Product Data Sheet
OK 63.30
E 'Manual metal-arc welding'
Signed by
Approved by
Reg no
Cancelling
Reg date
Page
Claes Gillenius
Tapio Huhtala/Barbro Karlström
EN003290
EN003085
2006-05-02
1 (2)
REASON FOR ISSUE
Mechanical data and approvals revised. CE approval added, SS, CL and Ü deleted.
GENERAL
Extra low carbon stainless steel electrode for welding steels of the 18Cr 12Ni 2.8Mo-type.
Also suitable for welding of stabilized stainless steels of similar composition, except when the full creep
resistance of the base metal is to be met.
Min AC OCV: 50
Polarity: DC+, AC
Alloy Type: Austenitic CrNiMo
Coating Type: Acid-Rutile
Ferrite Content: FN 3-10
WELDING POSITIONS
CLASSIFICATIONS Electrode
APPROVALS
EN 1600
SFA/AWS A5.4
CSA W48
Werkstoffnummer
ABS
BV
CE
CWB
DB
DNV
GL
LR
Sepros
VdTÜV
E 19 12 3 L R 1 2
E316L-17
E316L-17
1.4430
CHEMICAL COMPOSITION
All Weld Metal (%)
Min
C
Si
Mn
P
S
Cr
Ni
Mo
Cu
0.5
17.0
11.0
2.5
Max
0.030
0.90
1.2
0.025
0.020
19.0
13.0
3.0
0.2
E316L-17
316L
EN 13479
CSA W48
30.039.06
316L
4571
316L
UNA 409820
00262
Product Data Sheet
OK 63.30
E 'Manual metal-arc welding'
Signed by
Approved by
Reg no
Cancelling
Reg date
Page
Claes Gillenius
Tapio Huhtala/Barbro Karlström
EN003290
EN003085
2006-05-02
2 (2)
MECHANICAL PROPERTIES OF WELD METAL
All Weld Metal
ISO
AWS
As welded
Min
Typ
As welded
Min
320
510
460
570
320
510
30
27
40
60
Charpy V at 20°C (J) 47
Charpy V at -20°C (J)
Charpy V at -60°C (J) 32
60
55
43
Properties
Rp0.2 (MPa)
Rm (MPa)
A4 (%)
A5 (%)
Z (%)
Comments:
Interpass temperature maximum 150 °C.
Hardness weld metal 180 - 220 HV.
ECONOMICS & CURRENT DATA
Dimension (mm)
Ø x Length
1.6 x 300
2.0 x 300
2.5 x 300
2.5 x 350
3.2 x 350
4.0 x 350
5.0 x 350
-
-
W
η
N
B
H
T
U
Current (A)
Min
Max
30
45
45
65
45
90
45
80
60
125
70
190
100
280
W
η
N
B
H
T
U
0.7
1.1
1.9
2.2
3.5
5.3
8.3
95
104
100
105
100
100
100
0.56
0.60
0.55
0.56
0.55
0.56
0.56
250
147
96
83
52
34
21
0.4
0.6
0.9
1.1
1.4
2.0
3.0
37
39
45
41
57
57
63
29
29
29
30
30
32
32
= Weight (kg / 100 electrodes)
= Efficiency (g weld metal x 100 / g core wire)
= Effective value (kg weld metal / kg electrodes)
= Changes (number of electrodes / kg weld metal)
= Deposit rate at 90% of max current (kg weld metal / hour arc time)
= Fusion time at 90% of max current (s / electrode)
= Arc voltage (V)
OTHER DATA
Redrying: 350 °C, 2h.