Synthesis and Characterization of ZnxHg1–xSeyS1–y Quantum Dots

advertisement
Synthesis and Characterization of
ZnxHg1–xSeyS1–y Quantum Dots
Guo-Yu Lan, Yang-Wei Lin, Zong-Hong Lin, and Huan-Tsung Chang*
Department of Chemistry, National Taiwan University, Taipei, Taiwan
Correspondence: Professor Huan-Tsung Chang, Department of Chemistry, National
Taiwan University, 1, Section 4, Roosevelt Road, Taipei 106, Taiwan
Tel and fax: 011-886-2-33661171
E-mail: [email protected]
1
Figure S1.
Histogram show the size distribution of ZnxHg1-xSeyS1-y QDs synthesized
at (a) 25, (b) 50, (c) 65, and (d) 80 oC.
Each counting was 100 nanoparticles.
Other conditions were the same as those described in Figure 3.
2
Figure S2.
A linear relationship of the lattice parameter c of the ZnxHg1–xSeyS1–y
QDs as a function of Zn mole fractions.