A N I N T E R N AT I O N A L CO D E 2010 ASME Boiler & Pressure Vessel Code 2011a Addenda July 1, 2011 II Part D Properties (Metric) MATERIALS ASME Boiler and Pressure Vessel Committee on Materials Three Park Avenue • New York, NY • 10016 USA X2DM11 Date of Issuance: July 1, 2011 This international code or standard was developed under procedures accredited as meeting the criteria for American National Standards and it is an American National Standard. The Standards Committee that approved the code or standard was balanced to assure that individuals from competent and concerned interests have had an opportunity to participate. The proposed code or standard was made available for public review and comment that provides an opportunity for additional public input from industry, academia, regulatory agencies, and the public-at-large. ASME does not “approve,” “rate,” or “endorse” any item, construction, proprietary device, or activity. ASME does not take any position with respect to the validity of any patent rights asserted in connection with any items mentioned in this document, and does not undertake to insure anyone utilizing a standard against liability for infringement of any applicable letters patent, nor assume any such liability. Users of a code or standard are expressly advised that determination of the validity of any such patent rights, and the risk of infringement of such rights, is entirely their own responsibility. Participation by federal agency representative(s) or person(s) affiliated with industry is not to be interpreted as government or industry endorsement of this code or standard. ASME accepts responsibility for only those interpretations of this document issued in accordance with the established ASME procedures and policies, which precludes the issuance of interpretations by individuals. The footnotes in this document are part of this American National Standard. No part of this document may be reproduced in any form, in an electronic retrieval system or otherwise, without the prior written permission of the publisher. Library of Congress Catalog Card Number: 56-3934 Printed in the United States of America The American Society of Mechanical Engineers Three Park Avenue, New York, NY 10016-5990 Copyright © 2011 by THE AMERICAN SOCIETY OF MECHANICAL ENGINEERS All rights reserved CONTENTS List of Sections . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Foreword . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Statement of Policy on the Use of the Certification Mark and Code Authorization in Advertising . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Statement of Policy on the Use of ASME Marking to Identify Manufactured Items . . . . . . . . . . . . Submittal of Technical Inquiries to the Boiler and Pressure Vessel Committee — Mandatory . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Personnel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Summary of Changes . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . List of Changes in Record Number Order . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . SUBPART 1 1A 1B 2A 2B 3 4 5A 5B U U-2 Y-1 Y-2 SUBPART 2 TE-1 TE-2 TE-3 TE-4 TE-5 STRESS TABLES . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Statement of Policy on Information Provided in the Stress Tables . . . . . . . . . . . . . . . . Guideline on Locating Materials in Stress Tables, and in Tables of Mechanical and Physical Properties . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Section I; Section III, Classes 2 and 3; Section VIII, Division 1; and Section XII Maximum Allowable Stress Values S for Ferrous Materials. . . . . . . . . . . . . . . . Section I; Section III, Classes 2 and 3; Section VIII, Division 1; and Section XII Maximum Allowable Stress Values S for Nonferrous Materials. . . . . . . . . . . . . Section III, Division 1, Classes 1 and MC, and Section III, Division 3, Classes TC and SC Design Stress Intensity Values Sm for Ferrous Materials . . . . . . . . . . . . Section III, Division 1, Class 1 and Section III, Division 3, Classes TC and SC Design Stress Intensity Values Sm for Nonferrous Materials . . . . . . . . . . . . . . . . Section III, Classes 2 and 3; Section VIII, Divisions 1 and 2; and Section XII Maximum Allowable Stress Values S for Bolting Materials . . . . . . . . . . . . . . . . . . . . Section III, Classes 1, TC, and SC; and Section VIII, Division 2 Design Stress Intensity Values Sm for Bolting Materials . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Section VIII, Division 2 Maximum Allowable Stress Values Sm for Ferrous Materials . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Section VIII, Division 2 Maximum Allowable Stress Values Sm for Nonferrous Materials . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Tensile Strength Values Su for Ferrous and Nonferrous Materials . . . . . . . . . . . . . . . . . Section VIII, Division 3 Tensile Strength Values Su for Ferrous Materials . . . . . . . . . Yield Strength Values Sy for Ferrous and Nonferrous Materials . . . . . . . . . . . . . . . . . . Factors for Limiting Permanent Strain in Nickel, High Nickel Alloys, and High Alloy Steels . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . PHYSICAL PROPERTIES TABLES . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Introduction . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Thermal Expansion for Ferrous Materials . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Thermal Expansion for Aluminum Alloys . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Thermal Expansion for Copper Alloys . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Thermal Expansion for Nickel Alloys . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Thermal Expansion for Titanium Alloys . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . iii viii x xii xii xiii xv xxviii xxxi 1 1 2 6 150 268 326 334 364 376 434 460 535 536 705 707 707 708 714 715 716 725 TCD TM-1 TM-2 TM-3 TM-4 TM-5 PRD SUBPART 3 Figures G CS-1 CS-2 CS-3 CS-4 CS-5 CS-6 HT-1 HT-2 HA-1 HA-2 HA-3 HA-4 HA-5 HA-6 HA-7 HA-8 CI-1 CD-1 NFA-1 NFA-2 NFA-3 NFA-4 NFA-5 NFA-6 NFA-7 NFA-8 NFA-9 NFA-10 NFA-11 NFA-12 NFA-13 NFC-1 Nominal Coefficients of Thermal Conductivity (TC) and Thermal Diffusivity (TD). . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Moduli of Elasticity E of Ferrous Materials for Given Temperatures. . . . . . . . . . . . . . Moduli of Elasticity E of Aluminum and Aluminum Alloys for Given Temperatures . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Moduli of Elasticity E of Copper and Copper Alloys for Given Temperatures . . . . . Moduli of Elasticity E of High Nickel Alloys for Given Temperatures . . . . . . . . . . . . Moduli of Elasticity E of Titanium and Zirconium for Given Temperatures . . . . . . . Poisson’s Ratio and Density of Materials . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 726 738 740 741 742 743 744 CHARTS AND TABLES FOR DETERMINING SHELL THICKNESS OF COMPONENTS UNDER EXTERNAL PRESSURE. . . . . . . . . . . . . . . . . . . . 747 Geometric Chart for Components Under External or Compressive Loadings (for All Materials) . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Carbon or Low Alloy Steels With Specified Minimum Yield Strength Less Than 207 MPa . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Carbon or Low Alloy Steels With Specified Minimum Yield Strength 207 MPa and Higher . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Carbon Steel and Low Alloy Steels With Specified Minimum Yield Strength 260 MPa and Higher for Temperatures 150°C and Less . . . . . . . . . . . . . . . . . . . . . . . SA-537 Thickness 64 mm and Less . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . SA-508 Class 1, Grades 2 and 3; SA-508 Class 2, Grade 2; SA-533 Class 1, Grades A, B, C, and D; SA-533 Class 2, Grades A, B, C, and D; or SA-541 Grades 2 and 3. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Carbon Steel With Specified Minimum Yield Strength of 138 MPa. . . . . . . . . . . . . . . Quenched and Tempered Low Alloy Steel With Specified Minimum Yield Strength of 689 MPa and Thickness 64 mm and Less . . . . . . . . . . . . . . . . . . . . . . . . . SA-508 Grade 4N, Class 2 or SA-543 Types B and C, Class 2 With Specified Minimum Yield Strength of 689 MPa . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Austenitic Steel 18Cr–8Ni, Type 304 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Austenitic Steel 16Cr–12Ni–2Mo, Type 316 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Austenitic Steel 18Cr–8Ni–0.035 Maximum Carbon, Type 304L . . . . . . . . . . . . . . . . . Austenitic Steel 18Cr–8Ni–Mo–0.035 Maximum Carbon, Type 316L . . . . . . . . . . . . . Austenitic–Ferritic Steel 18Cr–5Ni–3Mo S31500 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Austenitic Steel 21Cr–11Ni–N S30815 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . SA-564 Type 630 H1150 (17Cr–4Ni–4Cu S17400) . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Austenitic–Ferritic Steel 25Cr–7Ni–3Mo–2W–0.28N S39274 . . . . . . . . . . . . . . . . . . . . Cast Iron . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Cast Ductile Iron With a Specified Minimum Yield Strength of 275 MPa . . . . . . . . . Aluminum Alloy 3003 in O Temper. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Aluminum Alloy 3003 in H14 Temper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Aluminum Alloy 3004 in O Temper. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Aluminum Alloy 3004 in H34 Temper . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Aluminum Alloy 5154 in O Temper. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Aluminum Alloy 5454 in O Temper. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Aluminum Alloy 1060 in O Temper. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Aluminum Alloy 5052 in O Temper. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Aluminum Alloy 5086 in O Temper. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Aluminum Alloy 5456 in O Temper. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Aluminum Alloy 5083 in O Temper. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Welded Aluminum Alloy 6061-T6 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Welded Aluminum Alloy 6061-T4 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Annealed Copper, Type DHP . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . iv 748 750 750 751 751 752 752 753 753 754 754 755 755 756 756 757 758 758 759 759 760 761 762 763 763 764 764 765 765 766 766 767 767 NFC-2 NFC-3 NFC-4 NFC-5 NFC-6 NFN-22 NFN-23 NFN-24 NFN-25 NFN-26 NFN-27 NFT-1 NFT-2 NFT-3 NFT-4 NFT-5 NFZ-1 NFZ-2 Copper–Silicon Alloys A and C. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Annealed 90–10 Copper–Nickel Alloy . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Annealed 70–30 Copper–Nickel Alloy . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Welded Copper–Iron Alloy Tube C19400 (SB-543 Welded) . . . . . . . . . . . . . . . . . . . . . SB-75 and SB-111 Light Drawn Seamless Copper Tubes, Alloys C10200, C12000, C12200, and C14200 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Annealed Copper, SB-75, UNS C12200, Temper O50. . . . . . . . . . . . . . . . . . . . . . . . . . . Aluminum Bronze Alloy C61400 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Annealed Low Carbon Nickel N02201. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Annealed Nickel N02200. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Annealed Nickel–Copper Alloy N04400 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Annealed Nickel–Chromium–Iron Alloy N06600 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Nickel–Molybdenum Alloy N10001 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Nickel–Molybdenum–Chromium–Iron Alloy N10003 . . . . . . . . . . . . . . . . . . . . . . . . . . . Nickel–Iron–Chromium–Molybdenum–Copper Alloy N08825 . . . . . . . . . . . . . . . . . . . . Annealed Nickel–Iron–Chromium Alloy N08800 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Annealed Nickel–Iron–Chromium Alloy N08810 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Low Carbon Nickel–Molybdenum–Chromium Alloy N10276 . . . . . . . . . . . . . . . . . . . . Solution Treated Nickel–Chromium–Iron–Molybdenum–Copper Alloy N06007 . . . . Chromium–Nickel–Iron–Molybdenum–Copper–Columbium Alloy N08020 . . . . . . . . Nickel–Iron–Chromium–Silicon Alloy N08330 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Nickel–Chromium–Molybdenum Alloy N06455 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Nickel–Molybdenum Alloy N06002 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Nickel–Molybdenum Alloy N10665 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Annealed Nickel–Chromium–Molybdenum–Columbium Alloy N06625 (SB-443, SB-444, and SB-446) . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Nickel–Molybdenum–Chromium–Iron–Copper Alloy N06985 Having a Minimum Yield Strength of 240 MPa . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Nickel–Molybdenum–Chromium–Iron–Copper Alloy N06985 Having a Minimum Yield Strength of 207 MPa . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Work-Hardened Nickel. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Nickel–Chromium–Iron Alloy N06600 (Specified Minimum Yield Strength 276 MPa). . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Solution Annealed Ni–Cr–Mo–Cb Alloy, Grade 2 N06625. . . . . . . . . . . . . . . . . . . . . . . Cold Worked Nickel–Iron–Chromium Alloy N08800. . . . . . . . . . . . . . . . . . . . . . . . . . . . Nickel Alloy N06230 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Stress Relieved Nickel Alloy N02200 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Alloy S31277 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Alloy N06035 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Unalloyed Titanium Grade 3 (UNS R50550) . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Unalloyed Titanium Grade 2 (UNS R50400) . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Titanium Grade 1 (UNS R50250) . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Titanium Grade 9 Alloy (UNS R56320) . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Titanium Grade 12 Alloy (UNS R53400) . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Zirconium Alloy (UNS R60702) . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Zirconium Alloy (UNS R60705) . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Tables G CS-1 CS-2 CS-3 CS-4 CS-5 Tabular Tabular Tabular Tabular Tabular Tabular NFC-7 NFC-8 NFN-1 NFN-2 NFN-3 NFN-4 NFN-5 NFN-6 NFN-7 NFN-8 NFN-9 NFN-10 NFN-11 NFN-12 NFN-13 NFN-14 NFN-15 NFN-16 NFN-17 NFN-18 NFN-19 NFN-20 NFN-21 Values Values Values Values Values Values for for for for for for Fig. Fig. Fig. Fig. Fig. Fig. G .................................................... CS-1 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . CS-2 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . CS-3 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . CS-4 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . CS-5 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . v 768 768 769 769 770 770 771 771 772 772 773 773 774 774 775 775 776 776 777 777 778 778 779 779 780 780 781 781 782 782 783 783 784 784 785 786 786 787 787 788 789 791 793 794 794 795 795 CS-6 HT-1 HT-2 HA-1 HA-2 HA-3 HA-4 HA-5 HA-6 HA-7 HA-8 CI-1 CD-1 NFA-1 NFA-2 NFA-3 NFA-4 NFA-5 NFA-6 NFA-7 NFA-8 NFA-9 NFA-10 NFA-11 NFA-12 NFA-13 NFC-1 NFC-2 NFC-3 NFC-4 NFC-5 NFC-6 NFC-7 NFC-8 NFN-1 NFN-2 NFN-3 NFN-4 NFN-5 NFN-6 NFN-7 NFN-8 NFN-9 NFN-10 NFN-11 NFN-12 NFN-13 NFN-14 NFN-15 NFN-16 NFN-17 NFN-18 NFN-19 NFN-20 Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values Values for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for for Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. CS-6 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . HT-1 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . HT-2 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . HA-1. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . HA-2. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . HA-3. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . HA-4. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . HA-5. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . HA-6. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . HA-7. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . HA-8. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . CI-1. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . CD-1 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFA-1 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFA-2 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFA-3 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFA-4 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFA-5 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFA-6 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFA-7 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFA-8 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFA-9 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFA-10 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFA-11 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFA-12 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFA-13 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFC-1. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFC-2. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFC-3. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFC-4. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFC-5. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFC-6. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFC-7. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFC-8. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-1 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-2 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-3 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-4 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-5 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-6 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-7 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-8 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-9 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-10 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-11 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-12 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-13 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-14 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-15 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-16 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-17 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-18 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-19 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-20 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . vi 796 796 796 797 798 798 799 799 800 801 801 802 802 803 804 805 806 806 807 807 808 808 808 809 810 810 811 811 811 812 812 813 813 814 814 815 816 817 817 818 818 819 820 821 821 822 822 823 824 825 826 827 828 829 NFN-22 NFN-23 NFN-24 NFN-25 NFN-26 NFN-27 NFT-1 NFT-2 NFT-3 NFT-4 NFT-5 NFZ-1 NFZ-2 Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Tabular Values Values Values Values Values Values Values Values Values Values Values Values Values for for for for for for for for for for for for for Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. Fig. NFN-22 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-23 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-24 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-25 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-26 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFN-27 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFT-1. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFT-2. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFT-3. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFT-4 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFT-5. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFZ-1. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . NFZ-2. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 829 830 831 832 832 833 834 835 835 836 837 838 838 Basis for Establishing Stress Values in Tables 1A and 1B . . . . . . . . . . . . . . . . . . . . . . . Basis for Establishing Design Stress Intensity Values for Tables 2A, 2B, and 4, and Allowable Stress Values for Table 3 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Basis for Establishing External Pressure Charts . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Submittal of Technical Inquiries to the Boiler and Pressure Vessel Committee. . . . . Guideline on the Approval of New Materials Under the ASME Boiler and Pressure Vessel Code . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Guidelines on Multiple Marking of Materials. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Standard Units for Use in Equations. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Basis for Establishing Maximum Allowable Stress Values for Tables 5A and 5B . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 839 MANDATORY APPENDICES 1 2 3 4 5 7 9 10 842 845 850 851 855 857 858 NONMANDATORY APPENDICES A C Metallurgical Phenomena. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 860 Guidance for the Use of U.S. Customary and SI Units in the ASME Boiler and Pressure Vessel Code . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 868 vii 2010 ASME BOILER AND PRESSURE VESSEL CODE (10) SECTIONS I Rules for Construction of Power Boilers II Materials Part A — Ferrous Material Specifications Part B — Nonferrous Material Specifications Part C — Specifications for Welding Rods, Electrodes, and Filler Metals Part D — Properties (Customary) Part D — Properties (Metric) III Rules for Construction of Nuclear Facility Components Subsection NCA — General Requirements for Division 1 and Division 2 Division 1 Subsection NB — Class 1 Components Subsection NC — Class 2 Components Subsection ND — Class 3 Components Subsection NE — Class MC Components Subsection NF — Supports Subsection NG — Core Support Structures Subsection NH — Class 1 Components in Elevated Temperature Service Appendices Division 2 — Code for Concrete Containments Division 3 — Containments for Transportation and Storage of Spent Nuclear Fuel and High Level Radioactive Material and Waste IV Rules for Construction of Heating Boilers V Nondestructive Examination VI Recommended Rules for the Care and Operation of Heating Boilers VII Recommended Guidelines for the Care of Power Boilers VIII Rules for Construction of Pressure Vessels Division 1 Division 2 — Alternative Rules Division 3 — Alternative Rules for Construction of High Pressure Vessels IX Welding and Brazing Qualifications X Fiber-Reinforced Plastic Pressure Vessels XI Rules for Inservice Inspection of Nuclear Power Plant Components XII Rules for Construction and Continued Service of Transport Tanks viii ADDENDA and 2, will be included with the update service to Subsection NCA. Interpretations of the Code are posted in January and July at http://cstools.asme.org/interpretations.cfm. Addenda, which include additions and revisions to individual Sections of the Code, will be sent automatically to purchasers of the applicable Sections up to the publication of the 2013 Code. The 2010 Code is available only in the loose-leaf format; accordingly, the Addenda will be issued in the loose-leaf format. CODE CASES The Boiler and Pressure Vessel Committee meets regularly to consider proposed additions and revisions to the Code and to formulate Cases to clarify the intent of existing requirements or provide, when the need is urgent, rules for materials or constructions not covered by existing Code rules. Those Cases that have been adopted will appear in the appropriate 2010 Code Cases book: “Boilers and Pressure Vessels” and “Nuclear Components.” Supplements will be sent automatically to the purchasers of the Code Cases books up to the publication of the 2013 Code. INTERPRETATIONS ASME issues written replies to inquiries concerning interpretation of technical aspects of the Code. The Interpretations for each individual Section will be published separately and will be included as part of the update service to that Section. Interpretations of Section III, Divisions 1 ix (10) (a) FOREWORD The American Society of Mechanical Engineers set up a committee in 1911 for the purpose of formulating standard rules for the construction of steam boilers and other pressure vessels. This committee is now called the Boiler and Pressure Vessel Committee. The Committee’s function is to establish rules of safety, relating only to pressure integrity, governing the construction 1 of boilers, pressure vessels, transport tanks and nuclear components, and inservice inspection for pressure integrity of nuclear components and transport tanks, and to interpret these rules when questions arise regarding their intent. This Code does not address other safety issues relating to the construction of boilers, pressure vessels, transport tanks and nuclear components, and the inservice inspection of nuclear components and transport tanks. The user of the Code should refer to other pertinent codes, standards, laws, regulations, or other relevant documents. With few exceptions, the rules do not, of practical necessity, reflect the likelihood and consequences of deterioration in service related to specific service fluids or external operating environments. Recognizing this, the Committee has approved a wide variety of construction rules in this Section to allow the user or his designee to select those which will provide a pressure vessel having a margin for deterioration in service so as to give a reasonably long, safe period of usefulness. Accordingly, it is not intended that this Section be used as a design handbook; rather, engineering judgment must be employed in the selection of those sets of Code rules suitable to any specific service or need. This Code contains mandatory requirements, specific prohibitions, and nonmandatory guidance for construction activities. The Code does not address all aspects of these activities and those aspects that are not specifically addressed should not be considered prohibited. The Code is not a handbook and cannot replace education, experience, and the use of engineering judgment. The phrase engineering judgment refers to technical judgments made by knowledgeable designers experienced in the application of the Code. Engineering judgments must be consistent with Code philosophy and such judgments must never be used to overrule mandatory requirements or specific prohibitions of the Code. The Committee recognizes that tools and techniques used for design and analysis change as technology progresses and expects engineers to use good judgment in the application of these tools. The designer is responsible for complying with Code rules and demonstrating compliance with Code equations when such equations are mandatory. The Code neither requires nor prohibits the use of computers for the design or analysis of components constructed to the requirements of the Code. However, designers and engineers using computer programs for design or analysis are cautioned that they are responsible for all technical assumptions inherent in the programs they use and they are responsible for the application of these programs to their design. The Code does not fully address tolerances. When dimensions, sizes, or other parameters are not specified with tolerances, the values of these parameters are considered nominal and allowable tolerances or local variances may be considered acceptable when based on engineering judgment and standard practices as determined by the designer. The Boiler and Pressure Vessel Committee deals with the care and inspection of boilers and pressure vessels in service only to the extent of providing suggested rules of good practice as an aid to owners and their inspectors. The rules established by the Committee are not to be interpreted as approving, recommending, or endorsing any proprietary or specific design or as limiting in any way the manufacturer’s freedom to choose any method of design or any form of construction that conforms to the Code rules. The Boiler and Pressure Vessel Committee meets regularly to consider revisions of the rules, new rules as dictated by technological development, Code Cases, and requests for interpretations. Only the Boiler and Pressure Vessel Committee has the authority to provide official interpretations of this Code. Requests for revisions, new rules, Code Cases, or interpretations shall be addressed to the Secretary in writing and shall give full particulars in order to receive consideration and action (see Submittal of Technical Inquiries to the Boiler and Pressure Vessel Committee). Proposed revisions to the Code resulting from inquiries will be presented to the Standards Committees for appropriate action. The action of the Standards Committees becomes effective only after confirmation by letter ballot of the Committees and approval by ASME. 1 Construction, as used in this Foreword, is an all-inclusive term comprising materials, design, fabrication, examination, inspection, testing, certification, and pressure relief. x Proposed revisions to the Code approved by the Committee are submitted to the American National Standards Institute and published at http://cstools. asme.org/csconnect/public/index.cfm?PublicReviewp Revisions to invite comments from all interested persons. After the allotted time for public review and final approval by ASME, revisions are published in updates to the Code. Code Cases may be used in the construction of components to be stamped with the Certification Mark beginning with the date of their approval by ASME. After Code revisions are approved by ASME, they may be used beginning with the date of issuance. Revisions, except for revisions to material specifications in Section II, Parts A and B, become mandatory six months after such date of issuance, except for boilers or pressure vessels contracted for prior to the end of the six-month period. Revisions to material specifications are originated by the American Society for Testing and Materials (ASTM) and other recognized national or international organizations, and are usually adopted by ASME. However, those revisions may or may not have any effect on the suitability of material, produced to earlier editions of specifications, for use in ASME construction. ASME material specifications approved for use in each construction Code are listed in the Guideline for Acceptable ASTM Editions and in the Guideline for Acceptable Non-ASTM Editions, in Section II, Parts A and B. These Guidelines list, for each specification, the latest edition adopted by ASME, and earlier and later editions considered by ASME to be identical for ASME construction. The Boiler and Pressure Vessel Committee in the formulation of its rules and in the establishment of maximum design and operating pressures considers materials, construction, method of fabrication, inspection, and safety devices. The Code Committee does not rule on whether a component shall or shall not be constructed to the provisions of the Code. The Scope of each Section has been established to identify the components and parameters considered by the Committee in formulating the Code rules. Questions or issues regarding compliance of a specific component with the Code rules are to be directed to the ASME Certificate Holder (Manufacturer). Inquiries concerning the interpretation of the Code are to be directed to the ASME Boiler and Pressure Vessel Committee. ASME is to be notified should questions arise concerning improper use of the Certification Mark. The specifications for materials given in Section II are identical with or similar to those of specifications published by ASTM, AWS, and other recognized national or international organizations. When reference is made in an ASME material specification to a non-ASME specification for which a companion ASME specification exists, the reference shall be interpreted as applying to the ASME material specification. Not all materials included in the material specifications in Section II have been adopted for Code use. Usage is limited to those materials and grades adopted by at least one of the other Sections of the Code for application under rules of that Section. All materials allowed by these various Sections and used for construction within the scope of their rules shall be furnished in accordance with material specifications contained in Section II or referenced in the Guidelines for Acceptable Editions in Section II, Parts A and B, except where otherwise provided in Code Cases or in the applicable Section of the Code. Materials covered by these specifications are acceptable for use in items covered by the Code Sections only to the degree indicated in the applicable Section. Materials for Code use should preferably be ordered, produced, and documented on this basis; Guidelines for Acceptable Editions in Section II, Parts A and B list editions of ASME and year dates of specifications that meet ASME requirements and which may be used in Code construction. Material produced to an acceptable specification with requirements different from the requirements of the corresponding specifications listed in the Guidelines for Acceptable Editions in Part A or Part B may also be used in accordance with the above, provided the material manufacturer or vessel manufacturer certifies with evidence acceptable to the Authorized Inspector that the corresponding requirements of specifications listed in the Guidelines for Acceptable Editions in Part A or Part B have been met. Material produced to an acceptable material specification is not limited as to country of origin. When required by context in this Section, the singular shall be interpreted as the plural, and vice-versa; and the feminine, masculine, or neuter gender shall be treated as such other gender as appropriate. xi (10) (a) STATEMENT OF POLICY ON THE USE OF THE CERTIFICATION MARK AND CODE AUTHORIZATION IN ADVERTISING ASME has established procedures to authorize qualified organizations to perform various activities in accordance with the requirements of the ASME Boiler and Pressure Vessel Code. It is the aim of the Society to provide recognition of organizations so authorized. An organization holding authorization to perform various activities in accordance with the requirements of the Code may state this capability in its advertising literature. Organizations that are authorized to use the Certification Mark for marking items or constructions that have been constructed and inspected in compliance with the ASME Boiler and Pressure Vessel Code are issued Certificates of Authorization. It is the aim of the Society to maintain the standing of the Certification Mark for the benefit of the users, the enforcement jurisdictions, and the holders of the Certification Mark who comply with all requirements. Based on these objectives, the following policy has been established on the usage in advertising of facsimiles of the Certification Mark, Certificates of Authorization, and reference to Code construction. The American Society of (a) Mechanical Engineers does not “approve,” “certify,” “rate,” or “endorse” any item, construction, or activity and there shall be no statements or implications that might so indicate. An organization holding the Certification Mark and/or a Certificate of Authorization may state in advertising literature that items, constructions, or activities “are built (produced or performed) or activities conducted in accordance with the requirements of the ASME Boiler and Pressure Vessel Code,” or “meet the requirements of the ASME Boiler and Pressure Vessel Code.” An ASME corporate logo shall not be used by any organization other than ASME. The Certification Mark shall be used only for stamping and nameplates as specifically provided in the Code. However, facsimiles may be used for the purpose of fostering the use of such construction. Such usage may be by an association or a society, or by a holder of the Certification Mark who may also use the facsimile in advertising to show that clearly specified items will carry the Certification Mark. General usage is permitted only when all of a manufacturer’s items are constructed under the rules. STATEMENT OF POLICY ON THE USE OF ASME MARKING TO IDENTIFY MANUFACTURED ITEMS The ASME Boiler and Pressure Vessel Code provides rules for the construction of boilers, pressure vessels, and nuclear components. This includes requirements for materials, design, fabrication, examination, inspection, and stamping. Items constructed in accordance with all of the applicable rules of the Code are identified with the official Certification Mark described in the governing Section of the Code. Markings such as “ASME,” “ASME Standard,” or any other marking including “ASME” or the Certification Mark shall not be used on any item that is not constructed in accordance with all of the applicable requirements of the Code. Items shall not be described on ASME Data Report Forms nor on similar forms referring to ASME that tend to imply that all Code requirements have been met when, in fact, they have not been. Data Report Forms covering items not fully complying with ASME requirements should not refer to ASME or they should clearly identify all exceptions to the ASME requirements. xii SUBMITTAL OF TECHNICAL INQUIRIES TO THE BOILER AND PRESSURE VESSEL COMMITTEE — MANDATORY 1 the freedom of manufacturers, constructors, or owners to choose any method of design or any form of construction that conforms to the Code rules. (c) Inquiries that do not comply with these provisions or that do not provide sufficient information for the Committee’s full understanding may result in the request being returned to the inquirer with no action. INTRODUCTION (a) The following information provides guidance to Code users for submitting technical inquiries to the Committee. See Guideline on the Approval of New Materials Under the ASME Boiler and Pressure Vessel Code in Section II, Parts C and D for additional requirements for requests involving adding new materials to the Code. Technical inquiries include requests for revisions or additions to the Code rules, requests for Code Cases, and requests for Code interpretations, as described below. (1) Code Revisions. Code revisions are considered to accommodate technological developments, address administrative requirements, incorporate Code Cases, or to clarify Code intent. (2) Code Cases. Code Cases represent alternatives or additions to existing Code rules. Code Cases are written as a question and reply, and are usually intended to be incorporated into the Code at a later date. When used, Code Cases prescribe mandatory requirements in the same sense as the text of the Code. However, users are cautioned that not all jurisdictions or owners automatically accept Code Cases. The most common applications for Code Cases are: (a) to permit early implementation of an approved Code revision based on an urgent need (b) to permit the use of a new material for Code construction (c) to gain experience with new materials or alternative rules prior to incorporation directly into the Code (3) Code Interpretations. Code Interpretations provide clarification of the meaning of existing rules in the Code, and are also presented in question and reply format. Interpretations do not introduce new requirements. In cases where existing Code text does not fully convey the meaning that was intended, and revision of the rules is required to support an interpretation, an Intent Interpretation will be issued and the Code will be revised. (b) The Code rules, Code Cases, and Code Interpretations established by the Committee are not to be considered as approving, recommending, certifying, or endorsing any proprietary or specific design, or as limiting in any way 2 INQUIRY FORMAT Submittals to the Committee shall include: (a) Purpose. Specify one of the following: (1) revision of present Code rules (2) new or additional Code rules (3) Code Case (4) Code Interpretation (b) Background. Provide the information needed for the Committee’s understanding of the inquiry, being sure to include reference to the applicable Code Section, Division, Edition, Addenda (if applicable), paragraphs, figures, and tables. Preferably, provide a copy of the specific referenced portions of the Code. (c) Presentations. The inquirer may desire or be asked to attend a meeting of the Committee to make a formal presentation or to answer questions from the Committee members with regard to the inquiry. Attendance at a Committee meeting shall be at the expense of the inquirer. The inquirer’s attendance or lack of attendance at a meeting shall not be a basis for acceptance or rejection of the inquiry by the Committee. 3 CODE REVISIONS OR ADDITIONS Requests for Code revisions or additions shall provide the following: (a) Proposed Revisions or Additions. For revisions, identify the rules of the Code that require revision and submit a copy of the appropriate rules as they appear in the Code, marked up with the proposed revision. For additions, provide the recommended wording referenced to the existing Code rules. xiii (a) (b) Statement of Need. Provide a brief explanation of the need for the revision or addition. (c) Background Information. Provide background information to support the revision or addition, including any data or changes in technology that form the basis for the request that will allow the Committee to adequately evaluate the proposed revision or addition. Sketches, tables, figures, and graphs should be submitted as appropriate. When applicable, identify any pertinent paragraph in the Code that would be affected by the revision or addition and identify paragraphs in the Code that reference the paragraphs that are to be revised or added. 4 Reply should be “yes” or “no,” with brief provisos if needed. (3) Background Information. Provide any background information that will assist the Committee in understanding the proposed Inquiry and Reply. (b) Requests for Code Interpretations must be limited to an interpretation of a particular requirement in the Code or a Code Case. The Committee cannot consider consulting type requests such as the following: (1) a review of calculations, design drawings, welding qualifications, or descriptions of equipment or parts to determine compliance with Code requirements; (2) a request for assistance in performing any Codeprescribed functions relating to, but not limited to, material selection, designs, calculations, fabrication, inspection, pressure testing, or installation; (3) a request seeking the rationale for Code requirements. CODE CASES Requests for Code Cases shall provide a Statement of Need and Background Information similar to that defined in 3(b) and 3(c), respectively, for Code revisions or additions. The urgency of the Code Case (e.g., project underway or imminent, new procedure, etc.) must be defined and it must be confirmed that the request is in connection with equipment that will bear the Certification Mark, with the exception of Section XI applications. The proposed Code Case should identify the Code Section and Division, and be written as a Question and a Reply in the same format as existing Code Cases. Requests for Code Cases should also indicate the applicable Code Editions and Addenda (if applicable) to which the proposed Code Case applies. 5 6 SUBMITTALS Submittals to and responses from the Committee shall meet the following: (a) Submittal. Inquiries from Code users shall be in English and preferably be submitted in typewritten form; however, legible handwritten inquiries will also be considered. They shall include the name, address, telephone number, fax number, and e-mail address, if available, of the inquirer and be mailed to the following address: Secretary ASME Boiler and Pressure Vessel Committee Three Park Avenue New York, NY 10016-5990 As an alternative, inquiries may be submitted via e-mail to: SecretaryBPV@asme.org. (b) Response. The Secretary of the ASME Boiler and Pressure Vessel Committee or of the appropriate Subcommittee shall acknowledge receipt of each properly prepared inquiry and shall provide a written response to the inquirer upon completion of the requested action by the Code Committee. CODE INTERPRETATIONS (a) Requests for Code Interpretations shall provide the following: (1) Inquiry. Provide a condensed and precise question, omitting superfluous background information and, when possible, composed in such a way that a “yes” or a “no” Reply, with brief provisos if needed, is acceptable. The question should be technically and editorially correct. (2) Reply. Provide a proposed Reply that will clearly and concisely answer the Inquiry question. Preferably, the xiv PERSONNEL ASME Boiler and Pressure Vessel Standards Committees, Subgroups, and Working Groups As of January 1, 2011 TECHNICAL OVERSIGHT MANAGEMENT COMMITTEE (TOMC) J. G. Feldstein, Chair T. P. Pastor, Vice Chair J. S. Brzuszkiewicz, Staff Secretary R. W. Barnes R. J. Basile J. E. Batey T. L. Bedeaux D. L. Berger M. N. Bressler D. A. Canonico A. Chaudouet R. P. Deubler D. A. Douin D. Eisberg R. E. Gimple M. Gold CONFERENCE COMMITTEE T. E. Hansen J. F. Henry C. L. Hoffmann G. G. Karcher W. M. Lundy J. R. MacKay U. R. Miller W. E. Norris G. C. Park M. D. Rana B. W. Roberts S. C. Roberts F. J. Schaaf, Jr. A. Selz B. F. Shelley W. J. Sperko R. W. Swayne J. M. Given, Jr. — North Carolina (Chair) J. T. Amato — Minnesota (Vice Chair) D. A. Douin — Ohio (Secretary) B. P. Anthony — Rhode Island R. D. Austin — Arizona B. F. Bailey — Illinois J. E. Bell — Michigan W. K. Brigham — New Hampshire C. W. Bryan — Tennessee M. A. Burns — Florida J. H. Burpee — Maine C. B. Cantrell — Nebraska D. C. Cook — California E. L. Creaser — New Brunswick, Canada W. E. Crider, Jr. — Vermont P. L. Dodge — Nova Scotia, Canada S. Donovan — Northwest Territories, Canada D. Eastman — Newfoundland and Labrador, Canada C. Fulton — Alaska M. Graham — Oregon R. J. Handy — Kentucky D. R. Hannon — Arkansas E. G. Hilton — Virginia K. Hynes — Prince Edward Island, Canada D. T. Jagger — Ohio D. J. Jenkins — Kansas E. S. Kawa, Jr. — Massachusetts HONORARY MEMBERS (MAIN COMMITTEE) F. P. Barton L. J. Chockie T. M. Cullen W. D. Doty J. R. Farr G. E. Feigel R. C. Griffin O. F. Hedden E. J. Hemzy M. H. Jawad A. J. Justin W. G. Knecht J. LeCoff T. G. McCarty G. C. Millman R. A. Moen R. F. Reedy K. K. Tam ADMINISTRATIVE COMMITTEE J. G. Feldstein, Chair J. S. Brzuszkiewicz, Staff Secretary R. W. Barnes J. E. Batey T. L. Bedeaux D. L. Berger J. F. Henry U. R. Miller G. C. Park M. D. Rana B. F. Shelley W. J. Sperko INTERNATIONAL INTEREST REVIEW GROUP V. Felix Y.-G. Kim S. H. Leong W. Lin O. F. Manafa MARINE CONFERENCE GROUP H. N. Patel, Chair J. S. Brzuszkiewicz, Staff Secretary M. R. Klosterman — Iowa M. Kotb — Quebec, Canada K. J. Kraft — Maryland B. L. Krasiun — Saskatchewan, Canada K. T. Lau — Alberta, Canada W. McGivney — New York T. J. Monroe — Oklahoma S. V. Nelson — Colorado W. R. Owens — Louisiana R. P. Pate — Alabama R. L. Perry — Nevada H. D. Pfaff — South Dakota J. F. Porcella — West Virginia R. S. Pucek — Wisconsin R. D. Reetz — North Dakota C. F. Reyes — California T. W. Rieger — Manitoba, Canada K. A. Rudolph — Hawaii M. J. Ryan — Illinois T. S. Scholl — Ontario, Canada G. Scribner — Missouri R. Spiker — North Carolina T. Stewart — Montana R. K. Sturm — Utah W. Vallance — Michigan M. J. Verhagen — Wisconsin P. L. Vescio, Jr. — New York M. Washington — New Jersey K. L. Watson — Mississippi P. J. Welch — Georgia L. Williamson — Washington D. J. Willis — Indiana J. G. Hungerbuhler, Jr. G. Pallichadath J. D. Reynolds xv C. Minu Y.-W. Park R. Reynaga P. Williamson (a) PROJECT TEAM ON HYDROGEN TANKS M. D. Rana, Chair A. P. Amato, Staff Secretary F. L. Brown D. A. Canonico D. C. Cook J. Coursen J. W. Felbaum B. D. Hawkes N. L. Newhouse K. Nibur A. S. Olivares G. B. Rawls, Jr. B. F. Shelley J. R. Sims, Jr. N. Sirosh J. H. Smith S. Staniszewski R. Subramanian T. Tahara D. W. Treadwell E. Upitis Y. Wada Subgroup on General Requirements (BPV I) C. T. I. Webster R. C. Biel, Contributing Member J. Birdsall, Contributing Member M. Duncan, Contributing Member D. R. Frikken, Contributing Member L. E. Hayden, Jr., Contributing Member K. T. Lau, Contributing Member K. Oyamada, Contributing Member C. H. Rivkin, Contributing Member C. San Marchi, Contributing Member B. Somerday, Contributing Member R. E. McLaughlin, Chair T. E. Hansen, Vice Chair F. Massi, Secretary P. D. Edwards W. L. Lowry T. C. McGough E. M. Ortman J. T. Pillow Subgroup on Heat Recovery Steam Generators (BPV I) T. E. Hansen, Chair D. Dziubinski, Secretary J. P. Bell L. R. Douglas J. Gertz G. B. Komora C. T. McDaris B. W. Moore L. Moedinger, Chair S. M. Butler, Secretary P. Boschan J. Braun J. D. Conrad R. C. Franzen, Jr. D. W. Griner S. D. Jackson M. A. Janssen T. C. McGough P. A. Molvie Y. Oishi J. T. Pillow B. W. Roberts R. D. Schueler, Jr. J. P. Swezy, Jr. J. M. Tanzosh R. V. Wielgoszinski D. J. Willis G. Ardizzoia, Delegate H. Michael, Delegate E. M. Ortman, Alternate D. N. French, Honorary Member R. L. Williams, Honorary Member S. A. Lee G. M. Ray G. L. Scerbo R. D. Schueler, Jr. R. B. Stone M. W. Westland W. L. Withuhn R. Yuill Subgroup on Materials (BPV I) B. W. Roberts, Chair J. S. Hunter, Secretary S. H. Bowes D. A. Canonico K. K. Coleman P. Fallouey G. W. Galanes Subgroup on Design (BPV I) P. A. Molvie, Chair J. Vattappilly, Secretary D. I. Anderson P. Dhorajia J. P. Glaspie G. B. Komora J. C. Light B. W. Moore Y. Oishi E. M. Ortman R. D. Schueler, Jr. J. C. Steverman, Jr. D. Tompkins S. V. Torkildson B. C. Turczynski Subgroup on Locomotive Boilers (BPV I) COMMITTEE ON POWER BOILERS (BPV I) D. L. Berger, Chair R. E. McLaughlin, Vice Chair U. D’Urso, Staff Secretary J. L. Arnold S. W. Cameron D. A. Canonico K. K. Coleman P. D. Edwards P. Fallouey J. G. Feldstein G. W. Galanes T. E. Hansen J. F. Henry J. S. Hunter W. L. Lowry J. R. MacKay F. Massi D. Tompkins S. V. Torkildson D. E. Tuttle M. Wadkinson R. V. Wielgoszinski D. J. Willis C. F. Jeerings, Contributing Member R. D. Schueler, Jr. J. P. Swezy, Jr. S. V. Torkildson M. Wadkinson G. Ardizzoia, Delegate C. F. Jeerings, Contributing Member K. L. Hayes J. F. Henry O. X. Li J. R. MacKay F. Masuyama D. W. Rahoi J. M. Tanzosh Subgroup on Piping (BPV I) T. E. Hansen, Chair D. Tompkins, Secretary D. L. Berger P. D. Edwards G. W. Galanes T. G. Kosmatka W. L. Lowry F. Massi T. C. McGough E. A. Whittle Subgroup on Fabrication and Examination (BPV I) J. T. Pillow, Chair G. W. Galanes, Secretary J. L. Arnold D. L. Berger S. W. Cameron G. Dunker P. F. Gilston J. Hainsworth Subgroup on Solar Boilers (BPV I) T. E. Hansen C. T. McDaris T. C. McGough R. E. McLaughlin R. J. Newell Y. Oishi J. P. Swezy, Jr. R. V. Wielgoszinski J. S. Hunter, Chair J. R. Briggs G. W. Galanes R. E. Hearne P. L. Johnson D. J. Koza xvi J. C. Light Y. Magen F. Massi S. V. Torkildson J. T. Trimble, Jr. COMMITTEE ON MATERIALS (BPV II) J. F. Henry, Chair D. W. Rahoi, Vice Chair N. Lobo, Staff Secretary F. Abe A. Appleton J. Cameron D. A. Canonico A. Chaudouet P. Fallouey J. R. Foulds D. W. Gandy M. H. Gilkey M. Gold J. F. Grubb J. A. Hall C. L. Hoffmann M. Katcher F. Masuyama R. K. Nanstad M. L. Nayyar B. W. Roberts E. Shapiro M. H. Skillingberg R. C. Sutherlin R. W. Swindeman J. M. Tanzosh Subgroup on Nonferrous Alloys (BPV II) D. Tyler D. Kwon, Delegate O. Oldani, Delegate W. R. Apblett, Jr., Contributing Member M. N. Bressler, Contributing Member H. D. Bushfield, Contributing Member E. G. Nisbett, Contributing Member E. Upitis, Contributing Member T. M. Cullen, Honorary Member W. D. Doty, Honorary Member W. D. Edsall, Honorary Member G. C. Hsu, Honorary Member R. A. Moen, Honorary Member C. E. Spaeder, Jr., Honorary Member A. W. Zeuthen, Honorary Member M. Katcher, Chair R. C. Sutherlin, Secretary W. R. Apblett, Jr. M. H. Gilkey J. F. Grubb A. Heino J. Kissell T. M. Malota S. Matsumoto Subgroup on Physical Properties (BPV II) J. F. Grubb, Chair H. D. Bushfield P. Fallouey E. Shapiro Subgroup on Strength, Ferrous Alloys (BPV II) C. L. Hoffmann, Chair J. M. Tanzosh, Secretary F. Abe W. R. Apblett, Jr. D. A. Canonico A. Di Rienzo P. Fallouey J. R. Foulds M. Gold J. A. Hall J. F. Henry K. Kimura Subgroup on External Pressure (BPV II) R. W. Mikitka, Chair J. A. A. Morrow, Secretary L. F. Campbell D. S. Griffin J. F. Grubb J. R. Harris III H. Matsuo J. A. McMaster D. W. Rahoi E. Shapiro M. H. Skillingberg D. Tyler R. Zawierucha H. D. Bushfield, Contributing Member M. Katcher D. L. Kurle C. R. Thomas C. H. Sturgeon, Contributing Member F. Masuyama S. Matsumoto D. W. Rahoi B. W. Roberts M. S. Shelton J. P. Shingledecker M. J. Slater R. W. Swindeman T. P. Vassallo, Jr. H. Murakami, Contributing Member Subgroup on Ferrous Specifications (BPV II) A. Appleton, Chair R. M. Davison B. M. Dingman M. J. Dosdourian P. Fallouey T. Graham J. M. Grocki J. F. Grubb K. M. Hottle D. S. Janikowski D. C. Krouse L. J. Lavezzi W. C. Mack J. K. Mahaney R. J. Marciniec A. S. Melilli E. G. Nisbett K. E. Orie J. Shick E. Upitis R. Zawierucha Subgroup on Strength of Weldments (BPV II & BPV IX) J. M. Tanzosh, Chair W. F. Newell, Jr., Secretary S. H. Bowes K. K. Coleman P. D. Flenner J. R. Foulds D. W. Gandy M. Gold K. L. Hayes J. F. Henry D. W. Rahoi B. W. Roberts J. P. Shingledecker W. J. Sperko J. P. Swezy, Jr. Subgroup on International Material Specifications (BPV II) A. Chaudouet, Chair D. Dziubinski, Secretary S. W. Cameron D. A. Canonico P. Fallouey A. F. Garbolevsky D. O. Henry M. Ishikawa O. X. Li W. M. Lundy T. F. Miskell A. R. Nywening R. D. Schueler, Jr. E. Upitis D. Kwon, Delegate O. Oldani, Delegate H. Lorenz, Contributing Member Special Working Group on Nonmetallic Materials (BPV II) C. W. Rowley, Chair W. I. Adams F. L. Brown A. Crabtree S. R. Frost xvii M. Golliet P. S. Hill M. R. Kessler E. Lever F. Worth COMMITTEE ON CONSTRUCTION OF NUCLEAR FACILITY COMPONENTS (BPV III) R. W. Barnes, Chair J. R. Cole, Vice Chair M. L. Vazquez, Staff Secretary W. H. Borter M. N. Bressler T. D. Burchell R. P. Deubler A. C. Eberhardt B. A. Erler G. M. Foster R. S. Hill III C. L. Hoffmann R. M. Jessee V. Kostarev W. C. LaRochelle K. A. Manoly W. N. McLean M. N. Mitchell D. K. Morton R. F. Reedy J. D. Stevenson Working Group on Core Support Structures (SG-D) (BPV III) J. Yang, Chair J. F. Kielb, Secretary F. G. Al-Chammas H. S. Mehta K. R. Wichman C. S. Withers Y. H. Choi, Delegate T. Ius, Delegate H.-T. Wang, Delegate C. C. Kim, Contributing Member E. B. Branch, Honorary Member P. Chilukuri, Honorary Member G. D. Cooper, Honorary Member W. D. Doty, Honorary Member D. F. Landers, Honorary Member R. A. Moen, Honorary Member C. J. Pieper, Honorary Member Working Group on Design Methodology (SG-D) (BPV III) R. B. Keating, Chair S. D. Snow, Secretary K. Avrithi M. Basol R. D. Blevins D. L. Caldwell H. T. Harrison III P. Hirschberg H. Kobayashi H. Lockert J. F. McCabe A. N. Nguyen E. L. Pleins, Chair D. J. Ammerman G. Bjorkman S. Horowitz D. W. Lewis J. C. Minichiello D. K. Morton C. G. May P. E. McConnell I. D. McInnes A. B. Meichler R. E. Nickell E. L. Pleins T. Saegusa H. P. Shrivastava N. M. Simpson R. H. Smith J. D. Stevenson C. J. Temus P. Hirschberg, Chair G. Z. Tokarski, Secretary T. M. Adams G. A. Antaki C. Basavaraju J. Catalano F. Claeys J. R. Cole M. A. Gray R. W. Haupt J. Kawahata R. B. Keating V. Kostarev Y. Liu J. F. McCabe J. C. Minichiello R. J. Masterson D. E. Matthews W. N. McLean J. C. Minichiello T. Nagata E. L. Pleins I. Saito G. C. Slagis J. D. Stevenson J. P. Tucker K. R. Wichman J. Yang T. Ius, Delegate M. N. Bressler, Contributing Member I. K. Nam E. R. Nelson A. N. Nguyen N. J. Shah M. S. Sills G. C. Slagis N. C. Sutherland E. A. Wais C.-I. Wu D. F. Landers, Corresponding Member R. D. Patel, Contributing Member E. C. Rodabaugh, Honorary Member Working Group on Probabilistic Methods in Design (SG-D) (BPV III) R. S. Hill III, Chair N. A. Palm, Secretary T. Asayama K. Avrithi B. M. Ayyub A. A. Dermenjian M. R. Graybeal D. O. Henry S. D. Kulat Working Group on Supports (SG-D) (BPV III) R. J. Masterson, Chair F. J. Birch, Secretary K. Avrithi T. H. Baker U. S. Bandyopadhyay R. P. Deubler W. P. Golini H. P. Shrivastava C. J. Temus I. D. McInnes, Contributing Member R. E. Nickell, Contributing Member Working Group on Piping (SG-D) (BPV III) Subgroup on Component Design (BPV III) R. S. Hill III, Chair T. M. Adams, Vice Chair A. N. Nguyen, Secretary S. Asada C. W. Bruny J. R. Cole R. E. Cornman, Jr. A. A. Dermenjian R. P. Deubler P. Hirschberg R. I. Jetter R. B. Keating H. Kobayashi D. F. Landers K. A. Manoly D. H. Roarty E. A. Rodriguez J. D. Stevenson A. Tsirigotis T. M. Wiger J. Yang D. F. Landers, Corresponding Member M. K. Au-Yang, Contributing Member W. S. Lapay, Contributing Member Working Group on Design of Division 3 Containments (SG-D) (BPV III) Subgroup on Containment Systems for Spent Fuel and High-Level Waste Transport Packagings (BPV III) G. M. Foster, Chair G. J. Solovey, Vice Chair D. K. Morton, Secretary D. J. Ammerman W. G. Beach G. Bjorkman W. H. Borter G. R. Cannell J. L. Gorczyca R. S. Hill III S. Horowitz D. W. Lewis A. Tsirigotis J. T. Land, Contributing Member A. N. Nguyen I. Saito J. R. Stinson T. G. Terryah G. Z. Tokarski C.-I. Wu xviii A. McNeill III M. Morishita P. J. O’Regan I. Saito M. E. Schmidt A. Tsirigotis J. P. Tucker R. M. Wilson Working Group on Pumps (SG-D) (BPV III) R. E. Cornman, Jr., Chair P. W. Behnke M. D. Eftychiou A. Fraser R. Ghanbari M. Higuchi Subgroup on Materials, Fabrication, and Examination (BPV III) R. A. Ladefian J. W. Leavitt R. A. Patrick R. Udo A. G. Washburn C. L. Hoffmann, Chair W. G. Beach W. H. Borter G. R. Cannell R. H. Davis G. M. Foster B. D. Frew G. B. Georgiev S. E. Gingrich R. M. Jessee Working Group on Valves (SG-D) (BPV III) J. P. Tucker, Chair J. O’Callaghan, Secretary G. A. Jolly W. N. McLean T. A. McMahon C. A. Mizer J. D. Page K. E. Reid II S. N. Shields H. R. Sonderegger P. Vock C. C. Kim M. Lau H. Murakami J. Ossmann N. M. Simpson W. J. Sperko J. R. Stinson J. F. Strunk K. B. Stuckey H. Michael, Delegate Subgroup on Pressure Relief (BPV III) J. F. Ball, Chair E. M. Petrosky A. L. Szeglin D. G. Thibault Working Group on Vessels (SG-D) (BPV III) D. E. Matthews, Chair R. M. Wilson, Secretary C. Basavaraju C. W. Bruny J. V. Gregg, Jr. W. J. Heilker A. Kalnins R. B. Keating O.-S. Kim K. Matsunaga P. K. Shah C. Turylo D. Vlaicu W. F. Weitze Executive Committee on Strategy and Management (BPV III, Divisions 1 and 2) J. R. Cole, Chair C. A. Sanna, Staff Secretary R. W. Barnes B. K. Bobo N. Broom B. A. Erler C. M. Faidy J. M. Helmey R. S. Hill III E. V. Imbro Special Working Group on Environmental Effects (SG-D) (BPV III) W. Z. Novak, Chair R. S. Hill III C. L. Hoffmann Y. H. Choi, Delegate R. M. Jessee K. A. Manoly D. K. Morton J. Ramirez R. F. Reedy C. T. Smith W. K. Sowder, Jr. Y. Urabe M. F. Sullivan, Contributing Member Subgroup on General Requirements (BPV III & 3C) W. C. LaRochelle, Chair L. M. Plante, Secretary A. Appleton J. R. Berry M. N. Bressler J. V. Gardiner W. P. Golini J. W. Highlands China International Group (BPV III) G. L. Hollinger R. P. McIntyre M. R. Minick C. T. Smith W. K. Sowder, Jr. D. M. Vickery C. S. Withers H. Michael, Delegate C. A. Sanna, Staff Secretary Y. Chen G. Tang Special Working Group for New Advanced Light Water Reactor Plant Construction Issues (BPV III) Working Group on Duties and Responsibilities (SG-GR) (BPV III) J. V. Gardiner, Chair G. L. Hollinger, Secretary J. R. Berry Y. Diaz-Castillo G. Gratti M. E. Jennings C. A. Sanna, Chair A. Cardillo J. Honcharik E. V. Imbro K. A. Kavanagh M. A. Lockwood L. M. Plante D. J. Roszman S. Scardigno E. L. Pleins J. A. Schulz M. C. Scott R. R. Stevenson Subgroup on Editing and Review (BPV III) D. K. Morton, Chair W. H. Borter M. N. Bressler R. P. Deubler Working Group on Quality Assurance, Certification, and Stamping (SG-GR) (BPV III) C. T. Smith, Chair C. S. Withers, Secretary A. Appleton B. K. Bobo S. M. Goodwin J. W. Highlands R. P. McIntyre M. R. Minick J. Yan Z. Yan Z. Zhong R. B. Patel E. C. Renaud S. J. Salvador W. K. Sowder, Jr. J. F. Strunk M. F. Sullivan G. E. Szabatura D. M. Vickery B. A. Erler W. C. LaRochelle R. F. Reedy J. D. Stevenson Subgroup on Management Resources (BPV III) R. M. Jessee, Chair V. Broz I. I. Jeong xix J. McLean B. S. Sandhu Subgroup on Polyethylene Pipe (BPV III) J. C. Minichiello, Chair T. M. Adams W. I. Adams G. A. Antaki C. Basavaraju S. J. Boros D. Burwell A. Crabtree J. M. Craig R. R. Croft E. L. Farrow E. M. Focht M. Golliet A. N. Haddad Subgroup on High-Temperature Reactors (BPV III) R. S. Hill III P. Krishnaswamy E. Lever E. W. McElroy D. P. Munson T. M. Musto L. J. Petroff C. W. Rowley F. J. Schaaf, Jr. C. T. Smith H. E. Svetlik D. M. Vickery Z. J. Zhou M. Morishita, Chair R. I. Jetter, Vice Chair T.-L. Sham, Secretary N. Broom T. D. Burchell Working Group on Liquid Metal Reactors (BPV III) T.-L. Sham, Chair T. Asayama, Secretary R. W. Barnes P. Carter C. M. Faidy W. Hoffelner Working Group on Nuclear High-Temperature Gas-Cooled Reactors (BPV III) N. Broom, Chair J. E. Nestell, Secretary T. D. Burchell R. S. Hill III W. Hoffelner E. V. Imbro R. I. Jetter Y. W. Kim T. R. Lupold D. L. Marriott D. K. Morton T.-L. Sham Y. Tachibana T. Yuhara G. L. Hollinger, Chair W. F. Weitze, Secretary S. A. Adams M. R. Breach R. G. Brown T. M. Damiani B. F. Hantz C. F. Heberling II C. E. Hinnant D. P. Jones A. Kalnins G. O. Hayner M. P. Hindley Y. Katoh M. N. Mitchell N. N. Nemeth T. Oku J. Ossmann T. Shibata M. Srinivasan A. G. Steer S. Yu R. I. Jetter, Chair T.-L. Sham, Secretary J. J. Abou-Hanna T. Asayama C. Becht IV F. W. Brust P. Carter J. F. Cervenka B. Dogan D. S. Griffin B. F. Hantz W. Hoffelner O.-S. Kim K. Matsunaga D. E. Matthews R. E. McLaughlin J. Ossmann R. D. Patel J. C. Poehler D. W. Sandusky R. R. Schaefer D. M. Swann T. Tsuruta E. R. Willis S. M. Yee A. B. Hull M. H. Jawad G. H. Koo W. J. Koves M. Li S. Majumdar D. L. Marriott T. E. McGreevy J. E. Nestell W. J. O’Donnell R. W. Swindeman Subgroup on Fatigue Strength (BPV III) W. J. O’Donnell, Chair S. A. Adams G. S. Chakrabarti T. M. Damiani P. R. Donavin R. J. Gurdal C. F. Heberling II C. E. Hinnant P. Hirschberg D. P. Jones Subgroup on Fusion Energy Devices (BPV III) W. K. Sowder, Jr., Chair D. Andrei, Staff Secretary R. W. Barnes M. Higuchi G. Holtmeier K. A. Kavanagh H.-J. Kim W. J. Koves K. Matsunaga G. A. Miller W. D. Reinhardt D. H. Roarty G. Sannazzaro T. G. Seipp G. Taxacher R. A. Whipple K. Wright Subgroup on Elevated Temperature Design (BPV III) Subgroup on Industry Experience for New Plants (BPV III & BPV XI) G. M. Foster, Chair J. T. Lindberg, Chair H. L. Gustin, Secretary V. L. Armentrout T. L. Chan M. L. Coats A. A. Dermenjian J. Fletcher E. B. Gerlach D. O. Henry J. Honcharik E. V. Imbro C. C. Kim R. I. Jetter G. H. Koo M. Li S. Majumdar M. Morishita J. E. Nestell Subgroup on Design Analysis (BPV III) Subgroup on Graphite Core Components (BPV III) T. D. Burchell, Chair C. A. Sanna, Staff Secretary A. Appleton R. L. Bratton S.-H. Chi M. W. Davies S. W. Doms S. F. Duffy B. D. Frew O. Gelineau S. T. Gonczy W. Hoffelner G. H. Koo D. K. Morton J. E. Nestell N. N. Ray S. Lee G. Li X. Li P. Mokaria D. J. Roszman S. J. Salvador xx G. Kharshafdjian S. Majumdar S. N. Malik R. Nayal D. H. Roarty M. S. Shelton G. Taxacher A. Tsirigotis K. Wright H. H. Ziada Subgroup on Care and Operation of Heating Boilers (BPV IV) JOINT ACI-ASME COMMITTEE ON CONCRETE COMPONENTS FOR NUCLEAR SERVICE (BPV 3C) A. C. Eberhardt, Chair C. T. Smith, Vice Chair M. L. Vazquez, Staff Secretary N. Alchaar J. F. Artuso C. J. Bang F. Farzam P. S. Ghosal J. Gutierrez J. K. Harrold G. A. Harstead M. F. Hessheimer T. C. Inman O. Jovall N.-H. Lee J. Munshi N. Orbovic P. A. Molvie B. B. Scott R. E. Shewmaker J. D. Stevenson M. L. Williams T. D. Al-Shawaf, Contributing Member B. A. Erler, Contributing Member T. E. Johnson, Contributing Member T. Muraki, Contributing Member M. R. Senecal, Contributing Member M. K. Thumm, Contributing Member Subgroup on Cast Iron Boilers (BPV IV) K. M. McTague, Chair T. L. Bedeaux, Vice Chair J. P. Chicoine B. G. French J. A. Hall Subgroup on Materials (BPV IV) J. A. Hall, Chair M. Wadkinson, Vice Chair J. Calland J. Calland, Chair J. P. Chicoine B. G. French T. D. Gantt B. J. Iske K. M. McTague M. F. Hessheimer T. C. Inman T. E. Johnson O. Jovall N.-H. Lee J. D. Stevenson M. K. Thumm J. Calland, Chair T. L. Bedeaux C. M. Dove B. G. French E. A. Nordstrom R. E. Olson J. Gutierrez B. B. Scott C. T. Smith J. F. Strunk J. E. Batey, Chair F. B. Kovacs, Vice Chair J. S. Brzuszkiewicz, Staff Secretary S. J. Akrin C. A. Anderson J. E. Aycock A. S. Birks P. L. Brown M. A. Burns N. Y. Faransso A. F. Garbolevsky G. W. Hembree R. W. Kruzic J. R. McGimpsey J. K. Harrold N. Orbovic M. A. Ugalde COMMITTEE ON HEATING BOILERS (BPV IV) T. L. Bedeaux, Chair J. A. Hall, Vice Chair G. Moino, Staff Secretary J. Calland J. P. Chicoine C. M. Dove B. G. French W. L. Haag, Jr. A. Heino B. J. Iske D. J. Jenkins M. Wadkinson R. V. Wielgoszinski H. Michael, Delegate J.-M. Andre, Contributing Member COMMITTEE ON NONDESTRUCTIVE EXAMINATION (BPV V) Working Group on Modernization (BPV 3C) N. Alchaar, Chair O. Jovall, Vice Chair C. T. Smith, Secretary J. F. Artuso O. A. Missoum R. E. Olson F. J. Schreiner M. A. Taylor T. E. Trant M. T. Roby, Alternate Subgroup on Welded Boilers (BPV IV) Working Group on Materials, Fabrication, and Examination (BPV 3C) J. F. Artuso, Chair P. S. Ghosal, Vice Chair M. L. Williams, Secretary A. C. Eberhardt A. Heino B. J. Iske J. L. Kliess Subgroup on Water Heaters (BPV IV) Working Group on Design (BPV 3C) J. Munshi, Chair N. Alchaar L. J. Colarusso A. C. Eberhardt F. Farzam P. S. Ghosal J. K. Harrold G. A. Harstead V. G. Kleftis J. L. Kliess E. A. Nordstrom M. T. Roby, Alternate J. L. Kleiss M. R. Klosterman K. M. McTague P. A. Molvie B. W. Moore R. E. Olson T. M. Parks R. V. Wielgoszinski H. Michael, Delegate D. Picart, Delegate E. A. Nordstrom, Alternate M. D. Moles A. B. Nagel T. L. Plasek F. J. Sattler G. M. Gatti, Delegate B. H. Clark, Jr., Honorary Member H. C. Graber, Honorary Member O. F. Hedden, Honorary Member J. R. MacKay, Honorary Member T. G. McCarty, Honorary Member Subgroup on General Requirements/ Personnel Qualifications and Inquiries (BPV V) F. B. Kovacs, Chair C. A. Anderson J. E. Aycock J. E. Batey A. S. Birks xxi N. Y. Faransso G. W. Hembree J. W. Houf J. R. MacKay J. P. Swezy, Jr. Subgroup on Design (BPV VIII) Subgroup on Surface Examination Methods (BPV V) J. E. Aycock, Chair N. Farrenbaugh S. J. Akrin N. A. Finney A. S. Birks G. W. Hembree P. L. Brown R. W. Kruzic B. Caccamise F. J. Sattler N. Y. Faransso G. M. Gatti, Delegate R. J. Basile, Chair M. D. Lower, Secretary O. A. Barsky F. L. Brown J. R. Farr C. E. Hinnant M. H. Jawad R. W. Mikitka U. R. Miller K. Mokhtarian T. P. Pastor M. D. Rana G. B. Rawls, Jr. S. C. Roberts C. D. Rodery Subgroup on Volumetric Methods (BPV V) G. W. Hembree, Chair R. W. Hardy S. J. Akrin F. B. Kovacs J. E. Aycock R. W. Kruzic J. E. Batey J. R. McGimpsey P. L. Brown M. D. Moles B. Caccamise A. B. Nagel N. Y. Faransso T. L. Plasek A. F. Garbolevsky F. J. Sattler J. F. Halley G. M. Gatti, Delegate Working Group on Acoustic Emissions (SG-VM) (BPV V) N. Y. Faransso, Chair J. E. Batey J. E. Aycock R. K. Miller A. Selz S. C. Shah J. C. Sowinski C. H. Sturgeon D. A. Swanson K. K. Tam J. Vattappilly R. A. Whipple A. A. Gibbs, Delegate K. Oyamada, Delegate M. E. Papponetti, Delegate W. S. Jacobs, Corresponding Member E. L. Thomas, Jr., Honorary Member Subgroup on Fabrication and Inspection (BPV VIII) Working Group on Radiography (SG-VM) (BPV V) F. B. Kovacs, Chair R. W. Hardy S. J. Akrin G. W. Hembree J. E. Aycock R. W. Kruzic J. E. Batey J. R. McGimpsey P. L. Brown R. J. Mills B. Caccamise A. B. Nagel N. Y. Faransso T. L. Plasek A. F. Garbolevsky D. E. Williams C. D. Rodery, Chair J. P. Swezy, Jr., Vice Chair B. R. Morelock, Secretary J. L. Arnold W. J. Bees L. F. Campbell H. E. Gordon D. J. Kreft J. S. Lee D. I. Morris Working Group on Ultrasonics (SG-VM) (BPV V) R. W. Kruzic, Chair J. F. Halley J. E. Aycock O. F. Hedden B. Caccamise M. D. Moles K. J. Chizen A. B. Nagel N. Y. Faransso F. J. Sattler N. A. Finney M. J. Pischke M. J. Rice B. F. Shelley P. L. Sturgill T. Tahara K. Oyamada, Delegate R. Uebel, Delegate W. S. Jacobs, Contributing Member Subgroup on General Requirements (BPV VIII) S. C. Roberts, Chair D. B. DeMichael, Vice Chair F. L. Richter, Secretary R. J. Basile V. Bogosian D. T. Davis J. P. Glaspie L. E. Hayden, Jr. K. T. Lau M. D. Lower Working Group on Guided Wave Ultrasonic Testing (SG-VM) (BPV V) N. Y. Faransso, Chair M. D. Moles J. F. Halley COMMITTEE ON PRESSURE VESSELS (BPV VIII) U. R. Miller, Chair D. T. Peters R. J. Basile, Vice Chair M. J. Pischke S. J. Rossi, Staff Secretary M. D. Rana T. Schellens, Staff Secretary G. B. Rawls, Jr. V. Bogosian S. C. Roberts J. Cameron C. D. Rodery A. Chaudouet A. Selz D. B. DeMichael J. R. Sims, Jr. J. P. Glaspie E. Soltow M. Gold D. A. Swanson J. F. Grubb K. K. Tam L. E. Hayden, Jr. S. Terada G. G. Karcher E. Upitis K. T. Lau P. A. McGowan, Delegate J. S. Lee H. Michael, Delegate R. Mahadeen K. Oyamada, Delegate R. W. Mikitka M. E. Papponetti, Delegate K. Mokhtarian D. Rui, Delegate C. C. Neely T. Tahara, Delegate T. W. Norton W. S. Jacobs, Contributing T. P. Pastor Member C. C. Neely A. S. Olivares J. C. Sowinski D. B. Stewart D. A. Swanson K. K. Tam A. A. Gibbs, Delegate K. Oyamada, Delegate R. Uebel, Delegate Subgroup on Heat Transfer Equipment (BPV VIII) R. Mahadeen, Chair T. W. Norton, Vice Chair G. Aurioles, Sr., Secretary S. R. Babka J. H. Barbee O. A. Barsky I. G. Campbell A. Chaudouet M. D. Clark J. I. Gordon M. J. Holtz F. E. Jehrio G. G. Karcher xxii D. L. Kurle B. J. Lerch S. Mayeux U. R. Miller R. J. Stastny R. P. Wiberg K. Oyamada, Delegate F. Osweiller, Corresponding Member S. Yokell, Corresponding Member S. M. Caldwell, Honorary Member Subgroup on High-Pressure Vessels (BPV VIII) D. T. Peters, Chair A. P. Maslowski, Staff Secretary L. P. Antalffy R. C. Biel P. N. Chaku R. Cordes R. D. Dixon L. Fridlund D. M. Fryer R. T. Hallman A. H. Honza M. M. James P. Jansson J. A. Kapp J. Keltjens D. P. Kendall A. K. Khare S. C. Mordre Task Group on Design (BPV VIII) J. Keltjens, Chair R. C. Biel D. J. Burns R. Cordes R. D. Dixon L. Fridlund D. M. Fryer R. T. Hallman D. P. Kendall S. C. Mordre E. A. Rodriguez E. D. Roll J. R. Sims, Jr. D. L. Stang F. W. Tatar S. Terada J. L. Traud R. Wink K. Oyamada, Delegate R. M. Hoshman, Contributing Member M. D. Mann, Contributing Member G. J. Mraz, Contributing Member D. J. Burns, Honorary Member E. H. Perez, Honorary Member Task Group on Materials (BPV VIII) F. W. Tatar, Chair L. P. Antalffy P. N. Chaku R. E. Nickell, Chair E. A. Rodriguez, Vice Chair P. O. Leslie, Secretary G. A. Antaki J. K. Asahina D. D. Barker D. W. Bowman A. M. Clayton J. E. Didlake, Jr. T. A. Duffey B. L. Haroldsen H. L. Heaton K. Oyamada, Delegate E. E. Morgenegg, Corresponding Member E. G. Nisbett, Corresponding Member G. S. Dixit, Contributing Member J. A. McMaster, Contributing Member W. J. Sperko, Chair D. A. Bowers, Vice Chair S. J. Rossi, Staff Secretary M. Bernasek R. K. Brown, Jr. M. L. Carpenter J. G. Feldstein P. D. Flenner R. M. Jessee J. S. Lee W. M. Lundy T. Melfi W. F. Newell, Jr. B. R. Newmark A. S. Olivares C. C. Neely M. D. Rana F. L. Richter J. P. Swezy, Jr. E. Upitis J. Vattappilly K. Oyamada, Delegate Special Working Group on Graphite Pressure Equipment (BPV VIII) E. Soltow, Chair T. F. Bonn F. L. Brown R. W. Dickerson D. Hilding K. W. King R. Kitamura R. A. Leishear F. Ohlson C. Romero J. E. Shepherd Q. Dong, Corresponding Member M. Yip, Corresponding Member C. R. Vaught, Alternate COMMITTEE ON WELDING AND BRAZING (BPV IX) Subgroup on Toughness (BPV II & BPV VIII) D. A. Swanson, Chair J. L. Arnold R. J. Basile J. Cameron H. E. Gordon W. S. Jacobs D. L. Kurle K. Mokhtarian M. M. James J. A. Kapp A. K. Khare Task Group on Impulsively Loaded Vessels (BPV VIII) Subgroup on Materials (BPV VIII) J. F. Grubb, Chair J. Cameron, Vice Chair P. G. Wittenbach, Secretary A. Di Rienzo M. Gold M. Katcher W. M. Lundy D. W. Rahoi R. C. Sutherlin E. Upitis G. T. Nelson E. H. Perez D. T. Peters E. D. Roll J. R. Sims, Jr. D. L. Stang S. Terada J. L. Traud R. Wink M. J. Pischke M. J. Rice M. B. Sims M. J. Stanko J. P. Swezy, Jr. P. L. Van Fosson R. R. Young S. A. Jones, Contributing Member S. Raghunathan, Contributing Member W. D. Doty, Honorary Member S. D. Reynolds, Jr., Honorary Member Subgroup on Brazing (BPV IX) M. J. Pischke, Chair E. W. Beckman L. F. Campbell B. Lukasch S. Malone M. R. Minick A. A. Stupica M. L. Carpenter A. F. Garbolevsky J. P. Swezy, Jr. Subgroup on General Requirements (BPV IX) B. R. Newmark, Chair E. W. Beckman P. R. Evans A. Howard R. M. Jessee A. S. Olivares Special Working Group on Bolted Flanged Joints (BPV VIII) R. W. Mikitka, Chair G. D. Bibel W. Brown W. J. Koves M. S. Shelton xxiii H. B. Porter P. L. Sturgill K. R. Willens E. W. Woelfel E. Molina, Delegate Subgroup on Materials (BPV IX) M. L. Carpenter, Chair S. D. Reynolds, Jr. J. L. Arnold C. E. Sainz M. Bernasek W. J. Sperko S. E. Gingrich M. J. Stanko R. M. Jessee P. L. Sturgill C. C. Kim R. R. Young T. Melfi V. G. V. Giunto, Delegate Executive Committee (BPV XI) R. W. Swayne, Chair W. E. Norris G. C. Park, Vice Chair R. K. Rhyne R. L. Crane, Staff Secretary J. C. Spanner, Jr. W. H. Bamford, Jr. K. B. Thomas R. L. Dyle R. A. West R. E. Gimple R. A. Yonekawa J. T. Lindberg Subgroup on Performance Qualification (BPV IX) D. A. Bowers, Chair K. L. Hayes V. A. Bell J. S. Lee M. A. Boring W. M. Lundy R. B. Corbit E. G. Reichelt P. R. Evans M. B. Sims P. D. Flenner Subgroup on Evaluation Standards (SG-ES) (BPV XI) W. H. Bamford, Jr., Chair K. Koyama G. L. Stevens, Secretary D. R. Lee H. D. Chung H. S. Mehta R. C. Cipolla J. G. Merkle G. H. DeBoo M. A. Mitchell R. L. Dyle K. Miyazaki B. R. Ganta S. Ranganath T. J. Griesbach D. A. Scarth K. Hasegawa T.-L. Sham K. Hojo T. V. Vo D. N. Hopkins K. R. Wichman Y. Imamura Subgroup on Procedure Qualification (BPV IX) D. A. Bowers, Chair M. B. Sims M. J. Rice, Secretary W. J. Sperko M. Bernasek S. A. Sprague M. A. Boring J. P. Swezy, Jr. R. K. Brown, Jr. P. L. Van Fosson J. R. McGimpsey T. C. Wiesner W. F. Newell, Jr. E. Molina, Delegate A. S. Olivares Working Group on Flaw Evaluation (SG-ES) (BPV XI) R. C. Cipolla, Chair J. G. Merkle G. H. DeBoo, Secretary G. A. Miessi W. H. Bamford, Jr. K. Miyazaki M. Basol R. K. Qashu B. Bezensek S. Ranganath H. D. Chung D. L. Rudland B. R. Ganta P. J. Rush R. G. Gilada D. A. Scarth H. L. Gustin W. L. Server F. D. Hayes N. J. Shah P. H. Hoang T. V. Vo K. Hojo K. R. Wichman D. N. Hopkins G. M. Wilkowski K. Koyama S. X. Xu D. R. Lee K. K. Yoon H. S. Mehta V. A. Zilberstein COMMITTEE ON FIBER-REINFORCED PLASTIC PRESSURE VESSELS (BPV X) D. Eisberg, Chair B. M. Linnemann P. D. Stumpf, Staff Secretary N. L. Newhouse F. L. Brown D. J. Painter J. L. Bustillos G. Ramirez T. W. Cowley J. R. Richter I. L. Dinovo J. A. Rolston T. J. Fowler B. F. Shelley M. R. Gorman F. W. Van Name D. H. Hodgkinson D. O. Yancey, Jr. L. E. Hunt P. H. Ziehl D. L. Keeler COMMITTEE ON NUCLEAR INSERVICE INSPECTION (BPV XI) G. C. Park, Chair R. K. Rhyne R. W. Swayne, Vice Chair D. A. Scarth R. L. Crane, Staff Secretary F. J. Schaaf, Jr. V. L. Armentrout J. C. Spanner, Jr. W. H. Bamford, Jr. K. B. Thomas T. L. Chan D. E. Waskey R. C. Cipolla R. A. West D. D. Davis C. J. Wirtz G. H. DeBoo R. A. Yonekawa R. L. Dyle T. Yuhara E. L. Farrow H. D. Chung, Delegate J. Fletcher J. T. Lindberg, Alternate E. B. Gerlach G. L. Stevens, Alternate R. E. Gimple L. J. Chockie, Honorary T. J. Griesbach Member K. Hasegawa C. D. Cowfer, Honorary D. O. Henry Member R. D. Kerr F. E. Gregor, Honorary S. D. Kulat Member G. L. Lagleder O. F. Hedden, Honorary D. W. Lamond Member G. A. Lofthus P. C. Riccardella, Honorary W. E. Norris Member J. E. O’Sullivan K. K. Yoon, Honorary Member A. S. Reed Working Group on Operating T. J. Griesbach, Chair D. V. Sommerville, Secretary W. H. Bamford, Jr. H. Behnke T. L. Dickson R. L. Dyle S. R. Gosselin M. Hayashi Plant Criteria (SG-ES) (BPV XI) H. S. Mehta M. A. Mitchell R. Pace N. A. Palm S. Ranganath W. L. Server D. P. Weakland Working Group on Pipe Flaw Evaluation (SG-ES) (BPV XI) D. A. Scarth, Chair K. Hojo G. M. Wilkowski, Secretary D. N. Hopkins T. A. Bacon K. Kashima W. H. Bamford, Jr. R. O. McGill B. Bezensek H. S. Mehta H. D. Chung K. Miyazaki R. C. Cipolla D. L. Rudland N. G. Cofie P. J. Rush J. M. Davis T.-L. Sham G. H. DeBoo D. J. Shim B. Dogan T. V. Vo B. R. Ganta B. S. Wasiluk L. F. Goyette S. X. Xu K. Hasegawa K. K. Yoon P. H. Hoang V. A. Zilberstein xxiv Working Group on Design and Programs (SG-RRA) (BPV XI) Subgroup on Nondestructive Examination (SG-NDE) (BPV XI) J. C. Spanner, Jr., Chair G. A. Lofthus, Secretary C. A. Anderson T. L. Chan C. B. Cheezem D. R. Cordes F. E. Dohmen M. E. Gothard D. O. Henry E. B. Gerlach, Chair S. B. Brown, Secretary O. Bhatty J. W. Collins R. R. Croft G. G. Elder E. V. Farrell, Jr. S. K. Fisher J. M. Gamber G. L. Lagleder J. T. Lindberg T. R. Lupold G. R. Perkins A. S. Reed S. A. Sabo F. J. Schaaf, Jr. C. J. Wirtz Subgroup on Water-Cooled Systems (SG-WCS) (BPV XI) Working Group on Personnel Qualification and Surface Visual and Eddy Current Examination (SG-NDE) (BPV XI) A. S. Reed, Chair D. R. Cordes, Secretary C. A. Anderson B. L. Curtis N. Farenbaugh D. O. Henry K. M. Hoffman J. W. Houf K. B. Thomas, Chair N. A. Palm, Secretary J. M. Agold V. L. Armentrout J. M. Boughman S. T. Chesworth D. D. Davis H. Q. Do E. L. Farrow M. J. Ferlisi O. F. Hedden P. J. Hennessey J. T. Lindberg D. R. Quattlebaum, Jr. D. Spake J. C. Spanner, Jr. M. C. Weatherly M. L. Whytsell C. J. Wirtz Working Group on Procedure Qualification and Volumetric Examination (SG-NDE) (BPV XI) M. E. Gothard, Chair G. R. Perkins, Secretary M. T. Anderson C. B. Cheezem A. D. Chockie S. R. Doctor F. E. Dohmen D. R. Graham G. F. Harttraft T. E. Hiss M. A. Pyne R. R. Stevenson R. W. Swayne A. H. Taufique T. P. Vassallo, Jr. R. A. Yonekawa S. D. Kulat D. W. Lamond A. McNeill III T. Nomura W. E. Norris G. C. Park J. E. Staffiera H. M. Stephens, Jr. R. A. West G. E. Whitman H. L. Graves III, Alternate Working Group on Containment (SG-WCS) (BPV XI) K. J. Hacker G. A. Lofthus C. A. Nove S. A. Sabo R. V. Swain B. A. Thigpen S. J. Todd J. E. Staffiera, Chair H. M. Stephens, Jr., Secretary S. G. Brown J. W. Crider P. S. Ghosal D. H. Goche H. L. Graves III H. T. Hill R. D. Hough C. N. Krishnaswamy D. J. Naus F. Poteet III G. Thomas W. E. Norris, Alternate Subgroup on Repair/Replacement Activities (SG-RRA) (BPV XI) R. A. Yonekawa, Chair E. V. Farrell, Jr., Secretary S. B. Brown R. E. Cantrell P. D. Fisher J. M. Gamber E. B. Gerlach R. E. Gimple D. R. Graham R. A. Hermann Working Group on ISI Optimization (SG-WCS) (BPV XI) K. J. Karwoski R. D. Kerr S. L. McCracken B. R. Newton J. E. O’Sullivan R. R. Stevenson R. W. Swayne D. E. Waskey J. G. Weicks E. G. Reichelt, Alternate D. R. Cordes, Chair S. A. Norman, Secretary W. H. Bamford, Jr. J. M. Boughman J. W. Collins M. E. Gothard R. E. Hall Working Group on Implementation of Risk-Based Examination (SG-WCS) (BPV XI) Working Group on Welding and Special Repair Processes (SG-RRA) (BPV XI) D. E. Waskey, Chair D. J. Tilly, Secretary R. E. Cantrell S. J. Findlan P. D. Fisher M. L. Hall R. A. Hermann K. J. Karwoski C. C. Kim A. H. Mahindrakar E. L. McClain F. Poteet III S. A. Sabo K. B. Thomas G. E. Whitman Y. Yuguchi S. D. Kulat, Chair S. T. Chesworth, Secretary J. M. Agold C. Cueto-Felgueroso H. Q. Do R. Fougerousse M. R. Graybeal R. Haessler J. Hakii K. W. Hall M. Lau S. L. McCracken D. B. Meredith B. R. Newton J. E. O’Sullivan R. E. Smith J. G. Weicks K. R. Willens xxv K. M. Hoffman D. W. Lamond J. T. Lewis R. K. Mattu A. McNeill III P. J. O’Regan N. A. Palm M. A. Pyne J. C. Younger Subgroup on Design and Materials (BPV XII) Working Group on Inspection of Systems and Components (SG-WCS) (BPV XI) J. M. Agold, Chair V. L. Armentrout, Secretary C. Cueto-Felgueroso R. E. Day H. Q. Do M. J. Ferlisi R. Fougerousse K. W. Hall A. P. Varghese, Chair R. C. Sallash, Secretary D. K. Chandiramani P. Chilukuri T. Hitchcock G. G. Karcher T. P. Lokey S. L. McWilliams S. D. Kulat T. A. Meyer D. G. Naujock T. Nomura J. C. Nygaard C. M. Ross K. B. Thomas G. E. Whitman Subgroup on Fabrication, Inspection, and Continued Service (BPV XII) Working Group on Pressure Testing (SG-WCS) (BPV XI) D. W. Lamond, Chair J. M. Boughman, Secretary Y.-K. Chung J. J. Churchwell T. Coste J. A. Doughty R. E. Hall T. R. Lupold J. K. McClanahan B. L. Montgomery P. N. Passalugo M. Pitts, Chair P. Chilukuri, Secretary J. A. Byers W. L. Garfield D. J. Kreft C. H. Hochman, Chair A. N. Antoniou, Secretary T. W. Alexander S. E. Benet J. L. Freiler W. L. Garfield K. L. Gilmore J. E. Staffiera D. J. Tilly C. J. Wirtz Special Working Group on Nuclear Plant Aging Management (BPV XI) T. A. Meyer, Chair D. V. Burgess, Secretary S. Asada Y.