RELY ON EXCELLENCE
Statotherm HT 9560
Packings & Gaskets | Mica gasket sheets
Advantages
Extreme temperature stability
Active expansion behavior when exposed
to high temperatures
Good chemical resistance
•
•
•
Operating range
Pressure: p = 5 bar
Temperature
Continuous operation:
tmax = + 950 °C
•
•
Inert environment:
tmax>1,200 °C
Recommended surface roughness:
RZ = 40 … 60 μm
Features
Statotherm HT 9560 is a gasket made from
particularly heat-resistant natural mica.
The outstanding thermoactive sealing
behavior (from around 600 °C) is achieved
through a specially developed treatment.
The materialʼs expansion ratio actively
counteracts any loss of surface pressure,
which in turn guarantees the tightness and
stability that the gasket needs for sealing
even extreme conditions.
Guaranteed chemical resistance even in
many gaseous media.
Sealing parameters
Thermal conductivity coefficient of sealant
at 400 °C: λ = 0,35 W/mK Compressive
strength for sealant to DIN 52913 (16 hours at
300 °C): 35 ... 40 MPa
Materials
Soft gasket made from mica compound
Tanged insert from 1.4828 or 1.4401
•
•
Notes
The gasket is normally installed between flat
sealing surfaces. Please note that the seal
thickness is set during installation as a result
of the bolt-tightening forces acting on the
flange. The standard thickness of 1.3 mm
when new settles to around 1.05 mm with
surface pressure of 15 MPa at room
temperature. Once this adaption has taken
place, there is no further significant settling
or flow.
Article numbers of variants
9560/2P (with tanged metal reinforcement
(1.4828)
9560/2RIG (with tanged metal reinforcement
(1.4828) and eyeletting (1.4828)
9560/3P (with tanged metal reinforcement
(1.4401)
9560/3RIG ((with tanged metal reinforcement
(1.4401) and eyeletting (1.4571)
Forms of supply
Unreinforced sheets:
1,000 x 1,016 mm
0.4 mm thick
1,500 x 1,000 mm
0.7 / 1.0 mm thick
Sheets with tanged insert
in 1.4828:
1,500 x 1,000 mm
1.3 / 1.7 mm thick
Sheets with tanged insert
in 1.4401:1,200 x 1,000 mm
1.3 / 1.7 / 2.0 mm thick
Rings and molded parts:
Standard dimensions
•
•
•
•
eagleburgmann.com
info@eagleburgmann.com
08.02.2023 © EagleBurgmann
All technical specifications are based on extensive tests and our many years of
experience. The diversity of possible applications, however, means that they can serve
only as guide values.
We must be notified of the exact conditions of application before we can provide any
guarantee for a specific case. This is subject to change.
1
RELY ON EXCELLENCE
as per DIN EN 1514-1 or
ASME B16.21
Gaskets and rings
9560/P: 1,000 x 1,016 mm in thickness 0.4
mm
9560/P: 1,500 x 1,000 mm in thickness 0.7
and 1.0 mm
9560/2P: 1,000 x 500 mm in thickness 1,3 mm
9560/3P: 1,000 x 1,200 mm in thickness 1.3 ;
1.7 and 2.0 mm
Recommended applications
Industries
Aviation and aerospace industry
Power plant technology
Metal production and processing
Blowers
Flange connections
Exhaust ducting
Ovens
Furnaces
•
•
•
•
•
•
•
•
eagleburgmann.com
info@eagleburgmann.com
08.02.2023 © EagleBurgmann
All technical specifications are based on extensive tests and our many years of
experience. The diversity of possible applications, however, means that they can serve
only as guide values.
We must be notified of the exact conditions of application before we can provide any
guarantee for a specific case. This is subject to change.