should be
consulted in the event of severe irritation or burns. Contaminated clothing should be
changed immediately.
Anyone taken ill after inhaling vapours should be moved out of doors immediately. In all
cases of doubt call for medical assistance.
Ciba Specialty
Chemicals Inc.
All recommendations for use of our products, whether given by us in writing, verbally, or
to be implied from results of tests carried out by us are based on the current state of our
knowledge. Notwithstanding any such recommendations the Buyer shall remain
responsible for satisfying himself that the products as supplied by us are suitable for his
intended process or purpose. Since we cannot control the application, use or processing
of the products, we cannot accept responsibility therefore. The Buyer shall ensure that
the intended use of the products will not infringe any third party's intellectual property
rights. We warrant that our products are free from defects in accordance with and subject
to our general conditions of supply.