-K. Chung B. Clark III D. D. Davis A. L. Hiser, Jr. A. B. Meichler R. E. Nickell K. Sakamoto W. L. Server R. L. Turner G. G. Young C. E. Carpenter, Alternate T. A. Rogers, Chair S. Staniszewski, Secretary S. E. Benet P. Chilukuri S. L. McWilliams M. Pitts A. Selz D. G. Shelton A. P. Varghese M. R. Ward M. R. Graybeal A. B. Hull R. K. Miller M. N. Mitchell T. Roney R. W. Swayne W. C. LaRochelle, Chair P. D. Edwards, Vice Chair K. I. Baron, Staff Secretary W. J. Bees S. W. Cameron T. E. Hansen D. J. Jenkins K. T. Lau L. E. McDonald K. M. McTague D. Miller B. R. Morelock J. D. O’Leary T. M. Parks B. C. Turczynski D. E. Tuttle E. A. Whittle S. F. Harrison, Jr., Contributing Member R. Fox P. J. Hennessey R. K. Mattu C. E. Moyer R. L. Williams COMMITTEE ON TRANSPORT TANKS (BPV XII) M. D. Rana, Chair S. Staniszewski, Vice Chair D. R. Sharp, Staff Secretary A. N. Antoniou C. H. Hochman G. G. Karcher N. J. Paulick D. D. Brusewitz, Contributing Member J. L. Conley, Contributing Member T. Eubanks, Contributing Member T. Hitchcock, Contributing Member N. J. Paulick, Contributing Member COMMITTEE ON BOILER AND PRESSURE VESSEL CONFORMITY ASSESSMENT (CBPVCA) Working Group on General Requirements (BPV XI) R. K. Rhyne, Chair E. J. Maloney, Secretary G. P. Alexander T. L. Chan M. L. Coats E. L. Farrow B. F. Pittel M. Pitts T. Rummel R. C. Sallash S. Staniszewski L. H. Strouse Subgroup on Nonmandatory Appendices (BPV XII) Special Working Group on High-Temperature Gas-Cooled Reactors (BPV XI) J. Fletcher, Chair F. J. Schaaf, Jr., Vice Chair M. A. Lockwood, Secretary N. Broom C. Cueto-Felgueroso S. R. Doctor T. P. Lokey A. S. Olivares R. C. Sallash S. Staniszewski L. H. Strouse Subgroup on General Requirements (BPV XII) Special Working Group on Editing and Review (BPV XI) R. W. Swayne, Chair C. E. Moyer K. R. Rao N. J. Paulick M. D. Pham M. D. Rana T. A. Rogers A. Selz M. R. Ward K. Xu M. D. Pham M. Pitts T. A. Rogers A. Selz A. P. Varghese M. R. Ward xxvi V. Bogosian, Alternate D. C. Cook, Alternate R. D. Danzy, Alternate M. A. DeVries, Alternate G. L. Hollinger, Alternate D. W. King, Alternate B. L. Krasiun, Alternate P. F. Martin, Alternate K. McPhie, Alternate G. P. Milley, Alternate M. R. Minick, Alternate T. W. Norton, Alternate F. J. Pavlovicz, Alternate M. T. Roby, Alternate J. A. West, Alternate R. V. Wielgoszinski, Alternate A. J. Spencer, Honorary Member COMMITTEE ON NUCLEAR CERTIFICATION (CNC) R. R. Stevenson, Chair W. C. LaRochelle, Vice Chair P. Camurati, Staff Secretary M. N. Bressler G. Deily S. M. Goodwin K. A. Huber M. Kotb J. C. Krane R. P. McIntyre M. R. Minick H. B. Prasse T. E. Quaka D. M. Vickery C. S. Withers M. F. Sullivan, Contributing Member V. Bogosian, Alternate P. D. Edwards, Alternate D. P. Gobbi, Alternate J. W. Highlands, Alternate K. M. Hottle, Alternate K. A. Kavanagh, Alternate B. G. Kovarik, Alternate B. L. Krasiun, Alternate M. A. Lockwood, Alternate R. J. Luymes, Alternate L. M. Plante, Alternate D. W. Stepp, Alternate E. A. Whittle, Alternate H. L. Wiger, Alternate R. D. Danzy, Chair C. E. Beair J. A. Conley R. J. Doelling D. Miller T. Patel T. R. Tarbay J. A. West Subgroup on General Requirements (BPV-SVR) D. B. DeMichael, Chair J. F. Ball G. Brazier J. P. Glaspie D. K. Parrish B. F. Pittel J. W. Ramsey J. W. Richardson D. E. Tuttle S. T. French, Alternate Subgroup on Testing (BPV-SVR) COMMITTEE ON SAFETY VALVE REQUIREMENTS (BPV-SVR) J. A. West, Chair D. B. DeMichael, Vice Chair C. E. O’Brien, Staff Secretary J. F. Ball S. Cammeresi J. A. Cox R. D. Danzy R. J. Doelling J. P. Glaspie Subgroup on Design (BPV-SVR) S. F. Harrison, Jr. W. F. Hart D. Miller D. K. Parrish T. Patel D. J. Scallan T. R. Tarbay Z. Wang J. A. Cox, Chair J. E. Britt S. Cammeresi G. D. Goodson W. F. Hart B. K. Nutter D. J. Scallan C. Sharpe Z. Wang U.S. Technical Advisory Group ISO/TC 185 Safety Relief Valves T. J. Bevilacqua, Chair C. E. O’Brien, Staff Secretary J. F. Ball G. Brazier xxvii D. B. DeMichael D. Miller B. K. Nutter J. A. West SUMMARY OF CHANGES The 2011 Code, which includes Addenda changes, is being issued in its entirety. While the pages of the Code are printed in loose-leaf format for the users’ convenience, it is advisable that the existing 2010 pages be retained for reference. The next Edition of the Code will be published in 2013. A Special Notice may be posted on the ASME Web site in advance of the next edition of the Boiler and Pressure Vessel Code to provide approved revisions to Code requirements. Such revisions may be used on the date posted and will become mandatory 6 months after the date of issuance in the next edition. A Special Notice may also include a revision to a Code Case. The superseded version of the Code Case shall not be used. Errata to the BPV Code may be posted on the ASME Web site to provide corrections to incorrectly published items, or to correct typographical or grammatical errors in BPV Codes. Such errata shall be used on the date posted. Information regarding Special Notices and Errata is published on the ASME Web site under the Boiler and Pressure Vessel Code Resources Page at http://www.asme.org/kb/standards/publications/bpvc-resources. Changes in this Addenda, given below, are identified on the pages by a margin note, (a), placed next to the affected area, except that in stress tables, changes affecting the table, columns, or a large number of lines are identified by †. Revisions to the 2010 Edition are indicated by (10) or #. For the listing below, the Page references the affected area. A margin note, (a) or †, placed next to the heading indicates Location. Revisions are listed under Change. The Record Numbers listed below are explained in more detail in “List of Changes in Record Number Order” following the Summary of Changes. Page Location Change (Record Number) x, xi Foreword Tenth and fourteenth paragraphs revised xii Statement of Policy on the Use of the Certification Mark and Code Authorization in Advertising Revised Statement of Policy on the Use of ASME Marking to Identify Manufactured Items Revised xiii, xiv Submittal of Technical Inquiries to the Boiler and Pressure Vessel Committee — Mandatory Moved from Mandatory Appendix 4 and revised xv–xxvii Personnel Updated 3 2.3 Revised (10-63) 14–17 Table 1A, Line 20 For Section I and Section VIII, Division 1, Carbon steel SA/AS 1548 7-430A deleted (08-1531) Table 1A, Line 21 For I and VIII-1, for SA/AS 1548 PT430N, Grade and Group No. revised (08-1531) xxviii Page Location Change (Record Number) Table 1A, Line 22 For I and VIII-1, for SA/AS 1548 PT430NR, Grade, Condition, Size/Thickness, and Group No. revised (08-1531) Table 1A, Line 38 For I and VIII-1, SA/AS 1548 7-460A deleted (08-1531) Table 1A, Line 39 For I and VIII-1, for SA/AS 1548 PT460N, Grade and Group No. revised (08-1531) Table 1A, Line 40 For I and VIII-1, for SA/AS 1548 PT460NR, Grade, Condition, Size/Thickness, and Group No. revised (08-1531) Table 1A, Line 34 For VIII-1 and Section XII, for SA-537 Class 3, Note G21 deleted (10-825) Table 1A, Lines 42 & 43 For Sections III, VIII-1, and XII, for SA-537 Class 2 and SA-738 C, Note 21 deleted (10-825) Table 1A, Line 5 For VIII-1, SA-841 A added (09-1349) Table 1A, Lines 6–8 For I and VIII-1, SA/AS 1548 7-490A, 7-490N, and 7-490R deleted (08-1531) Table 1A, Line 26 For III, VIII-1, and XII, for SA-738 C, Note G21 deleted (10-825) Table 1A, Line 36 For VIII-1, SA-841 B added (09-1349) Table 1A, Line 39 For III, VIII-1, and XII, for SA-738 B, Note G20 deleted (10-825) Table 1A, Line 1 For III, VIII-1, and XII, for C–Mn–Si–Cb SA-737 B, Note G19 deleted (10-825) Table 1A, Line 2 For I, SA/AS 1548 5-490A deleted (08-1531) Table 1A, Line 3 (1) For I, for SA/AS 1548 PT490N, Grade revised (08-1531) (2) For VIII-1, SA/AS 1548 PT490N added (08-1531) Table 1A, Line 4 For I and VIII-1, SA/AS 1548 PT490NR added (08-1531) Table 1A, Line 5 For III, VIII-1, and XII, for C–Mn–Si–V SA-737 C, Note G20 deleted (10-825) Table 1A, Line 21 For VIII-1, for 17Cr–4Ni–3Cu SA-747 CB7Cu-1, External Pressure Chart No. revised (09-935) Table 1A, Line 22 For III and VIII-1, for 17Cr–4Ni–4Cu SA-564 630 H1150, External Pressure Chart No. revised (09-935) Table 1A, Lines 23 & 24 For III, for SA-693 630 H1150 and SA-705 630 H1150, External Pressure Chart No. revised (09-935) Table 1A, Line 25 For III and VIII-1, for SA-564 630 H1100, External Pressure Chart No. revised (09-935) Table 1A, Lines 26–30 For III, for SA-693 630 H1100 and H1075, SA-705 630 H1100 and H1075, and SA-564 630 H1075, External Pressure Chart No. revised (09-935) 70–73 Table 1A, Lines 13 & 16 For VIII-1, 16Cr–12Ni–2Mo SA-451 CPF3M and CPF8M added (10-387) 102–105 Table 1A, Lines 12–15 For VIII-1, 18Cr–10Ni–Cb SA-213 TP347LN and SA-312 TP347LN added (10-794) 146 Table 1A Notes G19, G20, and G21 deleted (10-825) 178–181 Table 1B, Line 23 For III and VIII-1, for C12200 H55 SB-359, Min. Tensile Strength, Min. Yield Strength, External Pressure Chart No., Notes, and stress values revised (10-478) 18–21 22–25 26–29 46–49 xxix Page 182–185 Location Change (Record Number) Table 1B, Line 42 For I, III, VIII-1, and XII, for C23000 H58 SB-43, Note G7 deleted (10-827) Table 1B, Line 44 For III, VIII-1, and XII, for O60 SB-135, Note G7 deleted (10-827) Table 1B, Line 1 For I, III, VIII-1, and XII, for O61 SB-43, Note G7 deleted (10-827) Table 1B, Lines 2&3 For III, VIII-1, and XII, for O61 SB-111 and SB-395, Note G7 deleted (10-827) 268–322 Table 2A Title revised (10-63) 276–278 Table 2A, Line 14 Carbon steel SA-738 B added (10-63) 288–290 Table 2A, Lines 11–19 For 17Cr–4Ni– 4Cu SA-564 630, SA-693 630, and SA-705 630, External Pressure Chart No. revised (09-935) 380–383 Table 5A, Lines 20 & 34 Carbon steel SA-841 A and B added (09-1349) 462, 463 Table U, Line 40 For Carbon steel SA/AS 1548 PT430, Grade revised (08-1531) 464, 465 Table U, Line 10 For SA/AS 1548 PT460, Grade revised (08-1531) 466, 467 Table U, Line 9 SA-841 A added (09-1349) Table U, Line 10 SA/AS 1548 7-490 deleted (08-1531) Table U, Line 38 SA-841 B added (09-1349) 468, 469 Table U, Line 11 For C–Mn–Si–Cb SA/AS 1548 PT490, Grade revised (08-1531) 496, 497 Table U, Lines 28 & 29 18Cr–10Ni–Cb SA-213 TP347LN and SA-312 TP347LN added (10-794) 510, 511 Table U, Line 22 For C12200 H55 SB-359, Min. Tensile Strength and tensile strength values revised (10-478) 540–543 Table Y-1, Lines 43– 46 For Carbon steel SA/AS 1548 PT430, Grade revised (08-1531) 544–547 Table Y-1, Lines 16, 17, 21 & 23 For SA/AS 1548 PT460, Grade revised (08-1531) 548–551 Table Y-1, Line 22 SA-841 A added (09-1349) Table Y-1, Lines 23–26 SA/AS 1548 7-490 deleted (08-1531) Table Y-1, Line 10 SA-841 B added (09-1349) Table Y-1, Lines 39–42 For C–Mn–Si–Cb SA/AS 1548 PT490, Grade revised (08-1531) 620–623 Table Y-1, Lines 6&7 18Cr–10Ni–Cb SA-213 TP347LN and SA-312 TP347LN added (10-794) 652–655 Table Y-1, Line 33 For C12200 H55 SB-359, Min. Tensile Strength, Min. Yield Strength, and yield strength values revised (10-478) 770 Fig. NFC-7 (1) Values for E deleted (07-1193) (2) General Note (b) added (07-1193) 813 Table NFC-7 Three values added for B p 7.00 (07-1193) 850 Mandatory Appendix 4 Moved to the front matter and revised 552–555 xxx LIST OF CHANGES IN RECORD NUMBER ORDER Record Number 07-1193 08-1531 09-935 09-1349 10-63 10-387 10-478 10-794 10-825 10-827 Change –Deleted E (modulus) from Fig. NFC-7. –Added General Note (b) to Fig. NFC-7. –Added tabular values for A to Table NFC-7 where B p 7.00 MPa. –Deleted Grade 7-490 for SA/AS 1548. –Deleted all other grades with “A” designation. –Corrected Group No. for Grades PT430 and PT460, to be consistent with Section IX, Table QW/QB-422. –Increased the maximum thickness for normalized rolled (NR) plates to 150 mm from 40 mm for as-rolled plates. –Changed Applicability column for Grade PT490N from NP to 538°C for Section VIII, Division 1 use. –Added Grade PT490NR for Sections I and VIII, Division 1 use. EPC reassigned from HA-7 to HT-1 for UNS S17400 in Tables 1A and 2A. Added SA-841, Grade A Class 1 and Grade B Class 2 to Tables 1A, 5A, U, and Y-1. –Added SA-738 Grade B to Table 2A. –Added the designation “MC” to the title of Table 2A. Incorporation of SA-451 J92800 (CPF3M) and J92900 (CPF8M) from Code Case 2456. –In Table 1B, revised minimum tensile strength from 205 MPa to 250 MPa and minimum yield strength from 62 MPa to 205 MPa, to be consistent with H55 temper values listed in SB-359. –Revised allowable stress values to be the same as those listed for H55 SB-111 seamless tube. –Revised the EPC to NFC-6. –Corrected the Notes in Table 1B. –Tensile and yield strength values corrected in Tables U and Y-1. Revised Tables 1A, U, and Y-1 to incorporate SA-213 TP347LN and SA-312 TP347LN, S34751. Deleted Notes G19, G20, and G21 from Table 1A. Deleted references to Note G7 in Table 1B for five C23000 stress lines. xxxi INTENTIONALLY LEFT BLANK xxxii 2011a SECTION II, PART D (METRIC) SUBPART 1 STRESS TABLES STATEMENT OF POLICY ON INFORMATION PROVIDED IN THE STRESS TABLES The purpose of this Statement of Policy is to clarify which information in the stress tables is mandatory and which is not. The information and restrictions provided in the Notes found throughout the various stress tables provided in Subpart 1 of Section II, Part D are mandatory. It is vital to recognize that lines of information in Tables 1A, 1B, 2A, 2B, 3, and 4 frequently have essential information referenced in the Notes column. These Notes are organized as follows: nature of the information, is that in Tables 1B and 2B, the UNS number information is used as the basis of the sorting scheme for materials and is almost always mandatory. Where provided, the information in the columns for Product Form, Specification Number, Type/Grade, Class/Condition/ Temper, Size/Thickness, and External Pressure Chart Number is mandatory. The information in the P-Number and Group Number columns is also mandatory; however, the primary source for this information is Table QW/QB-422 in Section IX. When there is a conflict between the P-number and Group number information in these stress tables and that in Section IX, the numbers in Section IX shall govern. The information in the Minimum Tensile Strength and Minimum Yield Strength columns is nonmandatory. These values are a primary basis for establishing the allowable stresses and design stress intensities. When there is a conflict between the tensile and yield strength values in the stress tables and those in the material specifications in Section II, Parts A and B, the values in Parts A and B shall govern. The information in the Applicability and Maximum Temperature Limits columns is mandatory. Where a material is permitted for use in more than one Construction Code, and in the SI units version of these tables, the maximum use temperature limit in these columns is critical. The temperature to which allowable stress or design stress intensity values are listed is not necessarily the temperature to which use is permitted by a particular Construction Code. Different Construction Codes often have different use temperature limits for the same material and condition. Further, in the SI units version of the stress tables, values may be listed in the table at temperatures above the maximum use temperature limit. These stress values are provided to permit interpolation to be used to determine the allowable stress or design stress intensity at temperatures between the next lowest temperature for which stress values are listed and the maximum-use temperature limit listed in these columns. (a) EXX: defining onset of values based on successful experience in service (b) GXX: general requirements (c) HXX: heat treatment requirements (d) SXX: size requirements (e) TXX: defining onset of time-dependent behavior (f) WXX: welding requirements The specifications and grades or types, coupled with the assigned Notes for each line, provide the complete description of material in the context of the allowable stresses or design stress intensities. Additional requirements for particular types of construction must also be obtained from the rules governing the construction. In Tables 1A and 2A, the information in the Nominal Composition column is nonmandatory and is for information only. However, these nominal compositions are the primary sorting used in these two tables. See Appendix A. The information in the Alloy Designation/UNS Number column is nonmandatory for specifications for which a grade or type is provided. This is primarily true for the nonstainless-steel alloys in these tables. For specifications for which no type or grade is listed, the UNS number is mandatory. Particularly for the stainless steels, for which no type or grade is listed, the UNS number is the grade. The only difference between Tables 1A and 2A, and Tables 1B and 2B, with regard to the mandatory/nonmandatory 1 2011a SECTION II, PART D (METRIC) GUIDELINE ON LOCATING MATERIALS IN STRESS TABLES, AND IN TABLES OF MECHANICAL AND PHYSICAL PROPERTIES 1 fingerprints or widely recognized designators for each alloy or alloy class. These nominal compositions are arranged in Table 1A as follows: (a) carbon steels (b) carbon steels with small additions of Cb, Ti, and V (microalloyed steels) (c) C–1⁄2Mo steels (d) chromium steels, including ferritic stainless steels, by increasing Cr content [1⁄2Cr, 3⁄4Cr, 1Cr, 11⁄4Cr, 21⁄4Cr, 3Cr, 5Cr, 9Cr, 11Cr, 12Cr, 13Cr, 15Cr, 17Cr (including 17Cr–4Ni–4Cu and 17Cr–7Ni–1Al), 18Cr, 26Cr, 27Cr, and 29Cr] (e) manganese steels (Mn–1⁄4Mo, Mn–1⁄2Mo, Mn–1⁄2Ni, and Mn–V) (f) silicon steel (11⁄2Si–1⁄2Mo) (g) nickel steels (1⁄2Ni, 3⁄4Ni, 1Ni, 11⁄4Ni, 2Ni, 21⁄2Ni, 3 2 ⁄4Ni, 3Ni, 31⁄2Ni, 4Ni, 5Ni, 8Ni, and 9Ni) (h) other high nickel steels [25Ni–15Cr–2Ti (Grade 660) and 29Ni–20Cr–3Cu–2Mo (CN7M)] (i) high alloy steels, including the duplex stainless steels, in order of increasing chromium content [beginning with 16Cr–9Mn–2Ni–N, then 16Cr–12Ni–2Mo (316L), etc.], then by increasing nickel content within a given chromium or other alloy content [18Cr–8Ni, 18Cr–8Ni– N, 18Cr–8Ni–4Si–N, 18Cr–10Ni–Cb (first S34700, then S34709, S34800, and S34809), 18Cr–10Ni–Ti, 18Cr– 11Ni, etc., ending with 25Cr–22Ni–2Mo–N]. Unfortunately, most specifications for materials do not give nominal compositions — and without that information, one may not know the nominal composition for a particular material in Table 1A. If the specification number and alloy grade or type designation are known, then one can go to Table QW/QB-422 of Section IX of the Code and find the corresponding nominal composition. Now, for a given nominal composition, Table 1A is arranged by increasing tensile strength. For a given nominal composition and tensile strength, stress listings are provided in order of increasing specification number. Sometimes, for a given nominal composition, tensile strength, yield strength, and specification number/grade or type, there may be more than one line of stresses. At this point, INTRODUCTION The goal of this Guideline is to assist the users of Section II, Part D in locating materials in stress tables (Tables 1A, 1B, 2A, 2B, 3, 4, 5A, and 5B), tables of mechanical properties (Tables U, U-2, and Y-1), and tables of physical properties (Tables TE-1 through TE-5, TCD, TM-1 through TM-5, and PRD). This Guideline defines the logic used to place materials within these tables. 2 STRESS TABLES Stress tables are all found within Subpart 1 of Section II, Part D. Tables 1A, 1B, 3, 5A, and 5B cover allowable stresses, while Tables 2A, 2B, and 4 cover design stress intensities. Although Subpart 1 also covers ultimate tensile strength and yield strength, the organization of those mechanical property tables will be discussed separately in para. 3. A table-by-table listing of the materialsorganization logic used to place materials within the designated tables follows. (10) 2.1 TABLE 1A Table 1A provides allowable stresses for ferrous1 materials used in Section I; Section III, Division 1, Classes 2 and 3; Section VIII, Division 1; and Section XII construction. Within Table 1A, the first step in ordering materials is to use their nominal compositions. These nominal compositions are nothing more than accepted compositional 1 ASME uses the current ASTM definition of ferrous alloy: an alloy whose major constituent is iron, even if the iron content is less than 50% of the total composition. However, this is a recently adopted definition and the change to specifications is occurring over time. Therefore, some alloys that were formerly defined as nonferrous are still listed in the nonferrous tables or both. 2 2011a SECTION II, PART D (METRIC) the Notes referenced on the second page of each page set within Table 1A will define why there are two or more lines of stresses and when each applies. 2.2 2.5 Table 3 provides allowable stresses for bolting materials for use in Section III, Division 1, Classes 2 and 3; Section VIII, Division 1; Section VIII, Division 2 (using Part 4.16 of Section VIII, Division 2); and Section XII construction. The table first covers ferrous materials and then nonferrous materials. For the ferrous materials, the ordering logic parallels that used in Tables 1A and 2A — first by nominal composition, then by increasing ultimate tensile strength, then by increasing yield strength, and finally by increasing specification number. Again, refer back to para. 2.1 for a discussion on nominal composition. Nonferrous materials are presented using the same logic as in Tables 1B and 2B; see para. 2.2 for that discussion. TABLE 1B Table 1B provides allowable stresses for nonferrous materials used in Section I; Section III, Division 1, Classes 2 and 3; Section VIII, Division 1; and Section XII construction. Aluminum alloys (UNS AXXXXX materials) are the first materials covered in Table 1B, followed by copper alloys (UNS CXXXXX), nickel alloys (UNS NXXXXX), and the reactive and refractory metals and alloys (UNS RXXXXX). Within this latter category there are the following: (a) chromium alloys (R2XXXX) (b) cobalt alloys (R3XXXX) (c) titanium alloys (R5XXXX) (d) zirconium alloys (R6XXXX) Within each of these material class groupings, stress lines are first organized by increasing UNS (Unified Numbering System) number. The nonferrous specifications now show these numbers in association with grade designations. Then, for a given UNS number, stress lines are next ordered by strength — first tensile strength and then yield strength. Finally, for a given UNS number, tensile strength, and yield strength, stress lines are ordered by increasing specification number. Again, some materials may have two or more stress lines even if their UNS number, tensile strength, yield strength, and specification number are the same. The Notes provide direction for the applicability of each line. For those material specifications that may not show UNS numbers associated with alloy grades, one again can refer to Section IX’s Table QW/QB-422 for that information. For Table 1B, nominal compositions are shown only for the NXXXXX and RXXXXX materials, but they have no influence on the location of alloys in the table. In this table, the nominal compositions are simply for information. (a) 2.3 2.6 TABLE 4 Table 4 provides design stress intensities for bolting materials used in Section III, Division 1, Classes 1, TC, and SC; and in Section VIII, Division 2 (using Part 5 and Annex 5.F of Section VIII, Division 2). Table 4 is organized in the same manner as Table 3 — first covering ferrous materials and then nonferrous materials — except that Table 4 covers far fewer materials. For the ordering logic, again refer to paras. 2.1 and 2.2 for ferrous and nonferrous materials, respectively. 2.7 TABLE 5A Table 5A provides allowable stresses for ferrous materials for Section VIII, Division 2 construction. This table is organized in the same manner as Table 1A. Refer back to para. 2.1 for that description. 2.8 TABLE 5B Table 5B provides allowable stresses for nonferrous materials for Section VIII, Division 2 construction. This table is organized in the same manner as Table 1B. Refer back to para. 2.2 for that description. TABLE 2A Table 2A provides design stress intensities for ferrous materials for Section III, Division 1, Classes 1, MC, TC, and SC construction. This table is organized in the same manner as Table 1A. Refer back to para. 2.1 for that description. 2.4 TABLE 3 3 MECHANICAL PROPERTY TABLES Ultimate tensile strength values and yield strength values are to be used in design calculations according to the rules of the Construction Codes. However, they are not to be construed as minimum strength values at temperature. This is explained in the General Notes to these tables. Paragraphs 3.1 through 3.3 provide a table-by-table listing of the materials-organization logic. TABLE 2B Table 2B provides design stress intensities for nonferrous materials for Section III, Division 1, Classes 1, TC, and SC construction. Table 2B materials are ordered in the same manner as in Table 1B. Refer back to para. 2.2 for that description. 3 2011a SECTION II, PART D (METRIC) 3.1 TABLE U (linear thermal expansion). This table is split into five parts as follows: (a) Table TE-1 covers numerous individual ferrous materials and ferrous material groupings. Notes at the end of Table TE-1 list the nominal compositions covered by the designated groupings. Again, knowledge of the nominal composition for a given material is essential, and it was noted previously that these can be extracted from Table QW/QB-422 of Section IX, given the specification number and grade or type designation. (b) Table TE-2 covers aluminum alloys. One set of A/B/C values covers all of the aluminum-base materials listed in General Note (a) of Table TE-2. (c) Table TE-3 covers copper alloys, currently in five general groupings: C1XXXX alloys, bronze alloys, brass alloys, 70Cu–30Ni, and 90Cu–10Ni. According to an article in ASM International’s “Advanced Materials & Processes” (December 1999), the general terms of bronze and brass cover the following alloys: (1) wrought copper-base alloys (a) C20500–C28580 — brasses (Cu–Zn) (b) C31200–C38590 — leaded brasses (Cu–Zn– Pb) (c) C40400–C49080 — tin brasses (Cu–Zn–Sn– Pb) (d) C60600–C64400 — aluminum bronzes (Cu–Al–Ni–Fe–Si–Sn) (e) C64700–C66100 — silicon bronzes (Cu–Si– Sn) (2) cast copper-base alloys (a) C83300–C85800 — red and leaded red brasses (Cu–Zn–Sn–Pb) (b) C86100–C86800 — manganese bronzes and leaded manganese bronzes (Cu–Zn–Mn–Fe–Pb) (c) C90200–C94500 — tin bronzes and leaded tin bronzes (Cu–Sn–Zn–Pb) (d) C95300–C95810 — aluminum bronzes (Cu–Al–Fe–Ni) This guidance should help define which group of A/B/C values of thermal expansion to select for a given brass or bronze. (d) Table TE-4 provides thermal expansion values for nickel alloys and refractory alloys. The thermal expansion value sets for the nickel alloys are arranged by increasing UNS NXXXXX numbers. (e) Table TE-5 provides thermal expansion values for two groupings of titanium-base alloys. One group covers only Grade 9; the other group covers the other alloys. In this table, there is no reference to the UNS number, just to the grade number. Table U provides tensile strength values for ferrous and nonferrous materials, in that order. The ordering logic for ferrous materials is the same as used in Table 1A, except yield strength level is not shown. Using the logic described in para. 2.1, stress lines are organized by nominal composition, then by increasing tensile strength level, and then by increasing specification number. Nonferrous materials coverage begins following the last of the high alloy steels (25Cr–22Ni–2Mo–N). Coverage of nonferrous alloys begins with the UNS CXXXXX alloys, followed by NXXXXX and RXXXXX alloys. No tensile strength values are available at this time for the aluminum alloys. The ordering of materials within these three groups has been previously described in para. 2.2. 3.2 TABLE U-2 Table U-2 provides ultimate tensile strengths for special ferrous materials used in Section VIII, Division 3 construction. The only material covered is wire produced to either SA-231 or SA-232, and lines are arranged in order of decreasing tensile strength, resulting from increasing wire diameter. 3.3 TABLE Y-1 Table Y-1 provides yield strength values for ferrous and nonferrous materials, in that order. Again, the ordering of yield strength lines parallels the logic described for ferrous and nonferrous materials in paras. 2.1 and 2.2, respectively. Unlike Table U, for ferrous materials, the tensile strength level does enter into the ordering process, again following nominal composition designation. And, unlike Table U, Table Y-1’s nonferrous materials listings do begin with the aluminum-base alloys (UNS AXXXXX). These are followed by the copper materials (CXXXXX), nickel-base materials (NXXXXX), and the reactive and refractory metals and alloys (RXXXXX). 4 PHYSICAL PROPERTY TABLES Since physical properties (thermal conductivity, thermal diffusivity, thermal expansion, and density), Young’s modulus, and Poisson’s ratio values can be shown for numerous materials with a single set of property values, most of the tables found in Subpart 2 of Section II, Part D are based on nominal composition. Paragraphs 4.1 through 4.4 describe how these tables are organized. 4.1 TABLE TE 4.2 Table TE covers thermal expansion behavior, presented in terms of A (instantaneous coefficient of thermal expansion), B (mean coefficient of thermal expansion), and C TABLE TCD Table TCD provides both thermal conductivity (TC) and thermal diffusivity (TD) values for numerous ferrous and 4 2011a SECTION II, PART D (METRIC) nonferrous materials and material groupings. The table begins with ferrous materials, split into groups of carbon and low alloy steels, followed by groups of high chromium steels and groups of high alloy steels. For each of these groups, there is a listing of nominal composition designations found at the end of the table, defining the extent of coverage. The next series of materials are the nickel-base alloys, covered by TC/TD listings for nickel alloys (arranged by increasing UNS number) and refractory alloys. Then there are TC/TD listings for individual titanium and aluminum alloys (arranged by increasing UNS number). Table TCD does not currently provide values for copper or zirconium alloys. 4.3 (e) Table TM-5 covers titanium alloys, listed by increasing grade numbers, and zirconium-base alloys, listed by increasing UNS number (or grade) designation. 4.4 TABLE PRD Table PRD provides Poisson’s ratio and density for ferrous and nonferrous alloys. 5 REFERENCES The official reference for UNS numbers is Metals & Alloys in the Unified Numbering System, ASTM DS-56. This document is periodically updated as various material specifications are revised, added, or deleted by their sponsoring organizations. Only UNS numbers published in this reference appear in Section II, Part A and Part B specifications, and in the various Section II, Part D stress tables, mechanical property tables, and physical property tables. Nominal compositions are defined by various groups within the ASME Code committee structure and there are no published guidelines describing how these designations are developed. These designations have the greatest relevance in the arrangement of ferrous materials and, as indicated previously, the simplest way to obtain these designations is to look in Section IX of the ASME Boiler and Pressure Vessel Code and use Table QW/QB-422, which is arranged by increasing specification number. These start with the “SA” specification numbers, followed by the “SB” numbers. TABLE TM Table TM provides moduli of elasticity for five categories of materials, as follows: (a) Table TM-1 covers ferrous materials in nine general categories and with additional lines for specific materials. Groups A through G are subdivided by nominal composition; see the Notes at the end of Table TM-1. (b) Table TM-2 covers aluminum alloys, listed by UNS number designation. (c) Table TM-3 covers copper alloys, listed by UNS number designation. (d) Table TM-4 covers nickel alloys, listed by UNS number designation. 5 2011a SECTION II, PART D (METRIC) TABLE 1A SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 Carbon steel Carbon steel Carbon steel Sheet Sheet Bar SA-1008 SA-1008 SA-675 CS-A CS-B 45 … … … … … … … … … 1 1 1 1 1 1 4 5 6 7 8 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Wld. pipe Plate Plate Wld. pipe Sheet SA-134 SA-283 SA-285 SA-672 SA-414 A283A A A A45 A … … K01700 K01700 K01501 … … … … … … … … … … 1 1 1 1 1 1 1 1 1 1 9 10 11 Carbon steel Carbon steel Carbon steel Wld. tube Wld. tube Smls. tube SA-178 SA-178 SA-179 A A … K01200 K01200 K01200 … … … … … … 1 1 1 1 1 1 12 13 14 15 Carbon steel Carbon steel Carbon steel Carbon steel Smls. tube Wld. tube Smls. tube Wld. tube SA-192 SA-214 SA-556 SA-557 … … A2 A2 K01201 K01807 K01807 K01807 … … … … … … … … 1 1 1 1 1 1 1 1 16 17 18 19 20 21 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Wld. pipe Wld. pipe Wld. pipe Wld. pipe Smls. pipe Smls. pipe SA-53 SA-53 SA-53 SA-53 SA-53 SA-53 E/A E/A E/A F/A S/A S/A K02504 K02504 K02504 … K02504 K02504 … … … … … … … … … … … … 1 1 1 1 1 1 1 1 1 1 1 1 22 23 24 25 26 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Smls. pipe Wld. pipe Forged pipe Wld. pipe Wld. pipe SA-106 SA-135 SA-369 SA-587 SA-587 A A FPA … … K02501 … K02501 K11500 K11500 … … … … … … … … … … 1 1 1 1 1 1 1 1 1 1 27 28 29 30 Carbon steel Carbon steel Carbon steel Carbon steel Bar Bar Wld. pipe Plate SA-675 SA-675 SA-134 SA-283 50 50 A283B B … … … … … … … … … … … … 1 1 1 1 1 1 1 1 31 32 33 Carbon steel Carbon steel Carbon steel Plate Plate Wld. pipe SA-285 SA-285 SA-672 B B A50 K02200 K02200 K02200 … … … … … … 1 1 1 1 1 1 34 35 36 37 38 39 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Sheet Plate Plate Plate Bar Bar SA-414 SA/EN 10028-3 SA/EN 10028-3 SA/EN 10028-3 SA-675 SA-675 B P275NH P275NH P275NH 55 55 K02201 … … … … … … … … … … … … 150 < t ≤ 250 100 < t ≤ 150 50 < t ≤ 100 … … 1 1 1 1 1 1 1 1 1 1 1 1 40 41 42 Carbon steel Carbon steel Carbon steel Wld. pipe Plate Plate SA-134 SA-283 SA-285 A283C C C K02401 K02401 K02801 … … … … … … 1 1 1 1 1 1 Line No. (10) (10) (10) 6 2011a SECTION II, PART D (METRIC) TABLE 1A SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 275 275 310 140 140 155 NP NP NP NP NP 343 (Cl. 3 only) 343 343 482 NP NP 343 CS-6 CS-6 CS-6 … … G10, G22, T10 4 5 6 7 8 310 310 310 310 310 165 165 165 165 170 NP NP 482 NP NP 149 (Cl. 3 only) 149 (Cl. 3 only) 371 371 NP NP 343 482 NP 482 NP 343 343 NP 343 CS-1 CS-1 CS-1 CS-1 CS-1 W12 … G10, T2 S6, W10, W12 G10, T2 9 10 11 325 325 325 180 180 180 538 538 NP NP NP NP NP 538 482 NP 343 343 CS-1 CS-1 CS-1 G4, G10, S1, T2, W13 G3, G10, G24, S1, T2, W6 G10, T2 12 13 14 15 325 325 325 325 180 180 180 180 538 NP NP NP NP NP NP NP 538 538 538 538 343 343 343 343 CS-1 CS-1 CS-1 CS-1 G10, S1, T2 G24, T2, W6 G10, T2 G24, T2, W6 16 17 18 19 20 21 330 330 330 330 330 330 205 205 205 205 205 205 482 482 NP 399 482 NP NP 149 (Cl. 3 only) NP NP 149 (Cl. 3 only) 371 (SPT) NP NP 482 NP NP 482 NP NP 343 NP NP 343 CS-2 CS-2 CS-2 CS-2 CS-2 CS-2 G3, G10, S1, T2 G10, S1, T2, W12, W13 G24, T2, W6 G2, G10, S10, T2, W15 G10, S1, T2 G10, T2 22 23 24 25 26 330 330 330 330 330 205 205 205 205 205 538 NP 538 NP NP 371 NP NP 149 (Cl. 3 only) NP 538 482 NP NP 454 343 343 NP NP 343 CS-2 CS-2 CS-2 CS-2 CS-2 G10, S1, T1 G24, T2, W6 G10, S1, T1 … G24, T2, W6 27 28 29 30 345 345 345 345 170 170 185 185 NP 454 NP NP 343 (Cl. 3 only) 371 (SPT) 149 (Cl. 3 only) 149 (Cl. 3 only) NP 482 NP 343 NP 343 NP 343 CS-1 CS-1 CS-1 CS-1 … G10, G15, G22, S1, T2 W12 … 31 32 33 345 345 345 185 185 185 482 NP NP NP 371 371 NP 482 NP NP 343 NP CS-1 CS-1 CS-1 G10, S1, T1 G10, T1 S6, T1, W10, W12 34 35 36 37 38 39 345 350 360 370 380 380 205 215 225 235 190 190 NP NP NP NP 454 NP NP NP NP NP 371 (SPT) 343 (Cl. 3 only) 482 204 204 204 482 NP 343 NP NP NP 343 NP CS-2 CS-2 CS-2 CS-2 CS-1 CS-1 G10, T1 G10 G10 G10 G10, G15, G22, S1, T2 … 40 41 42 380 380 380 205 205 205 NP NP 482 149 (Cl. 3 only) 149 (Cl. 3 only) 371 NP 343 482 NP 343 343 CS-2 CS-2 CS-2 W12 … G10, S1, T2 7 (10) (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1A SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (10) (10) (10) Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 78.6 78.6 88.9 78.6 78.6 88.9 78.6 78.6 88.9 78.6 78.6 88.9 78.6 78.6 88.9 78.6 78.6 88.4 76.0 76.0 85.0 71.6 71.6 80.7 69.6 69.6 78.4 67.8 67.8 75.8 … … 73.5 … … 71.5 … … 64.0 … … 56.1 … … 44.5 4 5 6 7 8 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 … 88.9 88.9 88.9 88.9 … 88.9 88.9 88.9 88.9 … 86.3 86.3 86.3 88.5 … 83.8 83.8 83.8 87.5 … 81.4 81.4 81.4 84.8 … … 78.8 78.8 81.2 … … 73.4 … 73.4 … … 64.0 … 64.0 … … 56.1 … 56.1 … … 44.5 … 44.5 9 10 11 92.4 78.6 92.4 92.4 78.6 92.4 92.4 78.6 92.4 92.4 78.6 92.4 92.4 78.6 92.4 92.4 78.6 92.4 92.4 78.6 92.4 91.9 78.1 91.9 90.7 77.1 90.7 87.8 74.7 87.8 84.3 71.4 84.3 73.3 62.3 73.3 63.9 54.2 63.9 56.2 47.6 56.2 44.5 37.7 44.5 12 13 14 15 92.4 78.6 92.4 78.6 92.4 78.6 92.4 78.6 92.4 78.6 92.4 78.6 92.4 78.6 92.4 78.6 92.4 78.6 92.4 78.6 92.4 78.6 92.4 78.6 92.4 78.6 92.4 78.6 91.9 78.1 91.9 78.1 90.7 77.1 90.7 77.1 87.8 74.7 87.8 74.7 84.3 71.4 84.3 71.4 73.3 62.3 73.3 62.3 63.9 54.2 63.9 54.2 56.2 47.6 56.2 47.6 44.5 37.7 44.5 37.7 16 17 18 19 20 21 80.7 94.5 80.7 56.5 94.5 94.5 80.7 94.5 80.7 56.5 94.5 94.5 80.7 94.5 80.7 56.5 94.5 94.5 80.7 94.5 80.7 56.5 94.5 94.5 80.7 94.5 80.7 56.5 94.5 94.5 80.7 94.5 80.7 56.5 94.5 94.5 80.7 94.5 80.7 56.5 94.5 94.5 80.7 94.5 80.7 56.5 94.5 94.5 80.7 94.5 80.7 56.5 94.5 94.5 79.8 93.5 79.8 56.0 93.5 93.6 71.6 84.5 71.6 50.7 84.5 84.4 62.3 73.3 62.4 43.8 73.3 73.3 53.7 62.8 54.9 … 62.8 64.7 43.9 51.2 47.5 … 51.2 56.0 32.9 38.3 40.1 … 38.3 47.6 22 23 24 25 26 94.5 80.7 94.5 94.5 80.7 94.5 80.7 94.5 94.5 80.7 94.5 80.7 94.5 94.5 80.7 94.5 80.7 94.5 94.5 80.7 94.5 80.7 94.5 94.5 80.7 94.5 80.7 94.5 … 80.7 94.5 80.7 94.5 … 80.7 94.5 80.7 94.5 … 80.7 94.5 80.7 94.5 … 80.7 93.6 79.8 93.5 … 79.8 84.4 71.6 84.5 … 71.6 73.3 62.4 73.3 … 62.4 64.7 54.9 62.8 … 54.9 56.0 47.5 51.2 … 47.5 47.6 40.1 38.3 … 40.1 27 28 29 30 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.1 98.1 … 98.6 94.7 94.7 … 98.6 89.8 89.8 … 96.6 87.3 87.3 … 94.1 84.9 84.9 … 90.6 … 81.2 … … … 73.4 … … … 64.7 … … … 56.0 … … … 47.3 … … 31 32 33 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 98.6 96.6 96.6 96.6 94.1 94.1 94.1 90.7 90.6 90.6 85.0 85.1 85.1 75.4 76.8 … 65.6 66.8 … 52.8 57.8 … 38.6 44.9 … 34 35 36 37 38 39 98.6 100 103 105 108 108 98.6 100 103 105 108 108 98.6 100 103 105 108 108 98.6 100 103 105 108 108 98.6 100 103 105 108 108 98.6 100 103 105 108 108 98.6 … … … 104 104 98.6 … … … 98.8 98.8 98.6 … … … 96.1 96.1 96.9 … … … 92.9 92.9 84.5 … … … 89.9 … 76.8 … … … 87.3 … 66.8 … … … 75.4 … 57.7 … … … 62.5 … 44.9 … … … 46.0 … 40 41 42 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 … 108 108 … 108 108 … 107 107 … 104 104 … 101 101 … … 97.8 … … 89.1 … … 75.4 … … 62.6 … … 45.5 8 2011a SECTION II, PART D (METRIC) TABLE 1A SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 … … 31.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 4 5 6 7 8 … … 31.7 … 31.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 10 11 31.9 27.1 31.9 21.8 18.5 … 12.7 10.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 12 13 14 15 31.9 27.1 31.9 27.1 21.8 18.5 21.8 18.5 12.7 10.6 12.7 10.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 20 21 21.7 25.3 32.6 … 25.3 36.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 25 26 36.2 32.6 25.3 … … 23.5 … 14.9 … … 11.2 … 5.88 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 27 28 29 30 … 38.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 24.3 30.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 37 38 39 30.9 … … … 28.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 40 41 42 … … 31.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 (10) (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 Carbon steel Carbon steel Carbon steel Smls. & wld. pipe Smls. & wld. tube Wld. tube SA-333 SA-334 SA-334 1 1 1 K03008 K03008 K03008 … … … … … … 1 1 1 1 1 1 4 5 6 7 Carbon steel Carbon steel Carbon steel Carbon steel Plate Smls. pipe Wld. pipe Wld. pipe SA-516 SA-524 SA-671 SA-671 55 II CA55 CE55 K01800 K02104 K02801 K02202 … … … … … … … … 1 1 1 1 1 1 1 1 8 9 10 11 12 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Wld. pipe Wld. pipe Wld. pipe Wld. pipe Sheet SA-672 SA-672 SA-672 SA-672 SA-414 A55 B55 C55 E55 C K02801 K02001 K01800 K02202 K02503 … … … … … … … … … … 1 1 1 1 1 1 1 1 1 1 13 14 15 16 Carbon steel Carbon steel Carbon steel Carbon steel Plate Bar Plate, sheet Plate, sheet SA/EN 10028-3 SA-36 SA-36 SA-662 P275NH … … A … K02600 K02600 K01701 … … … … ≤ 50 … … … 1 1 1 1 1 1 1 1 17 18 19 20 21 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Forgings Castings Forgings Forgings Castings SA-181 SA-216 SA-266 SA-350 SA-352 … WCA 1 LF1 LCA K03502 J02502 K03506 K03009 J02504 60 … … 1 … … … … … … 1 1 1 1 1 1 1 1 1 1 22 23 24 25 Carbon steel Carbon steel Carbon steel Carbon steel Cast pipe Bar Bar Forgings SA-660 SA-675 SA-675 SA-765 WCA 60 60 I J02504 … … K03046 … … … … … … … … 1 1 1 1 1 1 1 1 26 27 28 29 30 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Plate Plate Wld. pipe Wld. pipe Wld. pipe SA-515 SA-516 SA-671 SA-671 SA-671 60 60 CB60 CC60 CE60 K02401 K02100 K02401 K02100 K02402 … … … … … … … … … … 1 1 1 1 1 1 1 1 1 1 31 32 33 34 35 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Wld. pipe Wld. pipe Wld. pipe Wld. pipe Plate SA-672 SA-672 SA-672 SA-134 SA-283 B60 C60 E60 A283D D K02401 K02100 K02402 K02702 K02702 … … … … … … … … … … 1 1 1 1 1 1 1 1 1 1 36 37 38 39 Carbon steel Carbon steel Carbon steel Carbon steel Wld. pipe Wld. pipe Smls. pipe Smls. pipe SA-53 SA-53 SA-53 SA-53 E/B E/B S/B S/B K03005 K03005 K03005 K03005 … … … … … … … … 1 1 1 1 1 1 1 1 40 41 42 Carbon steel Carbon steel Carbon steel Smls. pipe SA-106 Wld. pipe SA-135 Smls. & wld. fittings SA-234 B B WPB K03006 … K03006 … … … … … … 1 1 1 1 1 1 Line No. 10 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 380 380 380 205 205 205 NP NP NP 371 371 NP 343 343 343 343 343 343 CS-2 CS-2 CS-2 W12, W14 W12, W14 G24, W6 4 5 6 7 380 380 380 380 205 205 205 205 454 NP NP NP 371 NP 371 371 538 538 NP NP 343 343 NP NP CS-2 CS-2 CS-2 CS-2 G10, S1, T2 G10, T2 S6, W10, W12 S6, W10, W12 8 9 10 11 12 380 380 380 380 380 205 205 205 205 230 NP NP NP NP NP 371 371 371 371 371 NP NP NP NP 482 NP NP NP NP 343 CS-2 CS-2 CS-2 CS-2 CS-2 S6, W10, W12 S6, W10, W12 S6, W10, W12 S6, W10, W12 G10, T1 13 14 15 16 390 400 400 400 265 250 250 275 NP 343 NP NP NP 343 (SPT) 371 NP 204 482 343 371 204 343 343 343 CS-2 CS-2 CS-2 CS-2 G10 G10, G15, T1 G9, G10, T1 T1 17 18 19 20 21 415 415 415 415 415 205 205 205 205 205 538 538 538 NP NP 371 371 371 371 371 538 538 538 538 NP 343 343 343 343 NP CS-2 CS-2 CS-2 CS-2 CS-2 G10, S1, T2 G1, G10, G17, S1, T2 G10, S1, T2 G10, T2 G17 22 23 24 25 415 415 415 415 205 205 205 205 538 454 NP NP 371 371 (SPT) 343 (Cl. 3 only) NP NP NP 482 538 NP NP 343 343 CS-2 CS-2 CS-2 CS-2 G1, G10, G17, S1, T2 G10, G15, S1, T2 G10, G22, T2 G10, T2 26 27 28 29 30 415 415 415 415 415 220 220 220 220 220 538 454 NP NP NP 371 371 371 371 371 538 538 NP NP NP 343 343 NP NP NP CS-2 CS-2 CS-2 CS-2 CS-2 G10, S1, T2 G10, S1, T2 S6, W10, W12 S6, W10, W12 S6, W10, W12 31 32 33 34 35 415 415 415 415 415 220 220 220 230 230 NP NP NP NP NP 371 371 371 149 (Cl. 3 only) 149 (Cl. 3 only) NP NP NP NP 343 NP NP NP NP 343 CS-2 CS-2 CS-2 CS-2 CS-2 S6, W10, W12 S6, W10, W12 S6, W10, W12 W12 … 36 37 38 39 415 415 415 415 240 240 240 240 482 482 482 NP 149 (Cl. 3 only) NP 149 (Cl. 3 only) 371 (SPT) NP 482 NP 482 NP 343 NP 343 CS-2 CS-2 CS-2 CS-2 G10, S1, T1, W12, W13 G3, G10, G24, S1, T1, W6 G10, S1, T1 G10, T1 40 41 42 415 415 415 240 240 240 538 NP 538 371 NP 371 538 482 538 343 343 343 CS-2 CS-2 CS-2 G10, S1, T1 G24, T1, W6 G10, S1, T1 11 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 108 108 92.4 108 108 92.4 108 108 92.4 108 108 92.4 108 108 92.4 108 108 92.4 108 108 92.4 107 107 90.8 104 104 88.7 101 101 86.2 97.8 97.8 … … … … … … … … … … … … … 4 5 6 7 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 107 107 107 107 104 104 104 104 101 101 101 101 97.8 97.8 97.8 97.8 89.1 89.1 … … 75.4 75.4 … … 62.6 62.6 … … 45.5 45.5 … … 8 9 10 11 12 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 107 107 107 107 108 104 104 104 104 108 101 101 101 101 108 97.8 97.8 97.8 97.8 106 … … … … 88.8 … … … … 75.2 … … … … 62.6 … … … … 45.9 13 14 15 16 111 114 114 114 111 114 114 114 111 114 114 114 111 114 114 114 111 114 114 114 111 114 114 114 … 114 114 114 … 114 114 114 … 114 114 114 … 114 114 114 … 105 105 105 … 88.9 … … … 75.3 … … … 62.6 … … … 45.9 … … 17 18 19 20 21 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 114 114 114 114 114 107 107 107 107 107 104 104 104 104 104 101 101 101 101 101 97.8 97.8 97.8 97.8 97.8 89.1 89.1 89.1 89.1 … 75.4 75.4 75.4 75.4 … 62.6 62.6 62.6 62.6 … 45.5 45.5 45.5 45.5 … 22 23 24 25 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 114 114 114 114 107 107 107 107 104 104 104 104 101 101 101 101 97.8 97.8 97.8 97.8 89.1 89.1 89.1 89.1 75.4 75.4 75.4 75.4 62.6 62.6 62.6 62.6 45.5 45.5 45.5 45.5 26 27 28 29 30 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 115 115 115 115 115 112 112 112 112 112 108 108 108 108 108 104 104 104 104 104 88.9 88.9 … … … 75.3 75.3 … … … 62.7 62.7 … … … 45.5 45.5 … … … 31 32 33 34 35 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 … 118 118 118 118 … 118 115 115 115 … 118 112 112 112 … 115 108 108 108 … 111 104 104 104 … … … … … … … … … … … … … … … … … … … … … … 36 37 38 39 118 101 118 118 118 101 118 118 118 101 118 118 118 101 118 118 118 101 118 118 118 101 118 118 118 101 118 118 118 101 118 118 118 101 118 118 117 99.7 117 117 105 89.7 105 105 88.9 75.9 88.9 88.9 75.3 64.1 75.3 75.3 62.7 53.3 62.7 62.7 45.5 38.6 45.5 45.5 40 41 42 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 117 99.7 117 105 89.7 105 88.9 75.9 88.9 75.3 64.1 75.3 62.7 53.3 62.7 45.5 38.6 45.5 12 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 4 5 6 7 31.6 31.6 … … 21.9 21.9 … … 12.7 12.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 8 9 10 11 12 … … … … 28.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 13 14 15 16 … 28.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 17 18 19 20 21 31.6 31.6 31.6 31.6 … 21.9 21.9 21.9 21.9 … 12.7 12.7 12.7 12.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 25 31.6 … 31.6 31.6 21.9 … … 21.9 12.7 … … 12.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 26 27 28 29 30 31.6 31.6 … … … 21.9 21.9 … … … 12.7 12.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 34 35 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 36 37 38 39 31.6 26.8 31.6 31.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 40 41 42 31.6 26.8 31.6 21.9 … 21.9 12.7 … 12.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 13 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 Carbon steel Carbon steel Carbon steel Carbon steel Smls. & wld. pipe Wld. pipe Smls. & wld. tube Wld. tube SA-333 SA-333 SA-334 SA-334 6 6 6 6 K03006 K03006 K03006 K03006 … … … … … … … … 1 1 1 1 1 1 1 1 5 6 7 8 Carbon steel Carbon steel Carbon steel Carbon steel Forged pipe Forgings Sheet Smls. & wld. fittings SA-369 SA-372 SA-414 SA-420 FPB A D WPL6 K03006 K03002 K02505 … … … … … … … … … 1 1 1 1 1 1 1 1 9 10 11 12 Carbon steel Carbon steel Carbon steel Carbon steel Smls. pipe Bar Bar Forgings SA-524 SA-695 SA-696 SA-727 I B/35 B … K02104 K03504 K03200 K02506 … … … … … … … … 1 1 1 1 1 1 1 1 13 14 15 Carbon steel Carbon steel Carbon steel Wld. tube Wld. tube Wld. tube SA-178 SA-178 SA-178 C C C K03503 K03503 K03503 … … … … … … 1 1 1 1 1 1 16 17 18 19 Carbon steel Carbon steel Carbon steel Carbon steel Smls. tube Smls. tube Wld. tube Plate, bar SA-210 SA-556 SA-557 SA/CSA-G40.21 A-1 B2 B2 38W K02707 K02707 K03007 … … … … … … … … … 1 1 1 1 1 1 1 1 20 21 22 23 24 25 … Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel … Plate Plate Plate Plate Bar … SA/AS 1548 SA/AS 1548 SA/EN 10028-2 SA/EN 10028-2 SA-675 … PT430N PT430NR P295GH P295GH 65 … … … … … … … Normalized Norm. rld. … … … … ≤ 150 ≤ 150 150 < t ≤ 250 100 < t ≤ 150 … … 1 1 1 1 1 … 1 1 1 1 1 26 27 28 Carbon steel Carbon steel Carbon steel Castings Plate Plate SA-352 SA-515 SA-516 LCB 65 65 J03003 K02800 K02403 … … … … … … 1 1 1 1 1 1 29 30 31 32 Carbon steel Carbon steel Carbon steel Carbon steel Wld. pipe Wld. pipe Wld. pipe Wld. pipe SA-671 SA-671 SA-672 SA-672 CB65 CC65 B65 C65 K02800 K02403 K02800 K02403 … … … … … … … … 1 1 1 1 1 1 1 1 33 34 35 36 37 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Sheet Plate Plate Plate Wld. pipe SA-414 SA-662 SA/GB 6654 SA-537 SA-691 E B 16MnR … CMSH-70 K02704 K02203 … K12437 K12437 … … … 1 … … … 100 < t ≤ 120 64 < t ≤ 100 64 < t ≤ 100 1 1 1 1 1 1 1 1 2 2 38 39 40 41 42 … Carbon steel Carbon steel Carbon steel Carbon steel … Plate Plate Plate Plate … SA/AS 1548 SA/AS 1548 SA/EN 10028-2 SA/EN 10028-2 … PT460N PT460NR P295GH P295GH … … … … … … Normalized Norm. rld. … … … ≤ 150 ≤ 150 60 < t ≤ 100 ≤ 60 … 1 1 1 1 … 1 1 1 1 Line No. (a) (a) (a) (a) (a) (a) 14 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 415 415 415 415 240 240 240 240 371 371 NP NP 371 NP 371 NP 538 NP 343 343 343 NP 343 343 CS-2 CS-2 CS-2 CS-2 G10, T1, W12, W13, W14 T1 T1, W12, W14 G24, W6 5 6 7 8 415 415 415 415 240 240 240 240 538 NP NP NP NP NP NP 371 NP 343 482 454 NP 343 343 343 CS-2 CS-2 CS-2 CS-2 G10, S1, T1 … G10, T1 G10, T1, W14 9 10 11 12 415 415 415 415 240 240 240 250 NP NP NP NP NP 371 371 371 538 538 NP 538 343 343 NP 343 CS-2 CS-2 CS-2 CS-2 G10, T1 G10, G22, T1 T1 G10, G22, T1 13 14 15 415 415 415 255 255 255 538 538 538 NP 371 NP NP NP 538 NP NP 343 CS-2 CS-2 CS-2 G4, G10, S1, T2 G10, S1, T1, W13 G3, G10, G24, S1, T2, W6 16 17 18 19 415 415 415 415 255 255 255 260 538 NP NP NP 371 NP NP NP 538 538 538 343 343 343 343 343 CS-2 CS-2 CS-2 CS-2 G10, S1, T1 G10, T1 G24, T1, W6 … 20 21 22 23 24 25 … 430 430 430 440 450 … … … 220 235 225 … 538 538 454 454 454 … NP NP NP NP 343 (Cl. 3 only) … 538 538 538 538 538 … NP NP NP NP 343 … CS-2 CS-2 CS-2 CS-2 CS-2 … G10, G18, S1, T1 G10, G18, S1, T1 G10, S1, T2 G10, S1, T2 G10, G15, G22, S1, T2 26 27 28 450 450 450 240 240 240 NP 538 454 371 371 371 343 538 538 343 343 343 CS-2 CS-2 CS-2 G1, G17 G10, S1, T2 G10, S1, T2 29 30 31 32 450 450 450 450 240 240 240 240 NP NP NP NP 371 371 371 371 NP NP NP NP NP NP NP NP CS-2 CS-2 CS-2 CS-2 S6, W10, W12 S6, W10, W12 S6, W10, W12 S6, W10, W12 33 34 35 36 37 450 450 450 450 450 260 275 275 310 310 NP NP NP NP NP NP NP NP 371 371 482 371 250 343 NP 343 343 NP 343 NP CS-2 CS-2 CS-2 CS-2 CS-2 G10, T1 T1 … T1 G26, T1, W10, W12 38 39 40 41 42 … 460 460 460 460 … … … 260 … … 538 538 454 454 … NP NP NP NP … 538 538 538 538 … NP NP NP 343 … CS-2 CS-2 CS-2 CS-2 … G10, G18, S1, T1 G10, G18, S1, T1 G10, S1, T1 G10, G18, S1, T1 15 (a) (a) (a) (a) (a) (a) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (a) (a) (a) (a) (a) (a) Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 118 101 118 101 118 101 118 101 118 101 118 101 118 101 118 101 118 101 118 101 118 101 118 101 118 101 118 101 118 101 118 101 118 101 118 101 117 99.7 117 101 105 89.7 105 … 88.9 … … … 75.3 … … … 62.7 … … … 45.5 … … … 5 6 7 8 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 117 118 117 117 105 … 105 105 88.9 … 88.9 88.9 75.3 … 75.3 75.3 62.7 … 62.7 62.7 45.5 … 45.5 45.5 9 10 11 12 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 117 117 117 117 105 105 105 105 88.9 88.9 … 88.9 75.3 75.3 … 75.3 62.7 62.7 … 62.7 45.5 45.5 … 45.5 13 14 15 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 117 117 99.7 105 105 89.7 88.9 88.9 75.9 75.2 75.3 64.1 63.2 62.7 53.3 40.5 45.5 38.6 16 17 18 19 118 118 101 118 118 118 101 118 118 118 101 118 118 118 101 118 118 118 101 118 118 118 101 118 118 118 101 118 118 118 101 118 118 118 101 118 117 117 99.7 118 105 105 89.7 … 88.9 88.9 75.9 … 75.3 75.3 64.1 … 62.7 62.7 53.3 … 45.5 45.5 38.6 … 20 21 22 23 24 25 … 123 123 123 126 128 … 123 123 123 126 128 … 123 123 123 126 128 … 123 123 123 126 128 … 123 123 123 126 128 … 123 123 123 126 128 … 123 123 121 126 123 … 123 123 114 122 117 … 123 123 111 119 113 … 123 123 108 115 110 … 114 114 105 112 106 … 95.0 95.0 96.2 96.2 95.2 … 79.6 79.6 79.1 79.1 79.6 … 63.2 63.2 62.1 62.1 63.8 … 45.3 45.3 46.0 46.0 39.2 26 27 28 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 125 125 125 122 122 122 118 118 118 114 114 114 … 95.0 95.0 … 79.6 79.6 … 63.2 63.2 … 45.3 45.3 29 30 31 32 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 125 125 125 125 122 122 122 122 118 118 118 118 114 114 114 114 … … … … … … … … … … … … … … … … 33 34 35 36 37 128 128 129 128 128 128 128 129 128 128 128 128 129 128 128 128 128 129 128 128 128 128 129 128 128 128 128 129 128 128 128 128 129 128 128 128 128 129 128 128 128 128 … 128 128 127 127 … 127 127 114 114 … 114 114 95.1 … … … … 79.6 … … … … 63.1 … … … … 45.7 … … … … 38 39 40 41 42 … 131 131 131 131 … 131 131 131 131 … 131 131 131 131 … 131 131 131 131 … 131 131 131 131 … 131 131 131 131 … 131 131 131 131 … 131 131 131 131 … 131 131 131 131 … 129 129 127 127 … 114 114 112 112 … 95.1 95.1 96.2 96.2 … 79.6 79.6 79.1 79.1 … 63.2 63.2 62.1 62.1 … 45.3 45.3 46.0 46.0 16 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 31.6 … … … 21.9 … … … 12.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 31.6 … 31.6 … 21.9 … … … 12.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 10 11 12 31.6 31.6 … 31.6 21.9 21.9 … 21.9 12.7 12.7 … 12.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 13 14 15 26.2 31.6 26.8 18.8 21.9 18.6 10.5 12.7 10.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 31.6 31.6 26.8 … 21.9 21.9 18.6 … 12.7 12.7 10.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 23 24 25 … 31.7 31.7 32.1 32.1 30.1 … 21.9 21.9 21.2 21.2 22.4 … 12.7 12.7 14.4 14.4 12.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 26 27 28 … 31.7 31.7 … 21.9 21.9 … 12.7 12.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 30 31 32 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 33 34 35 36 37 28.3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 38 39 40 41 42 … 31.7 31.7 32.1 32.1 … 21.9 21.9 21.2 21.2 … 12.7 12.7 14.4 14.4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 17 (a) (a) (a) (a) (a) (a) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 Carbon steel Carbon steel Carbon steel Carbon steel Plate Plate Plate Bar SA/GB 6654 SA/GB 6654 SA-455 SA-675 16MnR 16MnR … 70 … … K03300 … … … … … 60 < t ≤ 100 36 < t ≤ 60 15 < t ≤ 19 … 1 1 1 1 1 1 2 2 5 6 7 8 9 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Forgings Forgings Castings Forgings Forgings SA-105 SA-181 SA-216 SA-266 SA-266 … … WCB 2 4 K03504 K03502 J03002 K03506 K03017 … 70 … … … … … … … … 1 1 1 1 1 2 2 2 2 2 10 11 12 13 Carbon steel Carbon steel Carbon steel Carbon steel Forgings Forgings Forgings Forgings SA-350 SA-350 SA-508 SA-508 LF2 LF2 1 1A K03011 K03011 K13502 K13502 1 2 … … … … … … 1 1 1 1 2 2 2 2 14 15 16 17 Carbon steel Carbon steel Carbon steel Carbon steel Forgings Forgings Cast pipe Forgings SA-541 SA-541 SA-660 SA-765 1 1A WCB II K03506 K03020 J03003 K03047 … … … … … … … … 1 1 1 1 2 2 2 2 18 19 20 Carbon steel Carbon steel Carbon steel Plate Plate Plate SA-515 SA-516 SA/JIS G3118 70 70 SGV480 K03101 K02700 … … … … … … … 1 1 1 2 2 2 21 22 23 24 Carbon steel Carbon steel Carbon steel Carbon steel Wld. pipe Wld. pipe Wld. pipe Wld. pipe SA-671 SA-671 SA-672 SA-672 CB70 CC70 B70 C70 K03101 K02700 K03101 K02700 … … … … … … … … 1 1 1 1 2 2 2 2 25 26 27 28 29 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Smls. pipe Wld. tube Wld. tube Wld. tube Smls. tube SA-106 SA-178 SA-178 SA-178 SA-210 C D D D C K03501 … … … K03501 … … … … … … … … … … 1 1 1 1 1 2 2 2 2 2 30 31 32 33 34 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Castings Smls. & wld. fittings Castings Castings Plate SA-216 SA-234 SA-352 SA-487 SA-537 WCC WPC LCC 16 … J02503 K03501 J02505 … K12437 … … … A 3 … … … … 100 < t ≤ 150 1 1 1 1 1 2 2 2 2 3 35 36 37 38 39 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Smls. tube Wld. tube Cast pipe Bar Bar SA-556 SA-557 SA-660 SA-695 SA-696 C2 C2 WCC B/40 C K03006 K03505 J02505 K03504 K03200 … … … … … … … … … … 1 1 1 1 1 2 2 2 2 2 40 41 42 43 Carbon steel Carbon steel Carbon steel Carbon steel Sheet Plate Plate Plate SA-414 SA-662 SA-537 SA-738 F C … C K03102 K02007 K12437 K02008 … … 2 … … … 100 < t ≤ 150 100 < t ≤ 150 1 1 1 1 2 2 3 3 Line No. (a) (a) (a) 18 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 460 470 485 485 285 305 240 240 NP NP NP 454 NP NP 204 (Cl. 3 only) 343 (Cl. 3 only) 250 250 343 538 NP NP 343 343 CS-2 CS-2 CS-2 CS-2 … … … G10, G15, G22, S1, T2 5 6 7 8 9 485 485 485 485 485 250 250 250 250 250 538 538 538 538 NP 371 371 371 371 NP 538 538 538 538 538 343 343 343 343 343 CS-2 CS-2 CS-2 CS-2 CS-2 G10, S1, T2 G10, S1, T2 G1, G10, G17, S1, T2 G10, S1, T2 G10, T2 10 11 12 13 485 485 485 485 250 250 250 250 NP NP NP NP 371 371 371 371 538 538 538 538 343 343 343 343 CS-2 CS-2 CS-2 CS-2 G10, T2 G10, T2 G10, T2 G10, T2 14 15 16 17 485 485 485 485 250 250 250 250 NP NP 538 NP 371 371 371 NP 538 538 NP 538 343 343 NP 343 CS-2 CS-2 CS-2 CS-2 G10, T2 G10, T2 G1, G10, G17, S1, T2 G10, T2 18 19 20 485 485 485 260 260 260 538 454 454 371 371 NP 538 538 NP 343 343 NP CS-2 CS-2 CS-2 G10, S1, T2 G10, S1, T2 G10, S1, T2 21 22 23 24 485 485 485 485 260 260 260 260 NP NP NP NP 371 371 371 371 NP NP NP NP NP NP NP NP CS-2 CS-2 CS-2 CS-2 S5, W10, W12 S6, W10, W12 S5, W10, W12 S6, W10, W12 25 26 27 28 29 485 485 485 485 485 275 275 275 275 275 538 538 538 538 538 371 NP NP NP NP 538 NP NP NP 538 343 NP NP NP 343 CS-2 CS-2 CS-2 CS-2 CS-2 G10, S1, T1 G10, S1, T1, W13 G4, G10, S1, T4 G3, G10, S1, T2 G10, S1, T1 30 31 32 33 34 485 485 485 485 485 275 275 275 275 275 538 427 NP NP NP 371 371 371 371 NP 538 427 NP NP 371 343 343 NP NP 343 CS-2 CS-2 CS-2 CS-2 CS-2 G1, G10, G17, S1, T1 G10, T1, W14 G17, T1 … G23, W11 35 36 37 38 39 485 485 485 485 485 275 275 275 275 275 NP NP 538 NP NP NP NP 371 371 371 427 538 NP 427 NP 343 343 NP 343 NP CS-2 CS-2 CS-2 CS-2 CS-2 G10, T1 G24, T2, W6 G1, G10, G17, S1, T1 G10, T1 T1 40 41 42 43 485 485 485 485 290 295 315 315 NP NP NP NP NP NP 371 343 482 371 371 343 343 343 343 343 CS-2 CS-3 CS-3 CS-3 G10, T1 T1 G23, T1, W11 G23, W11 19 (a) (a) (a) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (a) (a) (a) Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 131 134 138 138 131 134 138 138 131 134 138 138 131 134 138 138 131 134 138 138 131 134 137 137 131 134 132 132 … … 126 126 … … 122 122 … … 119 119 … … … 114 … … … 101 … … … 83.9 … … … 67.0 … … … 51.1 5 6 7 8 9 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 136 136 136 136 136 129 129 129 129 129 125 125 125 125 125 122 122 122 122 122 117 117 117 117 117 101 101 101 101 101 83.9 83.9 83.9 83.9 83.9 67.0 67.0 67.0 67.0 67.0 51.1 51.1 51.1 51.1 51.1 10 11 12 13 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 136 136 136 136 129 129 129 129 125 125 125 125 122 122 122 122 117 117 117 117 101 101 101 101 83.9 83.9 83.9 83.9 67.0 67.0 67.0 67.0 51.1 51.1 51.1 51.1 14 15 16 17 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 136 136 136 136 129 129 129 129 125 125 125 125 122 122 122 122 117 117 117 117 101 101 101 101 83.9 83.9 83.9 83.9 67.0 67.0 67.0 67.0 51.1 51.1 51.1 51.1 18 19 20 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 136 136 136 132 132 132 128 128 128 123 123 123 101 101 101 83.8 83.8 83.8 67.1 67.1 67.1 51.0 51.0 51.0 21 22 23 24 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 136 136 136 136 132 132 132 132 128 128 128 128 123 123 123 123 … … … … … … … … … … … … … … … … 25 26 27 28 29 138 138 138 117 138 138 138 138 117 138 138 138 138 117 138 138 138 138 117 138 138 138 138 117 138 138 138 138 117 138 138 138 138 117 138 138 138 138 117 138 138 138 138 117 138 135 135 135 115 135 123 123 123 104 123 101 101 101 86.1 101 83.8 83.8 83.7 71.3 83.8 67.0 67.0 67.6 56.9 67.0 51.0 51.0 45.5 43.4 51.0 30 31 32 33 34 138 138 138 138 138 138 138 138 138 138 138 138 138 137 138 138 138 138 133 137 138 138 138 129 136 138 138 138 125 135 138 138 138 123 131 138 138 138 123 126 138 138 138 123 123 135 135 135 123 121 123 123 123 123 118 101 101 … … … 83.8 83.8 … … … 67.0 67.0 … … … 51.0 … … … … 35 36 37 38 39 138 117 138 138 138 138 117 138 138 138 138 117 138 138 138 138 117 138 138 138 138 117 138 138 138 138 117 138 138 138 138 117 138 138 138 138 117 138 138 138 138 117 138 138 138 135 115 135 135 135 123 104 123 123 123 101 86.1 101 101 … 83.8 71.3 83.8 83.8 … 67.0 56.9 67.0 67.0 … … 43.4 51.0 … … 40 41 42 43 138 138 138 138 138 138 138 138 138 138 138 138 138 138 137 137 138 138 136 136 138 138 134 134 138 138 134 134 138 138 134 134 138 138 134 134 137 137 133 133 123 123 125 … 101 … … … 83.8 … … … 67.1 … … … 50.8 … … … 20 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 … … … 33.6 … … … 21.3 … … … 12.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 9 33.6 33.6 33.6 33.6 33.6 21.3 21.3 21.3 21.3 21.3 12.9 12.9 12.9 12.9 12.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 33.6 33.6 33.6 33.6 21.3 21.3 21.3 21.3 12.9 12.9 12.9 12.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 17 33.6 33.6 33.6 33.6 21.3 21.3 21.3 21.3 12.9 12.9 12.9 12.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 18 19 20 33.6 33.6 … 21.3 21.3 … 12.9 12.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 24 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 28 29 33.6 33.6 27.9 28.6 33.6 21.3 21.3 18.3 18.1 21.3 12.9 12.9 10.6 10.7 12.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 30 31 32 33 34 33.6 … … … … 21.3 … … … … 12.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 35 36 37 38 39 … 28.6 33.6 … … … 18.1 21.3 … … … 10.7 12.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 40 41 42 43 34.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 (a) (a) (a) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 5 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Plate Wld. pipe Wld. pipe Wld. pipe Plate SA-537 SA-671 SA-672 SA-691 SA-841 … CD70 D70 CMSH-70 A K12437 K12437 K12437 K12437 … 1 … … … 1 ≤ 64 ≤ 64 ≤ 64 ≤ 64 ≤ 64 1 1 1 1 1 2 2 2 2 2 6 7 8 9 … … … Carbon steel … … … Plate … … … SA/GB 6654 … … … 16MnR … … … … … … … … … … … 16 < t ≤ 36 … … … 1 … … … 2 10 11 12 13 Carbon steel Carbon steel Carbon steel Carbon steel Plate Plate Forgings Plate SA-455 SA/GB 6654 SA-266 SA-455 … 16MnR 3 … K03300 … K05001 K03300 … … … … 10 < t ≤ 15 6 ≤ t ≤ 16 … ≤ 10 1 1 1 1 2 2 2 2 (10) 14 15 16 17 Carbon steel Carbon steel Carbon steel Carbon steel Plate Wld. pipe Wld. pipe Wld. pipe SA-299 SA-671 SA-672 SA-691 A CK75 N75 CMS-75 K02803 K02803 K02803 K02803 … … … … > 25 > 25 > 25 > 25 1 1 1 1 2 2 2 2 (10) 18 19 20 21 22 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Plate Wld. pipe Forgings Sheet Plate SA-299 SA-691 SA-372 SA-414 SA-738 A CMS-75 B G A K02803 K02803 K04001 K03103 K12447 … … … … … ≤ 25 ≤ 25 … … … 1 1 1 1 1 2 2 2 2 2 23 24 25 26 Carbon steel Carbon steel Carbon steel Carbon steel Plate Plate Wld. pipe Plate SA-537 SA-537 SA-691 SA-738 … … CMSH-80 C K12437 K12437 K12437 K02008 3 2 … … 64 < t ≤ 100 64 < t ≤ 100 64 < t ≤ 100 64 < t ≤ 100 1 1 1 1 3 3 3 3 27 28 29 30 31 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Plate Plate Forgings Plate Plate SA-299 SA-299 SA-765 SA-537 SA-537 B B IV … … K02803 K02803 K02009 K12437 K12437 … … … 3 2 > 25 ≤ 25 … ≤ 64 ≤ 64 1 1 1 1 1 3 3 3 3 3 (a) 32 33 34 35 36 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Wld. pipe Wld. pipe Wld. pipe Plate Plate SA-671 SA-672 SA-691 SA-738 SA-841 CD80 D80 CMSH-80 C B K12437 K12437 K12437 K02008 … … … … … 2 ≤ 64 ≤ 64 ≤ 64 ≤ 64 ≤ 64 1 1 1 1 1 3 3 3 3 3 (a) 37 38 39 Carbon steel Carbon steel Carbon steel Plate Plate Plate SA-612 SA-612 SA-738 … … B K02900 K02900 K12007 … … … 13 < t ≤ 25 ≤ 13 … 10C 10C 1 1 1 3 40 41 42 43 Carbon steel Carbon steel Carbon steel Carbon steel Forgings Plate Plate Plate SA-372 SA-724 SA-724 SA-724 C A C B K04801 K11831 K12037 K12031 … … … … … … … … … 1 1 1 … 4 4 4 Line No. (a) (a) (a) (a) (10) (a) (10) (10) 22 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 485 485 485 485 485 345 345 345 345 345 NP NP NP NP NP 371 371 371 371 NP 343 NP NP NP 343 343 NP NP NP NP CS-3 CS-3 CS-3 CS-3 CS-3 G23, T1 S6, T1, W10, W12 S6, T1, W10, W12 S6, T1, W10, W12 … 6 7 8 9 … … … 490 … … … 325 … … … NP … … … NP … … … 250 … … … NP … … … CS-2 … … … … 10 11 12 13 505 510 515 515 255 345 260 260 NP NP 538 NP 204 (Cl. 3 only) NP 371 204 (Cl. 3 only) 343 250 538 343 343 NP NP 343 CS-2 CS-2 CS-2 CS-2 … … G10, S1, T2, W8, W11 … 14 15 16 17 515 515 515 515 275 275 275 275 538 NP NP NP 371 371 371 371 538 NP NP NP 343 NP NP NP CS-2 CS-2 CS-2 CS-2 G10, S1, T2 S6, W10, W12 S6, W10, W12 S6, W10, W12 (10) 18 19 20 21 22 515 515 515 515 515 290 290 310 310 310 538 NP NP NP NP 371 371 NP NP NP 538 NP 343 482 371 343 NP 343 343 343 CS-2 CS-2 CS-3 CS-3 CS-2 G10, S1, T1 T1, W10, W12 W11 G10, T1 T1 (10) 23 24 25 26 515 515 515 515 345 380 380 380 NP NP NP NP NP 371 371 343 371 343 NP 343 343 343 NP 343 CS-5 CS-5 CS-5 CS-5 G23, T1, W11 G23, T1, W11 G26, T1, W10, W12 G23, W11 27 28 29 30 31 550 550 550 550 550 310 325 345 380 415 427 427 NP NP NP NP NP NP NP 371 538 538 371 371 343 343 343 NP 343 343 CS-3 CS-3 CS-3 CS-5 CS-5 G10, S1, T1 G10, S1, T1 … G23, T1, W11 G23, S6, T1, W10, W11, W12 32 33 34 35 36 550 550 550 550 550 415 415 415 415 415 NP NP NP NP NP 371 371 371 343 NP NP NP NP 343 343 NP NP NP 343 NP CS-5 CS-5 CS-5 CS-5 CS-3 S6, T1, W10, W12 S6, T1, W10, W12 S6, T1, W10, W12 G23, W11 … (a) 37 38 39 560 570 585 345 345 415 NP NP NP 371 343 343 343 343 343 343 343 343 CS-3 CS-3 CS-5 T1 … … (a) 40 41 42 43 620 620 620 655 380 485 485 515 NP NP NP NP NP NP NP NP 343 371 371 371 343 343 343 343 CS-3 CS-5 CS-5 CS-5 W11 … … … 23 (a) (a) (a) (a) (10) (a) (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 5 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 137 137 137 137 138 136 136 136 136 138 134 134 134 134 138 134 134 134 134 138 134 134 134 134 138 134 134 134 134 138 133 133 133 133 138 125 125 125 125 … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 … … … 140 … … … 140 … … … 140 … … … 140 … … … 140 … … … 140 … … … 140 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 144 146 148 148 144 146 148 148 144 146 148 148 144 146 148 148 144 146 148 148 144 146 148 148 140 146 142 143 133 … 135 136 129 … 131 132 125 … 127 129 … … 122 … … … 107 … … … 88.3 … … … 67.5 … … … 50.9 … (10) 14 15 16 17 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 143 143 143 143 139 139 139 139 135 135 135 135 130 130 130 130 107 … … … 88.1 … … … 67.5 … … … 50.8 … … … (10) 18 19 20 21 22 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 147 147 148 148 148 141 141 148 146 146 133 133 … 132 132 107 … … 107 … 88.1 … … 88.2 … 67.6 … … 67.6 … 50.8 … … 50.6 … 23 24 25 26 148 148 148 148 148 148 148 148 147 147 147 147 147 147 147 147 145 145 145 145 144 144 144 144 144 144 144 144 144 144 144 144 144 144 144 144 142 143 143 143 123 134 134 … … … … … … … … … … … … … … … … … 27 28 29 30 31 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 157 157 158 158 158 156 156 158 158 156 154 154 158 158 156 154 154 158 158 156 154 154 157 158 156 154 154 152 158 155 151 151 133 133 153 132 132 107 107 … … … 88.1 88.1 … … … 67.6 67.6 … … … 50.8 50.8 … … … (a) 32 33 34 35 36 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 157 157 157 157 158 156 156 156 156 158 154 154 154 154 158 154 154 154 154 158 154 154 154 154 158 154 154 154 154 158 151 151 151 151 158 132 132 132 … … … … … … … … … … … … … … … … … … … … … … (a) 37 38 39 159 163 168 159 163 168 159 163 168 158 162 168 157 161 168 156 160 168 156 160 168 155 157 167 155 154 165 149 151 163 133 … … … … … … … … … … … … … … 40 41 42 43 177 177 177 187 177 177 177 187 177 177 177 187 177 176 176 186 177 175 175 185 177 173 173 183 177 173 173 183 177 173 173 183 175 173 173 179 166 165 165 165 … 148 148 158 … … … … … … … … … … … … … … … … (a) (a) (a) (a) (10) (a) (10) (10) 24 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 … … 33.7 … … … 21.3 … … … 12.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 17 33.7 … … … 21.3 … … … 12.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) 18 19 20 21 22 33.7 … … 34.9 … 21.3 … … … … 12.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) 23 24 25 26 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 27 28 29 30 31 33.7 33.7 … … … 21.3 21.3 … … … 12.9 12.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (a) 37 38 39 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (a) 40 41 42 43 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 (a) (a) (a) (a) (10) (a) (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. (a) (a) (a) (a) 1 2 3 4 C – Mn – Si – Cb … C – Mn – Si – Cb C – Mn – Si – Cb Plate … Plate Plate SA-737 … SA/AS 1548 SA/AS 1548 B … PT490N PT490NR K12001 … … … … … Normalized Norm. rld. … … ≤ 150 ≤ 150 1 … 1 1 2 … 2 2 (a) 5 6 7 8 9 C – Mn – Si – V C – Mn – Si – V – Cb C – Mn – Si – V – Cb C – Mn – Si – V – Cb C – Mn – Si – V – Cb Plate Plate Plate Plate Plate SA-737 SA-656 SA-656 SA-656 SA-656 C T3 T7 T3 T7 K12202 … … … … … … … … … … ≤ 50 ≤ 50 ≤ 40 ≤ 40 1 1 1 1 1 3 1 1 2 2 10 11 12 13 14 15 C – Mn – Si – V – Cb C – Mn – Si – V – Cb C – Mn – Si – V – Cb C – Mn – Si – V – Cb C – Mn – Ti C – Si – Ti Plate Plate Plate Plate Plate, sheet Forgings SA-656 SA-656 SA-656 SA-656 SA-562 SA-836 T3 T7 T3 T7 … … … … … … K11224 … … … … … … 1 ≤ 25 ≤ 25 ≤ 20 ≤ 20 … … 1 1 1 1 1 1 3 3 4 4 1 1 16 17 18 C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo Smls. tube Wld. tube Wld. tube SA-209 SA-250 SA-250 T1b T1b T1b K11422 K11422 K11422 … … … … … … 3 3 3 1 1 1 19 20 21 22 23 24 C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo Smls. tube Smls. & wld. fittings Wld. tube Wld. tube Smls. pipe Forged pipe SA-209 SA-234 SA-250 SA-250 SA-335 SA-369 T1 WP1 T1 T1 P1 FP1 K11522 K12821 K11522 K11522 K11522 K11522 … … … … … … … … … … … … 3 3 3 3 3 3 1 1 1 1 1 1 25 26 27 C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo Smls. tube Wld. tube Wld. tube SA-209 SA-250 SA-250 T1a T1a T1a K12023 K12023 K12023 … … … … … … 3 3 3 1 1 1 28 29 30 C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo Castings Castings Cast pipe SA-217 SA-352 SA-426 WC1 LC1 CP1 J12524 J12522 J12521 … … … … … … 3 3 3 1 1 1 31 32 33 34 C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo Plate Wld. pipe Wld. pipe Wld. pipe SA-204 SA-672 SA-691 SA-691 A L65 CM-65 CM-65 K11820 K11820 K11820 K11820 … … … … … … … … 3 3 3 3 1 1 1 1 35 36 37 38 39 40 C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo Forgings Plate Forgings Wld. pipe Wld. pipe Wld. pipe SA-182 SA-204 SA-336 SA-672 SA-691 SA-691 F1 B F1 L70 CM-70 CM-70 K12822 K12020 K12520 K12020 K12020 K12020 … … … … … … … … … … … … 3 3 3 3 3 3 2 2 2 2 2 2 41 42 43 44 C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo Plate Wld. pipe Wld. pipe Wld. pipe SA-204 SA-672 SA-691 SA-691 C L75 CM-75 CM-75 K12320 K12320 K12320 K12320 … … … … … … … … 3 3 3 3 2 2 2 2 26 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 485 … 490 490 345 … … … NP … 538 538 371 … NP NP 371 … 538 538 343 … NP NP CS-3 … CS-2 CS-2 T1 … G10, G18, S1, T1 G10, G18, S1, T1 (a) (a) (a) (a) 5 6 7 8 9 550 414 414 483 483 415 345 345 414 414 NP NP NP NP NP 371 NP NP NP NP 371 NP NP NP NP 343 343 343 343 343 CS-3 … … … … … … … … … (a) 10 11 12 13 14 15 552 552 621 621 380 380 483 483 552 552 205 170 NP NP NP NP NP NP NP NP NP NP NP NP NP NP NP NP 343 343 343 343 343 343 NP 343 … … … … CS-6 CS-1 … … … … G30 … 16 17 18 365 365 365 195 195 195 538 538 538 NP NP NP 538 NP 538 343 NP 343 CS-1 CS-1 CS-1 G11, S3, T5 G11, S2, T5, W13 G3, G11, G24, S2, T5 19 20 21 22 23 24 380 380 380 380 380 380 205 205 205 205 205 205 538 538 538 538 538 538 NP 371 NP NP 371 371 538 538 NP 538 538 538 343 343 NP 343 343 343 CS-2 CS-2 CS-2 CS-2 CS-2 CS-2 G11, S3, T4 G11, T4, W14 G11, S2, T4, W13 G3, G11, G24, S2, T4 G11, S2, T4 G11, S2, T4 25 26 27 415 415 415 220 220 220 538 538 538 NP NP NP 538 NP 538 343 NP 343 CS-2 CS-2 CS-2 G11, S3, T4 G11, S2, T4, W13 G3, G11, G24, S2, T4 28 29 30 450 450 450 240 240 240 538 NP NP 371 371 371 538 343 NP 343 343 NP CS-2 CS-2 CS-2 G1, G11, G17, S2, T4 G1, G17 G17 31 32 33 34 450 450 450 450 255 255 255 255 538 NP NP NP 371 371 371 149 (Cl. 3 only) 538 NP NP NP 343 NP NP NP CS-2 CS-2 CS-2 CS-2 G11, S2, T4 G26, W10, W12 G26, W10, W12 G27, W10, W12 35 36 37 38 39 40 485 485 485 485 485 485 275 275 275 275 275 275 538 538 538 NP NP NP 371 371 371 371 371 149 (Cl. 3 only) 538 538 538 NP NP NP 343 343 343 NP NP NP CS-2 CS-2 CS-2 CS-2 CS-2 CS-2 G11, S2, T4 G11, S2, T4 G11, S2, T4 G26, W10, W12 G26, W10, W12 G27, W10, W12 41 42 43 44 515 515 515 515 295 295 295 295 538 NP NP NP 371 371 371 149 (Cl. 3 only) 538 NP NP NP 343 NP NP NP CS-2 CS-2 CS-2 CS-2 G11, S2, T4, W12 G26, W10, W12 G26, W10, W12 G27, W10, W12 27 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 (a) (a) (a) (a) 1 2 3 4 138 … 140 140 138 … 140 140 138 … 140 140 138 … 140 140 138 … 140 140 138 … 140 140 138 … 140 140 138 … 140 140 138 … 140 140 138 … 139 139 135 … 123 123 … … 101 101 … … 83.8 83.8 … … 67.0 67.0 … … 51.0 51.0 (a) 5 6 7 8 9 158 118 118 138 138 158 118 118 138 138 158 118 118 138 138 158 118 118 138 138 158 118 118 138 138 158 118 118 138 138 158 118 118 138 138 158 118 118 138 138 158 118 118 138 138 155 118 118 138 138 135 … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 14 15 158 158 177 177 88.9 108 158 158 177 177 84.0 103 158 158 177 177 78.3 97.6 158 158 177 177 75.1 94.1 158 158 177 177 73.0 91.6 158 158 177 177 71.7 89.7 158 158 177 177 71.7 89.6 158 158 177 177 71.7 89.4 158 158 177 177 71.7 88.5 158 158 177 177 71.7 87.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 104 104 88.9 104 104 88.9 104 104 88.9 104 104 88.9 104 104 88.9 104 104 88.9 104 104 88.9 104 104 88.9 104 104 88.6 103 103 87.2 101 101 85.9 98.5 98.5 84.0 96.7 96.7 82.2 93.6 93.6 79.7 90.7 90.7 77.4 19 20 21 22 23 24 108 108 108 92.4 108 108 108 108 108 92.4 108 108 108 108 108 92.4 108 108 108 108 108 92.4 108 108 108 108 108 92.4 108 108 108 108 108 92.4 108 108 108 108 108 92.4 108 108 108 108 108 92.4 108 108 108 108 108 92.4 108 108 108 108 108 92.4 108 108 108 108 108 92.2 108 108 106 106 106 90.2 106 106 103 103 103 87.7 103 103 101 101 101 85.4 101 101 96.1 96.1 96.1 81.4 96.1 96.1 25 26 27 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 100 115 115 98.2 113 113 95.8 110 110 93.9 107 107 90.9 100 100 84.9 28 29 30 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 126 126 126 123 … … 120 … … 117 … … 103 … … 31 32 33 34 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 128 … 128 128 128 … 128 128 128 … 128 128 128 … 128 128 128 … 128 128 128 … 128 … … … 127 … … … 124 … … … 105 … … … 35 36 37 38 39 40 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 … 138 138 138 138 138 … 138 138 138 138 138 … 138 138 138 138 138 … 138 138 138 138 138 … 138 138 138 138 138 … 138 138 138 … … … 137 137 137 … … … 134 134 134 … … … 107 107 107 … … … 41 42 43 44 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 148 … 148 148 148 … 148 148 148 … 148 148 148 … 148 148 148 … 148 148 148 … 148 … … … 148 … … … 144 … … … 109 … … … 28 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 … … 33.6 33.6 … … 21.3 21.3 … … 12.9 12.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (a) (a) (a) (a) 5 6 7 8 9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (a) 10 11 12 13 14 15 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 70.4 70.4 60.2 42.2 42.2 36.0 23.4 23.4 20.0 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 19 20 21 22 23 24 72.1 72.1 72.1 61.3 72.1 72.1 41.7 41.7 41.7 35.7 41.7 41.7 23.6 23.6 23.6 20.1 23.6 23.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 70.4 70.4 59.9 42.3 42.3 36.2 23.4 23.4 19.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 69.5 … … 42.6 … … 23.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 34 68.9 … … … 42.8 … … … 23.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 35 36 37 38 39 40 68.1 68.1 68.1 … … … 43.1 43.1 43.1 … … … 23.1 23.1 23.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 41 42 43 44 67.2 … … … 43.3 … … … 23.0 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 5 1 ⁄2Cr – 1⁄5Mo ⁄2Cr – 1⁄5Mo 1 ⁄2Cr – 1⁄5Mo – V 1 ⁄2Cr – 1⁄4Mo – Si 1 ⁄2Cr – 1⁄4Mo – Si Forgings Forgings Plate Plate Forgings SA-372 SA-372 SA-517 SA-517 SA-592 G H B A A K13049 K13547 K11630 K11856 K11856 70 70 … … … … … ≤ 32 ≤ 32 ≤ 64 6 7 8 9 10 1 ⁄2Cr – 1⁄2Mo ⁄2Cr – 1⁄2Mo 1 ⁄2Cr – 1⁄2Mo 1 ⁄2Cr – 1⁄2Mo 1 ⁄2Cr – 1⁄2Mo Smls. pipe Forged pipe Plate Wld. pipe Wld. pipe SA-335 SA-369 SA-387 SA-691 SA-691 P2 FP2 2 1 ⁄2CR 1 ⁄2CR K11547 K11547 K12143 K12143 K12143 … … 1 … … 11 12 13 14 1 ⁄2Cr – 1⁄2Mo ⁄2Cr – 1⁄2Mo 1 ⁄2Cr – 1⁄2Mo 1 ⁄2Cr – 1⁄2Mo Smls. tube Wld. tube Wld. tube Cast pipe SA-213 SA-250 SA-250 SA-426 T2 T2 T2S1 CP2 K11547 K11547 K11547 J11547 15 16 17 18 19 1 ⁄2Cr – 1⁄2Mo ⁄2Cr – 1⁄2Mo 1 ⁄2Cr – 1⁄2Mo 1 ⁄2Cr – 11⁄4Mn – Si 1 ⁄2Cr – 11⁄4Mn – Si Forgings Plate Wld. pipe Plate Plate SA-182 SA-387 SA-691 SA-202 SA-202 F2 2 1 ⁄2CR A B 20 21 22 3 3 ⁄4Cr – 1⁄2Ni – Cu ⁄4Cr – 1⁄2Ni – Cu 3 ⁄4Cr – 3⁄4Ni – Cu – Al Smls. & wld. tube Wld. tube Pipe SA-423 SA-423 SA-333 23 24 25 26 27 28 1Cr – 1⁄5Mo 1Cr – 1⁄5Mo 1Cr – 1⁄5Mo 1Cr – 1⁄5Mo 1Cr – 1⁄5Mo 1Cr – 1⁄5Mo Forgings Forgings Forgings Forgings Forgings Forgings 29 30 31 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo Plate Wld. pipe Cast pipe 32 33 34 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo 35 36 37 38 39 40 41 42 43 Line No. … … 11B 11B 11B … … 4 1 1 … … … … … 3 3 3 3 3 1 1 1 1 1 … … … … … … … … 3 3 3 3 1 1 1 1 K12122 K12143 K12143 K11742 K12542 … 2 … … … … … … … … 3 3 3 4 4 2 2 2 1 1 1 1 4 K11535 K11535 K11267 … … … … … … 4 4 4 2 2 2 SA-372 SA-372 SA-372 SA-372 SA-372 SA-372 E J E F J J K13047 K13548 K13047 G41350 K13548 G41370 65 65 70 70 70 110 … … … … … … … … … … … … … … … … … … SA-387 SA-691 SA-426 12 1CR CP12 K11757 K11757 J11562 1 … … … … … 4 4 4 1 1 1 Forgings SA-182 Smls. tube SA-213 Smls. & wld. fittings SA-234 F12 T12 WP12 K11562 K11562 K12062 1 … 1 … … … 4 4 4 1 1 1 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo Wld. tube Wld. tube Smls. pipe Forged pipe SA-250 SA-250 SA-335 SA-369 T12 T12S1 P12 FP12 K11562 K11562 K11562 K11562 … … … … … … … … 4 4 4 4 1 1 1 1 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo 1Cr – V Plate Wld. pipe Forgings Forgings Smls. tube SA-387 SA-691 SA-182 SA-336 SA-213 12 1CR F12 F12 T17 K11757 K11757 K11564 K11564 K12047 2 … 2 … … … … … … … 4 4 4 4 10B 1 1 1 1 1 1 1 1 1 30 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 825 825 795 795 795 485 485 690 690 690 NP NP NP NP NP NP NP 343 (SPT) 343 (SPT) 343 (SPT) 93 93 343 343 343 93 93 343 343 343 CS-3 CS-3 HT-1 HT-1 HT-1 W11 W11 … … … 6 7 8 9 10 380 380 380 380 380 205 205 230 230 230 538 538 538 NP NP 371 371 371 371 149 (Cl. 3 only) 538 538 538 NP NP 343 343 343 NP NP CS-2 CS-2 CS-2 CS-2 CS-2 T5 T5 T5 G26, W10, W12 G27, W10, W12 11 12 13 14 415 415 415 415 205 205 205 205 538 538 538 NP 371 NP NP 371 538 NP NP NP 343 NP NP NP CS-2 CS-2 CS-2 CS-2 T5 G3, T5 T5, W13 G17 15 16 17 18 19 485 485 485 515 585 275 310 310 310 325 538 NP NP 538 538 NP 371 371 NP NP 538 538 NP 538 538 343 343 NP NP NP CS-2 CS-3 CS-3 CS-3 CS-3 T5 T5 G26, W10, W12 S1, T2 S1, T2 20 21 22 415 415 415 255 255 240 371 371 NP NP NP 371 343 343 343 NP NP NP CS-2 CS-2 CS-2 W13, W14 G3, G24 … 23 24 25 26 27 28 725 725 825 825 825 930 450 450 485 485 485 760 NP NP NP NP NP NP NP NP NP NP NP NP 343 343 343 343 343 343 343 343 343 343 343 343 CS-2 CS-2 CS-5 CS-5 CS-5 HT-1 W11 W11 W11 W11 W11 W11 29 30 31 380 380 415 230 230 205 649 NP NP 371 371 371 649 NP NP NP NP NP CS-2 CS-2 CS-2 S4, T5 G26, W10, W12 G17 32 33 34 415 415 415 220 220 220 649 649 649 NP 371 371 649 649 649 NP NP NP CS-2 CS-2 CS-2 T5 S4, T5 S4, T5, W14 35 36 37 38 415 415 415 415 220 220 220 220 649 649 649 649 NP NP 371 371 NP NP 649 649 NP NP NP NP CS-2 CS-2 CS-2 CS-2 G3, S4, T5 S4, T5, W13 S4, T5 S4, T5 39 40 41 42 43 450 450 485 485 415 275 275 275 275 205 649 NP 649 649 NP 371 371 371 371 NP 649 NP 649 649 343 NP NP NP NP 343 CS-2 CS-2 CS-2 CS-2 CS-2 S4, T5 G26, W10, W12 S4, T4 S4, T4 … 31 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 5 236 236 227 227 227 236 236 227 227 227 236 236 227 227 227 … … 227 227 227 … … 227 227 227 … … 227 227 227 … … 227 227 227 … … 227 227 227 … … 227 227 227 … … 226 226 226 … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 10 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 108 … 108 108 108 108 … 108 108 108 108 … 108 108 108 108 … 108 108 108 108 … 108 108 108 108 … 106 106 108 … … 103 103 108 … … 100 100 106 … … 97.1 97.1 103 … … 11 12 13 14 118 100 118 118 118 100 118 118 118 100 118 118 118 100 118 118 118 100 118 118 118 100 118 118 117 99.6 117 117 114 96.7 114 114 112 95.5 112 112 110 93.8 110 110 108 91.5 108 108 106 90.2 106 … 103 87.7 103 … 100 85.3 100 … 97.1 82.4 97.1 … 15 16 17 18 19 138 138 138 148 168 138 138 138 148 168 138 138 138 148 168 138 138 138 148 168 138 138 138 148 168 138 138 138 148 168 138 138 138 148 168 138 138 138 148 165 138 138 138 148 160 138 138 138 147 153 138 138 138 136 143 138 138 … 107 121 137 138 … 84.3 85.0 134 135 … 58.1 57.6 130 130 … 38.6 38.9 20 21 22 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 118 101 118 … … … … … … … … … … … … 23 24 25 26 27 28 207 207 236 236 236 265 207 207 236 233 236 260 207 207 236 229 236 254 207 207 236 227 236 254 207 207 236 225 236 253 207 207 236 223 236 252 207 207 236 222 236 249 207 207 236 220 236 248 207 207 236 217 236 245 205 205 235 209 235 234 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 30 31 108 108 118 107 107 117 106 106 116 105 105 115 104 104 114 104 104 112 104 104 109 104 104 106 104 104 104 104 104 103 104 104 102 104 … … 104 … … 104 … … 102 … … 32 33 34 118 118 118 118 117 117 115 116 116 114 114 114 114 114 114 114 114 114 114 114 114 113 113 113 112 112 112 110 110 110 109 109 109 107 107 107 106 106 106 103 103 103 101 101 101 35 36 37 38 100 118 118 118 100 118 117 117 98.2 115 116 116 97.0 114 114 114 96.5 114 114 114 96.5 114 114 114 96.5 114 114 114 95.8 113 113 113 94.7 112 112 112 93.4 110 110 110 92.2 109 109 109 91.0 107 107 107 89.7 106 106 106 87.9 103 103 103 85.7 101 101 101 39 40 41 42 43 128 128 138 138 118 128 127 137 138 118 125 125 135 134 118 124 124 133 133 118 123 123 132 132 118 123 123 132 132 116 123 123 132 132 112 123 123 132 132 109 123 123 132 132 108 123 123 132 132 106 123 123 132 132 … 123 … 132 132 … 123 … 132 132 … 123 … 129 129 … 123 … 125 125 … 32 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 10 77.0 77.0 76.7 … … 49.5 49.5 49.6 … … 31.3 31.3 31.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 77.0 65.3 77.0 … 49.5 42.0 49.5 … 31.3 26.5 31.3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 15 16 17 18 19 89.1 88.9 … 25.2 25.1 46.0 46.0 … 14.9 14.9 32.5 32.5 … 5.87 5.86 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 23 24 25 26 27 28 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 30 31 88.8 … … 61.7 … … 40.3 … … 26.4 … … 17.3 … … 11.7 … … 7.40 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 88.3 88.3 88.3 61.9 61.9 61.9 40.3 40.3 40.3 26.4 26.4 26.4 17.3 17.3 17.3 11.7 11.7 11.7 7.40 7.40 7.40 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 35 36 37 38 72.9 88.3 88.3 88.3 53.2 61.9 61.9 61.9 33.7 40.3 40.3 40.3 22.5 26.4 26.4 26.4 14.8 17.3 17.3 17.3 9.71 11.7 11.7 11.7 6.34 7.40 7.40 7.40 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 39 40 41 42 43 94.4 … 97.2 97.2 … 60.2 … 59.3 59.3 … 40.8 … 41.0 41.0 … 26.3 … 26.2 26.2 … 17.3 … 17.3 17.3 … 11.7 … 11.7 11.7 … 7.40 … 7.40 7.40 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 33 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 11⁄4Cr – 1⁄2Mo 11⁄4Cr – 1⁄2Mo 11⁄4Cr – 1⁄2Mo Castings Cast pipe Bar SA-217 SA-426 SA-739 WC6 CP11 B11 J12072 J12072 K11797 … … … … … … 4 4 4 1 1 1 4 5 6 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si Forgings SA-182 Smls. tube SA-213 Smls. & wld. fittings SA-234 F11 T11 WP11 K11597 K11597 … 1 … 1 … … … 4 4 4 1 1 1 7 8 9 10 11 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si Wld. tube Wld. tube Smls. pipe Forgings Forged pipe SA-250 SA-250 SA-335 SA-336 SA-369 T11 T11S1 P11 F11 FP11 K11597 K11597 K11597 K11597 K11597 … … … 1 … … … … … … 4 4 4 4 4 1 1 1 1 1 12 13 14 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si Plate Wld. pipe Wld. pipe SA-387 SA-691 SA-691 11 11⁄4CR 11⁄4CR K11789 K11789 K11789 1 … … … … … 4 4 4 1 1 1 15 16 17 18 19 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si Forgings Forgings Forgings Plate Wld. pipe SA-182 SA-336 SA-336 SA-387 SA-691 F11 F11 F11 11 11⁄4CR K11572 K11572 K11572 K11789 K11789 2 2 3 2 … … … … … … 4 4 4 4 4 1 1 1 1 1 20 21 22 23 13⁄4Cr – 1⁄2Mo – Cu 13⁄4Cr – 1⁄2Mo – Cu 13⁄4Cr – 1⁄2Mo – Ti 13⁄4Cr – 1⁄2Mo – Ti Forgings Forgings Plate Plate SA-592 SA-592 SA-517 SA-517 E E E E K11695 K11695 K21604 K21604 … … … … 64 < t ≤ 100 ≤ 64 64 < t ≤ 150 ≤ 64 11B 11B 11B 11B 2 2 2 2 24 25 26 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo Forgings SA-182 Smls. tube SA-213 Smls. & wld. fittings SA-234 F22 T22 WP22 K21590 K21590 K21590 1 … 1 … … … 5A 5A 5A 1 1 1 27 28 29 30 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo Wld. tube Wld. tube Smls. pipe Forgings SA-250 SA-250 SA-335 SA-336 T22 T22S1 P22 F22 K21590 K21590 K21590 K21590 … … … 1 … … … … 5A 5A 5A 5A 1 1 1 1 31 32 33 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo Forged pipe Plate Wld. pipe SA-369 SA-387 SA-691 FP22 22 21⁄4CR K21590 K21590 K21590 … 1 … … … … 5A 5A 5A 1 1 1 34 35 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo Castings Cast pipe SA-217 SA-426 WC9 CP22 J21890 J21890 … … … … 5A 5A 1 1 36 37 38 39 40 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo Forgings Forgings Plate Wld. pipe Bar SA-182 SA-336 SA-387 SA-691 SA-739 F22 F22 22 21⁄4CR B22 K21590 K21590 K21590 K21590 K21390 3 3 2 … … … … … … … 5A 5A 5A 5A 5A 1 1 1 1 1 Line No. 34 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 485 485 485 275 275 310 593 NP NP 371 371 371 593 NP 649 NP NP NP CS-2 CS-2 CS-3 G1, G17, T4 G17 T4 4 5 6 415 415 415 205 205 205 649 649 649 NP 371 371 649 649 649 NP NP NP CS-2 CS-2 CS-2 S4, T5 S4, T5 S4, T5, W14 7 8 9 10 11 415 415 415 415 415 205 205 205 205 205 649 649 649 649 649 NP NP 371 NP 371 NP NP 649 NP 649 NP NP NP NP NP CS-2 CS-2 CS-2 CS-2 CS-2 G3, S4, T5 S4, T5, W13 S4, T5 S4, T5 S4, T5 12 13 14 415 415 415 240 240 240 649 NP NP 371 149 (Cl. 3 only) 371 649 NP NP NP NP NP CS-2 CS-2 CS-2 S4, T4 G27, W10, W12 G26, W10, W12 15 16 17 18 19 485 485 515 515 515 275 275 310 310 310 649 649 NP 649 NP 371 NP NP 371 371 649 649 649 649 NP NP NP NP NP NP CS-2 CS-2 CS-3 CS-3 CS-3 S4, T4 S4, T4 T3 S4, T3 G26, W10, W12 20 21 22 23 725 795 725 795 620 690 620 690 NP NP NP NP 343 (SPT) NP 371 (SPT) 343 (SPT) 343 343 343 343 343 343 343 343 CS-5 HT-1 CS-5 HT-1 S7 … … … 24 25 26 415 415 415 205 205 205 649 649 649 371 371 371 649 649 649 NP NP NP CS-2 CS-2 CS-2 S4, T4, W7, W9 S4, T4, W7, W9 S4, T4, W7, W9, W14 27 28 29 30 415 415 415 415 205 205 205 205 649 649 649 649 NP NP 371 371 NP NP 649 649 NP NP NP NP CS-2 CS-2 CS-2 CS-2 G3, S4, T4, W9 S4, T4, W9, W13 S4, T4, W7, W9 S4, T4, W7, W9 31 32 33 415 415 415 205 205 205 649 649 NP 371 371 371 649 649 NP NP NP NP CS-2 CS-2 CS-2 S4, T4, W7, W9 S4, T4, W7, W9 G26, W10, W12 34 35 485 485 275 275 649 NP 371 371 649 NP NP NP CS-2 CS-2 G1, G17, S4, T4, W7, W9 G17 36 37 38 39 40 515 515 515 515 515 310 310 310 310 310 649 649 649 NP NP 371 371 371 371 371 649 649 649 NP 649 NP NP NP NP NP CS-3 CS-3 CS-3 CS-3 CS-3 S4, T4, W7, W9 S4, T4, W7, W9 S4, T4, W7, W9 G26, W10, W12 T4, W7 35 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 136 … 138 133 … 138 130 … 135 105 … 107 4 5 6 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 116 116 116 112 112 112 109 109 109 108 108 108 106 106 106 104 104 104 102 102 102 99.5 99.5 99.5 96.9 96.9 96.9 94.7 94.7 94.7 7 8 9 10 11 100 118 118 118 118 100 118 118 118 118 100 118 118 118 118 100 118 118 118 118 100 118 118 118 118 98.8 116 116 116 116 95.8 112 112 112 112 92.5 109 109 109 109 91.3 108 108 108 108 89.8 106 106 106 106 88.0 104 104 104 104 86.8 102 102 102 102 84.3 99.5 99.5 99.5 99.5 82.3 96.9 96.9 96.9 96.9 80.7 94.7 94.7 94.7 94.7 12 13 14 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 118 … 118 118 … 118 118 … 118 118 … 118 118 … 118 118 … 118 118 … … 116 … … 114 … … 101 … … 15 16 17 18 19 138 138 148 148 148 138 138 148 148 148 138 138 148 148 148 138 138 148 148 148 138 138 148 148 148 138 138 148 148 148 138 138 148 148 148 138 138 148 148 148 138 138 148 148 148 138 138 148 148 148 138 138 148 148 148 136 136 148 148 … 133 133 148 148 … 130 130 143 143 … 105 105 107 107 … 20 21 22 23 207 227 207 227 207 227 207 227 207 227 207 227 207 227 207 227 207 227 207 227 207 227 207 227 207 227 207 227 207 227 207 227 207 227 207 227 207 227 207 227 … … 206 … … … … … … … … … … … … … … … … … 24 25 26 118 118 118 118 118 118 118 118 118 116 116 116 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 100 100 100 27 28 29 30 100 118 118 118 100 118 118 118 99.8 118 118 118 98.3 116 116 116 97.2 114 114 114 97.2 114 114 114 97.2 114 114 114 97.2 114 114 114 97.2 114 114 114 97.2 114 114 114 97.2 114 114 114 97.2 114 114 114 97.2 114 114 114 97.2 114 114 114 85.5 100 100 100 31 32 33 118 118 118 118 118 118 118 118 118 116 116 116 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 … 114 114 … 114 114 … 100 100 … 34 35 138 138 138 138 138 138 137 137 136 136 134 134 133 133 133 133 132 132 131 131 129 129 127 … 124 … 119 … 113 … 36 37 38 39 40 148 148 148 148 148 148 148 148 148 148 147 147 147 147 147 146 146 146 146 146 144 144 144 144 144 142 142 142 142 142 141 141 141 141 141 141 141 141 141 141 140 140 140 140 140 139 139 139 139 139 138 138 138 138 138 136 136 136 … 136 133 133 133 … 133 130 130 130 … 130 116 116 116 … 116 36 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 73.3 … 72.9 52.1 … 52.3 36.4 … 36.3 25.2 … 25.2 17.6 … 17.6 … … 12.4 … … 8.08 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 4 5 6 76.7 76.7 76.7 51.0 51.0 51.0 36.7 36.7 36.7 25.1 25.1 25.1 17.6 17.6 17.6 12.4 12.4 12.4 8.08 8.08 8.08 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 10 11 65.3 76.7 76.7 76.7 76.7 43.5 51.0 51.0 51.0 51.0 31.5 36.7 36.7 36.7 36.7 21.5 25.1 25.1 25.1 25.1 15.0 17.6 17.6 17.6 17.6 10.4 12.4 12.4 12.4 12.4 6.73 8.08 8.08 8.08 8.08 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 12 13 14 74.7 … … 51.7 … … 36.5 … … 25.2 … … 17.6 … … 12.4 … … 8.08 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 15 16 17 18 19 73.3 73.3 72.9 72.9 … 52.1 52.1 52.3 52.3 … 36.4 36.4 36.3 36.3 … 25.2 25.2 25.2 25.2 … 17.6 17.6 17.6 17.6 … 12.4 12.4 12.4 12.4 … 8.08 8.08 8.08 8.08 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 23 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 24 25 26 80.9 80.9 80.9 64.0 64.0 64.0 47.7 47.7 47.7 34.5 34.5 34.5 23.5 23.5 23.5 15.5 15.5 15.5 9.39 9.39 9.39 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 27 28 29 30 69.0 80.9 80.9 80.9 54.5 64.0 64.0 64.0 40.4 47.7 47.7 47.7 29.1 34.5 34.5 34.5 19.8 23.5 23.5 23.5 12.9 15.5 15.5 15.5 8.06 9.39 9.39 9.39 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 80.9 80.9 … 64.0 64.0 … 47.7 47.7 … 34.5 34.5 … 23.5 23.5 … 15.5 15.5 … 9.39 9.39 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 90.4 … 64.0 … 45.0 … 30.1 … 19.7 … 12.9 … 8.06 … … … … … … … … … … … … … … … … … … … … … 36 37 38 39 40 89.4 89.4 89.4 … 89.4 64.3 64.3 64.3 … 64.3 44.9 44.9 44.9 … 44.9 30.1 30.1 30.1 … 30.1 19.7 19.7 19.7 … 19.7 12.9 12.9 12.9 … 12.9 8.06 8.06 8.06 … 8.06 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 37 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo Castings Forgings Forgings Plate SA-487 SA-508 SA-541 SA-542 8 22 22 B J22091 K21590 K21390 K21590 A 3 3 4 … … … … 5C 5C 5C 5C 1 1 1 1 5 6 7 8 9 21⁄4Cr – 1Mo – V 21⁄4Cr – 1Mo – V 21⁄4Cr – 1Mo – V 21⁄4Cr – 1Mo – V 21⁄4Cr – 1Mo – V Forgings Forgings Forgings Plate Plate SA-182 SA-336 SA-541 SA-542 SA-832 F22V F22V 22V D 22V K31835 K31835 K31835 K31835 K31835 … … … 4a … … … … … … 5C 5C 5C 5C 5C 1 1 1 1 1 10 11 12 3Cr – 1Mo 3Cr – 1Mo 3Cr – 1Mo Smls. tube Smls. pipe Forgings SA-213 SA-335 SA-336 T21 P21 F21 K31545 K31545 K31545 … … 1 … … … 5A 5A 5A 1 1 1 13 14 15 3Cr – 1Mo 3Cr – 1Mo 3Cr – 1Mo Forged pipe Plate Cast pipe SA-369 SA-387 SA-426 FP21 21 CP21 K31545 K31545 J31545 … 1 … … … … 5A 5A 5A 1 1 1 16 17 18 3Cr – 1Mo 3Cr – 1Mo 3Cr – 1Mo Forgings Forgings Plate SA-182 SA-336 SA-387 F21 F21 21 K31545 K31545 K31545 … 3 2 … … … 5A 5A 5A 1 1 1 19 20 21 22 23 24 3Cr – 1Mo – 1⁄4V – Ti – B 3Cr – 1Mo – 1⁄4V – Ti – B 3Cr – 1Mo – 1⁄4V – Ti – B 3Cr – 1Mo – 1⁄4V – Ti – B 3Cr – 1Mo – 1⁄4V – Ti – B 3Cr – 1Mo – 1⁄4V – Ti – B Forgings Forgings Forgings Forgings Plate Plate SA-182 SA-336 SA-508 SA-541 SA-542 SA-832 F3V F3V 3V 3V C 21V K31830 K31830 K31830 K31830 K31830 K31830 … … … … 4a … … … … … … … 5C 5C 5C 5C 5C 5C 1 1 1 1 1 1 25 26 27 28 29 30 3Cr – 1Mo – 1⁄4V – Cb – Ca 3Cr – 1Mo – 1⁄4V – Cb – Ca 3Cr – 1Mo – 1⁄4V – Cb – Ca 3Cr – 1Mo – 1⁄4V – Cb – Ca 3Cr – 1Mo – 1⁄4V – Cb – Ca 3Cr – 1Mo – 1⁄4V – Cb – Ca Forgings Forgings Forgings Forgings Plate Plate SA-182 SA-336 SA-508 SA-541 SA-542 SA-832 F3VCb F3VCb 3VCb 3VCb E 23V … … … … … … … … … … 4a … … … … … … … 5C 5C 5C 5C 5C 5C 1 1 1 1 1 1 31 32 33 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo Smls. tube SA-213 Smls. & wld. fittings SA-234 Smls. pipe SA-335 T5 WP5 P5 K41545 K41545 K41545 … … … … … … 5B 5B 5B 1 1 1 34 35 36 37 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo Forged pipe Plate Wld. pipe Forgings SA-369 SA-387 SA-691 SA-336 FP5 5 5CR F5 K41545 K41545 K41545 K41545 … 1 … … … … … … 5B 5B 5B 5B 1 1 1 1 38 39 40 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo Forgings Plate Forgings SA-182 SA-387 SA-336 F5 5 F5A K41545 K41545 K42544 … 2 … … … … 5B 5B 5B 1 1 1 41 42 43 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo Castings Cast pipe Forgings SA-217 SA-426 SA-182 C5 CP5 F5a J42045 J42045 K42544 … … … … … … 5B 5B 5B 1 1 1 Line No. 38 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 585 585 585 585 380 380 380 380 NP NP NP NP NP NP NP NP 538 454 454 454 NP NP NP NP CS-3 CS-2 CS-2 CS-2 G1, T4, W7 … … … 5 6 7 8 9 585 585 585 585 585 415 415 415 415 415 NP NP NP NP NP NP NP NP NP NP 482 482 482 482 482 NP NP NP NP NP CS-2 CS-2 CS-2 CS-2 CS-2 … … … … … 10 11 12 415 415 415 205 205 205 649 649 649 371 371 371 649 649 649 NP NP NP CS-2 CS-2 CS-2 S4, T3 S4, T3 S4, T3 13 14 15 415 415 415 205 205 205 649 649 NP 371 371 371 649 649 NP NP NP NP CS-2 CS-2 CS-2 S4, T3 S4, T3 G17 16 17 18 515 515 515 310 310 310 649 649 649 371 371 371 649 649 649 NP NP NP CS-3 CS-3 CS-3 S4, T3 S4, T3 S4, T3 19 20 21 22 23 24 585 585 585 585 585 585 415 415 415 415 415 415 NP NP NP NP NP NP NP NP NP NP NP NP 482 482 482 482 482 482 NP NP NP NP NP NP CS-3 CS-3 CS-3 CS-3 CS-3 CS-3 … … … … … … 25 26 27 28 29 30 585 585 585 585 585 585 415 415 415 415 415 415 NP NP NP NP NP NP NP NP NP NP NP NP 482 482 482 482 482 482 NP NP NP NP NP NP CS-3 CS-3 CS-3 CS-3 CS-3 CS-3 … … … … … … 31 32 33 415 415 415 205 205 205 649 649 649 371 371 371 649 649 649 NP NP NP CS-2 CS-2 CS-2 T4 T4, W14 T4 34 35 36 37 415 415 415 415 205 205 205 250 649 649 NP 649 371 371 371 NP 649 649 NP 649 NP NP NP NP CS-2 CS-2 CS-2 CS-2 T4 T4 G26, W10, W12 T4 38 39 40 485 515 550 275 310 345 649 NP 649 371 371 NP 649 649 649 NP NP NP CS-2 CS-3 CS-3 T3 T3 T3 41 42 43 620 620 620 415 415 450 649 NP 649 371 371 NP 649 NP 649 NP NP NP CS-3 CS-3 CS-5 G1, G17, T3 G17 T3 39 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 168 168 168 168 168 168 168 168 167 168 168 168 165 168 168 168 163 168 168 168 162 168 168 168 162 165 165 165 161 161 161 161 160 160 160 160 160 159 159 159 157 158 158 158 154 156 156 156 150 151 151 151 145 142 142 142 120 133 133 133 5 6 7 8 9 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 165 165 165 165 165 162 162 162 162 162 159 159 159 159 159 157 157 157 157 157 153 153 153 153 153 149 149 149 149 149 145 145 145 145 145 141 141 141 141 141 10 11 12 118 118 118 118 118 118 118 118 118 116 116 116 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 113 113 113 90.5 90.5 90.5 13 14 15 118 118 118 118 118 118 118 118 118 116 116 116 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 114 … 114 114 … 113 113 … 90.5 90.5 … 16 17 18 148 148 148 148 148 148 147 147 147 146 146 146 144 144 144 142 142 142 141 141 141 141 141 141 140 140 140 139 139 139 138 138 138 136 136 136 133 133 133 127 127 127 100 100 100 19 20 21 22 23 24 168 168 168 168 168 168 168 168 168 168 168 168 167 167 167 167 167 167 164 164 164 164 164 164 161 161 161 161 161 161 156 156 156 156 156 156 154 154 154 154 154 154 151 151 151 151 151 151 150 150 150 150 150 150 149 149 149 149 149 149 147 147 147 147 147 147 145 145 145 145 145 145 144 144 144 144 144 144 141 141 141 141 141 141 139 139 139 139 139 139 25 26 27 28 29 30 168 168 168 168 168 168 168 168 168 168 168 168 167 167 167 167 167 167 164 164 164 164 164 164 161 161 161 161 161 161 156 156 156 156 156 156 154 154 154 154 154 154 151 151 151 151 151 151 150 150 150 150 150 150 149 149 149 149 149 149 147 147 147 147 147 147 145 145 145 145 145 145 144 144 144 144 144 144 141 141 141 141 141 141 139 139 139 139 139 139 31 32 33 118 118 118 118 118 118 118 118 118 116 116 116 114 114 114 114 114 114 113 113 113 112 112 112 111 111 111 109 109 109 107 107 107 104 104 104 100 100 100 96.1 96.1 96.1 81.4 81.4 81.4 34 35 36 37 118 118 118 118 118 118 118 118 118 118 118 118 116 116 116 116 114 114 114 114 114 114 114 114 113 113 113 113 112 112 112 112 111 111 111 111 109 109 109 109 107 107 107 107 104 104 … 104 100 100 … 100 96.1 96.1 … 96.1 81.4 81.4 … 81.4 38 39 40 138 148 158 138 148 158 138 147 157 136 146 154 134 143 152 132 142 152 132 142 151 131 140 150 130 139 148 128 137 146 125 134 143 121 130 139 118 126 133 102 104 104 81.1 80.5 80.3 41 42 43 177 177 177 177 177 177 177 177 177 174 174 174 172 172 172 170 170 170 170 170 170 169 169 169 167 167 167 164 164 164 161 161 161 156 … 156 134 … 134 103 … 103 80.6 … 80.6 40 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 88.1 … … … 65.1 … … … 42.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 9 137 137 137 137 137 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 68.2 68.2 68.2 54.1 54.1 54.1 43.5 43.5 43.5 34.4 34.4 34.4 25.3 25.3 25.3 17.4 17.4 17.4 10.0 10.0 10.0 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 13 14 15 68.2 68.2 … 54.1 54.1 … 43.5 43.5 … 34.4 34.4 … 25.3 25.3 … 17.4 17.4 … 10.0 10.0 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 72.8 72.8 72.8 54.9 54.9 54.9 40.7 40.7 40.7 29.4 29.4 29.4 20.4 20.4 20.4 15.7 15.7 15.7 8.64 8.64 8.64 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 19 20 21 22 23 24 136 136 136 136 136 136 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 28 29 30 136 136 136 136 136 136 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 61.7 61.7 61.7 46.4 46.4 46.4 34.7 34.7 34.7 25.8 25.8 25.8 18.0 18.0 18.0 11.5 11.5 11.5 6.68 6.68 6.68 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 37 61.7 61.7 … 61.7 46.4 46.4 … 46.4 34.7 34.7 … 34.7 25.8 25.8 … 25.8 18.0 18.0 … 18.0 11.5 11.5 … 11.5 6.68 6.68 … 6.68 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 38 39 40 61.8 62.0 62.1 46.4 46.3 46.3 34.7 34.8 34.8 25.8 25.8 25.8 18.0 18.0 18.0 11.5 11.5 11.5 6.68 6.68 6.68 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 41 42 43 62.0 … 62.0 46.3 … 46.3 34.8 … 34.8 25.8 … 25.8 18.0 … 18.0 11.5 … 11.5 6.68 … 6.68 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 41 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 5Cr – 1⁄2Mo – Si 5Cr – 1⁄2Mo – Si 5Cr – 1⁄2Mo – Ti 5Cr – 1⁄2Mo – Ti Smls. tube Smls. pipe Smls. tube Smls. pipe SA-213 SA-335 SA-213 SA-335 T5b P5b T5c P5c K51545 K51545 K41245 K41245 … … … … … … … … 5B 5B 5B 5B 1 1 1 1 5 6 7 8 9Cr – 1Mo 9Cr – 1Mo 9Cr – 1Mo 9Cr – 1Mo Smls. tube Fittings Smls. pipe Forged pipe SA-213 SA-234 SA-335 SA-369 T9 WP9 P9 FP9 K90941 K90941 K90941 K90941 … … … … … … … … 5B 5B 5B 5B 1 1 1 1 9 10 11 12 9Cr – 1Mo 9Cr – 1Mo 9Cr – 1Mo 9Cr – 1Mo Forgings Forgings Castings Cast pipe SA-182 SA-336 SA-217 SA-426 F9 F9 C12 CP9 K90941 K90941 J82090 J82090 … … … … … … … … 5B 5B 5B 5B 1 1 1 1 13 14 15 16 9Cr – 1Mo – V 9Cr – 1Mo – V 9Cr – 1Mo – V 9Cr – 1Mo – V Forgings Forgings Smls. tube Smls. tube SA-182 SA-182 SA-213 SA-213 F91 F91 T91 T91 K90901 K90901 K90901 K90901 … … … … t ≤ 75 t > 75 t ≤ 75 t > 75 15E 15E 15E 15E 1 1 1 1 17 18 19 20 9Cr – 1Mo – V 9Cr – 1Mo – V 9Cr – 1Mo – V 9Cr – 1Mo – V Fittings Fittings Smls. pipe Smls. pipe SA-234 SA-234 SA-335 SA-335 WP91 WP91 P91 P91 K90901 K90901 K90901 K90901 … … … … t ≤ 75 t > 75 t ≤ 75 t > 75 15E 15E 15E 15E 1 1 1 1 21 22 23 24 25 26 9Cr – 1Mo – V 9Cr – 1Mo – V 9Cr – 1Mo – V 9Cr – 1Mo – V 9Cr – 1Mo – V 9Cr – 1Mo – V Forgings Forgings Forged pipe Forged pipe Plate Plate SA-336 SA-336 SA-369 SA-369 SA-387 SA-387 F91 F91 FP91 FP91 91 91 K90901 K90901 K90901 K90901 K90901 K90901 … … … … 2 2 t ≤ 75 t > 75 t ≤ 75 t > 75 t ≤ 75 t > 75 15E 15E 15E 15E 15E 15E 1 1 1 1 1 1 27 28 29 30 31 11Cr – Ti 11Cr – Ti 11Cr – Ti 11Cr – Ti 11Cr – Ti Plate Plate Plate Wld. tube Smls. tube SA-240 SA-240 SA-240 SA-268 SA-268 … … … TP409 TP409 S40910 S40920 S40930 S40900 S40900 … … … … … … … … … … 7 7 7 7 7 1 1 1 1 1 32 33 34 35 12Cr 12Cr 12Cr 12Cr Plate Bar Bar Plate SA-1010 SA-479 SA-479 SA-1010 40 403 403 50 S41003 S40300 S40300 S41003 … A 1 … t ≤ 19 … … t ≤ 19 7 6 6 7 1 1 1 1 36 37 38 39 12Cr – Al 12Cr – Al 12Cr – Al 12Cr – Al Bar Plate Plate Bar SA/JIS G4303 SA-240 SA-240 SA-479 SUS405 405 405 405 … S40500 S40500 S40500 … … … … … … … … 7 7 7 7 1 1 1 1 40 41 42 43 12Cr – Al 12Cr – Al 12Cr – Ti 12Cr – Ti Smls. & wld. tube Wld. tube Wld. tube Smls. tube SA-268 SA-268 SA-268 SA-268 TP405 TP405 … … S40500 S40500 S40800 S40800 … … … … … … … … 7 7 7 7 1 1 1 1 Line No. (10) (10) (10) (10) (10) (10) (10) 42 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 415 415 415 415 205 205 205 205 649 649 649 649 NP NP NP NP 649 649 649 649 NP NP NP NP CS-2 CS-2 CS-2 CS-2 T4 T4 T4 T4 5 6 7 8 415 415 415 415 205 205 205 205 649 649 649 649 371 NP 371 371 649 649 649 649 NP NP NP NP CS-2 CS-2 CS-2 CS-2 T5 T5 T5 T5 9 10 11 12 585 585 620 620 380 380 415 415 649 NP 649 NP NP NP 371 (SPT) 371 649 649 649 NP NP NP NP NP CS-3 CS-3 CS-3 CS-3 T4 T4 G1, T4 G17 13 14 15 16 585 585 585 585 415 415 415 415 649 649 649 649 371 NP 371 371 649 649 649 649 NP NP NP NP CS-3 CS-3 CS-3 CS-3 T7 T7 T7 T7 17 18 19 20 585 585 585 585 415 415 415 415 649 649 649 649 NP NP 371 NP NP NP 649 649 NP NP NP NP CS-3 CS-3 CS-3 CS-3 T7 T7 T7 T7 21 22 23 24 25 26 585 585 585 585 585 585 415 415 415 415 415 415 649 649 649 649 649 649 NP NP NP NP 371 NP 649 649 NP NP 649 649 NP NP NP NP NP NP CS-3 CS-3 CS-3 CS-3 CS-3 CS-3 T7 T7 T7 T7 T7 T7 27 28 29 30 31 380 380 380 380 380 170 170 170 170 170 NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 NP NP NP 343 343 CS-1 CS-1 CS-1 CS-1 CS-1 … … … G24 … 32 33 34 35 455 485 485 485 275 275 275 345 NP NP NP NP NP 371 371 NP 316 NP NP 316 316 NP NP 316 CS-2 … … CS-3 … … … … 36 37 38 39 410 415 415 415 174 170 170 170 NP 371 NP NP 371 NP 371 371 538 538 NP 538 NP 343 NP 343 CS-1 CS-1 CS-1 CS-1 G32, T5 G32, T5 G32 G32, T5 40 41 42 43 415 415 380 380 205 205 205 205 371 371 NP NP NP NP NP NP 538 538 427 427 343 343 343 343 CS-2 CS-2 CS-2 CS-2 G32, T5, W13, W14 G3, G24, G32, T5 G32, W14 G32 43 (10) (10) (10) (10) (10) (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (10) (10) (10) (10) (10) (10) (10) Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 118 118 118 118 118 118 118 118 118 118 118 118 116 116 116 116 114 114 114 114 114 114 114 114 113 113 113 113 112 112 112 112 111 111 111 111 109 109 109 109 107 107 107 107 104 104 104 104 100 100 100 100 96.1 96.1 96.1 96.1 81.4 81.4 81.4 81.4 5 6 7 8 118 118 118 118 118 118 118 118 118 118 118 118 116 116 116 116 114 114 114 114 114 114 114 114 113 113 113 113 112 112 112 112 111 111 111 111 109 109 109 109 107 107 107 107 104 104 104 104 100 100 100 100 95.8 95.8 95.8 95.8 91.8 91.8 91.8 91.8 9 10 11 12 168 168 177 177 167 167 177 177 166 166 177 177 164 164 174 174 162 162 172 172 161 161 170 170 161 161 170 170 159 159 169 169 157 157 167 167 155 155 164 164 152 152 161 161 147 147 156 … 142 142 151 … 137 137 145 … 121 121 123 … 13 14 15 16 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 167 167 167 167 166 166 166 166 164 164 164 164 163 163 163 163 161 161 161 161 157 157 157 157 153 153 153 153 147 147 147 147 141 141 141 141 134 134 134 134 17 18 19 20 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 167 167 167 167 166 166 166 166 164 164 164 164 163 163 163 163 161 161 161 161 157 157 157 157 153 153 153 153 147 147 147 147 141 141 141 141 134 134 134 134 21 22 23 24 25 26 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 168 167 167 167 167 167 167 166 166 166 166 166 166 164 164 164 164 164 164 163 163 163 163 163 163 161 161 161 161 161 161 157 157 157 157 157 157 153 153 153 153 153 153 147 147 147 147 147 147 141 141 141 141 141 141 134 134 134 134 134 134 27 28 29 30 31 108 108 108 92.4 108 104 104 104 88.4 104 98.8 98.8 98.8 82.3 98.8 94.4 94.4 94.4 84.1 94.4 90.1 90.1 90.1 76.6 90.1 83.8 83.8 83.8 71.2 83.8 80.5 80.5 80.5 68.4 80.5 78.2 78.2 78.2 66.5 78.2 77.9 77.9 77.9 66.2 77.9 77.9 77.9 77.9 66.2 77.9 77.9 77.9 77.9 66.2 77.9 77.2 77.2 77.2 65.6 77.2 76.6 76.6 76.6 65.1 76.6 76.0 76.0 76.0 64.6 76.0 … … … … … 32 33 34 35 130 138 138 138 130 138 138 138 130 138 138 138 130 137 137 138 130 135 135 138 127 133 133 135 123 131 131 131 119 129 129 126 117 127 127 124 … 124 124 … … 122 122 … … … … … … … … … … … … … … … … … 36 37 38 39 115 115 115 115 110 110 110 110 105 105 105 105 103 103 103 103 102 102 102 102 100 100 100 100 98.9 98.9 98.9 98.9 97.2 97.2 97.2 97.2 96.1 96.1 96.1 96.1 94.7 94.7 94.7 94.7 92.7 92.7 92.7 92.7 90.2 90.2 … 90.2 87.1 87.1 … 87.1 83.5 83.5 … 83.5 79.2 79.2 … 79.2 40 41 42 43 118 101 92.4 108 118 101 92.4 108 118 101 92.3 108 117 99.7 91.4 107 116 98.5 90.3 106 114 96.7 89.0 104 113 95.4 87.8 103 111 93.9 86.3 101 109 92.4 84.8 99.6 107 90.5 82.9 98.0 104 88.6 81.0 95.5 101 86.1 78.5 92.9 97.5 83.0 76.0 89.2 93.2 79.3 73.5 85.5 88.4 75.2 … … 44 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 61.7 61.7 61.7 61.7 46.4 46.4 46.4 46.4 34.7 34.7 34.7 34.7 25.8 25.8 25.8 25.8 18.0 18.0 18.0 18.0 11.5 11.5 11.5 11.5 6.68 6.68 6.68 6.68 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 80.3 80.3 80.3 80.3 61.0 61.0 61.0 61.0 42.9 42.9 42.9 42.9 30.0 30.0 30.0 30.0 20.6 20.6 20.6 20.6 14.4 14.4 14.4 14.4 10.2 10.2 10.2 10.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 10 11 12 89.0 89.0 88.2 … 60.7 60.7 61.0 … 43.1 43.1 43.0 … 30.0 30.0 30.0 … 20.6 20.6 20.6 … 14.4 14.4 14.4 … 10.2 10.2 10.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 13 14 15 16 126 126 126 126 117 118 117 118 107 103 107 103 88.5 80.6 88.5 80.6 65.0 61.6 65.0 61.6 45.5 45.7 45.5 45.7 28.9 28.9 28.9 28.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 17 18 19 20 126 126 126 126 117 118 117 118 107 103 107 103 88.5 80.6 88.5 80.6 65.0 61.6 65.0 61.6 45.5 45.7 45.5 45.7 28.9 28.9 28.9 28.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 24 25 26 126 126 126 126 126 126 117 118 117 118 117 118 107 103 107 103 107 103 88.5 80.6 88.5 80.6 88.5 80.6 65.0 61.6 65.0 61.6 65.0 61.6 45.5 45.7 45.5 45.7 45.5 45.7 28.9 28.9 28.9 28.9 28.9 28.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 27 28 29 30 31 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 36 37 38 39 67.3 67.3 … 67.3 41.9 41.9 … 41.9 14.1 14.1 … 14.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 40 41 42 43 70.6 59.8 … … 40.9 34.6 … … 14.5 12.4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 45 (10) (10) (10) (10) (10) (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 13Cr 13Cr 13Cr Plate Smls. & wld. tube Wld. tube SA-240 SA-268 SA-268 410S TP410 TP410 S41008 S41000 S41000 … … … … … … 7 6 6 1 1 1 4 5 6 7 8 13Cr 13Cr 13Cr 13Cr 13Cr Plate Forgings Bar Bar Bar SA-240 SA-182 SA-479 SA-479 SA-479 410 F6a 410 410 410 S41000 S41000 S41000 S41000 S41000 … 1 … A 1 … … … … … 6 6 6 6 6 1 1 1 1 1 9 10 11 12 13 13Cr 13Cr 13Cr 13Cr – 4Ni 13Cr – 4Ni Forgings Castings Cast pipe Castings Forgings SA-182 SA-217 SA-426 SA-487 SA-182 F6a CA15 CPCA15 CA6NM F6NM S41000 J91150 J91150 J91540 S41500 2 … … A … … … … … … 6 6 6 6 6 3 3 3 4 4 14 15 16 15Cr 15Cr 15Cr Wld. tube Smls. & wld. tube Plate SA-268 SA-268 SA-240 TP429 TP429 429 S42900 S42900 S42900 … … … … … … 6 6 6 2 2 2 17 18 19 20 17Cr 17Cr 17Cr 17Cr Wld. tube Smls. & wld. tube Plate Bar SA-268 SA-268 SA-240 SA-479 TP430 TP430 430 430 S43000 S43000 S43000 S43000 … … … … … … … … 7 7 7 7 2 2 2 2 (a) (a)(10) (a)(10) (a)(10) 21 22 23 24 17Cr – 4Ni – 3Cu 17Cr – 4Ni – 4Cu 17Cr – 4Ni – 4Cu 17Cr – 4Ni – 4Cu Castings Bar Plate Forgings SA-747 SA-564 SA-693 SA-705 CB7Cu-1 630 630 630 J92180 S17400 S17400 S17400 … H1150 H1150 H1150 … … … … … … … … … … … … (a)(10) (a)(10) (a)(10) 25 26 27 17Cr – 4Ni – 4Cu 17Cr – 4Ni – 4Cu 17Cr – 4Ni – 4Cu Bar Plate Forgings SA-564 SA-693 SA-705 630 630 630 S17400 S17400 S17400 H1100 H1100 H1100 … … … … … … … … … (a)(10) (a)(10) (a)(10) 28 29 30 17Cr – 4Ni – 4Cu 17Cr – 4Ni – 4Cu 17Cr – 4Ni – 4Cu Bar Plate Forgings SA-564 SA-693 SA-705 630 630 630 S17400 S17400 S17400 H1075 H1075 H1075 … … … … … … … … … (10) (10) (10) (10) (10) (10) 31 32 33 34 35 36 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) 37 38 39 40 41 … … 18Cr – 2Mo 18Cr – 2Mo 18Cr – 2Mo … … Plate Wld. tube Smls. tube … … SA-240 SA-268 SA-268 … … … … … … … S44400 S44400 S44400 … … … … … … … … … … … … 7 7 7 … … 2 2 2 Line No. 46 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 415 415 415 205 205 205 NP 371 371 371 NP NP 649 649 649 343 343 343 CS-2 CS-2 CS-2 T4 T4, W13, W14 G3, G24, T4 4 5 6 7 8 450 485 485 485 485 205 275 275 275 275 NP NP NP NP 371 NP 371 NP 371 371 649 538 538 NP NP 343 343 343 NP NP CS-2 CS-2 CS-2 CS-2 CS-2 T4 T4 G22, T4 … … 9 10 11 12 13 585 620 620 760 795 380 450 450 550 620 NP NP NP NP NP 371 371 371 371 371 649 649 NP 427 NP 343 343 NP 343 NP CS-3 CS-5 CS-5 CS-5 CS-3 T3 G1, G17, T3 G17 G1, G17 G17 14 15 16 415 415 450 240 240 205 371 371 NP NP NP NP 371 649 649 343 343 343 CS-2 CS-2 CS-2 G3, G32, W14 G32, T4, W13, W14 G32, T4 17 18 19 20 415 415 450 485 240 240 205 275 371 371 NP 371 NP 371 NP 371 649 649 649 538 343 343 343 343 CS-2 CS-2 CS-2 CS-2 G3, G24, G32, T4 G32, T4, W12, W13, W14 G32, T4 G22, G32, T4 21 22 23 24 1035 930 930 930 965 725 725 725 NP NP NP NP NP 343 343 343 93 343 NP NP NP NP NP NP HT-1 HT-1 HT-1 HT-1 G1, G28, W1 G31, G32, W1 G32, W1 G32, W1 (a) (a)(10) (a)(10) (a)(10) 25 26 27 965 965 965 795 795 795 NP NP NP 343 343 343 343 NP NP NP NP NP HT-1 HT-1 HT-1 G31, G32, W1 G32, W1 G32, W1 (a)(10) (a)(10) (a)(10) 28 29 30 1000 1000 1000 860 860 860 NP NP NP 343 343 343 NP NP NP NP NP NP HT-1 HT-1 HT-1 G32, W1 G32, W1 G32, W1 (a)(10) (a)(10) (a)(10) 31 32 33 34 35 36 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) (10) 37 38 39 40 41 … … 415 415 415 … … 275 275 275 … … NP NP NP … … NP NP NP … … 343 343 343 … … 343 343 343 … … CS-2 CS-2 CS-2 … … G32 G24, G32 G32 (10) (10) 47 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 118 118 101 118 118 101 118 118 101 117 117 99.7 116 116 98.5 114 114 96.7 113 113 95.4 111 111 93.9 109 109 92.4 107 107 90.5 104 104 88.6 101 101 86.1 97.5 97.5 82.9 93.0 93.0 79.4 88.3 88.3 74.1 4 5 6 7 8 128 138 138 138 138 128 138 138 138 138 126 138 138 138 138 125 137 137 137 137 123 135 135 135 135 120 133 133 133 133 119 131 131 131 131 117 129 129 129 129 115 127 127 127 127 114 124 124 124 124 111 122 122 122 122 108 118 118 … … 104 113 113 … … 100 109 109 … … 89.9 92.1 92.1 … … 9 10 11 12 13 168 177 177 216 227 168 177 177 216 227 167 177 177 216 227 166 176 176 215 227 164 174 174 212 227 162 171 171 208 225 159 169 169 204 217 157 166 166 200 209 154 163 163 198 205 151 160 160 195 202 148 156 156 192 197 143 151 … 189 … 138 146 … 184 … 123 117 … 180 … 93.5 83.3 … … … 14 15 16 101 118 128 101 118 128 101 118 126 99.7 117 125 98.5 116 123 96.7 114 120 95.4 113 119 93.9 111 117 92.4 109 115 90.5 107 114 88.6 104 111 … 101 108 … 97.5 104 … 93.3 101 … 86.2 87.8 17 18 19 20 101 118 128 138 101 118 128 138 101 118 126 138 99.7 117 125 137 98.5 116 123 135 96.7 114 120 133 95.4 113 119 131 93.9 111 117 129 92.4 109 115 127 90.5 107 114 124 88.6 104 111 122 86.1 101 108 118 83.0 97.5 104 113 79.4 93.3 101 109 73.3 86.2 87.8 90.1 (a) (a)(10) (a)(10) (a)(10) 21 22 23 24 221 266 266 266 221 266 266 266 221 266 266 266 … 266 266 266 … 266 266 266 … 259 259 259 … 254 254 254 … 251 251 251 … 249 249 249 … 247 247 247 … … … … … … … … … … … … … … … … … … … … (a)(10) (a)(10) (a)(10) 25 26 27 276 276 276 276 276 276 276 276 276 276 276 276 276 276 276 269 269 269 263 263 263 260 260 260 258 258 258 256 256 256 … … … … … … … … … … … … … … … (a)(10) (a)(10) (a)(10) 28 29 30 285 285 285 285 285 285 285 285 285 285 285 285 285 285 285 279 279 279 273 273 273 270 270 270 267 267 267 265 265 265 … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) (10) 31 32 33 34 35 36 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) 37 38 39 40 41 … … 118 101 118 … … 118 101 118 … … 118 101 118 … … 116 99.0 116 … … 114 97.1 114 … … 112 95.3 112 … … 110 93.5 110 … … 107 91.3 107 … … 105 89.7 105 … … 104 87.7 104 … … … … … … … … … … … … … … … … … … … … … … … … … 48 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 69.7 69.7 60.0 50.7 50.7 42.8 37.9 37.9 31.9 26.4 26.4 22.4 18.0 18.0 15.5 11.6 11.6 9.59 6.68 6.68 5.69 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 4 5 6 7 8 69.2 68.4 68.4 … … 50.9 51.3 51.3 … … 37.8 37.0 37.0 … … 26.4 … … … … 18.0 … … … … 11.6 … … … … 6.68 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 10 11 12 13 68.0 60.1 … … … 51.3 42.0 … … … 37.7 28.6 … … … 26.4 19.8 … … … 17.9 13.8 … … … 11.6 9.81 … … … 6.68 6.76 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 … 70.9 70.4 … 52.8 53.0 … 38.1 38.1 … 27.5 27.5 … 20.5 20.5 … 15.9 15.9 … 12.2 12.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 17 18 19 20 60.2 70.9 70.4 69.5 44.8 52.8 53.0 53.6 32.2 38.1 38.1 36.5 23.2 27.5 27.5 … 17.3 20.5 20.5 … 13.3 15.9 15.9 … 10.2 12.2 12.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 24 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (a) (a)(10) (a)(10) (a)(10) 25 26 27 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (a)(10) (a)(10) (a)(10) 28 29 30 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (a)(10) (a)(10) (a)(10) 31 32 33 34 35 36 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) (10) 37 38 39 40 41 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) 49 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 5 18Cr – Ti 18Cr – Ti 18Cr – Ti 18Cr – Ti 18Cr – Ti Wld. tube Smls. tube Wld. tube Wld. pipe Smls. pipe SA-268 SA-268 SA-803 SA-731 SA-731 TP439 TP439 TP439 TP439 TP439 S43035 S43035 S43035 S43035 S43035 … … … … … … … … … … 7 7 7 7 7 2 2 2 2 2 6 7 8 18Cr – Ti 18Cr – Ti 18Cr – Ti Smls. tube Wld. tube Bar SA-268 SA-268 SA-479 TP430 Ti TP430 Ti 439 S43036 S43036 S43035 … … … … … … 7 7 7 2 2 2 9 10 11 12 13 26Cr – 3Ni – 3Mo 26Cr – 3Ni – 3Mo 26Cr – 3Ni – 3Mo 26Cr – 3Ni – 3Mo 26Cr – 3Ni – 3Mo Plate Smls. tube Wld. tube Wld. tube Wld. tube SA-240 SA-268 SA-268 SA-268 SA-803 26-3-3 26-3-3 26-3-3 26-3-3 26-3-3 S44660 S44660 S44660 S44660 S44660 … … … … … ≤5 ≤5 ≤5 ≤5 ≤5 10K 10K 10K 10K 10K 1 1 1 1 1 (10) (10) (10) (10) (10) 14 15 16 17 18 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) 19 20 21 22 23 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 24 25 26 27Cr 27Cr – 1Mo 27Cr – 1Mo Smls. tube Forgings Plate SA-268 SA-182 SA-240 TP446-1 FXM-27Cb XM-27 S44600 S44627 S44627 … … … … … … 10I 10I 10I 1 1 1 27 28 29 30 31 27Cr – 1Mo 27Cr – 1Mo 27Cr – 1Mo 27Cr – 1Mo 27Cr – 1Mo Wld. tube Smls. tube Bar Smls. pipe Wld. pipe SA-268 SA-268 SA-479 SA-731 SA-731 TPXM-27 TPXM-27 XM-27 TPXM-27 TPXM-27 S44627 S44627 S44627 S44627 S44627 … … … … … … … … … … 10I 10I 10I 10I 10I 1 1 1 1 1 32 33 34 35 36 27Cr – 1Mo – Ti 27Cr – 1Mo – Ti 27Cr – 1Mo – Ti 27Cr – 1Mo – Ti 27Cr – 1Mo – Ti Smls. pipe Wld. pipe Plate Smls. tube Wld. tube SA-731 SA-731 SA-240 SA-268 SA-268 TPXM-33 TPXM-33 XM-33 TPXM-33 TPXM-33 S44626 S44626 S44626 S44626 S44626 … … … … … … … … … … 10I 10I 10I 10I 10I 1 1 1 1 1 37 38 39 40 29Cr – 4Mo 29Cr – 4Mo 29Cr – 4Mo 29Cr – 4Mo Bar Plate Smls. tube Wld. tube SA-479 SA-240 SA-268 SA-268 … … 29-4 29-4 S44700 S44700 S44700 S44700 … … … … … … … … 10J 10J 10J 10J 1 1 1 1 Line No. (10) (10) 50 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 415 415 415 415 415 205 205 205 205 205 427 427 NP 427 427 NP NP NP NP NP 427 427 316 NP NP 343 343 316 NP NP CS-2 CS-2 CS-2 CS-2 CS-2 G24, G32 G32 G24, G32 G24, G32 G32 6 7 8 415 415 485 240 240 275 NP NP NP NP NP NP 427 427 538 NP NP 343 CS-2 CS-2 CS-2 G32 G24, G32 G22, G32, T4 9 10 11 12 13 585 585 585 585 585 450 450 450 450 450 NP NP NP NP NP NP 371 371 NP NP 371 371 NP 371 316 343 343 NP 343 316 HA-5 HA-5 HA-5 HA-5 HA-5 G32 G32, H5 G32, H5, W12 G24, G32 G24, G32 14 15 16 17 18 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) 19 20 21 22 23 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) 24 25 26 485 415 450 275 240 275 371 NP NP NP NP 343 343 343 343 343 343 343 CS-2 HA-2 HA-2 G32 G32 G32 27 28 29 30 31 450 450 450 450 450 275 275 275 275 275 NP NP NP NP NP NP 343 371 NP NP 343 343 343 343 343 343 343 343 343 343 HA-2 HA-2 HA-2 HA-2 HA-2 G24, G32 G32 G22, G32 G32 G24, G32 32 33 34 35 36 450 450 470 470 470 275 275 310 310 310 NP NP NP NP NP NP NP NP NP NP 343 343 343 343 343 343 343 343 343 343 HA-2 HA-2 HA-6 HA-6 HA-6 G32 G24, G32 G32 G32 G24, G32 37 38 39 40 485 550 550 550 380 415 415 415 NP NP NP NP NP NP NP NP 316 316 316 316 316 316 316 316 HA-6 HA-6 HA-6 HA-6 G22, G32 G32 G32 G24, G32 51 (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 5 101 118 101 101 118 101 118 101 101 118 100 118 100 100 118 96.5 113 96.5 96.5 113 91.5 108 91.5 91.5 108 85.9 101 85.9 85.9 101 81.9 96.6 81.9 81.9 96.6 80.3 94.0 80.3 80.3 94.0 79.7 93.8 79.7 79.7 93.8 79.3 93.7 … 79.3 93.7 79.2 93.0 … 79.2 93.0 78.6 92.3 … 78.6 92.3 77.3 91.1 … 77.3 91.1 76.1 89.8 … 76.1 89.8 … … … … … 6 7 8 118 100 138 118 100 138 118 100 138 116 98.5 136 114 97.0 133 111 94.6 130 109 92.8 127 107 90.8 124 105 89.7 123 104 88.3 121 102 86.7 119 99.7 84.8 116 97.0 82.5 113 93.8 79.7 110 … … 91.7 9 10 11 12 13 168 168 168 142 142 168 168 168 142 142 168 168 168 142 142 167 167 167 142 142 167 167 167 142 142 165 165 165 140 140 164 164 164 139 139 163 163 163 139 139 162 162 162 138 138 162 162 162 138 … 161 161 161 137 … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) 14 15 16 17 18 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) 19 20 21 22 23 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 24 25 26 138 118 128 138 118 128 138 118 128 136 116 127 133 114 126 130 111 125 127 111 125 124 111 125 123 111 125 121 111 125 119 … … … … … … … … … … … … … … 27 28 29 30 31 109 128 128 128 109 109 128 128 128 109 109 128 128 128 109 108 127 127 127 108 107 126 126 126 107 106 125 125 125 106 106 125 125 125 106 106 125 125 125 106 106 125 125 125 106 106 125 125 125 106 … … 125 … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 128 109 134 134 114 128 109 134 134 114 128 109 134 134 114 128 109 134 134 113 127 108 133 133 113 126 106 131 131 112 124 106 130 130 111 122 104 128 128 109 121 103 126 126 108 119 101 124 124 106 … … … … … … … … … … … … … … … … … … … … … … … … … 37 38 39 40 138 158 158 134 138 158 158 134 138 157 157 134 135 155 155 132 133 152 152 130 132 151 151 128 132 151 151 128 132 151 151 128 132 151 151 128 … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) 52 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 … … 69.9 … … 53.5 … … 36.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 10 11 12 13 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 17 18 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) 19 20 21 22 23 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) 24 25 26 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 27 28 29 30 31 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 37 38 39 40 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 53 (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 5 6 29Cr – 4Mo – 2Ni 29Cr – 4Mo – 2Ni 29Cr – 4Mo – 2Ni 29Cr – 4Mo – 2Ni 29Cr – 4Mo – Ti 29Cr – 4Mo – Ti Bar Plate Smls. tube Wld. tube Smls. tube Wld. tube SA-479 SA-240 SA-268 SA-268 SA-268 SA-268 … … 29-4-2 29-4-2 … … S44800 S44800 S44800 S44800 S44735 S44735 … … … … … … … … … … … … 10K 10K 10K 10K 10J 10J 1 1 1 1 1 1 7 8 9 Mn – 1⁄4Mo Mn – 1⁄4Mo – V Mn – 1⁄4Mo – V Forgings Castings Castings SA-372 SA-487 SA-487 D 2 2 K14508 J13005 J13005 … A B … … … … 3 3 … 3 3 10 11 12 13 14 15 Mn – 1⁄2Mo Mn – 1⁄2Mo Mn – 1⁄2Mo Mn – 1⁄2Mo Mn – 1⁄2Mo Mn – 1⁄2Mo Plate Wld. pipe Plate Plate Plate Plate SA-302 SA-672 SA-302 SA-533 SA-533 SA-533 A H75 B A A A K12021 K12021 K12022 K12521 K12521 K12521 … … … 1 2 3 … … … … … … 3 3 3 3 3 11A 2 2 3 3 3 4 16 17 18 Mn – 1⁄2Mo – 1⁄4Ni Mn – 1⁄2Mo – 1⁄4Ni Mn – 1⁄2Mo – 1⁄4Ni Plate Plate Plate SA-533 SA-533 SA-533 D D D K12529 K12529 K12529 1 2 3 … … … 3 3 11A 3 3 4 19 20 21 22 Mn – 1⁄2Mo – 1⁄2Ni Mn – 1⁄2Mo – 1⁄2Ni Mn – 1⁄2Mo – 1⁄2Ni Mn – 1⁄2Mo – 1⁄2Ni Plate Plate Wld. pipe Wld. pipe SA-302 SA-533 SA-672 SA-672 C B H80 J80 K12039 K12539 K12039 K12539 … 1 … … … … … … 3 3 3 3 3 3 3 3 23 24 25 26 Mn – 1⁄2Mo – 1⁄2Ni Mn – 1⁄2Mo – 1⁄2Ni Mn – 1⁄2Mo – 1⁄2Ni Mn – 1⁄2Mo – 1⁄2Ni Plate Wld. pipe Plate Wld. pipe SA-533 SA-672 SA-533 SA-672 B J90 B J100 K12539 K12539 K12539 K12539 2 … 3 … … … … … 3 3 11A 11A 3 3 4 4 27 28 29 30 Mn – 1⁄2Mo – 3⁄4Ni Mn – 1⁄2Mo – 3⁄4Ni Mn – 1⁄2Mo – 3⁄4Ni Mn – 1⁄2Mo – 3⁄4Ni Plate Plate Plate Plate SA-302 SA-533 SA-533 SA-533 D C C C K12054 K12554 K12554 K12554 … 1 2 3 … … … … 3 3 3 11A 3 3 3 4 31 32 33 34 35 Mn – 1⁄2Ni – V Mn – V Mn – V Mn – V 11⁄2Si – 1⁄2Mo Plate Castings Castings Castings Smls. pipe SA-225 SA-487 SA-487 SA-487 SA-335 C 1 1 1 P15 K12524 J13002 J13002 J13002 K11578 … A A B … … … … … … 10A 10A 10A 10A 3 1 1 1 1 1 36 37 38 39 40 1 ⁄2Ni – 1⁄2Cr – 1⁄4Mo – V ⁄2Ni – 1⁄2Cr – 1⁄4Mo – V 1 ⁄2Ni – 1⁄2Cr – 1⁄4Mo – V 1 ⁄2Ni – 1⁄2Mo – V 1 ⁄2Ni – 1⁄2Mo – V Castings Castings Castings Forgings Forgings SA-487 SA-487 SA-487 SA-541 SA-541 4 4 4 3 3 J13047 J13047 J13047 K12045 K12045 A B E 1 2 … … … … … 3 11A 11A 3 3 3 3 3 3 3 41 42 43 3 Forgings Plate Forgings SA-592 SA-517 SA-592 F F F K11576 K11576 K11576 … … … 64 < t ≤ 100 ≤ 64 ≤ 64 11B 11B 11B 3 3 3 Line No. 1 ⁄4Ni – 1⁄2Cr – 1⁄2Mo – V ⁄4Ni – 1⁄2Cr – 1⁄2Mo – V 3 ⁄4Ni – 1⁄2Cr – 1⁄2Mo – V 3 54 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 6 485 550 550 550 515 515 380 415 415 415 415 415 NP NP NP NP NP NP NP NP NP NP NP NP 316 316 316 316 316 316 316 316 316 316 316 316 HA-6 HA-6 HA-6 HA-6 HA-6 HA-6 G22, G32 G32 G32 G24, G32 G32 G24, G32 7 8 9 725 585 620 450 365 450 NP NP NP 343 371 (SPT) NP 343 343 343 343 343 343 CS-5 CS-3 CS-5 G25, W2, W11 G1 G1 10 11 12 13 14 15 515 515 550 550 620 690 310 310 345 345 485 570 538 NP 538 NP NP NP 371 371 371 371 371 371 538 NP 538 538 427 NP 343 NP 343 NP NP NP CS-3 CS-3 CS-3 CS-5 CS-5 CS-5 G11, S2, T3 S6, W10, W12 G11, S2, T3 G23, T4 … … 16 17 18 550 620 690 345 485 570 NP NP NP 371 371 371 NP 427 399 NP NP 343 CS-5 CS-5 CS-5 … … … 19 20 21 22 550 550 550 550 345 345 345 345 538 NP NP NP 371 371 371 371 538 427 NP NP 343 NP NP NP CS-3 CS-5 CS-3 CS-5 G11, S2, T3 G23 G26, W10, W12 G26, W10, W12 23 24 25 26 620 620 690 690 485 485 570 570 NP NP NP NP 371 371 371 371 427 NP 399 NP NP NP 343 NP CS-5 CS-5 CS-5 CS-5 … G26, W10, W12 … G26, W10, W12 27 28 29 30 550 550 620 690 345 345 485 570 538 NP NP NP 371 371 371 371 538 427 427 NP 343 NP NP NP CS-3 CS-5 CS-5 CS-5 G11, S2, T3 G23 … … 31 32 33 34 35 725 585 585 620 415 485 380 380 450 205 NP NP NP NP NP NP 371 (SPT) NP NP NP 371 NP 343 343 538 343 NP 343 343 343 CS-5 CS-3 CS-3 CS-5 CS-2 … … G1 G1 T3 36 37 38 39 40 620 725 795 550 620 415 585 655 345 450 NP NP NP NP NP 343 NP NP 371 371 343 371 371 427 371 343 343 343 343 NP CS-3 CS-5 CS-5 CS-5 CS-5 G1 G1 G1 G23 … 41 42 43 725 795 795 620 690 690 NP NP NP 343 (SPT) 343 (SPT) NP 343 343 343 343 343 343 CS-5 HT-1 HT-1 S7 … … 55 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 5 6 138 158 158 134 148 125 137 156 156 133 146 125 135 154 154 131 144 123 134 153 153 130 144 122 133 152 152 130 143 121 132 151 151 128 141 121 131 149 149 127 140 119 129 147 147 125 139 118 128 147 147 124 138 117 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 207 168 177 207 168 177 207 168 177 207 168 177 207 168 177 207 167 177 207 167 177 207 167 177 207 167 177 207 166 177 … 166 … … … … … … … … … … … … … 10 11 12 13 14 15 148 148 158 158 177 197 148 148 158 158 177 197 148 148 158 158 177 197 148 148 158 158 177 197 148 148 158 158 177 197 148 148 158 158 177 197 148 148 158 158 177 197 148 148 158 158 177 197 148 148 158 158 177 197 148 148 158 158 177 197 148 148 158 158 177 197 148 … 158 158 177 … 148 … 158 158 177 … 142 … 143 154 177 … 107 … 106 106 … … 16 17 18 158 177 197 158 177 197 158 177 197 158 177 197 158 177 197 158 177 197 158 177 197 158 177 197 158 177 197 158 177 197 158 177 197 … 177 197 … 177 … … 177 … … … … 19 20 21 22 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 158 … … 158 158 … … 143 158 … … 106 … … … 23 24 25 26 177 177 197 197 177 177 197 197 177 177 197 197 177 177 197 197 177 177 197 197 177 177 197 197 177 177 197 197 177 177 197 197 177 177 197 197 177 177 197 197 177 177 197 197 177 … 197 … 177 … … … 177 … … … … … … … 27 28 29 30 158 158 177 197 158 158 177 197 158 158 177 197 158 158 177 197 158 158 177 197 158 158 177 197 158 158 177 197 158 158 177 197 158 158 177 197 158 158 177 197 158 158 177 197 158 158 177 … 158 158 177 … 143 158 177 … 106 … … … 31 32 33 34 35 207 168 168 177 118 207 163 163 173 118 207 158 158 169 118 207 155 156 168 118 207 154 155 167 118 207 154 155 166 118 207 154 155 166 118 207 152 153 166 117 207 150 150 164 115 207 147 148 160 114 207 143 … … 112 … … … … 110 … … … … 107 … … … … 96.9 … … … … 88.8 36 37 38 39 40 177 207 227 158 177 177 207 227 158 177 177 207 227 158 177 177 207 227 158 177 177 207 227 158 177 177 207 227 158 177 177 207 227 158 177 177 207 227 158 177 177 207 227 158 177 177 207 227 158 177 … 207 227 158 177 … … … 158 … … … … 158 … … … … 158 … … … … … … 41 42 43 207 227 227 207 227 227 207 227 227 207 227 227 207 227 227 207 227 227 207 227 227 207 227 227 207 227 227 207 226 226 … … … … … … … … … … … … … … … 56 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 14 15 68.1 … 68.4 77.2 … … 43.1 … 43.0 55.6 … … 23.1 … 23.1 32.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 19 20 21 22 68.4 … … … 43.0 … … … 23.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 23 24 25 26 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 27 28 29 30 68.4 … … … 43.0 … … … 23.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 34 35 … … … … 76.4 … … … … 55.6 … … … … 32.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 36 37 38 39 40 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 41 42 43 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 57 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 5 6 3 ⁄4Ni – 1⁄2Cu – Mo ⁄4Ni – 1⁄2Cu – Mo 3 ⁄4Ni – 1⁄2Mo – 1⁄3Cr – V 3 ⁄4Ni – 1⁄2Mo – 1⁄3Cr – V 3 ⁄4Ni – 1⁄2Mo – 1⁄3Cr – V 3 ⁄4Ni – 1⁄2Mo – 1⁄3Cr – V Smls. & wld. tube Wld. tube Forgings Forgings Forgings Forgings SA-423 SA-423 SA-508 SA-541 SA-508 SA-541 2 2 2 2 2 2 K11540 K11540 K12766 K12765 K12766 K12765 … … 1 1 2 2 … … … … … … 4 4 3 3 3 3 2 2 3 3 3 3 7 8 9 3 3 ⁄4Ni – 1⁄2Mo – Cr – V ⁄4Ni – 1⁄2Mo – Cr – V 3 ⁄4Ni – 1Mo – 3⁄4Cr Forgings Forgings Castings SA-508 SA-508 SA-217 3 3 WC5 K12042 K12042 J22000 1 2 … … … … 3 3 4 3 3 1 10 11 12 1Ni – 1⁄2Cr – 1⁄2Mo 11⁄4Ni – 1Cr – 1⁄2Mo 11⁄4Ni – 1Cr – 1⁄2Mo Castings Plate Plate SA-217 SA-517 SA-517 WC4 P P J12082 K21650 K21650 … … … … 64 < t ≤ 100 ≤ 64 4 11B 11B 1 8 8 13 14 15 11⁄2Ni 11⁄2Ni 13⁄4Ni – 3⁄4Cr – Mo Forgings Forgings Forgings SA-350 SA-350 SA-372 LF5 LF5 L K13050 K13050 K24055 1 2 … … … … 9A 9A … 1 1 … 16 17 18 19 20 2Ni – 1Cu 2Ni – 1Cu 2Ni – 1Cu 2Ni – 1Cu 2Ni – 1Cu Forgings Fittings Pipe Smls. pipe Wld. pipe SA-182 SA-234 SA-333 SA-333 SA-333 FR WPR 9 9 9 K22035 K22035 K22035 K22035 K22035 … … … … … … … … … … 9A 9A 9A 9A 9A 1 1 1 1 1 21 22 23 2Ni – 1Cu 2Ni – 1Cu 2Ni – 1Cu Tube SA-334 Forgings SA-350 Smls. & wld. fittings SA-420 9 LF9 WPL9 K22035 K22036 K22035 … … … … … … 9A 9A 9A 1 1 1 24 25 26 27 28 2Ni – 11⁄2Cr – 1⁄4Mo – V 2Ni – 11⁄2Cr – 1⁄4Mo – V 2Ni – 11⁄2Cr – 1⁄4Mo – V 2Ni – 11⁄2Cr – 1⁄4Mo – V 2Ni – 11⁄2Cr – 1⁄4Mo – V Forgings Forgings Forgings Forgings Forgings SA-723 SA-723 SA-723 SA-723 SA-723 1 1 1 1 1 K23550 K23550 K23550 K23550 K23550 1 2 3 4 5 … … … … … … … … … … … … … … … 29 30 31 32 21⁄2Ni 21⁄2Ni 21⁄2Ni 21⁄2Ni Pipe Wld. pipe Tube Wld. tube SA-333 SA-333 SA-334 SA-334 7 7 7 7 K21903 K21903 K21903 K21903 … … … … … … … … 9A 9A 9A 9A 1 1 1 1 33 34 35 21⁄2Ni 21⁄2Ni 21⁄2Ni Plate Plate Castings SA-203 SA-203 SA-352 A B LC2 K21703 K22103 J22500 … … … … … … 9A 9A 9A 1 1 1 36 37 38 23⁄4Ni – 11⁄2Cr – 1⁄2Mo 23⁄4Ni – 11⁄2Cr – 1⁄2Mo 23⁄4Ni – 11⁄2Cr – 1⁄2Mo Plate Plate Plate SA-543 SA-543 SA-543 C C C … … … 3 1 2 … … … 3 11A 11B 3 5 10 39 40 41 42 43 23⁄4Ni – 11⁄2Cr – 1⁄2Mo – V 23⁄4Ni – 11⁄2Cr – 1⁄2Mo – V 23⁄4Ni – 11⁄2Cr – 1⁄2Mo – V 23⁄4Ni – 11⁄2Cr – 1⁄2Mo – V 23⁄4Ni – 11⁄2Cr – 1⁄2Mo – V Forgings Forgings Forgings Forgings Forgings SA-723 SA-723 SA-723 SA-723 SA-723 2 2 2 2 2 K34035 K34035 K34035 K34035 K34035 1 2 3 4 5 … … … … … … … … … … … … … … … Line No. 3 58 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 6 415 415 550 550 620 620 255 255 345 345 450 450 343 343 NP NP NP NP NP NP 371 371 371 371 343 343 427 427 371 371 NP NP 343 343 NP NP CS-2 CS-2 CS-5 CS-5 CS-5 CS-5 W13, W14 G3, G24 G23 G23 … … 7 8 9 550 620 485 345 450 275 NP NP 593 371 371 371 427 371 593 343 NP NP CS-5 CS-5 CS-2 G23 … G1, G17, T4 10 11 12 485 725 795 275 620 690 538 NP NP 371 371 (SPT) 343 (SPT) 538 343 343 NP 343 343 CS-2 CS-5 HT-1 G1, G17, T4 … … 13 14 15 415 485 1070 205 260 930 NP NP NP NP NP NP 260 260 343 260 260 343 CS-2 CS-2 … … … W11 16 17 18 19 20 435 435 435 435 435 315 315 315 315 315 NP NP NP NP NP NP NP NP 38 NP 38 38 38 NP 38 38 NP 38 NP 38 CS-3 CS-3 CS-3 CS-3 CS-3 … … … … G24 21 22 23 435 435 435 315 315 315 NP NP NP NP NP 38 38 38 38 38 38 38 CS-3 CS-3 CS-3 … … W14 24 25 26 27 28 795 930 1070 1205 1310 690 825 965 1105 1240 NP NP NP NP NP 371 (SPT) 371 (SPT) 371 (SPT) 371 (SPT) 371 (SPT) NP NP NP NP NP NP NP NP NP NP HT-1 HT-1 HT-1 HT-1 HT-1 W1 W1 W1 W1 W1 29 30 31 32 450 450 450 450 240 240 240 240 NP NP NP NP NP NP NP NP 343 343 343 343 343 343 343 343 CS-2 CS-2 CS-2 CS-2 … G24 … G24 33 34 35 450 485 485 255 275 275 NP NP NP 371 343 38 538 538 343 343 343 343 CS-2 CS-2 CS-2 T2 S1, T2 G1 36 37 38 620 725 795 485 585 690 NP NP NP NP NP NP 343 343 343 NP NP NP CS-5 CS-5 HT-1 … … … 39 40 41 42 43 795 930 1070 1205 1310 690 825 965 1105 1240 NP NP NP NP NP 371 (SPT) 371 (SPT) 371 (SPT) 371 (SPT) 371 (SPT) NP NP NP NP NP NP NP NP NP NP HT-1 HT-1 HT-1 HT-1 HT-1 W1 W1 W1 W1 W1 59 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 5 6 118 101 158 158 177 177 118 101 158 158 177 177 118 101 158 158 177 177 118 101 158 158 177 177 118 101 158 158 177 177 118 101 158 158 177 177 118 101 158 158 177 177 118 101 158 158 177 177 118 101 158 158 177 177 118 101 158 158 177 177 … … 158 158 177 177 … … 158 158 … … … … 158 158 … … … … 158 158 … … … … … … … … 7 8 9 158 177 138 158 177 138 158 177 138 158 177 138 158 177 138 158 177 138 158 177 138 158 177 138 158 177 138 158 177 138 158 177 138 158 … 138 158 … 138 158 … 135 … … 120 10 11 12 138 207 227 138 207 227 138 207 227 138 207 227 138 207 227 138 207 227 138 207 227 138 207 227 138 207 227 138 206 226 138 202 … 138 … … 138 … … 135 … … 113 … … 13 14 15 118 138 305 116 135 305 113 132 305 111 129 305 108 126 305 106 123 305 105 123 305 … … 305 … … 302 … … 294 … … … … … … … … … … … … … … … 16 17 18 19 20 125 125 125 123 105 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 125 125 125 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 24 25 26 27 28 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 226 265 305 343 373 222 261 299 337 367 217 255 293 330 359 … … … … … … … … … … … … … … … … … … … … 29 30 31 32 128 109 128 109 128 109 128 109 128 109 128 109 128 109 128 109 128 109 128 109 128 109 128 109 128 109 128 109 124 105 124 105 119 101 119 101 114 96.7 114 96.7 … … … … … … … … … … … … … … … … … … … … 33 34 35 128 138 138 128 138 138 128 138 138 128 138 138 128 138 138 128 138 138 128 138 138 128 138 138 126 136 136 120 129 129 112 122 … 95.1 101 … 79.6 83.8 … 64.8 67.3 … 49.1 49.4 … 36 37 38 177 207 227 177 207 227 177 207 227 177 207 227 177 207 227 176 205 224 175 204 223 173 202 221 172 200 219 169 197 217 … … … … … … … … … … … … … … … 39 40 41 42 43 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 226 265 305 343 373 222 261 299 337 367 217 255 293 330 359 … … … … … … … … … … … … … … … … … … … … 60 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 … … 89.3 … … 58.8 … … 39.6 … … 27.4 … … 16.3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 76.6 … … 49.7 … … 31.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 13 14 15 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 20 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 24 25 26 27 28 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 30 31 32 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 33 34 35 35.8 35.6 … 23.7 23.7 … 11.1 11.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 36 37 38 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 39 40 41 42 43 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 61 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 3Ni – 13⁄4Cr – 1⁄2Mo 3Ni – 13⁄4Cr – 1⁄2Mo 3Ni – 13⁄4Cr – 1⁄2Mo 3Ni – 13⁄4Cr – 1⁄2Mo 3Ni – 13⁄4Cr – 1⁄2Mo Plate Forgings Plate Plate Forgings SA-543 SA-372 SA-543 SA-543 SA-372 B M B B M K42339 K42365 K42339 K42339 K42365 3 85 1 2 100 … … … … … 3 … 11A 11B … 3 … 5 10 … 6 7 8 9 10 31⁄2Ni 31⁄2Ni 31⁄2Ni 31⁄2Ni 31⁄2Ni Pipe Wld. pipe Tube Wld. tube Fittings SA-333 SA-333 SA-334 SA-334 SA-420 3 3 3 3 WPL3 K31918 K31918 K31918 K31918 … … … … … … … … … … … 9B 9B 9B 9B 9B 1 1 1 1 1 11 12 13 14 31⁄2Ni 31⁄2Ni 31⁄2Ni 31⁄2Ni Plate Forgings Forgings Forgings SA-203 SA-350 SA-350 SA-765 D LF3 LF3 III K31718 K32025 K32025 K32026 … 1 2 … … … … … 9B 9B 9B 9B 1 1 1 1 15 16 17 18 19 31⁄2Ni 31⁄2Ni 31⁄2Ni 31⁄2Ni 31⁄2Ni Plate Plate Castings Plate Plate SA-203 SA-203 SA-352 SA-203 SA-203 E E LC3 F F K32018 K32018 J31550 … … … … … … … … … … > 50 ≤ 50 9B 9B 9B 9B 9B 1 1 1 1 1 20 21 22 31⁄2Ni – 13⁄4Cr – 1⁄2Mo – V 31⁄2Ni – 13⁄4Cr – 1⁄2Mo – V 31⁄2Ni – 13⁄4Cr – 1⁄2Mo – V Forgings Forgings Forgings SA-508 SA-508 SA-508 4N 4N 4N K22375 K22375 K22375 3 1 2 … … … 3 11A 11B 3 5 10 23 24 25 26 27 4Ni – 11⁄2Cr – 1⁄2Mo – V 4Ni – 11⁄2Cr – 1⁄2Mo – V 4Ni – 11⁄2Cr – 1⁄2Mo – V 4Ni – 11⁄2Cr – 1⁄2Mo – V 4Ni – 11⁄2Cr – 1⁄2Mo – V Forgings Forgings Forgings Forgings Forgings SA-723 SA-723 SA-723 SA-723 SA-723 3 3 3 3 3 K44045 K44045 K44045 K44045 K44045 1 2 3 4 5 … … … … … … … … … … … … … … … 28 29 30 31 5Ni – 1⁄4Mo 8Ni 8Ni 8Ni Plate Forgings Plate Plate SA-645 SA-522 SA-553 SA-553 A II II II K41583 K71340 K71340 K71340 … … … … … … … … 11A 11A 11A 11A 2 1 1 1 32 33 34 35 36 9Ni 9Ni 9Ni 9Ni 9Ni Smls. & wld. pipe Smls. & wld. pipe Smls. pipe Smls. pipe Wld. pipe SA-333 SA-333 SA-333 SA-333 SA-333 8 8 8 8 8 K81340 K81340 K81340 K81340 K81340 … … … … … … … … … … 11A 11A 11A 11A 11A 1 1 1 1 1 37 38 39 40 41 9Ni 9Ni 9Ni 9Ni 9Ni Wld. tube Smls. & wld. tube Smls. tube Smls. tube Wld. tube SA-334 SA-334 SA-334 SA-334 SA-334 8 8 8 8 8 K81340 K81340 K81340 K81340 K81340 … … … … … … … … … … 11A 11A 11A 11A 11A 1 1 1 1 1 42 43 44 9Ni 9Ni 9Ni Plate Plate Plate SA-353 SA-353 SA-353 … … … K81340 K81340 K81340 … … … … … … 11A 11A 11A 1 1 1 Line No. 1 2 3 4 5 (10) 62 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 620 725 725 795 825 485 585 585 690 690 NP NP NP NP NP NP NP NP NP NP 343 343 343 343 343 NP 343 NP NP 343 CS-5 … CS-5 HT-1 … … W11 … … W11 6 7 8 9 10 450 450 450 450 450 240 240 240 240 240 NP NP NP NP NP NP NP NP NP NP 343 343 343 343 343 343 343 343 343 343 CS-2 CS-2 CS-2 CS-2 CS-2 … G24 … G24 … 11 12 13 14 450 485 485 485 255 260 260 260 NP NP NP NP 371 343 343 NP 538 343 343 343 343 343 343 343 CS-2 CS-2 CS-2 CS-2 T2 … … … 15 16 17 18 19 485 485 485 515 550 275 275 275 345 380 NP NP NP NP NP 149 (SPT) 343 38 NP NP NP 538 343 343 343 NP 343 343 343 343 CS-2 CS-2 CS-2 CS-3 CS-3 S1 T2 G1 … … 20 21 22 620 725 795 485 585 690 NP NP NP NP 316 (SPT) NP 343 343 343 343 NP NP CS-5 CS-5 HT-1 … … … 23 24 25 26 27 795 930 1070 1205 1310 690 825 965 1105 1240 NP NP NP NP NP 371 (SPT) 371 (SPT) 371 (SPT) 371 (SPT) 371 (SPT) NP NP NP NP NP NP NP NP NP NP HT-1 HT-1 HT-1 HT-1 HT-1 W1 W1 W1 W1 W1 28 29 30 31 655 690 690 690 450 515 585 585 NP NP NP NP NP 93 (Cl. 3 only) 93 (Cl. 3 only) 93 (Cl. 3 only) 121 NP 121 121 121 NP 121 121 CS-3 CS-3 CS-3 CS-3 … G33, W5 G33, W5 G33, W4 32 33 34 35 36 690 690 690 690 690 515 515 515 515 515 NP NP NP NP NP 93 (Cl. 3 only) 93 (Cl. 3 only) NP NP NP NP NP 121 121 121 NP NP 121 121 121 CS-3 CS-3 CS-3 CS-3 CS-3 G33, W12 G33, W5, W12 G33, W4 G33, W5 G24, G33, W3 37 38 39 40 41 690 690 690 690 690 515 515 515 515 515 NP NP NP NP NP 93 (Cl. 3 only) 93 (Cl. 3 only) NP NP NP NP NP 121 121 121 NP NP 121 121 121 CS-3 CS-3 CS-3 CS-3 CS-3 G33, W12 G33, W5, W12 G33, W4 G33, W5 G24, G33, W3 42 43 44 690 690 690 515 515 515 NP NP NP 93 (Cl. 3 only) NP 93 (Cl. 3 only) 121 121 NP 121 121 NP CS-3 CS-3 CS-3 G33, W4 G33, W5 G33, W5 63 (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (10) Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 5 177 207 207 227 236 177 207 207 227 236 177 207 207 227 236 177 207 207 227 236 177 207 207 227 236 176 205 205 224 234 175 204 204 223 233 173 202 202 221 231 172 200 200 219 229 169 197 197 217 226 … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 10 128 109 128 109 128 128 109 128 109 128 128 109 128 109 128 128 109 128 109 128 128 109 128 109 128 128 109 128 109 128 128 109 128 109 128 124 105 124 105 124 119 101 119 101 119 114 96.7 114 96.7 114 … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 128 138 138 138 128 138 138 138 128 138 138 138 128 138 138 138 128 138 138 138 128 138 138 138 128 138 138 138 128 133 133 133 126 128 128 128 120 122 122 122 112 … … … 95.1 … … … 79.6 … … … 64.8 … … … 49.1 … … … 15 16 17 18 19 138 138 138 148 158 138 138 138 148 158 138 138 138 148 158 138 138 138 148 158 138 138 138 148 158 … 138 138 148 158 … 138 138 148 158 … 138 138 148 158 … 136 136 146 152 … 129 129 140 137 … 122 … … … … 101 … … … … 83.8 … … … … 67.3 … … … … 49.4 … … … 20 21 22 177 207 227 177 207 227 177 207 227 177 207 227 177 207 227 176 205 224 175 204 223 173 202 221 172 200 219 169 197 217 … … … … … … … … … … … … … … … 23 24 25 26 27 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 227 266 305 345 374 226 265 305 343 373 222 261 299 337 367 217 255 293 330 359 … … … … … … … … … … … … … … … … … … … … 28 29 30 31 187 187 187 197 187 187 187 197 186 173 173 182 183 … 169 178 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 197 187 197 187 168 197 187 197 187 168 182 173 182 173 155 … … 178 169 152 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 37 38 39 40 41 197 187 197 187 168 197 187 197 187 168 182 173 182 173 155 … … 178 169 152 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 42 43 44 197 187 187 197 187 187 182 173 173 178 169 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 64 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 10 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 35.8 … … … 23.7 … … … 11.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 15 16 17 18 19 … 35.6 … … … … 23.7 … … … … 11.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 23 24 25 26 27 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 31 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 37 38 39 40 41 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 42 43 44 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 65 (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 9Ni 9Ni 9Ni 9Ni Smls. & wld. fittings Smls. & wld. fittings Forgings Forgings SA-420 SA-420 SA-522 SA-522 WPL8 WPL8 I I K81340 K81340 K81340 K81340 … … … … … … … … 11A 11A 11A 11A 1 1 1 1 5 6 7 9Ni 9Ni 25Ni – 15Cr – 2Ti Plate Plate Bar SA-553 SA-553 SA-638 I I 660 K81340 K81340 S66286 … … … … … … 11A 11A … 1 1 … 8 9 10 11 12 13 27Ni – 22Cr – 7Mo – Mn – Cu – N 27Ni – 22Cr – 7Mo – Mn – Cu – N 27Ni – 22Cr – 7Mo – Mn – Cu – N 27Ni – 22Cr – 7Mo – Mn – Cu – N 27Ni – 22Cr – 7Mo – Mn – Cu – N 27Ni – 22Cr – 7Mo – Mn – Cu – N Smls. tube Smls. tube Plate Plate Wld. tube Wld. tube SA-213 SA-213 SA-240 SA-240 SA-249 SA-249 … … … … … … S31277 S31277 S31277 S31277 S31277 S31277 … … … … … … … … … … … … 45 45 45 45 45 45 … … … … … … (10) (10) (10) (10) 14 15 16 17 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) 18 19 20 21 … … 29Ni – 20Cr – 3Cu – 2Mo 29Ni – 20Cr – 3Cu – 2Mo … … Castings Castings … … SA-351 SA-351 … … CN7M CN7M … … J95150 J95150 … … … … … … … … … … 45 45 … … … … 22 23 24 25 16Cr – 4Ni – 6Mn 16Cr – 4Ni – 6Mn 16Cr – 9Mn – 2Ni – N 16Cr – 9Mn – 2Ni – N Plate Plate Plate Plate SA-240 SA-240 SA-240 SA-240 201LN 201LN 204 204 S20153 S20153 S20400 S20400 … … … … … … … … 8 8 8 8 3 3 3 3 26 27 28 29 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Forgings Forgings Forgings Forgings SA-182 SA-182 SA-965 SA-965 F316L F316L F316L F316L S31603 S31603 S31603 S31603 … … … … > 125 > 125 … … 8 8 8 8 1 1 1 1 30 31 32 33 34 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Bar Forgings Forgings Smls. tube Smls. tube SA/JIS G4303 SA-182 SA-182 SA-213 SA-213 SUS316L F316L F316L TP316L TP316L … S31603 S31603 S31603 S31603 … … … … … … ≤ 125 ≤ 125 … … 8 8 8 8 8 1 1 1 1 1 35 36 37 38 39 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Plate Plate Wld. tube Wld. tube Wld. tube SA-240 SA-240 SA-249 SA-249 SA-249 316L 316L TP316L TP316L TP316L S31603 S31603 S31603 S31603 S31603 … … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 40 41 42 43 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Smls. & wld. pipe Smls. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP316L TP316L TP316L TP316L S31603 S31603 S31603 S31603 … … … … … … … … 8 8 8 8 1 1 1 1 Line No. 66 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 690 690 690 690 515 515 515 515 NP NP NP NP NP NP 93 (Cl. 3 only) NP 121 121 121 121 121 121 121 121 CS-3 CS-3 CS-3 CS-3 G33, W4 G33, W3 G33, S8, W4 G33, S8, W5 5 6 7 690 690 895 585 585 585 NP NP NP 93 (Cl. 3 only) 93 (Cl. 3 only) 371 121 121 371 121 121 NP CS-3 CS-3 HA-5 G33, W4 G33, W5 W1 8 9 10 11 12 13 772 772 772 772 772 772 359 359 359 359 359 359 NP NP NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 427 NP NP NP NP NP NP NFN-26 NFN-26 NFN-26 NFN-26 NFN-26 NFN-26 14 15 16 17 … … … … … … … … … … … … … … … … … … … … … … … … … … … … 18 19 20 21 … … 425 425 … … 170 170 … … 316 316 … … 316 (Cl. 3 only) NP … … 316 316 … … NP NP … … NFN-9 NFN-9 22 23 24 25 655 655 655 655 310 310 330 330 NP NP NP NP NP NP NP NP 427 427 482 482 343 343 343 343 HA-6 HA-6 HA-6 HA-6 G5 … G5 … 26 27 28 29 450 450 450 450 170 170 170 170 454 454 454 454 427 NP 427 NP 454 454 454 454 343 343 343 343 HA-4 HA-4 HA-4 HA-4 G5, G34 G34 G5, G34 G34 30 31 32 33 34 480 485 485 485 485 175 170 170 170 170 454 454 454 454 454 427 427 NP 427 NP 454 454 454 454 454 NP 343 343 NP NP HA-4 HA-4 HA-4 HA-4 HA-4 G5, G22, G34 G5, G34 G34 G5, G34 G34 35 36 37 38 39 485 485 485 485 485 170 170 170 170 170 454 454 NP 454 454 427 NP 427 NP NP 454 454 NP 454 454 343 343 NP 343 343 HA-4 HA-4 HA-4 HA-4 HA-4 G5, G34 G34 G5, W12 G5, G24, G34 G24, G34 40 41 42 43 485 485 485 485 170 170 170 170 454 454 454 454 427 NP NP NP 454 454 454 454 343 343 343 343 HA-4 HA-4 HA-4 HA-4 G5, G34, W12, W14 G34 G5, G24, G34 G24, G34 67 G5 … G5 … G3, G5 … … … … … (10) (10) (10) (10) … … G1, G5 G1 (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 197 187 197 187 197 187 197 187 182 173 182 173 178 169 178 169 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 197 187 256 197 187 256 182 173 256 178 169 256 … … 256 … … 256 … … 253 … … 248 … … 246 … … 243 … … 241 … … … … … … … … … … … … 8 9 10 11 12 13 221 221 221 221 188 188 221 221 221 221 188 188 220 219 220 219 187 186 … … … … … … 212 198 212 198 180 169 203 184 203 184 173 156 197 177 197 177 167 150 191 175 191 175 162 149 189 175 189 175 160 149 186 175 186 175 158 149 185 175 185 175 157 149 183 173 183 173 155 147 181 172 181 172 154 146 181 172 181 172 154 146 … … … … … … (10) (10) (10) (10) 14 15 16 17 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) 18 19 20 21 … … 115 115 … … 114 107 … … 109 97.7 … … 101 92.8 … … 93.5 88.8 … … 88.5 81.9 … … 84.3 75.6 … … 80.9 70.4 … … 79.4 68.0 … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 25 187 187 187 187 177 177 175 175 164 161 160 160 152 152 150 149 146 146 142 140 139 139 131 124 136 136 125 115 136 134 124 110 135 131 123 108 135 127 123 107 134 124 123 107 132 120 123 105 130 115 122 104 128 112 120 102 … … 117 99.5 26 27 28 29 115 115 115 115 115 106 115 106 115 96.3 115 96.3 115 91.3 115 91.3 115 87.4 115 87.4 109 81.2 109 81.2 103 76.0 103 76.0 98.0 72.5 98.0 72.5 95.7 71.2 95.7 71.2 94.1 70.0 94.1 70.0 92.8 68.8 92.8 68.8 90.9 67.5 90.9 67.5 89.0 66.3 89.0 66.3 87.8 65.0 87.8 65.0 86.6 63.8 86.6 63.8 30 31 32 33 34 115 115 115 115 115 115 115 106 115 106 115 115 96.3 115 96.3 115 115 91.3 115 91.3 115 115 87.4 115 87.4 109 109 81.2 109 81.2 103 103 76.0 103 76.0 98.0 98.0 72.5 98.0 72.5 95.7 95.7 71.2 95.7 71.2 94.1 94.1 70.0 94.1 70.0 92.8 92.8 68.8 92.8 68.8 90.9 90.9 67.5 90.9 67.5 89.0 89.0 66.3 89.0 66.3 87.8 87.8 65.0 87.8 65.0 86.6 86.6 63.8 86.6 63.8 35 36 37 38 39 115 115 115 97.9 97.9 115 106 115 97.9 90.3 115 96.3 115 97.9 82.1 115 91.3 115 97.9 77.8 115 87.4 115 97.9 74.3 109 81.2 109 93.0 68.7 103 76.0 103 87.2 64.8 98.0 72.5 98.0 82.9 61.4 95.7 71.2 95.7 81.6 60.4 94.1 70.0 94.1 80.2 59.7 92.8 68.8 92.8 78.4 58.4 90.9 67.5 90.9 77.2 57.2 89.0 66.3 89.0 75.9 55.9 87.8 65.0 87.8 74.7 55.2 86.6 63.8 … 73.4 54.7 40 41 42 43 115 115 97.9 97.9 115 106 97.9 90.3 115 96.3 97.9 82.1 115 91.3 97.9 77.8 115 87.4 97.9 74.3 109 81.2 93.0 68.7 103 76.0 87.2 64.8 98.0 72.5 82.9 61.4 95.7 71.2 81.6 60.4 94.1 70.0 80.2 59.7 92.8 68.8 78.4 58.4 90.9 67.5 77.2 57.2 89.0 66.3 75.9 55.9 87.8 65.0 74.7 55.2 86.6 63.8 73.4 54.7 68 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 8 9 10 11 12 13 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 17 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) 18 19 20 21 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) 22 23 24 25 … … 114 96.4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 26 27 28 29 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 30 31 32 33 34 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 35 36 37 38 39 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 40 41 42 43 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 69 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 5 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Wld. pipe Smls. & wld. fittings Wld. pipe Bar Bar SA-358 SA-403 SA-409 SA-479 SA-479 316L 316L TP316L 316L 316L S31603 S31603 S31603 S31603 S31603 1 … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 6 7 8 9 10 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Wld. tube Wld. tube Wld. tube Wld. pipe Wld. pipe SA-688 SA-688 SA-688 SA-813 SA-814 TP316L TP316L TP316L TP316L TP316L S31603 S31603 S31603 S31603 S31603 … … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 (a) 11 12 13 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Castings Castings Cast pipe SA-351 SA-351 SA-451 CF3M CF3M CPF3M J92800 J92800 J92800 … … … … … … 8 8 8 1 1 1 (a) 14 15 16 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Castings Castings Cast pipe SA-351 SA-351 SA-451 CF8M CF8M CPF8M J92900 J92900 J92900 … … … … … … 8 8 8 1 1 1 17 18 19 20 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Forgings Forgings Forgings Forgings SA-182 SA-182 SA-965 SA-965 F316 F316 F316 F316 S31600 S31600 S31600 S31600 … … … … > 125 > 125 … … 8 8 8 8 1 1 1 1 21 22 23 24 25 26 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Forgings Forgings Smls. tube Smls. tube Plate Plate SA-182 SA-182 SA-213 SA-213 SA-240 SA-240 F316 F316 TP316 TP316 316 316 S31600 S31600 S31600 S31600 S31600 S31600 … … … … … … ≤ 125 ≤ 125 … … … … 8 8 8 8 8 8 1 1 1 1 1 1 27 28 29 30 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Wld. tube Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 SA-249 TP316 TP316 TP316 TP316 S31600 S31600 S31600 S31600 … … … … … … … … 8 8 8 8 1 1 1 1 31 32 33 34 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Smls. & wld. pipe Smls. & wld. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP316 TP316 TP316 TP316 S31600 S31600 S31600 S31600 … … … … … … … … 8 8 8 8 1 1 1 1 35 36 37 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Wld. pipe Smls. pipe Smls. pipe SA-358 SA-376 SA-376 316 TP316 TP316 S31600 S31600 S31600 1 … … … … … 8 8 8 1 1 1 38 39 40 41 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Smls. & wld. fittings Wld. pipe Bar Bar SA-403 SA-409 SA-479 SA-479 316 TP316 316 316 S31600 S31600 S31600 S31600 … … … … … … … … 8 8 8 8 1 1 1 1 Line No. 70 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 485 485 485 485 485 170 170 170 170 170 NP NP NP 454 454 427 427 427 427 NP NP 454 NP 454 454 NP 343 NP 343 343 HA-4 HA-4 HA-4 HA-4 HA-4 G5 G5, W12, W14 G5 G5, G22, G34 G22, G34 6 7 8 9 10 485 485 485 485 485 170 170 170 170 170 NP NP NP NP NP 427 NP NP 427 427 NP 454 454 NP NP NP 343 343 NP NP HA-4 HA-4 HA-4 HA-4 HA-4 G5, W12 G5, G24 G24 G5, W12 G5, W12 11 12 13 485 485 485 205 205 205 NP NP NP 427 NP 427 454 454 427 343 343 NP HA-4 HA-4 HA-4 G1, G5, G16, G17, G32 G1, G32 G1, G5, G16, G17, G32 (a) 14 15 16 485 485 485 205 205 205 816 816 NP 427 NP 427 816 816 427 343 343 NP HA-2 HA-2 HA-2 G1, G5, G12, G16, G17, G32, H1, T6 G1, G12, G32, H1, T8 G1, G5, G16, G17, G32 (a) 17 18 19 20 485 485 485 485 205 205 205 205 816 816 816 816 427 NP 427 NP 816 816 816 816 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, T8 G12, T9 G5, G12, T8 G12, T9 21 22 23 24 25 26 515 515 515 515 515 515 205 205 205 205 205 205 816 816 816 816 816 816 427 NP 427 NP 427 NP 816 816 816 816 816 816 NP NP NP NP 343 343 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, G12, T8 G12, T9 G5, G12, T8 G12, T9 G5, G12, T8 G12, T9 27 28 29 30 515 515 515 515 205 205 205 205 816 816 816 816 NP 427 NP NP NP NP 816 816 NP NP 343 343 HA-2 HA-2 HA-2 HA-2 G12, T9, W13 G5, G12, T8, W12, W13 G3, G5, G12, G24, T7 G3, G12, G24, T9 31 32 33 34 515 515 515 515 205 205 205 205 816 816 816 816 427 NP NP NP 816 816 816 816 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, T8, W12, W13, W14 G12, T9, W13, W14 G3, G5, G12, G24, T7 G3, G12, G24, T9 35 36 37 515 515 515 205 205 205 NP 816 816 427 427 NP NP 816 816 NP 343 343 HA-2 HA-2 HA-2 G5, W12 G5, G12, H1, T8, W12 G12, H1, T9 38 39 40 41 515 515 515 515 205 205 205 205 NP NP 816 816 427 427 427 NP 816 NP 816 816 343 NP 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, T8, W12, W14 G5, W12 G5, G12, G22, H1, T8 G12, G22, H1, T9 71 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 5 115 115 115 115 115 115 115 115 115 106 115 115 115 115 96.3 115 115 115 115 91.3 115 115 115 115 87.4 109 109 109 109 81.2 103 103 103 103 76.0 98.0 98.0 98.0 98.0 72.5 95.7 95.7 95.7 95.7 71.2 94.1 94.1 94.1 94.1 70.0 92.8 92.8 92.8 92.8 68.8 90.9 90.9 90.9 90.9 67.5 89.0 89.0 89.0 89.0 66.3 87.8 87.8 87.8 87.8 65.0 … 86.6 … 86.6 63.8 6 7 8 9 10 115 97.9 97.9 115 115 115 97.9 90.3 115 115 115 97.9 82.1 115 115 115 97.9 77.8 115 115 115 97.9 74.3 115 115 109 93.0 68.7 109 109 103 87.2 64.8 103 103 98.0 82.9 61.4 98.0 98.0 95.7 81.6 60.4 95.7 95.7 94.1 80.2 59.7 94.1 94.1 92.8 78.4 58.4 92.8 92.8 90.9 77.2 57.2 90.9 90.9 89.0 75.9 55.9 89.0 89.0 87.8 74.7 55.2 87.8 87.8 … 73.4 54.7 … … (a) 11 12 13 138 138 138 138 128 138 138 117 138 136 111 136 134 107 134 133 98.5 133 125 92.7 125 119 88.2 119 116 86.1 116 114 84.4 114 112 83.2 112 111 82.0 111 110 81.1 110 108 80.2 108 107 79.5 … (a) 14 15 16 138 138 138 138 128 138 138 117 138 136 111 136 134 107 134 133 98.5 133 125 92.7 125 119 88.2 119 116 86.1 116 114 84.4 114 112 83.2 112 111 82.0 111 110 81.1 110 108 80.2 108 107 79.5 … 17 18 19 20 138 138 138 138 138 128 138 128 138 118 138 118 136 112 136 112 134 107 134 107 133 99.2 133 99.2 126 92.8 126 92.8 119 88.1 119 88.1 116 86.1 116 86.1 114 84.1 114 84.1 112 82.9 112 82.9 111 82.0 111 82.0 110 81.4 110 81.4 108 80.6 108 80.6 108 79.8 108 79.8 21 22 23 24 25 26 138 138 138 138 138 138 138 128 138 128 138 128 138 118 138 118 138 118 138 112 138 112 138 112 138 107 138 107 138 107 134 99.2 134 99.2 134 99.2 126 92.8 126 92.8 126 92.8 119 88.1 119 88.1 119 88.1 116 86.1 116 86.1 116 86.1 114 84.1 114 84.1 114 84.1 112 82.9 112 82.9 112 82.9 111 82.0 111 82.0 111 82.0 110 81.4 110 81.4 110 81.4 108 80.6 108 80.6 108 80.6 108 79.8 108 79.8 108 79.8 27 28 29 30 138 138 117 117 128 138 117 109 118 138 117 99.8 112 138 117 94.9 107 138 117 90.8 99.2 134 114 84.0 92.8 126 107 78.8 88.1 119 101 74.7 86.1 116 99.0 73.3 84.1 114 96.8 72.1 82.9 112 95.7 70.8 82.0 111 94.4 69.6 81.4 110 93.1 69.0 80.6 108 92.5 68.4 79.8 108 91.4 67.7 31 32 33 34 138 138 117 117 138 128 117 109 138 118 117 99.8 138 112 117 94.9 138 107 117 90.8 134 99.2 114 84.0 126 92.8 107 78.8 119 88.1 101 74.7 116 86.1 99.0 73.3 114 84.1 96.8 72.1 112 82.9 95.7 70.8 111 82.0 94.4 69.6 110 81.4 93.1 69.0 108 80.6 92.5 68.4 108 79.8 91.4 67.7 35 36 37 138 138 138 138 138 128 138 138 118 138 138 112 138 138 107 134 134 99.2 126 126 92.8 119 119 88.1 116 116 86.1 114 114 84.1 112 112 82.9 111 111 82.0 110 110 81.4 108 108 80.6 … 108 79.8 38 39 40 41 138 138 138 138 138 138 138 128 138 138 138 118 138 138 138 112 138 138 138 107 134 134 134 99.2 126 126 126 92.8 119 119 119 88.1 116 116 116 86.1 114 114 114 84.1 112 112 112 82.9 111 111 111 82.0 110 110 110 81.4 108 108 108 80.6 108 … 108 79.8 72 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 10 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (a) 14 15 16 107 78.9 … 104 78.2 … 94.7 77.6 … 73.7 73.7 … 57.9 57.9 … 46.0 46.0 … 36.9 36.9 … 30.1 30.1 … 24.3 24.3 … 20.3 20.3 … 17.0 17.0 … 14.3 14.3 … 12.1 12.1 … 10.3 10.3 … … … … … … … … … … (a) 17 18 19 20 107 79.2 107 79.2 106 78.7 106 78.7 105 77.8 105 77.8 99.8 77.1 99.8 77.1 80.3 75.0 80.3 75.0 65.5 65.5 65.5 65.5 50.4 50.4 50.4 50.4 38.6 38.6 38.6 38.6 29.6 29.6 29.6 29.6 23.0 23.0 23.0 23.0 17.7 17.7 17.7 17.7 13.4 13.4 13.4 13.4 10.4 10.4 10.4 10.4 8.05 8.05 8.05 8.05 … … … … … … … … … … … … 21 22 23 24 25 26 107 79.2 107 79.2 107 79.2 106 78.7 106 78.7 106 78.7 105 77.8 105 77.8 105 77.8 99.8 77.1 99.8 77.1 99.8 77.1 80.3 75.0 80.3 75.0 80.3 75.0 65.5 65.5 65.5 65.5 65.5 65.5 50.4 50.4 50.4 50.4 50.4 50.4 38.6 38.6 38.6 38.6 38.6 38.6 29.6 29.6 29.6 29.6 29.6 29.6 23.0 23.0 23.0 23.0 23.0 23.0 17.7 17.7 17.7 17.7 17.7 17.7 13.4 13.4 13.4 13.4 13.4 13.4 10.4 10.4 10.4 10.4 10.4 10.4 8.05 8.05 8.05 8.05 8.05 8.05 … … … … … … … … … … … … … … … … … … 27 28 29 30 79.2 107 90.5 67.1 78.7 106 89.9 66.5 77.8 105 89.3 65.9 77.1 99.8 85.3 65.3 75.0 80.3 68.1 64.0 65.5 65.5 55.6 55.6 50.4 50.4 42.9 42.9 38.6 38.6 33.0 33.0 29.6 29.6 25.3 25.3 23.0 23.0 19.4 19.4 17.7 17.7 14.7 14.7 13.4 13.4 11.3 11.3 10.4 10.4 8.90 8.90 8.05 8.05 6.77 6.77 … … … … … … … … … … … … 31 32 33 34 107 79.2 90.5 67.1 106 78.7 89.9 66.5 105 77.8 89.3 65.9 99.8 77.1 85.3 65.3 80.3 75.0 68.1 64.0 65.5 65.5 55.6 55.6 50.4 50.4 42.9 42.9 38.6 38.6 33.0 33.0 29.6 29.6 25.3 25.3 23.0 23.0 19.4 19.4 17.7 17.7 14.7 14.7 13.4 13.4 11.3 11.3 10.4 10.4 8.90 8.90 8.05 8.05 6.77 6.77 … … … … … … … … … … … … 35 36 37 … 107 79.2 … 106 78.7 … 105 77.8 … 99.8 77.1 … 80.3 75.0 … 65.5 65.5 … 50.4 50.4 … 38.6 38.6 … 29.6 29.6 … 23.0 23.0 … 17.7 17.7 … 13.4 13.4 … 10.4 10.4 … 8.05 8.05 … … … … … … … … … 38 39 40 41 107 … 107 79.2 106 … 106 78.7 105 … 105 77.8 99.8 … 99.8 77.1 80.3 … 80.3 75.0 65.5 … 65.5 65.5 50.4 … 50.4 50.4 38.6 … 38.6 38.6 29.6 … 29.6 29.6 23.0 … 23.0 23.0 17.7 … 17.7 17.7 13.4 … 13.4 13.4 10.4 … 10.4 10.4 8.05 … 8.05 8.05 … … … … … … … … … … … … 73 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 5 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Wld. tube Wld. tube Wld. tube Wld. pipe Wld. pipe SA-688 SA-688 SA-688 SA-813 SA-814 TP316 TP316 TP316 TP316 TP316 S31600 S31600 S31600 S31600 S31600 … … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 6 7 8 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Bar Plate Plate SA/JIS G4303 SA/EN 10028-7 SA/EN 10028-7 SUS316 X5CrNiMo17-12-2 X5CrNiMo17-12-2 … … … … … … … ≤ 75 ≤ 75 8 8 8 1 1 1 9 10 11 12 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Forgings Forgings Forgings Forgings SA-182 SA-182 SA-965 SA-965 F316H F316H F316H F316H S31609 S31609 S31609 S31609 … … … … > 125 > 125 … … 8 8 8 8 1 1 1 1 13 14 15 16 17 18 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Forgings Forgings Smls. tube Smls. tube Plate Plate SA-182 SA-182 SA-213 SA-213 SA-240 SA-240 F316H F316H TP316H TP316H 316H 316H S31609 S31609 S31609 S31609 S31609 S31609 … … … … … … ≤ 125 ≤ 125 … … … … 8 8 8 8 8 8 1 1 1 1 1 1 19 20 21 22 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Wld. tube Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 SA-249 TP316H TP316H TP316H TP316H S31609 S31609 S31609 S31609 … … … … … … … … 8 8 8 8 1 1 1 1 23 24 25 26 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Smls. & wld. pipe Smls. & wld. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP316H TP316H TP316H TP316H S31609 S31609 S31609 S31609 … … … … … … … … 8 8 8 8 1 1 1 1 27 28 29 30 31 32 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Wld. pipe Smls. pipe Smls. pipe Smls. & wld. fittings Bar Bar SA-358 SA-376 SA-376 SA-403 SA-479 SA-479 316H TP316H TP316H 316H 316H 316H S31609 S31609 S31609 S31609 S31609 S31609 1 … … … … … … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 33 34 35 36 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo – Cb 16Cr – 12Ni – 2Mo – Cb Wld. pipe Wld. pipe Plate Plate SA-813 SA-814 SA-240 SA-240 TP316H TP316H 316Cb 316Cb S31609 S31609 S31640 S31640 … … … … … … … … 8 8 8 8 1 1 1 1 37 38 39 40 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N Forgings Forgings Forgings Smls. tube SA-182 SA-965 SA-182 SA-213 F316LN F316LN F316LN TP316LN S31653 S31653 S31653 S31653 … … … … > 125 … ≤ 125 … 8 8 8 8 1 1 1 1 41 42 43 44 45 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N Plate Wld. tube Smls. & wld. pipe Wld. pipe Smls. pipe SA-240 SA-249 SA-312 SA-358 SA-376 316LN TP316LN TP316LN 316LN TP316LN S31653 S31653 S31653 S31653 S31653 … … … 1 … … … … … … 8 8 8 8 8 1 1 1 1 1 Line No. 74 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 515 515 515 515 515 205 205 205 205 205 NP NP NP NP NP 427 NP NP 427 427 NP 816 816 NP NP NP 343 343 NP NP HA-2 HA-2 HA-2 HA-2 HA-2 G5, W12 G5, G12, G24, T7 G12, G24, T9 G5, W12 G5, W12 6 7 8 520 520 520 205 220 220 816 NP NP 427 NP NP 816 550 550 NP NP NP HA-2 HA-2 HA-2 G5, G12, G22, H1, T8 G5 … 9 10 11 12 485 485 485 485 205 205 205 205 816 816 NP NP 427 NP 427 NP 816 816 816 816 NP NP NP NP HA-2 HA-2 HA-2 HA-2 G5, G12, T8 T9 G5, T8 T9 13 14 15 16 17 18 515 515 515 515 515 515 205 205 205 205 205 205 816 816 816 816 816 816 427 NP 427 NP 427 NP 816 816 816 816 816 816 NP NP NP NP NP NP HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, T8 T9 G5, T8 T9 G5, T8 T9 19 20 21 22 515 515 515 515 205 205 205 205 816 816 816 816 NP NP NP 427 816 816 NP NP NP NP NP NP HA-2 HA-2 HA-2 HA-2 G3, G5, G24, T7 G3, G24, T9 T9, W13 G5, T8, W12, W13 23 24 25 26 515 515 515 515 205 205 205 205 816 816 816 816 427 NP NP NP 816 816 816 816 NP NP NP NP HA-2 HA-2 HA-2 HA-2 G5, T8, W12, W13 T9, W13 G3, G5, G24, T7 G3, G24, T9 27 28 29 30 31 32 515 515 515 515 515 515 205 205 205 205 205 205 NP 816 816 NP 816 816 427 427 NP 427 427 NP NP 816 816 816 NP NP NP NP NP NP NP NP HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, W12 G5, H1, T8 H1, T9 G5, G12, T8, W12, W14 G5, H1, T8 H1, T9 33 34 35 36 515 515 515 515 205 205 205 205 NP NP NP NP 427 427 NP NP NP NP 816 816 NP NP 343 343 HA-2 HA-2 HA-2 HA-2 G5, W12 G5, W12 G5, G12, T8 G12, T9 37 38 39 40 485 485 515 515 205 205 205 205 NP NP NP NP 427 427 427 427 NP NP NP NP NP NP NP NP HA-2 HA-2 HA-2 HA-2 G5 G5 G5 G5 41 42 43 44 45 515 515 515 515 515 205 205 205 205 205 NP NP NP NP NP 427 427 427 427 427 NP NP NP NP NP NP NP NP NP NP HA-2 HA-2 HA-2 HA-2 HA-2 G5 G5, W12 G5, W12 G5, W12 G5 75 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 5 138 117 117 138 138 138 117 109 138 138 138 117 99.8 138 138 138 117 94.9 138 138 138 117 90.8 138 138 134 114 84.0 134 134 126 107 78.8 126 126 119 101 74.7 119 119 116 99.0 73.3 116 116 114 96.8 72.1 114 114 112 95.7 70.8 112 112 111 94.4 69.6 111 111 110 93.1 69.0 110 110 108 92.5 68.4 108 108 … 91.4 67.7 … … 6 7 8 138 147 147 138 147 134 138 147 125 138 146 119 138 144 114 134 142 106 126 133 98.7 119 126 93.7 116 124 91.7 114 121 90.0 112 120 88.6 111 119 87.4 110 117 86.4 108 115 85.5 108 114 84.8 9 10 11 12 138 138 138 138 138 128 138 128 138 118 138 118 136 112 136 112 134 107 134 107 133 99.2 133 99.2 126 92.8 126 92.8 119 88.1 119 88.1 116 86.1 116 86.1 114 84.1 114 84.1 112 82.9 112 82.9 111 82.0 111 82.0 110 81.4 110 81.4 108 80.6 108 80.6 108 79.8 108 79.8 13 14 15 16 17 18 138 138 138 138 138 138 138 128 138 128 138 128 138 118 138 118 138 118 138 112 138 112 138 112 138 107 138 107 138 107 134 99.2 134 99.2 134 99.2 126 92.8 126 92.8 126 92.8 119 88.1 119 88.1 119 88.1 116 86.1 116 86.1 116 86.1 114 84.1 114 84.1 114 84.1 112 82.9 112 82.9 112 82.9 111 82.0 111 82.0 111 82.0 110 81.4 110 81.4 110 81.4 108 80.6 108 80.6 108 80.6 108 79.8 108 79.8 108 79.8 19 20 21 22 117 117 138 138 117 109 128 138 117 99.8 118 138 117 94.9 112 138 117 90.8 107 138 114 84.0 99.2 134 107 78.8 92.8 126 101 74.7 88.1 119 99.0 73.3 86.1 116 96.8 72.1 84.1 114 95.7 70.8 82.9 112 94.4 69.6 82.0 111 93.1 69.0 81.4 110 92.5 68.4 80.6 108 91.4 67.7 79.8 108 23 24 25 26 138 138 117 117 138 128 117 109 138 118 117 99.8 138 112 117 94.9 138 107 117 90.8 134 99.2 114 84.0 126 92.8 107 78.8 119 88.1 101 74.7 116 86.1 99.0 73.3 114 84.1 96.8 72.1 112 82.9 95.7 70.8 111 82.0 94.4 69.6 110 81.4 93.1 69.0 108 80.6 92.5 68.4 108 79.8 91.4 67.7 27 28 29 30 31 32 138 138 138 138 138 138 138 138 128 138 138 128 138 138 118 138 138 118 138 138 112 138 138 112 138 138 107 138 138 107 134 134 99.2 134 134 99.2 126 126 92.8 126 126 92.8 119 119 88.1 119 119 88.1 116 116 86.1 116 116 86.1 114 114 84.1 114 114 84.1 112 112 82.9 112 112 82.9 111 111 82.0 111 111 82.0 110 110 81.4 110 110 81.4 108 108 80.6 108 108 80.6 … 108 79.8 108 108 79.8 33 34 35 36 138 138 138 138 138 138 138 130 138 138 138 120 138 138 138 114 138 138 138 109 134 134 134 99.3 126 126 125 92.2 119 119 117 86.7 116 116 116 85.0 114 114 114 84.1 112 112 112 82.9 111 111 111 82.0 110 110 110 81.4 108 108 109 80.6 … … 108 79.8 37 38 39 40 138 138 138 138 138 138 138 138 138 138 138 138 134 134 138 138 130 130 138 138 124 124 131 131 119 119 122 122 115 115 116 116 113 113 113 113 110 110 110 110 107 107 107 107 105 105 105 105 102 102 102 102 99.7 99.7 99.7 99.7 … … … … 41 42 43 44 45 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 131 131 131 131 131 122 122 122 122 122 116 116 116 116 116 113 113 113 113 113 110 110 110 110 110 107 107 107 107 107 105 105 105 105 105 102 102 102 102 102 99.7 99.7 99.7 99.7 99.7 … … … … … 76 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 … 90.5 67.1 … … … 89.9 66.5 … … … 89.3 65.9 … … … 85.3 65.3 … … … 68.1 64.0 … … … 55.6 55.6 … … … 42.9 42.9 … … … 33.0 33.0 … … … 25.3 25.3 … … … 19.4 19.4 … … … 14.7 14.7 … … … 11.3 11.3 … … … 8.90 8.90 … … … 6.77 6.77 … … … … … … … … … … … … … … … … … 6 7 8 107 114 84.1 106 113 83.4 105 112 82.6 99.8 … … 80.3 … … 65.5 … … 50.4 … … 38.6 … … 29.6 … … 23.0 … … 17.7 … … 13.4 … … 10.4 … … 8.05 … … … … … … … … … … … 9 10 11 12 107 79.2 107 79.2 106 78.7 106 78.7 105 77.8 105 77.8 99.8 77.1 99.8 77.1 80.3 75.0 80.3 75.0 65.5 65.5 65.5 65.5 50.4 50.4 50.4 50.4 38.6 38.6 38.6 38.6 29.6 29.6 29.6 29.6 23.0 23.0 23.0 23.0 17.7 17.7 17.7 17.7 13.4 13.4 13.4 13.4 10.4 10.4 10.4 10.4 8.05 8.05 8.05 8.05 … … … … … … … … … … … … 13 14 15 16 17 18 107 79.2 107 79.2 107 79.2 106 78.7 106 78.7 106 78.7 105 77.8 105 77.8 105 77.8 99.8 77.1 99.8 77.1 99.8 77.1 80.3 75.0 80.3 75.0 80.3 75.0 65.5 65.5 65.5 65.5 65.5 65.5 50.4 50.4 50.4 50.4 50.4 50.4 38.6 38.6 38.6 38.6 38.6 38.6 29.6 29.6 29.6 29.6 29.6 29.6 23.0 23.0 23.0 23.0 23.0 23.0 17.7 17.7 17.7 17.7 17.7 17.7 13.4 13.4 13.4 13.4 13.4 13.4 10.4 10.4 10.4 10.4 10.4 10.4 8.05 8.05 8.05 8.05 8.05 8.05 … … … … … … … … … … … … … … … … … … 19 20 21 22 90.5 67.1 79.2 107 89.9 66.5 78.7 106 89.3 65.9 77.8 105 85.3 65.3 77.1 99.8 68.1 64.0 75.0 80.3 55.6 55.6 65.5 65.5 42.9 42.9 50.4 50.4 33.0 33.0 38.6 38.6 25.3 25.3 29.6 29.6 19.4 19.4 23.0 23.0 14.7 14.7 17.7 17.7 11.3 11.3 13.4 13.4 8.90 8.90 10.4 10.4 6.77 6.77 8.05 8.05 … … … … … … … … … … … … 23 24 25 26 107 79.2 90.5 67.1 106 78.7 89.9 66.5 105 77.8 89.3 65.9 99.8 77.1 85.3 65.3 80.3 75.0 68.1 64.0 65.5 65.5 55.6 55.6 50.4 50.4 42.9 42.9 38.6 38.6 33.0 33.0 29.6 29.6 25.3 25.3 23.0 23.0 19.4 19.4 17.7 17.7 14.7 14.7 13.4 13.4 11.3 11.3 10.4 10.4 8.90 8.90 8.05 8.05 6.77 6.77 … … … … … … … … … … … … 27 28 29 30 31 32 … 107 79.2 107 107 79.2 … 106 78.7 106 106 78.7 … 105 77.8 105 105 77.8 … 99.8 77.1 99.8 99.8 77.1 … 80.3 75.0 80.3 80.3 75.0 … 65.5 65.5 65.5 65.5 65.5 … 50.4 50.4 50.4 50.4 50.4 … 38.6 38.6 38.6 38.6 38.6 … 29.6 29.6 29.6 29.6 29.6 … 23.0 23.0 23.0 23.0 23.0 … 17.7 17.7 17.7 17.7 17.7 … 13.4 13.4 13.4 13.4 13.4 … 10.4 10.4 10.4 10.4 10.4 … 8.05 8.05 8.05 8.05 8.05 … … … … … … … … … … … … … … … … … … 33 34 35 36 … … 107 79.2 … … 106 78.7 … … 105 77.8 … … 99.8 77.1 … … 80.3 75.0 … … 65.5 65.5 … … 50.4 50.4 … … 38.6 38.6 … … 29.6 29.6 … … 23.0 23.0 … … 17.7 17.7 … … 13.4 13.4 … … 10.4 10.4 … … 8.05 8.05 … … … … … … … … … … … … 37 38 39 40 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 41 42 43 44 45 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 77 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N Fittings Bar Wld. tube SA-403 SA-479 SA-688 316LN 316LN TP316LN S31653 S31653 S31653 … … … … … … 8 8 8 1 1 1 4 5 6 7 8 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N Forgings Smls. tube Smls. tube Plate Plate SA-182 SA-213 SA-213 SA-240 SA-240 F316N TP316N TP316N 316N 316N S31651 S31651 S31651 S31651 S31651 … … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 9 10 11 12 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N Wld. tube Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 SA-249 TP316N TP316N TP316N TP316N S31651 S31651 S31651 S31651 … … … … … … … … 8 8 8 8 1 1 1 1 13 14 15 16 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N Smls. & wld. pipe Smls. & wld. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP316N TP316N TP316N TP316N S31651 S31651 S31651 S31651 … … … … … … … … 8 8 8 8 1 1 1 1 17 18 19 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N Wld. pipe Smls. pipe Smls. pipe SA-358 SA-376 SA-376 316N TP316N TP316N S31651 S31651 S31651 1 … … … … … 8 8 8 1 1 1 20 21 22 23 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N Smls. & wld. fittings Bar Bar Wld. tube SA-403 SA-479 SA-479 SA-688 316N 316N 316N TP316N S31651 S31651 S31651 S31651 … … … … … … … … 8 8 8 8 1 1 1 1 24 25 26 27 28 29 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – Ti 16Cr – 12Ni – 2Mo – Ti Wld. pipe Wld. pipe Forgings Forgings Plate Plate SA-813 SA-814 SA-965 SA-965 SA-240 SA-240 TP316N TP316N F316N F316N 316Ti 316Ti S31651 S31651 S31651 S31651 S31635 S31635 … … … … … … … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 (10) (10) (10) (10) 30 31 32 33 17Cr – 4Ni – 6Mn 17Cr – 4Ni – 6Mn 17Cr – 4Ni – 6Mn 17Cr – 4Ni – 6Mn Plate Plate Plate Plate SA-240 SA-240 SA-666 SA-666 201-1 201-1 201-1 201-1 S20100 S20100 S20100 S20100 … … … … … … … … 8 8 8 8 3 3 3 3 (10) (10) (10) (10) 34 35 36 37 17Cr – 4Ni – 6Mn 17Cr – 4Ni – 6Mn 17Cr – 7Ni 17Cr – 7Ni Plate Plate Plate, sheet, strip Plate, sheet, strip SA-240 SA-666 SA-240 SA-240 201-2 201-2 301 301 S20100 S20100 S30100 S30100 … … … … … … … … 8 8 8 8 3 3 1 1 38 39 40 41 18Cr – 3Ni – 12Mn 18Cr – 3Ni – 12Mn 18Cr – 3Ni – 12Mn 18Cr – 3Ni – 12Mn Plate Plate Wld. tube Wld. tube SA-240 SA-240 SA-249 SA-249 XM-29 XM-29 XM-29 XM-29 S24000 S24000 S24000 S24000 … … … … … … … … 8 8 8 8 3 3 3 3 78 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 515 515 515 205 205 205 NP NP NP 427 427 427 NP NP NP NP NP NP HA-2 HA-2 HA-2 G5, W12 G5 G5, W12 4 5 6 7 8 550 550 550 550 550 240 240 240 240 240 NP 649 649 NP NP 427 427 NP 427 NP NP 649 649 649 649 NP NP NP 343 343 HA-2 HA-2 HA-2 HA-2 HA-2 G5 G5, G12, T7 G12, T8 G5, G12, T7 G12, T8 9 10 11 12 550 550 550 550 240 240 240 240 649 649 649 649 NP NP NP NP NP NP 649 649 NP NP 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, T7, W13 G12, T8, W13 G3, G12, G24, T8 G3, G5, G12, G24, T7 13 14 15 16 550 550 550 550 240 240 240 240 649 649 649 649 427 NP NP NP 649 649 649 649 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, T7, W12, W13, W14 G12, T8, W13, W14 G3, G12, G24, T8 G3, G5, G12, G24, T7 17 18 19 550 550 550 240 240 240 NP 649 649 427 427 NP NP 649 649 NP 343 343 HA-2 HA-2 HA-2 G5, W12 G5, G12, H1, T7 G12, H1, T8 20 21 22 23 550 550 550 550 240 240 240 240 NP 649 649 NP 427 427 NP 427 649 NP NP NP 343 NP NP NP HA-2 HA-2 HA-2 HA-2 G5, G12, T7, W12, W14 G5, G12, H1, T7 G12, H1, T8 G5, W12 24 25 26 27 28 29 550 550 550 550 515 515 240 240 240 240 205 205 NP NP NP NP NP NP 427 427 427 NP NP NP NP NP 649 649 816 816 NP NP 343 343 343 343 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, W12 G5, W12 G5, G12, T7 G12, T8 G5, G12, T8 G12, T9 30 31 32 33 515 515 515 515 260 260 260 260 NP NP NP NP NP NP NP NP 149 149 149 149 149 149 149 149 HA-2 HA-2 HA-2 HA-2 … G5 … G5 (10) (10) (10) (10) 34 35 36 37 655 655 515 515 310 310 205 205 NP NP NP NP NP NP NP NP 149 149 427 427 149 149 NP NP HA-6 HA-6 HA-1 HA-1 … … G5 … (10) (10) (10) (10) 38 39 40 41 690 690 690 690 380 380 380 380 NP NP NP NP NP NP NP NP 427 427 427 427 343 343 343 343 HA-6 HA-6 HA-6 HA-6 G5 … G5, G24 G24 79 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 131 131 131 122 122 122 116 116 116 113 113 113 110 110 110 107 107 107 105 105 105 102 102 102 99.7 99.7 99.7 … … … 4 5 6 7 8 158 158 158 158 158 158 158 150 158 150 158 158 141 158 141 155 155 136 155 136 152 152 131 152 131 148 148 122 148 122 146 146 115 146 115 145 145 109 145 109 144 144 107 144 107 140 140 104 140 104 137 137 102 137 102 135 135 99.9 135 99.9 133 133 98.0 133 98.0 130 130 96.1 130 96.1 … 128 94.9 128 94.9 9 10 11 12 158 158 134 134 158 150 128 134 158 141 120 133 155 136 115 131 152 131 111 129 148 122 104 126 146 115 97.6 125 145 109 93.1 124 144 107 90.7 122 140 104 88.4 119 137 102 86.6 117 135 99.9 84.7 115 133 98.0 83.5 113 130 96.1 82.3 111 128 94.9 80.5 109 13 14 15 16 158 158 134 134 158 150 128 134 158 141 120 133 155 136 115 131 152 131 111 129 148 122 104 126 146 115 97.6 125 145 109 93.1 124 144 107 90.7 122 140 104 88.4 119 137 102 86.6 117 135 99.9 84.7 115 133 98.0 83.5 113 130 96.1 82.3 111 128 94.9 80.5 109 17 18 19 158 158 158 158 158 150 158 158 141 155 155 136 152 152 131 148 148 122 146 146 115 145 145 109 144 144 107 140 140 104 137 137 102 135 135 99.9 133 133 98.0 130 130 96.1 … 128 94.9 20 21 22 23 158 158 158 158 158 158 150 158 158 158 141 158 155 155 136 155 152 152 131 152 148 148 122 148 146 146 115 146 145 145 109 145 144 144 107 144 140 140 104 140 137 137 102 137 135 135 99.9 135 133 133 98.0 133 130 130 96.1 130 128 128 94.9 … 24 25 26 27 28 29 158 158 158 158 138 138 158 158 158 150 138 130 158 158 158 141 138 120 155 155 155 136 138 114 152 152 152 131 138 109 148 148 148 122 134 99.3 146 146 146 115 125 92.2 145 145 145 109 117 86.7 144 144 144 107 116 85.0 140 140 140 104 114 84.1 137 137 137 102 112 82.9 135 135 135 99.9 111 82.0 133 133 133 98.0 110 81.4 130 130 130 96.1 109 80.6 … … 128 94.9 108 79.8 (10) (10) (10) (10) 30 31 32 33 147 147 147 147 147 147 147 147 130 140 130 140 121 134 121 134 114 130 114 130 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) 34 35 36 37 187 187 138 138 171 171 133 120 154 154 118 109 145 145 112 104 135 135 108 99.3 … … 106 93.4 … … 106 90.0 … … 106 87.2 … … 106 85.6 … … 106 83.8 … … 105 81.7 … … 103 79.3 … … 101 76.9 … … 98.7 74.7 … … … … 38 39 40 41 197 197 168 168 196 196 166 167 191 191 162 162 185 182 157 155 179 172 152 146 172 152 146 130 168 140 143 119 165 134 140 114 163 131 139 112 161 129 137 110 158 127 134 108 154 125 132 106 151 123 128 104 147 120 124 102 … … … … 80 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 4 5 6 7 8 … 126 93.1 126 93.1 … 124 91.7 124 91.7 … 119 90.1 119 90.1 … 101 88.5 101 88.5 … 81.6 81.6 81.6 81.6 … 65.3 65.3 65.3 65.3 … 50.4 50.4 50.4 50.4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 10 11 12 126 93.1 79.1 107 124 91.7 77.8 105 119 90.1 76.8 101 101 88.5 74.7 85.7 81.6 81.6 70.0 70.0 65.3 65.3 55.3 55.3 50.4 50.4 42.9 42.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 13 14 15 16 126 93.1 79.1 107 124 91.7 77.8 105 119 90.1 76.8 101 101 88.5 74.7 85.7 81.6 81.6 70.0 70.0 65.3 65.3 55.3 55.3 50.4 50.4 42.9 42.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 17 18 19 … 126 93.1 … 124 91.7 … 119 90.1 … 101 88.5 … 81.6 81.6 … 65.3 65.3 … 50.4 50.4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 23 126 126 93.1 … 124 124 91.7 … 119 119 90.1 … 101 101 88.5 … 81.6 81.6 81.6 … 65.3 65.3 65.3 … 50.4 50.4 50.4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 24 25 26 27 28 29 … … 126 93.1 107 79.2 … … 124 91.7 106 78.7 … … 119 90.1 105 77.8 … … 101 88.5 99.8 77.1 … … 81.6 81.6 80.3 75.0 … … 65.3 65.3 65.5 65.5 … … 50.4 50.4 50.4 50.4 … … … … 38.6 38.6 … … … … 29.6 29.6 … … … … 23.0 23.0 … … … … 17.7 17.7 … … … … 13.4 13.4 … … … … 10.4 10.4 … … … … 8.05 8.05 … … … … … … … … … … … … … … … … … … 30 31 32 33 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) 34 35 36 37 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) 38 39 40 41 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 81 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 5 6 18Cr – 3Ni – 12Mn 18Cr – 3Ni – 12Mn 18Cr – 3Ni – 12Mn 18Cr – 3Ni – 12Mn 18Cr – 3Ni – 12Mn 18Cr – 3Ni – 12Mn Wld. pipe Wld. pipe Bar Bar Wld. tube Wld. tube SA-312 SA-312 SA-479 SA-479 SA-688 SA-688 XM-29 XM-29 XM-29 XM-29 TPXM-29 TPXM-29 S24000 S24000 S24000 S24000 S24000 S24000 … … … … … … … … … … … … 8 8 8 8 8 8 3 3 3 3 3 3 7 8 9 10 18Cr – 5Ni – 3Mo 18Cr – 5Ni – 3Mo 18Cr – 5Ni – 3Mo 18Cr – 5Ni – 3Mo Smls. tube Wld. tube Smls. pipe Wld. pipe SA-789 SA-789 SA-790 SA-790 … … … … S31500 S31500 S31500 S31500 … … … … … … … … 10H 10H 10H 10H 1 1 1 1 11 12 13 14 15 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Forgings Forgings Forgings Forgings Bar SA-182 SA-182 SA-965 SA-965 SA/JIS G4303 F304L F304L F304L F304L SUS304L S30403 S30403 S30403 S30403 … … … … … … > 125 > 125 … … … 8 8 8 8 8 1 1 1 1 1 16 17 18 19 20 21 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Forgings Forgings Smls. tube Smls. tube Plate Plate SA-182 SA-182 SA-213 SA-213 SA-240 SA-240 F304L F304L TP304L TP304L 304L 304L S30403 S30403 S30403 S30403 S30403 S30403 … … … … … … ≤ 125 ≤ 125 … … … … 8 8 8 8 8 8 1 1 1 1 1 1 22 23 24 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 TP304L TP304L TP304L S30403 S30403 S30403 … … … … … … 8 8 8 1 1 1 25 26 27 28 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Smls. & wld. pipe Smls. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP304L TP304L TP304L TP304L S30403 S30403 S30403 S30403 … … … … … … … … 8 8 8 8 1 1 1 1 29 30 31 32 33 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Wld. pipe Smls. & wld. fittings Wld. pipe Bar Bar SA-358 SA-403 SA-409 SA-479 SA-479 304L 304L TP304L 304L 304L S30403 S30403 S30403 S30403 S30403 1 … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 34 35 36 37 38 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Wld. tube Wld. tube Wld. tube Wld. pipe Wld. pipe SA-688 SA-688 SA-688 SA-813 SA-814 TP304L TP304L TP304L TP304L TP304L S30403 S30403 S30403 S30403 S30403 … … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 39 40 41 42 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Forgings Forgings Forgings Forgings SA-182 SA-182 SA-182 SA-182 F304 F304 F304H F304H S30400 S30400 S30409 S30409 … … … … > 125 > 125 > 125 > 125 8 8 8 8 1 1 1 1 Line No. 82 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 6 690 690 690 690 690 690 380 380 380 380 380 380 NP NP NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 427 343 343 343 343 343 343 HA-6 HA-6 HA-6 HA-6 HA-6 HA-6 G5, G24 G24 G5, G22 G22 G5, G24 G24 7 8 9 10 635 635 635 635 440 440 440 440 NP NP NP NP NP NP NP NP 399 399 399 399 343 343 343 343 HA-5 HA-5 HA-5 HA-5 G32 G24, G32 G32 G24, G32 11 12 13 14 15 450 450 450 450 480 170 170 170 170 175 427 427 427 427 427 427 NP 427 NP 427 649 649 649 649 649 343 343 343 343 NP HA-3 HA-3 HA-3 HA-3 HA-3 G5, G34, T4 G34, T5 G5, G34, T4 G34, T5 G5, G22, G34, T4 16 17 18 19 20 21 485 485 485 485 485 485 170 170 170 170 170 170 427 427 427 427 427 427 427 NP 427 NP 427 NP 649 649 649 649 649 649 343 343 NP NP 343 343 HA-3 HA-3 HA-3 HA-3 HA-3 HA-3 G5, G34, T4 G34, T5 G5, G34, T4 G34, T5 G5, G34, T4 G34, T5 22 23 24 485 485 485 170 170 170 NP 427 427 427 NP NP NP 649 649 NP 343 343 HA-3 HA-3 HA-3 G5, W12 G5, G24, G34, T4 G24, G34, T5 25 26 27 28 485 485 485 485 170 170 170 170 427 427 427 427 427 NP NP NP 649 649 649 649 343 343 343 343 HA-3 HA-3 HA-3 HA-3 G5, G34, T4, W12, W14 G34, T5 G5, G24, G34, T4 G24, G34, T5 29 30 31 32 33 485 485 485 485 485 170 170 170 170 170 NP NP NP 427 427 427 427 427 427 NP NP 649 NP 649 649 NP 343 NP 343 343 HA-3 HA-3 HA-3 HA-3 HA-3 G5, W12 G5, T4, W12, W14 G5, W12 G5, G22, G34, T4 G22, G34, T5 34 35 36 37 38 485 485 485 485 485 170 170 170 170 170 NP NP NP NP NP 427 NP NP 427 427 NP 649 649 NP NP NP 343 343 NP NP HA-3 HA-3 HA-3 HA-3 HA-3 G5, W12 G5, G24, T4 G24, T5 G5, W12 G5, W12 39 40 41 42 485 485 485 485 205 205 205 205 816 816 816 816 427 NP 427 NP 816 816 816 816 343 343 NP NP HA-1 HA-1 HA-1 HA-1 G5, G12, T7 G12, T8 G5, T7 T8 83 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 5 6 168 168 197 197 168 168 166 167 196 196 166 167 162 162 191 191 162 162 157 155 185 182 157 155 152 146 179 172 152 146 146 130 172 152 146 130 143 119 168 140 143 119 140 114 165 134 140 114 139 112 163 131 139 112 137 110 161 129 137 110 134 108 158 127 134 108 132 106 154 125 132 106 128 104 151 123 128 104 124 102 147 120 124 102 … … … … … … 7 8 9 10 181 154 181 154 178 152 178 152 174 148 174 148 171 145 171 145 168 143 168 143 167 142 167 142 167 142 167 142 167 142 167 142 167 142 167 142 167 142 167 142 167 142 167 142 167 142 167 142 … … … … … … … … … … … … 11 12 13 14 15 115 115 115 115 115 115 105 115 105 115 115 97.0 115 97.0 115 115 92.3 115 92.3 115 115 88.1 115 88.1 115 110 81.2 110 81.2 110 103 76.0 103 76.0 103 97.7 72.3 97.7 72.3 97.7 95.7 70.9 95.7 70.9 95.7 94.1 69.7 94.1 69.7 94.1 92.6 68.6 92.6 68.6 92.6 91.3 67.6 91.3 67.6 91.3 90.0 66.7 90.0 66.7 90.0 88.7 65.7 88.7 65.7 88.7 86.6 64.6 86.6 64.6 86.6 16 17 18 19 20 21 115 115 115 115 115 115 115 105 115 105 115 105 115 97.0 115 97.0 115 97.0 115 92.3 115 92.3 115 92.3 115 88.1 115 88.1 115 88.1 110 81.2 110 81.2 110 81.2 103 76.0 103 76.0 103 76.0 97.7 72.3 97.7 72.3 97.7 72.3 95.7 70.9 95.7 70.9 95.7 70.9 94.1 69.7 94.1 69.7 94.1 69.7 92.6 68.6 92.6 68.6 92.6 68.6 91.3 67.6 91.3 67.6 91.3 67.6 90.0 66.7 90.0 66.7 90.0 66.7 88.7 65.7 88.7 65.7 88.7 65.7 86.6 64.6 86.6 64.6 86.6 64.6 22 23 24 115 97.8 97.8 115 97.8 88.9 115 97.8 82.5 115 97.8 78.4 115 97.8 74.9 110 93.2 69.0 103 87.2 64.6 97.7 83.0 61.5 95.7 81.4 60.3 94.1 80.0 59.2 92.6 78.7 58.3 91.3 77.6 57.5 90.0 76.5 56.7 88.7 75.4 55.8 … 73.6 54.9 25 26 27 28 115 115 97.8 97.8 115 105 97.8 88.9 115 97.0 97.8 82.5 115 92.3 97.8 78.4 115 88.1 97.8 74.9 110 81.2 93.2 69.0 103 76.0 87.2 64.6 97.7 72.3 83.0 61.5 95.7 70.9 81.4 60.3 94.1 69.7 80.0 59.2 92.6 68.6 78.7 58.3 91.3 67.6 77.6 57.5 90.0 66.7 76.5 56.7 88.7 65.7 75.4 55.8 86.6 64.6 73.6 54.9 29 30 31 32 33 115 115 115 115 115 115 115 115 115 105 115 115 115 115 97.0 115 115 115 115 92.3 115 115 115 115 88.1 110 110 110 110 81.2 103 103 103 103 76.0 97.7 97.7 97.7 97.7 72.3 95.7 95.7 95.7 95.7 70.9 94.1 94.1 94.1 94.1 69.7 92.6 92.6 92.6 92.6 68.6 91.3 91.3 91.3 91.3 67.6 90.0 90.0 90.0 90.0 66.7 88.7 88.7 88.7 88.7 65.7 … 86.6 … 86.6 64.6 34 35 36 37 38 115 97.8 97.8 115 115 115 97.8 88.9 115 115 115 97.8 82.5 115 115 115 97.8 78.4 115 115 115 97.8 74.9 115 115 110 93.2 69.0 110 110 103 87.2 64.6 103 103 97.7 83.0 61.5 97.7 97.7 95.7 81.4 60.3 95.7 95.7 94.1 80.0 59.2 94.1 94.1 92.6 78.7 58.3 92.6 92.6 91.3 77.6 57.5 91.3 91.3 90.0 76.5 56.7 90.0 90.0 88.7 75.4 55.8 88.7 88.7 … 73.6 54.9 … … 39 40 41 42 138 138 138 138 134 126 134 126 130 113 130 113 126 107 126 107 122 103 122 103 119 95.7 119 95.7 118 89.9 118 89.9 115 85.9 115 85.9 114 84.1 114 84.1 111 82.2 111 82.2 109 80.5 109 80.5 107 79.2 107 79.2 105 77.3 105 77.3 103 76.0 103 76.0 101 74.8 101 74.8 84 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 10 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 15 72.5 63.4 72.5 63.4 72.5 60.2 60.2 60.2 60.2 60.2 49.5 49.5 49.5 49.5 49.5 40.4 40.4 40.4 40.4 40.4 32.9 32.9 32.9 32.9 32.9 26.7 26.7 26.7 26.7 26.7 22.0 22.0 22.0 22.0 22.0 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 20 21 72.5 63.4 72.5 63.4 72.5 63.4 60.2 60.2 60.2 60.2 60.2 60.2 49.5 49.5 49.5 49.5 49.5 49.5 40.4 40.4 40.4 40.4 40.4 40.4 32.9 32.9 32.9 32.9 32.9 32.9 26.7 26.7 26.7 26.7 26.7 26.7 22.0 22.0 22.0 22.0 22.0 22.0 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 … 61.6 53.9 … 51.2 51.2 … 42.1 42.1 … 34.3 34.3 … 28.0 28.0 … 22.7 22.7 … 18.7 18.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 28 72.5 63.4 61.6 53.9 60.2 60.2 51.2 51.2 49.5 49.5 42.1 42.1 40.4 40.4 34.3 34.3 32.9 32.9 28.0 28.0 26.7 26.7 22.7 22.7 22.0 22.0 18.7 18.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 30 31 32 33 … 72.5 … 72.5 63.4 … 60.2 … 60.2 60.2 … 49.5 … 49.5 49.5 … 40.4 … 40.4 40.4 … 32.9 … 32.9 32.9 … 26.7 … 26.7 26.7 … 22.0 … 22.0 22.0 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 37 38 … 61.6 53.9 … … … 51.2 51.2 … … … 42.1 42.1 … … … 34.3 34.3 … … … 28.0 28.0 … … … 22.7 22.7 … … … 18.7 18.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 39 40 41 42 99.3 73.6 99.3 73.6 98.0 72.4 98.0 72.4 93.3 70.8 93.3 70.8 79.6 68.9 79.6 68.9 65.4 65.4 65.4 65.4 51.4 51.4 51.4 51.4 41.7 41.7 41.7 41.7 32.9 32.9 32.9 32.9 26.5 26.5 26.5 26.5 21.3 21.3 21.3 21.3 17.2 17.2 17.2 17.2 13.9 13.9 13.9 13.9 11.1 11.1 11.1 11.1 8.73 8.73 8.73 8.73 … … … … … … … … … … … … 85 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 5 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Castings Castings Castings Castings Castings SA-351 SA-351 SA-351 SA-351 SA-351 CF3 CF3 CF8 CF8 CF8 J92500 J92500 J92600 J92600 J92600 … … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 6 7 8 9 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Smls. pipe Smls. pipe Cast pipe Cast pipe SA-376 SA-376 SA-451 SA-451 TP304 TP304 CPF3 CPF8 S30400 S30400 J92500 J92600 … … … … … … … … 8 8 8 8 1 1 1 1 10 11 12 13 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Forgings Forgings Forgings Forgings SA-965 SA-965 SA-965 SA-965 F304 F304 F304H F304H S30400 S30400 S30409 S30409 … … … … … … … … 8 8 8 8 1 1 1 1 14 15 16 17 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Forgings Forgings Forgings Forgings SA-182 SA-182 SA-182 SA-182 F304 F304 F304H F304H S30400 S30400 S30409 S30409 … … … … ≤ 125 ≤ 125 ≤ 125 ≤ 125 8 8 8 8 1 1 1 1 18 19 20 21 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Smls. tube Smls. tube Smls. tube Smls. tube SA-213 SA-213 SA-213 SA-213 TP304 TP304 TP304H TP304H S30400 S30400 S30409 S30409 … … … … … … … … 8 8 8 8 1 1 1 1 22 23 24 25 26 27 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Plate Plate Plate Plate Plate Plate SA-240 SA-240 SA-240 SA-240 SA-240 SA-240 302 302 304 304 304H 304H S30200 S30200 S30400 S30400 S30409 S30409 … … … … … … … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 28 29 30 31 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Wld. tube Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 SA-249 TP304 TP304 TP304 TP304 S30400 S30400 S30400 S30400 … … … … … … … … 8 8 8 8 1 1 1 1 32 33 34 35 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Wld. tube Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 SA-249 TP304H TP304H TP304H TP304H S30409 S30409 S30409 S30409 … … … … … … … … 8 8 8 8 1 1 1 1 36 37 38 39 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Smls. & wld. pipe Smls. & wld. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP304 TP304 TP304 TP304 S30400 S30400 S30400 S30400 … … … … … … … … 8 8 8 8 1 1 1 1 40 41 42 43 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Smls. & wld. pipe Smls. & wld. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP304H TP304H TP304H TP304H S30409 S30409 S30409 S30409 … … … … … … … … 8 8 8 8 1 1 1 1 Line No. 86 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 485 485 485 485 485 205 205 205 205 205 NP NP 816 816 NP 427 NP 427 NP NP 427 427 NP 816 816 343 343 NP 343 343 HA-3 HA-3 HA-1 HA-1 HA-1 G1, G5, G16, G17, G32 G1, G32 G1, G5, G12, G16, G17, G32, H1, T6 G1, G12, G32, H1, T7 G1, G5, G12, G32, T6 6 7 8 9 485 485 485 485 205 205 205 205 NP NP NP NP 427 NP 427 427 816 816 NP NP 343 343 NP NP HA-1 HA-1 HA-3 HA-1 G5, G12, S9, T7 G12, S9, T8 G5, G16, G17, G32 G5, G16, G17, G32 10 11 12 13 485 485 485 485 205 205 205 205 816 816 NP NP 427 NP 427 NP 816 816 816 816 343 343 NP NP HA-1 HA-1 HA-1 HA-1 G5, G12, T7 G12, T8 G5, T7 T8 14 15 16 17 515 515 515 515 205 205 205 205 816 816 816 816 NP 427 NP 427 816 816 816 816 NP NP NP NP HA-1 HA-1 HA-1 HA-1 G12, T8 G5, G12, T7 T8 G5, T7 18 19 20 21 515 515 515 515 205 205 205 205 816 816 816 816 NP 427 NP 427 816 816 816 816 NP NP NP NP HA-1 HA-1 HA-1 HA-1 G12, T8 G5, G12, T7 T8 G5, T7 22 23 24 25 26 27 515 515 515 515 515 515 205 205 205 205 205 205 NP NP 816 816 816 816 NP NP NP 427 427 NP 399 399 816 816 816 816 343 343 343 343 NP NP HA-1 HA-1 HA-1 HA-1 HA-1 HA-1 G5 … G12, T8 G5, G12, H1, T7 G5, T7 T8 28 29 30 31 515 515 515 515 205 205 205 205 816 816 816 816 NP 427 NP NP NP NP 816 816 NP NP 343 343 HA-1 HA-1 HA-1 HA-1 G12, T8, W13 G5, G12, T7, W12, W13 G3, G5, G12, G24, T7 G3, G12, G24, T8 32 33 34 35 515 515 515 515 205 205 205 205 816 816 816 816 NP 427 NP NP NP NP 816 816 NP NP NP NP HA-1 HA-1 HA-1 HA-1 T8, W13 G5, T7, W12, W13 G3, G5, G24, T7 G3, G24, T8 36 37 38 39 515 515 515 515 205 205 205 205 816 816 816 816 427 NP NP NP 816 816 816 816 343 343 343 343 HA-1 HA-1 HA-1 HA-1 G5, G12, T7, W12, W13, W14 G12, T8, W13, W14 G3, G5, G12, G24, T7 G3, G12, G24, T8 40 41 42 43 515 515 515 515 205 205 205 205 816 816 816 816 427 NP NP NP 816 816 816 816 NP NP NP NP HA-1 HA-1 HA-1 HA-1 G5, T7, W12, W13, W14 T8, W13, W14 G3, G5, G24, T7 G3, G24, T8 87 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 5 138 138 138 138 138 134 126 134 126 134 130 113 130 113 130 126 107 126 107 126 122 103 122 103 122 119 95.7 119 95.7 119 118 90.0 118 90.0 118 115 85.6 115 85.6 115 114 83.9 114 83.9 114 111 82.3 111 82.3 111 109 80.5 109 80.5 109 107 79.2 107 79.2 107 105 77.7 105 77.7 105 103 76.4 103 76.4 103 … … 101 74.9 101 6 7 8 9 138 138 138 138 134 126 134 134 130 113 130 130 126 107 126 126 122 103 122 122 119 95.7 119 119 118 89.9 118 118 115 85.9 115 115 114 84.1 114 114 111 82.2 111 111 109 80.5 109 109 107 79.2 107 107 105 77.3 105 105 103 76.0 103 103 101 74.8 … … 10 11 12 13 138 138 138 138 134 126 134 126 130 113 130 113 126 107 126 107 122 103 122 103 119 95.7 119 95.7 118 89.9 118 89.9 115 85.9 115 85.9 114 84.1 114 84.1 111 82.2 111 82.2 109 80.5 109 80.5 107 79.2 107 79.2 105 77.3 105 77.3 103 76.0 103 76.0 101 74.8 101 74.8 14 15 16 17 138 138 138 138 126 138 126 138 113 137 113 137 107 134 107 134 103 130 103 130 95.7 126 95.7 126 89.9 122 89.9 122 85.9 116 85.9 116 84.1 114 84.1 114 82.2 111 82.2 111 80.5 109 80.5 109 79.2 107 79.2 107 77.3 105 77.3 105 76.0 103 76.0 103 74.8 101 74.8 101 18 19 20 21 138 138 138 138 126 138 126 138 113 137 113 137 107 134 107 134 103 130 103 130 95.7 126 95.7 126 89.9 122 89.9 122 85.9 116 85.9 116 84.1 114 84.1 114 82.2 111 82.2 111 80.5 109 80.5 109 79.2 107 79.2 107 77.3 105 77.3 105 76.0 103 76.0 103 74.8 101 74.8 101 22 23 24 25 26 27 138 138 138 138 138 138 138 126 126 138 138 126 137 113 113 137 137 113 134 107 107 134 134 107 130 103 103 130 130 103 126 95.7 95.7 126 126 95.7 122 90.0 89.9 122 122 89.9 116 85.6 85.9 116 116 85.9 114 83.9 84.1 114 114 84.1 111 82.3 82.2 111 111 82.2 109 80.5 80.5 109 109 80.5 107 79.2 79.2 107 107 79.2 … … 77.3 105 105 77.3 … … 76.0 103 103 76.0 … … 74.8 101 101 74.8 28 29 30 31 138 138 117 117 126 138 117 107 113 137 117 96.2 107 134 114 91.2 103 130 111 87.4 95.7 126 107 81.1 89.9 122 103 76.6 85.9 116 98.5 72.7 84.1 114 96.5 71.2 82.2 111 94.7 70.0 80.5 109 92.8 68.8 79.2 107 90.9 67.5 77.3 105 89.1 66.3 76.0 103 87.1 65.0 74.8 101 85.9 63.8 32 33 34 35 138 138 117 117 126 138 117 107 113 137 117 96.2 107 134 114 91.2 103 130 111 87.4 95.7 126 107 81.1 89.9 122 103 76.6 85.9 116 98.5 72.7 84.1 114 96.5 71.2 82.2 111 94.7 70.0 80.5 109 92.8 68.8 79.2 107 90.9 67.5 77.3 105 89.1 66.3 76.0 103 87.1 65.0 74.8 101 85.9 63.8 36 37 38 39 138 138 117 117 138 126 117 107 137 113 117 96.2 134 107 114 91.2 130 103 111 87.4 126 95.7 107 81.1 122 89.9 103 76.6 116 85.9 98.5 72.7 114 84.1 96.5 71.2 111 82.2 94.7 70.0 109 80.5 92.8 68.8 107 79.2 90.9 67.5 105 77.3 89.1 66.3 103 76.0 87.1 65.0 101 74.8 85.9 63.8 40 41 42 43 138 138 117 117 138 126 117 107 137 113 117 96.2 134 107 114 91.2 130 103 111 87.4 126 95.7 107 81.1 122 89.9 103 76.6 116 85.9 98.5 72.7 114 84.1 96.5 71.2 111 82.2 94.7 70.0 109 80.5 92.8 68.8 107 79.2 90.9 67.5 105 77.3 89.1 66.3 103 76.0 87.1 65.0 101 74.8 85.9 63.8 88 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 … … 99.5 73.6 99.5 … … 92.8 72.6 92.8 … … 75.6 70.0 75.6 … … 61.2 61.2 61.2 … … 49.0 49.0 49.0 … … 40.1 40.1 40.1 … … 32.8 32.8 32.8 … … 27.2 27.2 27.2 … … 23.4 23.4 23.4 … … 19.6 19.6 19.6 … … 16.7 16.7 16.7 … … 14.7 14.7 14.7 … … 12.9 12.9 12.9 … … 11.0 11.0 11.0 … … … … … … … … … … … … … … … 6 7 8 9 99.3 73.6 … … 98.0 72.4 … … 93.3 70.8 … … 79.6 68.9 … … 65.4 65.4 … … 51.4 51.4 … … 41.7 41.7 … … 32.9 32.9 … … 26.5 26.5 … … 21.3 21.3 … … 17.2 17.2 … … 13.9 13.9 … … 11.1 11.1 … … 8.73 8.73 … … … … … … … … … … … … … … 10 11 12 13 99.3 73.6 99.3 73.6 98.0 72.4 98.0 72.4 93.3 70.8 93.3 70.8 79.6 68.9 79.6 68.9 65.4 65.4 65.4 65.4 51.4 51.4 51.4 51.4 41.7 41.7 41.7 41.7 32.9 32.9 32.9 32.9 26.5 26.5 26.5 26.5 21.3 21.3 21.3 21.3 17.2 17.2 17.2 17.2 13.9 13.9 13.9 13.9 11.1 11.1 11.1 11.1 8.73 8.73 8.73 8.73 … … … … … … … … … … … … 14 15 16 17 73.6 99.3 73.6 99.3 72.4 98.0 72.4 98.0 70.8 93.3 70.8 93.3 68.9 79.6 68.9 79.6 65.4 65.4 65.4 65.4 51.4 51.4 51.4 51.4 41.7 41.7 41.7 41.7 32.9 32.9 32.9 32.9 26.5 26.5 26.5 26.5 21.3 21.3 21.3 21.3 17.2 17.2 17.2 17.2 13.9 13.9 13.9 13.9 11.1 11.1 11.1 11.1 8.73 8.73 8.73 8.73 … … … … … … … … … … … … 18 19 20 21 73.6 99.3 73.6 99.3 72.4 98.0 72.4 98.0 70.8 93.3 70.8 93.3 68.9 79.6 68.9 79.6 65.4 65.4 65.4 65.4 51.4 51.4 51.4 51.4 41.7 41.7 41.7 41.7 32.9 32.9 32.9 32.9 26.5 26.5 26.5 26.5 21.3 21.3 21.3 21.3 17.2 17.2 17.2 17.2 13.9 13.9 13.9 13.9 11.1 11.1 11.1 11.1 8.73 8.73 8.73 8.73 … … … … … … … … … … … … 22 23 24 25 26 27 … … 73.6 99.3 99.3 73.6 … … 72.4 98.0 98.0 72.4 … … 70.8 93.3 93.3 70.8 … … 68.9 79.6 79.6 68.9 … … 65.4 65.4 65.4 65.4 … … 51.4 51.4 51.4 51.4 … … 41.7 41.7 41.7 41.7 … … 32.9 32.9 32.9 32.9 … … 26.5 26.5 26.5 26.5 … … 21.3 21.3 21.3 21.3 … … 17.2 17.2 17.2 17.2 … … 13.9 13.9 13.9 13.9 … … 11.1 11.1 11.1 11.1 … … 8.73 8.73 8.73 8.73 … … … … … … … … … … … … … … … … … … 28 29 30 31 73.6 99.3 84.0 62.6 72.4 98.0 83.2 61.3 70.8 93.3 79.0 60.1 68.9 79.6 67.3 58.6 65.4 65.4 55.4 55.4 51.4 51.4 44.1 44.1 41.7 41.7 35.5 35.5 32.9 32.9 28.0 28.0 26.5 26.5 22.2 22.2 21.3 21.3 18.2 18.2 17.2 17.2 15.0 15.0 13.9 13.9 12.3 12.3 11.1 11.1 9.83 9.83 8.73 8.73 7.33 7.33 … … … … … … … … … … … … 32 33 34 35 73.6 99.3 84.0 62.6 72.4 98.0 83.2 61.3 70.8 93.3 79.0 60.1 68.9 79.6 67.3 58.6 65.4 65.4 55.4 55.4 51.4 51.4 44.1 44.1 41.7 41.7 35.5 35.5 32.9 32.9 28.0 28.0 26.5 26.5 22.2 22.2 21.3 21.3 18.2 18.2 17.2 17.2 15.0 15.0 13.9 13.9 12.3 12.3 11.1 11.1 9.83 9.83 8.73 8.73 7.33 7.33 … … … … … … … … … … … … 36 37 38 39 99.3 73.6 84.0 62.6 98.0 72.4 83.2 61.3 93.3 70.8 79.0 60.1 79.6 68.9 67.3 58.6 65.4 65.4 55.4 55.4 51.4 51.4 44.1 44.1 41.7 41.7 35.5 35.5 32.9 32.9 28.0 28.0 26.5 26.5 22.2 22.2 21.3 21.3 18.2 18.2 17.2 17.2 15.0 15.0 13.9 13.9 12.3 12.3 11.1 11.1 9.83 9.83 8.73 8.73 7.33 7.33 … … … … … … … … … … … … 40 41 42 43 99.3 73.6 84.0 62.6 98.0 72.4 83.2 61.3 93.3 70.8 79.0 60.1 79.6 68.9 67.3 58.6 65.4 65.4 55.4 55.4 51.4 51.4 44.1 44.1 41.7 41.7 35.5 35.5 32.9 32.9 28.0 28.0 26.5 26.5 22.2 22.2 21.3 21.3 18.2 18.2 17.2 17.2 15.0 15.0 13.9 13.9 12.3 12.3 11.1 11.1 9.83 9.83 8.73 8.73 7.33 7.33 … … … … … … … … … … … … 89 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Wld. pipe Wld. pipe Wld. pipe SA-358 SA-358 SA-358 304 304H 304LN S30400 S30409 S30453 1 1 1 … … … 8 8 8 1 1 1 4 5 6 7 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Smls. pipe Smls. pipe Smls. pipe Smls. pipe SA-376 SA-376 SA-376 SA-376 TP304 TP304 TP304H TP304H S30400 S30400 S30409 S30409 … … … … … … … … 8 8 8 8 1 1 1 1 8 9 10 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Smls. & wld. fittings SA-403 Smls. & wld. fittings SA-403 Wld. pipe SA-409 304 304H TP304 S30400 S30409 S30400 … … … … … … 8 8 8 1 1 1 11 12 13 14 15 16 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Bar Bar Bar Bar Bar Bar SA-479 SA-479 SA-479 SA-479 SA-479 SA-479 302 302 304 304 304H 304H S30200 S30200 S30400 S30400 S30409 S30409 … … … … … … … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 17 18 19 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Wld. tube Wld. tube Wld. tube SA-688 SA-688 SA-688 TP304 TP304 TP304 S30400 S30400 S30400 … … … … … … 8 8 8 1 1 1 20 21 22 23 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Wld. pipe Wld. pipe Wld. pipe Wld. pipe SA-813 SA-813 SA-814 SA-814 TP304 TP304H TP304 TP304H S30400 S30409 S30400 S30409 … … … … … … … … 8 8 8 8 1 1 1 1 24 25 26 27 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Bar Bar Plate Plate SA/JIS G4303 SA/JIS G4303 SA/EN 10028-7 SA/EN 10028-7 SUS302 SUS304 X5CrNi18-10 X5CrNi18-10 … … … … … … … … … … ≤ 75 ≤ 75 8 8 8 8 1 1 1 1 28 29 30 31 32 33 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Castings Castings Castings Castings Cast pipe Cast pipe SA-351 SA-351 SA-351 SA-351 SA-451 SA-451 CF3A CF3A CF8A CF8A CPF3A CPF8A J92500 J92500 J92600 J92600 J92500 J92600 … … … … … … … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 34 35 36 37 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N Forgings Forgings Forgings Smls. tube SA-182 SA-965 SA-182 SA-213 F304LN F304LN F304LN TP304LN S30453 S30453 S30453 S30453 … … … … > 125 … ≤ 125 … 8 8 8 8 1 1 1 1 38 39 40 41 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N Plate Wld. tube Smls. & wld. pipe Smls. pipe SA-240 SA-249 SA-312 SA-376 304LN TP304LN TP304LN TP304LN S30453 S30453 S30453 S30453 … … … … … … … … 8 8 8 8 1 1 1 1 Line No. 90 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 515 515 515 205 205 205 NP NP NP 427 427 427 NP NP NP NP NP NP HA-1 HA-1 HA-1 G5, W12 G5, W12 G5, W12 4 5 6 7 515 515 515 515 205 205 205 205 816 816 816 816 427 NP 427 NP 816 816 816 816 343 343 NP NP HA-1 HA-1 HA-1 HA-1 G5, G12, H1, T7 G12, H1, T8 G5, H1, T7 H1, T8 8 9 10 515 515 515 205 205 205 NP NP NP 427 427 427 816 816 NP 343 NP NP HA-1 HA-1 HA-1 G5, G12, T7, W12, W14 G5, T7, W12, W14 G5, W12 11 12 13 14 15 16 515 515 515 515 515 515 205 205 205 205 205 205 NP NP 816 816 816 816 427 NP 427 NP 427 NP 399 399 816 816 816 816 343 343 343 343 NP NP HA-1 HA-1 HA-1 HA-1 HA-1 HA-1 G5, G24 G22 G5, G12, G22, T7 G12, G22, T8 G5, G22, T7 G22, T8 17 18 19 515 515 515 205 205 205 NP NP NP 427 NP NP NP 816 816 NP 343 343 HA-1 HA-1 HA-1 G5, W12 G5, G12, G24, T7 G12, G24, T8 20 21 22 23 515 515 515 515 205 205 205 205 NP NP NP NP 427 427 427 427 NP NP NP NP NP NP NP NP HA-1 HA-1 HA-1 HA-1 G5, W12 G5, W12 G5, W12 G5, W12 24 25 26 27 520 520 520 520 205 205 210 210 NP 816 NP NP 427 427 NP NP 399 816 550 550 NP NP NP NP HA-1 HA-1 HA-1 HA-1 G5, G24 G5, G12, G22, T7 G5 … 28 29 30 31 32 33 530 530 530 530 530 530 240 240 240 240 240 240 NP NP NP NP NP NP 343 NP 343 NP 343 343 371 371 343 343 NP NP 343 343 343 343 NP NP HA-3 HA-3 HA-1 HA-1 HA-3 HA-1 G1, G5, G16, G17, G32 G1, G32 G1, G5, G16, G17, G32 G1, G32 G5, G16, G17, G32 G5, G16, G17, G32 34 35 36 37 485 485 515 515 205 205 205 205 NP NP NP NP 427 427 427 427 NP NP NP NP NP NP NP NP HA-1 HA-1 HA-1 HA-1 G5 G5 G5 G5 38 39 40 41 515 515 515 515 205 205 205 205 NP NP NP NP 427 427 427 427 NP NP NP NP NP NP NP NP HA-1 HA-1 HA-1 HA-1 G5 G5, W12 G5, W12, W14 G5 91 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 138 138 138 138 138 138 137 137 137 134 134 134 130 130 130 126 126 126 122 122 122 116 116 116 114 114 114 111 111 111 109 109 109 107 107 107 105 105 105 103 103 103 … … … 4 5 6 7 138 138 138 138 138 126 138 126 137 113 137 113 134 107 134 107 130 103 130 103 126 95.7 126 95.7 122 89.9 122 89.9 116 85.9 116 85.9 114 84.1 114 84.1 111 82.2 111 82.2 109 80.5 109 80.5 107 79.2 107 79.2 105 77.3 105 77.3 103 76.0 103 76.0 101 74.8 101 74.8 8 9 10 138 138 138 138 138 138 137 137 137 134 134 134 130 130 130 126 126 126 122 122 122 116 116 116 114 114 114 111 111 111 109 109 109 107 107 107 105 105 105 103 103 103 101 101 … 11 12 13 14 15 16 138 138 138 138 138 138 138 126 138 126 138 126 137 113 137 113 137 113 134 107 134 107 134 107 130 103 130 103 130 103 126 95.7 126 95.7 126 95.7 122 90.0 122 89.9 122 89.9 116 85.6 116 85.9 116 85.9 114 83.9 114 84.1 114 84.1 111 82.3 111 82.2 111 82.2 109 80.5 109 80.5 109 80.5 107 79.2 107 79.2 107 79.2 105 … 105 77.3 105 77.3 103 … 103 76.0 103 76.0 … … 101 74.8 101 74.8 17 18 19 138 117 117 138 117 107 137 117 96.2 134 114 91.2 130 111 87.4 126 107 81.1 122 103 76.6 116 98.5 72.7 114 96.5 71.2 111 94.7 70.0 109 92.8 68.8 107 90.9 67.5 105 89.1 66.3 103 87.1 65.0 … 85.9 63.8 20 21 22 23 138 138 138 138 138 138 138 138 137 137 137 137 134 134 134 134 130 130 130 130 126 126 126 126 122 122 122 122 116 116 116 116 114 114 114 114 111 111 111 111 109 109 109 109 107 107 107 107 105 105 105 105 103 103 103 103 … … … … 24 25 26 27 138 138 140 140 138 138 140 125 137 137 139 115 134 134 134 109 130 130 131 105 126 126 127 97.1 122 122 124 91.5 116 116 118 87.2 114 114 115 85.3 111 111 113 83.5 109 109 111 81.9 107 107 108 80.3 105 105 106 78.8 103 103 104 77.3 … 101 103 75.9 28 29 30 31 32 33 152 152 152 152 152 152 148 143 148 143 148 148 142 133 142 133 142 142 138 126 138 126 138 138 134 120 134 120 134 134 130 112 130 112 130 130 128 105 128 105 128 128 128 100 128 100 128 128 128 97.9 128 97.9 128 128 128 96.0 128 96.0 128 128 127 94.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 37 138 138 138 138 134 134 138 138 130 130 137 137 126 126 134 134 122 122 130 130 119 119 126 126 118 118 122 122 115 115 116 116 114 114 114 114 111 111 111 111 109 109 109 109 107 107 107 107 105 105 105 105 103 103 103 103 … … … … 38 39 40 41 138 138 138 138 138 138 138 138 137 137 137 137 134 134 134 134 130 130 130 130 126 126 126 126 122 122 122 122 116 116 116 116 114 114 114 114 111 111 111 111 109 109 109 109 107 107 107 107 105 105 105 105 103 103 103 103 … … … … 92 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 4 5 6 7 99.3 73.6 99.3 73.6 98.0 72.4 98.0 72.4 93.3 70.8 93.3 70.8 79.6 68.9 79.6 68.9 65.4 65.4 65.4 65.4 51.4 51.4 51.4 51.4 41.7 41.7 41.7 41.7 32.9 32.9 32.9 32.9 26.5 26.5 26.5 26.5 21.3 21.3 21.3 21.3 17.2 17.2 17.2 17.2 13.9 13.9 13.9 13.9 11.1 11.1 11.1 11.1 8.73 8.73 8.73 8.73 … … … … … … … … … … … … 8 9 10 99.3 99.3 … 98.0 98.0 … 93.3 93.3 … 79.6 79.6 … 65.4 65.4 … 51.4 51.4 … 41.7 41.7 … 32.9 32.9 … 26.5 26.5 … 21.3 21.3 … 17.2 17.2 … 13.9 13.9 … 11.1 11.1 … 8.73 8.73 … … … … … … … … … … 11 12 13 14 15 16 … … 99.3 73.6 99.3 73.6 … … 98.0 72.4 98.0 72.4 … … 93.3 70.8 93.3 70.8 … … 79.6 68.9 79.6 68.9 … … 65.4 65.4 65.4 65.4 … … 51.4 51.4 51.4 51.4 … … 41.7 41.7 41.7 41.7 … … 32.9 32.9 32.9 32.9 … … 26.5 26.5 26.5 26.5 … … 21.3 21.3 21.3 21.3 … … 17.2 17.2 17.2 17.2 … … 13.9 13.9 13.9 13.9 … … 11.1 11.1 11.1 11.1 … … 8.73 8.73 8.73 8.73 … … … … … … … … … … … … … … … … … … 17 18 19 … 84.0 62.6 … 83.2 61.3 … 79.0 60.1 … 67.3 58.6 … 55.4 55.4 … 44.1 44.1 … 35.5 35.5 … 28.0 28.0 … 22.2 22.2 … 18.2 18.2 … 15.0 15.0 … 12.3 12.3 … 9.83 9.83 … 7.33 7.33 … … … … … … … … … 20 21 22 23 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 24 25 26 27 … 99.3 101 74.6 … 98.0 97.5 73.2 … 93.3 95.6 71.8 … 79.6 … … … 65.4 … … … 51.4 … … … 41.7 … … … 32.9 … … … 26.5 … … … 21.3 … … … 17.2 … … … 13.9 … … … 11.1 … … … 8.73 … … … … … … … … … … … … … … 28 29 30 31 32 33 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 37 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 38 39 40 41 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 93 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 5 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N Smls. & wld. fittings Bar Wld. tube Wld. pipe Wld. pipe SA-403 SA-479 SA-688 SA-813 SA-814 304LN 304LN TP304LN TP304LN TP304LN S30453 S30453 S30453 S30453 S30453 WP … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 6 7 8 9 10 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N Forgings Smls. tube Smls. tube Plate Plate SA-182 SA-213 SA-213 SA-240 SA-240 F304N TP304N TP304N 304N 304N S30451 S30451 S30451 S30451 S30451 … … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 11 12 13 14 15 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N Wld. tube Wld. tube Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 SA-249 SA-249 TP304N TP304N TP304N TP304N TP304N S30451 S30451 S30451 S30451 S30451 … … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 16 17 18 19 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N Smls. & wld. pipe Smls. & wld. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP304N TP304N TP304N TP304N S30451 S30451 S30451 S30451 … … … … … … … … 8 8 8 8 1 1 1 1 20 21 22 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N Wld. pipe Smls. pipe Smls. pipe SA-358 SA-376 SA-376 304N TP304N TP304N S30451 S30451 S30451 1 … … … … … 8 8 8 1 1 1 23 24 25 26 27 28 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N Smls. & wld. fittings Bar Bar Wld. tube Wld. tube Wld. tube SA-403 SA-479 SA-479 SA-688 SA-688 SA-688 304N 304N 304N TP304N TP304N TP304N S30451 S30451 S30451 S30451 S30451 S30451 … … … … … … … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 29 30 31 32 33 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – 4Si – N Wld. pipe Wld. pipe Forgings Forgings Bar SA-813 SA-814 SA-965 SA-965 SA-479 TP304N TP304N F304N F304N … S30451 S30451 S30451 S30451 S21800 … … … … … … … … … … 8 8 8 8 8 1 1 1 1 3 34 35 36 37 38 39 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Forgings Forgings Castings Castings Castings Cast pipe SA-965 SA-965 SA-351 SA-351 SA-351 SA-451 F348H F348H CF8C CF8C CF8C CPF8C S34809 S34809 J92710 J92710 J92710 J92710 … … … … … … … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 40 41 42 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Forgings Forgings Forgings SA-182 SA-965 SA-965 F347 F347 F347 S34700 S34700 S34700 … … … > 125 … … 8 8 8 1 1 1 Line No. 94 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 515 515 515 515 515 205 205 205 205 205 NP NP NP NP NP 427 427 427 427 427 NP NP NP NP NP NP NP NP NP NP HA-1 HA-1 HA-1 HA-1 HA-1 G5, W12, W14 G5 G5, W12 G5, W12 G5, W12 6 7 8 9 10 550 550 550 550 550 240 240 240 240 240 NP 649 649 NP NP 427 427 NP 427 NP NP 649 649 649 649 NP NP NP 343 343 HA-1 HA-1 HA-1 HA-1 HA-1 G5 G5, G12, T7 G12, T8 G5, G12, T7 G12, T8 11 12 13 14 15 550 550 550 550 550 240 240 240 240 240 649 649 649 649 NP NP NP NP NP NP NP NP NP 649 649 NP NP NP 343 343 HA-1 HA-1 HA-1 HA-1 HA-1 G5, G12, T7, W13 G12, T8, W13 G3, G5, G12, T5 G3, G12, G24, T8 G5, G12, G24, T5 16 17 18 19 550 550 550 550 240 240 240 240 649 649 649 649 427 NP NP NP 649 649 649 649 343 343 343 343 HA-1 HA-1 HA-1 HA-1 G5, G12, T7, W12, W13, W14 G12, T8, W13, W14 G3, G5, G12, G24, T5 G3, G12, G24, T8 20 21 22 550 550 550 240 240 240 NP 649 649 427 427 NP NP 649 649 NP 343 343 HA-1 HA-1 HA-1 G5, W12 G5, G12, H1, T7 G12, H1, T8 23 24 25 26 27 28 550 550 550 550 550 550 240 240 240 240 240 240 NP 649 649 NP NP NP 427 NP 427 427 NP NP 649 NP NP NP 649 649 343 NP NP NP 343 343 HA-1 HA-1 HA-1 HA-1 HA-1 HA-1 G5, T7, W12, W14 G12, T8 G5, G12, T7 G5, W12 G5, G12, G24, T7 G12, G24, T8 29 30 31 32 33 550 550 550 550 655 240 240 240 240 345 NP NP NP NP NP 427 427 427 NP 427 NP NP 649 649 NP NP NP 343 343 NP HA-1 HA-1 HA-1 HA-1 HA-6 G5, W12 G5, W12 G5, G12, T7 G12, T8 … 34 35 36 37 38 39 450 450 485 485 485 485 170 170 205 205 205 205 NP NP NP NP NP NP NP NP 427 NP NP 427 816 816 NP 816 816 NP NP NP NP 343 343 NP HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, H2, T9 H2, T9 G5, G16, G17, G32 G1, G5, G12, G32, T7 G1, G12, G32, T7 G5, G16, G17, G32 40 41 42 485 485 485 205 205 205 816 816 816 427 427 NP 816 816 816 343 343 343 HA-2 HA-2 HA-2 G5, G12, T7 G5, G12, H1, T7 G12, H1, T7 95 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 5 138 138 138 138 138 138 138 138 138 138 137 137 137 137 137 134 134 134 134 134 130 130 130 130 130 126 126 126 126 126 122 122 122 122 122 116 116 116 116 116 114 114 114 114 114 111 111 111 111 111 109 109 109 109 109 107 107 107 107 107 105 105 105 105 105 103 103 103 103 103 … … … … … 6 7 8 9 10 158 158 158 158 158 158 158 144 158 144 158 158 129 158 129 154 154 121 154 121 149 149 115 149 115 141 141 105 141 105 132 132 97.6 132 97.6 125 125 92.9 125 92.9 122 122 90.9 122 90.9 120 120 89.3 120 89.3 118 118 88.0 118 88.0 116 116 86.1 116 86.1 115 115 84.9 115 84.9 113 113 83.7 113 83.7 … 111 81.8 111 81.8 11 12 13 14 15 158 158 134 134 134 158 144 134 122 134 158 129 133 110 133 154 121 131 103 131 149 115 127 97.7 127 141 105 120 88.9 120 132 97.6 112 82.9 112 125 92.9 106 79.1 106 122 90.9 104 77.2 104 120 89.3 102 75.5 102 118 88.0 100 74.3 100 116 86.1 99.2 73.0 99.2 115 84.9 97.4 72.4 97.4 113 83.7 95.4 71.3 95.4 111 81.8 94.2 69.4 94.2 16 17 18 19 158 158 134 134 158 144 134 122 158 129 133 110 154 121 131 103 149 115 127 97.7 141 105 120 88.9 132 97.6 112 82.9 125 92.9 106 79.1 122 90.9 104 77.2 120 89.3 102 75.5 118 88.0 100 74.3 116 86.1 99.2 73.0 115 84.9 97.4 72.4 113 83.7 95.4 71.3 111 81.8 94.2 69.4 20 21 22 158 158 158 158 158 144 158 158 129 154 154 121 149 149 115 141 141 105 132 132 97.6 125 125 92.9 122 122 90.9 120 120 89.3 118 118 88.0 116 116 86.1 115 115 84.9 113 113 83.7 … 111 81.8 23 24 25 26 27 28 158 158 158 158 134 134 158 144 158 158 134 122 158 129 158 158 133 110 154 121 154 154 131 103 149 115 149 149 127 97.7 141 105 141 141 120 88.9 132 97.6 132 132 112 82.9 125 92.9 125 125 106 79.1 122 90.9 122 122 104 77.2 120 89.3 120 120 102 75.5 118 88.0 118 118 100 74.3 116 86.1 116 116 99.2 73.0 115 84.9 115 115 97.4 72.4 113 83.7 113 113 95.4 71.3 111 81.8 111 … 94.2 69.4 29 30 31 32 33 158 158 158 158 187 158 158 158 144 185 158 158 158 129 176 154 154 154 121 164 149 149 149 115 152 141 141 141 105 137 132 132 132 97.6 128 125 125 125 92.9 123 122 122 122 90.9 121 120 120 120 89.3 119 118 118 118 88.0 118 116 116 116 86.1 116 115 115 115 84.9 116 113 113 113 83.7 115 … … 111 81.8 … 34 35 36 37 38 39 115 115 138 138 138 138 115 110 135 135 132 135 115 105 131 131 126 131 114 101 126 126 122 126 112 98.5 121 121 118 121 107 92.2 115 115 111 115 103 87.1 111 111 105 111 101 83.0 108 109 99.8 108 101 81.6 108 109 97.9 108 101 80.3 108 108 96.1 108 101 79.2 108 108 95.0 108 101 78.6 108 108 94.4 108 101 78.0 108 108 93.8 108 100 77.3 108 108 93.2 108 100 77.2 … 108 92.5 … 40 41 42 138 138 138 135 135 132 131 131 126 126 126 122 121 121 118 115 115 111 111 111 105 109 109 99.8 109 109 97.9 108 108 96.1 108 108 95.0 108 108 94.4 108 108 93.8 108 108 93.2 108 108 92.5 96 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 10 … 109 80.5 109 80.5 … 106 78.8 106 78.8 … 98.3 77.3 98.3 77.3 … 78.6 74.0 78.6 74.0 … 64.3 64.3 64.3 64.3 … 51.4 51.4 51.4 51.4 … 41.6 41.6 41.6 41.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 15 109 80.5 92.5 68.0 92.5 106 78.8 90.5 66.7 90.5 98.3 77.3 83.9 65.9 83.9 78.6 74.0 66.4 63.0 66.4 64.3 64.3 54.5 54.5 54.5 51.4 51.4 44.1 44.1 44.1 41.6 41.6 35.5 35.5 35.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 109 80.5 92.5 68.0 106 78.8 90.5 66.7 98.3 77.3 83.9 65.9 78.6 74.0 66.4 63.0 64.3 64.3 54.5 54.5 51.4 51.4 44.1 44.1 41.6 41.6 35.5 35.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 … 109 80.5 … 106 78.8 … 98.3 77.3 … 78.6 74.0 … 64.3 64.3 … 51.4 51.4 … 41.6 41.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 23 24 25 26 27 28 109 80.5 109 … 92.5 68.0 106 78.8 106 … 90.5 66.7 98.3 77.3 98.3 … 83.9 65.9 78.6 74.0 78.6 … 66.4 63.0 64.3 64.3 64.3 … 54.5 54.5 51.4 51.4 51.4 … 44.1 44.1 41.6 41.6 41.6 … 35.5 35.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 30 31 32 33 … … 109 80.5 … … … 106 78.8 … … … 98.3 77.3 … … … 78.6 74.0 … … … 64.3 64.3 … … … 51.4 51.4 … … … 41.6 41.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 37 38 39 99.7 77.2 … 107 92.4 … 98.6 77.2 … 106 92.4 … 97.3 76.9 … 98.3 90.3 … 95.8 76.5 … 77.2 77.2 … 91.3 75.6 … 57.7 57.7 … 70.9 70.9 … 39.9 39.9 … 53.9 53.9 … 30.0 30.0 … 41.4 41.4 … 23.2 23.2 … 31.9 31.9 … 16.3 16.3 … 23.9 23.9 … 11.2 11.2 … 18.8 18.8 … 8.93 8.93 … 14.6 14.6 … 7.08 7.08 … 10.8 10.8 … 5.77 5.77 … 7.83 7.83 … 5.32 5.32 … … … … … … … … … … … … … … … … … … … 40 41 42 107 107 92.4 106 106 92.4 98.3 98.3 90.3 77.2 77.2 77.2 57.7 57.7 57.7 39.9 39.9 39.9 30.0 30.0 30.0 23.2 23.2 23.2 16.3 16.3 16.3 11.2 11.2 11.2 8.93 8.93 8.93 7.08 7.08 7.08 5.77 5.77 5.77 5.32 5.32 5.32 … … … … … … … … … 97 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Forgings Forgings Forgings Forgings SA-182 SA-182 SA-965 SA-965 F347H F347H F347H F347H S34709 S34709 S34709 S34709 … … … … > 125 > 125 … … 8 8 8 8 1 1 1 1 5 6 7 8 9 10 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Forgings Forgings Forgings Forgings Forgings Forgings SA-182 SA-182 SA-965 SA-965 SA-182 SA-182 F348 F348 F348 F348 F348H F348H S34800 S34800 S34800 S34800 S34809 S34809 … … … … … … > 125 > 125 … … > 125 > 125 8 8 8 8 8 8 1 1 1 1 1 1 11 12 13 14 15 16 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Forgings Forgings Smls. tube Smls. tube Plate Plate SA-182 SA-182 SA-213 SA-213 SA-240 SA-240 F347 F347 TP347 TP347 347 347 S34700 S34700 S34700 S34700 S34700 S34700 … … … … … … ≤ 125 ≤ 125 … … … … 8 8 8 8 8 8 1 1 1 1 1 1 17 18 19 20 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Wld. tube Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 SA-249 TP347 TP347 TP347 TP347 S34700 S34700 S34700 S34700 … … … … … … … … 8 8 8 8 1 1 1 1 21 22 23 24 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Smls. & wld. pipe Smls. & wld. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP347 TP347 TP347 TP347 S34700 S34700 S34700 S34700 … … … … … … … … 8 8 8 8 1 1 1 1 25 26 27 28 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Wld. pipe Smls. pipe Smls. pipe Smls. & wld. fittings SA-358 SA-376 SA-376 SA-403 347 TP347 TP347 347 S34700 S34700 S34700 S34700 1 … … … … … … … 8 8 8 8 1 1 1 1 29 30 31 32 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Wld. pipe Bar Bar Wld. pipe SA-409 SA-479 SA-479 SA-813 TP347 347 347 TP347 S34700 S34700 S34700 S34700 … … … … … … … … 8 8 8 8 1 1 1 1 33 34 35 36 37 38 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Forgings Forgings Smls. tube Smls. tube Plate Plate SA-182 SA-182 SA-213 SA-213 SA-240 SA-240 F347H F347H TP347H TP347H 347H 347H S34709 S34709 S34709 S34709 S34709 S34709 … … … … … … ≤ 125 ≤ 125 … … … … 8 8 8 8 8 8 1 1 1 1 1 1 39 40 41 42 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Wld. tube Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 SA-249 TP347H TP347H TP347H TP347H S34709 S34709 S34709 S34709 … … … … … … … … 8 8 8 8 1 1 1 1 Line No. 98 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 485 485 485 485 205 205 205 205 816 816 NP NP NP 427 NP 427 NP 816 816 816 NP NP NP NP HA-2 HA-2 HA-2 HA-2 H2, T9 G5, H2, T8 H2, T9 G5, H2, T8 5 6 7 8 9 10 485 485 485 485 485 485 205 205 205 205 205 205 816 816 NP NP 816 816 NP 427 NP NP NP 427 NP 816 816 816 NP 816 NP 343 343 343 NP NP HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 T7 G5, G12, T7 G5, G12, H1, T7 G12, H1, T7 T9 G5, T8 11 12 13 14 15 16 515 515 515 515 515 515 205 205 205 205 205 205 816 816 816 816 816 816 427 NP 427 NP 427 NP 816 816 816 816 816 816 NP NP NP NP 343 343 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, G12, H1, T6 G12, H1, T7 G5, G12, H1, T6 G12, H1, T7 G5, G12, T6 G12, T7 17 18 19 20 515 515 515 515 205 205 205 205 816 816 816 816 NP 427 NP NP NP NP 816 816 NP NP 343 343 HA-2 HA-2 HA-2 HA-2 G12, T7, W13 G5, G12, T6, W12, W13 G3, G5, G12, G24, T6 G3, G12, G24, T7 21 22 23 24 515 515 515 515 205 205 205 205 816 816 816 816 427 NP NP NP 816 816 816 816 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, T6, W12, W13, W14 G12, T7, W13, W14 G3, G5, G12, G24, T6 G3, G12, G24, T7 25 26 27 28 515 515 515 515 205 205 205 205 NP 816 816 NP 427 427 NP 427 NP 816 816 816 NP 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, H1, W12 G5, G12, H1, T6 G12, H1, T7 G5, G12, T6, W12, W14 29 30 31 32 515 515 515 515 205 205 205 205 NP 816 816 NP 427 427 NP 427 NP 816 816 NP NP 343 343 NP HA-2 HA-2 HA-2 HA-2 G5, H1, W12 G5, G12, G22, T6 G12, G22, T7 G5, H1, W12 33 34 35 36 37 38 515 515 515 515 515 515 205 205 205 205 205 205 816 816 816 816 816 816 427 NP 427 NP 427 NP 816 816 816 816 816 816 NP NP NP NP NP NP HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, H2, T8 H2, T9 G5, H2, T8 H2, T9 G5, H2, T8 H2, T9 39 40 41 42 515 515 515 515 205 205 205 205 816 816 816 816 427 NP NP NP NP NP 816 816 NP NP NP NP HA-2 HA-2 HA-2 HA-2 G5, T8, W12, W13 T9, W13 G3, G5, G24, T8 G3, G24, T9 99 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 138 138 138 138 132 135 132 135 126 131 126 131 122 126 122 126 118 121 118 121 111 115 111 115 105 111 105 111 99.8 108 99.8 108 97.9 108 97.9 108 96.1 108 96.1 108 95.0 108 95.0 108 94.4 108 94.4 108 93.8 108 93.8 108 93.2 108 93.2 108 92.5 108 92.5 108 5 6 7 8 9 10 138 138 138 138 138 138 132 135 135 132 132 135 126 131 131 126 126 131 122 126 126 122 122 126 118 121 121 118 118 121 111 115 115 111 111 115 105 111 111 105 105 111 99.8 109 109 99.8 99.8 108 97.9 109 109 97.9 97.9 108 96.1 108 108 96.1 96.1 108 95.0 108 108 95.0 95.0 108 94.4 108 108 94.4 94.4 108 93.8 108 108 93.8 93.8 108 93.2 108 108 93.2 93.2 108 92.5 108 108 92.5 92.5 108 11 12 13 14 15 16 138 138 138 138 138 138 138 132 138 132 138 132 137 126 137 126 137 126 134 122 134 122 134 122 129 118 129 118 129 118 123 111 123 111 123 111 119 105 119 105 119 105 117 99.8 117 99.8 117 99.8 116 97.9 116 97.9 116 97.9 116 96.1 116 96.1 116 96.1 116 95.0 116 95.0 116 95.0 116 94.4 116 94.4 116 94.4 116 93.8 116 93.8 116 93.8 116 93.2 116 93.2 116 93.2 115 92.5 115 92.5 115 92.5 17 18 19 20 138 138 117 117 132 138 117 112 126 137 117 107 122 134 114 103 118 129 110 101 111 123 104 94.3 105 119 101 89.1 99.8 117 98.9 85.3 97.9 116 98.6 83.3 96.1 116 98.6 81.8 95.0 116 98.6 81.2 94.4 116 98.6 79.9 93.8 116 98.6 79.3 93.2 116 98.6 79.3 92.5 115 98.1 78.7 21 22 23 24 138 138 117 117 138 132 117 112 137 126 117 107 134 122 114 103 129 118 110 101 123 111 104 94.3 119 105 101 89.1 117 99.8 98.9 85.3 116 97.9 98.6 83.3 116 96.1 98.6 81.8 116 95.0 98.6 81.2 116 94.4 98.6 79.9 116 93.8 98.6 79.3 116 93.2 98.6 79.3 115 92.5 98.1 78.7 25 26 27 28 138 138 138 138 138 138 132 138 137 137 126 137 134 134 122 134 129 129 118 129 123 123 111 123 119 119 105 119 117 117 99.8 117 116 116 97.9 116 116 116 96.1 116 116 116 95.0 116 116 116 94.4 116 116 116 93.8 116 116 116 93.2 116 … 115 92.5 115 29 30 31 32 138 138 138 138 138 138 132 138 137 137 126 137 134 134 122 134 129 129 118 129 123 123 111 123 119 119 105 119 117 117 99.8 117 116 116 97.9 116 116 116 96.1 116 116 116 95.0 116 116 116 94.4 116 116 116 93.8 116 116 116 93.2 116 … 115 92.5 … 33 34 35 36 37 38 138 138 138 138 138 138 138 132 138 132 138 132 137 126 137 126 137 126 134 122 134 122 134 122 129 118 129 118 129 118 123 111 123 111 123 111 119 105 119 105 119 105 117 99.8 117 99.8 117 99.8 116 97.9 116 97.9 116 97.9 116 96.1 116 96.1 116 96.1 116 95.0 116 95.0 116 95.0 116 94.4 116 94.4 116 94.4 116 93.8 116 93.8 116 93.8 116 93.2 116 93.2 116 93.2 115 92.5 115 92.5 115 92.5 39 40 41 42 138 138 117 117 138 132 117 112 137 126 117 107 134 122 114 103 129 118 110 101 123 111 104 94.3 119 105 101 89.1 117 99.8 98.9 85.3 116 97.9 98.6 83.3 116 96.1 98.6 81.8 116 95.0 98.6 81.2 116 94.4 98.6 79.9 116 93.8 98.6 79.3 116 93.2 98.6 79.3 115 92.5 98.1 78.7 100 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 92.4 107 92.4 107 92.4 106 92.4 106 92.4 105 92.4 105 92.2 103 92.2 103 89.1 92.3 89.1 92.3 69.3 69.3 69.3 69.3 53.9 53.9 53.9 53.9 41.4 41.4 41.4 41.4 31.8 31.8 31.8 31.8 23.9 23.9 23.9 23.9 18.8 18.8 18.8 18.8 14.6 14.6 14.6 14.6 10.8 10.8 10.8 10.8 7.83 7.83 7.83 7.83 … … … … … … … … … … … … 5 6 7 8 9 10 92.4 107 107 92.4 92.4 107 92.4 106 106 92.4 92.4 106 90.3 98.3 98.3 90.3 92.4 105 77.2 77.2 77.2 77.2 92.2 103 57.7 57.7 57.7 57.7 89.1 92.3 39.9 39.9 39.9 39.9 69.3 69.3 30.0 30.0 30.0 30.0 53.9 53.9 23.2 23.2 23.2 23.2 41.4 41.4 16.3 16.3 16.3 16.3 31.8 31.8 11.2 11.2 11.2 11.2 23.9 23.9 8.93 8.93 8.93 8.93 18.8 18.8 7.08 7.08 7.08 7.08 14.6 14.6 5.77 5.77 5.77 5.77 10.8 10.8 5.32 5.32 5.32 5.32 7.83 7.83 … … … … … … … … … … … … … … … … … … 11 12 13 14 15 16 115 92.4 115 92.4 115 92.4 113 92.4 113 92.4 113 92.4 99.8 90.3 99.8 90.3 99.8 90.3 77.2 77.2 77.2 77.2 77.2 77.2 57.7 57.7 57.7 57.7 57.7 57.7 39.9 39.9 39.9 39.9 39.9 39.9 30.0 30.0 30.0 30.0 30.0 30.0 23.2 23.2 23.2 23.2 23.2 23.2 16.3 16.3 16.3 16.3 16.3 16.3 11.2 11.2 11.2 11.2 11.2 11.2 8.93 8.93 8.93 8.93 8.93 8.93 7.08 7.08 7.08 7.08 7.08 7.08 5.77 5.77 5.77 5.77 5.77 5.77 5.32 5.32 5.32 5.32 5.32 5.32 … … … … … … … … … … … … … … … … … … 17 18 19 20 92.4 115 97.6 78.6 92.4 113 95.4 78.6 90.3 99.8 85.5 76.8 77.2 77.2 65.9 65.9 57.3 57.7 49.5 49.5 39.9 39.9 34.0 34.0 30.0 30.0 25.9 25.9 23.2 23.2 19.7 19.7 16.3 16.3 14.0 14.0 11.2 11.2 9.80 9.80 8.93 8.93 7.53 7.53 7.08 7.08 5.95 5.95 5.77 5.77 4.96 4.96 5.32 5.32 4.50 4.50 … … … … … … … … … … … … 21 22 23 24 115 92.4 97.6 78.6 113 92.4 95.4 78.6 99.8 90.3 85.5 76.8 77.2 77.2 65.9 65.9 57.7 57.7 49.5 49.5 39.9 39.9 34.0 34.0 30.0 30.0 25.9 25.9 23.2 23.2 19.7 19.7 16.3 16.3 14.0 14.0 11.2 11.2 9.80 9.80 8.93 8.93 7.53 7.53 7.08 7.08 5.95 5.95 5.77 5.77 4.96 4.96 5.32 5.32 4.50 4.50 … … … … … … … … … … … … 25 26 27 28 … 115 92.4 115 … 113 92.4 113 … 99.8 90.3 99.8 … 77.2 77.2 77.2 … 57.7 57.7 57.7 … 39.9 39.9 39.9 … 30.0 30.0 30.0 … 23.2 23.2 23.2 … 16.3 16.3 16.3 … 11.2 11.2 11.2 … 8.93 8.93 8.93 … 7.08 7.08 7.08 … 5.77 5.77 5.77 … 5.32 5.32 5.32 … … … … … … … … … … … … 29 30 31 32 … 115 92.4 … … 113 92.4 … … 99.8 90.3 … … 77.2 77.2 … … 57.7 57.7 … … 39.9 39.9 … … 30.0 30.0 … … 23.2 23.2 … … 16.3 16.3 … … 11.2 11.2 … … 8.93 8.93 … … 7.08 7.08 … … 5.77 5.77 … … 5.32 5.32 … … … … … … … … … … … … … 33 34 35 36 37 38 115 92.4 115 92.4 115 92.4 114 92.4 114 92.4 114 92.4 113 92.4 113 92.4 113 92.4 109 92.2 109 92.2 109 92.2 92.3 89.1 92.3 89.1 92.3 89.1 69.3 69.3 69.3 69.3 69.3 69.3 53.9 53.9 53.9 53.9 53.9 53.9 41.4 41.4 41.4 41.4 41.4 41.4 31.8 31.8 31.8 31.8 31.8 31.8 23.9 23.9 23.9 23.9 23.9 23.9 18.8 18.8 18.8 18.8 18.8 18.8 14.6 14.6 14.6 14.6 14.6 14.6 10.8 10.8 10.8 10.8 10.8 10.8 7.83 7.83 7.83 7.83 7.83 7.83 … … … … … … … … … … … … … … … … … … 39 40 41 42 115 92.4 97.5 78.6 114 92.4 96.8 78.6 113 92.4 96.2 78.6 109 92.2 91.9 78.4 92.3 89.1 77.9 75.7 69.3 69.3 58.8 58.8 53.9 53.9 45.7 45.7 41.4 41.4 35.1 35.1 31.8 31.8 26.8 26.8 23.9 23.9 20.1 20.1 18.8 18.8 15.8 15.8 14.6 14.6 12.6 12.6 10.8 10.8 9.52 9.52 7.83 7.83 6.41 6.41 … … … … … … … … … … … … 101 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Smls. & wld. pipe Smls. & wld. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP347H TP347H TP347H TP347H S34709 S34709 S34709 S34709 … … … … … … … … 8 8 8 8 1 1 1 1 5 6 7 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Smls. pipe SA-376 Smls. pipe SA-376 Smls. & wld. fittings SA-403 TP347H TP347H 347H S34709 S34709 S34709 … … … … … … 8 8 8 1 1 1 8 9 10 11 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Bar Bar Wld. pipe Wld. pipe SA-479 SA-479 SA-813 SA-814 347H 347H TP347H TP347H S34709 S34709 S34709 S34709 … … … … … … … … 8 8 8 8 1 1 1 1 12 13 14 15 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Smls. tube Smls. tube Smls. pipe Smls. pipe SA-213 SA-213 SA-312 SA-312 TP347LN TP347LN TP347LN TP347LN S34751 S34751 S34751 S34751 … … … … … … … … 8 8 8 8 1 1 1 1 16 17 18 19 20 21 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Forgings Forgings Smls. tube Smls. tube Plate Plate SA-182 SA-182 SA-213 SA-213 SA-240 SA-240 F348 F348 TP348 TP348 348 348 S34800 S34800 S34800 S34800 S34800 S34800 … … … … … … ≤ 125 ≤ 125 … … … … 8 8 8 8 8 8 1 1 1 1 1 1 22 23 24 25 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Wld. tube Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 SA-249 TP348 TP348 TP348 TP348 S34800 S34800 S34800 S34800 … … … … … … … … 8 8 8 8 1 1 1 1 26 27 28 29 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Smls. & wld. pipe Smls. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP348 TP348 TP348 TP348 S34800 S34800 S34800 S34800 … … … … … … … … 8 8 8 8 1 1 1 1 30 31 32 33 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Wld. pipe Smls. pipe Smls. pipe Smls. & wld. fittings SA-358 SA-376 SA-376 SA-403 348 TP348 TP348 348 S34800 S34800 S34800 S34800 1 … … … … … … … 8 8 8 8 1 1 1 1 34 35 36 37 38 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Wld. pipe Bar Bar Wld. pipe Wld. pipe SA-409 SA-479 SA-479 SA-813 SA-814 TP348 348 348 TP348 TP348 S34800 S34800 S34800 S34800 S34800 … … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 39 40 41 42 43 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Forgings Forgings Smls. tube Smls. tube Plate SA-182 SA-182 SA-213 SA-213 SA-240 F348H F348H TP348H TP348H 348H S34809 S34809 S34809 S34809 S34809 … … … … … ≤ 125 ≤ 125 … … … 8 8 8 8 8 1 1 1 1 1 Line No. (a) (a) (a) (a) 102 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 515 515 515 515 205 205 205 205 816 816 816 816 427 NP NP NP 816 816 816 816 NP NP NP NP HA-2 HA-2 HA-2 HA-2 G5, H2, T8, W12, W13, W14 H2, T9, W13, W14 G3, G5, G24, H2, T8 G3, G24, H2, T9 5 6 7 515 515 515 205 205 205 816 816 NP 427 NP 427 816 816 816 NP NP NP HA-2 HA-2 HA-2 G5, H2, T8 H2, T9 G5, H2, T8, W12, W14 8 9 10 11 515 515 515 515 205 205 205 205 816 816 NP NP 427 NP 427 427 NP NP NP NP NP NP NP NP HA-2 HA-2 HA-2 HA-2 G5, H2, T8 H2, T9 G5, H2, W12 G5, W12 12 13 14 15 515 515 515 515 205 205 205 205 NP NP NP NP NP NP NP NP 593 593 593 593 NP NP NP NP HA-2 HA-2 HA-2 HA-2 G5, T8 … G5, T8 … 16 17 18 19 20 21 515 515 515 515 515 515 205 205 205 205 205 205 816 816 816 816 NP NP 427 NP 427 NP 427 NP 816 816 816 816 816 816 NP NP NP NP 343 343 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, G12, T6 G12, T7 G5, G12, T6 G12, T7 G5, G12, T6 G12, T7 22 23 24 25 515 515 515 515 205 205 205 205 816 816 816 816 NP 427 NP NP NP NP 816 816 NP NP 343 343 HA-2 HA-2 HA-2 HA-2 G12, T7, W13 G5, G12, T6, W12, W13 G3, G5, G12, G24, T6 G3, G12, G24, T7 26 27 28 29 515 515 515 515 205 205 205 205 816 816 NP NP 427 NP NP NP 816 816 816 816 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, T6, W12, W14 G12, T7 G5, G12, G24, T6 G12, G24, T7 30 31 32 33 515 515 515 515 205 205 205 205 NP 816 816 NP 427 427 NP 427 NP 816 816 816 NP 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, W12 G5, G12, H1, T6 G12, H1, T7 G5, G12, H2, T6, W12, W14 34 35 36 37 38 515 515 515 515 515 205 205 205 205 205 NP 816 816 NP NP 427 427 NP 427 427 NP 816 816 NP NP NP 343 343 NP NP HA-2 HA-2 HA-2 HA-2 HA-2 G5, W12 G5, G12, G22, H1, T6 G12, G22, H1, T7 G5, H1, W12 G5, W12 39 40 41 42 43 515 515 515 515 515 205 205 205 205 205 816 816 816 816 NP 427 NP 427 NP 427 816 816 816 816 NP NP NP NP NP NP HA-2 HA-2 HA-2 HA-2 HA-2 G5, T8 T9 G5, H2, T8 H2, T9 G5, H2 103 (a) (a) (a) (a) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (a) (a) (a) (a) Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 138 138 117 117 138 132 117 112 137 126 117 107 134 122 114 103 129 118 110 101 123 111 104 94.3 119 105 101 89.1 117 99.8 98.9 85.3 116 97.9 98.6 83.3 116 96.1 98.6 81.8 116 95.0 98.6 81.2 116 94.4 98.6 79.9 116 93.8 98.6 79.3 116 93.2 98.6 79.3 115 92.5 98.1 78.7 5 6 7 138 138 138 138 132 138 137 126 137 134 122 134 129 118 129 123 111 123 119 105 119 117 99.8 117 116 97.9 116 116 96.1 116 116 95.0 116 116 94.4 116 116 93.8 116 116 93.2 116 115 92.5 115 8 9 10 11 138 138 138 138 138 132 138 138 137 126 137 137 134 122 134 134 129 118 129 129 123 111 123 123 119 105 119 119 117 99.8 117 117 116 97.9 116 116 116 96.1 116 116 116 95.0 116 116 116 94.4 116 116 116 93.8 116 116 116 93.2 116 116 115 92.5 … … 12 13 14 15 138 138 138 138 137 128 137 128 137 120 137 120 136 115 136 115 131 110 131 110 123 101 123 101 117 94.7 117 94.7 114 90.2 114 90.2 113 88.6 113 88.6 112 87.5 112 87.5 112 86.7 112 86.7 112 86.2 112 86.2 112 85.9 112 85.9 112 85.7 112 85.7 111 85.7 111 85.7 16 17 18 19 20 21 138 138 138 138 138 138 138 132 138 132 138 132 137 126 137 126 137 126 134 122 134 122 134 122 129 118 129 118 129 118 123 111 123 111 123 111 119 105 119 105 119 105 117 99.8 117 99.8 117 99.8 116 97.9 116 97.9 116 97.9 116 96.1 116 96.1 116 96.1 116 95.0 116 95.0 116 95.0 116 94.4 116 94.4 116 94.4 116 93.8 116 93.8 116 93.8 116 93.2 116 93.2 116 93.2 115 92.5 115 92.5 115 92.5 22 23 24 25 138 138 117 117 132 138 117 112 126 137 117 107 122 134 114 103 118 129 110 101 111 123 104 94.3 105 119 101 89.1 99.8 117 98.9 85.3 97.9 116 98.6 83.3 96.1 116 98.6 81.8 95.0 116 98.6 81.2 94.4 116 98.6 79.9 93.8 116 98.6 79.3 93.2 116 98.6 79.3 92.5 115 98.1 78.7 26 27 28 29 138 138 117 117 138 132 117 112 137 126 117 107 134 122 114 103 129 118 110 101 123 111 104 94.3 119 105 101 89.1 117 99.8 98.9 85.3 116 97.9 98.6 83.3 116 96.1 98.6 81.8 116 95.0 98.6 81.2 116 94.4 98.6 79.9 116 93.8 98.6 79.3 116 93.2 98.6 79.3 115 92.5 98.1 78.7 30 31 32 33 138 138 138 138 138 138 132 138 137 137 126 137 134 134 122 134 129 129 118 129 123 123 111 123 119 119 105 119 117 117 99.8 117 116 116 97.9 116 116 116 96.1 116 116 116 95.0 116 116 116 94.4 116 116 116 93.8 116 116 116 93.2 116 … 115 92.5 115 34 35 36 37 38 138 138 138 138 138 138 138 132 138 138 137 137 126 137 137 134 134 122 134 134 129 129 118 129 129 123 123 111 123 123 119 119 105 119 119 117 117 99.8 117 117 116 116 97.9 116 116 116 116 96.1 116 116 116 116 95.0 116 116 116 116 94.4 116 116 116 116 93.8 116 116 116 116 93.2 116 116 … 115 92.5 … … 39 40 41 42 43 138 138 138 138 138 138 132 138 132 138 137 126 137 126 137 134 122 134 122 134 129 118 129 118 129 123 111 123 111 123 119 105 119 105 119 117 99.8 117 99.8 117 116 97.9 116 97.9 116 116 96.1 116 96.1 116 116 95.0 116 95.0 116 116 94.4 116 94.4 116 116 93.8 116 93.8 116 116 93.2 116 93.2 116 115 92.5 115 92.5 … 104 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 115 92.4 97.5 78.6 114 92.4 96.8 78.6 113 92.4 96.2 78.6 109 92.2 91.9 78.4 92.3 89.1 77.9 75.7 69.3 69.3 58.8 58.8 53.9 53.9 45.7 45.7 41.4 41.4 35.1 35.1 31.8 31.8 26.8 26.8 23.9 23.9 20.1 20.1 18.8 18.8 15.8 15.8 14.6 14.6 12.6 12.6 10.8 10.8 9.52 9.52 7.83 7.83 6.41 6.41 … … … … … … … … … … … … 5 6 7 115 92.4 115 114 92.4 114 113 92.4 113 109 92.2 109 92.3 89.1 92.3 69.3 69.3 69.3 53.9 53.9 53.9 41.4 41.4 41.4 31.8 31.8 31.8 23.9 23.9 23.9 18.8 18.8 18.8 14.6 14.6 14.6 10.8 10.8 10.8 7.83 7.83 7.83 … … … … … … … … … 8 9 10 11 115 92.4 … … 114 92.4 … … 113 92.4 … … 109 92.2 … … 92.3 89.1 … … 69.3 69.3 … … 53.9 53.9 … … 41.4 41.4 … … 31.8 31.8 … … 23.9 23.9 … … 18.8 18.8 … … 14.6 14.6 … … 10.8 10.8 … … 7.83 7.83 … … … … … … … … … … … … … … 12 13 14 15 111 85.6 111 85.6 110 85.4 110 85.4 108 85.1 108 85.1 106 84.7 106 84.7 84.5 83.2 84.5 83.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 20 21 115 92.4 115 92.4 115 92.4 113 92.4 113 92.4 113 92.4 99.8 90.3 99.8 90.3 99.8 90.3 77.2 77.2 77.2 77.2 77.2 77.2 57.7 57.7 57.7 57.7 57.7 57.7 39.9 39.9 39.9 39.9 39.9 39.9 30.0 30.0 30.0 30.0 30.0 30.0 23.2 23.2 23.2 23.2 23.2 23.2 16.3 16.3 16.3 16.3 16.3 16.3 11.2 11.2 11.2 11.2 11.2 11.2 8.93 8.93 8.93 8.93 8.93 8.93 7.08 7.08 7.08 7.08 7.08 7.08 5.77 5.77 5.77 5.77 5.77 5.77 5.32 5.32 5.32 5.32 5.32 5.32 … … … … … … … … … … … … … … … … … … 22 23 24 25 92.4 115 97.6 78.6 92.4 113 95.4 78.6 90.3 99.8 85.5 76.8 77.2 77.2 65.9 65.9 57.7 57.7 49.5 49.5 39.9 39.9 34.0 34.0 30.0 30.0 25.9 25.9 23.2 23.2 19.7 19.7 16.3 16.3 14.0 14.0 11.2 11.2 9.80 9.80 8.93 8.93 7.53 7.53 7.08 7.08 5.95 5.95 5.77 5.77 4.96 4.96 5.32 5.32 4.50 4.50 … … … … … … … … … … … … 26 27 28 29 115 92.4 97.6 78.6 113 92.4 95.4 78.6 99.8 90.3 85.5 76.8 77.2 77.2 65.9 65.9 57.7 57.7 49.5 49.5 39.9 39.9 34.0 34.0 30.0 30.0 25.9 25.9 23.2 23.2 19.7 19.7 16.3 16.3 14.0 14.0 11.2 11.2 9.80 9.80 8.93 8.93 7.53 7.53 7.08 7.08 5.95 5.95 5.77 5.77 4.96 4.96 5.32 5.32 4.50 4.50 … … … … … … … … … … … … 30 31 32 33 … 115 92.4 115 … 113 92.4 113 … 99.8 90.3 99.8 … 77.2 77.2 77.2 … 57.7 57.7 57.7 … 39.9 39.9 39.9 … 30.0 30.0 30.0 … 23.2 23.2 23.2 … 16.3 16.3 16.3 … 11.2 11.2 11.2 … 8.93 8.93 8.93 … 7.08 7.08 7.08 … 5.77 5.77 5.77 … 5.32 5.32 5.32 … … … … … … … … … … … … 34 35 36 37 38 … 115 92.4 … … … 113 92.4 … … … 99.8 90.3 … … … 77.2 77.2 … … … 57.7 57.7 … … … 39.9 39.9 … … … 30.0 30.0 … … … 23.2 23.2 … … … 16.3 16.3 … … … 11.2 11.2 … … … 8.93 8.93 … … … 7.08 7.08 … … … 5.77 5.77 … … … 5.32 5.32 … … … … … … … … … … … … … … … … … 39 40 41 42 43 115 92.4 115 92.4 … 114 92.4 114 92.4 … 113 92.4 113 92.4 … 109 92.2 109 92.2 … 92.3 89.1 92.3 89.1 … 69.3 69.3 69.3 69.3 … 53.9 53.9 53.9 53.9 … 41.4 41.4 41.4 41.4 … 31.8 31.8 31.8 31.8 … 23.9 23.9 23.9 23.9 … 18.8 18.8 18.8 18.8 … 14.6 14.6 14.6 14.6 … 10.8 10.8 10.8 10.8 … 7.83 7.83 7.83 7.83 … … … … … … … … … … … … … … … … 105 (a) (a) (a) (a) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Wld. tube Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 SA-249 TP348H TP348H TP348H TP348H S34809 S34809 S34809 S34809 … … … … … … … … 8 8 8 8 1 1 1 1 5 6 7 8 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Smls. & wld. pipe Smls. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP348H TP348H TP348H TP348H S34809 S34809 S34809 S34809 … … … … … … … … 8 8 8 8 1 1 1 1 9 10 11 12 13 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Smls. & wld. fittings Bar Bar Wld. pipe Wld. pipe SA-403 SA-479 SA-479 SA-813 SA-814 348H 348H 348H TP348H TP348H S34809 S34809 S34809 S34809 S34809 … … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 14 15 16 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Bar Smls. tube Smls. tube SA/JIS G4303 SA-213 SA-213 SUS347 TP347HFG TP347HFG … S34710 S34710 … … … … … … 8 8 8 1 1 1 17 18 19 20 21 22 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Smls. pipe Smls. pipe Wld. pipe Wld. pipe Smls. pipe Smls. pipe SA-312 SA-312 SA-312 SA-312 SA-376 SA-376 TP321 TP321 TP321 TP321 TP321 TP321 S32100 S32100 S32100 S32100 S32100 S32100 … … … … … … > 10 > 10 > 10 > 10 > 10 > 10 8 8 8 8 8 8 1 1 1 1 1 1 23 24 25 26 27 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Smls. pipe Smls. pipe Wld. pipe Wld. pipe Smls. pipe SA-312 SA-312 SA-312 SA-312 SA-376 TP321H TP321H TP321H TP321H TP321H S32109 S32109 S32109 S32109 S32109 … … … … … >5 >5 >5 >5 > 10 8 8 8 8 8 1 1 1 1 1 28 29 30 31 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Forgings Forgings Forgings Forgings SA-182 SA-182 SA-965 SA-965 F321 F321 F321 F321 S32100 S32100 S32100 S32100 … … … … > 125 > 125 … … 8 8 8 8 1 1 1 1 32 33 34 35 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Forgings Forgings Forgings Forgings SA-182 SA-182 SA-965 SA-965 F321H F321H F321H F321H S32109 S32109 S32109 S32109 … … … … > 125 > 125 … … 8 8 8 8 1 1 1 1 36 37 38 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Forgings Forgings Forgings SA-182 SA-182 SA-182 F321 F321 F321 S32100 S32100 S32100 … … … ≤ 125 ≤ 125 ≤ 125 8 8 8 1 1 1 39 40 41 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Smls. tube Smls. tube Smls. tube SA-213 SA-213 SA-213 TP321 TP321 TP321 S32100 S32100 S32100 … … … … … … 8 8 8 1 1 1 42 43 44 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Plate Plate Plate SA-240 SA-240 SA-240 321 321 321 S32100 S32100 S32100 … … … … … … 8 8 8 1 1 1 Line No. 106 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 515 515 515 515 205 205 205 205 816 816 816 816 427 NP NP NP NP NP 816 816 NP NP NP NP HA-2 HA-2 HA-2 HA-2 G5, T8, W12, W13 T9, W13 G3, G5, G24, T8 G3, G24, T9 5 6 7 8 515 515 515 515 205 205 205 205 816 816 NP NP 427 NP NP NP 816 816 816 816 NP NP NP NP HA-2 HA-2 HA-2 HA-2 G5, H2, T8, W12, W14 H2, T9 G5, G24, H2, T8 G24, H2, T9 9 10 11 12 13 515 515 515 515 515 205 205 205 205 205 NP 816 816 NP NP 427 427 NP 427 427 816 NP NP NP NP NP NP NP NP NP HA-2 HA-2 HA-2 HA-2 HA-2 G5, H2, T8, W12, W14 G5, H2, T8 H2, T9 G5, H2, W12 G5, W12 14 15 16 520 550 550 205 205 205 816 732 732 427 NP NP 816 NP NP NP NP NP HA-2 HA-2 HA-2 G5, G12, G22, T6 G5, T8 T9 17 18 19 20 21 22 485 485 485 485 485 485 170 170 170 170 170 170 816 816 816 816 NP NP 427 NP 427 NP 427 NP 816 816 816 816 816 816 NP NP NP NP 343 343 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, G12, T7 G12, T7 G5, G12, T7, W12, W13, W14 G12, T7, W13, W14 G5, G12, H1, T7 G12, H1, T7 23 24 25 26 27 485 485 485 485 485 170 170 170 170 170 816 816 816 816 NP 427 NP 427 NP 427 816 816 816 816 816 NP NP NP NP NP HA-2 HA-2 HA-2 HA-2 HA-2 G5, T8 T8 G5, T8, W12, W13, W14 T8, W13, W14 G5, H2, T8 28 29 30 31 485 485 485 485 205 205 205 205 816 816 816 816 427 NP 427 NP 816 816 816 816 NP NP 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, T6 G12, T7 G5, G12, H1, T6 G12, H1, T7 32 33 34 35 485 485 485 485 205 205 205 205 816 816 NP NP 427 NP 427 NP 816 816 816 816 NP NP NP NP HA-2 HA-2 HA-2 HA-2 G5, H2, T8 H2, T8 G5, H2, T8 H2, T8 36 37 38 515 515 515 205 205 205 816 816 NP NP NP 427 NP 816 816 NP 343 343 HA-2 HA-2 HA-2 G5, G12, T7 G12, T7 G5, G12, T6 39 40 41 515 515 515 205 205 205 816 816 NP NP NP 427 NP 816 816 NP NP NP HA-2 HA-2 HA-2 G5, G12, T7 G12, T7 G5, G12, T6 42 43 44 515 515 515 205 205 205 816 816 NP NP NP 427 NP 816 816 NP 343 343 HA-2 HA-2 HA-2 G5, G12, T7 G12, T7 G5, G12, T6 107 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 138 138 117 117 138 132 117 112 137 126 117 107 134 122 114 103 129 118 110 101 123 111 104 94.3 119 105 101 89.1 117 99.8 98.9 85.3 116 97.9 98.6 83.3 116 96.1 98.6 81.8 116 95.0 98.6 81.2 116 94.4 98.6 79.9 116 93.8 98.6 79.3 116 93.2 98.6 79.3 115 92.5 98.1 78.7 5 6 7 8 138 138 117 117 138 132 117 112 137 126 117 107 134 122 114 103 129 118 110 101 123 111 104 94.3 119 105 101 89.1 117 99.8 98.9 85.3 116 97.9 98.6 83.3 116 96.1 98.6 81.8 116 95.0 98.6 81.2 116 94.4 98.6 79.9 116 93.8 98.6 79.3 116 93.2 98.6 79.3 115 92.5 98.1 78.7 9 10 11 12 13 138 138 138 138 138 138 138 132 138 138 137 137 126 137 137 134 134 122 134 134 129 129 118 129 129 123 123 111 123 123 119 119 105 119 119 117 117 99.8 117 117 116 116 97.9 116 116 116 116 96.1 116 116 116 116 95.0 116 116 116 116 94.4 116 116 116 116 93.8 116 116 116 116 93.2 116 116 115 115 92.5 … … 14 15 16 138 138 138 138 138 129 137 138 123 134 138 120 129 138 116 123 138 110 119 134 105 117 132 102 116 131 100 116 131 98.5 116 130 97.2 116 130 96.0 116 128 94.9 116 127 93.9 115 125 92.9 17 18 19 20 21 22 115 115 115 115 115 115 115 109 115 109 115 109 115 102 115 102 115 102 115 98.7 115 98.7 115 98.7 115 95.0 115 95.0 115 95.0 115 88.8 115 88.8 115 88.8 112 83.0 112 83.0 112 83.0 106 79.0 106 79.0 106 79.0 104 77.2 104 77.2 104 77.2 102 75.5 102 75.5 102 75.5 100 74.3 100 74.3 100 74.3 98.5 73.0 98.5 73.0 98.5 73.0 97.3 72.5 97.3 72.5 97.3 72.5 96.0 71.2 96.0 71.2 96.0 71.2 95.4 70.5 95.4 70.5 95.4 70.5 23 24 25 26 27 115 115 115 115 115 115 108 115 108 115 115 102 115 102 115 115 98.7 115 98.7 115 115 95.0 115 95.0 115 115 88.8 115 88.8 115 112 83.0 112 83.0 112 106 79.0 106 79.0 106 104 77.2 104 77.2 104 102 75.5 102 75.5 102 100 74.3 100 74.3 100 98.5 73.0 98.5 73.0 98.5 97.3 72.5 97.3 72.5 97.3 96.0 71.2 96.0 71.2 96.0 95.4 70.5 95.4 70.5 95.4 28 29 30 31 138 138 138 138 135 130 135 130 130 123 130 123 126 118 126 118 123 114 123 114 121 106 121 106 121 99.7 121 99.7 121 94.5 121 94.5 121 92.3 121 92.3 121 90.7 121 90.7 121 89.4 121 89.4 119 87.5 119 87.5 117 86.9 117 86.9 115 85.7 115 85.7 114 85.0 114 85.0 32 33 34 35 138 138 138 138 135 131 135 131 130 123 130 123 126 118 126 118 123 114 123 114 121 106 121 106 121 99.7 121 99.7 121 94.5 121 94.5 121 92.3 121 92.3 121 90.7 121 90.7 121 89.4 121 89.4 119 87.5 119 87.5 117 86.9 117 86.9 115 85.7 115 85.7 114 85.0 114 85.0 36 37 38 138 138 138 138 130 138 138 123 138 135 118 135 132 114 132 129 106 129 129 99.7 129 127 94.5 127 125 92.3 125 123 90.7 123 120 89.4 121 119 87.5 119 117 86.9 117 115 85.7 115 114 85.0 114 39 40 41 138 138 138 138 130 138 138 123 138 135 118 135 132 114 132 129 106 129 129 99.7 129 127 94.5 127 125 92.3 125 123 90.7 123 120 89.4 121 119 87.5 119 117 86.9 117 115 85.7 115 114 85.0 114 42 43 44 138 138 138 138 130 138 138 123 138 135 118 135 132 114 132 129 106 129 129 99.7 129 127 94.5 127 125 92.3 125 123 90.7 123 120 89.4 121 119 87.5 119 117 86.9 117 115 85.7 115 114 85.0 114 108 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 115 92.4 97.5 78.6 114 92.4 96.8 78.6 113 92.4 96.2 78.6 109 92.2 91.9 78.4 92.3 89.1 77.9 75.7 69.3 69.3 58.8 58.8 53.9 53.9 45.7 45.7 41.4 41.4 35.1 35.1 31.8 31.8 26.8 26.8 23.9 23.9 20.1 20.1 18.8 18.8 15.8 15.8 14.6 14.6 12.6 12.6 10.8 10.8 9.52 9.52 7.83 7.83 6.41 6.41 … … … … … … … … … … … … 5 6 7 8 115 92.4 97.5 78.6 114 92.4 96.8 78.6 113 92.4 96.2 78.6 109 92.2 91.9 78.4 92.3 89.1 77.9 75.7 69.3 69.3 58.8 58.8 53.9 53.9 45.7 45.7 41.4 41.4 35.1 35.1 31.8 31.8 26.8 26.8 23.9 23.9 20.1 20.1 18.8 18.8 15.8 15.8 14.6 14.6 12.6 12.6 10.8 10.8 9.52 9.52 7.83 7.83 6.41 6.41 … … … … … … … … … … … … 9 10 11 12 13 115 115 92.4 … … 114 114 92.4 … … 113 113 92.4 … … 109 109 92.2 … … 92.3 92.3 89.1 … … 69.3 69.3 69.3 … … 53.9 53.9 53.9 … … 41.4 41.4 41.4 … … 31.8 31.8 31.8 … … 23.9 23.9 23.9 … … 18.8 18.8 18.8 … … 14.6 14.6 14.6 … … 10.8 10.8 10.8 … … 7.83 7.83 7.83 … … … … … … … … … … … … … … … … … 14 15 16 115 124 92.0 113 123 91.0 99.8 122 90.1 77.2 120 89.0 57.7 107 88.0 39.9 85.4 85.4 30.0 67.0 67.0 23.2 51.7 51.7 16.3 39.3 39.3 11.2 29.4 29.4 8.93 21.7 21.7 7.08 … … 5.77 … … 5.32 … … … … … … … … … … … 17 18 19 20 21 22 94.2 69.8 94.2 69.8 94.2 69.8 93.3 69.5 93.3 69.5 93.3 69.5 84.1 67.7 84.1 67.7 84.1 67.7 61.6 61.6 61.6 61.6 61.6 61.6 44.3 44.3 44.3 44.3 44.3 44.3 33.1 33.1 33.1 33.1 33.1 33.1 24.5 24.5 24.5 24.5 24.5 24.5 18.3 18.3 18.3 18.3 18.3 18.3 12.6 12.6 12.6 12.6 12.6 12.6 8.41 8.41 8.41 8.41 8.41 8.41 6.18 6.18 6.18 6.18 6.18 6.18 4.37 4.37 4.37 4.37 4.37 4.37 2.77 2.77 2.77 2.77 2.77 2.77 1.62 1.62 1.62 1.62 1.62 1.62 … … … … … … … … … … … … … … … … … … 23 24 25 26 27 94.2 69.9 94.2 69.9 94.2 93.6 69.2 93.6 69.2 93.6 91.2 68.8 91.2 68.8 91.2 78.0 67.4 78.0 67.4 78.0 59.5 59.5 59.5 59.5 59.5 46.0 46.0 46.0 46.0 46.0 36.9 36.9 36.9 36.9 36.9 28.7 28.7 28.7 28.7 28.7 22.9 22.9 22.9 22.9 22.9 18.4 18.4 18.4 18.4 18.4 14.4 14.4 14.4 14.4 14.4 11.5 11.5 11.5 11.5 11.5 9.16 9.16 9.16 9.16 9.16 6.64 6.64 6.64 6.64 6.64 … … … … … … … … … … … … … … … 28 29 30 31 113 83.9 113 83.9 111 83.0 111 83.0 87.4 77.6 87.4 77.6 57.5 59.2 57.5 59.2 44.4 44.8 44.4 44.8 32.9 32.9 32.9 32.9 24.5 24.5 24.5 24.5 18.3 18.3 18.3 18.3 12.6 12.6 12.6 12.6 8.41 8.41 8.41 8.41 6.18 6.18 6.18 6.18 4.37 4.37 4.37 4.37 2.77 2.77 2.77 2.77 1.62 1.62 1.62 1.62 … … … … … … … … … … … … 32 33 34 35 113 83.9 113 83.9 112 83.0 112 83.0 103 82.4 103 82.4 77.7 77.7 77.7 77.7 58.7 58.7 58.7 58.7 46.0 46.0 46.0 46.0 36.9 36.9 36.9 36.9 28.7 28.7 28.7 28.7 22.9 22.9 22.9 22.9 18.4 18.4 18.4 18.4 14.4 14.4 14.4 14.4 11.5 11.5 11.5 11.5 9.16 9.16 9.16 9.16 6.64 6.64 6.64 6.64 … … … … … … … … … … … … 36 37 38 113 83.9 113 112 83.0 111 94.6 77.6 87.4 59.2 59.2 57.5 44.8 44.8 44.4 32.9 32.9 32.9 24.5 24.5 24.5 18.3 18.3 18.3 12.6 12.6 12.6 8.41 8.41 8.41 6.18 6.18 6.18 4.37 4.37 4.37 2.77 2.77 2.77 1.62 1.62 1.62 … … … … … … … … … 39 40 41 113 83.9 113 112 83.0 111 94.6 77.6 87.4 59.2 59.2 57.5 44.8 44.8 44.4 32.9 32.9 32.9 24.5 24.5 24.5 18.3 18.3 18.3 12.6 12.6 12.6 8.41 8.41 8.41 6.18 6.18 6.18 4.37 4.37 4.37 2.77 2.77 2.77 1.62 1.62 1.62 … … … … … … … … … 42 43 44 113 83.9 113 112 83.0 111 94.6 77.6 87.4 59.2 59.2 57.5 44.8 44.8 44.4 32.9 32.9 32.9 24.5 24.5 24.5 18.3 18.3 18.3 12.6 12.6 12.6 8.41 8.41 8.41 6.18 6.18 6.18 4.37 4.37 4.37 2.77 2.77 2.77 1.62 1.62 1.62 … … … … … … … … … 109 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Wld. tube Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 SA-249 TP321 TP321 TP321 TP321 S32100 S32100 S32100 S32100 … … … … … … … … 8 8 8 8 1 1 1 1 5 6 7 8 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Smls. pipe Smls. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP321 TP321 TP321 TP321 S32100 S32100 S32100 S32100 … … … … ≤ 10 ≤ 10 ≤ 10 ≤ 10 8 8 8 8 1 1 1 1 9 10 11 12 13 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Wld. pipe Smls. pipe Smls. pipe Smls. pipe Smls. & wld. fittings SA-358 SA-376 SA-376 SA-376 SA-403 321 TP321 TP321 TP321 321 S32100 S32100 S32100 S32100 S32100 1 … … … … … ≤ 10 ≤ 10 ≤ 10 … 8 8 8 8 8 1 1 1 1 1 14 15 16 17 18 19 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Wld. pipe Bar Bar Bar Wld. pipe Wld. pipe SA-409 SA-479 SA-479 SA-479 SA-813 SA-814 TP321 321 321 321 TP321 TP321 S32100 S32100 S32100 S32100 S32100 S32100 … … … … … … … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 20 21 22 23 24 25 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Forgings Forgings Smls. tube Smls. tube Plate Plate SA-182 SA-182 SA-213 SA-213 SA-240 SA-240 F321H F321H TP321H TP321H 321H 321H S32109 S32109 S32109 S32109 S32109 S32109 … … … … … … ≤ 125 ≤ 125 … … … … 8 8 8 8 8 8 1 1 1 1 1 1 26 27 28 29 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Wld. tube Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 SA-249 TP321H TP321H TP321H TP321H S32109 S32109 S32109 S32109 … … … … … … … … 8 8 8 8 1 1 1 1 30 31 32 33 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Smls. pipe Smls. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP321H TP321H TP321H TP321H S32109 S32109 S32109 S32109 … … … … ≤5 ≤5 ≤5 ≤5 8 8 8 8 1 1 1 1 34 35 36 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Smls. pipe SA-376 Smls. pipe SA-376 Smls. & wld. fittings SA-403 TP321H TP321H 321H S32109 S32109 S32109 … … … ≤ 10 ≤ 10 … 8 8 8 1 1 1 37 38 39 40 41 42 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 11Ni Bar Bar Wld. pipe Wld. pipe Bar Plate 321H 321H TP321H TP321H SUS321 305 S32109 S32109 S32109 S32109 … S30500 … … … … … … … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 Line No. SA-479 SA-479 SA-813 SA-814 SA/JIS G4303 SA-240 110 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 515 515 515 515 205 205 205 205 816 816 816 816 NP 427 NP NP NP NP 816 816 NP NP 343 343 HA-2 HA-2 HA-2 HA-2 G12, T7, W13 G5, G12, T7, W12, W13 G3, G5, G12, G24, T7 G3, G12, G24, T7 5 6 7 8 515 515 515 515 205 205 205 205 816 816 816 816 427 NP 427 NP 816 816 816 816 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, T7 G12, T7 G5, G12, T7, W12, W13, W14 T7, W13, W14 9 10 11 12 13 515 515 515 515 515 205 205 205 205 205 NP 816 816 NP NP 427 NP NP 427 427 NP NP 816 816 816 NP NP NP NP 343 HA-2 HA-2 HA-2 HA-2 HA-2 G5, H1, W12 G5, G12, H1, T7 G12, H1, T7 G5, G12, T6 G5, G12, T6, W12, W14 14 15 16 17 18 19 515 515 515 515 515 515 205 205 205 205 205 205 NP 816 816 NP NP NP 427 NP NP 427 427 427 NP NP 816 816 NP NP NP NP 343 343 NP NP HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, W12 G5, G12, H1, T7 G12, G22, H1, T7 G5, G12, G22, H1, T6 G5, H1, W12 G5, W12 20 21 22 23 24 25 515 515 515 515 515 515 205 205 205 205 205 205 816 816 816 816 816 816 427 NP 427 NP 427 NP 816 816 816 816 816 816 NP NP NP NP NP NP HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, H2, T8 H2, T8 G5, H2, T8 H2, T8 G5, H2, T8 H2, T8 26 27 28 29 515 515 515 515 205 205 205 205 816 816 816 816 NP 427 NP NP NP NP 816 816 NP NP NP NP HA-2 HA-2 HA-2 HA-2 T8, W13 G5, T8, W12, W13 G3, G5, G24, T8 G3, G24, T8 30 31 32 33 515 515 515 515 205 205 205 205 816 816 816 816 427 NP 427 NP 816 816 816 816 NP NP NP NP HA-2 HA-2 HA-2 HA-2 G5, T8 T8 G5, T8, W12, W13, W14 T8, W13, W14 34 35 36 515 515 515 205 205 205 816 816 NP 427 NP 427 816 816 816 NP NP NP HA-2 HA-2 HA-2 G5, H2, T8 H2, T8 G5, H2, T8, W12, W14 37 38 39 40 41 42 515 515 515 515 520 515 205 205 205 205 205 205 816 816 NP NP NP NP NP 427 427 427 427 427 816 816 NP NP 816 NP NP NP NP NP NP NP HA-2 HA-2 HA-2 HA-2 HA-2 HA-1 H2, T8 G5, H2, T8 G5, H2, W12 G5, W12 G5, G12, G22, H1, T6 G5 111 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 138 138 117 117 130 138 117 111 123 138 117 104 118 135 114 101 114 132 112 97.1 106 129 110 90.2 99.7 129 110 85.0 94.5 127 108 80.6 92.3 125 106 78.5 90.7 123 104 76.9 89.4 120 102 75.6 87.5 119 101 74.4 86.9 117 99.4 73.8 85.7 115 98.1 72.6 85.0 114 97.5 71.9 5 6 7 8 138 138 138 138 138 130 138 130 138 123 138 123 135 118 135 118 132 114 132 114 129 106 129 106 129 99.7 129 99.7 127 94.5 127 94.5 125 92.3 125 92.3 123 90.7 123 90.7 120 89.4 120 89.4 119 87.5 119 87.5 117 86.9 117 86.9 115 85.7 115 85.7 114 85.0 114 85.0 9 10 11 12 13 138 138 138 138 138 138 138 130 138 138 138 138 123 138 138 135 135 118 135 135 132 132 114 132 132 129 129 106 129 129 129 129 99.7 129 129 127 127 94.5 127 127 125 125 92.3 125 125 123 123 90.7 123 123 120 120 89.4 121 121 119 119 87.5 119 119 117 117 86.9 117 117 115 115 85.7 115 115 … 114 85.0 114 114 14 15 16 17 18 19 138 138 138 138 138 138 138 138 130 138 138 138 138 138 123 138 138 138 135 135 118 135 135 135 132 132 114 132 132 132 129 129 106 129 129 129 129 129 99.7 129 129 129 127 127 94.5 127 127 127 125 125 92.3 125 125 125 123 123 90.7 123 123 123 120 120 89.4 121 120 120 119 119 87.5 119 119 119 117 117 86.9 117 117 117 115 115 85.7 115 115 115 … 114 85.0 114 … … 20 21 22 23 24 25 138 138 138 138 138 138 138 131 138 131 138 131 138 123 138 123 138 123 135 118 135 118 135 118 132 114 132 114 132 114 129 106 129 106 129 106 129 99.7 129 99.7 129 99.7 127 94.5 127 94.5 127 94.5 125 92.3 125 92.3 125 92.3 123 90.7 123 90.7 123 90.7 121 89.4 121 89.4 121 89.4 119 87.5 119 87.5 119 87.5 117 86.9 117 86.9 117 86.9 115 85.7 115 85.7 115 85.7 114 85.0 114 85.0 114 85.0 26 27 28 29 138 138 117 117 131 138 117 111 123 138 117 104 118 135 114 101 114 132 112 97.1 106 129 110 90.2 99.7 129 110 85.0 94.5 127 108 80.6 92.3 125 106 78.5 90.7 123 104 76.9 89.4 121 102 75.6 87.5 119 101 74.4 86.9 117 99.4 73.8 85.7 115 98.1 72.6 85.0 114 97.4 71.8 30 31 32 33 138 138 138 138 138 131 138 131 138 123 138 123 135 118 135 118 132 114 132 114 129 106 129 106 129 99.7 129 99.7 127 94.5 127 94.5 125 92.3 125 92.3 123 90.7 123 90.7 121 89.4 121 89.4 119 87.5 119 87.5 117 86.9 117 86.9 115 85.7 115 85.7 114 85.0 114 85.0 34 35 36 138 138 138 138 131 138 138 123 138 135 118 135 132 114 132 129 106 129 129 99.7 129 127 94.5 127 125 92.3 125 123 90.7 123 121 89.4 121 119 87.5 119 117 86.9 117 115 85.7 115 114 85.0 114 37 38 39 40 41 42 138 138 138 138 138 138 131 138 138 138 138 138 123 138 138 138 138 137 118 135 135 135 135 134 114 132 132 132 132 130 106 129 129 129 129 126 99.7 129 129 129 129 122 94.5 127 127 127 127 116 92.3 125 125 125 125 114 90.7 123 123 123 123 111 89.4 121 120 120 121 109 87.5 119 119 119 119 107 86.9 117 117 117 117 105 85.7 115 115 115 115 103 85.0 114 … … 114 … 112 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 83.9 113 96.3 71.2 83.0 112 95.2 70.5 77.6 94.6 78.7 64.2 59.2 59.2 51.2 51.2 44.8 44.8 38.0 38.0 32.9 32.9 28.4 28.4 24.5 24.5 21.1 21.1 18.3 18.3 15.5 15.5 12.6 12.6 10.4 10.4 8.41 8.41 6.86 6.86 6.18 6.18 5.18 5.18 4.37 4.37 3.76 3.76 2.77 2.77 2.39 2.39 1.62 1.62 1.41 1.41 … … … … … … … … … … … … 5 6 7 8 113 83.9 113 83.9 112 83.0 112 83.0 94.6 77.6 94.6 77.6 59.2 59.2 59.2 59.2 44.8 44.8 44.8 44.8 32.9 32.9 32.9 32.9 24.5 24.5 24.5 24.5 18.3 18.3 18.3 18.3 12.6 12.6 12.6 12.6 8.41 8.41 8.41 8.41 6.18 6.18 6.18 6.18 4.37 4.37 4.37 4.37 2.77 2.77 2.77 2.77 1.62 1.62 1.62 1.62 … … … … … … … … … … … … 9 10 11 12 13 … 113 83.9 113 113 … 112 83.0 111 111 … 94.6 77.6 87.4 87.4 … 59.2 59.2 57.5 57.5 … 44.8 44.8 44.4 44.4 … 32.9 32.9 32.9 32.9 … 24.5 24.5 24.5 24.5 … 18.3 18.3 18.3 18.3 … 12.6 12.6 12.6 12.6 … 8.41 8.41 8.41 8.41 … 6.18 6.18 6.18 6.18 … 4.37 4.37 4.37 4.37 … 2.77 2.77 2.77 2.77 … 1.62 1.62 1.62 1.62 … … … … … … … … … … … … … … … 14 15 16 17 18 19 … 113 83.9 113 … … … 112 83.0 111 … … … 94.6 77.6 87.4 … … … 59.2 59.2 57.5 … … … 44.8 44.8 44.4 … … … 32.9 32.9 32.9 … … … 24.5 24.5 24.5 … … … 18.3 18.3 18.3 … … … 12.6 12.6 12.6 … … … 8.41 8.41 8.41 … … … 6.18 6.18 6.18 … … … 4.37 4.37 4.37 … … … 2.77 2.77 2.77 … … … 1.62 1.62 1.62 … … … … … … … … … … … … … … … … … … … … 20 21 22 23 24 25 113 83.9 113 83.9 113 83.9 112 83.0 112 83.0 112 83.0 103 82.4 103 82.4 103 82.4 77.7 77.7 77.7 77.7 77.7 77.7 58.7 58.7 58.7 58.7 58.7 58.7 46.0 46.0 46.0 46.0 46.0 46.0 36.9 36.9 36.9 36.9 36.9 36.9 28.7 28.7 28.7 28.7 28.7 28.7 22.9 22.9 22.9 22.9 22.9 22.9 18.4 18.4 18.4 18.4 18.4 18.4 14.4 14.4 14.4 14.4 14.4 14.4 11.5 11.5 11.5 11.5 11.5 11.5 9.16 9.16 9.16 9.16 9.16 9.16 6.64 6.64 6.64 6.64 6.64 6.64 … … … … … … … … … … … … … … … … … … 26 27 28 29 83.9 113 96.3 71.3 83.0 112 95.4 70.6 82.4 103 87.8 69.9 77.7 77.7 64.4 64.0 58.7 58.7 49.7 49.7 46.0 46.0 39.3 39.3 36.9 36.9 31.4 31.4 28.7 28.7 24.5 24.5 22.9 22.9 19.4 19.4 18.4 18.4 15.5 15.5 14.4 14.4 12.1 12.1 11.5 11.5 9.85 9.85 9.16 9.16 7.93 7.93 6.64 6.64 5.62 5.62 … … … … … … … … … … … … 30 31 32 33 113 83.9 113 83.9 112 83.0 112 83.0 103 82.4 103 82.4 77.7 77.7 77.7 77.7 58.7 58.7 58.7 58.7 46.0 46.0 46.0 46.0 36.9 36.9 36.9 36.9 28.7 28.7 28.7 28.7 22.9 22.9 22.9 22.9 18.4 18.4 18.4 18.4 14.4 14.4 14.4 14.4 11.5 11.5 11.5 11.5 9.16 9.16 9.16 9.16 6.64 6.64 6.64 6.64 … … … … … … … … … … … … 34 35 36 113 83.9 113 112 83.0 112 103 82.4 103 77.7 77.7 77.7 58.7 58.7 58.7 46.0 46.0 46.0 36.9 36.9 36.9 28.7 28.7 28.7 22.9 22.9 22.9 18.4 18.4 18.4 14.4 14.4 14.4 11.5 11.5 11.5 9.16 9.16 9.16 6.64 6.64 6.64 … … … … … … … … … 37 38 39 40 41 42 83.9 113 … … 113 … 83.0 112 … … 111 … 82.4 103 … … 87.4 … 77.7 77.7 … … 57.5 … 58.7 58.7 … … 44.4 … 46.0 46.0 … … 32.9 … 36.9 36.9 … … 24.5 … 28.7 28.7 … … 18.3 … 22.9 22.9 … … 12.6 … 18.4 18.4 … … 8.41 … 14.4 14.4 … … 6.18 … 11.5 11.5 … … 4.37 … 9.16 9.16 … … 2.77 … 6.64 6.64 … … 1.62 … … … … … … … … … … … … … … … … … … … 113 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo Forgings Forgings Forgings Forgings SA-182 SA-182 SA-182 SA-182 F317L F317L F317L F317L S31703 S31703 S31703 S31703 … … … … > 125 > 125 ≤ 125 ≤ 125 8 8 8 8 1 1 1 1 5 6 7 8 9 10 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo Forgings Forgings Plate Plate Plate Plate SA-182 SA-182 SA-240 SA-240 SA-240 SA-240 F317 F317 317 317 317L 317L S31700 S31700 S31700 S31700 S31703 S31703 … … … … … … ≤ 125 ≤ 125 … … … … 8 8 8 8 8 8 1 1 1 1 1 1 11 12 13 14 15 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo Wld. tube Wld. tube Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 SA-249 SA-249 TP317 TP317 TP317 TP317L TP317L S31700 S31700 S31700 S31703 S31703 … … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 16 17 18 19 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo Smls. & wld. pipe Smls. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP317 TP317 TP317 TP317 S31700 S31700 S31700 S31700 … … … … … … … … 8 8 8 8 1 1 1 1 20 21 22 23 24 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo Smls. pipe Smls. pipe Wld. pipe Wld. pipe Smls. & wld. fittings SA-312 SA-312 SA-312 SA-312 SA-403 TP317L TP317L TP317L TP317L 317 S31703 S31703 S31703 S31703 S31700 … … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 25 26 27 28 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo Fittings Fittings Fittings Fittings SA-403 SA-403 SA-403 SA-403 317L 317L 317L 317L S31703 S31703 S31703 S31703 CR CR WP-S WP-S … … … … 8 8 8 8 1 1 1 1 29 30 31 32 33 34 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo Fittings Fittings Fittings Fittings Fittings Fittings SA-403 SA-403 SA-403 SA-403 SA-403 SA-403 317L 317L 317L 317L 317L 317L S31703 S31703 S31703 S31703 S31703 S31703 WP-W WP-W WP-WU WP-WU WP-WX WP-WX … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 Line No. 114 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 450 450 485 485 170 170 170 170 NP NP NP NP NP NP NP NP 454 454 454 454 343 343 343 343 HA-4 HA-4 HA-4 HA-4 G5 … G5 … 5 6 7 8 9 10 515 515 515 515 515 515 205 205 205 205 205 205 NP NP NP NP NP NP NP NP NP NP NP NP 816 816 816 816 454 454 343 343 343 343 343 343 HA-2 HA-2 HA-2 HA-2 HA-4 HA-4 G5, G12, T8 G12, T9 G5, G12, T8 G12, T9 G5 … 11 12 13 14 15 515 515 515 515 515 205 205 205 205 205 NP NP NP NP NP 427 NP NP NP NP NP 816 816 454 454 NP 343 343 343 343 HA-2 HA-2 HA-2 HA-4 HA-4 G5, W12 G5, G12, G24, T8 G12, G24, T9 G5, G24 G24 16 17 18 19 515 515 515 515 205 205 205 205 NP NP NP NP 427 NP NP NP 816 816 816 816 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, T8, W12, W14 G12, T9 G5, G12, G24, T8 G12, G24, T9 20 21 22 23 24 515 515 515 515 515 205 205 205 205 205 NP NP NP NP NP NP NP NP NP NP 454 454 454 454 816 343 343 343 343 343 HA-4 HA-4 HA-4 HA-4 HA-2 G5 … G5, G24 G24 G5, G12, T8, W14 25 26 27 28 515 515 515 515 205 205 205 205 NP NP NP NP NP NP NP NP 454 454 454 454 343 343 343 343 HA-4 HA-4 HA-4 HA-4 G5, G24 G24 G5 … 29 30 31 32 33 34 515 515 515 515 515 515 205 205 205 205 205 205 NP NP NP NP NP NP NP NP NP NP NP NP 454 454 454 454 454 454 343 343 343 343 343 343 HA-4 HA-4 HA-4 HA-4 HA-4 HA-4 G5, G24 G24 G5, G24 G24 G5, G24 G24 115 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 115 115 115 115 115 106 115 106 115 96.3 115 96.3 115 91.3 115 91.3 115 87.4 115 87.4 109 81.2 109 81.2 103 76.0 103 76.0 98.0 72.5 98.0 72.5 95.7 71.2 95.7 71.2 94.1 70.0 94.1 70.0 92.8 68.8 92.8 68.8 90.9 67.5 90.9 67.5 89.0 66.3 89.0 66.3 87.8 65.0 87.8 65.0 86.6 63.8 86.6 63.8 5 6 7 8 9 10 138 138 138 138 138 138 138 128 138 128 138 127 138 118 138 118 138 115 138 112 138 112 137 109 138 107 138 107 135 105 134 99.2 134 99.2 131 97.1 126 92.8 126 92.8 123 91.2 119 88.1 119 88.1 118 87.3 116 86.1 116 86.1 116 85.4 114 84.1 114 84.1 113 83.8 112 82.9 112 82.9 111 82.5 111 82.0 111 82.0 109 80.6 110 81.4 110 81.4 107 79.4 108 80.6 108 80.6 105 78.1 108 79.8 108 79.8 103 76.9 11 12 13 14 15 138 117 117 117 117 138 117 109 117 108 138 117 99.8 117 98.3 138 117 94.9 116 93.0 138 117 90.8 115 88.8 134 114 84.0 111 82.5 126 107 78.8 105 78.0 119 101 74.7 99.9 74.1 116 99.0 73.3 97.9 72.6 114 96.8 72.1 96.0 71.4 112 95.7 70.8 94.2 70.1 111 94.4 69.6 93.0 68.9 110 93.1 69.0 91.1 67.7 108 92.5 68.4 89.3 66.4 … 91.4 67.7 87.4 65.2 16 17 18 19 138 138 117 117 138 128 117 109 138 118 117 99.8 138 112 117 94.9 138 107 117 90.8 134 99.2 114 84.0 126 92.8 107 78.8 119 88.1 101 74.7 116 86.1 99.0 73.3 114 84.1 96.8 72.1 112 82.9 95.7 70.8 111 82.0 94.4 69.6 110 81.4 93.1 69.0 108 80.6 92.5 68.4 108 79.8 91.4 67.7 20 21 22 23 24 138 138 117 117 138 138 126 117 107 138 138 115 117 98.5 138 138 109 117 93.0 138 135 105 115 88.8 138 131 97.1 111 82.5 134 123 91.3 105 78.0 126 118 87.3 99.9 74.1 119 116 85.4 97.9 72.6 116 113 83.8 96.0 71.4 114 111 82.5 94.2 70.1 112 109 80.6 93.0 68.9 111 107 79.4 91.1 67.7 110 105 78.1 89.3 66.4 108 103 76.9 87.4 65.2 108 25 26 27 28 117 117 138 138 117 108 138 127 117 98.3 138 115 116 93.0 137 109 115 88.8 135 105 111 82.5 131 97.1 105 78.0 123 91.2 99.9 74.1 118 87.3 97.9 72.6 116 85.4 96.0 71.4 113 83.8 94.2 70.1 111 82.5 93.0 68.9 109 80.6 91.1 67.7 107 79.4 89.3 66.4 105 78.1 87.4 65.2 103 76.9 29 30 31 32 33 34 117 117 117 117 117 117 117 108 117 108 117 108 117 98.3 117 98.3 117 98.3 116 93.0 116 93.0 116 93.0 115 88.8 115 88.8 115 88.8 111 82.5 111 82.5 111 82.5 105 78.0 105 78.0 105 78.0 99.9 74.1 99.9 74.1 99.9 74.1 97.9 72.6 97.9 72.6 97.9 72.6 96.0 71.4 96.0 71.4 96.0 71.4 94.2 70.1 94.2 70.1 94.2 70.1 93.0 68.9 93.0 68.9 93.0 68.9 91.1 67.7 91.1 67.7 91.1 67.7 89.3 66.4 89.3 66.4 89.3 66.4 87.4 65.2 87.4 65.2 87.4 65.2 116 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 9 10 107 79.2 107 79.2 … … 106 78.7 106 78.7 … … 105 77.8 105 77.8 … … 99.8 77.1 99.8 77.1 … … 80.3 75.0 80.3 75.0 … … 65.5 65.5 65.5 65.5 … … 50.4 50.4 50.4 50.4 … … 38.6 38.6 38.6 38.6 … … 29.6 29.6 29.6 29.6 … … 23.0 23.0 23.0 23.0 … … 17.7 17.7 17.7 17.7 … … 13.4 13.4 13.4 13.4 … … 10.4 10.4 10.4 10.4 … … 8.05 8.05 8.05 8.05 … … … … … … … … … … … … … … … … … … … … 11 12 13 14 15 … 90.5 67.1 … … … 89.9 66.5 … … … 89.3 65.9 … … … 85.3 65.3 … … … 68.1 64.0 … … … 55.6 55.6 … … … 42.9 42.9 … … … 33.0 33.0 … … … 25.3 25.3 … … … 19.4 19.4 … … … 14.7 14.7 … … … 11.3 11.3 … … … 8.90 8.90 … … … 6.77 6.77 … … … … … … … … … … … … … … … … … 16 17 18 19 107 79.2 90.5 67.1 106 78.7 89.9 66.5 105 77.8 89.3 65.9 99.8 77.1 85.3 65.3 80.3 75.0 68.1 64.0 65.5 65.5 55.6 55.6 50.4 50.4 42.9 42.9 38.6 38.6 33.0 33.0 29.6 29.6 25.3 25.3 23.0 23.0 19.4 19.4 17.7 17.7 14.7 14.7 13.4 13.4 11.3 11.3 10.4 10.4 8.90 8.90 8.05 8.05 6.77 6.77 … … … … … … … … … … … … 20 21 22 23 24 … … … … 107 … … … … 106 … … … … 105 … … … … 99.8 … … … … 80.3 … … … … 65.5 … … … … 50.4 … … … … 38.6 … … … … 29.6 … … … … 23.0 … … … … 17.7 … … … … 13.4 … … … … 10.4 … … … … 8.05 … … … … … … … … … … … … … … … 25 26 27 28 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 30 31 32 33 34 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 117 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 18Cr – 18Ni – 2Si 18Cr – 18Ni – 2Si 18Cr – 18Ni – 2Si 18Cr – 18Ni – 2Si Smls. tube Smls. tube Plate Plate SA-213 SA-213 SA-240 SA-240 XM-15 XM-15 XM-15 XM-15 S38100 S38100 S38100 S38100 … … … … … … … … 8 8 8 8 1 1 1 1 5 6 7 8 18Cr – 18Ni – 2Si 18Cr – 18Ni – 2Si 18Cr – 18Ni – 2Si 18Cr – 18Ni – 2Si Wld. tube Wld. tube Wld. pipe Wld. pipe SA-249 SA-249 SA-312 SA-312 TPXM-15 TPXM-15 TPXM-15 TPXM-15 S38100 S38100 S38100 S38100 … … … … … … … … 8 8 8 8 1 1 1 1 9 10 11 12 13 14 19Cr – 9Ni – 1⁄2Mo 19Cr – 9Ni – 1⁄2Mo 19Cr – 9Ni – 2Mo 19Cr – 9Ni – 2Mo 19Cr – 10Ni – 3Mo 19Cr – 10Ni – 3Mo Castings Castings Castings Castings Castings Castings SA-351 SA-351 SA-351 SA-351 SA-351 SA-351 CF10 CF10 CF10M CF10M CG8M CG8M J92590 J92590 … … J93000 J93000 … … … … … … … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 15 16 17 18 19 20 19Cr – 15Ni – 4Mo 19Cr – 15Ni – 4Mo 19Cr – 15Ni – 4Mo 19Cr – 15Ni – 4Mo 19Cr – 15Ni – 4Mo 19Cr – 15Ni – 4Mo Smls. tube Smls. tube Plate Plate Wld. tube Wld. tube SA-213 SA-213 SA-240 SA-240 SA-249 SA-249 … … … … … … S31725 S31725 S31725 S31725 S31725 S31725 … … … … … … … … … … … … 8 8 8 8 8 8 4 4 4 4 4 4 21 22 23 24 25 26 19Cr – 15Ni – 4Mo 19Cr – 15Ni – 4Mo 19Cr – 15Ni – 4Mo 19Cr – 15Ni – 4Mo 19Cr – 15Ni – 4Mo 19Cr – 15Ni – 4Mo Smls. pipe Smls. pipe Wld. pipe Wld. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 SA-358 SA-358 … … … … … … S31725 S31725 S31725 S31725 S31725 S31725 … … … … … … … … … … … … 8 8 8 8 8 8 4 4 4 4 4 4 27 28 29 30 31 32 19Cr – 15Ni – 4Mo 19Cr – 15Ni – 4Mo 19Cr – 15Ni – 4Mo 19Cr – 15Ni – 4Mo 19Cr – 15Ni – 4Mo 19Cr – 15Ni – 4Mo Smls. pipe Smls. pipe Wld. pipe Wld. pipe Bar Bar SA-376 SA-376 SA-409 SA-409 SA-479 SA-479 … … … … … … S31725 S31725 S31725 S31725 S31725 S31725 … … … … … … … … … … … … 8 8 8 8 8 8 4 4 4 4 4 4 Line No. 118 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 515 515 515 515 205 205 205 205 NP NP NP NP NP NP NP NP 538 538 538 538 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5 … G5 … 5 6 7 8 515 515 515 515 205 205 205 205 NP NP NP NP NP NP NP NP 538 538 510 538 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, G24 G24 G5, G24 G24 9 10 11 12 13 14 485 485 485 485 515 515 205 205 205 205 240 240 NP NP NP NP NP NP NP NP NP NP NP NP 816 816 816 816 538 538 343 343 NP NP 343 343 HA-1 HA-1 HA-2 HA-2 HA-2 HA-2 G1, G5, G32, T6 G1, G32, T7 G1, G5, G32, T6 G1, G32, T8 G1, G5, G32 G1, G32 15 16 17 18 19 20 515 515 515 515 515 515 205 205 205 205 205 205 NP NP NP NP NP NP NP NP NP NP NP NP 204 204 204 204 204 204 204 204 204 204 204 204 HA-4 HA-4 HA-4 HA-4 HA-4 HA-4 G5 … G5 … G5, G24 G24 21 22 23 24 25 26 515 515 515 515 515 515 205 205 205 205 205 205 NP NP NP NP NP NP NP NP NP NP NP NP 204 204 204 204 204 204 NP NP NP NP 204 204 HA-4 HA-4 HA-4 HA-4 HA-4 HA-4 G5 … G5, G24 G24 G5, G24 G24 27 28 29 30 31 32 515 515 515 515 515 515 205 205 205 205 205 205 NP NP NP NP NP NP NP NP NP NP NP NP 204 204 204 204 204 204 204 204 204 204 204 204 HA-4 HA-4 HA-4 HA-4 HA-4 HA-4 G5 … G5, G24 G24 G5 … 119 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 138 138 138 138 138 126 138 126 137 113 137 113 134 107 134 107 130 103 130 103 126 95.7 126 95.7 122 89.9 122 89.9 116 85.9 116 85.9 114 84.1 114 84.1 111 82.2 111 82.2 109 80.5 109 80.5 107 79.2 107 79.2 105 77.3 105 77.3 103 76.0 103 76.0 101 74.8 101 74.8 5 6 7 8 117 117 117 117 117 107 117 107 117 96.2 117 96.2 114 91.2 114 91.2 111 87.4 111 87.4 107 81.1 107 81.1 103 76.6 103 76.6 98.5 72.7 98.5 72.7 96.5 71.2 96.5 71.2 94.7 70.0 94.7 70.0 92.8 68.8 92.8 68.8 90.9 67.5 90.9 67.5 89.1 66.3 89.1 66.3 87.1 65.0 87.1 65.0 85.9 63.8 85.9 63.8 9 10 11 12 13 14 138 138 138 138 148 148 134 126 138 129 146 139 130 113 138 119 143 127 126 107 136 113 139 120 122 103 134 108 135 113 119 95.7 133 99.3 132 102 118 90.0 125 92.7 128 94.9 115 85.6 119 88.1 122 90.0 114 83.9 116 86.1 120 88.4 111 82.3 114 84.4 117 87.2 109 80.5 112 83.2 116 86.0 107 79.2 111 82.0 114 84.7 105 77.7 110 81.1 113 83.5 103 76.4 108 80.2 112 82.9 101 74.9 107 79.5 111 81.7 15 16 17 18 19 20 138 138 138 138 117 117 138 127 138 127 117 108 138 115 138 115 117 97.6 137 109 137 109 116 92.6 135 105 135 105 114 88.8 131 97.2 131 97.2 111 82.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 24 25 26 138 138 117 117 117 117 138 127 117 108 117 108 138 115 117 97.6 117 97.6 137 109 116 92.6 116 92.6 135 105 114 88.8 114 88.8 131 97.2 111 82.6 111 82.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 27 28 29 30 31 32 138 138 117 117 138 138 138 127 117 108 138 127 138 115 117 97.6 138 115 137 109 116 92.6 137 109 135 105 114 88.8 135 105 131 97.2 111 82.6 131 97.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 120 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 99.3 73.6 99.3 73.6 98.0 72.4 98.0 72.4 93.3 70.8 93.3 70.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 84.0 62.6 84.0 62.6 83.2 61.3 83.2 61.3 79.0 60.1 … 60.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 10 11 12 13 14 99.5 73.6 107 78.9 109 80.5 92.8 72.6 104 78.2 97.7 78.9 75.6 70.0 94.7 77.6 72.6 77.0 61.2 61.2 73.7 73.7 … … 49.0 49.0 57.9 57.9 … … 40.1 40.1 46.0 46.0 … … 32.8 32.8 36.9 36.9 … … 27.2 27.2 30.1 30.1 … … 23.4 23.4 24.3 24.3 … … 19.6 19.6 20.3 20.3 … … 16.7 16.7 17.0 17.0 … … 14.7 14.7 14.3 14.3 … … 12.9 12.9 12.1 12.1 … … 11.0 11.0 10.3 10.3 … … … … … … … … … … … … … … … … … … … … 15 16 17 18 19 20 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 24 25 26 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 27 28 29 30 31 32 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 121 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 5 20Cr – 10Ni 20Cr – 18Ni – 6Mo 20Cr – 18Ni – 6Mo 20Cr – 18Ni – 6Mo 20Cr – 18Ni – 6Mo Bar Castings Castings Forgings Forgings SA-479 SA-351 SA-351 SA-182 SA-182 ER308 CK3MCuN CK3MCuN F44 F44 S30880 J93254 J93254 S31254 S31254 … … … … … … … … … … … 8 8 8 8 … 4 4 4 4 6 7 8 9 10 11 20Cr – 18Ni – 6Mo 20Cr – 18Ni – 6Mo 20Cr – 18Ni – 6Mo 20Cr – 18Ni – 6Mo 20Cr – 18Ni – 6Mo 20Cr – 18Ni – 6Mo Wld. tube Wld. tube Smls. pipe Smls. pipe Wld. pipe Wld. pipe SA-249 SA-249 SA-312 SA-312 SA-312 SA-312 … … … … … … S31254 S31254 S31254 S31254 S31254 S31254 … … … … … … … … … … … … 8 8 8 8 8 8 4 4 4 4 4 4 12 13 14 20Cr – 18Ni – 6Mo 20Cr – 18Ni – 6Mo 20Cr – 18Ni – 6Mo Wld. pipe Wld. pipe Fittings SA-358 SA-358 SA-403 … … … S31254 S31254 S31254 … … … … … … 8 8 8 4 4 4 15 16 17 18 20Cr – 18Ni – 6Mo 20Cr – 18Ni – 6Mo 20Cr – 18Ni – 6Mo 20Cr – 18Ni – 6Mo Plate Plate Plate Plate SA-240 SA-240 SA-240 SA-240 … … … … S31254 S31254 S31254 S31254 … … … … >5 >5 ≤5 ≤5 8 8 8 8 4 4 4 4 19 20 21 22 23 21Cr – 6Ni – 9Mn 21Cr – 6Ni – 9Mn 21Cr – 6Ni – 9Mn 21Cr – 6Ni – 9Mn 21Cr – 6Ni – 9Mn Forgings Smls. pipe Smls. pipe Wld. pipe Wld. pipe SA-182 SA-312 SA-312 SA-312 SA-312 FXM-11 TPXM-11 TPXM-11 TPXM-11 TPXM-11 S21904 S21904 S21904 S21904 S21904 … … … … … … … … … … 8 8 8 8 8 3 3 3 3 3 24 25 26 27 21Cr – 6Ni – 9Mn 21Cr – 6Ni – 9Mn 21Cr – 6Ni – 9Mn 21Cr – 6Ni – 9Mn Plate Plate Forgings Forgings SA-666 SA-666 SA-965 SA-965 XM-11 XM-11 FXM-11 FXM-11 S21904 S21904 S21904 S21904 … … … … … … … … 8 8 8 8 3 3 3 3 28 29 30 31 21Cr – 11Ni – N 21Cr – 11Ni – N 21Cr – 11Ni – N 21Cr – 11Ni – N Forgings Forgings Smls. tube Smls. tube SA-182 SA-182 SA-213 SA-213 F45 F45 … … S30815 S30815 S30815 S30815 … … … … … … … … 8 8 8 8 2 2 2 2 32 33 34 35 21Cr – 11Ni – N 21Cr – 11Ni – N 21Cr – 11Ni – N 21Cr – 11Ni – N Plate Plate Wld. tube Wld. tube SA-240 SA-240 SA-249 SA-249 … … … … S30815 S30815 S30815 S30815 … … … … … … … … 8 8 8 8 2 2 2 2 36 37 38 39 40 41 21Cr – 11Ni – N 21Cr – 11Ni – N 21Cr – 11Ni – N 21Cr – 11Ni – N 21Cr – 11Ni – N 21Cr – 11Ni – N Smls. pipe Smls. pipe Wld. pipe Wld. pipe Bar Bar SA-312 SA-312 SA-312 SA-312 SA-479 SA-479 … … … … … … S30815 S30815 S30815 S30815 S30815 S30815 … … … … … … … … … … … … 8 8 8 8 8 8 2 2 2 2 2 2 Line No. 122 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 515 550 550 650 650 205 260 260 305 305 NP NP NP NP NP 427 399 NP 399 NP NP 399 399 399 399 NP 343 343 343 343 HA-2 HA-2 HA-2 HA-2 HA-2 G5 G1, G5 G1 G5 … 6 7 8 9 10 11 650 650 650 650 650 650 305 305 305 305 305 305 NP NP NP NP NP NP 399 NP 399 NP 399 NP 399 399 399 399 399 399 343 343 NP NP NP NP HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, G24 G24 G5 … G5, G24 G24 12 13 14 650 650 650 305 305 305 NP NP NP 399 NP 399 399 399 NP 343 343 NP HA-2 HA-2 HA-2 G5, G24 G24 G5, W12 15 16 17 18 655 655 690 690 310 310 310 310 NP NP NP NP 399 NP 399 NP 399 399 399 399 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5 … G5 … 19 20 21 22 23 620 620 620 620 620 345 345 345 345 345 NP NP NP NP NP NP NP NP NP NP 316 316 316 316 316 316 316 316 316 316 HA-6 HA-6 HA-6 HA-6 HA-6 … G5 … G5, G24 G24 24 25 26 27 620 620 620 620 345 345 345 345 NP NP NP NP NP NP NP NP 316 316 316 316 316 316 316 316 HA-6 HA-6 HA-6 HA-6 G5 … G5 … 28 29 30 31 600 600 600 600 310 310 310 310 899 899 899 899 NP NP NP NP 899 899 899 899 343 343 343 343 HA-6 HA-6 HA-6 HA-6 G5, G6, T5 G6, T6 G5, G6, T5 G6, T6 32 33 34 35 600 600 600 600 310 310 310 310 899 899 899 899 NP NP NP NP 899 899 899 899 343 343 343 343 HA-6 HA-6 HA-6 HA-6 G5, G6, T5 G6, T6 G5, G6, G24, T5 G6, G24, T6 36 37 38 39 40 41 600 600 600 600 600 600 310 310 310 310 310 310 899 899 899 899 899 899 NP NP NP NP NP NP 899 899 899 899 899 899 343 343 343 343 343 343 HA-6 HA-6 HA-6 HA-6 HA-6 HA-6 G5, G6, T5 G6, T6 G5, G6, G24, T5 G6, G24, T6 G5, G6, T5 G6, T6 123 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 5 138 158 158 185 185 138 158 151 185 175 137 158 141 185 162 134 154 134 181 154 130 149 127 176 147 126 143 119 168 137 122 139 112 163 129 116 136 107 159 125 114 135 106 158 123 111 134 105 157 121 109 133 104 156 120 107 132 103 156 119 105 … … … … 103 … … … … … … … … … 6 7 8 9 10 11 157 157 185 185 157 157 157 149 185 175 157 149 157 138 185 162 157 138 154 131 181 154 154 131 149 125 176 147 149 125 143 116 168 137 143 116 139 110 163 129 139 110 135 106 159 125 135 106 134 104 158 123 134 104 134 103 157 121 134 103 133 102 156 120 133 102 132 101 156 119 132 101 … … … … … … … … … … … … … … … … … … 12 13 14 157 157 185 157 149 185 157 138 185 154 131 181 149 125 176 143 116 168 139 110 163 135 106 159 134 104 158 134 103 157 133 102 156 132 101 156 … … … … … … … … … 15 16 17 18 187 187 197 197 187 178 197 182 186 167 197 166 183 158 193 158 178 151 187 151 170 140 179 140 164 133 173 133 161 128 169 128 160 125 168 125 159 124 167 124 158 123 166 123 158 122 165 122 … … … … … … … … … … … … 19 20 21 22 23 177 177 177 151 151 177 177 177 151 151 176 177 176 151 150 165 172 165 146 140 151 165 151 140 128 136 158 136 134 115 126 153 126 130 107 120 149 120 127 102 117 148 117 126 99.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 24 25 26 27 177 177 177 177 177 177 177 177 177 176 177 176 172 165 172 165 165 151 165 151 158 136 158 136 153 126 153 126 149 120 149 120 148 117 148 117 … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 31 172 172 172 172 171 171 171 171 170 169 170 169 165 161 165 161 160 151 160 151 155 138 155 138 151 129 151 129 148 123 148 123 147 121 147 121 146 120 146 120 145 118 145 118 143 117 143 117 142 116 142 116 140 115 140 115 138 113 138 113 32 33 34 35 172 172 145 145 171 171 145 145 170 169 144 144 165 161 141 137 160 151 136 129 155 138 132 117 151 129 128 110 148 123 126 105 147 121 125 103 146 120 124 102 145 118 123 101 143 117 122 99.9 142 116 121 98.7 140 115 119 98.0 138 113 118 96.9 36 37 38 39 40 41 172 172 145 145 172 172 171 171 145 145 171 171 170 169 144 144 170 169 165 161 141 137 165 161 160 151 136 129 160 151 155 138 132 117 155 138 151 129 128 110 151 129 148 123 126 105 148 123 147 121 125 103 147 121 146 120 124 102 146 120 145 118 123 101 145 118 143 117 122 99.9 143 117 142 116 121 98.7 142 116 140 115 119 98.0 140 115 138 113 118 96.9 138 113 124 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 10 11 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 12 13 14 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 15 16 17 18 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 19 20 21 22 23 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 24 25 26 27 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 31 136 112 136 112 117 109 117 109 93.4 93.4 93.4 93.4 73.6 73.6 73.6 73.6 58.4 58.4 58.4 58.4 45.8 45.8 45.8 45.8 35.5 35.5 35.5 35.5 28.0 28.0 28.0 28.0 22.3 22.3 22.3 22.3 17.7 17.7 17.7 17.7 14.2 14.2 14.2 14.2 11.9 11.9 11.9 11.9 10.2 10.2 10.2 10.2 8.19 8.19 8.19 8.19 6.58 6.58 6.58 6.58 5.80 5.80 5.80 5.80 4.85 4.85 4.85 4.85 32 33 34 35 136 112 114 95.6 117 109 101 92.7 93.4 93.4 79.6 79.6 73.6 73.6 62.9 62.9 58.4 58.4 50.0 50.0 45.8 45.8 39.1 39.1 35.5 35.5 30.0 30.0 28.0 28.0 23.8 23.8 22.3 22.3 18.7 18.7 17.7 17.7 14.7 14.7 14.2 14.2 11.8 11.8 11.9 11.9 10.3 10.3 10.2 10.2 8.82 8.82 8.19 8.19 6.89 6.89 6.58 6.58 5.61 5.61 5.80 5.80 4.92 4.92 4.85 4.85 4.10 4.10 36 37 38 39 40 41 136 112 114 95.6 136 112 117 109 101 92.7 117 109 93.4 93.4 79.6 79.6 93.4 93.4 73.6 73.6 62.9 62.9 73.6 73.6 58.4 58.4 50.0 50.0 58.4 58.4 45.8 45.8 39.1 39.1 45.8 45.8 35.5 35.5 30.0 30.0 35.5 35.5 28.0 28.0 23.8 23.8 28.0 28.0 22.3 22.3 18.7 18.7 22.3 22.3 17.7 17.7 14.7 14.7 17.7 17.7 14.2 14.2 11.8 11.8 14.2 14.2 11.9 11.9 10.3 10.3 11.9 11.9 10.2 10.2 8.82 8.82 10.2 10.2 8.19 8.19 6.89 6.89 8.19 8.19 6.58 6.58 5.61 5.61 6.58 6.58 5.80 5.80 4.92 4.92 5.80 5.80 4.85 4.85 4.10 4.10 4.85 4.85 125 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (10) Line No. Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 5 22Cr – 5Ni – 3Mo – N 22Cr – 5Ni – 3Mo – N 22Cr – 5Ni – 3Mo – N 22Cr – 5Ni – 3Mo – N 22Cr – 5Ni – 3Mo – N Forgings Plate Bar Smls. tube Wld. tube SA-182 SA-240 SA-479 SA-789 SA-789 F51 … … … … S31803 S31803 S31803 S31803 S31803 … … … … … … … … … … 10H 10H 10H 10H 10H 1 1 1 1 1 6 7 8 9 10 22Cr – 5Ni – 3Mo – N 22Cr – 5Ni – 3Mo – N 22Cr – 5Ni – 3Mo – N 22Cr – 5Ni – 3Mo – N 22Cr – 5Ni – 3Mo – N Smls. pipe Wld. pipe Smls. fittings Wld. fittings Smls. & wld. fittings SA-790 SA-790 SA-815 SA-815 SA-815 … … … … … S31803 S31803 S31803 S31803 S31803 … … … … … … … … … … 10H 10H 10H 10H 10H 1 1 1 1 1 11 12 13 14 15 16 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn Castings Forgings Smls. tube Plate Wld. tube Wld. tube SA-351 SA-182 SA-213 SA-240 SA-249 SA-249 CG6MMN FXM-19 XM-19 XM-19 TPXM-19 TPXM-19 J93790 S20910 S20910 S20910 S20910 S20910 … … … … … … … … … … … … 8 8 8 8 8 8 3 3 3 3 3 3 17 18 19 20 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn Smls. & wld. pipe Smls. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-358 TPXM-19 TPXM-19 TPXM-19 XM-19 S20910 S20910 S20910 S20910 … … … 1 … … … … 8 8 8 8 3 3 3 3 21 22 23 24 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn Smls. & wld. fittings Bar Wld. pipe Wld. pipe SA-403 SA-479 SA-813 SA-814 XM-19 XM-19 TPXM-19 TPXM-19 S20910 S20910 S20910 S20910 … … … … … … … … 8 8 8 8 3 3 3 3 25 26 27 23Cr – 4Ni – Mo – Cu – N 23Cr – 4Ni – Mo – Cu – N 23Cr – 4Ni – Mo – Cu – N Plate Smls. tube Wld. tube SA-240 SA-789 SA-789 … … … S32304 S32304 S32304 … … … … > 25 > 25 10H 10H 10H 1 1 1 28 29 30 31 23Cr – 4Ni – Mo – Cu – N 23Cr – 4Ni – Mo – Cu – N 23Cr – 4Ni – Mo – Cu – N 23Cr – 4Ni – Mo – Cu – N Smls. pipe Wld. pipe Smls. tube Wld. tube SA-790 SA-790 SA-789 SA-789 … … … … S32304 S32304 S32304 S32304 … … … … … … ≤ 25 ≤ 25 10H 10H 10H 10H 1 1 1 1 32 33 34 35 36 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni Smls. & wld. fittings Smls. tube Smls. tube Plate Plate SA-403 SA-213 SA-213 SA-240 SA-240 309 TP309S TP309S 309S 309S S30900 S30908 S30908 S30908 S30908 … … … … … … … … … … 8 8 8 8 8 2 2 2 2 2 37 38 39 40 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni Wld. tube Wld. tube Smls. & wld. pipe Smls. pipe SA-249 SA-249 SA-312 SA-312 TP309S TP309S TP309S TP309S S30908 S30908 S30908 S30908 … … … … … … … … 8 8 8 8 2 2 2 2 41 42 43 44 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni Wld. pipe Wld. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP309S TP309S TP309S TP309S S30908 S30908 S30908 S30908 … … … … … … … … 8 8 8 8 2 2 2 2 126 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 620 620 620 620 620 450 450 450 450 450 316 316 316 316 316 NP NP NP NP NP 316 316 316 316 316 316 316 NP 316 316 HA-5 HA-5 HA-5 HA-5 HA-5 G32 G32 G32 G32 G24, G32 6 7 8 9 10 620 620 620 620 620 450 450 450 450 450 316 316 316 316 NP NP NP NP NP NP 316 316 NP NP 316 316 316 NP NP 316 HA-5 HA-5 HA-5 HA-5 HA-5 G32 G24, G32 G32 G24, G32 G32, W14 11 12 13 14 15 16 585 690 690 690 690 690 295 380 380 380 380 380 NP NP NP NP NP NP NP 427 NP 427 427 NP 566 649 649 649 NP 649 343 343 NP 343 NP 343 HA-2 HA-6 HA-6 HA-6 HA-6 HA-6 G1 G5, T8 T8 G5, T8 G5, W12 G24, T8 17 18 19 20 690 690 690 690 380 380 380 380 NP NP NP NP 427 NP NP 427 NP 649 649 NP NP 343 343 NP HA-6 HA-6 HA-6 HA-6 G5, W12 T8 G24, T8 G5, W12 21 22 23 24 690 690 690 690 380 380 380 380 NP NP NP NP 427 427 427 427 649 649 NP NP 343 343 NP NP HA-6 HA-6 HA-6 HA-6 G5, T8, W12, W14 G5, G22, T8 G5, W12 G5, W12 25 26 27 600 600 600 400 400 400 NP NP NP NP NP NP 316 316 316 316 316 316 HA-6 HA-6 HA-6 G32 G32 G24, G32 28 29 30 31 600 600 690 690 400 400 450 450 NP NP NP NP NP NP NP NP 316 316 316 316 316 316 316 316 HA-6 HA-6 HA-5 HA-5 G32 G24, G32 G32 G24, G32 32 33 34 35 36 515 515 515 515 515 205 205 205 205 205 NP 816 816 816 816 427 NP NP 427 NP 816 816 816 816 816 343 343 343 343 343 HA-2 HA-2 HA-2 HA-2 HA-2 G5, G12, T5, W12, W14 G5, G12, T5 G12, T6 G5, G12, T5 G12, T6 37 38 39 40 515 515 515 515 205 205 205 205 NP NP 816 816 NP NP 427 NP 816 816 816 816 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, G24, T5 G12, G24, T6 G5, G12, T5, W12, W14 G12, T6 41 42 43 44 515 515 515 515 205 205 205 205 816 816 816 816 NP NP NP NP NP NP 816 816 NP NP 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, T5, W13 G12, T6, W13 G3, G5, G12, G24, T5 G3, G12, G24, T6 127 (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (10) Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 5 177 177 177 177 151 177 177 177 177 151 177 177 177 177 151 174 174 174 174 148 171 171 171 171 145 165 165 165 165 140 161 161 161 161 137 160 160 160 160 135 159 159 159 159 135 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 10 177 151 177 151 177 177 151 177 151 177 177 151 177 151 177 174 148 174 148 174 171 145 171 145 171 165 140 165 140 165 161 137 161 137 161 160 135 160 135 160 159 135 159 135 159 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 15 16 134 197 197 197 197 168 133 196 196 196 196 167 132 195 195 195 195 165 128 191 191 191 191 162 123 185 185 185 185 158 116 180 180 180 180 153 111 176 176 176 176 149 107 174 174 174 174 147 106 173 172 173 173 146 104 171 169 171 171 144 102 170 167 170 170 142 101 169 165 169 169 140 101 167 162 167 167 138 99.5 165 161 165 165 137 98.2 163 159 163 … 135 17 18 19 20 197 197 168 197 196 196 167 196 195 195 165 195 191 191 162 191 185 185 158 185 180 180 153 180 176 176 149 176 174 174 147 174 173 172 146 173 171 169 144 171 170 167 142 170 169 165 140 169 167 162 138 167 165 161 137 165 … 159 135 … 21 22 23 24 197 197 197 197 196 196 196 196 195 195 195 195 191 191 191 191 185 185 185 185 180 180 180 180 176 176 176 176 174 174 174 174 173 173 173 173 171 171 171 171 170 170 170 170 169 169 169 169 167 167 167 167 165 165 165 165 163 163 … … 25 26 27 172 172 145 169 169 144 164 164 140 159 159 135 155 155 132 150 150 128 147 147 125 145 145 124 144 144 123 … … … … … … … … … … … … … … … … … … 28 29 30 31 172 145 197 168 169 144 194 165 164 140 189 160 159 135 184 156 155 132 178 152 150 128 173 147 147 125 170 145 145 124 168 143 144 123 167 142 … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 138 138 138 138 138 138 138 129 138 129 138 138 120 138 120 138 138 115 138 115 138 138 111 138 111 138 138 105 138 105 135 135 100 135 100 131 131 96.7 131 96.7 129 129 95.4 129 95.4 127 127 94.1 127 94.1 125 125 92.9 125 92.9 124 124 91.6 124 91.6 122 122 90.4 122 90.4 121 121 89.2 121 89.2 119 119 87.9 119 87.9 37 38 39 40 117 117 138 138 117 110 138 129 117 101 138 120 117 97.5 138 115 117 94.3 138 111 117 88.7 138 105 115 84.7 135 100 111 82.1 131 96.7 109 80.8 129 95.4 108 79.8 127 94.1 107 79.1 125 92.9 105 77.9 124 91.6 104 77.3 122 90.4 102 76.1 121 89.2 101 74.8 119 87.9 41 42 43 44 138 138 117 117 138 129 117 110 138 120 117 101 138 115 117 97.5 138 111 117 94.3 138 105 117 88.7 135 100 115 84.7 131 96.7 111 82.1 129 95.4 109 80.8 127 94.1 108 79.8 125 92.9 107 79.1 124 91.6 105 77.9 122 90.4 104 77.3 121 89.2 102 76.1 119 87.9 101 74.8 128 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 10 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 15 16 97.5 161 157 161 … 134 96.6 158 156 158 … 132 95.0 157 154 157 … 131 93.1 152 152 152 … 129 … 132 132 132 … 111 … 83.6 83.6 83.6 … 71.4 … 56.1 56.1 56.1 … 48.0 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 17 18 19 20 … 157 134 … … 156 132 … … 154 131 … … 152 129 … … 132 111 … … 83.6 71.4 … … 56.1 48.0 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 24 161 161 … … 158 158 … … 157 157 … … 152 152 … … 132 132 … … 83.6 83.6 … … 56.1 56.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 31 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 115 115 86.7 115 86.7 89.4 89.4 78.5 89.4 78.5 59.2 59.2 59.2 59.2 59.2 44.2 44.2 44.2 44.2 44.2 31.8 31.8 31.8 31.8 31.8 23.7 23.7 23.7 23.7 23.7 16.9 16.9 16.9 16.9 16.9 10.7 10.7 10.7 10.7 10.7 6.10 6.10 6.10 6.10 6.10 3.78 3.78 3.78 3.78 3.78 2.96 2.96 2.96 2.96 2.96 2.40 2.40 2.40 2.40 2.40 1.76 1.76 1.76 1.76 1.76 1.15 1.15 1.15 1.15 1.15 … … … … … … … … … … … … … … … 37 38 39 40 98.9 73.5 115 86.7 74.7 64.8 89.4 78.5 50.6 50.6 59.2 59.2 37.4 37.4 44.2 44.2 27.5 27.5 31.8 31.8 20.4 20.4 23.7 23.7 14.2 14.2 16.9 16.9 9.27 9.27 10.7 10.7 5.22 5.22 6.10 6.10 3.23 3.23 3.78 3.78 2.53 2.53 2.96 2.96 2.06 2.06 2.40 2.40 1.52 1.52 1.76 1.76 0.960 0.960 1.15 1.15 … … … … … … … … … … … … 41 42 43 44 115 86.7 98.9 73.5 89.4 78.5 74.7 64.8 59.2 59.2 50.6 50.6 44.2 44.2 37.4 37.4 31.8 31.8 27.5 27.5 23.7 23.7 20.4 20.4 16.9 16.9 14.2 14.2 10.7 10.7 9.27 9.27 6.10 6.10 5.22 5.22 3.78 3.78 3.23 3.23 2.96 2.96 2.53 2.53 2.40 2.40 2.06 2.06 1.76 1.76 1.52 1.52 1.15 1.15 0.960 0.960 … … … … … … … … … … … … 129 (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni Wld. pipe Bar Bar SA-358 SA-479 SA-479 309S 309S 309S S30908 S30908 S30908 1 … … … … … 8 8 8 2 2 2 4 5 6 7 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni Wld. pipe Wld. pipe Wld. pipe Wld. pipe SA-813 SA-813 SA-814 SA-814 TP309S TP309S TP309S TP309S S30908 S30908 S30908 S30908 … … … … … … … … 8 8 8 8 2 2 2 2 8 9 10 11 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni Smls. tube Smls. tube Plate Plate SA-213 SA-213 SA-240 SA-240 TP309H TP309H 309H 309H S30909 S30909 S30909 S30909 … … … … … … … … 8 8 8 8 2 2 2 2 12 13 14 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 TP309H TP309H TP309H S30909 S30909 S30909 … … … … … … 8 8 8 2 2 2 15 16 17 18 19 20 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni Smls. pipe Smls. pipe Wld. pipe Wld. pipe Bar Bar SA-312 SA-312 SA-312 SA-312 SA-479 SA-479 TP309H TP309H TP309H TP309H 309H 309H S30909 S30909 S30909 S30909 S30909 S30909 … … … … … … … … … … … … 8 8 8 8 8 8 2 2 2 2 2 2 21 22 23 24 25 26 23Cr – 12Ni – Cb 23Cr – 12Ni – Cb 23Cr – 12Ni – Cb 23Cr – 12Ni – Cb 23Cr – 12Ni – Cb 23Cr – 12Ni – Cb Smls. tube Smls. tube Plate Plate Wld. tube Wld. tube SA-213 SA-213 SA-240 SA-240 SA-249 SA-249 TP309Cb TP309Cb 309Cb 309Cb TP309Cb TP309Cb S30940 S30940 S30940 S30940 S30940 S30940 … … … … … … … … … … … … 8 8 8 8 8 8 2 2 2 2 2 2 27 28 29 30 23Cr – 12Ni – Cb 23Cr – 12Ni – Cb 23Cr – 12Ni – Cb 23Cr – 12Ni – Cb Smls. & wld. pipe Smls. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP309Cb TP309Cb TP309Cb TP309Cb S30940 S30940 S30940 S30940 … … … … … … … … 8 8 8 8 2 2 2 2 31 32 33 34 35 36 23Cr – 12Ni – Cb 23Cr – 12Ni – Cb 23Cr – 12Ni – Cb 23Cr – 12Ni – Cb 23Cr – 12Ni – Cb 23Cr – 12Ni – Cb Bar Bar Wld. pipe Wld. pipe Wld. pipe Wld. pipe SA-479 SA-479 SA-813 SA-813 SA-814 SA-814 309Cb 309Cb TP309Cb TP309Cb TP309Cb TP309Cb S30940 S30940 S30940 S30940 S30940 S30940 … … … … … … … … … … … … 8 8 8 8 8 8 2 2 2 2 2 2 37 38 39 24Cr – 10Ni – 4Mo – N 25Cr – 4Ni – 4Mo – Ti 25Cr – 4Ni – 4Mo – Ti Castings Plate Wld. tube SA-995 SA-240 SA-268 2A … … J93345 S44635 S44635 … … … … … … 10H 10I 10I 1 1 1 40 41 42 25Cr – 5Ni – 3Mo – 2Cu 25Cr – 5Ni – 3Mo – 2Cu 25Cr – 5Ni – 3Mo – 2Cu Castings Plate Bar SA-995 SA-240 SA-479 1B … … J93372 S32550 S32550 … … … … … … 10H 10H 10H 1 1 1 Line No. (10) 130 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 515 515 515 205 205 205 NP 538 538 427 NP NP NP 538 538 NP 343 343 HA-2 HA-2 HA-2 G5, W12 G5, G12, G22, T5 G12, G22, T6 4 5 6 7 515 515 515 515 205 205 205 205 NP NP NP NP NP NP NP NP 816 816 816 816 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, G24, T5 G12, G24, T6 G5, G12, G24, T5 G12, G24, T6 8 9 10 11 515 515 515 515 205 205 205 205 816 816 816 816 NP NP NP NP 816 816 816 816 NP NP NP NP HA-2 HA-2 HA-2 HA-2 G5, T6 T7 G5, H1, T6 H1, T7 12 13 14 515 515 515 205 205 205 NP NP NP 427 NP NP NP 816 816 NP NP NP HA-2 HA-2 HA-2 G5, W12 G5, G24, T6 G24, T7 15 16 17 18 19 20 515 515 515 515 515 515 205 205 205 205 205 205 816 816 816 816 816 816 NP NP NP NP NP NP 816 816 816 816 816 816 NP NP NP NP NP NP HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, T6 T7 G3, G5, G24, T6 G3, G24, T7 G5, T6 T7 21 22 23 24 25 26 515 515 515 515 515 515 205 205 205 205 205 205 NP NP NP NP NP NP NP NP NP NP NP NP 816 816 816 816 816 816 343 343 343 343 343 343 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, G12, T5 G12, T6 G5, G12, T5 G12, T6 G5, G12, G24, T5 G12, G24, T6 27 28 29 30 515 515 515 515 205 205 205 205 NP NP NP NP 427 NP NP NP 816 816 816 816 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, T5, W12 G12, T6 G5, G12, G24, T5 G12, G24, T6 31 32 33 34 35 36 515 515 515 515 515 515 205 205 205 205 205 205 NP NP NP NP NP NP NP NP NP NP NP NP 538 538 816 816 816 816 343 343 343 343 343 343 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, G12, G22 G12, G22 G5, G12, G24, T5 G12, G24, T6 G5, G12, G13, G24, T5 G12, G24, T6 37 38 39 655 620 620 450 515 515 NP NP NP NP NP NP 316 260 260 316 260 260 HA-5 HA-5 HA-5 G1, G32 G32 G24, G32 40 41 42 690 760 760 485 550 550 NP NP NP 316 NP NP NP 260 260 NP 260 260 HA-5 HA-5 HA-5 G29, G32 G32 G32 131 (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (10) Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 138 138 138 138 138 129 138 138 120 138 138 115 138 138 111 138 138 105 135 135 100 131 131 96.7 129 129 95.4 127 127 94.1 125 125 92.9 124 124 91.6 122 122 90.4 121 121 89.2 … 119 87.9 4 5 6 7 117 117 117 117 117 110 117 110 117 101 117 101 117 97.5 117 97.5 117 94.3 117 94.3 117 88.7 117 88.7 115 84.7 115 84.7 111 82.1 111 82.1 109 80.8 109 80.8 108 79.8 108 79.8 107 79.1 107 79.1 105 77.9 105 77.9 104 77.3 104 77.3 102 76.1 102 76.1 101 74.8 101 74.8 8 9 10 11 138 138 138 138 138 129 138 129 138 119 138 119 138 114 138 114 138 111 138 111 138 105 138 105 135 100 135 100 131 96.7 131 96.7 129 95.4 129 95.4 127 94.1 127 94.1 125 92.9 125 92.9 124 91.6 124 91.6 122 90.4 122 90.4 121 89.2 121 89.2 119 87.9 119 87.9 12 13 14 138 117 117 138 117 110 138 117 101 138 117 97.5 138 117 94.3 138 117 88.7 135 115 84.7 131 111 82.1 129 109 80.8 127 108 79.8 125 107 79.1 124 105 77.9 122 104 77.3 121 102 76.1 … 101 74.8 15 16 17 18 19 20 138 138 117 117 138 138 138 129 117 110 138 129 138 119 117 101 138 119 138 114 117 97.5 138 114 138 111 117 94.3 138 111 138 105 117 88.7 138 105 135 100 115 84.7 135 100 131 96.7 111 82.1 131 96.7 129 95.4 109 80.8 129 95.4 127 94.1 108 79.8 127 94.1 125 92.9 107 79.1 125 92.9 124 91.6 105 77.9 124 91.6 122 90.4 104 77.3 122 90.4 121 89.2 102 76.1 121 89.2 119 87.9 101 74.8 119 87.9 21 22 23 24 25 26 138 138 138 138 117 117 138 129 138 129 117 110 138 120 138 120 117 101 138 115 138 115 117 97.5 138 111 138 111 117 94.3 138 105 138 105 117 88.7 135 100 135 100 115 84.7 131 96.7 131 96.7 111 82.1 129 95.4 129 95.4 109 80.8 127 94.1 127 94.1 108 79.8 125 92.9 125 92.9 107 79.1 124 91.6 124 91.6 105 77.9 122 90.4 122 90.4 104 77.3 121 89.2 121 89.2 102 76.1 119 87.9 119 87.9 101 74.8 27 28 29 30 138 138 117 117 138 129 117 110 138 120 117 101 138 115 117 97.5 138 111 117 94.3 138 105 117 88.7 135 100 115 84.7 131 96.7 111 82.1 129 95.4 109 80.8 127 94.1 108 79.8 125 92.9 107 79.1 124 91.6 105 77.9 122 90.4 104 77.3 121 89.2 102 76.1 119 87.9 101 74.8 31 32 33 34 35 36 138 138 117 117 117 117 138 129 117 110 117 110 138 120 117 101 117 101 138 115 117 97.5 117 97.5 138 111 117 94.3 117 94.3 138 105 117 88.7 117 88.7 135 100 115 84.7 115 84.7 131 96.7 111 82.1 111 82.1 129 95.4 109 80.8 109 80.8 127 94.1 108 79.8 108 79.8 125 92.9 107 79.1 107 79.1 124 91.6 105 77.9 105 77.9 122 90.4 104 77.3 104 77.3 121 89.2 102 76.1 102 76.1 119 87.9 101 74.8 101 74.8 37 38 39 187 177 151 187 175 149 186 171 145 180 166 141 173 162 137 167 156 132 167 152 129 167 … … 167 … … … … … … … … … … … … … … … … … … … … 40 41 42 197 216 216 197 216 216 197 215 215 195 209 209 192 203 203 190 198 198 190 195 195 189 … … 189 … … … … … … … … … … … … … … … … … … … … 132 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 … 115 86.7 … 89.4 78.5 … 59.2 59.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 4 5 6 7 98.9 73.5 98.9 73.5 74.7 64.8 74.7 64.8 50.6 50.6 50.6 50.6 37.4 37.4 37.4 37.4 27.5 27.5 27.5 27.5 20.4 20.4 20.4 20.4 14.2 14.2 14.2 14.2 9.27 9.27 9.27 9.27 5.22 5.22 5.22 5.22 3.23 3.23 3.23 3.23 2.53 2.53 2.53 2.53 2.06 2.06 2.06 2.06 1.52 1.52 1.52 1.52 0.960 0.960 0.960 0.960 … … … … … … … … … … … … 8 9 10 11 117 86.7 117 86.7 107 85.4 107 85.4 83.8 78.9 83.8 78.9 65.2 65.2 65.2 65.2 48.6 48.6 48.6 48.6 36.3 36.3 36.3 36.3 27.3 27.3 27.3 27.3 21.1 21.1 21.1 21.1 15.9 15.9 15.9 15.9 12.5 12.5 12.5 12.5 9.89 9.89 9.89 9.89 7.77 7.77 7.77 7.77 6.12 6.12 6.12 6.12 4.59 4.59 4.59 4.59 … … … … … … … … … … … … 12 13 14 … 99.8 73.6 … 91.3 72.3 … 71.2 66.8 … 55.8 55.7 … 41.5 41.5 … 31.0 31.0 … 23.2 23.2 … 18.2 18.2 … 13.8 13.8 … 10.4 10.4 … 8.27 8.27 … 6.50 6.50 … 5.05 5.05 … 4.01 4.01 … … … … … … … … … 15 16 17 18 19 20 117 86.7 99.8 73.6 117 86.7 107 85.4 91.3 72.3 107 85.4 83.8 78.9 71.2 66.8 83.8 78.9 65.2 65.2 55.8 55.7 65.2 65.2 48.6 48.6 41.5 41.5 48.6 48.6 36.3 36.3 31.0 31.0 36.3 36.3 27.3 27.3 23.2 23.2 27.3 27.3 21.1 21.1 18.2 18.2 21.1 21.1 15.9 15.9 13.8 13.8 15.9 15.9 12.5 12.5 10.4 10.4 12.5 12.5 9.89 9.89 8.27 8.27 9.89 9.89 7.77 7.77 6.50 6.50 7.77 7.77 6.12 6.12 5.05 5.05 6.12 6.12 4.59 4.59 4.01 4.01 4.59 4.59 … … … … … … … … … … … … … … … … … … 21 22 23 24 25 26 115 86.7 115 86.7 98.9 73.5 89.4 78.5 89.4 78.5 74.7 64.8 59.2 59.2 59.2 59.2 50.6 50.6 44.2 44.2 44.2 44.2 37.4 37.4 31.8 31.8 31.8 31.8 27.5 27.5 23.7 23.7 23.7 23.7 20.4 20.4 16.9 16.9 16.9 16.9 14.2 14.2 10.7 10.7 10.7 10.7 9.27 9.27 6.10 6.10 6.10 6.10 5.22 5.22 3.78 3.78 3.78 3.78 3.23 3.23 2.96 2.96 2.96 2.96 2.53 2.53 2.40 2.40 2.40 2.40 2.06 2.06 1.76 1.76 1.76 1.76 1.52 1.52 1.15 1.15 1.15 1.15 0.960 0.960 … … … … … … … … … … … … … … … … … … 27 28 29 30 115 86.7 98.9 73.5 89.4 78.5 74.7 64.8 59.2 59.2 50.6 50.6 44.2 44.2 37.4 37.4 31.8 31.8 27.5 27.5 23.7 23.7 20.4 20.4 16.9 16.9 14.2 14.2 10.7 10.7 9.27 9.27 6.10 6.10 5.22 5.22 3.78 3.78 3.23 3.23 2.96 2.96 2.53 2.53 2.40 2.40 2.06 2.06 1.76 1.76 1.52 1.52 1.15 1.15 0.960 0.960 … … … … … … … … … … … … 31 32 33 34 35 36 115 86.7 98.9 73.5 98.9 73.5 89.4 78.5 74.7 64.8 74.7 64.8 59.2 59.2 50.6 50.6 50.6 50.6 … … 37.4 37.4 37.4 37.4 … … 27.5 27.5 27.5 27.5 … … 20.4 20.4 20.4 20.4 … … 14.2 14.2 14.2 14.2 … … 9.27 9.27 9.27 9.27 … … 5.22 5.22 5.22 5.22 … … 3.23 3.23 3.23 3.23 … … 2.53 2.53 2.53 2.53 … … 2.06 2.06 2.06 2.06 … … 1.52 1.52 1.52 1.52 … … 0.960 0.960 0.960 0.960 … … … … … … … … … … … … … … … … … … 37 38 39 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 40 41 42 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 133 (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 25Cr – 5Ni – 3Mo – 2Cu 25Cr – 5Ni – 3Mo – 2Cu 25Cr – 5Ni – 3Mo – 2Cu 25Cr – 5Ni – 3Mo – 2Cu Smls. tube Wld. tube Smls. pipe Wld. pipe SA-789 SA-789 SA-790 SA-790 … … … … S32550 S32550 S32550 S32550 … … … … … … … … 10H 10H 10H 10H 1 1 1 1 5 6 7 8 9 10 25Cr – 6Ni – Mo – N 25Cr – 6.5Ni – 3Mo – N 25Cr – 6.5Ni – 3Mo – N 25Cr – 6.5Ni – 3Mo – N 25Cr – 6.5Ni – 3Mo – N 25Cr – 6.5Ni – 3Mo – N Plate Smls. tube Wld. tube Smls. pipe Wld. pipe Plate SA-240 SA-789 SA-789 SA-790 SA-790 SA-240 … … … … … … S31200 S31260 S31260 S31260 S31260 S31260 … … … … … … … … … … … … 10H 10H 10H 10H 10H 10H 1 1 1 1 1 1 11 12 13 14 15 25Cr – 7Ni – 3Mo – W – Cu – N 25Cr – 7Ni – 3Mo – W – Cu – N 25Cr – 7Ni – 3Mo – W – Cu – N 25Cr – 7Ni – 3Mo – W – Cu – N 25Cr – 7Ni – 3Mo – W – Cu – N Forgings Smls. tube Wld. tube Smls. pipe Wld. pipe SA-182 SA-789 SA-789 SA-790 SA-790 F54 … … … … S39274 S39274 S39274 S39274 S39274 … … … … … … … … … … 10H 10H 10H 10H 10H 1 1 1 1 1 16 17 18 19 20 21 25Cr – 7Ni – 4Mo – N 25Cr – 7Ni – 4Mo – N 25Cr – 7Ni – 4Mo – N 25Cr – 7Ni – 4Mo – N 25Cr – 7Ni – 4Mo – N 25Cr – 7Ni – 4Mo – N Forgings Plate, sheet Smls. tube Wld. tube Smls. pipe Wld. pipe SA-182 SA-240 SA-789 SA-789 SA-790 SA-790 F53 … … … … … S32750 S32750 S32750 S32750 S32750 S32750 … … … … … … … … ≤ 25 ≤ 25 ≤ 25 ≤ 25 10H 10H 10H 10H 10H 10H 1 1 1 1 1 1 22 23 24 25Cr – 12Ni 25Cr – 12Ni 25Cr – 12Ni Castings Castings Cast pipe SA-351 SA-351 SA-451 CH8 CH8 CPH8 J93400 J93400 J93400 … … … … … … 8 8 8 2 2 2 25 26 27 25Cr – 12Ni 25Cr – 12Ni 25Cr – 12Ni Castings Castings Cast pipe SA-351 SA-351 SA-451 CH20 CH20 CPH20 J93402 J93402 J93402 … … … … … … 8 8 8 2 2 2 28 29 30 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni Castings Castings Cast pipe SA-351 SA-351 SA-451 CK20 CK20 CPK20 J94202 J94202 J94202 … … … … … … 8 8 8 2 2 2 31 32 33 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni Forgings Forgings Forgings SA-182 SA-182 SA-965 F310 F310 F310 S31000 S31000 S31000 … … … > 125 ≤ 125 … 8 8 8 2 2 2 34 35 36 37 38 39 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni Smls. tube Smls. tube Plate Plate Wld. tube Wld. tube SA-213 SA-213 SA-240 SA-240 SA-249 SA-249 TP310S TP310S 310S 310S TP310S TP310S S31008 S31008 S31008 S31008 S31008 S31008 … … … … … … … … … … … … 8 8 8 8 8 8 2 2 2 2 2 2 40 41 42 43 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni Smls. & wld. pipe Smls. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP310S TP310S TP310S TP310S S31008 S31008 S31008 S31008 … … … … … … … … 8 8 8 8 2 2 2 2 Line No. 134 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 760 760 760 760 550 550 550 550 NP NP NP NP NP NP NP NP 260 260 260 260 260 260 260 260 HA-5 HA-5 HA-5 HA-5 G32 G24, G32 G32 G24, G32 5 6 7 8 9 10 690 690 690 690 690 690 450 450 450 450 450 485 NP NP NP NP NP NP NP NP NP NP NP NP 316 343 343 343 343 343 316 343 343 343 343 343 HA-5 HA-5 HA-5 HA-5 HA-5 HA-5 G32 G32 G24, G32 G32 G24, G32 G32 11 12 13 14 15 800 800 800 800 800 550 550 550 550 550 NP NP NP NP NP NP NP NP NP NP 329 329 329 329 329 329 329 329 329 329 HA-8 HA-8 HA-8 HA-8 HA-8 G32 G32 G24, G32 G32 G24, G32 16 17 18 19 20 21 800 800 800 800 800 800 550 550 550 550 550 550 NP NP NP NP NP NP NP NP NP NP NP NP 316 316 316 316 316 316 NP NP 316 316 316 316 HA-5 HA-5 HA-5 HA-5 HA-5 HA-5 G32 G32 G32 G24, G32 G32 G24, G32 22 23 24 450 450 450 195 195 195 NP NP NP 427 NP 427 816 816 NP 343 343 NP HA-3 HA-3 HA-3 G1, G5, G12, G16, G17, G32, T6 G1, G12, G32, T7 G5, G16, G17, G32 25 26 27 485 485 485 205 205 205 NP NP NP 427 NP 427 816 816 NP 343 343 NP HA-2 HA-2 HA-2 G1, G5, G12, G16, G17, T6 G1, G12, T7 G5, G16, G17 28 29 30 450 450 450 195 195 195 NP NP NP 427 NP 427 816 816 NP 343 343 NP HA-3 HA-3 HA-3 G1, G5, G12, G16, G17, T6 G1, G12, T8 G5, G16, G17 31 32 33 485 515 515 205 205 205 NP NP NP 427 427 427 NP 816 816 NP 343 343 HA-2 HA-2 HA-2 G5 G5, G12, G14, T5 G5, G12, T5 34 35 36 37 38 39 515 515 515 515 515 515 205 205 205 205 205 205 816 816 816 816 NP NP NP NP 427 NP NP NP 816 816 816 816 816 816 343 343 343 343 343 343 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, G12, T5 G12, T6 G5, G12, T5 G12, T6 G5, G12, G24, T5 G12, G24, T6 40 41 42 43 515 515 515 515 205 205 205 205 816 816 816 816 427 NP NP NP 816 816 816 816 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, T5, W12, W14 G12, T6 G3, G5, G12, G14, G24, T5 G3, G12, G14, G24, T6 135 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 216 184 216 184 216 184 216 184 215 183 215 183 209 178 209 178 203 173 203 173 198 168 198 168 195 166 195 166 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 9 10 197 197 168 197 168 197 197 197 168 197 168 197 197 196 167 196 167 196 192 192 163 192 163 192 187 187 158 187 158 187 182 182 155 182 155 182 180 181 155 181 155 181 180 181 154 181 154 181 180 181 154 181 154 181 … 181 154 181 154 181 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 15 229 229 194 229 194 229 229 194 229 194 227 227 193 227 193 221 221 188 221 188 218 218 185 218 185 216 216 184 216 184 216 216 184 216 184 216 216 184 216 184 216 216 184 216 184 216 216 184 216 184 … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 20 21 228 228 228 194 228 194 228 228 228 194 228 194 227 227 227 192 227 192 221 221 221 188 221 188 215 215 215 183 215 183 208 208 208 177 208 177 205 205 205 174 205 174 203 203 203 173 203 173 202 202 202 172 202 172 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 128 128 128 123 116 123 116 104 116 112 99.5 112 109 97.1 109 106 93.4 106 106 90.7 106 106 88.5 106 106 86.9 106 105 85.0 105 105 83.2 105 103 81.3 103 102 78.8 102 99.8 76.2 99.8 96.9 74.3 … 25 26 27 138 138 138 132 124 132 125 111 125 120 106 120 117 104 117 114 100 114 114 97.1 114 114 94.6 114 114 93.2 114 114 91.0 114 113 88.6 113 112 86.8 112 110 84.3 110 107 81.8 107 104 79.3 … 28 29 30 128 128 128 123 116 123 116 104 116 112 99.5 112 109 97.1 109 106 93.4 106 106 90.7 106 106 88.5 106 106 86.9 106 105 85.0 105 105 83.2 105 103 81.3 103 102 78.8 102 99.8 76.2 99.8 96.9 74.3 … 31 32 33 138 138 138 138 138 138 136 138 138 133 138 138 130 138 138 128 138 138 128 135 135 128 129 129 127 127 127 125 125 125 123 123 123 122 122 122 120 120 120 118 119 119 … 117 117 34 35 36 37 38 39 138 138 138 138 117 117 138 129 138 129 117 110 138 120 138 120 117 102 138 115 138 115 117 97.8 138 111 138 111 117 94.3 138 105 138 105 117 88.7 135 100 135 100 114 84.1 129 95.4 129 95.4 109 81.4 127 94.0 127 94.0 108 80.2 125 92.8 125 92.8 106 79.0 123 91.5 123 91.5 105 77.7 122 90.3 122 90.3 103 76.5 120 89.0 120 89.0 102 75.9 119 87.8 119 87.8 101 74.7 117 86.5 117 86.5 99.3 74.0 40 41 42 43 138 138 117 117 138 129 117 110 138 120 117 102 138 115 117 97.8 138 111 117 94.3 138 105 117 88.7 135 100 114 84.1 129 95.4 109 81.4 127 94.0 108 80.2 125 92.8 106 79.0 123 91.5 105 77.7 122 90.3 103 76.5 120 89.0 102 75.9 119 87.8 101 74.7 117 86.5 99.3 74.0 136 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 9 10 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 15 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 20 21 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 92.7 72.0 … 84.6 69.5 … 68.4 63.9 … 54.3 54.3 … 42.1 42.1 … 33.2 33.2 … 25.9 25.9 … 20.3 20.3 … 16.4 16.4 … 13.3 13.3 … 10.2 10.2 … 7.25 7.25 … 5.74 5.74 … 5.33 5.33 … … … … … … … … … … 25 26 27 100 76.8 … 88.5 74.3 … 68.2 68.2 … 53.7 53.7 … 42.1 42.1 … 33.2 33.2 … 25.9 25.9 … 20.3 20.3 … 16.4 16.4 … 13.3 13.3 … 10.2 10.2 … 7.25 7.25 … 5.74 5.74 … 5.33 5.33 … … … … … … … … … … 28 29 30 92.7 72.1 … 84.7 69.5 … 72.8 67.0 … 64.5 63.2 … 56.8 56.8 … 49.1 49.1 … 41.0 41.0 … 33.6 33.6 … 25.5 25.5 … 18.3 18.3 … 12.8 12.8 … 8.93 8.93 … 6.59 6.59 … 4.84 4.84 … … … … … … … … … … 31 32 33 … 112 112 … 87.2 87.2 … 59.2 59.2 … 44.2 44.2 … 31.8 31.8 … 23.7 23.7 … 16.9 16.9 … 10.7 10.7 … 6.10 6.10 … 3.78 3.78 … 2.96 2.96 … 2.40 2.40 … 1.76 1.76 … 1.15 1.15 … … … … … … … … … 34 35 36 37 38 39 112 85.3 112 85.3 98.5 72.8 87.2 77.8 87.2 77.8 74.7 64.5 59.2 59.2 59.2 59.2 50.6 50.6 44.2 44.2 44.2 44.2 37.4 37.4 31.8 31.8 31.8 31.8 27.5 27.5 23.7 23.7 23.7 23.7 20.4 20.4 16.9 16.9 16.9 16.9 14.2 14.2 10.7 10.7 10.7 10.7 9.27 9.27 6.10 6.10 6.10 6.10 5.22 5.22 3.78 3.78 3.78 3.78 3.23 3.23 2.96 2.96 2.96 2.96 2.53 2.53 2.40 2.40 2.40 2.40 2.06 2.06 1.76 1.76 1.76 1.76 1.52 1.52 1.15 1.15 1.15 1.15 0.960 0.960 … … … … … … … … … … … … … … … … … … 40 41 42 43 112 85.3 98.5 72.8 87.2 77.8 74.7 64.5 59.2 59.2 50.6 50.6 44.2 44.2 37.4 37.4 31.8 31.8 27.5 27.5 23.7 23.7 20.4 20.4 16.9 16.9 14.2 14.2 10.7 10.7 9.27 9.27 6.10 6.10 5.22 5.22 3.78 3.78 3.23 3.23 2.96 2.96 2.53 2.53 2.40 2.40 2.06 2.06 1.76 1.76 1.52 1.52 1.15 1.15 0.960 0.960 … … … … … … … … … … … … 137 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni Wld. pipe Smls. & wld. fittings Bar Bar SA-358 SA-403 SA-479 SA-479 310S 310S 310S 310S S31008 S31008 S31008 S31008 1 … … … … … … … 8 8 8 8 2 2 2 2 5 6 7 8 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni Wld. pipe Wld. pipe Wld. pipe Wld. pipe SA-813 SA-813 SA-814 SA-814 TP310S TP310S TP310S TP310S S31008 S31008 S31008 S31008 … … … … … … … … 8 8 8 8 2 2 2 2 9 10 11 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni Smls. tube Plate Plate SA-213 SA-240 SA-240 TP310H 310H 310H S31009 S31009 S31009 … … … … … … 8 8 8 2 2 2 12 13 14 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni Wld. tube Wld. tube Wld. tube SA-249 SA-249 SA-249 TP310H TP310H TP310H S31009 S31009 S31009 … … … … … … 8 8 8 2 2 2 15 16 17 18 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni Smls. pipe Smls. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP310H TP310H TP310H TP310H S31009 S31009 S31009 S31009 … … … … … … … … 8 8 8 8 2 2 2 2 19 20 21 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni Bar Bar Bar SA-479 SA-479 SA/JIS G4303 310H 310H SUS310S S31009 S31009 … … … … … … … 8 8 8 2 2 2 22 23 24 25 26 27 25Cr – 20Ni – Cb 25Cr – 20Ni – Cb 25Cr – 20Ni – Cb 25Cr – 20Ni – Cb 25Cr – 20Ni – Cb 25Cr – 20Ni – Cb Smls. tube Smls. tube Plate Plate Wld. tube Wld. tube SA-213 SA-213 SA-240 SA-240 SA-249 SA-249 TP310Cb TP310Cb 310Cb 310Cb TP310Cb TP310Cb S31040 S31040 S31040 S31040 S31040 S31040 … … … … … … … … … … … … 8 8 8 8 8 8 2 2 2 2 2 2 28 29 30 31 25Cr – 20Ni – Cb 25Cr – 20Ni – Cb 25Cr – 20Ni – Cb 25Cr – 20Ni – Cb Smls. & wld. pipe Smls. pipe Wld. pipe Wld. pipe SA-312 SA-312 SA-312 SA-312 TP310Cb TP310Cb TP310Cb TP310Cb S31040 S31040 S31040 S31040 … … … … … … … … 8 8 8 8 2 2 2 2 32 33 34 35 25Cr – 20Ni – Cb 25Cr – 20Ni – Cb 25Cr – 20Ni – Cb 25Cr – 20Ni – Cb Bar Bar Wld. pipe Wld. pipe SA-479 SA-479 SA-813 SA-813 310Cb 310Cb TP310Cb TP310Cb S31040 S31040 S31040 S31040 … … … … … … … … 8 8 8 8 2 2 2 2 36 37 38 39 25Cr – 20Ni – Cb 25Cr – 20Ni – Cb 25Cr – 20Ni – Cb – N 25Cr – 20Ni – Cb – N Wld. pipe Wld. pipe Smls. tube Smls. tube SA-814 SA-814 SA-213 SA-213 TP310Cb TP310Cb TP310HCbN TP310HCbN S31040 S31040 S31042 S31042 … … … … … … … … 8 8 8 8 2 2 3 3 Line No. (10) (10) 138 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 515 515 515 515 205 205 205 205 NP NP 538 538 427 427 NP 427 NP 816 538 538 NP 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, W12 G5, G12, T5, W12, W14 G12, G22, T6 G5, G12, G22, T5 5 6 7 8 515 515 515 515 205 205 205 205 NP NP NP NP NP NP NP NP 816 816 816 816 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, G24, T5 G12, G24, T6 G5, G12, G24, T5 G12, G24, T6 9 10 11 515 515 515 205 205 205 816 816 816 427 NP NP 816 816 816 NP NP NP HA-2 HA-2 HA-2 G5, T6 G5, T6 T7 12 13 14 515 515 515 205 205 205 NP NP NP 427 NP NP NP 816 816 NP NP NP HA-2 HA-2 HA-2 G5, W12 G5, G12, G24, T6 G12, G24, T7 15 16 17 18 515 515 515 515 205 205 205 205 816 816 816 816 NP NP NP NP 816 816 816 816 NP NP NP NP HA-2 HA-2 HA-2 HA-2 G5, T6 T7 G3, G5, G24, T6 G3, G24, T7 19 20 21 515 515 520 205 205 205 816 816 538 NP NP 427 816 816 538 NP NP NP HA-2 HA-2 HA-2 G5, T6 T7 G5, G12, G22, T5 22 23 24 25 26 27 515 515 515 515 515 515 205 205 205 205 205 205 NP NP NP NP NP NP NP NP NP NP NP NP 816 816 816 816 816 816 343 343 343 343 343 343 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5, G12, T5 G12, T6 G5, G12, T5 G12, T6 G5, G12, G24, T5 G12, G24, T6 28 29 30 31 515 515 515 515 205 205 205 205 NP NP NP NP 427 NP NP NP 816 816 816 816 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, T5, W12, W14 G12, T6 G5, G12, G24, T5 G12, G14, G24, T6 32 33 34 35 515 515 515 515 205 205 205 205 NP NP NP NP NP NP NP NP 538 538 816 816 343 343 343 343 HA-2 HA-2 HA-2 HA-2 G5, G12, G22, T5 G12, G22, T6 G5, G12, G24, T5 G12, G24, T6 36 37 38 39 515 515 655 655 205 205 295 295 NP NP 732 732 NP NP NP NP 816 816 NP NP 343 343 NP NP HA-2 HA-2 HA-2 HA-2 G5, G12, G24, T5 G12, G24, T6 G5, G12, S4, T8 G12, S4, T9 139 (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (10) (10) Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 138 138 138 138 138 138 129 138 138 138 120 138 138 138 115 138 138 138 111 138 138 138 105 138 135 135 100 135 129 129 95.4 129 127 127 94.0 127 125 125 92.8 125 123 123 91.5 123 122 122 90.3 122 120 120 89.0 120 119 119 87.8 119 … 117 86.5 117 5 6 7 8 117 117 117 117 117 110 117 110 117 102 117 102 117 97.8 117 97.8 117 94.3 117 94.3 117 88.7 117 88.7 114 84.1 114 84.1 109 81.4 109 81.4 108 80.2 108 80.2 106 79.0 106 79.0 105 77.7 105 77.7 103 76.5 103 76.5 102 75.9 102 75.9 101 74.7 101 74.7 99.3 74.0 99.3 74.0 9 10 11 138 138 138 138 138 129 138 138 120 138 138 115 138 138 111 137 137 105 134 134 99.5 129 129 95.4 127 127 94.0 125 125 92.8 123 123 91.5 122 122 90.3 120 120 89.0 119 119 87.8 117 117 86.5 12 13 14 138 117 117 138 117 110 138 117 102 138 117 97.8 138 117 94.3 138 117 88.7 135 114 84.1 129 109 81.4 127 108 80.2 125 106 79.0 123 105 77.7 122 103 76.5 120 102 75.9 119 101 74.7 … 99.6 74.0 15 16 17 18 138 138 117 117 138 129 117 110 138 120 117 102 138 115 117 97.8 138 111 117 94.3 137 105 117 88.7 134 99.5 114 84.1 129 95.4 109 81.4 127 94.0 108 80.2 125 92.8 106 79.0 123 91.5 105 77.7 122 90.3 103 76.5 120 89.0 102 75.9 119 87.8 101 74.7 117 86.5 99.6 74.0 19 20 21 138 138 138 138 129 138 138 120 138 138 115 138 138 111 138 137 105 138 134 99.5 135 129 95.4 129 127 94.0 127 125 92.8 125 123 91.5 123 122 90.3 122 120 89.0 120 119 87.8 119 117 86.5 117 22 23 24 25 26 27 138 138 138 138 117 117 138 129 138 129 117 110 138 120 138 120 117 102 138 115 138 115 117 97.8 138 111 138 111 117 94.3 138 105 138 105 117 88.7 135 100 135 100 114 84.1 129 95.4 129 95.4 109 81.4 127 94.0 127 94.0 108 80.2 125 92.8 125 92.8 106 79.0 123 91.5 123 91.5 105 77.7 122 90.3 122 90.3 103 76.5 120 89.0 120 89.0 102 75.9 119 87.8 119 87.8 101 74.7 117 86.5 117 86.5 99.3 74.0 28 29 30 31 138 138 117 117 138 129 117 110 138 120 117 102 138 115 117 97.8 138 111 117 94.3 138 105 117 88.7 135 100 114 84.1 129 95.4 109 81.4 127 94.0 108 80.2 125 92.8 106 79.0 123 91.5 105 77.7 122 90.3 103 76.5 120 89.0 102 75.9 119 87.8 101 74.7 117 86.5 99.3 74.0 32 33 34 35 138 138 117 117 138 129 117 110 138 120 117 102 138 115 117 97.8 138 111 117 94.3 138 105 117 88.7 135 100 114 84.1 129 95.4 109 81.4 127 94.0 108 80.2 125 92.8 106 79.0 123 91.5 105 77.7 122 90.3 103 76.5 120 89.0 102 75.9 119 87.8 101 74.7 117 86.5 99.3 74.0 36 37 38 39 117 117 187 187 117 110 187 177 117 102 184 163 117 97.8 179 156 117 94.3 175 149 117 88.7 170 140 114 84.1 167 133 109 81.4 165 129 108 80.2 165 127 106 79.0 165 126 105 77.7 164 124 103 76.5 164 123 102 75.9 163 121 101 74.7 162 120 99.3 74.0 160 119 140 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 … 112 85.3 112 … 87.2 77.8 87.2 … 59.2 59.2 59.2 … 44.2 … … … 31.8 … … … 23.7 … … … 16.9 … … … 10.7 … … … 6.10 … … … 3.78 … … … 2.96 … … … 2.40 … … … 1.76 … … … 1.15 … … … … … … … … … … … … … … 5 6 7 8 98.5 72.8 98.5 72.8 74.7 64.5 74.7 64.5 50.6 50.6 50.6 50.6 37.4 37.4 37.4 37.4 27.5 27.5 27.5 27.5 20.4 20.4 20.4 20.4 14.2 14.2 14.2 14.2 9.27 9.27 9.27 9.27 5.22 5.22 5.22 5.22 3.23 3.23 3.23 3.23 2.53 2.53 2.53 2.53 2.06 2.06 2.06 2.06 1.52 1.52 1.52 1.52 0.960 0.960 0.960 0.960 … … … … … … … … … … … … 9 10 11 116 116 85.3 104 104 84.0 84.7 84.7 79.8 64.7 64.7 64.7 48.6 48.6 48.6 36.2 36.2 36.2 27.3 27.3 27.3 21.1 21.1 21.1 15.9 15.9 15.9 12.5 12.5 12.5 9.92 9.92 9.92 7.64 7.64 7.64 5.97 5.97 5.97 4.67 4.67 4.67 … … … … … … … … … 12 13 14 … 98.4 72.9 … 90.6 71.6 … 71.3 66.5 … 55.7 55.8 … 41.5 41.5 … 31.0 31.0 … 23.2 23.2 … 18.2 18.2 … 13.8 13.8 … 10.4 10.4 … 8.27 8.27 … 6.50 6.50 … 5.05 5.05 … 4.01 4.01 … … … … … … … … … 15 16 17 18 116 85.3 98.4 72.9 104 84.0 90.6 71.6 84.7 79.8 71.3 66.5 64.7 64.7 55.7 55.8 48.6 48.6 41.5 41.5 36.2 36.2 31.0 31.0 27.3 27.3 23.2 23.2 21.1 21.1 18.2 18.2 15.9 15.9 13.8 13.8 12.5 12.5 10.4 10.4 9.92 9.92 8.27 8.27 7.64 7.64 6.50 6.50 5.97 5.97 5.05 5.05 4.67 4.67 4.01 4.01 … … … … … … … … … … … … 19 20 21 116 85.3 112 104 84.0 87.2 84.7 79.8 59.2 64.7 64.7 … 48.6 48.6 … 36.2 36.2 … 27.3 27.3 … 21.1 21.1 … 15.9 15.9 … 12.5 12.5 … 9.92 9.92 … 7.64 7.64 … 5.97 5.97 … 4.67 4.67 … … … … … … … … … … 22 23 24 25 26 27 112 85.3 112 85.3 98.5 72.8 87.2 77.8 87.2 77.8 74.7 64.5 59.2 59.2 59.2 59.2 50.6 50.6 44.2 44.2 44.2 44.2 37.4 37.4 31.8 31.8 31.8 31.8 27.5 27.5 23.7 23.7 23.7 23.7 20.4 20.4 16.9 16.9 16.9 16.9 14.2 14.2 10.7 10.7 10.7 10.7 9.27 9.27 6.10 6.10 6.10 6.10 5.22 5.22 3.78 3.78 3.78 3.78 3.23 3.23 2.96 2.96 2.96 2.96 2.53 2.53 2.40 2.40 2.40 2.40 2.06 2.06 1.76 1.76 1.76 1.76 1.52 1.52 1.15 1.15 1.15 1.15 0.960 0.960 … … … … … … … … … … … … … … … … … … 28 29 30 31 112 85.3 98.5 72.8 87.2 77.8 74.7 64.5 59.2 59.2 50.6 50.6 44.2 44.2 37.4 37.4 31.8 31.8 27.5 27.5 23.7 23.7 20.4 20.4 16.9 16.9 14.2 14.2 10.7 10.7 9.27 9.27 6.10 6.10 5.22 5.22 3.78 3.78 3.23 3.23 2.96 2.96 2.53 2.53 2.40 2.40 2.06 2.06 1.76 1.76 1.52 1.52 1.15 1.15 0.960 0.960 … … … … … … … … … … … … 32 33 34 35 112 85.3 98.5 72.8 87.2 77.8 74.7 64.5 59.2 59.2 50.6 50.6 … … 37.4 37.4 … … 27.5 27.5 … … 20.4 20.4 … … 14.2 14.2 … … 9.27 9.27 … … 5.22 5.22 … … 3.23 3.23 … … 2.53 2.53 … … 2.06 2.06 … … 1.52 1.52 … … 0.960 0.960 … … … … … … … … … … … … 36 37 38 39 98.5 72.8 158 117 74.7 64.5 156 115 50.6 50.6 153 114 37.4 37.4 150 112 27.5 27.5 118 110 20.4 20.4 90.2 90.2 14.2 14.2 68.9 68.9 9.27 9.27 52.9 52.9 5.22 5.22 41.1 41.1 3.23 3.23 32.2 32.2 2.53 2.53 25.2 25.2 2.06 2.06 … … 1.52 1.52 … … 0.960 0.960 … … … … … … … … … … … … … … 141 (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Nominal Composition Product Form Spec No. Type/Grade Alloy Class/ Designation/ Condition/ Group UNS No. Temper Size/Thickness, mm P-No. No. 1 2 3 4 5 6 25Cr – 22Ni – 2Mo – N 25Cr – 22Ni – 2Mo – N 25Cr – 22Ni – 2Mo – N 25Cr – 22Ni – 2Mo – N 25Cr – 22Ni – 2Mo – N 25Cr – 22Ni – 2Mo – N Forgings Forgings Smls. tube Smls. tube Wld. tube Wld. tube SA-182 SA-182 SA-213 SA-213 SA-249 SA-249 F310MoLN F310MoLN TP310MoLN TP310MoLN TP310MoLN TP310MoLN S31050 S31050 S31050 S31050 S31050 S31050 … … … … … … … … 6 < t ≤ 32 6 < t ≤ 32 6 < t ≤ 32 6 < t ≤ 32 8 8 8 8 8 8 2 2 2 2 2 2 7 8 9 10 25Cr – 22Ni – 2Mo – N 25Cr – 22Ni – 2Mo – N 25Cr – 22Ni – 2Mo – N 25Cr – 22Ni – 2Mo – N Wld. pipe Wld. pipe Plate Plate SA-312 SA-312 SA-240 SA-240 TP310MoLN TP310MoLN 310MoLN 310MoLN S31050 S31050 S31050 S31050 … … … … 6 < t ≤ 32 6 < t ≤ 32 … … 8 8 8 8 2 2 2 2 11 12 13 14 15 16 25Cr – 22Ni – 2Mo – N 25Cr – 22Ni – 2Mo – N 25Cr – 22Ni – 2Mo – N 25Cr – 22Ni – 2Mo – N 25Cr – 22Ni – 2Mo – N 25Cr – 22Ni – 2Mo – N Smls. tube Smls. tube Wld. tube Wld. tube Wld. pipe Wld. pipe SA-213 SA-213 SA-249 SA-249 SA-312 SA-312 TP310MoLN TP310MoLN TP310MoLN TP310MoLN TP310MoLN TP310MoLN S31050 S31050 S31050 S31050 S31050 S31050 … … … … … … ≤ 6, wall ≤ 6, wall ≤ 6, wall ≤ 6, wall ≤ 6, wall ≤ 6, wall 8 8 8 8 8 8 2 2 2 2 2 2 (10) (10) (10) (10) (10) 17 18 19 20 21 26Cr – 4Ni – Mo 26Cr – 4Ni – Mo 26Cr – 4Ni – Mo 26Cr – 4Ni – Mo 26Cr – 4Ni – Mo Plate Wld. tube Smls. tube Wld. pipe Smls. pipe SA-240 SA-789 SA-789 SA-790 SA-790 329 … … … … S32900 S32900 S32900 S32900 S32900 … … … … … … … … … … 10H 10H 10H 10H 10H 1 1 1 1 1 (10) (10) (10) (10) (10) 22 23 24 25 26 26Cr – 4Ni – Mo – N 26Cr – 4Ni – Mo – N 26Cr – 4Ni – Mo – N 26Cr – 4Ni – Mo – N 26Cr – 4Ni – Mo – N Plate Wld. tube Smls. tube Wld. pipe Smls. pipe SA-240 SA-789 SA-789 SA-790 SA-790 … … … … … S32950 S32950 S32950 S32950 S32950 … … … … … … … … … … 10H 10H 10H 10H 10H 1 1 1 1 1 27 28 29 30 29Cr – 6.5Ni – 2Mo – N 29Cr – 6.5Ni – 2Mo – N 29Cr – 6.5Ni – 2Mo – N 29Cr – 6.5Ni – 2Mo – N Plate, sheet, strip Bar Smls. tube Smls. pipe SA-240 SA-479 SA-789 SA-790 … … … … S32906 S32906 S32906 S32906 … … … … ≥ 10 … ≥ 10 ≥ 10 10H 10H 10H 10H 1 1 1 1 31 32 33 29Cr – 6.5Ni – 2Mo – N 29Cr – 6.5Ni – 2Mo – N 29Cr – 6.5Ni – 2Mo – N Plate, sheet, strip Smls. tube Smls. pipe SA-240 SA-789 SA-790 … … … S32906 S32906 S32906 … … … < 10 < 10 < 10 10H 10H 10H 1 1 1 142 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 6 540 540 540 540 540 540 255 255 255 255 255 255 NP NP NP NP NP NP NP NP NP NP NP NP 316 316 482 482 482 482 316 316 343 343 343 343 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5 … G5 … G5, G24 G24 7 8 9 10 540 540 550 550 255 255 240 240 NP NP NP NP NP NP NP NP 482 482 316 316 343 343 316 316 HA-2 HA-2 HA-2 HA-2 G5, G24 G24 G5 … 11 12 13 14 15 16 580 580 580 580 580 580 270 270 270 270 270 270 NP NP NP NP NP NP NP NP NP NP NP NP 482 482 482 482 482 482 343 343 343 343 343 343 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G5 … G5, G24 G24 G5, G24 G24 17 18 19 20 21 620 620 620 620 620 485 485 485 485 485 NP NP NP NP NP NP NP NP NP NP 260 260 260 260 260 260 260 260 260 260 HA-5 HA-5 HA-5 HA-5 HA-5 G32 G24, G32 G32 G24, G32 G32 (10) (10) (10) (10) (10) 22 23 24 25 26 690 690 690 690 690 485 485 485 485 485 NP NP NP NP NP NP NP NP NP NP 316 316 316 316 316 316 316 316 316 316 HA-5 HA-5 HA-5 HA-5 HA-5 G32 G24, G32 G32 G24, G32 G32 (10) (10) (10) (10) (10) 27 28 29 30 750 750 750 750 550 550 550 550 NP NP NP NP NP NP NP NP 316 316 316 316 316 316 316 316 HA-5 HA-5 HA-5 HA-5 G32 G32 G32 G32 31 32 33 800 800 800 650 650 650 NP NP NP NP NP NP 316 316 316 316 316 316 HA-5 HA-5 HA-5 G32 G32 G32 143 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 1 2 3 4 5 6 154 154 154 154 130 130 153 150 153 150 130 127 151 143 151 143 128 121 147 137 147 137 125 116 143 131 143 131 122 111 138 123 138 123 118 105 135 117 135 117 114 99.6 132 111 132 111 112 94.5 130 109 130 109 111 92.3 … … 129 106 110 90.6 … … 129 104 110 88.6 … … 128 102 109 86.1 … … 127 99.5 108 84.2 … … 126 96.9 107 82.3 … … 124 95.0 105 81.0 7 8 9 10 130 130 158 158 130 127 158 147 128 121 155 135 125 116 151 129 122 111 147 125 118 105 142 116 114 99.6 138 111 112 94.5 135 106 111 92.3 134 103 110 90.6 … … 110 88.6 … … 109 86.1 … … 108 84.2 … … 107 82.3 … … 105 81.0 … … 11 12 13 14 15 16 165 165 141 141 141 141 165 159 141 135 141 135 163 151 139 128 139 128 158 144 135 123 135 123 154 138 132 118 132 118 149 130 126 110 126 110 146 123 123 104 123 104 142 117 121 100 121 100 141 115 120 97.6 120 97.6 140 112 119 95.3 119 95.3 138 110 118 93.4 118 93.4 138 107 117 90.9 117 90.9 137 105 116 89.1 116 89.1 135 102 115 87.2 115 87.2 134 100 113 85.3 113 85.3 (10) (10) (10) (10) (10) 17 18 19 20 21 177 151 177 151 177 177 151 177 151 177 177 151 177 151 177 174 148 174 148 174 171 145 171 145 171 168 142 168 142 168 168 142 168 142 168 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) 22 23 24 25 26 197 168 197 168 197 197 167 197 167 197 196 166 196 166 196 191 163 191 163 191 186 158 186 158 186 182 155 182 155 182 182 155 182 155 182 182 155 182 155 182 182 155 182 155 182 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 27 28 29 30 215 215 215 215 215 215 215 215 213 213 213 213 208 208 208 208 204 204 204 204 198 198 198 198 196 196 196 196 195 195 195 195 195 195 195 195 … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 229 229 229 229 229 229 227 227 227 221 221 221 217 217 217 211 211 211 208 208 208 207 207 207 207 207 207 … … … … … … … … … … … … … … … … … … 144 2011a SECTION II, PART D (METRIC) TABLE 1A (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR FERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 6 … … 122 93.1 103 79.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 10 103 79.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 15 16 132 98.7 112 83.5 112 83.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 17 18 19 20 21 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) 22 23 24 25 26 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) 27 28 29 30 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 145 2011a SECTION II, PART D (METRIC) NOTES TO TABLE 1A GENERAL NOTES (a) The following abbreviations are used: Norm. rld., Normalized rolled; Smls., Seamless; and Wld., Welded. (b) The stress values in this Table may be interpolated to determine values for intermediate temperatures. The values at intermediate temperatures shall be rounded to the same number of decimal places as the value at the higher temperature between which values are being interpolated. The rounding rule is: when the next digit beyond the last place to be retained is less than 5, retain unchanged the digit in the last place retained; when the digit next beyond the last place to be retained is 5 or greater, increase by 1 the digit in the last place retained. (c) For Section VIII and XII applications, stress values in restricted shear such as dowel bolts or similar construction in which the shearing member is so restricted that the section under consideration would fail without reduction of area shall be 0.80 times the values in the above Table. (d) For Section VIII and XII applications, stress values in bearing shall be 1.60 times the values in the above Table. (e) Stress values for −30°C to 40°C are applicable for colder temperatures when the toughness requirements of Section III, VIII, or XII are met. (f) An alternative typeface is used for stress values obtained from time-dependent properties (see Notes T1 through T11). (g) Where specifications, grades, classes, and types are listed in this Table, and where the material specification in Section II, Part A or Part B is a dual-unit specification (e.g., SA-516/SA-516M), the values listed in this Table shall be applicable to either the customary U.S. version of the material specification or the SI units version of the material specification. For example, the values listed for SA-516 Grade 70 shall be used when SA-516M Grade 485 is used in construction. (10) (h) The properties of steels are influenced by the processing history, heat treatment, melting practice, and level of residual elements. See Nonmandatory Appendix A for more information. NOTES — GENERAL REQUIREMENTS G1 To these stress values a casting quality factor as specified in PG-25 of Section I, UG-24 of Section VIII, Division 1, or TM-190 of Section XII shall be applied. G2 These stress values include a joint efficiency factor of 0.60. G3 These stress values include a joint efficiency factor of 0.85. G4 For Section I applications, these stresses apply when used for boiler, water wall, superheater, and economizer tubes that are enclosed within a setting. A joint efficiency factor of 0.85 is included in values above 450°C. G5 Due to the relatively low yield strength of these materials, these higher stress values were established at temperatures where the shorttime tensile properties govern to permit the use of these alloys where slightly greater deformation is acceptable. The stress values in this range exceed 662⁄3% but do not exceed 90% of the yield strength at temperature. Use of these stresses may result in dimensional changes due to permanent strain. These stress values are not recommended for the flanges of gasketed joints or other applications where slight amounts of distortion can cause leakage or malfunction. For Section III applications, Table Y-2 lists multiplying factors that, when applied to the yield strength values shown in Table Y-1, will give allowable stress values that will result in lower levels of permanent strain. G6 Creep-fatigue, thermal ratcheting, and environmental effects are increasingly significant failure modes at temperatures in excess of 825°C and shall be considered in the design. (10) G7 DELETED. (10) G8 DELETED. G9 For Section III applications, the use of these materials shall be limited to materials for tanks covered in Subsections NC and ND, component supports, and for nonpressure-retaining attachments (NC/ND-2190). G10 Upon prolonged exposure to temperatures above 425°C, the carbide phase of carbon steel may be converted to graphite. See Appendix A, A-240. G11 Upon prolonged exposure to temperatures above 475°C, the carbide phase of carbon'molybdenum steel may be converted to graphite. See Appendix A, A-240. G12 At temperatures above 550°C, these stress values apply only when the carbon is 0.04% or higher on heat analysis. G13 These stress values at 575°C and above shall be used only when the grain size is ASTM No. 6 or coarser. G14 These stress values shall be used when the grain size is not determined or is determined to be finer than ASTM No. 6. G15 For Section I applications, use is limited to stays as defined in PG-13 except as permitted by PG-11. G16 For Section III Class 3 applications, these S values do not include a casting quality factor. Statically and centrifugally cast products meeting the requirements of NC-2570 shall receive a casting quality factor of 1.00. G17 For Section III Class 3 applications, statically and centrifugally cast products meeting the requirements of NC-2571(a) and (b), and cast pipe fittings, pumps, and valves with inlet piping connections of DN 50 and less, shall receive a casting quality factor of 1.00. Other casting quality factors shall be in accordance with the following: (a) for visual examination, 0.80 (b) for magnetic particle examination, 0.85 (c) for liquid penetrant examination, 0.85 (d) for radiography, 1.00 (e) for ultrasonic examination, 1.00 (f) for magnetic particle or liquid penetrant plus ultrasonic examination or radiography, 1.00 G18 See Table Y-1 for yield strength values as a function of thickness over this range. Allowable stresses are independent of yield strength in this thickness range. (a) G19 DELETED. (a) G20 DELETED. (a) G21 DELETED. G22 For Section I applications, use of external pressure charts for material in the form of bar stock is permitted for stiffening rings only. G23 For temperatures above the maximum temperature shown on the external pressure chart for this material, Fig. CS-2 may be used for the design using this material. G24 A factor of 0.85 has been applied in arriving at the maximum allowable stress values in tension for this material. Divide tabulated values by 0.85 for maximum allowable longitudinal tensile stress. 146 2011a SECTION II, PART D (METRIC) NOTES TO TABLE 1A (CONT’D) NOTES — GENERAL REQUIREMENTS (CONT’D) G25 For Section III applications, for both Class 2 and Class 3, the completed vessel after final heat treatment shall be examined by the ultrasonic method in accordance with NB-2542 except that angle beam examination in both the circumferential and the axial directions may be performed in lieu of the straight beam examination in the axial direction. The tensile strength shall not exceed 860 MPa. G26 Material that conforms to Class 10, 11, or 12 is not permitted. G27 Material that conforms to Class 11 or 12 is not permitted. G28 Supplementary Requirement S15 of SA-781, Alternate Mechanical Test Coupons and Specimen Locations for Castings, is mandatory. G29 For Section III applications, impact testing in accordance with the requirements of NC-2300 is required for Class 2 components and in accordance with ND-2300 for Class 3 components. G30 For Section VIII applications, these stress values are based on expected minimum values of 310 MPa tensile strength and yield strength of 140 MPa resulting from loss of strength due to thermal treatment required for the glass coating operation. UG-85 does not apply. G31 These stress values are established from a consideration of strength only and will be satisfactory for average service. For bolted joints where freedom from leakage over a long period of time without retightening is required, lower stress values may be necessary as determined from the flexibility of the flange and bolts and corresponding relaxation properties. G32 This steel may be expected to develop embrittlement after service at moderately elevated temperature. See Appendix A, A-340 and A-360. G33 These stresses are based on weld metal properties. G34 For Section I, use is limited to PEB-5.3. See PG-5.5 for cautionary note. (10) G35 DELETED. NOTES — HEAT TREATMENT REQUIREMENTS H1 For temperatures above 550°C, these stress values may be used only if the material is heat treated by heating to the minimum temperature specified in the material specification, but not lower than 1040°C, and quenching in water or rapidly cooling by other means. H2 For temperatures above 550°C, these stress values may be used only if the material is heat treated by heating to a minimum temperature of 1095°C, and quenching in water or rapidly cooling by other means. (10) H3 DELETED. (10) H4 DELETED. H5 For Section III applications, if heat treatment is performed after forming or fabrication, it shall be performed at 825°C to 1000°C for a period of time not to exceed 10 min at temperature, followed by rapid cooling. NOTES — SIZE REQUIREMENTS S1 For Section I applications, stress values at temperatures of 450°C and above are permissible but, except for tubular products 75 mm O.D. or less enclosed within the boiler setting, use of these materials at these temperatures is not current practice. S2 For Section I applications, stress values at temperatures of 475°C and above are permissible but, except for tubular products 75 mm O.D. or less enclosed within the boiler setting, use of these materials at these temperatures is not current practice. S3 For Section I applications, stress values at temperatures of 550°C and above are permissible but, except for tubular products 75 mm O.D. or less enclosed within the boiler setting, use of these materials at these temperatures is not current practice. S4 For Section I applications, stress values at temperatures of 625°C and above are permissible but, except for tubular products 75 mm O.D. or less enclosed within the boiler setting, use of these materials at these temperatures is not current practice. S5 Material that conforms to Class 10, 11, or 12 is not permitted when the nominal thickness of the material exceeds 19 mm. S6 Material that conforms to Class 10, 11, or 12 is not permitted when the nominal thickness of the material exceeds 32 mm. S7 The maximum thickness of unheat-treated forgings shall not exceed 95 mm. The maximum thickness as-heat-treated may be 100 mm. S8 The maximum section thickness shall not exceed 75 mm for double-normalized-and-tempered forgings, or 125 mm for quenched-andtempered forgings. S9 Both DN 200 and larger, and schedule 140 and heavier. S10 The maximum pipe size shall be NPS 4 (DN 100) and the maximum thickness in any pipe size shall be Schedule 80. (10) NOTES — TIME-DEPENDENT PROPERTIES T1 Allowable stresses for temperatures of 370°C T2 Allowable stresses for temperatures of 400°C T3 Allowable stresses for temperatures of 455°C T4 Allowable stresses for temperatures of 480°C T5 Allowable stresses for temperatures of 510°C T6 Allowable stresses for temperatures of 540°C T7 Allowable stresses for temperatures of 565°C T8 Allowable stresses for temperatures of 595°C T9 Allowable stresses for temperatures of 620°C T10 Allowable stresses for temperatures of 425°C (10) T11 DELETED. and and and and and and and and and and above above above above above above above above above above are are are are are are are are are are values values values values values values values values values values obtained obtained obtained obtained obtained obtained obtained obtained obtained obtained from from from from from from from from from from time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent properties. properties. properties. properties. properties. properties. properties. properties. properties. properties. NOTES — WELDING REQUIREMENTS W1 Not for welded construction. W2 Not for welded construction in Section III. W3 Welded. W4 Nonwelded, or welded if the tensile strength of the Section IX reduced section tension test is not less than 690 MPa. W5 Welded, with the tensile strength of the Section IX reduced tension test less than 690 MPa but not less than 655 MPa. W6 This material may be welded by the resistance technique. W7 In welded construction for temperatures above 450°C, the weld metal shall have a carbon content of greater than 0.05%. W8 Welding and oxygen or other thermal cutting processes are not permitted when carbon content exceeds 0.35% by heat analysis. 147 2011a SECTION II, PART D (METRIC) NOTES TO TABLE 1A (CONT’D) NOTES — WELDING REQUIREMENTS (CONT’D) W9 For Section I applications, for pressure retaining welds in 21⁄4Cr–1Mo materials, other than circumferential butt welds less than or equal to 89 mm in outside diameter, when the design metal temperatures exceed 450°C, the weld metal shall have a carbon content greater than 0.05%. W10 For Section III applications, material that conforms to Class 10, 13, 20, 23, 30, 33, 40, 43, 50, or 53 is not permitted for Class 2 and Class 3 construction when a weld efficiency factor of 1.00 is used in accordance with Note W12. W11 For Section VIII applications, Section IX, QW-250 Variables QW-404.12, QW-406.3, QW-407.2, and QW-409.1 shall also apply to this material. These variables shall be applied in accordance with the rules for welding of Part UF. W12 These S values do not include a longitudinal weld efficiency factor. For Section III applications, for materials welded without filler metal, ultrasonic examination, radiographic examination, or eddy current examination, in accordance with NC-2550, shall provide a longitudinal weld efficiency factor of 1.00. Materials welded with filler metal meeting the requirements of NC-2560 shall receive a longitudinal weld efficiency factor of 1.00. Other longitudinal weld efficiency factors shall be in accordance with the following: (a) for single butt weld, with filler metal, 0.80 (b) for single or double butt weld, without filler metal, 0.85 (c) for double butt weld, with filler metal, 0.90 (d) for single or double butt weld, with radiography, 1.00 W13 For Section I applications, electric resistance and autogenous welded tubing may be used with these stresses, provided the following additional restrictions and requirements are met: (a) The tubing shall be used for boiler, waterwall, superheater, and economizer tubes that are enclosed within the setting. (b) The maximum outside diameter shall be 89 mm. (c) The weld seam of each tube shall be subjected to an angle beam ultrasonic inspection per SA-450. (d) A complete volumetric inspection of the entire length of each tube shall be performed in accordance with SA-450. (e) Material test reports shall be supplied. W14 These S values do not include a weld factor. For Section VIII, Division 1, and Section XII applications using welds made without filler metal, the tabulated tensile stress values shall be multiplied by 0.85. For welds made with filler metal, consult UW-12 for Section VIII, Division 1, or TW-130.4 for Section XII, as applicable. W15 The Nondestructive Electric Test requirements of SA-53 Type E pipe are required for all sizes. The pipe shall be additionally marked "NDE" and so noted on the material specification. 148 INTENTIONALLY LEFT BLANK 149 2011a SECTION II, PART D (METRIC) TABLE 1B SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 5 … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … Alclad 3003 Alclad 3003 Alclad 3003 Alclad 3003 Alclad 3003 O O H112 H112 H112 6 7 8 9 … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 … … … … Alclad 3003 Alclad 3003 Alclad 3003 Alclad 3003 H12 H12 H14 H14 10 11 12 13 … … … … Drawn smls. tube Drawn smls. tube Drawn smls. tube Drawn smls. tube SB-210 SB-210 SB-210 SB-210 … … … … Alclad 3003 Alclad 3003 Alclad 3003 Alclad 3003 O H113 H14 H18 14 15 16 17 … … … … Cond. & heat exch. tubes Cond. & heat exch. tubes Smls. extr. tube Smls. extr. tube SB-234 SB-234 SB-241 SB-241 … … … … Alclad 3003 Alclad 3003 Alclad 3003 Alclad 3003 H14 H25 O H112 18 19 20 21 … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 … … … … Alclad 3004 Alclad 3004 Alclad 3004 Alclad 3004 O O H112 H112 22 23 24 25 … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 … … … … Alclad 3004 Alclad 3004 Alclad 3004 Alclad 3004 H32 H32 H34 H34 26 27 28 29 30 … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … Alclad 6061 Alclad 6061 Alclad 6061 Alclad 6061 Alclad 6061 T4 T451 T451 T4 wld. T451 wld. 31 32 33 34 35 36 … … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … … Alclad 6061 Alclad 6061 Alclad 6061 Alclad 6061 Alclad 6061 Alclad 6061 T6 T651 T651 T651 T6 wld. T651 wld. 37 38 39 40 41 42 … … … … … … Castings Castings Castings Castings Castings Castings SB-26 SB-108 SB-26 SB-26 SB-108 SB-26 … … … … … … A02040 A02040 A03560 A03560 A03560 A24430 T4 T4 T71 T6 T6 F Line No. 150 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 0.15 – 12.69 12.70 – 76.20 6.35 – 12.69 12.70 – 50.80 50.81 – 76.2 21 21 21 21 21 90 97 110 100 100 31 34 62 41 41 NP NP NP NP NP 121 (Cl. 3 only) 121 (Cl. 3 only) 149 (Cl. 3 only) 93 (Cl. 3 only) 93 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 NFA-7 NFA-7 NFA-7 NFA-7 NFA-7 G16 G25 G16, W3 G26, W3 G26, W3 6 7 8 9 0.43 – 12.69 12.70 – 50.80 0.23 – 12.69 12.70 – 25.40 21 21 21 21 110 120 130 140 76 83 110 120 NP NP NP NP 149 (Cl. 3 only) 149 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-7 NFA-7 NFA-7 NFA-7 G16, W3 G25, W3 G16, W3 G25, W3 10 11 12 13 0.25 – 12.7 1.27 – 12.7 0.25 – 12.7 0.25 – 12.7 21 21 21 21 90 90 130 180 31 31 110 160 NP NP NP NP 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-7 NFA-7 NFA-1 NFA-1 G16 G16, W3 G16, W3 G16, W3 14 15 16 17 0.25 – 5.08 0.25 – 5.08 … … 21 21 21 21 130 145 90 90 110 125 31 31 NP NP NP NP 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-1 NFA-1 NFA-7 NFA-7 G16, W4 G16, W4 G16 G16, W3 18 19 20 21 1.30 – 12.69 12.70 – 76.20 6.35 – 12.69 12.70 – 76.20 22 22 22 22 145 150 150 160 55 59 59 62 NP NP NP NP 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-7 NFA-7 NFA-7 NFA-7 G16 G25 G16, W3 G25, W3 22 23 24 25 1.30 – 12.69 12.70 – 50.80 1.30 – 12.69 12.70 – 25.40 22 22 22 22 185 195 210 220 140 145 165 170 NP NP NP NP 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-7 NFA-7 NFA-7 NFA-7 G16, W3 G25, W3 G16, W3 G25, W3 26 27 28 29 30 1.30 – 6.34 6.35 – 12.69 12.70 – 76.20 1.30 – 6.34 6.35 – 76.2 23 23 23 23 23 185 185 205 165 165 97 97 110 … … NP NP NP NP NP 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 NFA-12 NFA-12 NFA-12 NFA-12 NFA-12 G16, G24, W4 G16, G24, W4 G24, G25, W4 G24, W7 G24, W7 31 32 33 34 35 36 1.30 – 6.34 6.35 – 12.69 12.70 – 101.60 101.61 – 127 1.30 – 6.34 6.35 – 127 23 23 23 23 23 23 260 260 290 275 165 165 220 220 240 240 … … NP NP NP NP NP NP 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 204 204 NFA-12 NFA-12 NFA-12 NFA-12 NFA-12 NFA-12 G16, G24, W4 G16, G24, W4 G24, G25, W4 G24, G26, W4 G24, W7 G24, W7 37 38 39 40 41 42 ≤ 50.8 ≤ 50.8 … … … … … … … … … … 310 330 170 205 230 120 195 200 125 140 150 41 NP NP NP NP NP NP NP NP 177 (Cl. 3 only) 121 (Cl. 3 only) NP 204 (Cl. 3 only) 66 66 204 121 121 204 66 66 204 121 121 204 NFA-12 NFA-12 NFA-1 NFA-12 NFA-12 NFA-1 G15, W4 G15, W4 G15, W4 G15, W4 G15, W4 G15, W4 151 2011a SECTION II, PART D (METRIC) TABLE 1B SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 5 20.7 20.7 29.6 26.9 26.2 20.7 20.7 29.6 26.9 26.2 20.2 20.2 29.2 26.1 24.7 18.3 18.3 25.7 19.7 19.2 15.0 15.0 22.6 15.0 15.0 11.2 11.2 18.9 11.2 11.2 9.24 9.24 15.1 9.24 9.24 7.47 7.47 11.4 7.47 7.47 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 29.6 29.6 35.2 35.2 29.6 29.6 35.2 35.2 29.2 29.2 34.6 34.6 25.7 25.7 30.5 30.5 22.6 22.6 26.6 26.6 18.9 18.9 19.0 19.0 15.1 15.1 15.0 15.0 11.4 11.4 11.5 11.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 20.7 20.7 35.2 48.3 20.7 20.7 35.2 48.3 20.2 20.2 34.6 46.5 18.3 18.3 30.5 39.0 15.0 15.0 26.6 32.7 11.2 11.2 19.0 22.6 9.24 9.24 15.0 16.7 7.47 7.47 11.5 11.4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 17 35.2 39.3 20.7 20.7 35.2 39.3 20.7 20.7 34.6 38.5 20.4 20.4 30.5 32.2 18.2 18.2 26.6 26.6 15.0 15.0 19.0 19.0 11.2 11.2 15.0 15.0 8.67 8.67 11.5 11.5 6.26 6.26 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 18 19 20 21 34.5 34.5 35.9 40.7 34.5 34.5 35.9 40.7 34.5 34.5 35.9 40.1 34.3 34.3 35.6 35.9 30.8 30.8 31.4 31.5 24.0 24.0 24.0 24.0 15.9 15.9 15.9 15.9 7.84 7.84 7.85 7.85 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 25 49.6 49.6 56.5 56.5 49.6 49.6 56.5 56.5 48.7 48.7 55.2 55.2 41.8 41.8 44.6 44.6 35.5 35.5 35.4 35.4 24.1 24.1 24.1 24.1 15.8 15.8 15.8 15.8 7.94 7.94 7.92 7.92 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 26 27 28 29 30 53.8 53.8 53.8 41.4 41.4 53.8 53.8 53.8 41.4 41.4 53.1 53.1 53.1 41.3 41.3 47.3 47.3 47.3 40.5 40.5 42.6 42.6 42.6 37.7 37.7 39.7 39.7 39.7 32.2 32.2 29.7 29.7 29.7 25.4 25.4 18.8 18.8 18.8 18.5 18.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 34 35 36 75.2 75.2 75.2 71.0 41.4 41.4 75.2 75.2 75.2 71.0 41.4 41.4 73.6 73.6 73.6 69.4 41.3 41.3 61.6 61.6 61.6 57.8 40.5 40.5 51.9 51.9 51.9 50.7 37.7 37.7 40.1 40.1 40.1 40.1 32.2 32.2 29.4 29.4 29.4 29.4 25.4 25.4 18.9 18.9 18.9 18.9 18.5 18.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 37 38 39 40 41 42 57.9 71.0 49.6 59.3 65.5 27.6 49.1 59.5 49.6 59.3 64.2 27.6 … … 48.8 57.3 55.7 27.4 … … 42.5 40.8 42.0 25.9 … … 37.0 … … 24.0 … … 28.9 … … 21.5 … … 18.5 … … 19.6 … … 7.84 … … 17.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 152 2011a SECTION II, PART D (METRIC) TABLE 1B SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 17 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 18 19 20 21 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 25 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 26 27 28 29 30 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 34 35 36 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 37 38 39 40 41 42 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 153 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 5 6 … … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … … A91060 A91060 A91060 A91060 A91060 A91060 O H112 H112 H112 H12 H14 7 8 9 … … … Drawn smls. tube Drawn smls. tube Drawn smls. tube SB-210 SB-210 SB-210 … … … A91060 A91060 A91060 O H14 H113 10 11 12 13 14 … … … … … Bar, rod, shapes Bar, rod, shapes Cond. & heat exch. tubes Smls. extr. tube Smls. extr. tube SB-221 SB-221 SB-234 SB-241 SB-241 … … … … … A91060 A91060 A91060 A91060 A91060 O H112 H14 O H112 15 16 17 18 19 20 … … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … … A91100 A91100 A91100 A91100 A91100 A91100 O H112 H112 H112 H12 H14 21 22 23 24 … … … … Bar, rod, shapes Bar, rod, shapes Smls. extr. tube Smls. extr. tube SB-221 SB-221 SB-241 SB-241 … … … … A91100 A91100 A91100 A91100 O H112 O H112 25 26 27 … … … Die forgings Die forgings Die forgings SB-247 SB-247 SB-247 … … … A92014 A92014 A92014 T4 T6 T6 28 29 30 31 … … … … Bar, rod, wire Bar, rod, wire Bar, rod, wire Bar, rod, wire SB-211 SB-211 SB-211 SB-211 … … … … A92024 A92024 A92024 A92024 T4 T4 T4 T4 32 33 34 35 … … … … Bar, rod, shapes Bar, rod, shapes Bar, rod, shapes Bar, rod, shapes SB-221 SB-221 SB-221 SB-221 … … … … A92024 A92024 A92024 A92024 T3 T3 T3 T3 36 37 38 39 40 41 … … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … … A93003 A93003 A93003 A93003 A93003 A93003 O H112 H112 H112 H12 H14 Line No. 154 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 6 1.30 – 76.2 6.35 – 12.69 12.70 – 25.40 25.41 – 76.2 1.30 – 50.8 1.30 – 25.4 21 21 21 21 21 21 55 76 69 62 76 83 17 48 34 28 62 69 NP NP NP NP NP NP 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 121 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 204 204 NFA-7 NFA-7 NFA-7 NFA-7 NFA-7 NFA-7 T3 T3, W3 T4, W3 T3, W3 T3, W3 T3, W3 7 8 9 0.46 – 12.7 0.46 – 12.7 0.46 – 12.7 21 … 21 59 83 59 17 69 17 NP NP NP 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 204 204 204 204 204 204 NFA-7 NFA-7 NFA-7 T3 T3, W3 T3, W3 10 11 12 13 14 … … 0.25 – 5.08 … … 21 21 21 21 21 59 59 83 59 59 17 17 69 17 17 NP NP NP NP NP 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 NFA-7 NFA-7 NFA-7 NFA-7 NFA-7 G13, T3 G13, T3, W3 T3, W4 T3 T3, W3 15 16 17 18 19 20 0.15 – 76.2 6.35 – 12.69 12.70 – 50.80 50.81 – 76.2 1.30 – 50.8 0.23 – 25.4 21 21 21 21 21 21 76 90 83 79 97 110 24 48 34 28 76 97 NP NP NP NP NP NP 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 204 204 NFA-7 NFA-7 NFA-7 NFA-7 NFA-7 NFA-7 T4 T4, W3 T4, W3 T4, W3 T4, W3 T4, W3 21 22 23 24 … … … … 21 21 21 21 76 76 76 76 21 21 21 21 NP NP NP NP 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-7 NFA-7 NFA-7 NFA-7 T4 T4, W3 T4 T4, W3 25 26 27 ≤ 101.6 ≤ 50.8 50.81 – 101.6 … … … 380 450 435 205 385 370 NP NP NP 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 NFA-6 NFA-6 NFA-6 T3, W4 T2, W4 T2, W4 28 29 30 31 3.18 – 12.69 12.70 – 114.30 114.31 – 165.10 165.11 – 203.2 … … … … 425 425 425 400 310 290 275 260 NP NP NP NP 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-6 NFA-6 NFA-6 NFA-6 T2, W4 T2, W4 T2, W4 T2, W4 32 33 34 35 ≤ 6.34 6.35 – 19.04 19.05 – 38.09 ≥ 38.10 … … … … 395 415 450 470 290 305 315 330 NP NP NP NP 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-6 NFA-6 NFA-6 NFA-6 G24, T2, W4 G24, T2, W4 G24, T2, W4 G24, T2, W4 36 37 38 39 40 41 0.15 – 76.2 6.35 – 12.69 12.70 – 50.80 50.81 – 76.2 0.43 – 50.8 0.23 – 25.4 21 21 21 21 21 21 97 120 100 100 120 140 34 69 41 41 83 120 NP NP NP NP NP NP 121 (Cl. 3 only) 149 (Cl. 3 only) 93 (Cl. 3 only) 93 (Cl. 3 only) 149 (Cl. 3 only) 121 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 204 204 NFA-1 NFA-1 NFA-1 NFA-1 NFA-1 NFA-2 T3 T4, W3 T3, W3 T3, W3 T4, W3 T4, W3 155 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 5 6 11.7 22.1 20.0 17.9 22.1 23.4 11.7 20.7 18.7 16.6 22.1 23.4 10.9 15.9 14.5 12.7 17.1 23.1 10.2 14.2 12.9 11.6 15.7 20.3 8.91 12.4 11.7 10.3 14.4 17.8 7.68 11.2 9.80 7.74 12.6 12.7 5.87 7.64 7.35 5.82 8.43 8.88 3.97 3.78 4.85 4.00 3.97 5.25 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 11.7 23.4 11.7 11.7 23.4 11.7 10.9 23.1 10.9 10.2 20.3 10.2 8.91 17.8 8.91 7.68 12.7 7.68 5.87 8.88 5.87 3.97 5.25 3.97 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 14 11.7 11.7 23.4 11.7 11.7 11.7 11.7 23.4 11.7 11.7 10.9 10.9 23.1 10.9 10.7 10.2 10.2 20.3 10.2 9.45 8.91 8.91 17.8 8.91 8.22 7.68 7.68 12.7 7.68 6.98 5.87 5.87 8.88 5.87 5.74 3.97 3.97 5.25 3.97 4.50 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 15 16 17 18 19 20 15.9 25.5 22.8 18.6 27.6 31.7 15.9 25.5 22.8 18.6 27.6 31.7 15.9 24.5 21.9 18.1 26.8 30.9 15.6 18.0 16.7 16.1 21.5 24.5 12.3 16.4 15.1 12.3 19.2 19.1 9.80 12.1 12.0 9.80 14.2 14.1 7.35 7.63 7.68 7.35 9.13 9.16 4.84 3.35 3.31 4.84 4.21 4.19 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 24 13.8 13.8 13.8 13.8 13.8 13.8 13.8 13.8 13.8 13.8 13.8 13.8 13.7 13.7 13.7 13.7 12.3 12.3 12.3 12.3 9.83 9.83 9.83 9.83 7.33 7.33 7.33 7.33 4.86 4.86 4.86 4.86 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 108 128 124 108 128 124 89.2 125 121 85.3 98.4 98.7 78.7 78.2 78.1 48.8 48.6 48.6 29.5 29.7 29.7 12.5 12.4 12.4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 31 122 122 122 114 122 122 122 114 118 118 118 111 90.6 90.6 90.6 84.6 70.7 70.7 70.7 66.0 46.3 46.3 46.3 43.3 32.7 32.7 32.7 30.7 21.2 21.2 21.2 19.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 112 118 128 134 112 118 128 134 109 114 124 130 83.2 87.2 94.4 99.1 64.6 68.0 73.4 76.8 42.6 44.7 48.3 50.4 30.6 32.0 34.3 36.3 20.0 20.9 22.0 24.0 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 36 37 38 39 40 41 23.4 33.8 26.2 24.8 33.8 39.3 23.4 33.8 26.2 24.8 33.8 39.3 23.1 32.9 25.0 23.9 32.9 38.5 20.1 26.9 21.3 21.4 26.9 33.1 16.4 24.7 16.3 16.3 24.7 29.4 12.6 21.0 12.6 12.6 21.0 21.1 10.1 17.2 10.1 10.1 17.2 17.0 7.64 13.5 7.63 7.63 13.5 13.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 156 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 14 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 15 16 17 18 19 20 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 24 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 31 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 36 37 38 39 40 41 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 157 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 5 … … … … … Drawn smls. tube Drawn smls. tube Drawn smls. tube Drawn smls. tube Drawn smls. tube SB-210 SB-210 SB-210 SB-210 SB-210 … … … … … A93003 A93003 A93003 A93003 A93003 O H113 H12 H14 H18 6 7 8 9 … … … … Bar, rod, shapes Bar, rod, shapes Cond. & heat exch. tubes Cond. & heat exch. tubes SB-221 SB-221 SB-234 SB-234 … … … … A93003 A93003 A93003 A93003 O H112 H14 H25 10 11 12 13 14 15 … … … … … … Smls. extr. tube Smls. extr. tube Smls. pipe Smls. pipe Die forgings Die forgings SB-241 SB-241 SB-241 SB-241 SB-247 SB-247 … … … … … … A93003 A93003 A93003 A93003 A93003 A93003 O H112 H112 H18 H112 H112 wld. 16 17 18 19 … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 … … … … A93004 A93004 A93004 A93004 O H112 H32 H34 20 21 22 23 24 … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … A95052 A95052 A95052 A95052 A95052 O H112 H112 H32 H34 25 26 27 … … … Drawn smls. tube Drawn smls. tube Drawn smls. tube SB-210 SB-210 SB-210 … … … A95052 A95052 A95052 O H32 H34 28 29 30 … … … Cond. & heat exch. tubes Cond. & heat exch. tubes Smls. extr. tube SB-234 SB-234 SB-241 … … … A95052 A95052 A95052 H32 H34 O 31 32 33 34 35 … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … A95083 A95083 A95083 A95083 A95083 O O O O O 36 37 38 39 … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 … … … … A95083 A95083 A95083 A95083 H112 H112 H321 H321 40 41 42 … … … Bar, rod, shapes Bar, rod, shapes Bar, rod, shapes SB-221 SB-221 SB-221 … … … A95083 A95083 A95083 O H111 H112 Line No. 158 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 0.25 – 12.7 0.25 – 12.7 0.25 – 12.7 0.25 – 12.7 0.25 – 12.7 21 21 21 21 21 97 97 120 140 185 34 34 83 120 165 NP NP NP NP NP 121 (Cl. 3 only) 121 (Cl. 3 only) 149 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 NFA-1 NFA-1 NFA-1 NFA-2 NFA-2 T3 T3, W3 T4, W3 T4, W3 T4, W3 6 7 8 9 … … 0.25 – 5.08 0.25 – 5.08 21 21 21 21 97 97 140 150 34 34 120 130 NP NP NP NP 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-1 NFA-1 NFA-2 NFA-2 T3 T3, W3 T4, W4 T4, W4 10 11 12 13 14 15 … … ≥ 25.4 < 25.4 ≤ 101.6 ≤ 101.6 21 21 21 21 21 21 97 97 97 185 97 97 34 34 34 165 34 … NP NP NP NP NP NP 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 204 204 NFA-1 NFA-1 NFA-1 NFA-1 NFA-1 NFA-1 T3 T3, W3 T3, W4 T4, W4 T3 T3, W7 16 17 18 19 0.15 – 76.2 6.35 – 76.2 1.30 – 50.8 1.30 – 25.4 22 22 22 22 150 160 195 220 59 62 145 170 NP NP NP NP 149 (Cl. 3 only) 149 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-3 NFA-3 NFA-3 NFA-4 … W3 W3 W3 20 21 22 23 24 1.30 – 76.2 6.35 – 12.69 12.70 – 76.20 1.30 – 50.8 1.30 – 25.4 22 22 22 22 22 170 195 170 210 235 65 110 65 160 180 NP NP NP NP NP 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 93 (Cl. 3 only) 93 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 NFA-8 NFA-8 NFA-8 NFA-3 NFA-4 … W3 W3 W3 W3 25 26 27 0.46 – 11.43 0.46 – 11.43 0.46 – 11.43 22 22 22 170 210 235 69 160 180 NP NP NP 149 (Cl. 3 only) 93 (Cl. 3 only) 93 (Cl. 3 only) 204 204 204 204 204 204 NFA-8 NFA-8 NFA-8 … W4 W4 28 29 30 0.25 – 5.08 0.25 – 5.08 … 22 22 22 210 235 170 160 180 69 NP NP NP 93 (Cl. 3 only) 93 (Cl. 3 only) 121 (Cl. 3 only) 204 204 204 204 204 204 NFA-8 NFA-8 NFA-8 W4 W4 … 31 32 33 34 35 1.30 – 38.10 38.11 – 76.20 76.21 – 127.00 127.01 – 177.80 177.81 – 203.2 25 25 25 25 25 275 270 260 255 250 125 120 110 100 97 NP NP NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 66 66 66 66 NFA-11 NFA-11 NFA-11 NFA-11 NFA-11 G18, G19 G18, G19 G18, G19 G18, G19 G18, G19 36 37 38 39 6.35 – 38.10 38.11 – 76.20 4.78 – 38.10 38.11 – 76.20 25 25 25 25 275 270 305 285 125 120 215 200 NP NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 66 66 NFA-11 NFA-11 NFA-11 NFA-11 G18, G19, W3 G18, G19, W3 G18, G19, W3 G18, G19, W3 40 41 42 ≤ 127.0 ≤ 127.0 ≤ 127.0 25 25 25 270 275 270 110 165 110 NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 NFA-11 NFA-11 NFA-11 G18, G19 G18, G19, W3 G18, G19, W3 159 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 5 23.4 23.4 33.8 39.3 53.8 23.4 23.4 33.8 39.3 53.8 23.1 23.1 32.9 38.5 51.6 20.1 20.1 26.9 33.1 42.4 16.4 16.4 24.7 29.4 36.8 12.6 12.6 21.0 21.1 24.8 10.1 10.1 17.2 17.0 18.1 7.64 7.64 13.5 13.6 12.3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 23.4 23.4 39.3 43.4 23.4 23.4 39.3 43.4 23.1 23.1 38.5 42.5 20.1 20.1 33.1 35.5 16.4 16.4 29.4 29.3 12.6 12.6 21.1 21.1 10.1 10.1 17.0 17.1 7.64 7.64 13.6 13.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 14 15 23.4 23.4 23.4 53.8 23.4 23.4 23.4 23.4 23.4 53.8 23.4 23.4 23.1 23.1 23.1 51.6 23.1 23.1 20.1 20.1 20.1 42.4 20.1 20.1 16.4 16.4 16.4 36.8 16.4 16.4 12.6 12.6 12.6 24.8 12.6 12.6 10.1 10.1 10.1 18.1 10.1 10.1 7.64 7.64 7.64 12.3 7.64 7.64 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 39.3 41.4 55.2 62.7 39.3 41.4 55.2 62.7 39.1 41.2 54.3 62.0 37.6 39.6 47.2 53.3 34.2 34.9 39.5 39.4 26.8 26.8 27.0 26.9 18.1 18.1 17.9 18.0 9.40 9.41 9.50 9.46 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 23 24 43.4 55.2 43.4 61.4 66.9 43.4 55.2 43.4 61.4 66.9 43.4 54.2 43.4 60.1 66.1 43.2 47.5 43.4 50.3 56.6 38.3 42.3 41.0 42.3 42.1 29.0 29.2 29.1 29.1 29.0 18.4 18.3 18.3 18.3 18.4 7.87 7.97 7.95 7.95 7.91 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 46.2 61.4 66.9 46.2 61.4 66.9 45.7 60.1 66.0 42.3 50.2 55.8 38.3 41.6 41.4 29.0 29.1 29.0 17.9 17.8 17.8 6.67 6.72 6.68 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 61.4 66.9 46.2 61.4 66.9 46.2 60.1 66.1 45.9 50.3 56.6 42.9 42.3 42.1 38.3 29.1 29.0 29.0 18.3 18.4 17.9 7.95 7.91 6.66 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 34 35 78.6 76.5 73.8 68.9 64.1 78.6 76.5 73.8 68.9 64.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 36 37 38 39 78.6 76.5 86.9 80.7 78.6 76.5 86.9 80.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 40 41 42 73.8 78.6 73.8 73.8 78.6 73.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 160 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 14 15 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 23 24 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 34 35 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 36 37 38 39 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 40 41 42 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 161 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 … … … Smls. extr. tube Smls. extr. tube Smls. extr. tube SB-241 SB-241 SB-241 … … … A95083 A95083 A95083 O H111 H112 4 5 6 7 … … … … Die & hand forgings Die & hand forgings Die & hand forgings Die & hand forgings SB-247 SB-247 SB-247 SB-247 … … … … A95083 A95083 A95083 A95083 H111 H112 H111 wld. H112 wld. 8 9 10 11 12 … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … A95086 A95086 A95086 A95086 A95086 O H112 H112 H112 H112 13 14 15 … … … Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 … … … A95086 A95086 A95086 H116 H32 H34 16 17 18 19 … … … … Bar, rod, shapes Smls. extr. tube Smls. extr. tube Smls. extr. tube SB-221 SB-241 SB-241 SB-241 … … … … A95086 A95086 A95086 A95086 H112 O H111 H112 20 21 22 23 24 … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … A95154 A95154 A95154 A95154 A95154 O H112 H112 H32 H34 25 26 27 28 … … … … Drawn smls. tube Drawn smls. tube Bar, rod, shapes Bar, rod, shapes SB-210 SB-210 SB-221 SB-221 … … … … A95154 A95154 A95154 A95154 O H34 O H112 29 30 31 32 33 … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … A95254 A95254 A95254 A95254 A95254 O H112 H112 H32 H34 34 35 36 37 38 … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … A95454 A95454 A95454 A95454 A95454 O H112 H112 H32 H34 39 40 41 … … … Bar, rod, shapes Bar, rod, shapes Bar, rod, shapes SB-221 SB-221 SB-221 … … … A95454 A95454 A95454 O H111 H112 Line No. 162 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 … … … 25 25 25 270 275 270 110 165 110 NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 NFA-11 NFA-11 NFA-11 G18, G19 G18, G19, W3 G18, G19, W3 4 5 6 7 ≤ 101.6 ≤ 101.6 ≤ 101.6 ≤ 101.6 25 25 25 25 270 270 260 260 140 110 … … NP NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 66 66 NFA-11 NFA-11 NFA-11 NFA-11 G18, G19, W4 G18, G19, W4 G18, G19, W7 G18, G19, W7 8 9 10 11 12 1.30 – 50.8 4.78 – 12.69 12.70 – 25.40 25.41 – 50.80 50.81 – 76.2 25 25 25 25 25 240 250 240 240 235 97 125 110 97 97 NP NP NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 66 66 66 66 NFA-9 NFA-9 NFA-9 NFA-9 NFA-9 G18, G19 G18, G19, W3 G18, G19, W3 G18, G19, W3 G18, G19 13 14 15 1.60 – 50.8 1.30 – 50.8 1.30 – 25.4 25 25 25 275 275 305 195 195 235 NP NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 NFA-11 NFA-11 NFA-11 G18, G19, W3 G18, G19, W3 G18, G19, W3 16 17 18 19 ≤ 127.0 ≤ 127.0 ≤ 127.0 ≤ 127.0 25 25 25 25 240 240 250 240 97 97 145 97 NP NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 66 66 NFA-9 NFA-9 NFA-9 NFA-9 G18, G19, W4 G18, G19 G18, G19, W3 … 20 21 22 23 24 1.30 – 76.2 6.35 – 12.69 12.70 – 76.20 1.30 – 50.8 1.30 – 25.4 22 22 22 22 22 205 220 205 250 270 76 125 76 180 200 NP NP NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 66 66 66 66 NFA-5 NFA-11 NFA-5 NFA-11 NFA-11 G18, G19 G18, G19, W3 G18, G19, W3 G18, G19, W3 G18, G19, W3 25 26 27 28 0.25 – 11.43 0.25 – 11.43 … … 22 22 22 22 205 270 205 205 76 200 76 76 NP NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 66 66 NFA-5 NFA-5 NFA-5 NFA-5 G18, G19 G18, G19, W3 G18, G19 G18, G19, W3 29 30 31 32 33 1.30 – 76.2 6.35 – 12.69 12.70 – 76.20 1.30 – 50.8 1.30 – 25.4 22 22 22 22 22 205 220 205 250 270 76 125 76 180 200 NP NP NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 66 66 66 66 NFA-5 NFA-11 NFA-5 NFA-11 NFA-11 G18, G19 G18, G19, W3 G18, G19, W3 G18, G19, W3 G18, G19, W3 34 35 36 37 38 1.30 – 76.2 6.35 – 12.69 12.70 – 76.20 1.30 – 50.8 1.30 – 25.4 22 22 22 22 22 210 220 210 250 270 83 125 83 180 200 NP NP NP NP NP 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 NFA-6 NFA-6 NFA-6 NFA-6 NFA-6 T1 T1, W3 T1, W3 T1, W3 T1, W3 39 40 41 ≤ 127.0 ≤ 127.0 ≤ 127.0 22 22 22 210 230 210 83 130 83 NP NP NP 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 204 204 204 204 204 204 NFA-6 NFA-6 NFA-6 T1 T1, W3 T1, W3 163 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 73.8 78.6 73.8 73.8 78.6 73.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 4 5 6 7 76.5 73.8 75.2 75.2 76.5 73.8 75.2 75.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 8 9 10 11 12 64.1 71.0 68.9 64.1 64.1 64.1 71.0 68.9 64.1 64.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 13 14 15 78.6 78.6 86.9 78.6 78.6 86.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 64.1 64.1 71.0 64.1 64.1 64.1 71.0 64.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 23 24 50.3 62.7 50.3 71.0 76.5 50.3 62.7 50.3 71.0 76.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 28 50.3 76.5 50.3 50.3 50.3 76.5 50.3 50.3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 30 31 32 33 50.3 62.7 50.3 71.0 76.5 50.3 62.7 50.3 71.0 76.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 37 38 55.2 62.7 55.2 71.0 76.5 55.2 62.7 55.2 71.0 76.5 54.4 61.5 54.4 68.4 73.1 50.6 49.6 50.6 49.0 48.5 37.4 37.5 37.4 37.5 37.6 28.7 28.8 28.7 28.8 28.8 21.9 21.9 21.9 21.8 21.8 15.1 15.1 15.1 15.1 15.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 39 40 41 55.2 64.8 55.2 55.2 64.8 55.2 54.4 63.2 54.4 50.6 49.5 50.6 37.4 37.5 37.4 28.7 28.8 28.7 21.9 21.9 21.9 15.1 15.1 15.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 164 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 4 5 6 7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 8 9 10 11 12 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 13 14 15 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 23 24 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 28 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 30 31 32 33 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 37 38 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 39 40 41 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 165 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 5 … … … … … Cond. & heat exch. tubes Cond. & heat exch. tubes Smls. extr. tube Smls. extr. tube Smls. extr. tube SB-234 SB-234 SB-241 SB-241 SB-241 … … … … … A95454 A95454 A95454 A95454 A95454 H32 H34 O H111 H112 6 7 8 9 10 … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … A95456 A95456 A95456 A95456 A95456 O O O O O 11 12 13 14 15 … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … A95456 A95456 A95456 A95456 A95456 H112 H112 H321 H321 H321 16 17 18 … … … Bar, rod, shapes Bar, rod, shapes Bar, rod, shapes SB-221 SB-221 SB-221 … … … A95456 A95456 A95456 O H111 H112 19 20 21 … … … Smls. extr. tube Smls. extr. tube Smls. extr. tube SB-241 SB-241 SB-241 … … … A95456 A95456 A95456 O H111 H112 22 23 24 25 26 … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … A95652 A95652 A95652 A95652 A95652 O H112 H112 H32 H34 (10) (10) 27 28 29 30 31 … … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 SB-209 … … … … … A96061 A96061 A96061 A96061 A96061 T4 T451 T6 T651 T651 (10) 32 33 34 35 … … … … Plate, sheet Plate, sheet Plate, sheet Plate, sheet SB-209 SB-209 SB-209 SB-209 … … … … A96061 A96061 A96061 A96061 T4 wld. T451 wld. T6 wld. T651 wld. 36 37 38 39 … … … … Drawn smls. tube Drawn smls. tube Drawn smls. tube Drawn smls. tube SB-210 SB-210 SB-210 SB-210 … … … … A96061 A96061 A96061 A96061 T4 T6 T4 wld. T6 wld. Line No. (10) (10) 166 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. 1 2 3 4 5 Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 0.25 – 6.35 0.25 – 6.35 ≤ 127.0 ≤ 127.0 ≤ 127.0 22 22 22 22 22 250 270 210 230 210 180 200 83 130 83 NP NP NP NP NP 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 NFA-6 NFA-6 NFA-6 NFA-6 NFA-6 T1, W4 T1, W4 T1 T1, W3 T1, W3 6 7 8 9 10 1.30 – 38.10 38.11 – 76.20 76.21 – 127.00 127.01 – 177.80 177.81 – 203.2 25 25 25 25 25 290 285 275 270 260 130 125 120 110 100 NP NP NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 66 66 66 66 NFA-10 NFA-10 NFA-10 NFA-10 NFA-10 G18, G19 G18, G19 G18, G19 G18, G19 G18, G19 11 12 13 14 15 6.35 – 38.10 38.11 – 76.20 4.78 – 12.69 12.70 – 38.10 38.11 – 76.20 25 25 25 25 25 290 285 315 305 285 130 125 230 215 200 NP NP NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 66 66 66 66 NFA-10 NFA-10 NFA-10 NFA-10 NFA-10 G18, G19, W3 G18, G19, W3 G18, G19, W3 G18, G19, W3 G18, G19, W3 16 17 18 ≤ 127.0 ≤ 127.0 ≤ 127.0 25 25 25 285 290 285 130 180 130 NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 NFA-10 NFA-10 NFA-10 G18, G19 G18, G19, W3 G18, G19, W3 19 20 21 ≤ 127.0 ≤ 127.0 ≤ 127.0 25 25 25 285 290 285 130 180 130 NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 NFA-10 NFA-10 NFA-10 G18, G19 G18, G19, W3 G18, G19, W3 22 23 24 25 26 1.30 – 76.2 6.35 – 12.69 12.70 – 76.20 1.30 – 50.8 1.30 – 25.4 22 22 22 22 22 170 195 170 210 235 65 110 65 160 180 NP NP NP NP NP 121 (Cl. 3 only) 121 (Cl. 3 only) 121 (Cl. 3 only) 93 (Cl. 3 only) 93 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 NFA-8 NFA-8 NFA-8 NFA-3 NFA-4 T2 T1, W3 T2, W3 T1, W3 T1, W3 27 28 29 30 31 1.30 – 6.34 6.35 – 76.2 1.30 – 6.34 6.35 – 101.60 101.61 – 152.4 23 23 23 23 23 205 205 290 290 275 110 110 240 240 240 NP NP NP NP NP 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 NFA-13 NFA-13 NFA-12 NFA-12,13 NFA-12,13 G24, T3, W4 G24, T3, W4 G24, T3, W4 G24, T3, W4, W16 G24, T3, W4, W16 (10) (10) 32 33 34 35 1.30 – 6.34 6.35 – 76.2 1.30 – 6.34 6.35 – 152.4 23 23 23 23 165 165 165 165 … … … … NP NP NP NP 204 (Cl. 3 only) NP 204 (Cl. 3 only) NP 204 204 204 204 204 204 204 204 NFA-13 NFA-13 NFA-12 NFA-12,13 G24, T3, W7 G24, T3, W7 G24, T3, W7 G24, T3, W7, W16 (10) 36 37 38 39 0.64 – 12.7 0.64 – 12.7 0.64 – 12.7 0.64 – 12.7 23 23 23 23 205 290 165 165 110 240 … … NP NP NP NP 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-13 NFA-12,13 NFA-13 NFA-12,13 T3, W4 T3, W4, W16 T3, W7 T3, W7, W16 167 (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 5 71.0 76.5 55.2 64.8 55.2 71.0 76.5 55.2 64.8 55.2 68.4 73.1 54.4 63.2 54.4 49.0 48.5 50.6 49.5 50.6 37.5 37.6 37.4 37.5 37.4 28.8 28.8 28.7 28.8 28.7 21.8 21.8 21.9 21.9 21.9 15.1 15.1 15.1 15.1 15.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 10 82.7 80.7 77.9 73.8 68.9 82.7 80.7 77.9 73.8 68.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 15 82.7 80.7 90.3 86.9 80.7 82.7 80.7 90.3 86.9 80.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 80.7 82.7 80.7 80.7 82.7 80.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 19 20 21 80.7 82.7 80.7 80.7 82.7 80.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 25 26 43.4 55.2 43.4 61.4 66.9 43.4 55.2 43.4 61.4 66.9 43.4 54.9 43.4 60.1 64.7 43.3 50.7 43.3 50.3 49.8 41.8 41.5 41.8 41.6 41.6 29.2 29.1 29.2 29.1 29.1 18.2 18.3 18.2 18.3 18.3 8.00 7.92 8.00 7.93 7.94 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) 27 28 29 30 31 59.3 59.3 82.7 82.7 78.6 59.3 59.3 82.7 82.7 78.6 58.1 58.1 80.7 80.7 76.9 50.1 50.1 66.4 66.4 64.5 47.4 47.4 57.5 57.5 56.1 43.8 43.8 44.3 44.3 44.3 33.3 33.3 32.9 32.9 32.4 21.6 21.6 21.9 21.9 20.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) 32 33 34 35 41.4 41.4 41.4 41.4 41.4 41.4 41.4 41.4 41.3 41.3 41.3 41.3 40.5 40.5 40.5 40.5 37.7 37.7 37.7 37.7 32.2 32.2 32.2 32.2 25.4 25.4 25.4 25.4 18.5 18.5 18.5 18.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 36 37 38 39 59.3 82.7 41.4 41.4 59.3 82.7 41.4 41.4 58.1 80.7 41.3 41.3 50.1 66.4 40.5 40.5 47.4 57.5 37.7 37.7 43.8 44.3 32.2 32.2 33.3 32.9 25.4 25.4 21.6 21.9 18.5 18.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) 168 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 10 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 15 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 19 20 21 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 25 26 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 27 28 29 30 31 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) 32 33 34 35 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) 36 37 38 39 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 169 (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 … … … … Bar, rod, wire Bar, rod, wire Bar, rod, wire Bar, rod, wire SB-211 SB-211 SB-211 SB-211 … … … … A96061 A96061 A96061 A96061 T6 T651 T6 wld. T651 wld. 5 6 7 8 … … … … Bar, rod, shapes Bar, rod, shapes Bar, rod, shapes Bar, rod, shapes SB-221 SB-221 SB-221 SB-221 … … … … A96061 A96061 A96061 A96061 T4 T6 T4 wld. T6 wld. 9 10 11 12 … … … … Cond. & heat exch. tubes Cond. & heat exch. tubes Cond. & heat exch. tubes Cond. & heat exch. tubes SB-234 SB-234 SB-234 SB-234 … … … … A96061 A96061 A96061 A96061 T4 T6 T4 wld. T6 wld. (10) 13 14 15 16 … … … … Smls. extr. tube Smls. extr. tube Smls. extr. tube Smls. extr. tube SB-241 SB-241 SB-241 SB-241 … … … … A96061 A96061 A96061 A96061 T4 T6 T4 wld. T6 wld. (10) (10) (10) 17 18 19 … … … Smls. pipe Smls. pipe Smls. pipe SB-241 SB-241 SB-241 … … … A96061 A96061 A96061 T6 T6 T6 wld. (10) (10) (10) (10) (10) (10) 20 21 22 23 24 25 … … … … … … Die forgings Hand forgings Hand forgings Die & hand forgings Shapes Shapes SB-247 SB-247 SB-247 SB-247 SB-308 SB-308 … … … … … … A96061 A96061 A96061 A96061 A96061 A96061 T6 T6 T6 T6 wld. T6 T6 wld. 26 27 28 29 … … … … Drawn smls. tube Drawn smls. tube Bar, rod, shapes Bar, rod, shapes SB-210 SB-210 SB-221 SB-221 … … … … A96063 A96063 A96063 A96063 T6 T6 wld. T1 T1 30 31 32 33 34 … … … … … Bar, rod, shapes Bar, rod, shapes Bar, rod, shapes Bar, rod, shapes Bar, rod, shapes SB-221 SB-221 SB-221 SB-221 SB-221 … … … … … A96063 A96063 A96063 A96063 A96063 T5 T5 T6 T5 wld. T6 wld. 35 36 37 38 … … … … Smls. extr. tube Smls. extr. tube Smls. extr. tube Smls. extr. tube SB-241 SB-241 SB-241 SB-241 … … … … A96063 A96063 A96063 A96063 T1 T1 T5 T5 39 40 41 42 43 … … … … … Smls. extr. tube Smls. extr. tube Smls. extr. tube Smls. pipe Smls. pipe SB-241 SB-241 SB-241 SB-241 SB-241 … … … … … A96063 A96063 A96063 A96063 A96063 T6 T5 wld. T6 wld. T6 T6 wld. Line No. (10) (10) (10) (10) (10) 170 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 3.18 – 6.34 6.35 – 203.2 3.18 – 6.34 6.35 – 203.2 23 23 23 23 290 290 165 165 240 240 … … NP NP NP NP 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-12 NFA-12,13 NFA-12 NFA-12,13 G24, T3, W4 G24, T3, W4, W16 G13, G24, T3, W7 G13, G24, T3, W7, W16 5 6 7 8 … … … … 23 23 23 23 180 260 165 165 110 240 … … NP NP NP NP 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-13 NFA-12,13 NFA-13 NFA-12,13 G24, T3, W4 G24, T3, W4, W16 G24, T3, W7 G13, G24, T3, W7, W16 9 10 11 12 0.64 – 5.08 0.64 – 5.08 0.64 – 5.08 0.64 – 5.08 23 23 23 23 205 290 165 165 110 240 … … NP NP NP NP 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-13 NFA-12 NFA-13 NFA-12 T3, W4 T3, W4 T3, W7 T3, W7 13 14 15 16 … … … … 23 23 23 23 180 260 165 165 110 240 … … NP NP NP NP 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-13 NFA-12,13 NFA-13 NFA-12,13 G24, T3, W4 G24, T3, W4, W16 G24, T3, W7 G24, T3, W7, W16 17 18 19 < 25.4 ≥ 25.4 … 23 23 23 290 260 165 240 240 … NP NP NP 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 NFA-12,13 NFA-12,13 NFA-12,13 T3, W4, W16 T3, W4, W16 T3, W7, W16 (10) (10) (10) 20 21 22 23 24 25 ≤ 101.6 ≤ 101.6 101.61 – 203.2 ≤ 203.2 … … 23 23 23 23 23 23 260 255 240 165 260 165 240 230 220 … 240 … NP NP NP NP NP NP 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 204 204 NFA-12,13 NFA-12,13 NFA-12,13 NFA-12,13 NFA-12,13 NFA-12,13 T3, W4, W16 T3, W4, W16 T3, W4, W16 T3, W7, W16 T3, W4, W16 G13, T3, W7, W16 (10) (10) (10) (10) (10) (10) 26 27 28 29 0.64 – 12.7 0.64 – 12.7 ≤ 12.70 12.71 – 25.4 23 23 23 23 230 120 120 110 195 … 62 55 NP NP NP NP 204 (Cl. 3 only) 204 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFA-1 NFA-1 NFA-1 NFA-1 T3, W4 T3, W7 T3, W4 T3, W4 30 31 32 33 34 ≤ 12.70 12.71 – 25.4 ≤ 25.4 ≤ 25.4 ≤ 25.4 23 23 23 23 23 150 145 205 120 120 110 100 170 … … NP NP NP NP NP 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 NFA-1 NFA-1 NFA-1 NFA-1 NFA-1 T3, W4 T3, W4 T3, W4 T3, W7 T3, W7 35 36 37 38 ≤ 12.70 12.71 – 25.4 ≤ 12.70 12.71 – 25.4 23 23 23 23 120 110 150 145 62 55 110 100 NP NP NP NP 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) NP NP 204 204 NP NP 204 204 NFA-1 NFA-1 NFA-1 NFA-1 T3, W4 T3, W4 T3, W4 T3, W4 39 40 41 42 43 ≤ 25.4 ≤ 25.4 ≤ 25.4 … … 23 23 23 23 23 205 120 120 205 120 170 … … 170 … NP NP NP NP NP 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 NFA-1 NFA-1 NFA-1 NFA-1 NFA-1 T3, W4 T3, W7 T3, W7 T3, W4 T3, W7 171 (10) (10) (10) (10) (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 82.7 82.7 41.4 41.4 82.7 82.7 41.4 41.4 80.7 80.1 41.3 41.3 66.4 66.5 40.5 40.5 57.5 57.5 37.7 37.7 44.3 45.0 32.2 32.2 32.9 33.1 25.4 25.4 21.9 21.4 18.5 18.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 51.0 75.2 41.4 41.4 51.0 75.2 41.4 41.4 50.0 73.4 41.3 41.3 43.3 61.1 40.5 40.5 41.4 54.1 37.7 37.7 40.3 44.2 32.2 32.2 32.7 33.0 25.4 25.4 24.3 21.8 18.5 18.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 10 11 12 59.3 82.7 41.4 41.4 59.3 82.7 41.4 41.4 58.1 80.7 41.3 41.3 50.1 66.4 40.5 40.5 47.4 57.5 37.7 37.7 43.8 44.3 32.2 32.2 33.3 32.9 25.4 25.4 21.6 21.9 18.5 18.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) 13 14 15 16 51.0 75.2 41.4 41.4 51.0 75.2 41.4 41.4 50.0 73.4 41.3 41.3 43.3 61.1 40.5 40.5 41.4 54.1 37.7 37.7 40.3 44.2 32.2 32.2 32.7 33.0 25.4 25.4 24.3 21.8 18.5 18.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) 17 18 19 82.7 75.2 41.4 82.7 75.2 41.4 80.7 73.4 41.3 66.4 61.1 40.5 57.5 54.1 37.7 44.3 44.2 32.2 32.9 33.0 25.4 21.9 21.8 18.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) (10) 20 21 22 23 24 25 75.2 73.1 68.9 41.4 75.2 41.4 75.2 73.1 68.9 41.4 75.2 40.7 73.4 71.3 67.4 41.3 72.8 38.8 61.1 59.1 56.5 40.5 56.6 36.9 54.1 52.8 50.8 37.7 49.3 34.3 44.2 44.1 42.7 32.2 39.3 29.3 33.0 33.1 32.8 25.4 29.3 23.2 21.8 21.8 22.8 18.5 19.4 16.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 26 27 28 29 64.8 29.6 33.8 31.7 64.8 29.6 33.8 31.7 63.0 29.5 32.9 31.0 48.9 28.8 29.0 27.6 37.4 26.7 29.0 27.6 24.2 21.1 24.0 23.8 15.2 14.9 15.4 15.6 6.74 8.69 6.61 6.50 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 30 31 32 33 34 43.4 41.4 59.3 29.6 29.6 43.4 41.4 59.3 29.6 29.6 42.2 40.3 57.7 29.5 29.5 34.3 32.9 44.9 28.8 28.8 31.5 29.5 34.0 26.7 26.7 24.0 23.9 24.1 21.1 21.1 15.3 15.4 15.3 14.9 14.9 6.66 6.60 6.67 8.69 8.69 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 35 36 37 38 33.8 31.7 43.4 41.4 33.8 31.7 43.4 41.4 32.9 31.0 42.2 40.3 29.0 27.6 34.3 33.0 29.0 27.6 31.5 30.2 24.0 23.8 24.0 24.0 15.4 15.6 15.3 15.4 … … 6.66 6.62 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 39 40 41 42 43 59.3 29.6 29.6 59.3 29.6 59.3 29.6 29.6 59.3 29.6 57.7 29.5 29.5 57.7 29.5 44.9 28.8 28.8 44.9 28.8 34.0 26.7 26.7 34.0 26.7 24.1 21.1 21.1 24.1 21.1 15.3 14.9 14.9 15.3 14.9 6.67 8.69 8.69 6.67 8.69 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) 172 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 10 11 12 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 13 14 15 16 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 17 18 19 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) 20 21 22 23 24 25 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) (10) 26 27 28 29 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 30 31 32 33 34 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 35 36 37 38 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 39 40 41 42 43 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 173 (10) (10) (10) (10) (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 … … … Rod Smls. tube Smls. pipe SB-187 SB-75 SB-42 … … … C10200 C10200 C10200 O60 O60 O61 4 5 6 7 8 9 … … … … … … Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip SB-152 SB-152 SB-152 SB-152 SB-152 SB-152 … … … … … … C10200 C10200 C10200 C10200 C10200 C10200 H00 H01 H02 H03 H04 O25 10 11 12 13 … … … … Smls. pipe Smls. tube Smls. cond. tube Smls. U-bend tube SB-42 SB-75 SB-111 SB-395 … … … … C10200 C10200 C10200 C10200 H55 H55 H55 H55 14 15 16 … … … Smls. pipe Smls. tube Smls. cond. tube SB-42 SB-75 SB-111 … … … C10200 C10200 C10200 H80 H80 H80 17 18 19 20 21 22 … … … … … … Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip SB-152 SB-152 SB-152 SB-152 SB-152 SB-152 … … … … … … C10400 C10400 C10400 C10400 C10400 C10400 H00 H01 H02 H03 H04 O25 23 24 25 26 27 28 … … … … … … Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip SB-152 SB-152 SB-152 SB-152 SB-152 SB-152 … … … … … … C10500 C10500 C10500 C10500 C10500 C10500 H00 H01 H02 H03 H04 O25 29 30 31 32 33 34 … … … … … … Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip SB-152 SB-152 SB-152 SB-152 SB-152 SB-152 … … … … … … C10700 C10700 C10700 C10700 C10700 C10700 H00 H01 H02 H03 H04 O25 35 36 … … Bar, rod Bar, rod SB-187 SB-187 … … C11000 C11000 H04 O60 37 38 39 40 41 42 … … … … … … Plate, sheet, strip, bar Plate, sheet, strip, bar Plate, sheet, strip, bar Plate, sheet, strip, bar Plate, sheet, strip, bar Plate, sheet, strip, bar SB-152 SB-152 SB-152 SB-152 SB-152 SB-152 … … … … … … C11000 C11000 C11000 C11000 C11000 C11000 H00 H01 H02 H03 H04 O25 43 44 45 … … … Smls. tube Smls. tube Smls. pipe SB-75 SB-75 SB-42 … … … C12000 C12000 C12000 O50 O60 O61 Line No. (10) (10) (10) (10) (10) (10) 174 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 … … 6 < DN ≤ 50 31 31 31 195 205 205 … 62 62 NP 204 204 149 149 (Cl. 3 only) 149 204 204 204 204 204 204 NFC-1 NFC-1 NFC-1 T2 G1, T3, W10 G1, T3, W10 4 5 6 7 8 9 … … … … … … 31 31 31 31 31 31 205 205 205 205 205 205 69 69 69 69 69 69 NP NP NP NP NP NP 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 204 204 NFC-1 NFC-1 NFC-1 NFC-1 NFC-1 NFC-1 T2 T2 T2 T2 T2 T2 10 11 12 13 50 < DN ≤ 300 … < 75 … 31 31 31 31 250 250 250 250 205 205 205 205 204 204 NP NP 204 204 (Cl. 3 only) 204 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFC-6 NFC-6 NFC-6 NFC-6 G1, W9, W10 G1, G9, W9, W10 G9, W9 W9 14 15 16 6 < DN ≤ 50 < 100 < 75 31 31 31 310 310 310 275 275 275 204 204 NP 149 177 149 204 204 204 204 204 204 NFC-6 NFC-6 NFC-6 G1, G5, G6, T4, W9, W10 G1, G9, T4, W9, W10 G9, T4, W9 17 18 19 20 21 22 … … … … … … 31 31 31 31 31 31 205 205 205 205 205 205 69 69 69 69 69 69 NP NP NP NP NP NP 149 149 149 149 149 149 204 204 204 204 204 204 204 204 204 204 204 204 NFC-1 NFC-1 NFC-1 NFC-1 NFC-1 NFC-1 T2 T2 T2 T2 T2 T2 23 24 25 26 27 28 … … … … … … 31 31 31 31 31 31 205 205 205 205 205 205 69 69 69 69 69 69 NP NP NP NP NP NP 149 149 149 149 149 149 204 204 204 204 204 204 204 204 204 204 204 204 NFC-1 NFC-1 NFC-1 NFC-1 NFC-1 NFC-1 T2 T2 T2 T2 T2 T2 29 30 31 32 33 34 … … … … … … 31 31 31 31 31 31 205 205 205 205 205 205 69 69 69 69 69 69 NP NP NP NP NP NP 149 149 149 149 149 149 204 204 204 204 204 204 204 204 204 204 204 204 NFC-1 NFC-1 NFC-1 NFC-1 NFC-1 NFC-1 T2 T2 T2 T2 T2 T2 35 36 … … 31 31 195 195 … … NP NP 149 149 204 204 204 204 NFC-1 NFC-1 T2 T2 37 38 39 40 41 42 ≤ 50 ≤ 50 ≤ 50 ≤ 50 ≤ 50 ≤ 50 31 31 31 31 31 31 205 205 205 205 205 205 69 69 69 69 69 69 NP NP NP NP NP NP NP NP NP NP NP NP 204 204 204 204 204 204 204 204 204 204 204 204 NFC-1 NFC-1 NFC-1 NFC-1 NFC-1 NFC-1 T2 T2 T2 T2 T2 T2 43 44 45 … … 6 < DN ≤ 50 31 31 31 205 205 205 62 62 62 NP 204 204 149 (Cl. 3 only) 149 (Cl. 3 only) 149 NP 204 204 NP 204 204 NFC-1 NFC-1 NFC-1 … G1, T3, W10 G1, T3, W10 175 (10) (10) (10) (10) (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (10) (10) (10) (10) (10) (10) Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 36.5 41.4 41.4 31.1 35.2 35.2 29.5 33.6 33.6 28.9 33.1 33.1 27.4 32.3 32.3 22.4 28.0 28.0 17.4 21.8 21.8 12.5 15.6 15.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 4 5 6 7 8 9 46.2 46.2 46.2 46.2 46.2 46.2 38.7 38.7 38.7 38.7 38.7 38.7 37.1 37.1 37.1 37.1 37.1 37.1 36.4 36.4 36.4 36.4 36.4 36.4 34.3 34.3 34.3 34.3 34.3 34.3 28.0 28.0 28.0 28.0 28.0 28.0 21.8 21.8 21.8 21.8 21.8 21.8 15.6 15.6 15.6 15.6 15.6 15.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 71.0 71.0 71.0 71.0 71.0 71.0 71.0 71.0 71.0 71.0 71.0 71.0 70.9 70.9 70.9 70.9 68.8 68.8 68.8 68.8 67.0 67.0 67.0 67.0 65.1 65.1 65.1 65.1 63.3 63.3 63.3 63.3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.8 88.8 88.8 86.0 86.0 86.0 82.1 82.1 82.1 39.8 39.8 39.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 17 18 19 20 21 22 46.2 46.2 46.2 46.2 46.2 46.2 38.7 38.7 38.7 38.7 38.7 38.7 37.1 37.1 37.1 37.1 37.1 37.1 36.4 36.4 36.4 36.4 36.4 36.4 34.3 34.3 34.3 34.3 34.3 34.3 28.0 28.0 28.0 28.0 28.0 28.0 21.8 21.8 21.8 21.8 21.8 21.8 15.6 15.6 15.6 15.6 15.6 15.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 23 24 25 26 27 28 46.2 46.2 46.2 46.2 46.2 46.2 38.7 38.7 38.7 38.7 38.7 38.7 37.1 37.1 37.1 37.1 37.1 37.1 36.4 36.4 36.4 36.4 36.4 36.4 34.3 34.3 34.3 34.3 34.3 34.3 28.0 28.0 28.0 28.0 28.0 28.0 21.8 21.8 21.8 21.8 21.8 21.8 15.6 15.6 15.6 15.6 15.6 15.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 30 31 32 33 34 46.2 46.2 46.2 46.2 46.2 46.2 38.7 38.7 38.7 38.7 38.7 38.7 37.1 37.1 37.1 37.1 37.1 37.1 36.4 36.4 36.4 36.4 36.4 36.4 34.3 34.3 34.3 34.3 34.3 34.3 28.0 28.0 28.0 28.0 28.0 28.0 21.8 21.8 21.8 21.8 21.8 21.8 15.6 15.6 15.6 15.6 15.6 15.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 35 36 36.5 36.5 31.1 31.1 29.5 29.5 28.9 28.9 27.4 27.4 22.4 22.4 17.4 17.4 12.5 12.5 … … … … … … … … … … … … … … … … … … … … 37 38 39 40 41 42 46.2 46.2 46.2 46.2 46.2 46.2 38.7 38.7 38.7 38.7 38.7 38.7 37.1 37.1 37.1 37.1 37.1 37.1 36.4 36.4 36.4 36.4 36.4 36.4 34.3 34.3 34.3 34.3 34.3 34.3 28.0 28.0 28.0 28.0 28.0 28.0 21.8 21.8 21.8 21.8 21.8 21.8 15.6 15.6 15.6 15.6 15.6 15.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 43 44 45 41.4 41.4 41.4 35.2 35.2 35.2 33.6 33.6 33.6 33.1 33.1 33.1 32.3 32.3 32.3 … 28.0 28.0 … 21.8 21.8 … 15.6 15.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 176 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 4 5 6 7 8 9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 17 18 19 20 21 22 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 23 24 25 26 27 28 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 30 31 32 33 34 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 35 36 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 37 38 39 40 41 42 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 43 44 45 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 177 (10) (10) (10) (10) (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 … … … … Smls. pipe Smls. tube Smls. cond. tube Smls. U-bend tube SB-42 SB-75 SB-111 SB-395 … … … … C12000 C12000 C12000 C12000 H55 H55 H55 H55 5 6 7 … … … Smls. pipe Smls. tube Smls. cond. tube SB-42 SB-75 SB-111 … … … C12000 C12000 C12000 H80 H80 H80 8 9 10 11 12 … … … … … Smls. tube Smls. tube Smls. pipe Finned tube Wld. cond. tube SB-75 SB-75 SB-42 SB-359 SB-543 … … … … … C12200 C12200 C12200 C12200 C12200 O50 O60 O61 O61 W061 13 14 15 16 17 18 … … … … … … Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip SB-152 SB-152 SB-152 SB-152 SB-152 SB-152 … … … … … … C12200 C12200 C12200 C12200 C12200 C12200 H00 H01 H02 H03 H04 O25 19 20 21 22 23 24 … … … … … … Wld. cond. tube Smls. pipe Smls. tube Smls. cond. tube Finned tube Smls. U-bend tube SB-543 SB-42 SB-75 SB-111 SB-359 SB-395 … … … … … … C12200 C12200 C12200 C12200 C12200 C12200 WC55 H55 H55 H55 H55 H55 25 26 27 … … … Smls. pipe Smls. cond. tube Smls. tube SB-42 SB-75 SB-111 … … … C12200 C12200 C12200 H80 H80 H80 28 29 30 31 32 33 … … … … … … Plate, sheet, strip, bar Plate, sheet, strip, bar Plate, sheet, strip, bar Plate, sheet, strip, bar Plate, sheet, strip, bar Plate, sheet, strip, bar SB-152 SB-152 SB-152 SB-152 SB-152 SB-152 … … … … … … C12300 C12300 C12300 C12300 C12300 C12300 H00 H01 H02 H03 H04 O25 34 35 36 37 … … … … Plate, sheet, strip Smls. cond. tube Smls. U-bend tube Smls. cond. tube SB-152 SB-111 SB-395 SB-111 … … … … C14200 C14200 C14200 C14200 O25 H55 H55 H80 38 39 40 41 … … … … Smls. cond. tube Smls. U-bend tube Wld. cond. tube Wld. cond. tube SB-111 SB-395 SB-543 SB-543 … … … … C19200 C19200 C19400 C19400 O61 O61 WO61 WC55 42 43 44 … … … Smls. pipe Smls. tube Smls. red brass tube SB-43 SB-135 SB-135 … … … C23000 C23000 C23000 H58 O50 O60 Line No. (a) (a) (a) 178 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Min. Tensile Strength, MPa Min. Yield Strength, MPa Line No. Size/Thickness, mm P-No. 1 2 3 4 50 < DN ≤ 300 … < 75 < 50 31 31 31 31 250 250 250 250 5 6 7 6 < DN ≤ 50 … < 75 31 31 31 8 9 10 11 12 … … 6 < DN ≤ 50 … … 13 14 15 16 17 18 Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) External Pressure Chart No. I III VIII-1 XII 205 205 205 205 204 204 NP NP 204 204 (Cl. 3 only) 204 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFC-6 NFC-6 NFC-6 NFC-6 G1, W9, W10 G1, G9, W9, W10 G9, W9 W9 310 310 310 275 275 275 204 204 NP 149 177 (Cl. 3 only) 149 204 204 204 204 204 204 NFC-6 NFC-6 NFC-6 G1, G6, T4, W9, W10 G1, G9, T4, W9, W10 G9, T4, W9 31 31 31 31 31 205 205 205 205 205 62 62 62 62 62 NP 204 204 NP NP 149 149 149 149 (Cl. 3 only) 149 (Cl. 3 only) 204 NP 204 204 204 204 NP 204 NP 204 NFC-7 NFC-1 NFC-1 NFC-1 NFC-1 T3 G1, T3, W10 G1, T3, W10 G1, T3, W10 G14, W11 … … … … … … 31 31 31 31 31 31 205 205 205 205 205 205 69 69 69 69 69 69 NP NP NP NP NP NP 149 149 149 149 149 149 204 204 204 204 204 204 204 204 204 204 204 204 NFC-1 NFC-1 NFC-1 NFC-1 NFC-1 NFC-1 T2 T2 T2 T2 T2 T2 19 20 21 22 23 24 … 50 < DN ≤ 300 … < 75 … < 50 31 31 31 31 31 31 220 250 250 250 250 250 100 205 205 205 205 205 NP 204 204 NP NP NP 149 (Cl. 3 only) 204 204 (Cl. 3 only) 204 149 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 NP 204 NFC-1 NFC-6 NFC-6 NFC-6 NFC-6 NFC-6 G14, W3 G1, W9, W10 G1, G9, W9, W10 G9, W9 G1, G9, W9, W10 W9 25 26 27 6 < DN ≤ 75 < 100 < 75 31 31 31 310 310 310 275 275 275 204 204 NP 149 177 (Cl. 3 only) 149 204 204 204 204 204 204 NFC-6 NFC-6 NFC-6 G1, G6, T4, W9, W10 G1, G9, T4, W9, W10 G9, T4, W9 28 29 30 31 32 33 … … … … … … 31 31 31 31 31 31 205 205 205 205 205 205 69 69 69 69 69 69 NP NP NP NP NP NP 149 149 149 149 149 149 204 204 204 204 204 204 204 204 204 204 204 204 NFC-1 NFC-1 NFC-1 NFC-1 NFC-1 NFC-1 T2 T2 T2 T2 T2 T2 34 35 36 37 … < 75 … < 75 31 31 31 31 205 250 250 310 69 205 205 275 NP NP NP NP 149 (Cl. 3 only) 204 204 (Cl. 3 only) 149 NP 204 204 204 NP 204 204 204 NFC-1 NFC-6 NFC-6 NFC-6 T2 G9, W9 W9 G9, T4, W9 38 39 40 41 < 75 … … … 31 31 31 31 260 260 310 310 83 83 100 150 NP NP NP NP NP NP NP 149 (Cl. 3 only) 149 149 204 204 149 149 204 204 NFC-1 NFC-1 NFC-5 NFC-5 … … G14, G15 G14, G15 42 43 44 … … … 32 32 32 275 275 275 83 83 83 232 NP NP 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 232 NP 232 232 NP 232 NFC-1 NFC-1 NFC-1 G1, T3, W10 … T3 179 Notes (a) (a) (a) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (a) (a) (a) Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 71.0 71.0 71.0 71.0 71.0 71.0 71.0 71.0 71.0 71.0 71.0 71.0 70.9 70.9 70.9 70.9 68.8 68.8 68.8 68.8 67.0 67.0 67.0 67.0 65.1 65.1 65.1 65.1 63.3 63.3 63.3 63.3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.8 88.8 88.8 86.0 86.0 86.0 82.1 82.1 82.1 39.8 39.8 39.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 8 9 10 11 12 41.4 41.4 41.4 41.4 35.2 35.2 35.2 35.2 35.2 29.7 33.6 33.6 33.6 33.6 28.3 33.1 33.1 33.1 33.1 28.3 32.3 32.3 32.3 32.3 27.5 28.0 28.0 28.0 28.0 23.8 21.8 21.8 21.8 21.8 18.8 15.6 15.6 15.6 15.6 13.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 13 14 15 16 17 18 46.2 46.2 46.2 46.2 46.2 46.2 38.7 38.7 38.7 38.7 38.7 38.7 37.1 37.1 37.1 37.1 37.1 37.1 36.4 36.4 36.4 36.4 36.4 36.4 34.3 34.3 34.3 34.3 34.3 34.3 28.0 28.0 28.0 28.0 28.0 28.0 21.8 21.8 21.8 21.8 21.8 21.8 15.6 15.6 15.6 15.6 15.6 15.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 19 20 21 22 23 24 53.8 71.0 71.0 71.0 71.0 71.0 53.8 71.0 71.0 71.0 71.0 71.0 53.8 71.0 71.0 71.0 71.0 71.0 53.6 70.9 70.9 70.9 70.9 70.9 51.7 68.8 68.8 68.8 68.8 68.8 50.7 67.0 67.0 67.0 67.0 67.0 24.4 65.1 65.1 65.1 65.1 65.1 … 63.3 63.3 63.3 63.3 63.3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.9 88.8 88.8 88.8 86.0 86.0 86.0 82.1 82.1 82.1 39.8 39.8 39.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 31 32 33 46.2 46.2 46.2 46.2 46.2 46.2 38.7 38.7 38.7 38.7 38.7 38.7 37.1 37.1 37.1 37.1 37.1 37.1 36.4 36.4 36.4 36.4 36.4 36.4 34.3 34.3 34.3 34.3 34.3 34.3 28.0 28.0 28.0 28.0 28.0 28.0 21.8 21.8 21.8 21.8 21.8 21.8 15.6 15.6 15.6 15.6 15.6 15.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 37 46.2 71.0 71.0 88.9 38.7 71.0 71.0 88.9 37.1 71.0 71.0 88.9 36.4 70.9 70.9 88.8 34.3 68.8 68.8 86.0 … 67.0 67.0 82.1 … 65.1 65.1 39.8 … 63.3 63.3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 38 39 40 41 55.2 55.2 58.6 75.2 49.0 49.0 57.9 75.2 45.7 45.7 57.0 74.7 43.9 43.9 55.6 73.0 42.7 42.7 53.7 69.2 … … 52.6 54.1 … … 43.5 43.0 … … 33.0 32.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 42 43 44 55.2 55.2 55.2 55.2 55.2 55.2 55.2 55.2 55.2 55.2 55.2 55.2 55.1 55.2 55.1 48.9 … 48.9 37.2 … 37.2 19.4 … 19.4 0.422 … 0.422 … … … … … … … … … … … … … … … … … … … … … … … … … … … 180 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 8 9 10 11 12 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 13 14 15 16 17 18 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 19 20 21 22 23 24 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 31 32 33 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 37 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 38 39 40 41 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 42 43 44 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 181 (a) (a) (a) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 5 6 … … … … … … Smls. pipe Smls. cond. tube Smls. tube Wld. cond. tube Wld. cond. tube Smls. tube SB-43 SB-111 SB-395 SB-543 SB-543 SB-111 … … … … … … C23000 C23000 C23000 C23000 C23000 C28000 O61 O61 O61 WO61 WC55 O61 7 8 9 10 11 12 … … … … … … Plate Plate Plate Plate Plate Plate SB-171 SB-171 SB-171 SB-171 SB-171 SB-171 … … … … … … C36500 C36500 C36500 C36500 C36500 C36500 M20 O25 M20 O25 M20 O25 13 14 15 16 … … … … Forgings, brass Forgings, brass Forgings, brass Forgings, brass SB-283 SB-283 SB-283 SB-283 … … … … C37700 C37700 C37700 C37700 M10 M11 O20 TQ50 17 18 19 20 … … … … Forgings, brass Forgings, brass Forgings, brass Forgings, brass SB-283 SB-283 SB-283 SB-283 … … … … C37700 C37700 C37700 C37700 M10 M11 O20 TQ50 21 22 23 24 25 26 … … … … … … Plate Plate Smls. cond. tube Finned tube Smls. U-bend tube Wld. cond. tube SB-171 SB-171 SB-111 SB-359 SB-395 SB-543 … … … … … … C44300 C44300 C44300 C44300 C44300 C44300 M20 O25 O61 O61 O61 WO61 27 28 29 30 31 32 … … … … … … Plate Plate Smls. cond. tube Finned tube Smls. U-bend tube Wld. cond. tube SB-171 SB-171 SB-111 SB-359 SB-395 SB-543 … … … … … … C44400 C44400 C44400 C44400 C44400 C44400 M20 O25 O61 O61 O61 WO61 33 34 35 36 37 38 … … … … … … Plate Plate Smls. cond. tube Finned tube Smls. U-bend tube Wld. cond. tube SB-171 SB-171 SB-111 SB-359 SB-395 SB-543 … … … … … … C44500 C44500 C44500 C44500 C44500 C44500 M20 O25 O61 O61 O61 WO61 39 40 41 42 … … … … Plate Plate Plate Plate SB-171 SB-171 SB-171 SB-171 … … … … C46400 C46400 C46400 C46400 M20 O25 M20 O25 Line No. (a) (a) (a) 182 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes … < 75 … … … … 32 32 32 32 32 32 275 275 275 275 290 345 83 83 83 83 140 140 232 NP NP NP NP 204 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 177 (Cl. 3 only) 232 232 232 232 232 204 232 232 232 232 232 204 NFC-1 NFC-1 NFC-1 NFC-1 NFC-2 NFC-3 G1, T3, W10 T3 T3 G14, G15, T3 G14, G15, T3 G1, G6, T3, W10 7 8 9 10 11 12 89 < t ≤ 125 89 < t ≤ 125 50 < t ≤ 89 50 < t ≤ 89 ≤ 50 ≤ 50 32 32 32 32 32 32 275 275 310 310 345 345 83 83 100 100 140 140 NP NP NP NP NP NP 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 204 204 NFC-2 NFC-2 NFC-2 NFC-2 NFC-2 NFC-2 G7, T4 G7, T4 T4 T4 T3 T3 13 14 15 16 > 38 > 38 > 38 > 38 … … … … 315 315 315 315 100 100 100 100 NP NP NP NP NP NP NP NP 93 93 93 93 93 93 93 93 NFC-2 NFC-2 NFC-2 NFC-2 W14 W14 W14 W14 17 18 19 20 ≤ 38 ≤ 38 ≤ 38 ≤ 38 … … … … 345 345 345 345 125 125 125 125 NP NP NP NP NP NP NP NP 93 93 93 93 93 93 93 93 NFC-2 NFC-2 NFC-2 NFC-2 W14 W14 W14 W14 21 22 23 24 25 26 ≤ 100 ≤ 100 < 75 … … … 32 32 32 32 32 32 310 310 310 310 310 310 100 100 100 100 100 100 NP NP 232 NP NP NP 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) NP 232 232 232 232 232 232 232 232 232 NP 232 232 NFC-2 NFC-2 NFC-2 NFC-2 NFC-2 NFC-2 T3 T3 G1, G6, T3, W10 G1, G6, T3, W10 T3 G7, G14, G15, T3 27 28 29 30 31 32 ≤ 100 ≤ 100 < 75 … … … 32 32 32 32 32 32 310 310 310 310 310 310 100 100 100 100 100 100 NP NP 232 NP NP NP 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) NP 232 232 232 232 232 232 232 232 232 NP 232 232 NFC-2 NFC-2 NFC-2 NFC-2 NFC-2 NFC-2 T3 T3 G1, G6, T3, W10 G1, G6, T3, W10 T3 G7, G14, G15, T3 33 34 35 36 37 38 ≤ 100 ≤ 100 < 75 … … … 32 32 32 32 32 32 310 310 310 310 310 310 100 100 100 100 100 100 NP NP 232 NP NP NP 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) NP 232 232 232 232 232 232 232 232 232 NP 232 232 NFC-2 NFC-2 NFC-2 NFC-2 NFC-2 NFC-2 T3 T3 G1, G6, T3, W10 G1, G6, T3, W10 T3 G7, G14, G15, T3 39 40 41 42 75 < t ≤ 125 75 < t ≤ 125 ≤ 75 ≤ 75 32 32 32 32 345 345 345 345 125 125 140 140 NP NP NP NP 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 204 204 204 204 204 204 204 204 NFC-2 NFC-2 NFC-2 NFC-2 T3 T3 T3 T3 1 2 3 4 5 6 183 (a) (a) (a) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (a) (a) (a) Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 5 6 55.2 55.2 55.2 46.9 46.9 91.7 55.2 55.2 55.2 46.9 46.9 91.7 55.2 55.2 55.2 46.9 46.9 91.7 55.2 55.2 55.2 46.9 46.9 91.7 55.1 55.1 55.1 46.8 46.8 91.6 48.9 48.9 48.9 41.9 41.9 76.3 37.2 37.2 37.2 32.0 32.0 42.3 19.4 19.4 19.4 16.6 16.6 17.6 0.422 0.422 0.422 0.134 0.134 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 10 11 12 55.2 55.2 68.9 68.9 91.7 91.7 55.2 55.2 68.9 68.9 91.7 91.7 55.2 55.2 68.9 68.9 91.7 91.7 55.2 55.2 68.9 68.9 91.7 91.7 55.2 55.2 68.9 68.9 91.6 91.6 55.2 55.2 68.9 68.9 76.3 76.3 40.3 40.3 43.0 43.0 42.3 42.3 22.3 22.3 11.7 11.7 17.6 17.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 13 14 15 16 68.9 68.9 68.9 68.9 64.9 64.9 64.9 64.9 61.4 61.4 61.4 61.4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 17 18 19 20 82.7 82.7 82.7 82.7 78.0 78.0 78.0 78.0 73.7 73.7 73.7 73.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 24 25 26 68.9 68.9 68.9 68.9 68.9 58.6 68.9 68.9 68.9 68.9 68.9 58.6 68.9 68.9 68.9 68.9 68.9 58.6 68.9 68.9 68.9 68.9 68.9 58.6 68.9 68.9 68.9 68.9 68.9 58.6 68.3 68.3 68.3 68.3 68.3 57.8 29.4 29.4 29.4 29.4 29.4 25.1 16.4 16.4 16.4 16.4 16.4 14.0 9.10 9.10 9.10 9.10 9.10 6.04 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 27 28 29 30 31 32 68.9 68.9 68.9 68.9 68.9 58.6 68.9 68.9 68.9 68.9 68.9 58.6 68.9 68.9 68.9 68.9 68.9 58.6 68.9 68.9 68.9 68.9 68.9 58.6 68.9 68.9 68.9 68.9 68.9 58.6 68.3 68.3 68.3 68.3 68.3 57.8 29.4 29.4 29.4 29.4 29.4 25.1 16.4 16.4 16.4 16.4 16.4 14.0 9.10 9.10 9.10 9.10 9.10 6.04 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 33 34 35 36 37 38 68.9 68.9 68.9 68.9 68.9 58.6 68.9 68.9 68.9 68.9 68.9 58.6 68.9 68.9 68.9 68.9 68.9 58.6 68.9 68.9 68.9 68.9 68.9 58.6 68.9 68.9 68.9 68.9 68.9 58.6 68.3 68.3 68.3 68.3 68.3 57.8 29.4 29.4 29.4 29.4 29.4 25.1 16.4 16.4 16.4 16.4 16.4 14.0 9.10 9.10 9.10 9.10 9.10 6.04 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 39 40 41 42 82.7 82.7 91.7 91.7 82.7 82.7 91.7 91.7 82.7 82.7 91.7 91.7 82.7 82.7 91.7 91.7 82.2 82.2 91.0 91.0 46.0 46.0 46.4 46.4 20.6 20.6 20.3 20.3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 184 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 10 11 12 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 13 14 15 16 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 17 18 19 20 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 24 25 26 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 27 28 29 30 31 32 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 33 34 35 36 37 38 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 39 40 41 42 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 185 (a) (a) (a) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 5 6 … … … … … … Plate Plate Plate Plate Smls. cond. tube Smls. U-bend tube SB-171 SB-171 SB-171 SB-171 SB-111 SB-395 … … … … … … C46500 C46500 C46500 C46500 C60800 C60800 M20 O25 M20 O25 O61 O61 7 8 9 … … … Plate Plate Plate, sheet SB-171 SB-171 SB-169 … … … C61400 C61400 C61400 M20 O25 O25 or O60 10 11 12 13 … … … … Plate Plate Plate, sheet Plate, sheet SB-171 SB-171 SB-169 SB-169 … … … … C61400 C61400 C61400 C61400 M20 O25 O25 or O60 O25 or O60 14 15 16 17 18 19 … … … … … … Plate Plate Plate Plate Plate Plate SB-171 SB-171 SB-171 SB-171 SB-171 SB-171 … … … … … … C63000 C63000 C63000 C63000 C63000 C63000 M20 O25 M20 O25 M20 O25 20 21 22 23 … … … … Forgings Forgings Forgings Forgings SB-283 SB-283 SB-283 SB-283 … … … … C64200 C64200 C64200 C64200 M10 M11 O20 TQ50 24 25 26 27 28 29 … … … … … … Forgings Forgings Forgings Forgings Bar, rod Bar, rod SB-283 SB-283 SB-283 SB-283 SB-98 SB-98 … … … … … … C64200 C64200 C64200 C64200 C65100 C65100 M10 M11 O20 TQ50 O60 H02 30 31 32 33 … … … … Smls. pipe & tube Plate, sheet Bar, rod Bar, rod SB-315 SB-96 SB-98 SB-98 … … … … C65500 C65500 C65500 C65500 O61 O61 O60 H02 34 35 36 37 38 … … … … … Bar, rod Bar, rod Smls. cond. tube Smls. U-bend tube Wld. cond. tube SB-98 SB-98 SB-111 SB-395 SB-543 … … … … … C66100 C66100 C68700 C68700 C68700 O60 H02 O61 O61 WO61 39 40 41 … … … Wld. tube Smls. cond. tube Smls. cond. tube SB-543 SB-111 SB-111 … … … C70400 C70400 C70400 WO61 O61 H55 42 43 44 … … … Smls. pipe & tube Wld. pipe Bar, rod SB-466 SB-467 SB-151 … … … C70600 C70600 C70600 O60 WO61 O60 Line No. 186 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 6 75 < t ≤ 125 75 < t ≤ 125 ≤ 75 ≤ 75 … … 32 32 32 32 35 35 345 345 345 345 345 345 125 125 140 140 130 130 NP NP NP NP NP NP 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 149 (Cl. 3 only) 204 204 204 204 260 260 204 204 204 204 260 260 NFC-2 NFC-2 NFC-2 NFC-2 NFC-3 NFC-2 T3 T3 T3 T3 G6, T4 T4 7 8 9 50 < t ≤ 125 50 < t ≤ 125 50 < t ≤ 125 35 35 35 450 450 450 195 195 195 NP NP NP 260 (Cl. 3 only) 260 (Cl. 3 only) 260 (Cl. 3 only) 260 260 260 260 260 260 NFC-8 NFC-8 NFC-8 … … … 10 11 12 13 ≤ 50 ≤ 50 13 < t ≤ 50 ≤ 13 35 35 35 35 485 485 485 495 205 205 205 220 NP NP NP NP 260 (Cl. 3 only) 260 (Cl. 3 only) 260 (Cl. 3 only) 232 (Cl. 3 only) 260 260 260 260 260 260 260 260 NFC-8 NFC-8 NFC-8 NFC-8 … … … … 14 15 16 17 18 19 89 < t ≤ 125 89 < t ≤ 125 50 < t ≤ 89 50 < t ≤ 89 ≤ 50 ≤ 50 35 35 35 35 35 35 550 550 585 585 620 620 205 205 230 230 250 250 NP NP NP NP NP NP 260 (Cl. 3 only) 260 (Cl. 3 only) 260 (Cl. 3 only) 260 (Cl. 3 only) 260 (Cl. 3 only) 260 (Cl. 3 only) 371 371 371 371 371 371 343 343 343 343 343 343 NFC-8 NFC-8 NFC-8 NFC-8 NFC-8 NFC-8 T6 T6 T6 T6 T6 T6 20 21 22 23 > 38 > 38 > 38 > 38 … … … … 470 470 470 470 160 160 160 160 NP NP NP NP NP NP NP NP 260 260 260 260 260 260 260 260 NFC-3 NFC-3 NFC-3 NFC-3 G10, W14 G10, W14 G10, W14 G10, W14 24 25 26 27 28 29 ≤ 38 ≤ 38 ≤ 38 ≤ 38 … … … … … … 33 33 485 485 485 485 275 380 170 170 170 170 83 140 NP NP NP NP NP NP NP NP NP NP 149 149 260 260 260 260 177 177 260 260 260 260 177 177 NFC-3 NFC-3 NFC-3 NFC-3 NFC-1 NFC-2 W14 W14 W14 W14 G17 G17, W9 30 31 32 33 … ≤ 50 … … 33 33 33 33 345 345 360 485 100 125 100 260 NP NP NP NP 149 (Cl. 3 only) 149 (Cl. 3 only) 149 149 204 177 177 177 204 177 177 177 NFC-2 NFC-2 NFC-2 NFC-2 G17 G17 G17 G17 34 35 36 37 38 … … < 75 … … 33 33 32 32 32 360 485 345 345 345 100 260 125 125 125 NP NP NP NP NP 149 149 149 (Cl. 3 only) 149 (Cl. 3 only) NP 177 177 232 232 232 177 177 232 232 232 NFC-2 NFC-2 NFC-2 NFC-2 NFC-2 G17 G17, W9 … … G14, G15 39 40 41 … < 75 < 75 34 34 34 260 260 275 83 83 205 NP NP NP NP 66 (Cl. 3 only) 66 (Cl. 3 only) 66 66 66 66 66 66 NFC-2 NFC-2 NFC-2 G14, G15 … G7, W9 42 43 44 … > 114 … 34 34 34 260 260 260 90 90 100 NP NP NP 204 232 (Cl. 3 only) 93 316 316 NP 316 316 NP NFC-3 NFC-3 NFC-3 T6 G14, G15 … 187 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 5 6 82.7 82.7 91.7 91.7 87.6 87.6 82.7 82.7 91.7 91.7 84.2 84.2 82.7 82.7 91.7 91.7 84.2 84.2 82.7 82.7 91.7 91.7 84.2 84.2 82.2 82.2 91.0 91.0 82.5 82.5 46.0 46.0 46.4 46.4 70.4 70.4 20.6 20.6 20.3 20.3 45.2 45.2 … … … … 30.4 30.4 … … … … 19.0 19.0 … … … … 6.23 6.23 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 128 128 128 128 128 128 127 127 127 126 126 126 125 125 125 125 125 125 124 124 124 121 121 121 118 118 118 115 115 115 … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 138 138 138 142 137 137 137 142 136 136 136 142 136 136 136 142 134 134 134 142 134 134 134 142 133 133 133 140 131 131 131 135 128 128 128 131 124 124 124 127 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 17 18 19 138 138 152 152 165 165 137 137 150 150 164 164 135 135 148 148 162 162 133 133 146 146 160 160 132 132 145 145 158 158 131 131 144 144 157 157 130 130 143 143 156 156 128 128 140 140 153 153 124 124 137 137 151 151 117 117 123 123 128 128 99.3 99.3 97.9 97.9 96.7 96.7 73.8 73.8 74.1 74.1 74.4 74.4 54.7 54.7 54.7 54.7 54.6 54.6 38.9 38.9 38.9 38.9 38.9 38.9 … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 23 105 105 105 105 93.2 93.2 93.2 93.2 88.7 88.7 88.7 88.7 86.1 86.1 86.1 86.1 86.1 86.1 86.1 86.1 82.9 82.9 82.9 82.9 78.1 78.1 78.1 78.1 58.1 58.1 58.1 58.1 40.8 40.8 40.8 40.8 27.6 27.6 27.6 27.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 24 25 26 27 28 29 115 115 115 115 55.2 91.7 100 100 100 100 55.2 91.7 95.7 95.7 95.7 95.7 55.2 91.7 93.0 93.0 93.0 93.0 54.9 86.2 93.0 93.0 93.0 93.0 47.8 68.2 89.9 89.9 89.9 89.9 35.3 55.9 79.2 79.2 79.2 79.2 22.8 43.7 57.5 57.5 57.5 57.5 … … 41.5 41.5 41.5 41.5 … … 25.1 25.1 25.1 25.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 30 31 32 33 68.9 82.7 68.9 138 68.9 82.1 68.9 138 68.9 80.8 68.9 138 68.9 80.2 68.5 138 67.6 67.9 67.7 137 35.4 36.7 36.9 74.0 34.4 5.30 5.65 9.88 34.4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 37 38 68.9 138 82.7 82.7 70.3 68.9 138 82.1 82.1 69.6 68.9 138 81.1 81.1 68.7 68.9 138 80.7 80.7 68.3 68.5 137 80.2 80.2 67.9 37.0 74.0 47.2 47.2 39.9 4.94 9.88 24.8 24.8 20.5 … … 14.9 14.9 11.8 … … 5.88 5.88 4.01 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 39 40 41 46.9 55.2 68.9 46.9 55.2 68.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 42 43 44 60.0 51.0 68.9 57.9 49.7 67.2 56.2 47.9 65.2 54.9 46.8 … 53.7 46.2 … 53.1 44.9 … 51.9 44.2 … 51.1 43.6 … 50.8 43.1 … 49.2 41.6 … 45.8 35.5 … 38.8 26.2 … … … … … … … … … … … … … … … … … … … 188 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 17 18 19 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 23 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 24 25 26 27 28 29 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 30 31 32 33 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 37 38 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 39 40 41 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 42 43 44 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 189 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 … … … Plate Plate, sheet Plate SB-171 SB-171 SB-171 … … … C70600 C70600 C70600 M20 M20 M20 4 5 6 … … … Plate Plate, sheet Plate SB-171 SB-171 SB-171 … … … C70600 C70600 C70600 O25 O25 O25 7 8 9 10 … … … … Smls. cond. tube Smls. cond. tube Finned tube Smls. U-bend tube SB-111 SB-111 SB-359 SB-395 … … … … C70600 C70600 C70600 C70600 O61 O61 O61 O61 11 12 13 … … … Wld. pipe Wld. tube Finned wld. tube SB-467 SB-543 SB-956 … … … C70600 C70600 C70600 WO61 WO61 WO61 14 15 16 17 18 … … … … … Wld. pipe Smls. tube Wld. tube Finned wld. tube Wld. pipe SB-467 SB-111 SB-543 SB-956 SB-467 … … … … … C70600 C70600 C70600 C70600 C70600 WM50 H55 WC55 WC55 Wld. fr. cold rld. strip 19 20 21 22 … … … … Smls. tube Smls. cond. tube Finned tube Smls. tube SB-466 SB-111 SB-359 SB-395 … … … … C71000 C71000 C71000 C71000 O60 O61 O61 O61 23 24 25 … … … Wld. pipe Plate, sheet Plate, sheet SB-467 SB-171 SB-171 … … … C71500 C71500 C71500 WO61 M20 O25 26 27 28 … … … Plate, sheet Plate, sheet Wld. pipe SB-171 SB-171 SB-467 … … … C71500 C71500 C71500 M20 O25 WO61 29 30 31 32 … … … … Smls. pipe & tube Smls. cond. tube Finned tube Smls. U-bend tube SB-466 SB-111 SB-359 SB-395 … … … … C71500 C71500 C71500 C71500 O60 O61 O61 O61 33 34 35 36 … … … … Wld. cond. tube Finned wld. cond. tube Smls. cond. tube Smls. U-bend tube SB-543 SB-956 SB-111 SB-395 … … … … C71500 C71500 C71500 C71500 WO61 WO61 HR50 HR58 37 38 39 40 … … … … Smls. cond. tube Castings Castings Castings SB-111 SB-62 SB-61 SB-584 … … … … C72200 C83600 C92200 C92200 O61 M01 M01 M01 Line No. (10) 190 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 ≤ 125 ≤ 125 ≤ 125 34 34 34 275 275 275 100 100 100 NP NP NP 204 232 (Cl. 3 only) NP NP NP 316 NP NP 316 NFC-3 NFC-3 NFC-3 … … T5 4 5 6 ≤ 125 ≤ 125 ≤ 125 34 34 34 275 275 275 100 100 100 NP NP NP 204 232 (Cl. 3 only) NP NP NP 316 NP NP 316 NFC-3 NFC-3 NFC-3 … … T5 7 8 9 10 … … … … 34 34 34 34 275 275 275 275 100 100 100 100 316 NP NP NP 204 232 (Cl. 3 only) 232 (Cl. 3 only) 232 (Cl. 3 only) NP 316 316 316 NP 316 NP 316 NFC-3 NFC-3 NFC-3 NFC-3 G1, T5, W10 T5 G1, T5, W10 T5 11 12 13 ≤ 114 … … 34 34 34 275 275 275 100 100 100 NP NP NP 232 (Cl. 3 only) 232 (Cl. 3 only) NP 316 316 316 316 316 NP NFC-3 NFC-3 NFC-3 G14, G15 G14, G15 G14 14 15 16 17 18 ≤ 114 … … … ≤ 114 34 34 34 34 34 310 310 310 310 370 205 240 240 240 310 NP NP NP NP NP NP 232 (Cl. 3 only) 232 (Cl. 3 only) NP NP 316 316 316 316 316 316 316 316 NP 316 NFC-3 NFC-3 NFC-3 NFC-3 NFC-3 G14 T5 G14, G15 G14 G14 19 20 21 22 … … … … 34 34 34 34 310 310 310 310 110 110 110 110 NP 371 NP NP 371 (Cl. 3 only) 371 (Cl. 3 only) 371 (Cl. 3 only) 371 (Cl. 3 only) 371 371 371 371 343 343 NP 343 NFC-3 NFC-3 NFC-3 NFC-3 T7 G1, T7, W10 G1, T7, W10 T7 23 24 25 > 114 64 < t ≤ 125 64 < t ≤ 125 34 34 34 310 310 310 100 125 125 NP NP NP 316 (Cl. 3 only) 371 371 NP 371 371 NP 343 343 NFC-3 NFC-4 NFC-4 G14 … … 26 27 28 ≤ 64 ≤ 64 ≤ 114 34 34 34 345 345 345 140 140 140 NP NP NP 371 371 316 (Cl. 3 only) 371 371 NP 343 343 NP NFC-4 NFC-4 NFC-4 … … G14 29 30 31 32 … … … … 34 34 34 34 360 360 360 360 125 125 125 125 NP 371 NP NP 371 371 371 (Cl. 3 only) 371 (Cl. 3 only) 371 371 371 371 343 343 NP 343 NFC-4 NFC-4 NFC-4 NFC-4 … G1, W10 G1, W10 … 33 34 35 36 … … ≤ 79 … 34 34 34 34 360 360 495 495 125 125 345 345 NP NP NP NP 316 (Cl. 3 only) NP 371 371 316 316 427 427 316 NP 343 343 NFC-4 NFC-4 NFC-4 NFC-8 G14, G15 G14 T9, W9 T9, W9 37 38 39 40 ≤ 50 … … … 34 … … … 310 205 235 235 110 97 110 110 NP 232 288 NP NP 232 (Cl. 3 only) 260 (Cl. 3 only) 260 (Cl. 3 only) 66 232 288 288 66 232 288 288 NFC-3 NFC-1 NFN-1 NFN-1 … G1, G3, G15, W10, W14 G1, G3, G15, W10, W14 G15 191 (10) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (10) Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 68.9 68.9 68.9 67.3 66.9 66.9 65.1 65.2 65.2 63.4 63.9 63.9 62.0 62.0 62.0 61.0 60.7 60.7 60.1 60.1 60.1 59.2 59.1 59.1 … 56.8 56.8 … … 51.7 … … 45.2 … … 39.0 … … … … … … … … … … … … … … … … … … 4 5 6 68.9 68.9 68.9 67.3 66.9 66.9 65.1 65.2 65.2 63.4 63.9 63.9 62.0 62.0 62.0 61.0 60.7 60.7 60.1 60.1 60.1 59.2 59.1 59.1 … 56.8 56.8 … … 51.7 … … 45.2 … … 39.0 … … … … … … … … … … … … … … … … … … 7 8 9 10 68.9 68.9 68.9 68.9 66.9 66.9 66.9 66.9 65.2 65.2 65.2 65.2 63.9 63.9 63.9 63.9 62.0 62.0 62.0 62.0 60.7 60.7 60.7 60.7 60.1 60.1 60.1 60.1 59.1 59.1 59.1 59.1 56.8 56.8 56.8 56.8 51.7 51.7 51.7 51.7 45.2 45.2 45.2 45.2 39.0 39.0 39.0 39.0 … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 58.6 58.6 58.6 57.3 57.3 57.3 55.5 55.5 55.5 54.3 54.3 54.3 53.0 53.0 53.0 51.8 51.8 51.8 51.2 51.2 51.2 50.0 50.0 50.0 45.8 45.8 45.8 41.3 41.3 41.3 35.6 35.6 35.6 26.2 26.2 26.2 … … … … … … … … … … … … … … … … … … 14 15 16 17 18 58.6 68.9 58.6 58.6 58.6 57.3 66.9 57.3 57.3 57.3 55.5 65.2 55.5 55.5 55.5 54.3 63.9 54.3 54.3 54.3 53.0 62.0 53.0 53.0 53.0 51.8 60.7 51.8 51.8 51.8 51.2 60.1 51.2 51.2 51.2 50.0 59.1 50.0 50.0 50.0 45.8 56.8 45.8 45.8 45.8 41.3 51.7 41.3 41.3 41.3 35.6 45.2 35.6 35.6 35.6 26.2 39.0 26.2 26.2 26.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 19 20 21 22 73.8 73.8 73.8 73.8 73.1 73.1 73.1 73.1 72.3 72.3 72.3 72.3 71.5 71.5 71.5 71.5 70.3 70.3 70.3 70.3 69.7 69.7 69.7 69.7 68.5 68.5 68.5 68.5 66.7 66.7 66.7 66.7 64.9 64.9 64.9 64.9 62.7 62.7 62.7 62.7 60.0 60.0 60.0 60.0 56.4 56.4 56.4 56.4 51.9 51.9 51.9 51.9 47.6 47.6 47.6 47.6 … … … … … … … … … … … … … … … … 23 24 25 58.6 82.7 82.7 56.6 80.0 80.0 54.8 77.4 77.4 53.6 75.6 75.6 52.4 74.4 74.4 51.8 72.5 72.5 50.5 71.2 71.2 49.8 70.0 70.0 48.8 68.7 68.7 47.8 67.9 67.9 47.3 67.0 67.0 46.6 65.9 65.9 … 65.4 65.4 … 64.7 64.7 … … … … … … … … … … … … 26 27 28 91.7 91.7 77.9 89.0 89.0 75.2 86.4 86.4 73.3 84.5 84.5 71.5 82.6 82.6 70.3 80.8 80.8 69.1 79.5 79.5 67.1 77.7 77.7 66.4 76.3 76.3 65.4 75.1 75.1 64.0 74.1 74.1 63.1 73.6 73.6 62.5 72.8 72.8 … 71.5 71.5 … … … … … … … … … … … … … 29 30 31 32 82.7 82.7 82.7 82.7 80.0 80.0 80.0 80.0 77.4 77.4 77.4 77.4 75.6 75.6 75.6 75.6 74.4 74.4 74.4 74.4 72.5 72.5 72.5 72.5 71.2 71.2 71.2 71.2 70.0 70.0 70.0 70.0 68.7 68.7 68.7 68.7 67.9 67.9 67.9 67.9 67.0 67.0 67.0 67.0 65.9 65.9 65.9 65.9 65.4 65.4 65.4 65.4 64.7 64.7 64.7 64.7 … … … … … … … … … … … … … … … … 33 34 35 36 70.3 70.3 142 142 67.6 67.6 142 142 65.9 65.9 142 142 64.6 64.6 142 142 63.4 63.4 142 142 62.1 62.1 139 139 60.9 60.9 136 136 59.7 59.7 133 133 58.4 58.4 131 131 57.5 57.5 129 129 56.9 56.9 128 128 56.3 56.3 127 127 … … 126 126 … … 123 123 … … 118 118 … … 63.0 63.0 … … 7.30 7.30 … … … … 37 38 39 40 73.8 59.3 66.9 66.9 71.7 59.3 66.9 66.9 … 59.3 66.9 66.9 … 59.1 66.9 66.9 … 57.2 66.9 66.9 … 56.0 66.9 66.9 … 48.4 57.9 57.9 … 47.1 54.0 54.0 … 46.5 50.9 50.9 … … 42.8 42.8 … … 27.3 27.3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … 192 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 4 5 6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 10 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 17 18 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 19 20 21 22 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 23 24 25 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 26 27 28 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 30 31 32 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 33 34 35 36 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 37 38 39 40 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 193 (10) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 … … … … Castings Castings Castings Castings SB-584 SB-148 SB-271 SB-505 … … … … C93700 C95200 C95200 C95200 M01 M01 M02 M07 5 6 7 8 … … … … Castings Castings Castings Castings SB-148 SB-271 SB-369 SB-584 … … … … C95400 C95400 C96200 C97600 M01 M02 M01 M01 9 10 11 12 13 14 99Ni 99Ni 99Ni 99Ni 99Ni 99Ni Smls. pipe & tube Smls. & wld. fittings Bar, rod Smls. pipe & tube Plate, sheet, strip Smls. tube SB-161 SB-366 SB-160 SB-161 SB-162 SB-163 … … … … … … N02200 N02200 N02200 N02200 N02200 N02200 Annealed Annealed Annealed Annealed Annealed Annealed 15 16 17 18 99Ni 99Ni 99Ni 99Ni Plate, sheet, strip Bar, rod Smls. pipe & tube Smls. tube SB-162 SB-160 SB-161 SB-163 … … … … N02200 N02200 N02200 N02200 As rolled Hot rolled Stress rel. Stress rel. 19 20 21 99Ni – Low C 99Ni – Low C 99Ni – Low C Smls. pipe & tube Smls. & wld. fittings Bar, rod SB-161 SB-366 SB-160 … … … N02201 N02201 N02201 Annealed Annealed Hot rolled/ann. 22 23 24 25 26 99Ni – Low C 99Ni – Low C 99Ni – Low C 99Ni – Low C 99Ni – Low C Smls. pipe & tube Smls. tube Plate, sheet, strip Smls. pipe & tube Smls. pipe & tube SB-161 SB-163 SB-162 SB-161 SB-163 … … … … … N02201 N02201 N02201 N02201 N02201 Annealed Annealed Hot rolled/ann. Stress rel. Stress rel. 27 28 29 67Ni – 30Cu 67Ni – 30Cu 67Ni – 30Cu Bar Smls. pipe & tube Forgings SB-164 SB-165 SB-564 … … … N04400 N04400 N04400 Annealed Annealed Annealed 30 31 32 33 67Ni – 30Cu 67Ni – 30Cu 67Ni – 30Cu 67Ni – 30Cu Plate Smls. tube Smls. pipe & tube Smls. & wld. fittings SB-127 SB-163 SB-165 SB-366 … … … … N04400 N04400 N04400 N04400 Annealed Annealed Annealed Annealed 34 35 36 67Ni – 30Cu 67Ni – 30Cu 67Ni – 30Cu Bar Plate Bar, rod SB-164 SB-127 SB-164 … … … N04400 N04400 N04400 Hot worked As rolled Hot worked 37 38 39 67Ni – 30Cu 67Ni – 30Cu 67Ni – 30Cu Bar, rod Smls. tube Smls. pipe & tube SB-164 SB-163 SB-165 … … … N04400 N04400 N04400 Hot worked Stress rel. Stress rel. 40 41 67Ni – 30Cu – S 67Ni – 30Cu – S Bar Bar SB-164 SB-164 … … N04405 N04405 Annealed Hot worked Line No. (10) 194 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 … … … … … 35 35 35 205 450 450 470 83 170 170 180 NP 288 NP NP 204 (SPT) 260 (Cl. 3 only) 260 (Cl. 3 only) 260 (Cl. 3 only) 204 316 316 NP 204 316 316 NP NFC-1 NFC-4 NFC-4 NFC-4 G15, W15 G15 G15 G15 5 6 7 8 … … … … 35 35 34 … 515 515 310 275 205 205 170 120 288 NP NP NP 232 (Cl. 3 only) 232 (Cl. 3 only) 93 (Cl. 3 only) NP 316 NP NP 149 316 NP NP 149 NFC-4 NFC-4 NFC-4 NFC-1 G15, W8 G15, W8 G15 G15, W15 9 10 11 12 13 14 > 125 O.D. … … ≤ 125 O.D. … … 41 41 41 41 41 41 380 380 380 380 380 380 83 83 100 100 100 100 NP NP NP NP NP NP 316 (Cl. 3 only) NP 316 (Cl. 3 only) 316 (Cl. 3 only) 316 (Cl. 3 only) 316 (Cl. 3 only) 316 316 316 316 316 316 316 316 316 316 316 316 NFN-2 NFN-2 NFN-2 NFN-2 NFN-2 NFN-2 … W12 … … … … 15 16 17 18 … … … … 41 41 41 41 380 415 450 450 140 100 275 275 NP NP NP NP 316 (Cl. 3 only) 316 (Cl. 3 only) 316 (Cl. 3 only) 316 (Cl. 3 only) 316 316 316 316 316 316 316 316 NFN-2 NFN-2 NFN-25 NFN-25 G20 … … … 19 20 21 > 125 O.D. … … 41 41 41 345 345 345 69 69 69 NP NP NP 427 (Cl. 3 only) NP 427 (Cl. 3 only) 649 621 649 343 343 343 NFN-1 NFN-1 NFN-1 T10 T10, W12 T10 22 23 24 25 26 ≤ 125 O.D. … … … … 41 41 41 41 41 345 345 345 415 415 83 83 83 205 205 NP NP NP NP NP 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 316 (Cl. 3 only) 427 (Cl. 3 only) 649 649 649 316 482 343 343 343 316 343 NFN-1 NFN-1 NFN-1 NFN-1 NFN-1 T9 T9 T9 … … 27 28 29 … > 125 O.D. … 42 42 42 485 485 485 170 170 170 NP NP NP 427 427 427 482 482 482 343 343 343 NFN-3 NFN-3 NFN-3 T10 T10 T10 30 31 32 33 … ≤ 75 ≤ 125 O.D. … 42 42 42 42 485 485 485 485 195 195 195 195 NP NP NP NP 427 427 427 NP 482 482 482 482 343 343 343 343 NFN-3 NFN-3 NFN-3 NFN-3 T10 T10 T10 T10, W12 34 35 36 … … … 42 42 42 515 515 515 205 275 275 NP NP NP 427 427 NP 482 482 482 343 343 343 NFN-3 NFN-3 NFN-3 T9 G12, G20, T9 T9 37 38 39 … … … 42 42 42 550 585 585 275 380 380 NP NP NP 427 (Cl. 3 only) 427 427 482 427 260 343 343 260 NFN-3 NFN-3 NFN-3 T9 G11, T8 G5, G21, T8 40 41 … … 42 42 485 515 170 240 NP NP 427 427 482 482 343 343 NFN-3 NFN-3 T10 T10 195 (10) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (10) Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 59.3 115 115 119 59.3 108 108 112 48.7 104 104 108 46.7 102 102 106 45.5 99.9 99.9 104 44.8 98.7 98.7 103 44.2 98.0 98.0 102 43.6 97.9 97.9 101 … 97.9 97.9 101 … 91.4 91.4 101 … 68.1 68.1 … … 40.8 40.8 … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 138 138 65.5 51.7 131 131 65.5 49.7 129 129 62.9 48.1 128 128 … 47.4 128 128 … 46.1 128 128 … … 128 128 … … 116 116 … … 101 101 … … 85.4 … … … 67.8 … … … 52.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 10 11 12 13 14 55.2 55.2 68.9 68.9 68.9 68.9 55.2 55.2 68.9 68.9 68.9 68.9 55.2 55.2 68.9 68.9 68.9 68.9 55.2 55.2 68.9 68.9 68.9 68.9 55.2 55.2 68.9 68.9 68.9 68.9 55.2 55.2 68.9 68.9 68.9 68.9 55.2 55.2 68.9 68.9 68.9 68.9 55.2 55.2 68.9 68.9 68.9 68.9 55.2 55.2 68.9 68.9 68.9 68.9 55.2 55.2 68.9 68.9 68.9 68.9 55.2 55.2 68.9 68.9 68.9 68.9 55.2 55.2 68.9 68.9 68.9 68.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 15 16 17 18 91.7 68.9 128 128 91.7 68.9 128 128 91.7 68.9 128 128 91.7 68.9 128 128 91.7 68.9 128 128 91.7 68.9 128 128 91.7 68.9 128 128 90.7 68.9 128 128 88.1 68.9 127 127 84.9 68.9 125 125 81.4 68.9 123 123 78.0 68.9 121 121 … … … … … … … … … … … … … … … … … … … … … … … … 19 20 21 46.2 46.2 46.2 45.0 45.0 45.0 44.0 44.0 44.0 43.7 43.7 43.7 43.4 43.4 43.4 43.0 43.0 43.0 42.8 42.8 42.8 42.7 42.7 42.7 42.7 42.7 42.7 42.7 42.7 42.7 42.7 42.7 42.7 42.7 42.7 42.7 42.7 42.7 42.7 42.7 42.7 42.7 42.0 42.0 42.0 41.4 41.4 41.4 40.3 40.3 40.3 33.6 33.6 33.6 22 23 24 25 26 55.2 55.2 55.2 118 118 54.1 54.1 54.1 118 118 52.8 52.8 52.8 118 118 52.1 52.1 52.1 118 118 51.7 51.7 51.7 117 117 51.7 51.7 51.7 117 117 51.7 51.7 51.7 117 117 51.7 51.7 51.7 117 117 51.7 51.7 51.7 116 116 51.7 51.7 51.7 115 115 51.7 51.7 51.7 114 114 51.7 51.7 51.7 107 107 51.6 51.6 51.6 … 95.4 51.0 51.0 51.0 … 91.8 51.0 51.0 51.0 … 88.1 50.0 50.0 50.0 … 83.7 41.8 41.8 41.8 … 81.1 33.0 33.0 33.0 … 77.7 27 28 29 115 115 115 107 107 107 99.4 99.4 99.4 95.9 95.9 95.9 93.7 93.7 93.7 92.1 92.1 92.1 91.1 91.1 91.1 90.6 90.6 90.6 90.4 90.4 90.4 90.3 90.3 90.3 90.3 90.3 90.3 90.3 90.3 90.3 90.2 90.2 90.2 89.5 89.5 89.5 88.9 88.9 88.9 87.9 87.9 87.9 78.5 78.5 78.5 60.8 60.8 60.8 30 31 32 33 129 129 129 129 121 121 121 121 112 112 112 112 108 108 108 108 105 105 105 105 103 103 103 103 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 100 100 100 100 99.3 99.3 99.3 99.3 79.9 79.9 79.9 79.9 60.2 60.2 60.2 60.2 34 35 36 138 148 148 136 148 148 133 148 148 131 148 148 128 148 148 126 148 148 124 148 148 122 148 148 122 148 148 121 148 148 120 148 148 119 148 148 118 147 147 117 141 141 116 127 127 102 102 102 65.2 64.9 64.9 34.9 35.0 35.0 37 38 39 158 168 168 158 168 168 158 168 168 158 168 168 158 168 168 158 168 168 158 168 168 158 168 168 158 168 168 158 167 167 158 166 166 158 164 164 157 162 162 149 154 154 127 123 123 102 89.7 89.7 65.0 56.9 56.9 35.0 … … 40 41 115 148 107 148 99.4 148 95.9 148 93.7 148 92.1 146 91.1 144 90.6 143 90.4 142 90.3 141 90.3 140 90.3 139 90.2 138 89.5 136 88.9 127 87.9 102 78.5 64.9 60.8 35.1 196 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 10 11 12 13 14 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 15 16 17 18 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 19 20 21 27.0 27.0 27.0 23.0 23.0 23.0 18.7 18.7 18.7 15.6 15.6 15.6 13.0 13.0 13.0 9.96 9.96 9.96 8.20 … 8.20 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 25 26 27.3 27.3 27.3 … 73.8 22.9 22.9 22.9 … … 18.7 18.7 18.7 … … 15.6 15.6 15.6 … … 13.0 13.0 13.0 … … 9.96 9.96 9.96 … … 8.20 8.20 8.20 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 27 28 29 41.8 41.8 41.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 30 31 32 33 42.1 42.1 42.1 42.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 8.09 8.02 8.02 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 37 38 39 8.04 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 40 41 41.8 8.01 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 197 (10) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 47Ni – 22Cr – 9Mo – 18Fe 47Ni – 22Cr – 9Mo – 18Fe 47Ni – 22Cr – 9Mo – 18Fe 47Ni – 22Cr – 9Mo – 18Fe Plate, sheet, strip Plate, sheet, strip Rod Rod SB-435 SB-435 SB-572 SB-572 … … … … N06002 N06002 N06002 N06002 Annealed Annealed Annealed Annealed 5 6 7 47Ni – 22Cr – 9Mo – 18Fe 47Ni – 22Cr – 9Mo – 18Fe 47Ni – 22Cr – 9Mo – 18Fe Smls. & wld. fittings Wld. pipe Wld. pipe SB-366 SB-619 SB-619 … … … N06002 N06002 N06002 Annealed Solution ann. Solution ann. 8 9 10 11 47Ni – 22Cr – 9Mo – 18Fe 47Ni – 22Cr – 9Mo – 18Fe 47Ni – 22Cr – 9Mo – 18Fe 47Ni – 22Cr – 9Mo – 18Fe Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-622 SB-622 SB-626 SB-626 … … … … N06002 N06002 N06002 N06002 Solution ann. Solution ann. Solution ann. Solution ann. 12 13 14 15 47Ni – 22Cr – 19Fe – 6Mo 47Ni – 22Cr – 19Fe – 6Mo 47Ni – 22Cr – 19Fe – 6Mo 47Ni – 22Cr – 19Fe – 6Mo Rod Rod Plate, sheet, strip Plate, sheet, strip SB-581 SB-581 SB-582 SB-582 … … … … N06007 N06007 N06007 N06007 Solution ann. Solution ann. Solution ann. Solution ann. 16 17 18 19 20 47Ni – 22Cr – 19Fe – 6Mo 47Ni – 22Cr – 19Fe – 6Mo 47Ni – 22Cr – 19Fe – 6Mo 47Ni – 22Cr – 19Fe – 6Mo 47Ni – 22Cr – 19Fe – 6Mo Smls. & wld. fittings Rod Rod Plate, sheet, strip Plate, sheet, strip SB-366 SB-581 SB-581 SB-582 SB-582 … … … … … N06007 N06007 N06007 N06007 N06007 Annealed Solution ann. Solution ann. Solution ann. Solution ann. 21 22 23 24 25 26 47Ni – 22Cr – 19Fe – 6Mo 47Ni – 22Cr – 19Fe – 6Mo 47Ni – 22Cr – 19Fe – 6Mo 47Ni – 22Cr – 19Fe – 6Mo 47Ni – 22Cr – 19Fe – 6Mo 47Ni – 22Cr – 19Fe – 6Mo Wld. pipe Wld. pipe Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-619 SB-619 SB-622 SB-622 SB-626 SB-626 … … … … … … N06007 N06007 N06007 N06007 N06007 N06007 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 27 28 29 30 31 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo Smls. & wld. fittings Forgings Forgings Forgings Forgings SB-366 SB-462 SB-462 SB-564 SB-564 … … … … … N06022 N06022 N06022 N06022 N06022 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 32 33 34 35 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo Rod Rod Plate, sheet, strip Plate, sheet, strip SB-574 SB-574 SB-575 SB-575 … … … … N06022 N06022 N06022 N06022 Solution ann. Solution ann. Solution ann. Solution ann. 36 37 38 39 40 41 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo Wld. pipe Wld. pipe Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-619 SB-619 SB-622 SB-622 SB-626 SB-626 … … … … … … N06022 N06022 N06022 N06022 N06022 N06022 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 42 43 44 40Ni – 29Cr – 15Fe – 5Mo 40Ni – 29Cr – 15Fe – 5Mo 40Ni – 29Cr – 15Fe – 5Mo Smls. & wld. fittings Forgings Forgings SB-366 SB-462 SB-462 … … … N06030 N06030 N06030 Solution ann. Solution ann. Solution ann. Line No. 198 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 … … … … 43 43 43 43 655 655 655 655 240 240 240 240 NP NP NP NP 427 NP 427 NP 899 899 899 899 343 343 343 343 NFN-15 NFN-15 NFN-15 NFN-15 G4, G5, T15 G4, T16 G4, G5, G13, T15 G4, G13, T16 5 6 7 … … … 43 43 43 690 690 690 275 275 275 NP NP NP NP 427 NP 899 899 899 343 343 343 NFN-15 NFN-15 NFN-15 G4, G5, T15, W12 G4, G5, G14, T14, W5 G4, G14, T16 8 9 10 11 … … … … 43 43 43 43 690 690 690 690 275 275 275 275 NP NP NP NP 427 NP 427 NP 899 899 899 899 343 343 343 343 NFN-15 NFN-15 NFN-15 NFN-15 G4, G5, T14 G4, T16 G4, G5, G14, T14, W5 G4, G14, T16 12 13 14 15 > 19 > 19 > 19 > 19 45 45 45 45 585 585 585 585 205 205 205 205 NP NP NP NP NP NP NP NP 538 538 538 538 343 343 343 343 NFN-11 NFN-11 NFN-11 NFN-11 … G5 … G5 16 17 18 19 20 … ≤ 19 ≤ 19 ≤ 19 ≤ 19 45 45 45 45 45 620 620 620 620 620 240 240 240 240 240 NP NP NP NP NP NP NP NP NP NP 538 538 538 538 538 343 343 343 343 343 NFN-11 NFN-11 NFN-11 NFN-11 NFN-11 G5, W12 … G5 … G5 21 22 23 24 25 26 … … … … … … 45 45 45 45 45 45 620 620 620 620 620 620 240 240 240 240 240 240 NP NP NP NP NP NP NP NP NP NP NP NP 538 538 538 538 538 538 343 343 343 343 343 343 NFN-11 NFN-11 NFN-11 NFN-11 NFN-11 NFN-11 G14 G5, G14 … G5 G14 G5, G14 27 28 29 30 31 … … … … … 43 43 43 43 43 690 690 690 690 690 310 310 310 310 310 677 677 677 677 677 NP NP NP 427 NP 677 677 677 677 677 343 NP NP 343 343 NFN-10 NFN-10 NFN-10 NFN-10 NFN-10 G5, G27, G28, T15, W12 G5, G27, G28, T15 G27, G28, T15 G5, G27, G28, T15 G27, G28, T15 32 33 34 35 … … … … 43 43 43 43 690 690 690 690 310 310 310 310 677 677 677 677 427 NP 427 NP 677 677 677 677 343 343 343 343 NFN-10 NFN-10 NFN-10 NFN-10 G5, G27, G28, T15 G27, G28, T15 G5, G27, G28, T15 G27, G28, T15 36 37 38 39 40 41 … … … … … … 43 43 43 43 43 43 690 690 690 690 690 690 310 310 310 310 310 310 677 677 677 677 677 677 427 NP 427 NP 427 NP 677 677 677 677 677 677 343 343 343 343 343 343 NFN-10 NFN-10 NFN-10 NFN-10 NFN-10 NFN-10 G5, G14, G27, G28, T15, W6 G14, G27, G28, T15 G5, G27, G28, T15 G27, G28, T15 G5, G14, G27, G28, T15, W6 G14, G27, G28, T15 42 43 44 … … … 45 45 45 585 585 585 240 240 240 NP NP NP NP NP NP 427 427 427 343 NP NP NFN-19 NFN-19 NFN-19 G5, W12 G5 … 199 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 161 161 161 161 161 153 161 153 161 143 161 143 161 137 161 137 161 132 161 132 161 127 161 127 161 123 161 123 159 119 159 119 155 115 155 115 152 112 152 112 148 110 148 110 145 107 145 107 142 105 142 105 140 104 140 104 139 103 139 103 137 101 137 101 136 101 136 101 135 100 135 100 5 6 7 184 157 157 184 157 148 184 157 139 184 157 134 184 157 129 184 157 124 184 157 119 182 155 116 178 151 112 173 147 109 169 143 106 166 140 104 163 138 102 160 136 100 158 134 99.2 157 133 98.6 155 132 98.0 155 131 97.4 8 9 10 11 184 184 157 157 184 175 157 148 184 164 157 139 184 157 157 134 184 151 157 129 184 146 157 124 184 141 157 119 182 136 155 116 178 132 151 112 173 128 147 109 169 125 143 106 166 122 140 104 163 120 138 102 160 118 136 100 158 117 134 99.2 157 116 133 98.6 155 115 132 98.0 155 115 131 97.4 12 13 14 15 138 138 138 138 131 138 131 138 123 138 123 138 119 138 119 138 115 138 115 138 112 138 112 138 109 138 109 138 106 138 106 138 104 138 104 138 102 137 102 137 100 136 100 136 98.8 134 98.8 134 97.7 132 97.7 132 97.1 131 97.1 131 96.5 130 96.5 130 95.9 129 95.9 129 95.3 128 95.3 128 94.7 128 94.7 128 16 17 18 19 20 161 161 161 161 161 161 152 161 152 161 161 143 161 143 161 161 138 161 138 161 161 134 161 134 161 161 130 161 130 161 161 127 161 127 161 161 124 161 124 161 161 121 161 121 161 160 119 160 119 160 158 117 158 117 158 156 115 156 115 156 154 114 154 114 154 153 113 153 113 153 152 112 152 112 152 150 112 150 112 150 150 111 150 111 150 149 110 149 110 149 21 22 23 24 25 26 137 137 161 161 137 137 129 137 152 161 129 137 121 137 143 161 121 137 117 137 138 161 117 137 114 137 134 161 114 137 110 137 130 161 110 137 107 137 127 161 107 137 105 137 124 161 105 137 103 137 121 161 103 137 101 136 119 160 101 136 99.5 134 117 158 99.5 134 98.1 133 115 156 98.1 133 97.0 131 114 154 97.0 131 96.4 129 113 153 96.4 129 95.1 129 112 152 95.1 129 94.5 128 112 150 94.5 128 94.5 127 111 150 94.5 127 94.0 126 110 149 94.0 126 27 28 29 30 31 197 197 197 197 197 197 197 191 197 191 197 197 182 197 182 196 196 176 196 176 194 194 169 194 169 191 191 164 191 164 188 188 159 188 159 185 185 154 185 154 183 183 150 183 150 182 182 146 182 146 180 180 142 180 142 179 179 140 179 140 178 178 137 178 137 176 176 135 176 135 175 175 133 175 133 174 174 131 174 131 173 173 130 173 130 172 172 129 172 129 32 33 34 35 197 197 197 197 197 191 197 191 197 182 197 182 196 176 196 176 194 169 194 169 191 164 191 164 188 159 188 159 185 154 185 154 183 150 183 150 182 146 182 146 180 142 180 142 179 140 179 140 178 137 178 137 176 135 176 135 175 133 175 133 174 131 174 131 173 130 173 130 172 129 172 129 36 37 38 39 40 41 168 168 197 197 168 168 168 162 197 191 168 162 167 155 197 182 167 155 166 149 196 176 166 149 165 144 194 169 165 144 162 139 191 164 162 139 160 134 188 159 160 134 158 131 185 154 158 131 156 127 183 150 156 127 155 124 182 146 155 124 153 122 180 142 153 122 152 119 179 140 152 119 151 117 178 137 151 117 150 115 176 135 150 115 149 113 175 133 149 113 148 112 174 131 148 112 147 111 173 130 147 111 146 109 172 129 146 109 42 43 44 161 161 161 161 161 148 161 161 136 161 161 130 161 161 126 159 159 122 156 156 119 153 153 116 152 152 114 150 150 112 148 148 110 146 146 108 143 143 106 141 141 105 138 138 103 136 136 101 134 134 98.9 … … … 200 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 135 99.5 135 99.5 134 98.8 134 98.8 133 98.6 133 98.6 131 98.4 131 98.4 115 97.8 115 97.8 95.9 95.9 95.9 95.9 77.3 77.3 77.3 77.3 64.8 64.8 64.8 64.8 54.9 54.9 54.9 54.9 44.8 44.8 44.8 44.8 36.1 36.1 36.1 36.1 29.2 29.2 29.2 29.2 23.7 23.7 23.7 23.7 19.0 19.0 19.0 19.0 14.8 14.8 14.8 14.8 11.2 11.2 11.2 11.2 8.14 8.14 8.14 8.14 5 6 7 153 131 96.8 153 130 96.1 151 129 95.8 143 122 95.6 114 96.8 93.6 94.8 80.3 80.3 77.2 65.6 65.6 64.8 55.1 55.1 54.8 46.3 46.3 45.3 38.1 38.1 36.3 30.9 30.9 29.2 24.7 24.7 23.7 20.1 20.1 19.0 16.6 16.6 14.8 12.7 12.7 11.2 9.19 9.19 8.14 6.79 6.79 8 9 10 11 153 114 131 96.8 153 113 130 96.1 151 113 129 95.8 143 112 122 95.6 114 110 96.8 93.6 94.8 94.8 80.3 80.3 77.2 77.2 65.6 65.6 64.8 64.8 55.1 55.1 54.8 54.8 46.3 46.3 45.3 45.3 38.1 38.1 36.3 36.3 30.9 30.9 29.2 29.2 24.7 24.7 23.7 23.7 20.1 20.1 19.0 19.0 16.6 16.6 14.8 14.8 12.7 12.7 11.2 11.2 9.19 9.19 8.14 8.14 6.79 6.79 12 13 14 15 94.0 127 94.0 127 93.8 126 93.8 126 93.8 126 93.8 126 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 20 149 110 148 110 148 148 109 148 109 148 147 109 147 109 147 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 24 25 26 93.3 126 110 148 93.3 126 93.1 126 109 148 93.1 126 93.1 125 109 147 93.1 125 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 27 28 29 30 31 171 171 128 171 128 169 169 127 169 127 167 167 126 167 126 148 148 124 148 124 116 116 116 116 116 83.9 83.9 83.9 83.9 83.9 65.6 65.6 65.6 65.6 65.6 53.2 53.2 53.2 53.2 53.2 40.9 40.9 40.9 40.9 40.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 171 128 171 128 169 127 169 127 167 126 167 126 148 124 148 124 116 116 116 116 83.9 83.9 83.9 83.9 65.6 65.6 65.6 65.6 53.2 53.2 53.2 53.2 40.9 40.9 40.9 40.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 36 37 38 39 40 41 145 108 171 128 145 108 144 108 169 127 144 108 142 108 167 126 142 108 126 105 148 124 126 105 98.4 98.4 116 116 98.4 98.4 71.4 71.4 83.9 83.9 71.4 71.4 56.1 56.1 65.6 65.6 56.1 56.1 45.5 45.5 53.2 53.2 45.5 45.5 35.0 35.0 40.9 40.9 35.0 35.0 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 42 43 44 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 201 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 40Ni – 29Cr – 15Fe – 5Mo 40Ni – 29Cr – 15Fe – 5Mo 40Ni – 29Cr – 15Fe – 5Mo 40Ni – 29Cr – 15Fe – 5Mo Rod Rod Plate, sheet, strip Plate, sheet, strip SB-581 SB-581 SB-582 SB-582 … … … … N06030 N06030 N06030 N06030 Solution ann. Solution ann. Solution ann. Solution ann. 5 6 7 8 9 10 40Ni – 29Cr – 15Fe – 5Mo 40Ni – 29Cr – 15Fe – 5Mo 40Ni – 29Cr – 15Fe – 5Mo 40Ni – 29Cr – 15Fe – 5Mo 40Ni – 29Cr – 15Fe – 5Mo 40Ni – 29Cr – 15Fe – 5Mo Wld. pipe Wld. pipe Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-619 SB-619 SB-622 SB-622 SB-626 SB-626 … … … … … … N06030 N06030 N06030 N06030 N06030 N06030 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 11 12 13 58Ni – 33Cr – 8Mo 58Ni – 33Cr – 8Mo 58Ni – 33Cr – 8Mo Smls. & wld. fittings Forgings Forgings SB-366 SB-462 SB-462 … … … N06035 N06035 N06035 Solution ann. Solution ann. Solution ann. 14 15 16 17 58Ni – 33Cr – 8Mo 58Ni – 33Cr – 8Mo 58Ni – 33Cr – 8Mo 58Ni – 33Cr – 8Mo Forgings Forgings Rod Rod SB-564 SB-564 SB-574 SB-574 … … … … N06035 N06035 N06035 N06035 Solution ann. Solution ann. Solution ann. Solution ann. 18 19 20 21 58Ni – 33Cr – 8Mo 58Ni – 33Cr – 8Mo 58Ni – 33Cr – 8Mo 58Ni – 33Cr – 8Mo Plate, sheet, strip Plate, sheet, strip Wld. pipe Wld. pipe SB-575 SB-575 SB-619 SB-619 … … … … N06035 N06035 N06035 N06035 Solution ann. Solution ann. Solution ann. Solution ann. 22 23 24 25 58Ni – 33Cr – 8Mo 58Ni – 33Cr – 8Mo 58Ni – 33Cr – 8Mo 58Ni – 33Cr – 8Mo Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-622 SB-622 SB-626 SB-626 … … … … N06035 N06035 N06035 N06035 Solution ann. Solution ann. Solution ann. Solution ann. 26 27 28 29 46Ni – 27Cr – 23Fe – 2.75Si 46Ni – 27Cr – 23Fe – 2.75Si 46Ni – 27Cr – 23Fe – 2.75Si 46Ni – 27Cr – 23Fe – 2.75Si Rod Rod Smls. pipe & tube Smls. pipe & tube SB-166 SB-166 SB-167 SB-167 … … … … N06045 N06045 N06045 N06045 Solution ann. Solution ann. Solution ann. Solution ann. 30 31 32 33 34 46Ni – 27Cr – 23Fe – 2.75Si 46Ni – 27Cr – 23Fe – 2.75Si 46Ni – 27Cr – 23Fe – 2.75Si 46Ni – 27Cr – 23Fe – 2.75Si 46Ni – 27Cr – 23Fe – 2.75Si Plate, sheet, strip Plate, sheet, strip Smls. & wld. fittings Forged fittings Forged fittings SB-168 SB-168 SB-366 SB-462 SB-462 … … … … … N06045 N06045 N06045 N06045 N06045 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 35 36 37 38 39 40 46Ni – 27Cr – 23Fe – 2.75Si 46Ni – 27Cr – 23Fe – 2.75Si 46Ni – 27Cr – 23Fe – 2.75Si 46Ni – 27Cr – 23Fe – 2.75Si 46Ni – 27Cr – 23Fe – 2.75Si 46Ni – 27Cr – 23Fe – 2.75Si Wld. tube Wld. tube Wld. pipe Wld. pipe Forgings Forgings SB-516 SB-516 SB-517 SB-517 SB-564 SB-564 … … … … … … N06045 N06045 N06045 N06045 N06045 N06045 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 41 42 43 44 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo Fittings Fittings Wld. fittings Fittings SB-366 SB-366 SB-366 SB-366 CR5923 WP5923 WP5923W WP5923WX N06059 N06059 N06059 N06059 Annealed Annealed Annealed Annealed Line No. 202 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 … … … … 45 45 45 45 585 585 585 585 240 240 240 240 NP NP NP NP 427 NP 427 NP 427 427 427 427 343 343 343 343 NFN-19 NFN-19 NFN-19 NFN-19 G5 … G5 … 5 6 7 8 9 10 … … … … … … 45 45 45 45 45 45 585 585 585 585 585 585 240 240 240 240 240 240 NP NP NP NP NP NP 427 NP 427 NP 427 NP 427 427 427 427 427 427 343 343 343 343 343 343 NFN-19 NFN-19 NFN-19 NFN-19 NFN-19 NFN-19 G5, G14, W6 G14 G5 … G5, G14, W6 G14 11 12 13 … … … 43 43 43 586 586 586 241 241 241 NP NP NP NP NP NP 427 427 427 NP NP NP NFN-27 NFN-27 NFN-27 G5, W12 G5 … 14 15 16 17 … … … … 43 43 43 43 586 586 586 586 241 241 241 241 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-27 NFN-27 NFN-27 NFN-27 G5 … G5 … 18 19 20 21 … … … … 43 43 43 43 586 586 586 586 241 241 241 241 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-27 NFN-27 NFN-27 NFN-27 G5 … G5, G14 G14 22 23 24 25 … … … … 43 43 43 43 586 586 586 586 241 241 241 241 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-27 NFN-27 NFN-27 NFN-27 G5 … G5, G14 G14 26 27 28 29 … … … … 46 46 46 46 620 620 620 620 240 240 240 240 816 816 816 816 NP NP NP NP 816 816 816 816 NP NP NP NP NFN-8 NFN-8 NFN-8 NFN-8 G5, T11 T11 G5, T11 T11 30 31 32 33 34 … … … … … 46 46 46 46 46 620 620 620 620 620 240 240 240 240 240 816 816 816 816 816 NP NP NP NP NP 816 816 816 816 816 NP NP NP NP NP NFN-8 NFN-8 NFN-8 NFN-8 NFN-8 G5, T11 T11 G5, T11, W12 G5, T11 T11 35 36 37 38 39 40 … … … … … … 46 46 46 46 46 46 620 620 620 620 620 620 240 240 240 240 240 240 816 816 816 816 816 816 NP NP NP NP NP NP 816 816 816 816 816 816 NP NP NP NP NP NP NFN-8 NFN-8 NFN-8 NFN-8 NFN-8 NFN-8 G5, G14, T11 G14, T11 G5, G14, T11 G14, T11 G5, T11 T11 41 42 43 44 … … … … 43 43 43 43 690 690 690 690 310 310 310 310 NP NP NP NP 427 427 427 427 760 760 760 760 343 343 343 343 NFN-14 NFN-14 NFN-14 NFN-14 G5, G14, G23, T16 G5, G23, T16 G5, G14, G23, T16 G5, G23, T16 203 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 161 161 161 161 161 148 161 148 161 136 161 136 161 130 161 130 161 126 161 126 159 122 159 122 156 119 156 119 153 116 153 116 152 114 152 114 150 112 150 112 148 110 148 110 146 108 146 108 143 106 143 106 141 105 141 105 138 103 138 103 136 101 136 101 134 98.9 134 98.9 … … … … 5 6 7 8 9 10 137 137 161 161 137 137 137 126 161 148 137 126 137 116 161 136 137 116 137 111 161 130 137 111 136 107 161 126 136 107 135 104 159 122 135 104 132 101 156 119 132 101 130 98.6 153 116 130 98.6 129 96.5 152 114 129 96.5 128 94.9 150 112 128 94.9 126 93.4 148 110 126 93.4 124 91.7 146 108 124 91.7 121 89.9 143 106 121 89.9 120 88.8 141 105 120 88.8 118 87.5 138 103 118 87.5 116 85.6 136 101 116 85.6 114 83.7 134 98.9 114 83.7 … … … … … … 11 12 13 161 161 161 161 161 149 161 161 139 161 161 132 161 161 125 161 161 119 154 154 114 149 149 110 144 144 107 140 140 104 137 137 102 135 135 100 133 133 98.8 132 132 97.8 131 131 96.9 129 129 95.8 128 128 94.7 … … … 14 15 16 17 161 161 161 161 161 149 161 149 161 139 161 139 161 132 161 132 161 125 161 125 161 119 161 119 154 114 154 114 149 110 149 110 144 107 144 107 140 104 140 104 137 102 137 102 135 100 135 100 133 98.8 133 98.8 132 97.8 132 97.8 131 96.9 131 96.9 129 95.8 129 95.8 128 94.7 128 94.7 … … … … 18 19 20 21 161 161 137 137 161 149 137 127 161 139 137 118 161 132 137 112 161 125 137 106 161 119 137 101 154 114 131 96.9 149 110 127 93.5 144 107 122 91.0 140 104 119 88.4 137 102 116 86.7 135 100 115 85.0 133 98.8 113 84.0 132 97.8 112 83.1 131 96.9 111 82.4 129 95.8 110 81.4 128 94.7 109 80.5 … … … … 22 23 24 25 161 161 137 137 161 149 137 127 161 139 137 118 161 132 137 112 161 125 137 106 161 119 137 101 154 114 131 96.9 149 110 127 93.5 144 107 122 91.0 140 104 119 88.4 137 102 116 86.7 135 100 115 85.0 133 98.8 113 84.0 132 97.8 112 83.1 131 96.9 111 82.4 129 95.8 110 81.4 128 94.7 109 80.5 … … … … 26 27 28 29 161 161 161 161 161 152 161 152 161 142 161 142 161 137 161 137 161 133 161 133 161 129 161 129 161 125 161 125 160 123 160 123 157 121 157 121 155 119 155 119 153 118 153 118 152 117 152 117 151 116 151 116 149 116 149 116 149 115 149 115 148 115 148 115 146 114 146 114 121 113 121 113 30 31 32 33 34 161 161 161 161 161 161 152 161 161 152 161 142 161 161 142 161 137 161 161 137 161 133 161 161 133 161 129 161 161 129 161 125 161 161 125 160 123 160 160 123 157 121 157 157 121 155 119 155 155 119 153 118 153 153 118 152 117 152 152 117 151 116 151 151 116 149 116 149 149 116 149 115 149 149 115 148 115 148 148 115 146 114 146 146 114 121 113 121 121 113 35 36 37 38 39 40 137 137 137 137 161 161 137 129 137 129 161 152 137 121 137 121 161 142 137 117 137 117 161 137 137 113 137 113 161 133 137 110 137 110 161 129 137 107 137 107 161 125 135 104 135 104 160 123 133 103 133 103 157 121 131 101 131 101 155 119 130 101 130 101 153 118 129 99.4 129 99.4 152 117 128 98.6 128 98.6 151 116 127 98.6 127 98.6 149 116 127 97.9 127 97.9 149 115 126 97.3 126 97.3 148 115 124 96.5 124 96.5 146 114 102 95.7 102 95.7 121 113 41 42 43 44 168 197 168 197 168 197 168 197 168 197 168 197 168 197 168 197 168 197 168 197 166 196 166 196 164 194 164 194 162 191 162 191 160 187 160 187 157 184 157 184 154 181 154 181 152 178 152 178 150 176 150 176 147 173 147 173 146 172 146 172 144 170 144 170 143 168 143 168 142 167 142 167 204 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 9 10 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 17 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 18 19 20 21 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 25 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 26 27 28 29 98.1 98.1 98.1 98.1 76.1 76.1 76.1 76.1 56.8 56.8 56.8 56.8 45.1 45.1 45.1 45.1 36.5 36.5 36.5 36.5 29.3 29.3 29.3 29.3 23.9 23.9 23.9 23.9 19.6 19.6 19.6 19.6 15.7 15.7 15.7 15.7 13.1 13.1 13.1 13.1 10.6 10.6 10.6 10.6 8.45 8.45 8.45 8.45 6.81 6.81 6.81 6.81 5.28 5.28 5.28 5.28 … … … … … … … … … … … … 30 31 32 33 34 98.1 98.1 98.1 98.1 98.1 76.1 76.1 76.1 76.1 76.1 56.8 56.8 56.8 56.8 56.8 45.1 45.1 45.1 45.1 45.1 36.5 36.5 36.5 36.5 36.5 29.3 29.3 29.3 29.3 29.3 23.9 23.9 23.9 23.9 23.9 19.6 19.6 19.6 19.6 19.6 15.7 15.7 15.7 15.7 15.7 13.1 13.1 13.1 13.1 13.1 10.6 10.6 10.6 10.6 10.6 8.45 8.45 8.45 8.45 8.45 6.81 6.81 6.81 6.81 6.81 5.28 5.28 5.28 5.28 5.28 … … … … … … … … … … … … … … … 35 36 37 38 39 40 83.5 83.5 83.5 83.5 98.1 98.1 64.6 64.6 64.6 64.6 76.1 76.1 48.1 48.1 48.1 48.1 56.8 56.8 38.3 38.3 38.3 38.3 45.1 45.1 31.2 31.2 31.2 31.2 36.5 36.5 24.7 24.7 24.7 24.7 29.3 29.3 20.5 20.5 20.5 20.5 23.9 23.9 16.8 16.8 16.8 16.8 19.6 19.6 13.6 13.6 13.6 13.6 15.7 15.7 11.0 11.0 11.0 11.0 13.1 13.1 9.00 9.00 9.00 9.00 10.6 10.6 7.11 7.11 7.11 7.11 8.45 8.45 5.54 5.54 5.54 5.54 6.81 6.81 4.38 4.38 4.38 4.38 5.28 5.28 … … … … … … … … … … … … … … … … … … 41 42 43 44 140 165 140 165 137 161 137 161 134 158 134 158 128 150 128 150 104 122 104 122 83.1 97.8 83.1 97.8 67.7 79.3 67.7 79.3 55.9 65.7 55.9 65.7 45.2 53.1 45.2 53.1 36.5 43.0 36.5 43.0 30.4 35.7 30.4 35.7 25.0 29.0 25.0 29.0 … … … … … … … … … … … … … … … … … … … … 205 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 5 6 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo Forged fittings Forged fittings Forgings Forgings Rod Rod SB-462 SB-462 SB-564 SB-564 SB-574 SB-574 … … … … … … N06059 N06059 N06059 N06059 N06059 N06059 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 7 8 9 10 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo Plate, sheet, strip Plate, sheet, strip Wld. pipe Wld. pipe SB-575 SB-575 SB-619 SB-619 … … … … N06059 N06059 N06059 N06059 Solution ann. Solution ann. Solution ann. Solution ann. 11 12 13 14 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-622 SB-622 SB-626 SB-626 … … … … N06059 N06059 N06059 N06059 Solution ann. Solution ann. Solution ann. Solution ann. 15 16 17 18 19 59Ni – 23Cr – 16Mo – 1.6Cu 59Ni – 23Cr – 16Mo – 1.6Cu 59Ni – 23Cr – 16Mo – 1.6Cu 59Ni – 23Cr – 16Mo – 1.6Cu 59Ni – 23Cr – 16Mo – 1.6Cu Smls. & wld. fittings Forgings Forgings Forgings Forgings SB-366 SB-462 SB-462 SB-564 SB-564 … … … … … N06200 N06200 N06200 N06200 N06200 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 20 21 22 23 59Ni – 23Cr – 16Mo – 1.6Cu 59Ni – 23Cr – 16Mo – 1.6Cu 59Ni – 23Cr – 16Mo – 1.6Cu 59Ni – 23Cr – 16Mo – 1.6Cu Rod Rod Plate, sheet, strip Plate, sheet, strip SB-574 SB-574 SB-575 SB-575 … … … … N06200 N06200 N06200 N06200 Solution ann. Solution ann. Solution ann. Solution ann. 24 25 26 27 28 29 59Ni – 23Cr – 16Mo – 1.6Cu 59Ni – 23Cr – 16Mo – 1.6Cu 59Ni – 23Cr – 16Mo – 1.6Cu 59Ni – 23Cr – 16Mo – 1.6Cu 59Ni – 23Cr – 16Mo – 1.6Cu 59Ni – 23Cr – 16Mo – 1.6Cu Wld. pipe Wld. pipe Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-619 SB-619 SB-622 SB-622 SB-626 SB-626 … … … … … … N06200 N06200 N06200 N06200 N06200 N06200 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 30 31 32 33 34 60Ni – 19Cr – 19Mo – 1.8Ta 60Ni – 19Cr – 19Mo – 1.8Ta 60Ni – 19Cr – 19Mo – 1.8Ta 60Ni – 19Cr – 19Mo – 1.8Ta 60Ni – 19Cr – 19Mo – 1.8Ta Smls. & wld. fittings Forgings Forgings Rod Rod SB-366 SB-564 SB-564 SB-574 SB-574 … … … … … N06210 N06210 N06210 N06210 N06210 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 35 36 37 38 60Ni – 19Cr – 19Mo – 1.8Ta 60Ni – 19Cr – 19Mo – 1.8Ta 60Ni – 19Cr – 19Mo – 1.8Ta 60Ni – 19Cr – 19Mo – 1.8Ta Plate, sheet, strip Plate, sheet, strip Wld. pipe Wld. pipe SB-575 SB-575 SB-619 SB-619 … … … … N06210 N06210 N06210 N06210 Solution ann. Solution ann. Solution ann. Solution ann. 39 40 41 42 60Ni – 19Cr – 19Mo – 1.8Ta 60Ni – 19Cr – 19Mo – 1.8Ta 60Ni – 19Cr – 19Mo – 1.8Ta 60Ni – 19Cr – 19Mo – 1.8Ta Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-622 SB-622 SB-626 SB-626 … … … … N06210 N06210 N06210 N06210 Solution ann. Solution ann. Solution ann. Solution ann. Line No. 206 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 6 … … … … … … 43 43 43 43 43 43 690 690 690 690 690 690 310 310 310 310 310 310 NP NP NP NP NP NP NP NP 427 427 427 427 760 760 760 760 760 760 343 343 343 343 343 343 NFN-14 NFN-14 NFN-14 NFN-14 NFN-14 NFN-14 G23, T16 G5, G23, T16 G23, T16 G5, G23, T16 G23, T16 G5, G23, T16 7 8 9 10 … … … … 43 43 43 43 690 690 690 690 310 310 310 310 NP NP NP NP 427 427 427 427 760 760 760 760 343 343 343 343 NFN-14 NFN-14 NFN-14 NFN-14 G23, T16 G5, G23, T16 G14, G23, T16 G5, G14, G23, T16 11 12 13 14 … … … … 43 43 43 43 690 690 690 690 310 310 310 310 NP NP NP NP 427 427 427 427 760 760 760 760 343 343 343 343 NFN-14 NFN-14 NFN-14 NFN-14 G23, T16 G5, G23, T16 G14, G23, T16 G5, G14, G23, T16 15 16 17 18 19 … … … … … 43 43 43 43 43 690 690 690 690 690 310 310 310 310 310 NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 NP NP NP NP NP NFN-10 NFN-10 NFN-10 NFN-10 NFN-10 G5, W12 … G5 … G5 20 21 22 23 … … … … 43 43 43 43 690 690 690 690 310 310 310 310 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-10 NFN-10 NFN-10 NFN-10 … G5 … G5 24 25 26 27 28 29 … … … … … … 43 43 43 43 43 43 690 690 690 690 690 690 310 310 310 310 310 310 NP NP NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 427 NP NP NP NP NP NP NFN-10 NFN-10 NFN-10 NFN-10 NFN-10 NFN-10 G14 G5, G14 … G5 G14 G5, G14 30 31 32 33 34 … … … … … 43 43 43 43 43 690 690 690 690 690 310 310 310 310 310 NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 NP NP NP NP NP NFN-14 NFN-14 NFN-14 NFN-14 NFN-14 G5, W12 … G5 … G5 35 36 37 38 … … … … 43 43 43 43 690 690 690 690 310 310 310 310 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-14 NFN-14 NFN-14 NFN-14 … G5 G14 G5, G14 39 40 41 42 … … … … 43 43 43 43 690 690 690 690 310 310 310 310 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-14 NFN-14 NFN-14 NFN-14 … G5 G14 G5, G14 207 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 5 6 197 197 197 197 197 197 191 197 191 197 191 197 184 197 184 197 184 197 179 197 179 197 179 197 174 197 174 197 174 197 169 196 169 196 169 196 165 194 165 194 165 194 161 191 161 191 161 191 157 187 157 187 157 187 154 184 154 184 154 184 150 181 150 181 150 181 146 178 146 178 146 178 142 176 142 176 142 176 139 173 139 173 139 173 135 172 135 172 135 172 132 170 132 170 132 170 128 168 128 168 128 168 125 167 125 167 125 167 7 8 9 10 197 197 168 168 191 197 163 168 184 197 157 168 179 197 152 168 174 197 147 168 169 196 143 166 165 194 140 164 161 191 137 162 157 187 134 160 154 184 131 157 150 181 127 154 146 178 124 152 142 176 121 150 139 173 118 147 135 172 115 146 132 170 112 144 128 168 109 143 125 167 106 142 11 12 13 14 197 197 168 168 191 197 163 168 184 197 157 168 179 197 152 168 174 197 147 168 169 196 143 166 165 194 140 164 161 191 137 162 157 187 134 160 154 184 131 157 150 181 127 154 146 178 124 152 142 176 121 150 139 173 118 147 135 172 115 146 132 170 112 144 128 168 109 143 125 167 106 142 15 16 17 18 19 197 197 197 197 197 … … … … … 197 184 197 184 197 … … … … … 197 171 197 171 197 … … … … … 191 159 191 159 191 … … … … … 185 148 185 148 185 … … … … … 182 139 182 139 182 180 136 180 136 180 179 133 179 133 179 177 131 177 131 177 175 130 175 130 175 174 129 174 129 174 172 128 172 128 172 … … … … … 20 21 22 23 197 197 197 197 … … … … 184 197 184 197 … … … … 171 197 171 197 … … … … 159 191 159 191 … … … … 148 185 148 185 … … … … 139 182 139 182 136 180 136 180 133 179 133 179 131 177 131 177 130 175 130 175 129 174 129 174 128 172 128 172 … … … … 24 25 26 27 28 29 167 167 197 197 167 167 … … … … … … 156 167 184 197 156 167 … … … … … … 145 167 171 197 145 167 … … … … … … 135 162 159 191 135 162 … … … … … … 126 158 148 185 126 158 … … … … … … 118 154 139 182 118 154 116 153 136 180 116 153 113 152 133 179 113 152 112 151 131 177 112 151 110 149 130 175 110 149 109 148 129 174 109 148 109 146 128 172 109 146 … … … … … … 30 31 32 33 34 197 197 197 197 197 197 192 197 192 197 197 182 197 182 197 197 175 197 175 197 196 169 196 169 196 … … … … … 191 157 191 157 191 … … … … … 186 146 186 146 186 … … … … … 183 137 183 137 183 180 133 180 133 180 175 129 175 129 175 170 126 170 126 170 166 123 166 123 166 163 121 163 121 163 160 118 160 118 160 … … … … … 35 36 37 38 197 197 167 167 192 197 163 167 182 197 155 167 175 197 149 167 169 196 143 167 … … … … 157 191 133 162 … … … … 146 186 124 158 … … … … 137 183 117 155 133 180 113 153 129 175 110 149 126 170 107 145 123 166 105 141 121 163 102 138 118 160 101 136 … … … … 39 40 41 42 197 197 167 167 192 197 163 167 182 197 155 167 175 197 149 167 169 196 143 167 … … … … 157 191 133 162 … … … … 146 186 124 158 … … … … 137 183 117 155 133 180 113 153 129 175 110 149 126 170 107 145 123 166 105 141 121 163 102 138 118 160 101 136 … … … … 208 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 6 122 165 122 165 122 165 119 161 119 161 119 161 117 158 117 158 117 158 115 150 115 150 115 150 112 122 112 122 112 122 97.8 97.8 97.8 97.8 97.8 97.8 79.3 79.3 79.3 79.3 79.3 79.3 65.7 65.7 65.7 65.7 65.7 65.7 53.1 53.1 53.1 53.1 53.1 53.1 43.0 43.0 43.0 43.0 43.0 43.0 35.7 35.7 35.7 35.7 35.7 35.7 29.0 29.0 29.0 29.0 29.0 29.0 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 10 122 165 104 140 119 161 101 137 117 158 99.3 134 115 150 97.9 128 112 122 95.1 104 97.8 97.8 83.1 83.1 79.3 79.3 67.7 67.7 65.7 65.7 55.9 55.9 53.1 53.1 45.2 45.2 43.0 43.0 36.5 36.5 35.7 35.7 30.4 30.4 29.0 29.0 25.0 25.0 … … … … … … … … … … … … … … … … … … … … 11 12 13 14 122 165 104 140 119 161 101 137 117 158 99.3 134 115 150 97.9 128 112 122 95.1 104 97.8 97.8 83.1 83.1 79.3 79.3 67.7 67.7 65.7 65.7 55.9 55.9 53.1 53.1 45.2 45.2 43.0 43.0 36.5 36.5 35.7 35.7 30.4 30.4 29.0 29.0 25.0 25.0 … … … … … … … … … … … … … … … … … … … … 15 16 17 18 19 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 23 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 24 25 26 27 28 29 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 30 31 32 33 34 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 35 36 37 38 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 39 40 41 42 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 209 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. Class/Condition/ Temper (10) (10) (10) (10) (10) 1 2 3 4 5 57Ni – 22Cr – 14W – 2Mo – La 57Ni – 22Cr – 14W – 2Mo – La 57Ni – 22Cr – 14W – 2Mo – La 57Ni – 22Cr – 14W – 2Mo – La 57Ni – 22Cr – 14W – 2Mo – La Smls. & wld. fittings Plate, sheet, strip Plate, sheet, strip Forgings Forgings SB-366 SB-435 SB-435 SB-564 SB-564 … … … … … N06230 N06230 N06230 N06230 N06230 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. (10) (10) (10) (10) 6 7 8 9 57Ni – 22Cr – 14W – 2Mo – La 57Ni – 22Cr – 14W – 2Mo – La 57Ni – 22Cr – 14W – 2Mo – La 57Ni – 22Cr – 14W – 2Mo – La Bar Bar Wld. pipe Wld. pipe SB-572 SB-572 SB-619 SB-619 … … … … N06230 N06230 N06230 N06230 Solution ann. Solution ann. Solution ann. Solution ann. (10) (10) (10) (10) 10 11 12 13 57Ni – 22Cr – 14W – 2Mo – La 57Ni – 22Cr – 14W – 2Mo – La 57Ni – 22Cr – 14W – 2Mo – La 57Ni – 22Cr – 14W – 2Mo – La Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-622 SB-622 SB-626 SB-626 … … … … N06230 N06230 N06230 N06230 Solution ann. Solution ann. Solution ann. Solution ann. 14 15 16 17 18 61Ni – 16Mo – 16Cr 61Ni – 16Mo – 16Cr 61Ni – 16Mo – 16Cr 61Ni – 16Mo – 16Cr 61Ni – 16Mo – 16Cr Smls. & wld. fittings Rod Rod Plate, sheet, strip Plate, sheet, strip SB-366 SB-574 SB-574 SB-575 SB-575 … … … … … N06455 N06455 N06455 N06455 N06455 Annealed Solution ann. Solution ann. Solution ann. Solution ann. 19 20 21 22 23 24 61Ni – 16Mo – 16Cr 61Ni – 16Mo – 16Cr 61Ni – 16Mo – 16Cr 61Ni – 16Mo – 16Cr 61Ni – 16Mo – 16Cr 61Ni – 16Mo – 16Cr Wld. pipe Wld. pipe Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-619 SB-619 SB-622 SB-622 SB-626 SB-626 … … … … … … N06455 N06455 N06455 N06455 N06455 N06455 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 25 26 27 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe Smls. pipe & tube Smls. pipe & tube Smls. & wld. fittings SB-167 SB-167 SB-366 … … … N06600 N06600 N06600 Hot fin./ann. Hot fin./ann. Annealed 28 29 30 31 32 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe Smls. pipe & tube Smls. pipe & tube Smls. pipe & tube Smls. pipe & tube Smls. pipe & tube SB-167 SB-167 SB-167 SB-167 SB-167 … … … … … N06600 N06600 N06600 N06600 N06600 Cold drawn/ann. Cold drawn/ann. Hot fin./ann. Hot fin./ann. Hot fin./ann. 33 34 35 36 37 38 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe Smls. tube Smls. tube Bar Bar Plate Plate, sheet, strip SB-163 SB-163 SB-166 SB-166 SB-168 SB-168 … … … … … … N06600 N06600 N06600 N06600 N06600 N06600 Annealed Annealed Annealed Annealed Annealed Annealed 39 40 41 42 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe Wld. tube Wld. tube Forgings Forgings SB-516 SB-516 SB-564 SB-564 … … … … N06600 N06600 N06600 N06600 Annealed Annealed … Annealed 210 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 … … … … … 43 43 43 43 43 760 760 760 760 760 310 310 310 310 310 899 899 899 899 899 NP NP NP NP NP 982 982 982 982 982 343 343 343 343 343 NFN-24 NFN-24 NFN-24 NFN-24 NFN-24 G4, G5, G31, T15, W12 G4, G31, T16 G4, G5, G31, T15 G4, G31, T16 G4, G5, G31, T15 (10) (10) (10) (10) (10) 6 7 8 9 … … … … 43 43 43 43 760 760 760 760 310 310 310 310 899 899 899 899 NP NP NP NP 982 982 982 982 343 343 343 343 NFN-24 NFN-24 NFN-24 NFN-24 G4, G31, T16 G4, G5, G31, T15 G4, G14, G32, T16 G4, G5, G14, G32, T15 (10) (10) (10) (10) 10 11 12 13 … … … … 43 43 43 43 760 760 760 760 310 310 310 310 899 899 899 899 NP NP NP NP 982 982 982 982 343 343 343 343 NFN-24 NFN-24 NFN-24 NFN-24 G4, G31, T16 G4, G5, G31, T15 G4, G14, G32, T16 G4, G5, G14, G32, T15 (10) (10) (10) (10) 14 15 16 17 18 … … … … … 43 43 43 43 43 690 690 690 690 690 275 275 275 275 275 NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 343 343 343 343 343 NFN-14 NFN-14 NFN-14 NFN-14 NFN-14 G5, W12 … G5 … G5 19 20 21 22 23 24 … … … … … … 43 43 43 43 43 43 690 690 690 690 690 690 275 275 275 275 275 275 NP NP NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 427 343 343 343 343 343 343 NFN-14 NFN-14 NFN-14 NFN-14 NFN-14 NFN-14 G14 G5, G14 … G5 G14 G5, G14 25 26 27 > 125 > 125 … 43 43 43 515 515 550 170 170 205 NP NP NP 427 427 NP 649 649 649 343 343 343 NFN-4 NFN-4 NFN-4 T12 G5, T11 G5, T11, W12 28 29 30 31 32 > 125 > 125 … ≤ 125 ≤ 125 43 43 43 43 43 550 550 550 550 550 205 205 205 205 205 NP NP NP NP NP 427 (Cl. 3 only) 427 (Cl. 3 only) 427 427 (Cl. 3 only) NP 649 649 NP 649 649 343 343 NP 343 343 NFN-4 NFN-4 NFN-4 NFN-4 NFN-4 T12 G5, T11 G5 G5, T11 T12 33 34 35 36 37 38 ≤ 75 ≤ 75 … … … … 43 43 43 43 43 43 550 550 550 550 550 550 240 240 240 240 240 240 649 649 649 649 649 649 427 NP 427 NP 427 NP 649 649 649 649 649 649 343 343 343 343 343 343 NFN-4 NFN-4 NFN-4 NFN-4 NFN-4 NFN-4 G5, T11 T11 G5, T11 T11 G5, T11 T11 39 40 41 42 … … … … 43 43 43 43 550 550 550 550 240 240 240 240 NP NP NP NP NP NP 427 NP 649 649 NP 649 343 343 NP 343 NFN-4 NFN-4 NFN-4 NFN-4 G14, T11 G5, G14, T11 G5 T11 211 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 (10) (10) (10) (10) (10) 1 2 3 4 5 207 207 207 207 207 207 200 207 200 207 207 193 207 193 207 207 188 207 188 207 207 182 207 182 207 207 176 207 176 207 207 171 207 171 207 207 166 207 166 207 207 161 207 161 207 206 157 206 157 206 206 153 206 153 206 203 150 203 150 203 200 148 200 148 200 197 146 197 146 197 196 145 196 145 196 195 144 195 144 195 195 144 195 144 195 195 144 195 144 195 (10) (10) (10) (10) 6 7 8 9 207 207 176 176 200 207 170 176 193 207 164 176 188 207 159 176 182 207 155 176 176 207 150 176 171 207 145 176 166 207 141 176 161 207 137 176 157 206 133 176 153 206 130 176 150 203 128 173 148 200 126 170 146 197 124 167 145 196 123 167 144 195 123 166 144 195 122 166 144 195 122 166 (10) (10) (10) (10) 10 11 12 13 207 207 176 176 200 207 170 176 193 207 164 176 188 207 159 176 182 207 155 176 176 207 150 176 171 207 145 176 166 207 141 176 161 207 137 176 157 206 133 176 153 206 130 176 150 203 128 173 148 200 126 170 146 197 124 167 145 196 123 167 144 195 123 166 144 195 122 166 144 195 122 166 14 15 16 17 18 184 184 184 184 184 184 177 184 177 184 184 168 184 168 184 184 163 184 163 184 184 158 184 158 184 184 154 184 154 184 184 150 184 150 184 184 147 184 147 184 184 144 184 144 184 184 142 184 142 184 184 140 184 140 184 184 138 184 138 184 184 137 184 137 184 182 135 182 135 182 180 134 180 134 180 178 132 178 132 178 176 130 176 130 176 … … … … … 19 20 21 22 23 24 157 157 184 184 157 157 150 157 177 184 150 157 143 157 168 184 143 157 138 157 163 184 138 157 134 157 158 184 134 157 131 157 154 184 131 157 128 157 150 184 128 157 125 157 147 184 125 157 123 157 144 184 123 157 121 157 142 184 121 157 119 157 140 184 119 157 117 157 138 184 117 157 116 156 137 184 116 156 115 155 135 182 115 155 114 153 134 180 114 153 112 151 132 178 112 151 110 149 130 176 110 149 … … … … … … 25 26 27 115 115 138 112 115 138 109 115 138 107 115 138 105 115 138 103 115 138 101 115 138 99.1 115 138 97.2 115 138 95.5 115 138 93.9 115 138 92.6 115 138 91.4 115 138 90.1 115 138 88.9 115 138 87.7 115 138 86.3 115 138 85.7 115 120 28 29 30 31 32 138 138 138 138 138 135 138 138 138 135 131 138 138 138 131 129 138 138 138 129 126 138 138 138 126 124 138 138 138 124 121 138 138 138 121 119 138 138 138 119 117 138 138 138 117 115 138 138 138 115 113 138 138 138 113 111 138 138 138 111 109 138 138 138 109 108 138 138 138 108 107 138 138 138 107 105 138 138 138 105 104 138 138 138 104 103 120 … 120 103 33 34 35 36 37 38 158 158 158 158 158 158 158 152 158 152 158 152 158 146 158 146 158 146 158 144 158 144 158 144 158 143 158 143 158 143 158 142 158 142 158 142 158 142 158 142 158 142 158 141 158 141 158 141 158 140 158 140 158 140 158 139 158 139 158 139 158 138 158 138 158 138 158 137 158 137 158 137 158 136 158 136 158 136 158 135 158 135 158 135 158 134 158 134 158 134 158 132 158 132 158 132 156 130 156 130 156 130 124 118 124 118 124 118 39 40 41 42 134 134 158 158 129 134 158 152 124 134 158 146 123 134 158 144 122 134 158 143 121 134 158 142 120 134 158 142 119 134 158 141 119 134 158 140 118 134 158 139 117 134 158 138 116 134 158 137 116 134 158 136 115 134 158 135 114 134 158 134 112 134 158 132 110 132 158 130 99.9 106 … 118 212 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 195 144 195 144 195 195 144 195 144 195 195 144 195 144 195 183 144 183 144 183 153 144 153 144 153 128 128 128 128 128 107 107 107 107 107 89.7 89.7 89.7 89.7 89.7 74.7 74.7 74.7 74.7 74.7 61.9 61.9 61.9 61.9 61.9 50.8 50.8 50.8 50.8 50.8 41.1 41.1 41.1 41.1 41.1 32.6 32.8 32.6 32.8 32.6 25.2 25.2 25.2 25.2 25.2 18.9 18.9 18.9 18.9 18.9 13.8 13.8 13.8 13.8 13.8 10.2 10.2 10.2 10.2 10.2 (10) (10) (10) (10) (10) 6 7 8 9 144 195 122 166 144 195 122 166 144 195 122 166 144 183 122 156 144 153 122 130 128 128 109 109 107 107 91.0 91.0 89.7 89.7 76.2 76.2 74.7 74.7 63.5 63.5 61.9 61.9 52.6 52.6 50.8 50.8 43.2 43.2 41.1 41.1 34.9 34.9 32.8 32.6 27.7 27.7 25.2 25.2 21.4 21.4 18.9 18.9 16.1 16.1 13.8 13.8 11.7 11.7 10.2 10.2 8.67 8.67 (10) (10) (10) (10) 10 11 12 13 144 195 122 166 144 195 122 166 144 195 122 166 144 183 122 156 144 153 122 130 128 128 109 109 107 107 91.0 91.0 89.7 89.7 76.2 76.2 74.7 74.7 63.5 63.5 61.9 61.9 52.6 52.6 50.8 50.8 43.2 43.2 41.1 41.1 34.9 34.9 32.8 32.6 27.7 27.7 25.2 25.2 21.4 21.4 18.9 18.9 16.1 16.1 13.8 13.8 11.7 11.7 10.2 10.2 8.67 8.67 (10) (10) (10) (10) 14 15 16 17 18 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 19 20 21 22 23 24 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 79.7 87.5 86.1 59.8 59.8 58.3 40.1 40.1 40.0 26.9 26.9 26.8 19.0 19.0 19.0 14.8 14.8 14.8 13.8 13.8 13.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 31 32 86.1 86.1 … 86.1 86.1 58.3 58.3 … 58.3 58.3 40.0 40.0 … 40.0 40.0 26.8 26.8 … 26.8 26.8 19.0 19.0 … 19.0 19.0 14.8 14.8 … 14.8 14.8 13.8 13.8 … 13.8 13.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 33 34 35 36 37 38 86.5 86.5 86.5 86.5 86.5 86.5 58.7 58.7 58.7 58.7 58.7 58.7 40.0 40.0 40.0 40.0 40.0 40.0 26.8 26.8 26.8 26.8 26.8 26.8 19.0 19.0 19.0 19.0 19.0 19.0 14.8 14.8 14.8 14.8 14.8 14.8 13.8 13.8 13.8 13.8 13.8 13.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 39 40 41 42 73.4 73.4 … 86.5 50.1 50.1 … 58.7 34.1 34.1 … 40.0 22.7 22.7 … 26.8 16.5 16.5 … 19.0 12.7 12.7 … 14.8 11.7 11.7 … 13.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 213 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe Smls. pipe & tube Smls. pipe & tube Wld. pipe Wld. pipe SB-167 SB-167 SB-517 SB-517 … … … … N06600 N06600 N06600 N06600 Cold drawn/ann. Cold drawn/ann. Cold drawn/ann. Cold drawn/ann. 5 6 7 8 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe Bar, rod Bar, rod Plate, sheet, strip Plate, sheet, strip SB-166 SB-166 SB-168 SB-168 … … … … N06600 N06600 N06600 N06600 Hot fin. Hot fin. Hot rolled Hot rolled 9 10 11 12 60Ni – 23Cr – Fe 60Ni – 23Cr – Fe 60Ni – 23Cr – Fe 60Ni – 23Cr – Fe Smls. tube Smls. tube Bar Bar SB-163 SB-163 SB-166 SB-166 … … … … N06601 N06601 N06601 N06601 Annealed Annealed Annealed Annealed 13 14 15 16 60Ni – 23Cr – Fe 60Ni – 23Cr – Fe 60Ni – 23Cr – Fe 60Ni – 23Cr – Fe Smls. pipe & tube Smls. pipe & tube Plate, sheet, strip Plate, sheet, strip SB-167 SB-167 SB-168 SB-168 … … … … N06601 N06601 N06601 N06601 Annealed Annealed Annealed Annealed (10) (10) (10) (10) 17 18 19 20 52Ni – 22Cr – 13Co – 9Mo 52Ni – 22Cr – 13Co – 9Mo 52Ni – 22Cr – 13Co – 9Mo 52Ni – 22Cr – 13Co – 9Mo Bar, rod Bar, rod Smls. pipe & tube Smls. pipe & tube SB-166 SB-166 SB-167 SB-167 … … … … N06617 N06617 N06617 N06617 Annealed Annealed Annealed Annealed (10) (10) (10) (10) 21 22 23 24 52Ni – 22Cr – 13Co – 9Mo 52Ni – 22Cr – 13Co – 9Mo 52Ni – 22Cr – 13Co – 9Mo 52Ni – 22Cr – 13Co – 9Mo Plate, sheet, strip Plate, sheet, strip Forgings Forgings SB-168 SB-168 SB-564 SB-564 … … … … N06617 N06617 N06617 N06617 Annealed Annealed Annealed Annealed 25 26 27 28 29 30 60Ni – 22Cr – 9Mo – 3.5Cb 60Ni – 22Cr – 9Mo – 3.5Cb 60Ni – 22Cr – 9Mo – 3.5Cb 60Ni – 22Cr – 9Mo – 3.5Cb 60Ni – 22Cr – 9Mo – 3.5Cb 60Ni – 22Cr – 9Mo – 3.5Cb Plate, sheet, strip Plate, sheet, strip Smls. pipe & tube Smls. pipe & tube Bar Bar SB-443 SB-443 SB-444 SB-444 SB-446 SB-446 2 2 2 2 2 2 N06625 N06625 N06625 N06625 N06625 N06625 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 31 32 33 60Ni – 22Cr – 9Mo – 3.5Cb 60Ni – 22Cr – 9Mo – 3.5Cb 60Ni – 22Cr – 9Mo – 3.5Cb Smls. & wld. fittings Bar Forgings SB-366 SB-446 SB-564 … 1 … N06625 N06625 N06625 Annealed Annealed Annealed 34 35 36 37 60Ni – 22Cr – 9Mo – 3.5Cb 60Ni – 22Cr – 9Mo – 3.5Cb 60Ni – 22Cr – 9Mo – 3.5Cb 60Ni – 22Cr – 9Mo – 3.5Cb Plate, sheet, strip Plate, sheet, strip Smls. pipe Bar SB-443 SB-443 SB-444 SB-446 1 1 1 1 N06625 N06625 N06625 N06625 Annealed Annealed Annealed Annealed 38 39 40 60Ni – 22Cr – 9Mo – 3.5Cb 60Ni – 22Cr – 9Mo – 3.5Cb 60Ni – 22Cr – 9Mo – 3.5Cb Forgings Wld. tube Wld. pipe SB-564 SB-704 SB-705 … … 1 N06625 N06625 N06625 Annealed Annealed Annealed Line No. 214 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 ≤ 125 ≤ 125 … … 43 43 43 43 550 550 550 550 240 240 240 240 649 649 NP NP 427 (Cl. 3 only) 427 NP NP 649 649 649 649 343 343 343 343 NFN-4 NFN-4 NFN-4 NFN-4 T11 G5, T11 G14, T11 G5, G14, T11 5 6 7 8 … … … … 43 43 43 43 585 585 585 585 240 240 240 240 649 649 649 649 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 649 649 649 649 343 343 343 343 NFN-4 NFN-4 NFN-4 NFN-4 T13 G5, T12 G20, T13 G5, G20, T12 9 10 11 12 ≤ 75 O.D. ≤ 75 O.D. … … 43 43 43 43 552 552 552 552 207 207 207 207 899 899 899 899 NP NP NP NP 899 899 899 899 NP NP NP NP NFN-4 NFN-4 NFN-4 NFN-4 G4, T14 G4, G5, T13 G4, T14 G4, G5, T13 13 14 15 16 … … … … 43 43 43 43 552 552 552 552 207 207 207 207 899 899 899 899 NP NP NP NP 899 899 899 899 NP NP NP NP NFN-4 NFN-4 NFN-4 NFN-4 G4, T14 G4, G5, T13 G4, T14 G4, G5, T13 17 18 19 20 … … … … 43 43 43 43 655 655 655 655 240 240 240 240 899 899 899 899 NP NP NP NP 982 982 982 982 NP NP NP NP NFN-4 NFN-4 NFN-4 NFN-4 G4, G29, T18 G4, G5, G29, T17 G4, G29, T18 G4, G5, G29, T17 (10) (10) (10) (10) 21 22 23 24 … … … … 43 43 43 43 655 655 655 655 240 240 240 240 899 899 899 899 NP NP NP NP 982 982 982 982 NP NP NP NP NFN-4 NFN-4 NFN-4 NFN-4 G4, G29, T18 G4, G5, G29, T17 G4, G29, T18 G4, G5, G29, T17 (10) (10) (10) (10) 25 26 27 28 29 30 … … … … … … 43 43 43 43 43 43 690 690 690 690 690 690 275 275 275 275 275 275 593 593 593 593 593 593 NP NP NP NP NP NP 871 871 871 871 871 871 343 343 343 343 343 343 NFN-22 NFN-22 NFN-22 NFN-22 NFN-22 NFN-22 G4, G5, G23, T17, W13 G4, G23, T18, W13 G4, G5, G23, T17, W13 G4, G23, T18, W13 G4, G5, G23, T17, W13 G4, G23, T18, W13 31 32 33 … 100 < t ≤ 250 100 < t ≤ 250 43 43 43 760 760 760 345 345 345 593 593 593 NP 427 427 649 649 649 343 343 343 NFN-17 NFN-17 NFN-17 G23, T16, W12 G23, T16 G23, T16 34 35 36 37 … … … ≤ 100 43 43 43 43 760 825 825 825 380 415 415 415 593 593 593 593 427 NP 427 427 649 649 649 649 343 343 343 343 NFN-17 NFN-17 NFN-17 NFN-17 G23, T16 G22, G23, T16 G23, T16 G22, G23, T16 38 39 40 ≤ 100 … … 43 43 43 825 825 825 415 415 415 593 593 593 427 427 NP 649 649 649 343 343 343 NFN-17 NFN-17 NFN-17 G22, G23, T16 G14, G23, T16 G14, G23, T16 215 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 158 158 134 134 152 158 129 134 146 158 124 134 144 158 123 134 143 158 122 134 142 158 121 134 142 158 120 134 141 158 119 134 140 158 119 134 139 158 118 134 138 158 117 134 137 158 116 134 136 158 116 134 135 158 115 134 134 158 114 134 132 158 112 134 130 156 110 132 118 124 99.9 106 5 6 7 8 161 161 161 161 156 161 156 161 152 161 152 161 150 161 150 161 148 161 148 161 147 161 147 161 147 161 147 161 147 161 147 161 147 161 147 161 147 161 147 161 146 161 146 161 146 161 146 161 145 161 145 161 145 161 145 161 143 161 143 161 141 161 141 161 139 161 139 161 137 161 137 161 9 10 11 12 138 138 138 138 128 138 128 138 122 138 122 138 118 138 118 138 114 138 114 138 111 138 111 138 108 138 108 138 105 138 105 138 102 138 102 138 100 136 100 136 98.9 133 98.9 133 97.6 132 97.6 132 96.6 130 96.6 130 95.9 129 95.9 129 95.4 129 95.4 129 95.1 128 95.1 128 94.9 128 94.9 128 94.8 128 94.8 128 13 14 15 16 138 138 138 138 128 138 128 138 122 138 122 138 118 138 118 138 114 138 114 138 111 138 111 138 108 138 108 138 105 138 105 138 102 138 102 138 100 136 100 136 98.9 133 98.9 133 97.6 132 97.6 132 96.6 130 96.6 130 95.9 129 95.9 129 95.4 129 95.4 129 95.1 128 95.1 128 94.9 128 94.9 128 94.8 128 94.8 128 (10) (10) (10) (10) 17 18 19 20 161 161 161 161 152 161 152 161 142 161 142 161 136 161 136 161 132 161 132 161 129 161 129 161 125 161 125 161 122 161 122 161 120 161 120 161 117 160 117 160 115 157 115 157 114 154 114 154 113 152 113 152 111 151 111 151 110 150 110 150 110 148 110 148 109 147 109 147 108 146 108 146 (10) (10) (10) (10) 21 22 23 24 161 161 161 161 152 161 152 161 142 161 142 161 136 161 136 161 132 161 132 161 129 161 129 161 125 161 125 161 122 161 122 161 120 161 120 161 117 160 117 160 115 157 115 157 114 154 114 154 113 152 113 152 111 151 111 151 110 150 110 150 110 148 110 148 109 147 109 147 108 146 108 146 25 26 27 28 29 30 184 184 184 184 184 184 184 175 184 175 184 175 184 169 184 169 184 169 184 165 184 165 184 165 184 161 184 161 184 161 184 158 184 158 184 158 184 155 184 155 184 155 184 153 184 153 184 153 184 150 184 150 184 150 184 148 184 148 184 148 184 146 184 146 184 146 184 144 184 144 184 144 184 143 184 143 184 143 184 141 184 141 184 141 184 140 184 140 184 140 184 139 184 139 184 139 184 138 184 138 184 138 184 137 184 137 184 137 31 32 33 217 217 217 217 217 217 217 217 217 217 217 217 215 215 215 212 212 212 209 209 209 206 206 206 204 204 204 201 201 201 199 199 199 197 197 197 194 194 194 192 192 192 191 191 191 189 189 189 187 187 187 186 186 186 34 35 36 37 217 236 236 236 217 236 236 236 217 236 236 236 217 236 236 236 217 236 236 236 217 234 234 234 217 232 232 232 217 230 230 230 217 228 228 228 207 226 226 226 205 224 224 224 204 222 222 222 202 221 221 221 201 219 219 219 199 217 217 217 197 215 215 215 196 213 213 213 194 212 212 212 38 39 40 236 201 201 236 201 201 236 201 201 236 201 201 236 201 201 234 199 199 232 197 197 230 195 195 228 194 194 226 192 192 224 190 191 222 189 189 221 188 188 219 186 186 217 185 185 215 183 183 213 182 181 212 180 180 216 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 86.5 86.5 73.4 73.4 58.7 58.7 50.1 50.1 40.0 40.0 34.1 34.1 26.8 26.8 22.7 22.7 19.0 19.0 16.5 16.5 14.8 14.8 12.7 12.7 13.8 13.8 11.7 11.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 134 151 134 151 118 119 118 119 85.6 85.6 85.6 85.6 62.9 62.9 62.9 62.9 46.2 46.2 46.2 46.2 39.4 39.4 39.4 39.4 37.9 37.9 37.9 37.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 10 11 12 94.8 128 94.8 128 94.7 128 94.7 128 94.5 108 94.5 108 85.7 85.7 85.7 85.7 67.5 67.5 67.5 67.5 52.9 52.9 52.9 52.9 41.5 41.5 41.5 41.5 32.5 32.5 32.5 32.5 25.6 25.6 25.6 25.6 20.3 20.3 20.3 20.3 16.2 16.2 16.2 16.2 13.0 13.0 13.0 13.0 10.5 10.5 10.5 10.5 8.6 8.6 8.6 8.6 7.0 7.0 7.0 7.0 5.8 5.8 5.8 5.8 5.0 5.0 5.0 5.0 13 14 15 16 94.8 128 94.8 128 94.7 128 94.7 128 94.5 108 94.5 108 85.7 85.7 85.7 85.7 67.5 67.5 67.5 67.5 52.9 52.9 52.9 52.9 41.5 41.5 41.5 41.5 32.5 32.5 32.5 32.5 25.6 25.6 25.6 25.6 20.3 20.3 20.3 20.3 16.2 16.2 16.2 16.2 13.0 13.0 13.0 13.0 10.5 10.5 10.5 10.5 8.6 8.6 8.6 8.6 7.0 7.0 7.0 7.0 5.8 5.8 5.8 5.8 5.0 5.0 5.0 5.0 17 18 19 20 108 145 108 145 107 144 107 144 106 144 106 144 106 144 106 144 106 143 106 143 105 142 105 142 105 124 105 124 101 101 101 101 81.0 81.0 81.0 81.0 64.1 64.1 64.1 64.1 50.4 50.4 50.4 50.4 39.5 39.5 39.5 39.5 31.3 31.3 31.3 31.3 24.6 24.6 24.6 24.6 19.4 19.4 19.4 19.4 15.3 15.3 15.3 15.3 12.3 12.3 12.3 12.3 (10) (10) (10) (10) 21 22 23 24 108 145 108 145 107 144 107 144 106 144 106 144 106 144 106 144 106 143 106 143 105 142 105 142 105 124 105 124 101 101 101 101 81.0 81.0 81.0 81.0 64.1 64.1 64.1 64.1 50.4 50.4 50.4 50.4 39.5 39.5 39.5 39.5 31.3 31.3 31.3 31.3 24.6 24.6 24.6 24.6 19.4 19.4 19.4 19.4 15.3 15.3 15.3 15.3 12.3 12.3 12.3 12.3 (10) (10) (10) (10) 25 26 27 28 29 30 184 136 184 136 184 136 183 135 183 135 183 135 182 135 182 135 182 135 181 134 181 134 181 134 178 134 178 134 178 134 173 133 173 133 173 133 136 133 136 133 136 133 105 105 105 105 105 105 84.3 84.3 84.3 84.3 84.3 84.3 63.6 63.6 63.6 63.6 63.6 63.6 50.2 50.2 50.2 50.2 50.2 50.2 39.3 39.3 39.3 39.3 39.3 39.3 30.3 30.3 30.3 30.3 30.3 30.3 23.4 23.4 23.4 23.4 23.4 23.4 16.5 16.5 16.5 16.5 16.5 16.5 12.5 12.5 12.5 12.5 12.5 12.5 … … … … … … 31 32 33 185 192 192 184 190 190 183 188 188 182 185 185 178 179 179 137 137 137 88.8 88.9 88.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 37 192 210 210 210 190 207 207 207 188 205 205 205 185 202 202 202 179 192 192 192 137 136 136 136 88.9 89.0 89.0 89.0 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 38 39 40 210 178 178 207 176 176 205 174 174 202 172 172 192 164 164 136 116 116 89.0 75.5 75.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 217 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 5 6 Ni – Cr – Mo – W Ni – Cr – Mo – W Ni – Cr – Mo – W Ni – Cr – Mo – W Ni – Cr – Mo – W Ni – Cr – Mo – W Forged fittings Forged fittings Forgings Forgings Rod Rod SB-462 SB-462 SB-564 SB-564 SB-574 SB-574 … … … … … … N06686 N06686 N06686 N06686 N06686 N06686 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 7 8 9 10 Ni – Cr – Mo – W Ni – Cr – Mo – W Ni – Cr – Mo – W Ni – Cr – Mo – W Plate, sheet, strip Plate, sheet, strip Wld. pipe Wld. pipe SB-575 SB-575 SB-619 SB-619 … … … … N06686 N06686 N06686 N06686 Solution ann. Solution ann. Solution ann. Solution ann. 11 12 13 14 Ni – Cr – Mo – W Ni – Cr – Mo – W Ni – Cr – Mo – W Ni – Cr – Mo – W Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-622 SB-622 SB-626 SB-626 … … … … N06686 N06686 N06686 N06686 Solution ann. Solution ann. Solution ann. Solution ann. 15 16 17 18 19 20 58Ni – 29Cr – 9Fe 58Ni – 29Cr – 9Fe 58Ni – 29Cr – 9Fe 58Ni – 29Cr – 9Fe 58Ni – 29Cr – 9Fe 58Ni – 29Cr – 9Fe Bar, rod Bar, rod Plate, sheet, strip Plate, sheet, strip Smls. pipe & tube Smls. pipe & tube SB-166 SB-166 SB-168 SB-168 SB-167 SB-167 … … … … … … N06690 N06690 N06690 N06690 N06690 N06690 Annealed Annealed Annealed Annealed Cold drawn/ann. Cold drawn/ann. 21 22 23 24 49Ni – 25Cr – 18Fe – 6Mo 49Ni – 25Cr – 18Fe – 6Mo 49Ni – 25Cr – 18Fe – 6Mo 49Ni – 25Cr – 18Fe – 6Mo Plate, sheet, strip Plate, sheet, strip Wld. pipe Wld. pipe SB-582 SB-582 SB-619 SB-619 … … … … N06975 N06975 N06975 N06975 Solution ann. Solution ann. Solution ann. Solution ann. 25 26 27 28 49Ni – 25Cr – 18Fe – 6Mo 49Ni – 25Cr – 18Fe – 6Mo 49Ni – 25Cr – 18Fe – 6Mo 49Ni – 25Cr – 18Fe – 6Mo Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-622 SB-622 SB-626 SB-626 … … … … N06975 N06975 N06975 N06975 Solution ann. Solution ann. Solution ann. Solution ann. 29 30 31 32 47Ni – 22Cr – 20Fe – 7Mo 47Ni – 22Cr – 20Fe – 7Mo 47Ni – 22Cr – 20Fe – 7Mo 47Ni – 22Cr – 20Fe – 7Mo Rod Rod Plate, sheet, strip Plate, sheet, strip SB-581 SB-581 SB-582 SB-582 … … … … N06985 N06985 N06985 N06985 Annealed Annealed Annealed Annealed 33 34 35 36 37 47Ni – 22Cr – 20Fe – 7Mo 47Ni – 22Cr – 20Fe – 7Mo 47Ni – 22Cr – 20Fe – 7Mo 47Ni – 22Cr – 20Fe – 7Mo 47Ni – 22Cr – 20Fe – 7Mo Smls. & wld. fittings Rod Rod Plate, sheet, strip Plate, sheet, strip SB-366 SB-581 SB-581 SB-582 SB-582 … … … … … N06985 N06985 N06985 N06985 N06985 Annealed Annealed Annealed Annealed Annealed 38 39 40 41 42 43 47Ni – 22Cr – 20Fe – 7Mo 47Ni – 22Cr – 20Fe – 7Mo 47Ni – 22Cr – 20Fe – 7Mo 47Ni – 22Cr – 20Fe – 7Mo 47Ni – 22Cr – 20Fe – 7Mo 47Ni – 22Cr – 20Fe – 7Mo Wld. pipe Wld. pipe Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-619 SB-619 SB-622 SB-622 SB-626 SB-626 … … … … … … N06985 N06985 N06985 N06985 N06985 N06985 Annealed Annealed Annealed Annealed Annealed Annealed Line No. (10) (10) 218 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 6 ≤ 88.9 ≤ 88.9 … … ≤ 88.9 ≤ 88.9 43 43 43 43 43 43 689 689 689 689 689 689 310 310 310 310 310 310 NP NP NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 427 NP NP NP NP NP NP NFN-10 NFN-10 NFN-10 NFN-10 NFN-10 NFN-10 G5 … G5 … G5 … 7 8 9 10 … … ≤ 203.2 ≤ 203.2 43 43 43 43 689 689 689 689 310 310 310 310 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-10 NFN-10 NFN-10 NFN-10 G5 … G5, G14 G14 11 12 13 14 … … ≤ 88.9 ≤ 88.9 43 43 43 43 689 689 689 689 310 310 310 310 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-10 NFN-10 NFN-10 NFN-10 G5 … G5, G14 G14 15 16 17 18 19 20 … … … … … … 43 43 43 43 43 43 585 585 585 585 585 585 240 240 240 240 240 240 NP NP NP NP 649 649 NP NP NP NP NP NP 454 454 454 454 454 454 343 343 343 343 343 343 NFN-4 NFN-4 NFN-4 NFN-4 NFN-4 NFN-4 … G5 … G5 H3, T12 G5, H3, T11 21 22 23 24 … … … … 45 45 45 45 585 585 585 585 220 220 220 220 NP NP NP NP NP NP NP NP 427 427 427 427 343 343 343 343 NFN-11 NFN-11 NFN-11 NFN-11 … G5 G14 G5, G14 25 26 27 28 … … … … 45 45 45 45 585 585 585 585 220 220 220 220 NP NP NP NP NP NP NP NP 427 427 427 427 343 343 343 343 NFN-11 NFN-11 NFN-11 NFN-11 … G5 G14 G5, G14 29 30 31 32 > 19 > 19 > 19 > 19 45 45 45 45 585 585 585 585 205 205 205 205 NP NP NP NP NP NP NP NP 427 427 427 427 343 343 343 343 NFN-19 NFN-19 NFN-19 NFN-19 … G5 … G5 33 34 35 36 37 … ≤ 19 ≤ 19 ≤ 19 ≤ 19 45 45 45 45 45 620 620 620 620 620 240 240 240 240 240 NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 343 343 343 343 343 NFN-18 NFN-18 NFN-18 NFN-18 NFN-18 G5, W12 … G5 … G5 38 39 40 41 42 43 … … … … … … 45 45 45 45 45 45 620 620 620 620 620 620 240 240 240 240 240 240 NP NP NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 427 343 343 343 343 343 343 NFN-18 NFN-18 NFN-18 NFN-18 NFN-18 NFN-18 G14 G5, G14 … G5 G14 G5, G14 219 (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (10) (10) Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 5 6 197 197 197 197 197 197 197 182 197 182 197 182 197 170 197 170 197 170 … … … … … … 194 161 194 161 194 161 … … … … … … 188 155 188 155 188 155 … … … … … … 183 150 183 150 183 150 … … … … … … 180 145 180 145 180 145 178 142 178 142 178 142 177 140 177 140 177 140 175 139 175 139 175 139 174 137 174 137 174 137 172 137 172 137 172 137 170 137 170 137 170 137 … … … … … … 7 8 9 10 197 197 167 167 197 182 167 154 197 170 167 144 … … … … 194 161 165 137 … … … … 188 155 160 132 … … … … 183 150 156 128 … … … … 180 145 153 123 178 142 151 121 177 140 150 119 175 139 149 118 174 137 148 117 172 137 146 116 170 137 144 116 … … … … 11 12 13 14 197 197 167 167 197 182 167 154 197 170 167 144 … … … … 194 161 165 137 … … … … 188 155 160 132 … … … … 183 150 156 128 … … … … 180 145 153 123 178 142 151 121 177 140 150 119 175 139 149 118 174 137 148 117 172 137 146 116 170 137 144 116 … … … … 15 16 17 18 19 20 161 161 161 161 161 161 153 161 153 161 151 161 144 161 144 161 144 161 140 161 140 161 140 161 137 161 137 161 137 161 134 161 134 161 134 161 132 161 132 161 132 161 130 160 130 160 130 160 129 160 129 160 129 159 128 159 128 159 128 159 127 158 127 158 127 158 127 158 127 158 127 158 127 158 127 158 127 158 127 157 127 157 127 157 127 156 127 156 127 157 127 156 127 156 127 156 127 155 127 155 127 155 127 155 127 155 127 154 21 22 23 24 147 147 125 125 140 147 119 125 133 147 114 125 130 147 111 125 127 147 108 125 124 147 106 125 121 147 103 125 118 147 100 125 115 147 97.6 125 112 147 95.1 125 109 146 92.9 124 107 145 91.0 123 105 141 89.1 120 103 139 87.4 118 102 138 86.9 117 101 137 86.2 116 101 135 85.6 115 … … … … 25 26 27 28 147 147 125 125 140 147 119 125 133 147 114 125 130 147 111 125 127 147 108 125 124 147 106 125 121 147 103 125 118 147 100 125 115 147 97.6 125 112 147 95.1 125 109 146 92.9 124 107 145 91.0 123 105 141 89.1 120 103 139 87.4 118 102 138 86.9 117 101 137 86.2 116 101 135 85.6 115 … … … … 29 30 31 32 138 138 138 138 130 138 130 138 121 138 121 138 116 138 116 138 111 138 111 138 107 138 107 138 103 138 103 138 100 136 100 136 97.0 132 97.0 132 94.2 127 94.2 127 91.7 124 91.7 124 89.6 121 89.6 121 87.7 119 87.7 119 86.0 116 86.0 116 84.7 114 84.7 114 82.9 112 82.9 112 81.0 110 81.0 110 … … … … 33 34 35 36 37 161 161 161 161 161 161 152 161 152 161 161 142 161 142 161 161 135 161 135 161 161 130 161 130 161 161 125 161 125 161 161 121 161 121 161 158 117 158 117 158 153 113 153 113 153 148 110 148 110 148 145 107 145 107 145 142 104 142 104 142 138 102 138 102 138 135 100 135 100 135 133 98.5 133 98.5 133 130 96.6 130 96.6 130 128 94.8 128 94.8 128 … … … … … 38 39 40 41 42 43 137 137 161 161 137 137 129 137 152 161 129 137 121 137 142 161 121 137 115 137 135 161 115 137 111 137 130 161 111 137 107 137 125 161 107 137 103 137 121 161 103 137 99.3 135 117 158 99.3 135 96.3 130 113 153 96.3 130 93.5 126 110 148 93.5 126 91.0 123 107 145 91.0 123 88.9 120 104 142 88.9 120 87.1 117 102 138 87.1 117 85.2 115 100 135 85.2 115 83.4 113 98.5 133 83.4 113 82.1 111 96.6 130 82.1 111 80.9 109 94.8 128 80.9 109 … … … … … … 220 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 10 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 15 16 17 18 19 20 … … … … 126 127 … … … … 95.0 95.0 … … … … 71.4 71.4 … … … … 54.3 54.3 … … … … 41.4 41.4 … … … … 30.6 30.6 … … … … 19.7 19.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 24 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 28 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 30 31 32 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 33 34 35 36 37 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 38 39 40 41 42 43 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 221 (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 35Ni – 35Fe – 20Cr – Cb 35Ni – 35Fe – 20Cr – Cb 35Ni – 35Fe – 20Cr – Cb 35Ni – 35Fe – 20Cr – Cb Forgings Forgings Plate Plate SB-462 SB-462 SB-463 SB-463 … … … … N08020 N08020 N08020 N08020 Annealed Annealed Annealed Annealed 5 6 7 8 35Ni – 35Fe – 20Cr – Cb 35Ni – 35Fe – 20Cr – Cb 35Ni – 35Fe – 20Cr – Cb 35Ni – 35Fe – 20Cr – Cb Bar Bar Smls. pipe & tube Smls. pipe & tube SB-473 SB-473 SB-729 SB-729 … … … … N08020 N08020 N08020 N08020 Annealed Annealed Annealed Annealed 9 10 11 35Ni – 35Fe – 20Cr – Cb 35Ni – 35Fe – 20Cr – Cb 35Ni – 35Fe – 20Cr – Cb Wld. pipe Wld. pipe Wld. pipe SB-464 SB-464 SB-464 … … … N08020 N08020 N08020 Wld. ann. Wld. ann. Wld. ann. 12 13 14 15 35Ni – 35Fe – 20Cr – Cb 35Ni – 35Fe – 20Cr – Cb 35Ni – 35Fe – 20Cr – Cb 35Ni – 35Fe – 20Cr – Cb Wld. tube Wld. tube Wld. tube Smls. & wld. fittings SB-468 SB-468 SB-468 SB-366 … … … … N08020 N08020 N08020 N08020 Wld. ann. Wld. ann. Wld. ann. Annealed 16 17 18 19 20 21 37Ni – 33Fe – 23Cr – 4Mo – Cu 37Ni – 33Fe – 23Cr – 4Mo – Cu 37Ni – 33Fe – 23Cr – 4Mo – Cu 37Ni – 33Fe – 23Cr – 4Mo – Cu 37Ni – 33Fe – 23Cr – 4Mo – Cu 37Ni – 33Fe – 23Cr – 4Mo – Cu Plate, sheet, strip Plate, sheet, strip Wld. pipe Wld. pipe Wld. tube Wld. tube SB-463 SB-463 SB-464 SB-464 SB-468 SB-468 … … … … … … N08024 N08024 N08024 N08024 N08024 N08024 Annealed Annealed Wld. ann. Wld. ann. Wld. ann. Wld. ann. 22 23 24 25 26 27 35Ni – 30Fe – 24Cr – 6Mo – Cu 35Ni – 30Fe – 24Cr – 6Mo – Cu 35Ni – 30Fe – 24Cr – 6Mo – Cu 35Ni – 30Fe – 24Cr – 6Mo – Cu 35Ni – 30Fe – 24Cr – 6Mo – Cu 35Ni – 30Fe – 24Cr – 6Mo – Cu Plate, sheet, strip Plate, sheet, strip Wld. pipe Wld. pipe Wld. tube Wld. tube SB-463 SB-463 SB-464 SB-464 SB-468 SB-468 … … … … … … N08026 N08026 N08026 N08026 N08026 N08026 Annealed Annealed Wld. ann. Wld. ann. Wld. ann. Wld. ann. 28 29 30 31 31Ni – 31Fe – 29Cr – Mo 31Ni – 31Fe – 29Cr – Mo 31Ni – 31Fe – 29Cr – Mo 31Ni – 31Fe – 29Cr – Mo Smls. tube Smls. tube Plate, sheet, strip Plate, sheet, strip SB-668 SB-668 SB-709 SB-709 … … … … N08028 N08028 N08028 N08028 Annealed Annealed Annealed Annealed 32 33 34 31Ni – 33Fe – 27Cr – 6.5Mo – Cu – N 31Ni – 33Fe – 27Cr – 6.5Mo – Cu – N 31Ni – 33Fe – 27Cr – 6.5Mo – Cu – N Smls. & wld. fittings Forged fittings Forged fittings SB-366 SB-462 SB-462 … … … N08031 N08031 N08031 Solution ann. Solution ann. Solution ann. 35 36 37 38 31Ni – 33Fe – 27Cr – 6.5Mo – Cu – N 31Ni – 33Fe – 27Cr – 6.5Mo – Cu – N 31Ni – 33Fe – 27Cr – 6.5Mo – Cu – N 31Ni – 33Fe – 27Cr – 6.5Mo – Cu – N Forgings Forgings Rod Rod SB-564 SB-564 SB-581 SB-581 … … … … N08031 N08031 N08031 N08031 Solution ann. Solution ann. Solution ann. Solution ann. 39 40 41 42 31Ni – 33Fe – 27Cr – 6.5Mo – Cu – N 31Ni – 33Fe – 27Cr – 6.5Mo – Cu – N 31Ni – 33Fe – 27Cr – 6.5Mo – Cu – N 31Ni – 33Fe – 27Cr – 6.5Mo – Cu – N Wld. pipe Wld. pipe Smls. pipe & tube Smls. pipe & tube SB-619 SB-619 SB-622 SB-622 … … … … N08031 N08031 N08031 N08031 Solution ann. Solution ann. Solution ann. Solution ann. Line No. 222 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 … … … … 45 45 45 45 550 550 550 550 240 240 240 240 NP NP NP NP 427 NP NP 427 427 427 427 427 343 343 343 343 NFN-12 NFN-12 NFN-12 NFN-12 G5 … … G5 5 6 7 8 … … … … 45 45 45 45 550 550 550 550 240 240 240 240 NP NP NP NP 427 NP NP NP 427 427 427 427 343 343 343 343 NFN-12 NFN-12 NFN-12 NFN-12 G5 … … G5 9 10 11 … … … 45 45 45 550 550 550 240 240 240 NP NP NP 427 NP NP NP 427 427 NP 343 343 NFN-12 NFN-12 NFN-12 G5, W5 G14 G5, G14 12 13 14 15 … … … … 45 45 45 45 550 550 550 585 240 240 240 275 NP NP NP NP 427 NP NP NP NP 427 427 427 NP 343 343 343 NFN-12 NFN-12 NFN-12 NFN-12 G5, W5 G14 G5, G14 G5, W12 16 17 18 19 20 21 … … … … … … 45 45 45 45 45 45 550 550 550 550 550 550 240 240 240 240 240 240 NP NP NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 427 343 343 343 343 343 343 NFN-13 NFN-13 NFN-13 NFN-13 NFN-13 NFN-13 … G5 G14 G5, G14 G14 G5, G14 22 23 24 25 26 27 … … … … … … 45 45 45 45 45 45 550 550 550 550 550 550 240 240 240 240 240 240 NP NP NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 427 343 343 343 343 343 343 NFN-13 NFN-13 NFN-13 NFN-13 NFN-13 NFN-13 … G5 G14 G5, G14 G14 G5, G14 28 29 30 31 … … … … 45 45 45 45 505 505 505 505 215 215 215 215 NP NP NP NP 316 316 NP NP 454 454 454 454 343 343 343 343 NFN-13 NFN-13 NFN-13 NFN-13 … G5 … G5 32 33 34 … … … 45 45 45 650 650 650 275 275 275 NP NP NP NP NP NP 427 427 427 NP NP NP NFN-11 NFN-11 NFN-11 G5, W12 … G5 35 36 37 38 … … … … 45 45 45 45 650 650 650 650 275 275 275 275 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-11 NFN-11 NFN-11 NFN-11 … G5 … G5 39 40 41 42 … … … … 45 45 45 45 650 650 650 650 275 275 275 275 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-11 NFN-11 NFN-11 NFN-11 G14 G5, G14 … G5 223 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 158 158 158 158 158 149 149 158 158 141 141 158 157 138 138 157 156 136 136 156 154 133 133 154 153 131 131 153 153 128 128 153 152 126 126 152 152 124 124 152 152 123 123 152 152 122 122 152 152 120 120 152 151 120 120 151 150 119 119 150 150 116 116 150 150 114 114 150 … … … … 5 6 7 8 158 158 158 158 158 149 149 158 158 141 141 158 157 138 138 157 156 136 136 156 154 133 133 154 153 131 131 153 153 128 128 153 152 126 126 152 152 124 124 152 152 123 123 152 152 122 122 152 152 120 120 152 151 120 120 151 150 119 119 150 150 116 116 150 150 114 114 150 … … … … 9 10 11 158 134 134 158 127 134 158 120 134 157 117 133 156 115 132 154 113 131 153 111 130 153 109 130 152 108 130 152 106 130 152 104 130 152 103 129 152 103 129 151 102 128 150 101 128 150 98.7 128 150 96.9 128 … … … 12 13 14 15 158 134 134 158 158 127 134 158 158 120 134 158 157 117 133 157 156 115 132 156 154 113 131 154 153 111 130 153 153 109 130 153 152 108 130 152 152 106 130 152 152 104 130 152 152 103 129 152 152 103 129 152 151 102 128 151 150 101 128 150 150 98.7 128 150 150 96.9 128 150 … … … … 16 17 18 19 20 21 158 158 134 134 134 134 150 158 127 134 127 134 141 158 119 134 119 134 136 157 115 133 115 133 132 156 112 132 112 132 129 154 109 131 109 131 125 151 107 129 107 129 122 150 104 127 104 127 119 148 101 126 101 126 115 146 98.3 125 98.3 125 112 144 95.5 123 95.5 123 109 143 92.8 122 92.8 122 107 142 90.5 120 90.5 120 104 140 88.6 119 88.6 119 102 138 86.8 117 86.8 117 101 135 85.6 115 85.6 115 99.5 133 84.3 113 84.3 113 … … … … … … 22 23 24 25 26 27 158 158 134 134 134 134 150 158 128 134 128 134 141 158 120 134 120 134 136 157 115 133 115 133 131 155 111 132 111 132 126 153 107 130 107 130 121 151 103 128 103 128 117 149 99.8 126 99.8 126 114 147 96.4 125 96.4 125 110 145 93.4 123 93.4 123 107 143 91.0 122 91.0 122 105 141 88.9 120 88.9 120 102 138 87.1 117 87.1 117 99.6 135 85.2 115 85.2 115 97.8 132 83.4 112 83.4 112 96.0 130 82.1 110 82.1 110 94.1 127 80.9 109 80.9 109 … … … … … … 28 29 30 31 143 143 143 143 136 143 136 143 129 143 129 143 125 141 125 141 122 138 122 138 118 136 118 136 114 133 114 133 111 131 111 131 107 130 107 130 104 128 104 128 101 126 101 126 98.3 125 98.3 125 95.9 124 95.9 124 93.3 122 93.3 122 90.2 121 90.2 121 88.4 119 88.4 119 86.0 116 86.0 116 83.4 113 83.4 113 32 33 34 184 184 184 184 167 184 184 149 184 181 142 181 178 136 178 174 131 174 170 127 170 166 123 166 162 120 162 159 117 159 155 115 155 152 112 152 149 111 149 146 109 146 144 107 144 142 105 142 139 103 139 … … … 35 36 37 38 184 184 184 184 167 184 167 184 149 184 149 184 142 181 142 181 136 178 136 178 131 174 131 174 127 170 127 170 123 166 123 166 120 162 120 162 117 159 117 159 115 155 115 155 112 152 112 152 111 149 111 149 109 146 109 146 107 144 107 144 105 142 105 142 103 139 103 139 … … … … 39 40 41 42 157 157 184 184 142 157 167 184 127 156 149 184 121 154 142 181 115 151 136 178 112 147 131 174 108 144 127 170 105 141 123 166 102 138 120 162 99.7 135 117 159 97.0 132 115 155 95.4 129 112 152 94.0 126 111 149 92.2 125 109 146 90.9 123 107 144 89.1 120 105 142 87.2 118 103 139 … … … … 224 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 10 11 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 12 13 14 15 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 20 21 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 25 26 27 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 31 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 35 36 37 38 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 39 40 41 42 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 225 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 31Ni – 33Fe – 27Cr – 6.5Mo – Cu – N 31Ni – 33Fe – 27Cr – 6.5Mo – Cu – N 31Ni – 33Fe – 27Cr – 6.5Mo – Cu – N 31Ni – 33Fe – 27Cr – 6.5Mo – Cu – N Plate, sheet, strip Plate, sheet, strip Wld. tube Wld. tube SB-625 SB-625 SB-626 SB-626 … … … … N08031 N08031 N08031 N08031 Solution ann. Solution ann. Solution ann. Solution ann. 5 6 7 37Ni – 33Fe – 25Cr 37Ni – 33Fe – 25Cr 37Ni – 33Fe – 25Cr Condenser tubes Condenser tubes Smls. & wld. fittings SB-163 SB-163 SB-366 … … … N08120 N08120 N08120 Solution ann. Solution ann. Solution ann. 8 9 10 11 12 13 37Ni – 33Fe – 25Cr 37Ni – 33Fe – 25Cr 37Ni – 33Fe – 25Cr 37Ni – 33Fe – 25Cr 37Ni – 33Fe – 25Cr 37Ni – 33Fe – 25Cr Smls. pipe & tube Smls. pipe & tube Bar, rod Bar, rod Plate, sheet, strip Plate, sheet, strip SB-407 SB-407 SB-408 SB-408 SB-409 SB-409 … … … … … … N08120 N08120 N08120 N08120 N08120 N08120 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 14 15 16 17 18 19 37Ni – 33Fe – 25Cr 37Ni – 33Fe – 25Cr 37Ni – 33Fe – 25Cr 37Ni – 33Fe – 25Cr 37Ni – 33Fe – 25Cr 37Ni – 33Fe – 25Cr Wld. pipe Wld. pipe Wld. tube Wld. tube Forgings Forgings SB-514 SB-514 SB-515 SB-515 SB-564 SB-564 … … … … … … N08120 N08120 N08120 N08120 N08120 N08120 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 20 21 22 23 26Ni – 43Fe – 22Cr – 5Mo 26Ni – 43Fe – 22Cr – 5Mo 26Ni – 43Fe – 22Cr – 5Mo 26Ni – 43Fe – 22Cr – 5Mo Wld. pipe Wld. pipe Plate, sheet, strip Plate, sheet, strip SB-619 SB-619 SB-620 SB-620 … … … … N08320 N08320 N08320 N08320 Solution ann. Solution ann. Solution ann. Solution ann. 24 25 26 27 28 29 26Ni – 43Fe – 22Cr – 5Mo 26Ni – 43Fe – 22Cr – 5Mo 26Ni – 43Fe – 22Cr – 5Mo 26Ni – 43Fe – 22Cr – 5Mo 26Ni – 43Fe – 22Cr – 5Mo 26Ni – 43Fe – 22Cr – 5Mo Rod Rod Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-621 SB-621 SB-622 SB-622 SB-626 SB-626 … … … … … … N08320 N08320 N08320 N08320 N08320 N08320 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 30 31 32 33 35Ni – 19Cr – 11⁄4Si 35Ni – 19Cr – 11⁄4Si 35Ni – 19Cr – 11⁄4Si 35Ni – 19Cr – 11⁄4Si Bar Bar Bar Bar SB-511 SB-511 SB-511 SB-511 … … … … N08330 N08330 N08330 N08330 … … … … 34 35 36 37 35Ni – 19Cr – 11⁄4Si 35Ni – 19Cr – 11⁄4Si 35Ni – 19Cr – 11⁄4Si 35Ni – 19Cr – 11⁄4Si Pipe Pipe Plate Plate SB-535 SB-535 SB-536 SB-536 … … … … N08330 N08330 N08330 N08330 … … … … 38 39 40 35Ni – 19Cr – 11⁄4Si 35Ni – 19Cr – 11⁄4Si 35Ni – 19Cr – 11⁄4Si Smls. & wld. fittings Smls. & wld. pipe Smls. & wld. pipe SB-366 SB-535 SB-535 … … … N08330 N08330 N08330 Annealed Annealed Annealed 41 42 43 44 35Ni – 19Cr – 11⁄4Si 35Ni – 19Cr – 11⁄4Si 35Ni – 19Cr – 11⁄4Si 35Ni – 19Cr – 11⁄4Si Plate, sheet, strip Plate, sheet, strip Wld. pipe Wld. pipe SB-536 SB-536 SB-710 SB-710 … … … … N08330 N08330 N08330 N08330 Annealed Annealed Annealed Annealed Line No. 226 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 … … … … 45 45 45 45 650 650 650 650 275 275 275 275 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-11 NFN-11 NFN-11 NFN-11 … G5 G14 G5, G14 5 6 7 … … … 45 45 45 621 621 621 276 276 276 NP NP NP NP NP NP 899 899 899 NP NP NP NFN-9 NFN-9 NFN-9 G4, G14, T16 G4, G5, G14, T15 G4, G5, T15, W12 8 9 10 11 12 13 … … … … … … 45 45 45 45 45 45 621 621 621 621 621 621 276 276 276 276 276 276 NP NP NP NP NP NP NP NP NP NP NP NP 899 899 899 899 899 899 NP NP NP NP NP NP NFN-9 NFN-9 NFN-9 NFN-9 NFN-9 NFN-9 G4, T16 G4, G5, T15 G4, T16 G4, G5, T15 G4, T16 G4, G5, T15 14 15 16 17 18 19 … … … … … … 45 45 45 45 45 45 621 621 621 621 621 621 276 276 276 276 276 276 NP NP NP NP NP NP NP NP NP NP NP NP 899 899 899 899 899 899 NP NP NP NP NP NP NFN-9 NFN-9 NFN-9 NFN-9 NFN-9 NFN-9 G4, G14, T16 G4, G5, G14, T15 G4, G14, T16 G4, G5, G14, T15 G4, T16 G4, G5, T15 20 21 22 23 … … … … 45 45 45 45 515 515 515 515 195 195 195 195 NP NP NP NP NP NP NP NP 427 427 427 427 343 343 343 343 NFN-13 NFN-13 NFN-13 NFN-13 G14 G5, G14 … G5 24 25 26 27 28 29 … … … … … … 45 45 45 45 45 45 515 515 515 515 515 515 195 195 195 195 195 195 NP NP NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 427 343 343 343 343 343 343 NFN-13 NFN-13 NFN-13 NFN-13 NFN-13 NFN-13 … G5 … G5 G14 G5, G14 30 31 32 33 … … … … 46 46 46 46 690 485 485 485 205 205 205 205 816 816 NP NP NP NP NP NP NP NP 899 899 NP NP 343 343 NFN-13 NFN-13 NFN-13 NFN-13 G2, H2, T14 G2, G5, H2, T12 G4, H1, T14 G4, G5, H1, T12 34 35 36 37 … … … … 46 46 46 46 485 485 485 485 205 205 205 205 816 816 816 816 NP NP NP NP NP NP NP NP NP NP NP NP NFN-13 NFN-13 NFN-13 NFN-13 G2, H2, T14 G2, G5, H2, T12 G2, H2, T14 G2, G5, H2, T12 38 39 40 … … … 46 46 46 485 485 485 205 205 205 NP NP NP NP NP NP 899 816 816 343 343 343 NFN-13 NFN-13 NFN-13 G4, G5, T12, W12 H1, T14, W12 G5, H1, T12, W12 41 42 43 44 … … … … 46 46 46 46 485 485 485 485 205 205 205 205 NP NP NP NP NP NP NP NP 899 899 899 899 343 343 343 343 NFN-13 NFN-13 NFN-13 NFN-13 G4, H1, T14 G4, G5, H1, T12 G4, G14, H1, T14 G4, G5, G14, H1, T12 227 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 184 184 157 157 167 184 142 157 149 184 127 156 142 181 121 154 136 178 115 151 131 174 112 147 127 170 108 144 123 166 105 141 120 162 102 138 117 159 99.7 135 115 155 97.0 132 112 152 95.4 129 111 149 94.0 126 109 146 92.2 125 107 144 90.9 123 105 142 89.1 120 103 139 87.2 118 … … … … 5 6 7 177 177 177 172 177 177 162 177 177 155 176 176 149 173 173 143 170 170 138 167 167 134 166 166 130 164 164 126 163 163 123 162 162 121 162 162 119 161 161 117 158 158 116 157 157 115 155 155 114 154 154 113 153 153 8 9 10 11 12 13 177 177 177 177 177 177 172 177 172 177 172 177 162 177 162 177 162 177 155 176 155 176 155 176 149 173 149 173 149 173 143 170 143 170 143 170 138 167 138 167 138 167 134 166 134 166 134 166 130 164 130 164 130 164 126 163 126 163 126 163 123 162 123 162 123 162 121 162 121 162 121 162 119 161 119 161 119 161 117 158 117 158 117 158 116 157 116 157 116 157 115 155 115 155 115 155 114 154 114 154 114 154 113 153 113 153 113 153 14 15 16 17 18 19 150 150 150 150 177 177 146 150 146 150 172 177 138 150 138 150 162 177 132 150 132 150 155 176 127 147 127 147 149 173 122 145 122 145 143 170 117 142 117 142 138 167 114 141 114 141 134 166 111 139 111 139 130 164 107 139 107 139 126 163 105 138 105 138 123 162 103 138 103 138 121 162 101 137 101 137 119 161 99.5 134 99.5 134 117 158 98.6 133 98.6 133 116 157 97.8 132 97.8 132 115 155 96.9 131 96.9 131 114 154 96.1 130 96.1 130 113 153 20 21 22 23 110 110 129 129 105 110 124 129 101 110 118 129 98.0 110 115 129 95.7 110 112 129 93.3 110 109 129 90.8 110 107 129 88.2 110 104 129 85.7 110 101 129 83.6 109 98.5 129 81.8 109 96.4 128 79.9 108 94.4 127 78.2 106 92.5 125 77.0 104 90.8 122 75.8 103 89.6 121 74.5 101 87.7 119 73.3 98.9 85.8 117 … … … … 24 25 26 27 28 29 129 129 129 129 110 110 124 129 124 129 105 110 118 129 118 129 101 110 115 129 115 129 98.0 110 112 129 112 129 95.7 110 109 129 109 129 93.3 110 107 129 107 129 90.8 110 104 129 104 129 88.2 110 101 129 101 129 85.7 110 98.5 129 98.5 129 83.6 109 96.4 128 96.4 128 81.8 109 94.4 127 94.4 127 79.9 108 92.5 125 92.5 125 78.2 106 90.8 122 90.8 122 77.0 104 89.6 121 89.6 121 75.8 103 87.7 119 87.7 119 74.5 101 85.8 117 85.8 117 73.3 98.9 … … … … … … 30 31 32 33 138 138 138 138 130 138 130 138 121 138 121 138 116 138 116 138 113 138 113 138 110 137 110 137 107 135 107 135 105 134 105 134 102 134 102 134 100 133 100 133 97.8 132 97.8 132 95.8 129 95.8 129 94.0 127 94.0 127 92.1 124 92.1 124 90.3 122 90.3 122 89.0 120 89.0 120 87.2 118 87.2 118 85.9 116 85.9 116 34 35 36 37 138 138 138 138 130 138 130 138 121 138 121 138 116 138 116 138 113 138 113 138 110 137 110 137 107 135 107 135 105 134 105 134 102 134 102 134 100 133 100 133 97.8 132 97.8 132 95.8 129 95.8 129 94.0 127 94.0 127 92.1 124 92.1 124 90.3 122 90.3 122 89.0 120 89.0 120 87.2 118 87.2 118 85.9 116 85.9 116 38 39 40 138 138 138 138 130 138 138 121 138 138 116 138 138 113 138 137 110 137 135 107 135 134 105 134 134 102 134 133 100 133 132 97.8 132 129 95.8 129 127 94.0 127 124 92.1 124 122 90.3 122 120 89.0 120 118 87.2 118 116 85.9 116 41 42 43 44 138 138 117 117 130 138 110 117 121 138 102 117 116 138 98.9 117 113 138 96.4 117 110 137 93.9 116 107 135 91.4 115 105 134 89.2 115 102 134 87.0 114 100 133 84.9 113 97.8 132 83.0 112 95.8 129 81.6 110 94.0 127 80.2 108 92.1 124 78.4 106 90.3 122 77.2 104 89.0 120 75.3 102 87.2 118 74.0 100 85.9 116 72.8 98.6 228 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 113 153 153 113 152 152 112 152 152 112 143 143 112 117 117 96.2 96.2 96.2 79.3 79.3 79.3 65.6 65.6 65.6 54.4 54.4 54.4 45.0 45.0 45.0 37.2 37.2 37.2 30.6 30.6 30.6 25.1 25.1 25.1 20.5 20.5 20.5 16.5 16.5 16.5 13.0 13.0 13.0 9.8 9.8 9.8 8 9 10 11 12 13 113 153 113 153 113 153 113 152 113 152 113 152 112 152 112 152 112 152 112 143 112 143 112 143 112 117 112 117 112 117 96.2 96.2 96.2 96.2 96.2 96.2 79.3 79.3 79.3 79.3 79.3 79.3 65.6 65.6 65.6 65.6 65.6 65.6 54.4 54.4 54.4 54.4 54.4 54.4 45.0 45.0 45.0 45.0 45.0 45.0 37.2 37.2 37.2 37.2 37.2 37.2 30.6 30.6 30.6 30.6 30.6 30.6 25.1 25.1 25.1 25.1 25.1 25.1 20.5 20.5 20.5 20.5 20.5 20.5 16.5 16.5 16.5 16.5 16.5 16.5 13.0 13.0 13.0 13.0 13.0 13.0 9.8 9.8 9.8 9.8 9.8 9.8 14 15 16 17 18 19 96.1 130 96.1 130 113 153 96.1 129 96.1 129 113 152 95.2 129 95.2 129 112 152 95.2 122 95.2 122 112 143 95.2 99.5 95.2 99.5 112 117 81.8 81.8 81.8 81.8 96.2 96.2 67.4 67.4 67.4 67.4 79.3 79.3 55.8 55.8 55.8 55.8 65.6 65.6 46.2 46.2 46.2 46.2 54.4 54.4 38.3 38.3 38.3 38.3 45.0 45.0 31.6 31.6 31.6 31.6 37.2 37.2 26.0 26.0 26.0 26.0 30.6 30.6 21.3 21.3 21.3 21.3 25.1 25.1 17.4 17.4 17.4 17.4 20.5 20.5 14.0 14.0 14.0 14.0 16.5 16.5 11.1 11.1 11.1 11.1 13.0 13.0 8.33 8.33 8.33 8.33 9.8 9.8 20 21 22 23 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 24 25 26 27 28 29 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 30 31 32 33 84.2 112 84.2 112 82.6 100 82.6 100 77.9 78.1 77.9 78.1 63.7 63.7 63.7 63.7 50.5 50.5 50.5 50.5 39.9 39.9 39.9 39.9 32.1 32.1 32.1 32.1 26.5 26.5 26.5 26.5 22.1 22.1 22.1 22.1 17.8 17.8 17.8 17.8 13.7 13.7 13.7 13.7 11.3 11.3 11.3 11.3 9.12 9.12 9.12 9.12 7.12 7.12 7.12 7.12 … … 5.88 5.88 … … 4.48 4.48 … … 3.26 3.26 34 35 36 37 84.2 112 84.2 112 82.6 100 82.6 100 77.9 78.1 77.9 78.1 63.7 63.7 63.7 63.7 50.5 50.5 50.5 50.5 39.9 39.9 39.9 39.9 32.1 32.1 32.1 32.1 26.5 26.5 26.5 26.5 22.1 22.1 22.1 22.1 17.8 17.8 17.8 17.8 13.7 13.7 13.7 13.7 11.3 11.3 11.3 11.3 9.12 9.12 9.12 9.12 7.12 7.12 7.12 7.12 … … … … … … … … … … … … 38 39 40 112 84.2 112 100 82.6 100 78.1 77.9 78.1 63.7 63.7 63.7 50.5 50.5 50.5 39.9 39.9 39.9 32.1 32.1 32.1 26.5 26.5 26.5 22.1 22.1 22.1 17.8 17.8 17.8 13.7 13.7 13.7 11.3 11.3 11.3 9.12 9.12 9.12 7.12 7.12 7.12 5.88 … … 4.48 … … 3.26 … … 41 42 43 44 84.2 112 71.5 95.7 82.6 100 70.2 85.3 77.9 78.1 64.9 66.4 63.7 63.7 54.4 54.4 50.5 50.5 42.7 42.7 39.9 39.9 34.0 34.0 32.1 32.1 27.3 27.3 26.5 26.5 22.3 22.3 22.1 22.1 18.6 18.6 17.8 17.8 14.9 14.9 13.7 13.7 11.3 11.3 11.3 11.3 9.58 9.58 9.12 9.12 7.91 7.91 7.12 7.12 5.95 5.95 5.88 5.88 5.03 5.03 4.48 4.48 3.82 3.82 3.26 3.26 2.78 2.78 229 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 5 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N Smls. & wld. fittings Forgings Forgings Forgings Forgings SB-366 SB-462 SB-462 SB-564 SB-564 … … … … … N08367 N08367 N08367 N08367 N08367 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 6 7 8 9 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N Wld. pipe Wld. pipe Wld. tube Wld. tube SB-675 SB-675 SB-676 SB-676 … … … … N08367 N08367 N08367 N08367 Solution ann. Solution ann. Solution ann. Solution ann. 10 11 12 13 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N Plate, sheet, strip Plate, sheet, strip Smls. pipe & tube Smls. pipe & tube SB-688 SB-688 SB-690 SB-690 … … … … N08367 N08367 N08367 N08367 Solution ann. Solution ann. Solution ann. Solution ann. 14 15 16 17 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N Bar, rod, wire Bar, rod, wire Wld. pipe Wld. pipe SB-691 SB-691 SB-804 SB-804 … … … … N08367 N08367 N08367 N08367 Solution ann. Solution ann. Solution ann. Solution ann. 18 19 20 21 22 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N Smls. & wld. fittings Wld. pipe Wld. pipe Wld. tube Wld. tube SB-366 SB-675 SB-675 SB-676 SB-676 … … … … … N08367 N08367 N08367 N08367 N08367 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 23 24 25 26 27 28 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N 46Fe – 24Ni – 21Cr – 6Mo – Cu – N Plate, sheet, strip Plate, sheet, strip Smls. pipe & tube Smls. pipe & tube Wld. pipe Wld. pipe SB-688 SB-688 SB-690 SB-690 SB-804 SB-804 … … … … … … N08367 N08367 N08367 N08367 N08367 N08367 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 29 46Fe – 24Ni – 21Cr – 6Mo – Cu – N Castings SA-351 CN3MN J94651 Solution ann. 30 31 32 25Ni – 47Fe – 21Cr – 5Mo 25Ni – 47Fe – 21Cr – 5Mo 25Ni – 47Fe – 21Cr – 5Mo Plate, sheet, strip Plate, sheet, strip Bar, wire SB-599 SB-599 SB-672 … … … N08700 N08700 N08700 Solution ann. Solution ann. Solution ann. 33 32Ni – 45Fe – 20Cr – Cb Castings SA-351 CT15C … As cast 34 35 36 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr Smls. tube Smls. tube Smls. & wld. fittings SB-163 SB-163 SB-366 … … … N08800 N08800 N08800 Annealed Annealed Annealed 37 38 39 40 41 42 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr Smls. pipe & tube Smls. pipe & tube Bar Bar Plate Plate SB-407 SB-407 SB-408 SB-408 SB-409 SB-409 … … … … … … N08800 N08800 N08800 N08800 N08800 N08800 Annealed Annealed Annealed Annealed Annealed Annealed Line No. 230 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 >5 … … … … 45 45 45 45 45 655 655 655 655 655 310 310 310 310 310 NP NP NP NP NP NP 427 427 427 427 427 427 427 427 427 NP 343 343 343 343 NFN-12 NFN-12 NFN-12 NFN-12 NFN-12 G5, W12 … G5 … G5 6 7 8 9 >5 >5 >5 >5 45 45 45 45 655 655 655 655 310 310 310 310 NP NP NP NP 427 427 427 427 427 427 427 427 343 343 343 343 NFN-12 NFN-12 NFN-12 NFN-12 G14 G5, G14 G14 G5, G14 10 11 12 13 >5 >5 >5 >5 45 45 45 45 655 655 655 655 310 310 310 310 NP NP NP NP 427 427 427 427 427 427 427 427 343 343 343 343 NFN-12 NFN-12 NFN-12 NFN-12 … G5 … G5 14 15 16 17 … … >5 >5 45 45 45 45 655 655 655 655 310 310 310 310 NP NP NP NP 427 427 427 427 427 427 427 427 343 343 343 343 NFN-12 NFN-12 NFN-12 NFN-12 … G5 G14 G5, G14 18 19 20 21 22 ≤5 ≤5 ≤5 ≤5 ≤5 45 45 45 45 45 690 690 690 690 690 310 310 310 310 310 NP NP NP NP NP NP 427 427 427 427 427 427 427 427 427 NP 343 343 343 343 NFN-12 NFN-12 NFN-12 NFN-12 NFN-12 G5, W12 G14 G5, G14 G14 G5, G14 23 24 25 26 27 28 ≤5 ≤5 ≤5 ≤5 ≤5 ≤5 45 45 45 45 45 45 690 690 690 690 690 690 310 310 310 310 310 310 NP NP NP NP NP NP 427 427 427 427 427 427 427 427 427 427 427 427 343 343 343 343 343 343 NFN-12 NFN-12 NFN-12 NFN-12 NFN-12 NFN-12 … G5 … G5 G14 G5, G14 29 … 45 550 260 NP 427 427 343 NFN-12 G15 30 31 32 … … … 45 45 45 550 550 550 240 240 240 NP NP NP NP NP NP 343 343 343 343 343 343 NFN-8 NFN-8 NFN-8 … G5 … 33 … 45 435 170 NP NP 871 343 NFN-9 G4, G15 34 35 36 … … … 45 45 45 515 515 515 205 205 205 NP NP NP 427 NP NP 816 816 816 NP NP NP NFN-8 NFN-8 NFN-8 G5, T14 T15 G5, T14, W12 37 38 39 40 41 42 … … … … … … 45 45 45 45 45 45 515 515 515 515 515 515 205 205 205 205 205 205 816 816 816 816 816 816 427 NP 427 NP 427 NP 816 816 816 816 816 816 NP NP NP NP NP NP NFN-8 NFN-8 NFN-8 NFN-8 NFN-8 NFN-8 G5, T14 T15 G5, T14 T15 G5, T14 T15 231 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 5 187 187 187 187 187 185 185 187 185 187 179 179 186 179 186 172 172 182 172 182 164 164 177 164 177 157 157 173 157 173 152 152 170 152 170 147 147 167 147 167 143 143 165 143 165 139 139 163 139 163 136 136 161 136 161 133 133 160 133 160 130 130 159 130 159 128 128 158 128 158 126 126 157 126 157 124 124 156 124 156 122 122 155 122 155 … … … … … 6 7 8 9 159 159 159 159 157 159 157 159 152 159 152 159 145 155 145 155 139 150 139 150 134 147 134 147 130 144 130 144 125 142 125 142 121 140 121 140 118 138 118 138 115 137 115 137 113 136 113 136 110 135 110 135 109 134 109 134 107 134 107 134 106 132 106 132 104 131 104 131 … … … … 10 11 12 13 187 187 187 187 185 187 185 187 179 186 179 186 172 182 172 182 164 177 164 177 157 173 157 173 152 170 152 170 147 167 147 167 143 165 143 165 139 163 139 163 136 161 136 161 133 160 133 160 130 159 130 159 128 158 128 158 126 157 126 157 124 156 124 156 122 155 122 155 … … … … 14 15 16 17 187 187 159 159 185 187 157 159 179 186 152 159 172 182 145 155 164 177 139 150 157 173 134 147 152 170 130 144 147 167 125 142 143 165 121 140 139 163 118 138 136 161 115 137 133 160 113 136 130 159 110 135 128 158 109 134 126 157 107 134 124 156 106 132 122 155 104 131 … … … … 18 19 20 21 22 197 168 168 168 168 189 160 168 160 168 179 151 167 151 167 171 145 163 145 163 164 139 158 139 158 157 134 155 134 155 152 130 152 130 152 147 125 150 125 150 143 121 148 121 148 139 118 146 118 146 136 115 144 115 144 133 113 143 113 143 130 110 142 110 142 128 109 141 109 141 126 107 141 107 141 124 106 139 106 139 122 104 138 104 138 … … … … … 23 24 25 26 27 28 197 197 197 197 168 168 189 197 189 197 160 168 179 197 179 197 151 167 171 192 171 192 145 163 164 186 164 186 139 158 157 181 157 181 134 155 152 178 152 178 130 152 147 176 147 176 125 150 143 173 143 173 121 148 139 171 139 171 118 146 136 170 136 170 115 144 133 168 133 168 113 143 130 167 130 167 110 142 128 166 128 166 109 141 126 165 126 165 107 141 124 164 124 164 106 139 122 163 122 163 104 138 … … … … … … 29 158 154 146 138 129 123 117 113 110 106 104 102 101 99.9 99.2 98.0 96.7 … 30 31 32 158 158 158 152 158 152 143 158 143 137 157 137 131 156 131 126 154 126 123 152 123 120 150 120 118 149 118 117 148 117 116 148 116 112 148 112 108 148 108 … … … … … … … … … … … … … … … 33 115 111 108 106 105 104 103 102 101 100 98.9 97.2 95.4 94.3 93.0 91.8 90.5 89.3 34 35 36 138 138 138 138 132 138 138 127 138 138 124 138 138 123 138 138 121 138 138 119 138 138 117 138 138 116 138 138 115 138 138 113 138 138 112 138 138 111 138 138 109 138 138 108 138 138 107 138 138 106 138 138 104 138 37 38 39 40 41 42 138 138 138 138 138 138 138 132 138 132 138 132 138 127 138 127 138 127 138 124 138 124 138 124 138 123 138 123 138 123 138 121 138 121 138 121 138 119 138 119 138 119 138 117 138 117 138 117 138 116 138 116 138 116 138 115 138 115 138 115 138 113 138 113 138 113 138 112 138 112 138 112 138 111 138 111 138 111 138 109 138 109 138 109 138 108 138 108 138 108 138 107 138 107 138 107 138 106 138 106 138 106 138 104 138 104 138 104 232 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 17 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 18 19 20 21 22 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 23 24 25 26 27 28 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 … … … … … … … … … … … … … … … … … 30 31 32 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 33 88.0 84.0 74.8 66.7 59.5 52.7 45.9 39.7 34.0 28.9 24.4 20.4 17.0 14.2 11.8 9.26 … 34 35 36 138 103 138 137 102 137 131 101 131 108 98.1 108 85.0 85.0 85.0 64.4 64.4 64.4 44.8 44.8 44.8 30.0 30.0 30.0 15.5 15.5 15.5 11.3 11.3 11.3 8.82 8.82 8.82 6.98 6.98 6.98 6.43 6.43 6.43 5.00 5.00 5.00 … … … … … … … … … 37 38 39 40 41 42 138 103 138 103 138 103 137 102 137 102 137 102 131 101 131 101 131 101 108 98.1 108 98.1 108 98.1 85.0 85.0 85.0 85.0 85.0 85.0 64.4 64.4 64.4 64.4 64.4 64.4 44.8 44.8 44.8 44.8 44.8 44.8 30.0 30.0 30.0 30.0 30.0 30.0 15.5 15.5 15.5 15.5 15.5 15.5 11.3 11.3 11.3 11.3 11.3 11.3 8.82 8.82 8.82 8.82 8.82 8.82 6.98 6.98 6.98 6.98 6.98 6.98 6.43 6.43 6.43 6.43 6.43 6.43 5.00 5.00 5.00 5.00 5.00 5.00 … … … … … … … … … … … … … … … … … … 233 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 5 6 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr Wld. pipe Wld. pipe Wld. tube Wld. tube Forgings Forgings SB-514 SB-514 SB-515 SB-515 SB-564 SB-564 … … … … … … N08800 N08800 N08800 N08800 N08800 N08800 Annealed Annealed Annealed Annealed Annealed Annealed 7 8 9 10 32Ni – 44Fe – 21Cr 32Ni – 44Fe – 21Cr 32Ni – 44Fe – 21Cr 32Ni – 44Fe – 21Cr Smls. tube Smls. tube Smls. pipe & tube Smls. pipe & tube SB-163 SB-163 SB-407 SB-407 … … … … N08801 N08801 N08801 N08801 Ann./stabilized Ann./stabilized Ann./stabilized Ann./stabilized 11 12 13 14 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr Smls. tube Smls. tube Smls. pipe & tube Smls. pipe & tube SB-163 SB-163 SB-407 SB-407 … … … … N08810 N08810 N08810 N08810 Annealed Sol. treat./ann. Annealed Hot fin./ann. 15 16 17 18 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr Bar Bar Plate Plate SB-408 SB-408 SB-409 SB-409 … … … … N08810 N08810 N08810 N08810 Annealed Sol. treat./ann. Annealed Sol. treat./ann. 19 20 21 22 23 24 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr Wld. pipe Wld. pipe Wld. tube Wld. tube Forgings Forgings SB-514 SB-514 SB-515 SB-515 SB-564 SB-564 … … … … … … N08810 N08810 N08810 N08810 N08810 N08810 Annealed Annealed Annealed Annealed Annealed Sol. treat./ann. 25 26 27 28 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr Smls. tube Smls. tube Smls. pipe & tube Smls. pipe & tube SB-163 SB-163 SB-407 SB-407 … … … … N08811 N08811 N08811 N08811 Annealed Annealed Annealed Annealed 29 30 31 32 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr Bar Bar Plate Plate SB-408 SB-408 SB-409 SB-409 … … … … N08811 N08811 N08811 N08811 Annealed Annealed Annealed Annealed 33 34 35 36 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr 33Ni – 42Fe – 21Cr Wld. tube Wld. tube Forgings Forgings SB-515 SB-515 SB-564 SB-564 … … … … N08811 N08811 N08811 N08811 Annealed Annealed Annealed Annealed 37 38 39 42Ni – 21.5Cr – 3Mo – 2.3Cu 42Ni – 21.5Cr – 3Mo – 2.3Cu 42Ni – 21.5Cr – 3Mo – 2.3Cu Smls. tube Smls. tube Smls. & wld. fittings SB-163 SB-163 SB-366 … … … N08825 N08825 N08825 Annealed Annealed Annealed 40 41 42 43 44 45 42Ni – 21.5Cr – 3Mo – 2.3Cu 42Ni – 21.5Cr – 3Mo – 2.3Cu 42Ni – 21.5Cr – 3Mo – 2.3Cu 42Ni – 21.5Cr – 3Mo – 2.3Cu 42Ni – 21.5Cr – 3Mo – 2.3Cu 42Ni – 21.5Cr – 3Mo – 2.3Cu Smls. pipe & tube Smls. pipe & tube Plate Plate Bar, rod Bar, rod SB-423 SB-423 SB-424 SB-424 SB-425 SB-425 … … … … … … N08825 N08825 N08825 N08825 N08825 N08825 Cold worked/ann. Cold worked/ann. Annealed Annealed Annealed Annealed Line No. 234 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 6 … … … … … … 45 45 45 45 45 45 515 515 515 515 515 515 205 205 205 205 205 205 NP NP 816 816 816 816 NP NP NP NP 427 NP 816 816 816 816 816 816 NP NP NP NP NP NP NFN-8 NFN-8 NFN-8 NFN-8 NFN-8 NFN-8 G14, T15 G5, G14, T14 G5, G14, T14 G14, T15 G5, T14 T15 7 8 9 10 … … … … 45 45 45 45 450 450 450 450 170 170 170 170 566 566 566 566 NP NP NP NP 482 482 482 482 NP NP NP NP NFN-9 NFN-9 NFN-9 NFN-9 H4 G5, H4 H4 G5, H4 11 12 13 14 … … … … 45 45 45 45 450 450 450 450 170 170 170 170 NP NP 816 816 NP 427 NP 427 899 899 982 982 NP NP NP NP NFN-9 NFN-9 NFN-9 NFN-9 G4, T16 G4, G5, T15 G4, G30, T16 G4, G5, G30, T15 15 16 17 18 … … … … 45 45 45 45 450 450 450 450 170 170 170 170 816 816 816 816 NP 427 NP 427 899 899 899 899 NP NP NP NP NFN-9 NFN-9 NFN-9 NFN-9 G4, T16 G4, G5, T15 G4, T16 G4, G5, T15 19 20 21 22 23 24 … … … … … … 45 45 45 45 45 45 450 450 450 450 450 450 170 170 170 170 170 170 NP NP 816 816 816 816 NP NP NP NP NP 427 899 899 899 899 899 899 NP NP NP NP NP NP NFN-9 NFN-9 NFN-9 NFN-9 NFN-9 NFN-9 G4, G14, T16 G4, G5, G14, T15 G4, G14, T16 G4, G5, G14, T15 G4, T16 G4, G5, T15 25 26 27 28 … … … … 45 45 45 45 450 450 450 450 170 170 170 170 816 816 816 816 NP NP NP NP 899 899 899 899 NP NP NP NP NFN-9 NFN-9 NFN-9 NFN-9 G4, T17 G4, G5, T15 G4, T17 G4, G5, T15 29 30 31 32 … … … … 45 45 45 45 450 450 450 450 170 170 170 170 816 816 816 816 NP NP NP NP 899 899 899 899 NP NP NP NP NFN-9 NFN-9 NFN-9 NFN-9 G4, T17 G4, G5, T15 G4, T17 G4, G5, T15 33 34 35 36 … … … … 45 45 45 45 450 450 450 450 170 170 170 170 816 816 816 816 NP NP NP NP 899 899 899 899 NP NP NP NP NFN-9 NFN-9 NFN-9 NFN-9 G4, G14, T17 G4, G5, G14, T16 G4, T17 G4, G5, T15 37 38 39 … … … 45 45 45 585 585 585 240 240 240 NP NP NP 427 (Cl. 3 only) 427 (Cl. 3 only) NP 538 538 538 343 343 343 NFN-7 NFN-7 NFN-7 … G5 G5, W12 40 41 42 43 44 45 … … … … … … 45 45 45 45 45 45 585 585 585 585 585 585 240 240 240 240 240 240 538 538 538 538 538 538 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 538 538 538 538 538 538 343 343 343 343 343 343 NFN-7 NFN-7 NFN-7 NFN-7 NFN-7 NFN-7 … G5 … G5 … G5 235 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 5 6 117 117 117 117 138 138 112 117 117 112 138 132 108 117 117 108 138 127 106 117 117 106 138 124 104 117 117 104 138 123 102 117 117 102 138 121 101 117 117 101 138 119 99.5 117 117 99.5 138 117 98.3 117 117 98.3 138 116 97.4 117 117 97.4 138 115 96.5 117 117 96.5 138 113 95.4 117 117 95.4 138 112 94.1 117 117 94.1 138 111 92.9 117 117 92.9 138 109 91.7 117 117 91.7 138 108 91.1 117 117 91.1 138 107 89.9 117 117 89.9 138 106 88.5 117 117 88.5 138 104 7 8 9 10 115 115 115 115 111 115 111 115 105 115 105 115 102 115 102 115 99.2 115 99.2 115 96.6 115 96.6 115 94.2 115 94.2 115 92.0 115 92.0 115 89.8 115 89.8 115 87.6 115 87.6 115 85.4 115 85.4 115 83.4 113 83.4 113 81.5 110 81.5 110 79.8 108 79.8 108 78.5 105 78.5 105 76.6 104 76.6 104 75.3 102 75.3 102 74.2 100 74.2 100 11 12 13 14 115 115 115 115 111 115 111 115 105 115 105 115 102 115 102 115 99.2 115 99.2 115 96.6 115 96.6 115 94.2 115 94.2 115 92.0 115 92.0 115 89.8 115 89.8 115 87.6 115 87.6 115 85.4 115 85.4 115 83.4 113 83.4 113 81.5 110 81.5 110 79.8 108 79.8 108 78.5 105 78.5 105 76.6 104 76.6 104 75.3 102 75.3 102 74.2 100 74.2 100 15 16 17 18 115 115 115 115 111 115 111 115 105 115 105 115 102 115 102 115 99.2 115 99.2 115 96.6 115 96.6 115 94.2 115 94.2 115 92.0 115 92.0 115 89.8 115 89.8 115 87.6 115 87.6 115 85.4 115 85.4 115 83.4 113 83.4 113 81.5 110 81.5 110 79.8 108 79.8 108 78.5 105 78.5 105 76.6 104 76.6 104 75.3 102 75.3 102 74.2 100 74.2 100 19 20 21 22 23 24 97.9 97.9 97.9 97.9 115 115 94.0 97.9 94.0 97.9 111 115 89.6 97.9 89.6 97.9 105 115 87.0 97.9 87.0 97.9 102 115 84.7 97.9 84.7 97.9 99.2 115 82.6 97.9 82.6 97.9 96.6 115 80.4 97.9 80.4 97.9 94.2 115 78.1 97.9 78.1 97.9 92.0 115 75.9 97.9 75.9 97.9 89.8 115 74.2 97.8 74.2 97.8 87.6 115 72.7 97.2 72.7 97.2 85.4 115 71.0 95.9 71.0 95.9 83.4 113 69.2 93.8 69.2 93.8 81.5 110 68.1 91.3 68.1 91.3 79.8 108 66.8 89.6 66.8 89.6 78.5 105 65.6 88.4 65.6 88.4 76.6 104 64.4 86.5 64.4 86.5 75.3 102 63.0 85.1 63.0 85.1 74.2 100 25 26 27 28 115 115 115 115 111 115 111 115 105 115 105 115 102 115 102 115 99.2 115 99.2 115 96.6 115 96.6 115 94.2 115 94.2 115 92.0 115 92.0 115 89.8 115 89.8 115 87.6 115 87.6 115 85.4 115 85.4 115 83.4 113 83.4 113 81.5 110 81.5 110 79.8 108 79.8 108 78.5 105 78.5 105 76.6 104 76.6 104 75.3 102 75.3 102 74.2 100 74.2 100 29 30 31 32 115 115 115 115 111 115 111 115 105 115 105 115 102 115 102 115 99.2 115 99.2 115 96.6 115 96.6 115 94.2 115 94.2 115 92.0 115 92.0 115 89.8 115 89.8 115 87.6 115 87.6 115 85.4 115 85.4 115 83.4 113 83.4 113 81.5 110 81.5 110 79.8 108 79.8 108 78.5 105 78.5 105 76.6 104 76.6 104 75.3 102 75.3 102 74.2 100 74.2 100 33 34 35 36 97.9 97.9 115 115 94.0 97.9 111 115 89.6 97.9 105 115 87.0 97.9 102 115 84.7 97.9 99.2 115 82.6 97.9 96.6 115 80.4 97.9 94.2 115 78.1 97.9 92.0 115 75.9 97.9 89.8 115 74.2 97.8 87.6 115 72.7 97.2 85.4 115 71.0 95.9 83.4 113 69.2 93.8 81.5 110 68.1 91.3 79.8 108 66.8 89.6 78.5 105 65.6 88.4 76.6 104 64.4 86.5 75.3 102 63.0 85.1 74.2 100 37 38 39 161 161 161 154 161 161 146 161 161 143 161 161 140 161 161 137 161 161 134 161 161 131 161 161 129 161 161 126 161 161 124 161 161 122 161 161 120 161 161 119 161 161 119 160 160 117 159 159 117 158 158 117 157 157 40 41 42 43 44 45 161 161 161 161 161 161 154 161 154 161 154 161 146 161 146 161 146 161 143 161 143 161 143 161 140 161 140 161 140 161 137 161 137 161 137 161 134 161 134 161 134 161 131 161 131 161 131 161 129 161 129 161 129 161 126 161 126 161 126 161 124 161 124 161 124 161 122 161 122 161 122 161 120 161 120 161 120 161 119 161 119 161 119 161 119 160 119 160 119 160 117 159 117 159 117 159 117 158 117 158 117 158 117 157 117 157 117 157 236 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 6 87.9 117 117 87.9 138 103 86.8 117 117 86.8 137 102 85.8 112 112 85.8 131 101 83.2 91.8 91.8 83.2 108 98.1 72.6 72.6 72.6 72.6 85.0 85.0 54.5 54.5 54.5 54.5 64.4 64.4 38.0 38.0 38.0 38.0 44.8 44.8 25.7 25.7 25.7 25.7 30.0 30.0 12.8 12.8 12.8 12.8 15.5 15.5 10.2 10.2 10.2 10.2 11.3 11.3 7.63 7.63 7.63 7.63 8.82 8.82 6.16 6.16 6.16 6.16 6.98 6.98 5.46 5.46 5.46 5.46 6.43 6.43 4.27 4.27 4.27 4.27 5.00 5.00 … … … … … … … … … … … … … … … … … … 7 8 9 10 72.8 98.6 72.8 98.6 72.0 97.1 72.0 97.1 71.2 95.9 71.2 95.9 69.9 91.8 69.9 91.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 72.8 98.6 72.8 98.6 72.0 97.1 72.0 97.1 71.2 95.9 71.2 95.9 69.9 91.8 69.9 91.8 68.4 75.7 68.4 75.7 62.6 62.6 62.6 62.6 50.6 50.6 50.6 50.6 41.2 41.2 41.2 41.2 33.6 33.6 33.6 33.6 27.7 27.7 27.7 27.7 22.6 22.6 22.6 22.6 18.3 18.3 18.3 18.3 15.0 15.0 15.0 15.0 11.9 11.9 11.9 11.9 9.03 9.03 9.03 9.03 7.35 7.35 7.35 7.35 5.86 5.86 5.86 5.86 15 16 17 18 72.8 98.6 72.8 98.6 72.0 97.1 72.0 97.1 71.2 95.9 71.2 95.9 69.9 91.8 69.9 91.8 68.4 75.7 68.4 75.7 62.6 62.6 62.6 62.6 50.6 50.6 50.6 50.6 41.2 41.2 41.2 41.2 33.6 33.6 33.6 33.6 27.7 27.7 27.7 27.7 22.6 22.6 22.6 22.6 18.3 18.3 18.3 18.3 15.0 15.0 15.0 15.0 11.9 11.9 11.9 11.9 9.03 9.03 9.03 9.03 7.35 7.35 7.35 7.35 5.86 5.86 5.86 5.86 19 20 21 22 23 24 62.3 83.9 62.3 83.9 72.8 98.6 61.3 82.7 61.3 82.7 72.0 97.1 60.3 81.4 60.3 81.4 71.2 95.9 59.6 77.9 59.6 77.9 69.9 91.8 58.1 64.6 58.1 64.6 68.4 75.7 53.2 53.2 53.2 53.2 62.6 62.6 43.0 43.0 43.0 43.0 50.6 50.6 34.9 34.9 34.9 34.9 41.2 41.2 28.6 28.6 28.6 28.6 33.6 33.6 23.3 23.3 23.3 23.3 27.7 27.7 19.4 19.4 19.4 19.4 22.6 22.6 15.6 15.6 15.6 15.6 18.3 18.3 12.5 12.5 12.5 12.5 15.0 15.0 10.1 10.1 10.1 10.1 11.9 11.9 7.75 7.75 7.75 7.75 9.03 9.03 6.28 6.28 6.28 6.28 7.35 7.35 4.98 4.98 4.98 4.98 5.86 5.86 25 26 27 28 72.8 98.7 72.8 98.7 72.0 97.1 72.0 97.1 71.2 96.1 71.2 96.1 69.8 94.1 69.8 94.1 68.6 85.5 68.6 85.5 66.4 69.3 66.4 69.3 56.8 56.8 56.8 56.8 46.8 46.8 46.8 46.8 38.6 38.6 38.6 38.6 31.5 31.5 31.5 31.5 25.5 25.5 25.5 25.5 20.6 20.6 20.6 20.6 17.1 17.1 17.1 17.1 13.8 13.8 13.8 13.8 10.2 10.2 10.2 10.2 7.98 7.98 7.98 7.98 6.20 6.20 6.20 6.20 29 30 31 32 72.8 98.7 72.8 98.7 72.0 97.1 72.0 97.1 71.2 96.1 71.2 96.1 69.8 94.1 69.8 94.1 68.6 85.5 68.6 85.5 66.4 69.3 66.4 69.3 56.8 56.8 56.8 56.8 46.8 46.8 46.8 46.8 38.6 38.6 38.6 38.6 31.5 31.5 31.5 31.5 25.5 25.5 25.5 25.5 20.6 20.6 20.6 20.6 17.1 17.1 17.1 17.1 13.8 13.8 13.8 13.8 10.2 10.2 10.2 10.2 7.98 7.98 7.98 7.98 6.20 6.20 6.20 6.20 33 34 35 36 62.3 83.9 72.8 98.7 61.3 82.7 72.0 97.1 60.3 81.4 71.2 96.1 59.6 80.2 69.8 94.1 58.3 76.6 68.6 85.5 56.7 58.2 66.4 69.3 48.6 48.6 56.8 56.8 39.8 39.8 46.8 46.8 32.8 32.8 38.6 38.6 27.1 27.1 31.5 31.5 21.9 21.9 25.5 25.5 17.5 17.5 20.6 20.6 14.7 14.7 17.1 17.1 11.7 11.7 13.8 13.8 8.26 8.26 10.2 10.2 6.68 6.68 7.98 7.98 5.24 5.24 6.20 6.20 37 38 39 116 156 156 115 155 155 113 153 153 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 40 41 42 43 44 45 116 156 116 156 116 156 115 155 115 155 115 155 113 153 113 153 113 153 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 237 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 42Ni – 21.5Cr – 3Mo – 2.3Cu 42Ni – 21.5Cr – 3Mo – 2.3Cu 42Ni – 21.5Cr – 3Mo – 2.3Cu 42Ni – 21.5Cr – 3Mo – 2.3Cu 42Ni – 21.5Cr – 3Mo – 2.3Cu 42Ni – 21.5Cr – 3Mo – 2.3Cu Forgings Forgings Wld. tube Wld. tube Wld. pipe Wld. pipe SB-564 SB-564 SB-704 SB-704 SB-705 SB-705 … … … … … … N08825 N08825 N08825 N08825 N08825 N08825 Annealed Annealed Annealed Annealed Annealed Annealed 7 8 9 10 11 12 44Fe – 25Ni – 21Cr – Mo 44Fe – 25Ni – 21Cr – Mo 44Fe – 25Ni – 21Cr – Mo 44Fe – 25Ni – 21Cr – Mo 44Fe – 25Ni – 21Cr – Mo 44Fe – 25Ni – 21Cr – Mo Fittings Plate, sheet, strip Bar, wire Wld. pipe Wld. tube Smls. pipe & tube SB-366 SB-625 SB-649 SB-673 SB-674 SB-677 … … … … … … N08904 N08904 N08904 N08904 N08904 N08904 Annealed Annealed Annealed Annealed Annealed Annealed 13 14 15 16 25Ni – 20Cr – 6Mo – Cu – N 25Ni – 20Cr – 6Mo – Cu – N 25Ni – 20Cr – 6Mo – Cu – N 25Ni – 20Cr – 6Mo – Cu – N Plate, sheet, strip Plate, sheet, strip Bar, wire Bar, wire SB-625 SB-625 SB-649 SB-649 … … … … N08925 N08925 N08925 N08925 Annealed Annealed Annealed Annealed 17 18 19 20 21 22 25Ni – 20Cr – 6Mo – Cu – N 25Ni – 20Cr – 6Mo – Cu – N 25Ni – 20Cr – 6Mo – Cu – N 25Ni – 20Cr – 6Mo – Cu – N 25Ni – 20Cr – 6Mo – Cu – N 25Ni – 20Cr – 6Mo – Cu – N Wld. pipe Wld. pipe Wld. tube Wld. tube Smls. pipe & tube Smls. pipe & tube SB-673 SB-673 SB-674 SB-674 SB-677 SB-677 … … … … … … N08925 N08925 N08925 N08925 N08925 N08925 Annealed Annealed Annealed Annealed Annealed Annealed 23 24 25 62Ni – 28Mo – 5Fe 62Ni – 28Mo – 5Fe 62Ni – 28Mo – 5Fe Plate Plate Smls. & wld. fittings SB-333 SB-333 SB-366 … … … N10001 N10001 N10001 Annealed Annealed Annealed 26 27 28 29 30 31 62Ni – 28Mo – 5Fe 62Ni – 28Mo – 5Fe 62Ni – 28Mo – 5Fe 62Ni – 28Mo – 5Fe 62Ni – 28Mo – 5Fe 62Ni – 28Mo – 5Fe Wld. pipe Wld. pipe Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-619 SB-619 SB-622 SB-622 SB-626 SB-626 … … … … … … N10001 N10001 N10001 N10001 N10001 N10001 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 32 33 34 35 36 37 62Ni – 28Mo – 5Fe 62Ni – 28Mo – 5Fe 62Ni – 28Mo – 5Fe 62Ni – 28Mo – 5Fe 62Ni – 28Mo – 5Fe 62Ni – 28Mo – 5Fe Rod Rod Rod Rod Sheet, strip Sheet, strip SB-335 SB-335 SB-335 SB-335 SB-333 SB-333 … … … … … … N10001 N10001 N10001 N10001 N10001 N10001 Annealed Annealed Annealed Annealed Annealed Annealed 38 39 40 70Ni – 16Mo – 7Cr – 5Fe 70Ni – 16Mo – 7Cr – 5Fe 70Ni – 16Mo – 7Cr – 5Fe Smls. & wld. fittings Plate, sheet, strip Rod SB-366 SB-434 SB-573 … … … N10003 N10003 N10003 Annealed Annealed Annealed 41 42 43 62Ni – 25Mo – 8Cr – 2Fe 62Ni – 25Mo – 8Cr – 2Fe 62Ni – 25Mo – 8Cr – 2Fe Smls. & wld. fittings Plate, sheet, strip Plate, sheet, strip SB-366 SB-434 SB-434 … … … N10242 N10242 N10242 Annealed Annealed Annealed Line No. 1 2 3 4 5 6 238 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 6 … … … … … … 45 45 45 45 45 45 585 585 585 585 585 585 240 240 240 240 240 240 NP NP NP NP NP NP NP NP 427 NP NP NP 538 538 538 538 538 538 NP NP 343 343 343 343 NFN-7 NFN-7 NFN-7 NFN-7 NFN-7 NFN-7 … G5 G14 G5, G14 G14 G5, G14 7 8 9 10 11 12 … … … … … … 45 45 45 45 45 45 490 490 490 490 490 490 215 215 215 215 215 215 NP NP NP NP NP NP 371 371 371 371 371 371 371 371 371 371 371 371 343 343 343 343 343 343 NFN-9 NFN-9 NFN-9 NFN-9 NFN-9 NFN-9 W12 … … G14 G14 … 13 14 15 16 … … … … 45 45 45 45 600 600 600 600 295 295 295 295 NP NP NP NP NP NP NP NP 427 427 427 427 343 343 343 343 NFN-12 NFN-12 NFN-12 NFN-12 … G5 … G5 17 18 19 20 21 22 … … … … … … 45 45 45 45 45 45 600 600 600 600 600 600 295 295 295 295 295 295 NP NP NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 427 343 343 343 343 343 343 NFN-12 NFN-12 NFN-12 NFN-12 NFN-12 NFN-12 G14 G5, G14 G14 G5, G14 … G5 23 24 25 … … … 44 44 44 690 690 690 310 310 310 NP NP NP 427 (Cl. 3 only) 427 (Cl. 3 only) NP 427 427 427 343 343 343 NFN-5 NFN-5 NFN-5 … G5 G5, W12 26 27 28 29 30 31 … … … … … … 44 44 44 44 44 44 690 690 690 690 690 690 310 310 310 310 310 310 NP NP NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 427 343 343 343 343 343 343 NFN-5 NFN-5 NFN-5 NFN-5 NFN-5 NFN-5 G14 G5, G14 … G5 G14 G5, G14 32 33 34 35 36 37 … … … … … … 44 44 44 44 44 44 690 690 795 795 795 795 315 315 315 315 345 345 NP NP NP NP NP NP 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 427 427 427 427 427 427 343 343 343 343 343 NP NFN-5 NFN-5 NFN-5 NFN-5 NFN-5 NFN-5 G13 G5, G13 G13 G5, G13 … G5 38 39 40 … … … 44 44 44 690 690 690 275 275 275 NP NP NP NP NP NP 704 704 704 343 343 343 NFN-6 NFN-6 NFN-6 T15, W12 T15 T15 41 42 43 … … … 44 44 44 725 725 725 310 310 310 NP NP NP NP NP NP 538 538 538 NP NP NP NFN-6 NFN-6 NFN-6 G5, W12 G5 … 239 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 5 6 160 160 137 137 137 137 151 160 131 137 131 137 146 160 125 137 125 137 … … 122 137 122 137 139 160 119 137 119 137 … … 117 137 117 137 133 160 114 137 114 137 … … 112 137 112 137 128 160 110 137 110 137 … … 108 137 108 137 123 160 106 137 106 137 … … 104 137 104 137 120 160 102 137 102 137 119 160 101 136 101 136 118 159 101 136 101 136 117 158 100 135 100 135 116 157 99.4 135 99.4 135 116 156 98.8 134 98.8 134 7 8 9 10 11 12 140 140 140 119 119 140 126 126 126 107 107 126 113 113 113 96.3 96.3 113 108 108 108 91.9 91.9 108 104 104 104 88.8 88.8 104 99.9 99.9 99.9 85.5 85.5 99.9 95.8 95.8 95.8 82.0 82.0 95.8 92.1 92.1 92.1 78.6 78.6 92.1 88.8 88.8 88.8 75.6 75.6 88.8 85.9 85.9 85.9 72.9 72.9 85.9 83.4 83.4 83.4 70.7 70.7 83.4 81.3 81.3 81.3 69.1 69.1 81.3 79.6 79.6 79.6 67.9 67.9 79.6 78.4 78.4 78.4 66.7 66.7 78.4 … … … … … … … … … … … … … … … … … … … … … … … … 13 14 15 16 172 172 172 172 166 172 166 172 158 171 158 171 152 168 152 168 147 165 147 165 142 162 142 162 137 159 137 159 133 156 133 156 128 153 128 153 124 151 124 151 121 149 121 149 118 147 118 147 117 145 117 145 117 143 117 143 117 141 117 141 117 139 117 139 117 137 117 137 … … … … 17 18 19 20 21 22 145 145 145 145 172 172 141 145 141 145 166 172 135 145 135 145 158 171 129 143 129 143 152 168 125 141 125 141 147 165 120 138 120 138 142 162 117 135 117 135 137 159 113 132 113 132 133 156 109 130 109 130 128 153 106 129 106 129 124 151 103 127 103 127 121 149 101 125 101 125 118 147 99.3 123 99.3 123 117 145 99.3 122 99.3 122 117 143 99.3 120 99.3 120 117 141 99.3 117 99.3 117 117 139 99.3 115 99.3 115 117 137 … … … … … … 23 24 25 197 197 197 193 197 197 186 197 197 181 197 197 177 197 197 173 196 196 170 194 194 167 193 193 164 192 192 162 192 192 160 191 191 158 191 191 157 189 190 155 189 189 154 188 188 152 188 188 151 187 187 … … … 26 27 28 29 30 31 168 168 197 197 168 168 164 168 193 197 164 168 158 168 186 197 158 168 154 168 181 197 154 168 150 168 177 197 150 168 147 166 173 196 147 166 145 165 170 194 145 165 142 164 167 193 142 164 140 164 164 192 140 164 138 163 162 192 138 163 136 162 160 191 136 162 134 162 158 191 134 162 133 161 157 189 133 161 131 161 155 189 131 161 130 160 154 188 130 160 130 159 152 188 130 159 129 159 151 187 129 159 … … … … … … 32 33 34 35 36 37 197 197 212 212 227 227 195 197 201 212 217 227 191 197 190 212 207 227 186 197 185 212 201 227 181 197 181 212 197 227 177 196 177 212 193 225 174 194 174 212 189 223 171 193 171 212 186 222 168 192 168 212 183 221 166 192 166 212 180 220 164 191 164 212 178 220 162 191 162 212 176 219 160 189 160 212 174 218 158 189 158 212 172 217 157 188 157 212 171 216 156 188 156 210 170 216 155 187 155 209 168 215 … … … … … … 38 39 40 184 184 184 177 177 177 168 168 168 162 162 162 156 156 156 151 151 151 146 146 146 142 142 142 139 139 139 136 136 136 134 134 134 133 133 133 131 131 131 130 130 130 129 129 129 127 127 127 125 125 125 122 122 122 41 42 43 207 207 207 207 207 201 207 207 193 207 207 186 207 207 180 207 207 175 207 207 171 207 207 168 207 207 166 207 207 164 206 206 164 206 206 163 205 205 162 205 205 161 204 204 160 204 204 158 203 203 155 203 203 152 240 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 6 115 156 98.2 133 98.2 133 114 154 97.2 131 97.2 131 112 151 95.9 129 95.9 129 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 10 11 12 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 13 14 15 16 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 17 18 19 20 21 22 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 23 24 25 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 26 27 28 29 30 31 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 37 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 38 39 40 118 118 118 113 113 113 107 108 108 96.7 97.8 97.8 80.4 80.7 80.7 59.2 60.7 60.7 40.7 40.8 40.8 30.9 33.5 33.5 25.2 25.7 25.7 17.9 17.4 17.4 … … … … … … … … … … … … … … … … … … … … … 41 42 43 202 202 150 201 201 149 201 201 149 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 241 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 62Ni – 25Mo – 8Cr – 2Fe 62Ni – 25Mo – 8Cr – 2Fe 62Ni – 25Mo – 8Cr – 2Fe 62Ni – 25Mo – 8Cr – 2Fe Forgings Forgings Rod Rod SB-564 SB-564 SB-573 SB-573 … … … … N10242 N10242 N10242 N10242 Annealed Annealed Annealed Annealed 5 6 7 8 9 10 62Ni – 25Mo – 8Cr – 2Fe 62Ni – 25Mo – 8Cr – 2Fe 62Ni – 25Mo – 8Cr – 2Fe 62Ni – 25Mo – 8Cr – 2Fe 62Ni – 25Mo – 8Cr – 2Fe 62Ni – 25Mo – 8Cr – 2Fe Wld. pipe Wld. pipe Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-619 SB-619 SB-622 SB-622 SB-626 SB-626 … … … … … … N10242 N10242 N10242 N10242 N10242 N10242 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 11 12 13 14 15 54Ni – 16Mo – 15Cr 54Ni – 16Mo – 15Cr 54Ni – 16Mo – 15Cr 54Ni – 16Mo – 15Cr 54Ni – 16Mo – 15Cr Smls. & wld. fittings Forgings Forgings Forgings Forgings SB-366 SB-462 SB-462 SB-564 SB-564 … … … … … N10276 N10276 N10276 N10276 N10276 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 16 17 18 19 54Ni – 16Mo – 15Cr 54Ni – 16Mo – 15Cr 54Ni – 16Mo – 15Cr 54Ni – 16Mo – 15Cr Rod Rod Plate, sheet, strip Plate, sheet, strip SB-574 SB-574 SB-575 SB-575 … … … … N10276 N10276 N10276 N10276 Solution ann. Solution ann. Solution ann. Solution ann. 20 21 22 23 54Ni – 16Mo – 15Cr 54Ni – 16Mo – 15Cr 54Ni – 16Mo – 15Cr 54Ni – 16Mo – 15Cr Wld. pipe Wld. pipe Wld. pipe Wld. pipe SB-619 SB-619 SB-619 SB-619 … … … … N10276 N10276 N10276 N10276 Solution ann. Solution ann. Solution ann. Solution ann. 24 25 26 27 28 29 54Ni – 16Mo – 15Cr 54Ni – 16Mo – 15Cr 54Ni – 16Mo – 15Cr 54Ni – 16Mo – 15Cr 54Ni – 16Mo – 15Cr 54Ni – 16Mo – 15Cr Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube Wld. tube Wld. tube SB-622 SB-622 SB-626 SB-626 SB-626 SB-626 … … … … … … N10276 N10276 N10276 N10276 N10276 N10276 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 30 31 32 33 Ni – 28Mo – 3Fe – 1.3Cr – 0.25Al Ni – 28Mo – 3Fe – 1.3Cr – 0.25Al Ni – 28Mo – 3Fe – 1.3Cr – 0.25Al Ni – 28Mo – 3Fe – 1.3Cr – 0.25Al Plate, sheet, strip Plate, sheet, strip Rod Rod SB-333 SB-333 SB-335 SB-335 … … … … N10629 N10629 N10629 N10629 Solution ann. Solution ann. Solution ann. Solution ann. 34 35 36 Ni – 28Mo – 3Fe – 1.3Cr – 0.25Al Ni – 28Mo – 3Fe – 1.3Cr – 0.25Al Ni – 28Mo – 3Fe – 1.3Cr – 0.25Al Smls. & wld. fittings Forged fittings Forged fittings SB-366 SB-462 SB-462 … … … N10629 N10629 N10629 Solution ann. Solution ann. Solution ann. 37 38 39 40 Ni – 28Mo – 3Fe – 1.3Cr – 0.25Al Ni – 28Mo – 3Fe – 1.3Cr – 0.25Al Ni – 28Mo – 3Fe – 1.3Cr – 0.25Al Ni – 28Mo – 3Fe – 1.3Cr – 0.25Al Forgings Forgings Wld. pipe Wld. pipe SB-564 SB-564 SB-619 SB-619 … … … … N10629 N10629 N10629 N10629 Solution ann. Solution ann. Solution ann. Solution ann. 41 42 43 44 Ni – 28Mo – 3Fe – 1.3Cr – 0.25Al Ni – 28Mo – 3Fe – 1.3Cr – 0.25Al Ni – 28Mo – 3Fe – 1.3Cr – 0.25Al Ni – 28Mo – 3Fe – 1.3Cr – 0.25Al Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-622 SB-622 SB-626 SB-626 … … … … N10629 N10629 N10629 N10629 Solution ann. Solution ann. Solution ann. Solution ann. Line No. 242 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 … … … … 44 44 44 44 725 725 725 725 310 310 310 310 NP NP NP NP NP NP NP NP 538 538 538 538 NP NP NP NP NFN-6 NFN-6 NFN-6 NFN-6 G5 … G5 … 5 6 7 8 9 10 … … … … … … 44 44 44 44 44 44 725 725 725 725 725 725 310 310 310 310 310 310 NP NP NP NP NP NP NP NP NP NP NP NP 538 538 538 538 538 538 NP NP NP NP NP NP NFN-6 NFN-6 NFN-6 NFN-6 NFN-6 NFN-6 G5, G14 G14 G5 … G5, G14 G14 11 12 13 14 15 … … … … … 43 43 43 43 43 690 690 690 690 690 285 285 285 285 285 538 NP NP NP NP NP NP NP NP NP 677 677 677 677 677 343 NP NP 343 343 NFN-10 NFN-10 NFN-10 NFN-10 NFN-10 G5, T14, W12 T15 G5, T14 T15 G5, T14 16 17 18 19 … … … … 43 43 43 43 690 690 690 690 285 285 285 285 538 538 538 538 427 (Cl. 3 only) 427 427 427 (Cl. 3 only) 677 677 677 677 343 343 343 343 NFN-10 NFN-10 NFN-10 NFN-10 T15 G5, T14 G5, T14 T15 20 21 22 23 … … … … 43 43 43 43 690 690 690 690 285 285 285 285 NP NP 538 538 427 (Cl. 3 only) 427 (Cl. 3 only) 427 NP NP NP 677 677 NP NP 343 343 NFN-10 NFN-10 NFN-10 NFN-10 W5 G5, W5 G5, G14, T14, W6 G14, T15 24 25 26 27 28 29 … … … … … … 43 43 43 43 43 43 690 690 690 690 690 690 285 285 285 285 285 285 538 538 NP NP 538 538 427 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 427 NP 677 677 NP NP 677 677 343 343 NP NP 343 343 NFN-10 NFN-10 NFN-10 NFN-10 NFN-10 NFN-10 G5, T14 T15 W5 G5, W5 G5, G14, T14, W6 G14, T15 30 31 32 33 … … … … 44 44 44 44 760 760 760 760 350 350 350 350 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-16 NFN-16 NFN-16 NFN-16 G5 … G5 … 34 35 36 … … … 44 44 44 760 760 760 350 350 350 NP NP NP NP NP NP 427 427 427 NP NP NP NFN-16 NFN-16 NFN-16 G5, W12 G5 … 37 38 39 40 … … … … 44 44 44 44 760 760 760 760 350 350 350 350 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-16 NFN-16 NFN-16 NFN-16 G5 … G5, G14 G14 41 42 43 44 … … … … 44 44 44 44 760 760 760 760 350 350 350 350 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-16 NFN-16 NFN-16 NFN-16 G5 … G5, G14 G14 243 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 207 207 207 207 207 201 207 201 207 193 207 193 207 186 207 186 207 180 207 180 207 175 207 175 207 171 207 171 207 168 207 168 207 166 207 166 207 164 207 164 206 164 206 164 206 163 206 163 205 162 205 162 205 161 205 161 204 160 204 160 204 158 204 158 203 155 203 155 203 152 203 152 5 6 7 8 9 10 176 176 207 207 176 176 176 171 207 201 176 171 176 164 207 193 176 164 176 158 207 186 176 158 176 153 207 180 176 153 176 149 207 175 176 149 176 145 207 171 176 145 176 143 207 168 176 143 176 141 207 166 176 141 176 139 207 164 176 139 175 139 206 164 175 139 175 139 206 163 175 139 174 138 205 162 174 138 174 137 205 161 174 137 173 136 204 160 173 136 173 134 204 158 173 134 173 132 203 155 173 132 173 129 203 152 173 129 11 12 13 14 15 188 188 188 188 188 188 180 188 180 188 188 170 188 170 188 188 164 188 164 188 188 158 188 158 188 188 153 188 153 188 188 148 188 148 188 188 143 188 143 188 187 139 187 139 187 183 135 183 135 183 177 131 177 131 177 172 128 172 128 172 169 125 169 125 169 165 122 165 122 165 162 120 162 120 162 159 118 159 118 159 157 117 157 117 157 156 115 156 115 156 16 17 18 19 188 188 188 188 180 188 188 180 170 188 188 170 164 188 188 164 158 188 188 158 153 188 188 153 148 188 188 148 143 188 188 143 139 187 187 139 135 183 183 135 131 177 177 131 128 172 172 128 125 169 169 125 122 165 165 122 120 162 162 120 118 159 159 118 117 157 157 117 115 156 156 115 20 21 22 23 188 188 160 160 180 188 160 152 170 188 160 144 164 188 160 139 158 188 160 135 153 188 160 130 148 188 160 126 143 188 160 121 139 187 158 118 135 183 155 115 131 177 151 111 128 172 147 109 125 169 143 106 122 165 140 104 120 162 138 102 118 159 135 100 117 157 134 98.8 … … 133 98.1 24 25 26 27 28 29 188 188 188 188 160 160 188 180 180 188 160 152 188 170 170 188 160 144 188 164 164 188 160 139 188 158 158 188 160 135 188 153 153 188 160 130 188 148 148 188 160 126 188 143 143 188 160 121 187 139 139 187 158 118 183 135 135 183 155 115 177 131 131 177 151 111 172 128 128 172 147 109 169 125 125 169 143 106 165 122 122 165 140 104 162 120 120 162 138 102 159 118 118 159 135 100 157 117 117 157 134 98.8 156 115 … … 133 98.1 30 31 32 33 216 216 216 216 216 216 216 216 216 216 216 216 216 211 216 211 216 204 216 204 216 198 216 198 216 194 216 194 216 191 216 191 215 187 215 187 213 184 213 184 212 181 212 181 210 179 210 179 209 177 209 177 208 176 208 176 207 174 207 174 206 173 206 173 205 172 205 172 … … … … 34 35 36 216 216 216 216 216 216 216 216 216 216 216 211 216 216 204 216 216 198 216 216 194 216 216 191 215 215 187 213 213 184 212 212 181 210 210 179 209 209 177 208 208 176 207 207 174 206 206 173 205 205 172 … … … 37 38 39 40 216 216 184 184 216 216 184 184 216 216 184 184 216 211 184 179 216 204 184 174 216 198 184 169 216 194 184 165 216 191 184 162 215 187 183 160 213 184 181 157 212 181 180 154 210 179 179 152 209 177 178 151 208 176 177 149 207 174 176 148 206 173 175 147 205 172 174 146 … … … … 41 42 43 44 216 216 184 184 216 216 184 184 216 216 184 184 216 211 184 179 216 204 184 174 216 198 184 169 216 194 184 165 216 191 184 162 215 187 183 160 213 184 181 157 212 181 180 154 210 179 179 152 209 177 178 151 208 176 177 149 207 174 176 148 206 173 175 147 205 172 174 146 … … … … 244 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 202 150 202 150 201 149 201 149 201 149 201 149 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 9 10 172 128 202 150 172 128 171 127 201 149 171 127 171 127 201 149 171 127 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 15 155 115 155 115 155 154 114 154 114 154 145 114 145 114 145 118 112 118 112 118 99.1 99.1 99.1 99.1 99.1 81.6 81.6 81.6 81.6 81.6 67.0 67.0 67.0 67.0 67.0 54.6 54.6 54.6 54.6 54.6 42.2 42.2 42.2 42.2 42.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 115 155 155 115 114 154 154 114 114 145 145 114 112 118 118 112 99.1 99.1 99.1 99.1 81.6 81.6 81.6 81.6 67.0 67.0 67.0 67.0 54.6 54.6 54.6 54.6 42.2 42.2 42.2 42.2 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 23 … … 131 97.5 … … 131 96.7 … … 124 96.5 … … 100 95.2 … … 84.6 84.6 … … 69.5 69.5 … … 56.7 56.7 … … 46.2 46.2 … … 35.7 35.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 24 25 26 27 28 29 155 115 … … 131 97.5 154 114 … … 131 96.7 145 114 … … 124 96.5 118 112 … … 100 95.2 99.1 99.1 … … 84.6 84.6 81.6 81.6 … … 69.5 69.5 67.0 67.0 … … 56.7 56.7 54.6 54.6 … … 46.2 46.2 42.2 42.2 … … 35.7 35.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 30 31 32 33 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 37 38 39 40 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 41 42 43 44 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 245 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 5 65Ni – 28Mo – 2Fe 65Ni – 28Mo – 2Fe 65Ni – 28Mo – 2Fe 65Ni – 28Mo – 2Fe 65Ni – 28Mo – 2Fe Smls. & wld. fittings Wld. pipe Wld. pipe Wld. tube Wld. tube SB-366 SB-619 SB-619 SB-626 SB-626 … … … … … N10665 N10665 N10665 N10665 N10665 Annealed Annealed Annealed Annealed Annealed 6 7 8 9 65Ni – 28Mo – 2Fe 65Ni – 28Mo – 2Fe 65Ni – 28Mo – 2Fe 65Ni – 28Mo – 2Fe Plate, sheet, strip Plate, sheet, strip Rod Rod SB-333 SB-333 SB-335 SB-335 … … … … N10665 N10665 N10665 N10665 Solution ann. Solution ann. Solution ann. Solution ann. 10 11 12 13 65Ni – 28Mo – 2Fe 65Ni – 28Mo – 2Fe 65Ni – 28Mo – 2Fe 65Ni – 28Mo – 2Fe Forgings Forgings Forgings Forgings SB-462 SB-462 SB-564 SB-564 … … … … N10665 N10665 N10665 N10665 Solution ann. Solution ann. Solution ann. Solution ann. 14 15 16 17 18 19 65Ni – 28Mo – 2Fe 65Ni – 28Mo – 2Fe 65Ni – 28Mo – 2Fe 65Ni – 28Mo – 2Fe 65Ni – 28Mo – 2Fe 65Ni – 28Mo – 2Fe Wld. pipe Wld. pipe Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-619 SB-619 SB-622 SB-622 SB-626 SB-626 … … … … … … N10665 N10665 N10665 N10665 N10665 N10665 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 20 21 22 23 24 65Ni – 29.5Mo – 2Fe – 2Cr 65Ni – 29.5Mo – 2Fe – 2Cr 65Ni – 29.5Mo – 2Fe – 2Cr 65Ni – 29.5Mo – 2Fe – 2Cr 65Ni – 29.5Mo – 2Fe – 2Cr Plate, sheet, strip Plate, sheet, strip Rod Rod Smls. & wld. fittings SB-333 SB-333 SB-335 SB-335 SB-366 … … … … … N10675 N10675 N10675 N10675 N10675 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 25 26 27 28 29 30 65Ni – 29.5Mo – 2Fe – 2Cr 65Ni – 29.5Mo – 2Fe – 2Cr 65Ni – 29.5Mo – 2Fe – 2Cr 65Ni – 29.5Mo – 2Fe – 2Cr 65Ni – 29.5Mo – 2Fe – 2Cr 65Ni – 29.5Mo – 2Fe – 2Cr Forgings Forgings Forgings Forgings Wld. pipe Wld. pipe SB-462 SB-462 SB-564 SB-564 SB-619 SB-619 … … … … … … N10675 N10675 N10675 N10675 N10675 N10675 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 31 32 33 34 65Ni – 29.5Mo – 2Fe – 2Cr 65Ni – 29.5Mo – 2Fe – 2Cr 65Ni – 29.5Mo – 2Fe – 2Cr 65Ni – 29.5Mo – 2Fe – 2Cr Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-622 SB-622 SB-626 SB-626 … … … … N10675 N10675 N10675 N10675 Solution ann. Solution ann. Solution ann. Solution ann. 35 36 37 38 39 37Ni – 30Co – 28Cr – 2.7Si 37Ni – 30Co – 28Cr – 2.7Si 37Ni – 30Co – 28Cr – 2.7Si 37Ni – 30Co – 28Cr – 2.7Si 37Ni – 30Co – 28Cr – 2.7Si Smls. & wld. fittings Plate, sheet, strip Plate, sheet, strip Forgings Forgings SB-366 SB-435 SB-435 SB-564 SB-564 … … … … … N12160 N12160 N12160 N12160 N12160 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. 40 41 42 43 37Ni – 30Co – 28Cr – 2.7Si 37Ni – 30Co – 28Cr – 2.7Si 37Ni – 30Co – 28Cr – 2.7Si 37Ni – 30Co – 28Cr – 2.7Si Rod Rod Wld. pipe Wld. pipe SB-572 SB-572 SB-619 SB-619 … … … … N12160 N12160 N12160 N12160 Solution ann. Solution ann. Solution ann. Solution ann. Line No. 246 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 … … … … … 44 44 44 44 44 760 760 760 760 760 350 350 350 350 350 NP NP NP NP NP NP 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 427 NP NP NP NP 343 NP NP NP NP NFN-16 NFN-16 NFN-16 NFN-16 NFN-16 G5, W12 G5, W5 W5 G5, W5 W5 6 7 8 9 … … … … 44 44 44 44 760 760 760 760 350 350 350 350 NP NP NP NP 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 427 (Cl. 3 only) 427 427 427 427 343 NP 343 343 NFN-16 NFN-16 NFN-16 NFN-16 … G5 G13 G5, G13 10 11 12 13 … … … … 44 44 44 44 760 760 760 760 350 350 350 350 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-16 NFN-16 NFN-16 NFN-16 … G5 … G5 14 15 16 17 18 19 … … … … … … 44 44 44 44 44 44 760 760 760 760 760 760 350 350 350 350 350 350 NP NP NP NP NP NP NP NP 427 (Cl. 3 only) 427 (Cl. 3 only) NP NP 427 427 427 427 427 427 343 343 343 343 343 343 NFN-16 NFN-16 NFN-16 NFN-16 NFN-16 NFN-16 G14 G5, G14 … G5 G5, G14 G14 20 21 22 23 24 … … … … … 44 44 44 44 44 760 760 760 760 760 350 350 350 350 350 NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 343 343 343 343 343 NFN-16 NFN-16 NFN-16 NFN-16 NFN-16 G5 … G5 … G5, W12 25 26 27 28 29 30 … … … … … … 44 44 44 44 44 44 760 760 760 760 760 760 350 350 350 350 350 350 NP NP NP NP NP NP NP NP NP NP NP NP 427 427 427 427 427 427 NP NP 343 343 343 343 NFN-16 NFN-16 NFN-16 NFN-16 NFN-16 NFN-16 G5 … G5 … G5, G14 G14 31 32 33 34 … … … … 44 44 44 44 760 760 760 760 350 350 350 350 NP NP NP NP NP NP NP NP 427 427 427 427 343 343 343 343 NFN-16 NFN-16 NFN-16 NFN-16 G5 … G5, G14 G14 35 36 37 38 39 … … … … … 46 46 46 46 46 620 620 620 620 620 240 240 240 240 240 NP NP NP NP NP NP NP NP NP NP 816 816 816 816 816 NP NP NP NP NP NFN-13 NFN-13 NFN-13 NFN-13 NFN-13 G5, T14, W12 T14 G5, T14 T14 G5, T14 40 41 42 43 … … … … 46 46 46 46 620 620 620 620 240 240 240 240 NP NP NP NP NP NP NP NP 816 816 816 816 NP NP NP NP NFN-13 NFN-13 NFN-13 NFN-13 T14 G5, T14 G14, T14 G5, G14, T14 247 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 5 216 216 216 216 216 216 216 216 216 216 216 216 216 216 216 216 216 213 216 213 216 216 208 216 208 216 216 204 216 204 216 216 200 216 200 216 216 196 216 196 216 216 193 216 193 216 216 191 216 191 216 216 189 216 189 215 215 187 215 187 214 214 185 214 185 213 213 183 213 183 212 212 181 212 181 211 211 178 211 178 210 210 176 210 176 … … … … … 6 7 8 9 216 216 216 216 216 216 216 216 216 216 216 216 213 216 213 216 208 216 208 216 204 216 204 216 200 216 200 216 196 216 196 216 193 216 193 216 191 216 191 216 189 216 189 216 187 215 187 215 185 214 185 214 183 213 183 213 181 212 181 212 178 211 178 211 176 210 176 210 … … … … 10 11 12 13 216 216 216 216 216 216 216 216 216 216 216 216 213 216 213 216 208 216 208 216 204 216 204 216 200 216 200 216 196 216 196 216 193 216 193 216 191 216 191 216 189 216 189 216 187 215 187 215 185 214 185 214 183 213 183 213 181 212 181 212 178 211 178 211 176 210 176 210 … … … … 14 15 16 17 18 19 184 184 216 216 184 184 184 184 216 216 184 184 184 184 216 216 184 184 181 184 213 216 184 181 177 184 208 216 184 177 173 184 204 216 184 173 170 184 200 216 184 170 167 184 196 216 184 167 164 184 193 216 184 164 162 184 191 216 184 162 160 183 189 216 183 160 159 182 187 215 182 159 157 182 185 214 182 157 156 181 183 213 181 156 154 180 181 212 180 154 151 179 178 211 179 151 149 179 176 210 179 149 … … … … … … 20 21 22 23 24 216 216 216 216 216 216 216 216 216 216 216 216 216 216 216 216 213 216 213 216 216 209 216 209 216 216 204 216 204 216 216 199 216 199 216 216 195 216 195 216 215 191 215 191 215 213 187 213 187 213 212 183 212 183 212 210 180 210 180 210 209 177 209 177 209 208 175 208 175 208 207 173 207 173 207 206 171 206 171 206 205 169 205 169 205 … … … … … 25 26 27 28 29 30 216 216 216 216 184 184 216 216 216 216 184 184 216 216 216 216 184 184 216 213 216 213 184 181 216 209 216 209 184 178 216 204 216 204 184 174 216 199 216 199 184 170 216 195 216 195 184 166 215 191 215 191 183 163 213 187 213 187 181 160 212 183 212 183 180 156 210 180 210 180 179 153 209 177 209 177 178 150 208 175 208 175 177 149 207 173 207 173 176 147 206 171 206 171 175 146 205 169 205 169 174 144 … … … … … … 31 32 33 34 216 216 184 184 216 216 184 184 216 216 184 184 216 213 184 181 216 209 184 178 216 204 184 174 216 199 184 170 216 195 184 166 215 191 183 163 213 187 181 160 212 183 180 156 210 180 179 153 209 177 178 150 208 175 177 149 207 173 176 147 206 171 175 146 205 169 174 144 … … … … 35 36 37 38 39 161 161 161 161 161 161 151 161 151 161 161 139 161 139 161 161 132 161 132 161 161 126 161 126 161 159 120 159 120 159 154 115 154 115 154 148 110 148 110 148 142 105 142 105 142 137 101 137 101 137 133 98.6 133 98.6 133 130 96.5 130 96.5 130 128 94.7 128 94.7 128 127 93.8 127 93.8 127 126 93.8 126 93.8 126 126 93.1 126 93.1 126 126 93.1 126 93.1 126 126 93.1 126 93.1 126 40 41 42 43 161 161 137 137 151 161 128 137 139 161 118 137 132 161 113 137 126 161 107 136 120 159 102 135 115 154 97.3 131 110 148 93.1 126 105 142 89.5 121 101 137 86.6 117 98.6 133 84.1 113 96.5 130 81.9 111 94.7 128 80.4 108 93.8 127 80.0 108 93.8 126 80.0 108 93.1 126 79.3 108 93.1 126 79.3 108 93.1 126 79.3 108 248 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 17 18 19 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 23 24 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 28 29 30 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 34 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 35 36 37 38 39 126 93.1 126 93.1 126 122 93.1 122 93.1 122 105 93.0 105 93.0 105 89.2 89.2 89.2 89.2 89.2 72.4 72.4 72.4 72.4 72.4 61.2 61.2 61.2 61.2 61.2 51.3 51.3 51.3 51.3 51.3 43.2 43.2 43.2 43.2 43.2 36.2 36.2 36.2 36.2 36.2 31.0 31.0 31.0 31.0 31.0 26.5 26.5 26.5 26.5 26.5 22.5 22.5 22.5 22.5 22.5 19.1 19.1 19.1 19.1 19.1 16.1 16.1 16.1 16.1 16.1 … … … … … … … … … … … … … … … 40 41 42 43 93.1 126 79.3 108 93.1 122 79.3 104 93.0 105 79.3 89.4 89.2 89.2 76.1 76.1 72.4 72.4 61.8 61.8 61.2 61.2 51.8 51.8 51.3 51.3 43.8 43.8 43.2 43.2 37.0 37.0 36.2 36.2 30.6 30.6 31.0 31.0 26.5 26.5 26.5 26.5 22.8 22.8 22.5 22.5 19.4 19.4 19.1 19.1 16.4 16.4 16.1 16.1 13.3 13.3 … … … … … … … … … … … … 249 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 37Ni – 30Co – 28Cr – 2.7Si 37Ni – 30Co – 28Cr – 2.7Si 37Ni – 30Co – 28Cr – 2.7Si 37Ni – 30Co – 28Cr – 2.7Si Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-622 SB-622 SB-626 SB-626 … … … … N12160 N12160 N12160 N12160 Solution ann. Solution ann. Solution ann. Solution ann. 5 6 7 59Ni – 22Cr – 14Mo – 4Fe – 3W 53Ni – 17Mo – 16Cr – 6Fe – 5W 62Ni – 28Mo – 5Fe Castings Castings Castings SA-494 SA-494 SA-494 CX2MW CW-12MW/C N-12MV/B N26022 N30002 N30012 Solution ann. Annealed Annealed 8 9 10 11 33Cr – 31Ni – 32Fe – 1.5Mo – 0.6Cu – N 33Cr – 31Ni – 32Fe – 1.5Mo – 0.6Cu – N 33Cr – 31Ni – 32Fe – 1.5Mo – 0.6Cu – N 33Cr – 31Ni – 32Fe – 1.5Mo – 0.6Cu – N Smls. & wld. fittings Forged fittings Forgings Wld. pipe SB-366 SB-462 SB-564 SB-619 … … … … R20033 R20033 R20033 R20033 Solution ann. Solution ann. Solution ann. Solution ann. 12 13 14 15 33Cr – 31Ni – 32Fe – 1.5Mo – 0.6Cu – N 33Cr – 31Ni – 32Fe – 1.5Mo – 0.6Cu – N 33Cr – 31Ni – 32Fe – 1.5Mo – 0.6Cu – N 33Cr – 31Ni – 32Fe – 1.5Mo – 0.6Cu – N Smls. pipe & tube Plate, sheet, strip Wld. tube Rod SB-622 SB-625 SB-626 SB-649 … … … … R20033 R20033 R20033 R20033 Solution ann. Solution ann. Solution ann. Solution ann. 16 17 18 19 21Ni – 30Fe – 22Cr – 18Co – 3Mo – 3W 21Ni – 30Fe – 22Cr – 18Co – 3Mo – 3W 21Ni – 30Fe – 22Cr – 18Co – 3Mo – 3W 21Ni – 30Fe – 22Cr – 18Co – 3Mo – 3W Plate, sheet, strip Plate, sheet, strip Rod Rod SB-435 SB-435 SB-572 SB-572 … … … … R30556 R30556 R30556 R30556 Annealed Annealed Annealed Annealed 20 21 22 23 24 25 21Ni – 30Fe – 22Cr – 18Co – 3Mo – 3W 21Ni – 30Fe – 22Cr – 18Co – 3Mo – 3W 21Ni – 30Fe – 22Cr – 18Co – 3Mo – 3W 21Ni – 30Fe – 22Cr – 18Co – 3Mo – 3W 21Ni – 30Fe – 22Cr – 18Co – 3Mo – 3W 21Ni – 30Fe – 22Cr – 18Co – 3Mo – 3W Wld. pipe Wld. pipe Smls. pipe & tube Smls. pipe & tube Wld. tube Wld. tube SB-619 SB-619 SB-622 SB-622 SB-626 SB-626 … … … … … … R30556 R30556 R30556 R30556 R30556 R30556 Annealed Annealed Annealed Annealed Annealed Annealed 26 27 Co – 26Cr – 9Ni – 5Mo – 3Fe – 2W Co – 26Cr – 9Ni – 5Mo – 3Fe – 2W Rod Plate, sheet, strip SB-815 SB-818 … … R31233 R31233 Solution ann. Solution ann. 28 29 30 31 Ti Ti Ti Ti Plate, sheet, strip Smls. tube Wld. tube Bar, billet SB-265 SB-338 SB-338 SB-348 1 1 1 1 R50250 R50250 R50250 R50250 Annealed Annealed Annealed Annealed 32 33 34 35 Ti Ti Ti Ti Smls. & wld. fittings Forgings Smls. pipe Wld. pipe SB-363 SB-381 SB-861 SB-862 WPT1 F-1 1 1 R50250 R50250 R50250 R50250 Annealed Annealed Annealed Annealed 36 37 38 39 40 Ti Ti Ti Ti Ti Castings Plate, sheet, strip Smls. tube Wld. tube Bar, billet SB-367 SB-265 SB-338 SB-338 SB-348 C-2 2 2 2 2 R50400 R50400 R50400 R50400 R50400 … Annealed Annealed Annealed Annealed 41 42 43 44 Ti Ti Ti Ti Smls. & wld. fittings Forgings Smls. pipe Wld. pipe SB-363 SB-381 SB-861 SB-862 WPT2 F-2 2 2 R50400 R50400 R50400 R50400 Annealed Annealed Annealed Annealed Line No. 250 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 … … … … 46 46 46 46 620 620 620 620 240 240 240 240 NP NP NP NP NP NP NP NP 816 816 816 816 NP NP NP NP NFN-13 NFN-13 NFN-13 NFN-13 T14 G5, T14 G14, T14 G5, G14, T14 5 6 7 … … … 43 … … 550 495 525 310 275 275 NP NP NP NP NP NP 260 538 538 260 343 343 NFN-10 NFN-10 NFN-10 G15 G15, W1 G15, W1 8 9 10 11 … … … … 45 45 45 45 750 750 750 750 380 380 380 380 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-10 NFN-10 NFN-10 NFN-10 W12 … … G14 12 13 14 15 … … … … 45 45 45 45 750 750 750 750 380 380 380 380 NP NP NP NP NP NP NP NP 427 427 427 427 NP NP NP NP NFN-10 NFN-10 NFN-10 NFN-10 … … G14 … 16 17 18 19 … … … … 45 45 45 45 690 690 690 690 310 310 310 310 NP NP NP NP NP NP NP NP 899 899 899 899 343 343 343 343 NFN-15 NFN-15 NFN-15 NFN-15 G4, T17 G4, G5, T16 G4, T17 G4, G5, T16 20 21 22 23 24 25 … … … … … … 45 45 45 45 45 45 690 690 690 690 690 690 310 310 310 310 310 310 NP NP NP NP NP NP NP NP NP NP NP NP 899 899 899 899 899 899 343 343 343 343 343 343 NFN-15 NFN-15 NFN-15 NFN-15 NFN-15 NFN-15 G4, G14, T16 G4, G5, G14, T15 G4, T17 G4, G5, T16 G4, G14, T16 G4, G5, G14, T15 26 27 … … 49 49 896 896 379 379 NP NP NP NP 427 427 NP NP NFN-15 NFN-15 G8 G8 28 29 30 31 … … … … 51 51 51 51 240 240 240 240 138 138 138 138 316 316 316 316 316 316 316 316 316 316 316 316 NP NP NP NP NFT-3 NFT-3 NFT-3 NFT-3 … … G14, W6 … 32 33 34 35 … … … … 51 51 51 51 240 240 240 240 138 138 138 138 NP NP 316 316 316 316 316 316 316 316 316 316 NP NP NP NP NFT-3 NFT-3 NFT-3 NFT-3 W5, W12 … … G14, W6 36 37 38 39 40 … … … … … 51 51 51 51 51 345 345 345 345 345 275 275 275 275 275 NP 316 316 316 316 NP 316 316 316 316 260 316 316 316 316 260 316 316 316 316 NFT-2 NFT-2 NFT-2 NFT-2 NFT-2 G15, W1 … … G14, W6 … 41 42 43 44 … … … … 51 51 51 51 345 345 345 345 275 275 275 275 NP NP 316 316 316 316 316 316 316 316 316 316 316 316 316 316 NFT-2 NFT-2 NFT-2 NFT-2 W5, W12 … … G14, W6 251 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 161 161 137 137 151 161 128 137 139 161 118 137 132 161 113 137 126 161 107 136 120 159 102 135 115 154 97.3 131 110 148 93.1 126 105 142 89.5 121 101 137 86.6 117 98.6 133 84.1 113 96.5 130 81.9 111 94.7 128 80.4 108 93.8 127 80.0 108 93.8 126 80.0 108 93.1 126 79.3 108 93.1 126 79.3 108 93.1 126 79.3 108 5 6 7 158 142 150 156 138 143 152 133 140 150 130 140 149 128 140 148 128 140 148 128 140 148 127 140 148 126 140 148 122 138 … 118 132 … 117 127 … 117 126 … 117 124 … 117 122 … 117 119 … 117 118 … 115 115 8 9 10 11 214 214 214 182 214 214 214 182 212 212 212 180 204 204 204 173 193 193 193 164 186 186 186 158 181 181 181 154 177 177 177 150 173 173 173 147 168 168 168 143 164 164 164 140 162 162 162 138 161 161 161 137 159 159 159 135 158 158 158 134 156 156 156 133 154 154 154 131 … … … … 12 13 14 15 214 214 182 214 214 214 182 214 212 212 180 212 204 204 173 204 193 193 164 193 186 186 158 186 181 181 154 181 177 177 150 177 173 173 147 173 168 168 143 168 164 164 140 164 162 162 138 162 161 161 137 161 159 159 135 159 158 158 134 158 156 156 133 156 154 154 131 154 … … … … 16 17 18 19 197 197 197 197 187 197 187 197 174 197 174 197 166 195 166 195 159 193 159 193 153 190 153 190 148 187 148 187 143 185 143 185 140 183 140 183 137 181 137 181 135 180 135 180 132 178 132 178 130 176 130 176 129 173 129 173 127 172 127 172 126 170 126 170 124 168 124 168 123 167 123 167 20 21 22 23 24 25 168 168 197 197 168 168 159 168 187 197 159 168 148 167 174 197 148 167 141 166 166 195 141 166 135 164 159 193 135 164 130 161 153 190 130 161 125 159 148 187 125 159 122 157 143 185 122 157 119 156 140 183 119 156 116 155 137 181 116 155 114 153 135 180 114 153 112 151 132 178 112 151 111 149 130 176 111 149 109 147 129 173 109 147 108 145 127 172 108 145 107 144 126 170 107 144 106 143 124 168 106 143 105 142 123 167 105 142 26 27 236 236 235 235 218 218 … … 196 196 … … 177 177 … … 163 163 … … 154 154 151 151 148 148 146 146 144 144 142 142 139 139 … … 28 29 30 31 68.9 68.9 58.6 68.9 64.2 64.2 54.6 64.2 55.6 55.6 47.0 55.6 50.2 50.2 42.8 50.2 45.3 45.3 38.4 45.3 41.6 41.6 35.3 41.6 38.4 38.4 32.9 38.4 33.9 33.9 28.6 33.9 30.3 30.3 25.8 30.3 27.4 27.4 23.3 27.4 25.2 25.2 21.4 25.2 23.4 23.4 19.2 23.4 … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 68.9 68.9 68.9 58.6 64.2 64.2 64.2 54.6 55.6 55.6 55.6 47.0 50.2 50.2 50.2 42.8 45.3 45.3 45.3 38.4 41.6 41.6 41.6 35.3 38.4 38.4 38.4 32.9 33.9 33.9 33.9 28.6 30.3 30.3 30.3 25.8 27.4 27.4 27.4 23.3 25.2 25.2 25.2 21.4 23.4 23.4 23.4 19.2 … … … … … … … … … … … … … … … … … … … … … … … … 36 37 38 39 40 98.6 98.6 98.6 83.4 98.6 90.5 94.6 94.6 80.8 94.6 79.4 83.5 83.5 71.2 83.5 72.8 76.9 76.9 65.4 76.9 66.6 70.8 70.8 60.5 70.8 61.7 65.8 65.8 56.1 65.8 56.7 61.4 61.4 52.3 61.4 52.2 57.6 57.6 49.1 57.6 48.3 53.9 53.9 46.1 53.9 44.7 50.1 50.1 43.0 50.1 … 46.7 46.7 39.9 46.7 … 43.7 43.7 36.7 43.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 41 42 43 44 98.6 98.6 98.6 83.4 94.6 94.6 94.6 80.8 83.5 83.5 83.5 71.2 76.9 76.9 76.9 65.4 70.8 70.8 70.8 60.5 65.8 65.8 65.8 56.1 61.4 61.4 61.4 52.3 57.6 57.6 57.6 49.1 53.9 53.9 53.9 46.1 50.1 50.1 50.1 43.0 46.7 46.7 46.7 39.9 43.7 43.7 43.7 36.7 … … … … … … … … … … … … … … … … … … … … … … … … 252 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 93.1 126 79.3 108 93.1 122 79.3 104 93.0 105 79.3 89.4 89.2 89.2 76.1 76.1 72.4 72.4 61.8 61.8 61.2 61.2 51.8 51.8 51.3 51.3 43.8 43.8 43.2 43.2 37.0 37.0 36.2 36.2 30.6 30.6 31.0 31.0 26.5 26.5 26.5 26.5 22.8 22.8 22.5 22.5 19.4 19.4 19.1 19.1 16.4 16.4 16.1 16.1 13.3 13.3 … … … … … … … … … … … … 5 6 7 … 112 113 … 110 110 … 108 107 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 8 9 10 11 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 12 13 14 15 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 122 165 122 165 121 163 121 163 120 162 120 162 119 158 119 158 118 140 118 140 115 115 115 115 93.0 93.0 93.0 93.0 76.1 76.1 76.1 76.1 62.9 62.9 62.9 62.9 51.3 51.3 51.3 51.3 41.8 41.8 41.8 41.8 34.3 34.3 34.3 34.3 28.3 28.3 28.3 28.3 22.6 22.6 22.6 22.6 17.4 17.4 17.4 17.4 14.0 14.0 14.0 14.0 10.9 10.9 10.9 10.9 20 21 22 23 24 25 104 140 122 165 104 140 103 138 121 163 103 138 102 138 120 162 102 138 101 134 119 158 101 134 99.8 119 118 140 99.8 119 98.1 98.1 115 115 98.1 98.1 79.3 79.3 93.0 93.0 79.3 79.3 65.0 65.0 76.1 76.1 65.0 65.0 53.6 53.6 62.9 62.9 53.6 53.6 43.9 43.9 51.3 51.3 43.9 43.9 35.9 35.9 41.8 41.8 35.9 35.9 29.1 29.1 34.3 34.3 29.1 29.1 24.0 24.0 28.3 28.3 24.0 24.0 19.5 19.5 22.6 22.6 19.5 19.5 14.8 14.8 17.4 17.4 14.8 14.8 12.0 12.0 14.0 14.0 12.0 12.0 9.54 9.54 10.9 10.9 9.54 9.54 26 27 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 31 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 36 37 38 39 40 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 41 42 43 44 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 253 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 5 6 Ti Ti Ti Ti Ti Ti Plate, sheet, strip Smls. tube Wld. tube Bar, billet Smls. fittings Wld. fittings SB-265 SB-338 SB-338 SB-348 SB-363 SB-363 2H 2H 2H 2H WPT2H WPT2HW R50400 R50400 R50400 R50400 R50400 R50400 Annealed Annealed Annealed Annealed Annealed Annealed 7 8 9 Ti Ti Ti Forgings Smls. pipe Wld. pipe SB-381 SB-861 SB-862 F-2H 2H 2H R50400 R50400 R50400 Annealed Annealed Annealed 10 11 12 13 14 15 Ti Ti Ti Ti Ti Ti Castings Plate, sheet, strip Smls. tube Wld. tube Bar, billet Smls. & wld. fittings SB-367 SB-265 SB-338 SB-338 SB-348 SB-363 C-3 3 3 3 3 WPT3 R50550 R50550 R50550 R50550 R50550 R50550 … Annealed Annealed Annealed Annealed Annealed 16 17 18 Ti Ti Ti Forgings Smls. pipe Wld. pipe SB-381 SB-861 SB-862 F-3 3 3 R50550 R50550 R50550 Annealed Annealed Annealed 19 20 21 Ti – Pd Ti – Pd Ti – Ru Plate, sheet, strip Plate, sheet, strip Plate, sheet, strip SB-265 SB-265 SB-265 11 17 27 R52250 R52252 R52254 Annealed Annealed Annealed 22 23 24 25 26 27 Ti – Pd Ti – Pd Ti – Pd Ti – Pd Ti – Pd Ti – Pd Plate, sheet, strip Smls. tube Wld. tube Bar, billet Smls. fittings Wld. fittings SB-265 SB-338 SB-338 SB-348 SB-363 SB-363 7 7 7 7 WPT7 WPT7W R52400 R52400 R52400 R52400 R52400 R52400 Annealed Annealed Annealed Annealed Annealed Annealed 28 29 30 31 Ti – Pd Ti – Pd Ti – Pd Ti – Pd Castings Forgings Smls. pipe Wld. pipe SB-367 SB-381 SB-861 SB-862 C-7 F-7 7 7 R52400 R52400 R52400 R52400 Annealed Annealed Annealed Annealed 32 33 34 35 36 37 Ti – 0.15Pd Ti – 0.15Pd Ti – 0.15Pd Ti – 0.15Pd Ti – 0.15Pd Ti – 0.15Pd Plate, sheet, strip Smls. tube Wld. tube Bar, billet Smls. fittings Wld. fittings SB-265 SB-338 SB-338 SB-348 SB-363 SB-363 7H 7H 7H 7H WPT7H WPT7HW R52400 R52400 R52400 R52400 R52400 R52400 Annealed Annealed Annealed Annealed Annealed Annealed 38 39 40 Ti – 0.15Pd Ti – 0.15Pd Ti – 0.15Pd Forgings Smls. pipe Wld. pipe SB-381 SB-861 SB-862 F-7H 7H 7H R52400 R52400 R52400 Annealed Annealed Annealed 41 42 43 44 45 Ti – Pd Ti – Pd Ti – Pd Ti – Pd Ti – Pd Plate, sheet, strip Smls. tube Wld. tube Bar, billet Forgings SB-265 SB-338 SB-338 SB-348 SB-381 16 16 16 16 F-16 R52402 R52402 R52402 R52402 R52402 Annealed Annealed Annealed Annealed Annealed Line No. 254 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 6 … … … … … … 51 51 51 51 51 51 400 400 400 400 400 400 275 275 275 275 275 275 NP NP NP NP NP NP NP NP NP NP NP NP 260 260 260 260 260 260 NP NP NP NP NP NP NFT-2 NFT-2 NFT-2 NFT-2 NFT-2 NFT-2 … … G14, W6 … … W12 7 8 9 … … … 51 51 51 400 400 400 275 275 275 NP NP NP NP NP NP 260 260 260 NP NP NP NFT-2 NFT-2 NFT-2 … … W12 10 11 12 13 14 15 … … … … … … 52 52 52 52 52 52 450 450 450 450 450 450 380 380 380 380 380 380 NP 316 316 316 316 NP NP 316 316 316 316 316 260 316 316 316 316 316 NP 316 316 316 316 316 NFT-1 NFT-1 NFT-1 NFT-1 NFT-1 NFT-1 G15, W1 … … G14, W6 … W5, W12 16 17 18 … … … 52 52 52 450 450 450 380 380 380 NP 316 316 316 316 316 316 316 316 316 316 316 NFT-1 NFT-1 NFT-1 … … G14, W6 19 20 21 … … … 51 51 51 240 240 240 138 138 138 NP NP NP NP NP NP 316 316 316 NP NP NP NFT-3 NFT-3 NFT-3 … … … 22 23 24 25 26 27 … … … … … … 51 51 51 51 51 51 345 345 345 345 345 345 275 275 275 275 275 275 NP NP NP NP NP NP 316 316 316 316 NP NP 316 316 316 316 316 316 316 316 316 316 316 316 NFT-2 NFT-2 NFT-2 NFT-2 NFT-2 NFT-2 … … G14, W6 … … G14 28 29 30 31 … … … … 51 51 51 51 345 345 345 345 275 275 275 275 NP NP NP NP NP NP 316 316 260 316 316 316 260 316 316 316 NFT-2 NFT-2 NFT-2 NFT-2 G15, W1 … … G14, W6 32 33 34 35 36 37 … … … … … … 51 51 51 51 51 51 400 400 400 400 400 400 275 275 275 275 275 275 NP NP NP NP NP NP NP NP NP NP NP NP 260 260 260 260 260 260 NP NP NP NP NP NP NFT-2 NFT-2 NFT-2 NFT-2 NFT-2 NFT-2 … … G14, W6 … … W12 38 39 40 … … … 51 51 51 400 400 400 275 275 275 NP NP NP NP NP NP 260 260 260 NP NP NP NFT-2 NFT-2 NFT-2 … … W12 41 42 43 44 45 … … … … … 51 51 51 51 51 345 345 345 345 345 275 275 275 275 275 NP NP NP NP NP NP NP NP NP NP 316 316 316 316 316 316 316 316 316 316 NFT-2 NFT-2 NFT-2 NFT-2 NFT-2 … … G14, W6 … … 255 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 5 6 114 114 96.9 114 114 114 110 110 93.5 110 110 110 97.2 97.2 82.6 97.2 97.2 97.2 89.3 89.3 75.9 89.3 89.3 89.3 82.5 82.5 70.1 82.5 82.5 82.5 76.6 76.6 65.1 76.6 76.6 76.6 71.5 71.5 60.8 71.5 71.5 71.5 66.8 66.8 56.8 66.8 66.8 66.8 62.5 62.5 53.1 62.5 62.5 62.5 58.8 58.8 50.0 58.8 58.8 58.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 114 114 114 110 110 110 97.2 97.2 97.2 89.3 89.3 89.3 82.5 82.5 82.5 76.6 76.6 76.6 71.5 71.5 71.5 66.8 66.8 66.8 62.5 62.5 62.5 58.8 58.8 58.8 … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 14 15 128 128 128 109 128 128 121 121 121 103 121 121 106 106 106 90.1 106 106 96.5 96.5 96.5 82.2 96.5 96.5 87.9 87.9 87.9 74.1 87.9 87.9 79.8 79.8 79.8 67.3 79.8 79.8 72.3 72.3 72.3 61.7 72.3 72.3 65.8 65.8 65.8 56.0 65.8 65.8 60.4 60.4 60.4 51.2 60.4 60.4 56.2 56.2 56.2 47.6 56.2 56.2 … 52.9 52.9 44.9 52.9 52.9 … 49.9 49.9 42.5 49.9 49.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 128 128 109 121 121 103 106 106 90.1 96.5 96.5 82.2 87.9 87.9 74.1 79.8 79.8 67.3 72.3 72.3 61.7 65.8 65.8 56.0 60.4 60.4 51.2 56.2 56.2 47.6 52.9 52.9 44.9 49.9 49.9 42.5 … … … … … … … … … … … … … … … … … … 19 20 21 68.9 68.9 68.9 64.2 64.2 64.2 55.6 55.6 55.6 50.2 50.2 50.2 45.3 45.3 45.3 41.6 41.6 41.6 38.4 38.4 38.4 33.9 33.9 33.9 30.3 30.3 30.3 27.4 27.4 27.4 25.2 25.2 25.2 23.4 23.4 23.4 … … … … … … … … … … … … … … … … … … 22 23 24 25 26 27 98.6 98.6 83.4 98.6 98.6 83.4 94.6 94.6 80.8 94.6 94.6 80.8 83.5 83.5 71.2 83.5 83.5 71.2 76.9 76.9 65.4 76.9 76.9 65.4 70.8 70.8 60.5 70.8 70.8 60.5 65.8 65.8 56.1 65.8 65.8 56.1 61.4 61.4 52.3 61.4 61.4 52.3 57.6 57.6 49.1 57.6 57.6 49.1 53.9 53.9 46.1 53.9 53.9 46.1 50.1 50.1 43.0 50.1 50.1 43.0 46.7 46.7 39.9 46.7 46.7 39.9 43.7 43.7 36.7 43.7 43.7 36.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 31 98.6 98.6 98.6 83.4 90.5 94.6 94.6 80.8 79.4 83.5 83.5 71.2 72.8 76.9 76.9 65.4 66.6 70.8 70.8 60.5 61.7 65.8 65.8 56.1 56.7 61.4 61.4 52.3 52.2 57.6 57.6 49.1 48.3 53.9 53.9 46.1 44.7 50.1 50.1 43.0 … 46.7 46.7 39.9 … 43.7 43.7 36.7 … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 37 114 114 96.9 114 114 114 110 110 93.5 110 110 110 97.2 97.2 82.6 97.2 97.2 97.2 89.3 89.3 75.9 89.3 89.3 89.3 82.5 82.5 70.1 82.5 82.5 82.5 76.6 76.6 65.1 76.6 76.6 76.6 71.5 71.5 60.8 71.5 71.5 71.5 66.8 66.8 56.8 66.8 66.8 66.8 62.5 62.5 53.1 62.5 62.5 62.5 58.8 58.8 50.0 58.8 58.8 58.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 38 39 40 114 114 114 110 110 110 97.2 97.2 97.2 89.3 89.3 89.3 82.5 82.5 82.5 76.6 76.6 76.6 71.5 71.5 71.5 66.8 66.8 66.8 62.5 62.5 62.5 58.8 58.8 58.8 … … … … … … … … … … … … … … … … … … … … … … … … 41 42 43 44 45 98.6 98.6 83.4 98.6 98.6 94.6 94.6 80.8 94.6 94.6 83.5 83.5 71.2 83.5 83.5 76.9 76.9 65.4 76.9 76.9 70.8 70.8 60.5 70.8 70.8 65.8 65.8 56.1 65.8 65.8 61.4 61.4 52.3 61.4 61.4 57.6 57.6 49.1 57.6 57.6 53.9 53.9 46.1 53.9 53.9 50.1 50.1 43.0 50.1 50.1 46.7 46.7 39.9 46.7 46.7 43.7 43.7 36.7 43.7 43.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 256 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 14 15 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 19 20 21 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 25 26 27 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 31 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 37 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 38 39 40 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 41 42 43 44 45 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 257 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. 1 2 3 4 5 6 Ti – 0.05Pd Ti – 0.05Pd Ti – 0.05Pd Ti – 0.05Pd Ti – 0.05Pd Ti – 0.05Pd Plate, sheet, strip Smls. tube Wld. tube Bar, billet Smls. fittings Wld. fittings SB-265 SB-338 SB-338 SB-348 SB-363 SB-363 16H 16H 16H 16H WPT16H WPT16HW R52402 R52402 R52402 R52402 R52402 R52402 Annealed Annealed Annealed Annealed Annealed Annealed 7 8 9 Ti – 0.05Pd Ti – 0.05Pd Ti – 0.05Pd Forgings Smls. pipe Wld. pipe SB-381 SB-861 SB-862 F-16H 16H 16H R52402 R52402 R52402 Annealed Annealed Annealed 10 11 12 13 14 15 Ti – Ru Ti – Ru Ti – Ru Ti – Ru Ti – Ru Ti – Ru Plate, sheet, strip Smls. tube Wld. tube Bar, billet Smls. fittings Wld. fittings SB-265 SB-338 SB-338 SB-348 SB-363 SB-363 26 26 26 26 WPT26 WPT26W R52404 R52404 R52404 R52404 R52404 R52404 Annealed Annealed Annealed Annealed Annealed Annealed 16 17 18 Ti – Ru Ti – Ru Ti – Ru Forgings Smls. pipe Wld. pipe SB-381 SB-861 SB-862 F-26 26 26 R52404 R52404 R52404 Annealed Annealed Annealed 19 20 21 22 23 24 Ti – 0.10Ru Ti – 0.10Ru Ti – 0.10Ru Ti – 0.10Ru Ti – 0.10Ru Ti – 0.10Ru Plate, sheet, strip Smls. tube Wld. tube Bar, billet Smls. fittings Wld. fittings SB-265 SB-338 SB-338 SB-348 SB-363 SB-363 26H 26H 26H 26H WPT26H WPT26HW R52404 R52404 R52404 R52404 R52404 R52404 Annealed Annealed Annealed Annealed Annealed Annealed 25 26 27 Ti – 0.10Ru Ti – 0.10Ru Ti – 0.10Ru Forgings Smls. pipe Wld. pipe SB-381 SB-861 SB-862 F-26H 26H 26H R52404 R52404 R52404 Annealed Annealed Annealed 28 29 30 31 Ti – 0.3Mo – 0.8Ni Ti – 0.3Mo – 0.8Ni Ti – 0.3Mo – 0.8Ni Ti – 0.3Mo – 0.8Ni Plate, sheet, strip Smls. tube Wld. tube Bar, billet SB-265 SB-338 SB-338 SB-348 12 12 12 12 R53400 R53400 R53400 R53400 Annealed Annealed Annealed Annealed 32 33 34 35 36 Ti – 0.3Mo – 0.8Ni Ti – 0.3Mo – 0.8Ni Ti – 0.3Mo – 0.8Ni Ti – 0.3Mo – 0.8Ni Ti – 0.3Mo – 0.8Ni Smls. fittings Wld. fittings Forgings Smls. pipe Wld. pipe SB-363 SB-363 SB-381 SB-861 SB-862 WPT12 WPT12W F-12 12 12 R53400 R53400 R53400 R53400 R53400 Annealed Annealed Annealed Annealed Annealed 37 38 39 40 Ti – 3Al – 2.5V Ti – 3Al – 2.5V Ti – 3Al – 2.5V Ti – 3Al – 2.5V Plate, sheet, strip Smls. tube Wld. tube Bar, billet SB-265 SB-338 SB-338 SB-348 9 9 9 9 R56320 R56320 R56320 R56320 Annealed Annealed Annealed Annealed 41 42 43 44 45 Ti – 3Al – 2.5V Ti – 3Al – 2.5V Ti – 3Al – 2.5V Ti – 3Al – 2.5V Ti – 3Al – 2.5V Smls. fittings Wld. fittings Forgings Smls. pipe Wld. pipe SB-363 SB-363 SB-381 SB-861 SB-862 WPT9 WPT9W F-9 9 9 R56320 R56320 R56320 R56320 R56320 Annealed Annealed Annealed Annealed Annealed Line No. 258 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 5 6 … … … … … … 51 51 51 51 51 51 400 400 400 400 400 400 275 275 275 275 275 275 NP NP NP NP NP NP NP NP NP NP NP NP 260 260 260 260 260 260 NP NP NP NP NP NP NFT-2 NFT-2 NFT-2 NFT-2 NFT-2 NFT-2 … … G14, W6 … … W12 7 8 9 … … … 51 51 51 400 400 400 275 275 275 NP NP NP NP NP NP 260 260 260 NP NP NP NFT-2 NFT-2 NFT-2 … … W12 10 11 12 13 14 15 … … … … … … 51 51 51 51 51 51 345 345 345 345 345 345 275 275 275 275 275 275 NP NP NP NP NP NP NP NP NP NP NP NP 316 316 316 316 316 316 316 316 316 316 316 316 NFT-2 NFT-2 NFT-2 NFT-2 NFT-2 NFT-2 … … G14, W6 … … G14 16 17 18 … … … 51 51 51 345 345 345 275 275 275 NP NP NP NP NP NP 316 316 316 316 316 316 NFT-2 NFT-2 NFT-2 … … G14, W6 19 20 21 22 23 24 … … … … … … 51 51 51 51 51 51 400 400 400 400 400 400 275 275 275 275 275 275 NP NP NP NP NP NP NP NP NP NP NP NP 260 260 260 260 260 260 NP NP NP NP NP NP NFT-2 NFT-2 NFT-2 NFT-2 NFT-2 NFT-2 … … G14, W6 … … W12 25 26 27 … … … 51 51 51 400 400 400 275 275 275 NP NP NP NP NP NP 260 260 260 NP NP NP NFT-2 NFT-2 NFT-2 … … W12 28 29 30 31 … … … … 52 52 52 52 485 485 485 485 345 345 345 345 NP NP NP NP NP NP NP NP 316 316 316 316 316 316 316 316 NFT-1 NFT-1 NFT-1 NFT-1 … … G14, W6 … 32 33 34 35 36 … … … … … 52 52 52 52 52 485 485 485 485 485 345 345 345 345 345 NP NP NP NP NP NP NP NP NP NP 316 316 316 316 316 316 316 316 316 316 NFT-1 NFT-1 NFT-1 NFT-1 NFT-1 … G14 … … G14, W6 37 38 39 40 … … … … 53 53 53 53 620 620 620 620 485 485 485 485 NP NP NP NP 316 316 316 316 316 316 316 NP 316 316 316 NP NFT-4 NFT-4 NFT-4 NFT-4 … … G14, W6 … 41 42 43 44 45 … … … … … 53 53 53 53 53 620 620 620 620 620 485 485 485 485 485 NP NP NP NP NP 316 316 316 316 316 NP NP NP 316 316 NP NP NP 316 316 NFT-4 NFT-4 NFT-4 NFT-4 NFT-4 … G14, W6 … … G14, W6 259 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 1 2 3 4 5 6 114 114 96.9 114 114 114 110 110 93.5 110 110 110 97.2 97.2 82.6 97.2 97.2 97.2 89.3 89.3 75.9 89.3 89.3 89.3 82.5 82.5 70.1 82.5 82.5 82.5 76.6 76.6 65.1 76.6 76.6 76.6 71.5 71.5 60.8 71.5 71.5 71.5 66.8 66.8 56.8 66.8 66.8 66.8 62.5 62.5 53.1 62.5 62.5 62.5 58.8 58.8 50.0 58.8 58.8 58.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 114 114 114 110 110 110 97.2 97.2 97.2 89.3 89.3 89.3 82.5 82.5 82.5 76.6 76.6 76.6 71.5 71.5 71.5 66.8 66.8 66.8 62.5 62.5 62.5 58.8 58.8 58.8 … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 14 15 98.6 98.6 83.4 98.6 98.6 83.4 94.6 94.6 80.8 94.6 94.6 80.8 83.5 83.5 71.2 83.5 83.5 71.2 76.9 76.9 65.4 76.9 76.9 65.4 70.8 70.8 60.5 70.8 70.8 60.5 65.8 65.8 56.1 65.8 65.8 56.1 61.4 61.4 52.3 61.4 61.4 52.3 57.6 57.6 49.1 57.6 57.6 49.1 53.9 53.9 46.1 53.9 53.9 46.1 50.1 50.1 43.0 50.1 50.1 43.0 46.7 46.7 39.9 46.7 46.7 39.9 43.7 43.7 36.7 43.7 43.7 36.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 98.6 98.6 83.4 94.6 94.6 80.8 83.5 83.5 71.2 76.9 76.9 65.4 70.8 70.8 60.5 65.8 65.8 56.1 61.4 61.4 52.3 57.6 57.6 49.1 53.9 53.9 46.1 50.1 50.1 43.0 46.7 46.7 39.9 43.7 43.7 36.7 … … … … … … … … … … … … … … … … … … 19 20 21 22 23 24 114 114 96.9 114 114 114 110 110 93.5 110 110 110 97.2 97.2 82.6 97.2 97.2 97.2 89.3 89.3 75.9 89.3 89.3 89.3 82.5 82.5 70.1 82.5 82.5 82.5 76.6 76.6 65.1 76.6 76.6 76.6 71.5 71.5 60.8 71.5 71.5 71.5 66.8 66.8 56.8 66.8 66.8 66.8 62.5 62.5 53.1 62.5 62.5 62.5 58.8 58.8 50.0 58.8 58.8 58.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 114 114 114 110 110 110 97.2 97.2 97.2 89.3 89.3 89.3 82.5 82.5 82.5 76.6 76.6 76.6 71.5 71.5 71.5 66.8 66.8 66.8 62.5 62.5 62.5 58.8 58.8 58.8 … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 31 138 138 117 138 138 138 117 138 126 126 108 126 119 119 101 119 111 111 94.9 111 105 105 89.3 105 99.5 99.5 84.2 99.5 94.9 94.9 80.2 94.9 91.4 91.4 77.4 91.4 88.8 88.8 75.4 88.8 86.4 86.4 73.6 86.4 83.9 83.9 71.7 83.9 … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 138 117 138 138 117 138 117 138 138 117 126 108 126 126 108 119 101 119 119 101 111 94.9 111 111 94.9 105 89.3 105 105 89.3 99.5 84.2 99.5 99.5 84.2 94.9 80.2 94.9 94.9 80.2 91.4 77.4 91.4 91.4 77.4 88.8 75.4 88.8 88.8 75.4 86.4 73.6 86.4 86.4 73.6 83.9 71.7 83.9 83.9 71.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 37 38 39 40 177 177 151 177 177 177 151 177 168 168 143 168 162 162 138 162 155 155 132 155 148 148 126 148 141 141 119 141 133 133 113 133 127 127 108 127 122 122 104 122 120 120 102 120 118 118 101 118 … … … … … … … … … … … … … … … … … … … … … … … … 41 42 43 44 45 177 151 177 177 151 177 151 177 177 151 168 143 168 168 143 162 138 162 162 138 155 132 155 155 132 148 126 148 148 126 141 119 141 141 119 133 113 133 133 113 127 108 127 127 108 122 104 122 122 104 120 102 120 120 102 118 101 118 118 101 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 260 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 5 6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 14 15 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 19 20 21 22 23 24 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 31 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 37 38 39 40 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 41 42 43 44 45 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 261 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. (10) (10) (10) (10) 1 2 3 4 Ti – 3Al – 2.5V – 0.1Ru Ti – 3Al – 2.5V – 0.1Ru Ti – 3Al – 2.5V – 0.1Ru Ti – 3Al – 2.5V – 0.1Ru Plate, sheet, strip Smls. tube Wld. tube Bar, billet SB-265 SB-338 SB-338 SB-348 28 28 28 28 R56323 R56323 R56323 R56323 Annealed Annealed Annealed Annealed (10) (10) (10) (10) (10) 5 6 7 8 9 Ti – 3Al – 2.5V – 0.1Ru Ti – 3Al – 2.5V – 0.1Ru Ti – 3Al – 2.5V – 0.1Ru Ti – 3Al – 2.5V – 0.1Ru Ti – 3Al – 2.5V – 0.1Ru Smls. fittings Wld. fittings Forgings Smls. pipe Wld. pipe SB-363 SB-363 SB-381 SB-861 SB-862 WPT28 WPT28W F-28 28 28 R56323 R56323 R56323 R56323 R56323 Annealed Annealed Annealed Annealed Annealed 10 11 12 13 99.2Zr 99.2Zr 99.2Zr 99.2Zr Forgings Smls. tube Wld. tube Bar, wire SB-493 SB-523 SB-523 SB-550 … … … … R60702 R60702 R60702 R60702 Annealed Annealed Annealed Annealed 14 15 16 17 99.2Zr 99.2Zr 99.2Zr 99.2Zr Plate, sheet, strip Smls. fittings Wld. fittings Smls. & wld. pipe SB-551 SB-653 SB-653 SB-658 … PZ-2 PZ-2W … R60702 R60702 R60702 R60702 Annealed Annealed Annealed Annealed 18 19 20 21 22 23 95.2Zr + Nb 95.2Zr + Nb 95.2Zr + Nb 95.2Zr + Nb 95.2Zr + Nb 95.2Zr + Nb Forgings Smls. tube Wld. tube Bar, wire Plate, sheet, strip Smls. & wld. pipe SB-493 SB-523 SB-523 SB-550 SB-551 SB-658 … … … … … … R60705 R60705 R60705 R60705 R60705 R60705 Annealed Annealed Annealed Annealed Annealed Annealed 262 Class/Condition/ Temper 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Line No. Size/Thickness, mm P-No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) (SPT p Supports Only) I III VIII-1 XII External Pressure Chart No. Notes 1 2 3 4 … … … … 53 53 53 53 620 620 620 620 485 485 485 485 NP NP NP NP NP NP NP NP 316 316 316 316 NP NP NP NP NFT-4 NFT-4 NFT-4 NFT-4 … … G14, W6 … (10) (10) (10) (10) 5 6 7 8 9 … … … … … 53 53 53 53 53 620 620 620 620 620 485 485 485 485 485 NP NP NP NP NP NP NP NP NP NP 316 316 316 316 316 NP NP NP NP NP NFT-4 NFT-4 NFT-4 NFT-4 NFT-4 … G14, W6 … … G14, W6 (10) (10) (10) (10) (10) 10 11 12 13 … … … … 61 61 61 61 380 380 380 380 205 205 205 205 NP NP NP NP 204 204 204 204 371 371 371 371 NP NP NP NP NFZ-1 NFZ-1 NFZ-1 NFZ-1 … … G14, W6 … 14 15 16 17 … … … … 61 61 61 61 380 380 380 380 205 205 205 205 NP NP NP NP 204 204 204 204 371 371 371 371 NP NP NP NP NFZ-1 NFZ-1 NFZ-1 NFZ-1 … … G14, W6 W12 18 19 20 21 22 23 … … … … … … 62 62 62 62 62 62 485 550 550 550 550 550 380 380 380 380 380 380 NP NP NP NP NP NP NP NP NP NP NP NP 371 371 371 371 371 371 NP NP NP NP NP NP NFZ-2 NFZ-2 NFZ-2 NFZ-2 NFZ-2 NFZ-2 W2 W2 G14, W2, W6 W2 W2 W2, W12 263 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 (10) (10) (10) (10) 1 2 3 4 177 177 151 177 177 177 151 177 168 168 143 168 162 162 138 162 155 155 132 155 148 148 126 148 141 141 119 141 133 133 113 133 127 127 108 127 122 122 104 122 120 120 102 120 118 118 101 118 … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) 5 6 7 8 9 177 151 177 177 151 177 151 177 177 151 168 143 168 168 143 162 138 162 162 138 155 132 155 155 132 148 126 148 148 126 141 119 141 141 119 133 113 133 133 113 127 108 127 127 108 122 104 122 122 104 120 102 120 120 102 118 101 118 118 101 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 108 108 92.4 108 104 104 88.4 104 92.1 92.1 78.0 92.1 84.3 84.3 71.4 84.3 76.9 76.9 65.2 76.9 70.1 70.1 59.7 70.1 63.7 63.7 54.0 63.7 58.7 58.7 49.4 58.7 53.3 53.3 45.2 53.3 47.9 47.9 40.7 47.9 43.5 43.5 37.0 43.5 40.3 40.3 34.1 40.3 38.0 38.0 32.0 38.0 35.5 35.5 30.9 35.5 … … … … … … … … … … … … … … … … 14 15 16 17 108 108 92.4 108 104 104 88.4 104 92.1 92.1 78.0 92.1 84.3 84.3 71.4 84.3 76.9 76.9 65.2 76.9 70.1 70.1 59.7 70.1 63.7 63.7 54.0 63.7 58.7 58.7 49.4 58.7 53.3 53.3 45.2 53.3 47.9 47.9 40.7 47.9 43.5 43.5 37.0 43.5 40.3 40.3 34.1 40.3 38.0 38.0 32.0 38.0 35.5 35.5 30.9 35.5 … … … … … … … … … … … … … … … … 18 19 20 21 22 23 138 158 134 158 158 158 126 144 122 144 144 144 112 128 109 128 128 128 104 119 101 119 119 119 97.6 111 94.9 111 111 111 91.9 105 89.5 105 105 105 87.0 99.5 84.9 99.5 99.5 99.5 82.8 94.7 80.8 94.7 94.7 94.7 79.2 90.5 77.2 90.5 90.5 90.5 76.0 86.8 73.9 86.8 86.8 86.8 73.2 83.7 71.1 83.7 83.7 83.7 71.0 81.2 68.9 81.2 81.2 81.2 69.4 79.4 67.4 79.4 79.4 79.4 68.0 77.6 66.0 77.6 77.6 77.6 … … … … … … … … … … … … … … … … … … … … … … … … 264 2011a SECTION II, PART D (METRIC) TABLE 1B (CONT’D) SECTION I; SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISION 1; AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR NONFERROUS MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 1 2 3 4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) 5 6 7 8 9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … (10) (10) (10) (10) (10) 10 11 12 13 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 17 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 18 19 20 21 22 23 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 265 2011a SECTION II, PART D (METRIC) NOTES TO TABLE 1B (10) GENERAL NOTES (a) The following abbreviations are used: ann., annealed; cond., condenser; exch., exchanger; extr., extruded; fin., finished; fr., from; rel., relieved; rld., rolled; Smls., Seamless; Sol., Solution; treat., treated; and Wld., Welded. (b) The stress values in this Table may be interpolated to determine values for intermediate temperatures. The values at intermediate temperatures shall be rounded to the same number of decimal places as the value at the higher temperature between which values are being interpolated. The rounding rule is: when the next digit beyond the last place to be retained is less than 5, retain unchanged the digit in the last place retained; when the digit next beyond the last place to be retained is 5 or greater, increase by 1 the digit in the last place retained. (c) For Section VIII and XII applications, stress values in restricted shear, such as dowel bolts, rivets, or similar construction in which the shearing is so restricted that the section under consideration would fail without reduction of areas, shall be 0.80 times the values in this Table. (d) For Section VIII and XII applications, stress values in bearing shall be 1.60 times the values in this Table. (e) An alternative typeface is used for stress values obtained from time-dependent properties (see Notes T1 through T18). (f) Where specifications, grades, classes, and types are listed in this Table, and where the material specification in Section II, Part A or Part B is a dual-unit specification (e.g., SB-407/SB-407M), the values listed in this Table shall be applicable to either the customary U.S. version of the material specification or the SI units version of the material specification. For example, the values listed for SB-407 Grade N08800 shall be used when SB-407M Grade N08800 is used in construction. (g) The properties of steels are influenced by the processing history, heat treatment, melting practice, and level of residual elements. See Nonmandatory Appendix A for more information. NOTES — GENERAL REQUIREMENTS G1 For steam at 1700 kPa (208°C), the values given for 200°C may be used. G2 At temperatures over 550°C, these stress values apply only when the carbon is 0.04% or higher. G3 In the absence of evidence that the casting is of high quality throughout, values not in excess of 80% of those given in the Table shall be used. This is not intended to apply to valves and fittings made to recognized standards. G4 Creep-fatigue, thermal ratcheting, and environmental effects are increasingly significant failure modes at temperatures in excess of 825°C and shall be considered in the design. G5 Due to the relatively low yield strength of these materials, these higher stress values were established at temperatures where the shorttime tensile properties govern to permit the use of these alloys where slightly greater deformation is acceptable. The stress values in this range exceed 662⁄3% but do not exceed 90% of the yield strength at temperature. Use of these stresses may result in dimensional changes due to permanent strain. These stress values are not recommended for the flanges of gasketed joints or other applications where slight amounts of distortion can cause leakage or malfunction. For Section III applications, Table Y-2 lists multiplying factors that, when applied to the yield strength values shown in Table Y-1, will give allowable stress values that will result in lower levels of permanent strain. G6 Maximum temperature for external pressure not to exceed 175°C. G7 Use 175°C curve for all temperature values below 175°C. G8 The stresses for this material are based on 828 MPa minimum tensile strength because of weld metal strength limitations. G9 Use Fig. NFC-6 up to and including 150°C. Use the 325°C curve of Fig. NFC-3 above 150°C up to and including 200°C. Maximum temperature for external pressure not to exceed 200°C. G10 Maximum temperature for external pressure not to exceed 225°C. G11 Referenced external pressure chart is applicable up to 375°C. G12 Referenced external pressure chart is applicable up to 425°C. G13 For Section VIII and XII applications, use of external pressure charts for material in the form of bar stock is permitted for stiffener rings only. G14 For Section VIII applications, a factor of 0.85 has been applied in arriving at the maximum allowable stress values in tension for this material. Divide tabulated values by 0.85 for maximum allowable longitudinal tensile stress. G15 To these stress values a quality factor as specified in ND-3115 of Section III; UG-24 of Section VIII, Division 1; or TM-190 of Section XII shall be applied for castings. This is not intended to apply to valves and fittings made to recognized standards. G16 Allowable stress values shown are 90% of those for the corresponding core material. G17 Copper–silicon alloys are not always suitable when exposed to certain media and high temperatures, particularly steam above 100°C. The user should ensure that the alloy selected is satisfactory for the service for which it is to be used. G18 Because of the occasionally contingent danger from the failure of pressure vessels by stress corrosion cracking, the following is pertinent. These materials are suitable for engineering use under a wide variety of ordinary corrosive conditions with no particular hazard in respect to stress corrosion. G19 Few alloys are completely immune to stress corrosion cracking in all combinations of stress and corrosive environments, and the supplier of the material should be consulted. Reference may also be made to the following sources: (1) Stress Corrosion Cracking Control Measures, B. F. Brown, U.S. National Bureau of Standards (1977), available from NACE, Texas; (2) The Stress Corrosion of Metals, H. L. Logan, John Wiley & Sons, New York, 1966. G20 For plate only. G21 The maximum operating temperature is arbitrarily set at 250°C because harder temper adversely affects design stress in the creep rupture temperature range. G22 The minimum tensile strength of reduced tension specimens in accordance with QW-462.1 of Section IX shall not be less than 760 MPa. G23 This alloy is subject to severe loss of impact strength at room temperatures after exposure in the range of 550°C to 750°C. G24 For stress relieved tempers (T351, T3510, T3511, T451, T4510, T4511, T651, T6510, T6511), stress values for materials in the basic temper shall be used. G25 The tension test specimen from plate 13 mm and thicker is machined from the core and does not include the cladding alloy; therefore, the allowable stress values for thickness less than 13 mm shall be used. G26 The tension test specimen from plate 13 mm and thicker is machined from the core and does not include the cladding alloy; therefore, the allowable stress values shown are 90% of those for the core material of the same thickness. G27 Alloy N06022 in the solution annealed condition is subject to severe loss of impact strength at room temperatures after exposure in the range of 550°C to 675°C. G28 For external pressure design, the maximum design temperature is limited to 550°C. G29 The maximum allowable stress values for greater than 900°C are 9.7 MPa (927°C), 7.6 MPa (954°C), and 5.0 MPa (982°C). 266 2011a SECTION II, PART D (METRIC) NOTES TO TABLE 1B (CONT’D) NOTES — GENERAL REQUIREMENTS (CONT’D) G30 The maximum allowable stress values for greater than 900°C are 5.0 MPa (925°C), 4.0 MPa (950°C), 3.2 MPa (975°C), and 2.6 MPa (1000°C). The maximum use temperature is 982°C; the value listed at 1000°C is provided for interpolation purposes only. G31 The maximum allowable stress values for greater than 900°C are 7.8 MPa (925°C), 5.2 MPa (950°C), 3.5 MPa (975°C), and 2.4 MPa (1000°C). The maximum use temperature is 982°C; the value listed at 1000°C is provided for interpolation purposes only. G32 The maximum allowable stress values for greater than 900°C are 6.6 MPa (925°C), 4.4 MPa (950°C), 2.9 MPa (975°C), and 2.0 MPa (1000°C). The maximum use temperature is 982°C; the value listed at 1000°C is provided for interpolation purposes only. (10) (10) (10) NOTES — HEAT TREATMENT REQUIREMENTS H1 For temperatures above 550°C, these stress values may be used only if the material is annealed at a minimum temperature of 1040°C and has a carbon content of 0.04% or higher. H2 For temperatures above 550°C, these stress values may be used only if the material is heat treated by heating it to a minimum temperature of 1040°C and quenching in water or rapidly cooling by other means. H3 For Section I applications, cold drawn pipe and tube shall be annealed at 1038°C minimum. H4 The material shall be given a 940°C to 995°C stabilizing heat treatment. NOTES — TIME-DEPENDENT PROPERTIES [See General Note (e)] T1 Allowable stresses for temperatures of 125°C and above are values T2 Allowable stresses for temperatures of 150°C and above are values T3 Allowable stresses for temperatures of 175°C and above are values T4 Allowable stresses for temperatures of 205°C and above are values T5 Allowable stresses for temperatures of 260°C and above are values T6 Allowable stresses for temperatures of 290°C and above are values T7 Allowable stresses for temperatures of 315°C and above are values T8 Allowable stresses for temperatures of 400°C and above are values T9 Allowable stresses for temperatures of 425°C and above are values T10 Allowable stresses for temperatures of 455°C and above are values T11 Allowable stresses for temperatures of 480°C and above are values T12 Allowable stresses for temperatures of 510°C and above are values T13 Allowable stresses for temperatures of 540°C and above are values T14 Allowable stresses for temperatures of 565°C and above are values T15 Allowable stresses for temperatures of 595°C and above are values T16 Allowable stresses for temperatures of 620°C and above are values T17 Allowable stresses for temperatures of 650°C and above are values T18 Allowable stresses for temperatures of 675°C and above are values obtained obtained obtained obtained obtained obtained obtained obtained obtained obtained obtained obtained obtained obtained obtained obtained obtained obtained from from from from from from from from from from from from from from from from from from time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent time-dependent properties. properties. properties. properties. properties. properties. properties. properties. properties. properties. properties. properties. properties. properties. properties. properties. properties. properties. NOTES — WELDING REQUIREMENTS W1 No welding or brazing permitted. W2 For Section VIII applications, UNF-56(d) shall apply for welded constructions. W3 For welded and brazed constructions, stress values for O (annealed) temper material shall be used. W4 The stress values given for this material are not applicable when either welding or thermal cutting is employed. W5 These S values do not include a longitudinal weld efficiency factor. For Section III applications, for materials welded without filler metal, ultrasonic examination, radiographic examination, or eddy current examination, in accordance with NC-2550, shall provide a longitudinal weld efficiency factor of 1.00. Materials welded with filler metal meeting the requirements of NC-2560 shall receive a longitudinal weld efficiency factor of 1.00. Other longitudinal weld efficiency factors shall be in accordance with the following: (a) for single butt weld, with filler metal, 0.80; (b) for single or double butt weld, without filler metal, 0.85; (c) for double butt weld, with filler metal, 0.90; (d) for single or double butt weld, with radiography or ultrasonic, 1.00. W6 Filler metal shall not be used in the manufacture of welded pipe or tubing. W7 Strength of reduced-section tensile specimen required to qualify welding procedures. See QW-150, Section IX. W8 After welding, heat treat at 625°C to 650°C, hold 11⁄2 h at temperature for the first 25 mm of cross-section thickness and 1⁄2 h for each additional 25 mm, and air cool. For castings used in pumps, valves, and fittings DN 50 and less, PWHT is not required for socket welds and attachment welds when the castings have been temper annealed at 625°C to 650°C prior to welding. W9 If welded or brazed, the allowable stress values for the annealed condition shall be used and the minimum tensile strength of the reduced tension specimen in accordance with QW-462.1 of Section IX shall not be less than 205 MPa. W10 When nonferrous materials conforming to specifications in Section II, Part B are used in welded or brazed construction, the maximum allowable working stresses shall not exceed the values given herein for annealed material at the metal temperature shown. W11 These maximum allowable stress values are to be used in welded or brazed constructions. W12 These S values do not include a weld factor. For Section VIII, Division 1 and Section XII applications using welds made without filler metal, the tabulated tensile stress values shall be multiplied by 0.85. For welds made with filler metal, consult UW-12 of Section VIII, Division 1, or TW-130.4 of Section XII, as applicable. W13 For service at 650°C or higher, the deposited weld metal shall be of the same nominal chemistry as the base metal. W14 No welding permitted. W15 For Section VIII and XII applications, no welding is permitted. W16 Use NFA-12 when welded with 5356 or 5556 filler metal, all thicknesses, or 4043 or 5554 filler metal, thickness ≤ 10 mm. Use NFA13 when welded with 4043 or 5554 filler metal, thickness > 10 mm. 267 2011a SECTION II, PART D (METRIC) TABLE 2A SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Line No. Alloy Designation/ UNS No. Class/ Condition/ Temper P-No. Group No. … … … … … 1 1 1 1 1 1 1 1 1 1 … … … … … ≤ 50 … … 1 1 1 1 1 1 1 1 K02801 K03008 K03008 … … … ≤ 50 … … 1 1 1 1 1 1 55 CA55 CE55 K01800 K02801 K02202 … … … … … … 1 1 1 1 1 1 SA-672 SA-672 SA-672 SA-672 A55 B55 C55 E55 K02801 K02001 K01800 K02202 … … … … … … … … 1 1 1 1 1 1 1 1 Plate, bar, shapes Forgings Castings Forgings SA-36 SA-181 SA-216 SA-266 … … WCA 1 K02600 K03502 J02502 K03506 … 60 … … … … … … 1 1 1 1 1 1 1 1 Carbon steel Carbon steel Carbon steel Carbon steel Forgings Castings Cast pipe Bar, shapes SA-350 SA-352 SA-660 SA-675 LF1 LCA WCA 60 K03009 J02504 J02504 … 1 … … … … … … … 1 1 1 1 1 1 1 1 28 29 30 31 32 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Plate Plate Wld. pipe Wld. pipe Wld. pipe SA-515 SA-516 SA-671 SA-671 SA-671 60 60 CB60 CC60 CE60 K02401 K02100 K02401 K02100 K02402 … … … … … … … … … … 1 1 1 1 1 1 1 1 1 1 33 34 35 Carbon steel Carbon steel Carbon steel Wld. pipe Wld. pipe Wld. pipe SA-672 SA-672 SA-672 B60 C60 E60 K02401 K02100 K02402 … … … … … … 1 1 1 1 1 1 36 37 38 39 40 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Wld. pipe Smls. pipe Smls. pipe Fittings Wld. fittings SA-53 SA-53 SA-106 SA-234 SA-234 E/B S/B B WPB WPB K03005 K03005 K03006 K03006 K03006 … … … … W … … … … … 1 1 1 1 1 1 1 1 1 1 41 42 43 44 Carbon steel Carbon steel Carbon steel Carbon steel Smls. & wld. pipe Smls. & wld. tube Fittings Wld. fittings SA-333 SA-334 SA-420 SA-420 6 6 WPL6 WPL6 K03006 K03006 … … … … … WP-W … … … … 1 1 1 1 1 1 1 1 Nominal Composition Product Form Spec No. Type/Grade 1 2 3 4 5 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Plate Wld. pipe Wld. pipe Smls. pipe Smls. pipe SA-285 SA-672 SA-53 SA-53 SA-106 A A45 E/A S/A A K01700 K01700 K02504 K02504 K02501 … … … … … 6 7 8 9 Carbon steel Carbon steel Carbon steel Carbon steel Bar, shapes Plate Wld. pipe Bar, shapes SA-675 SA-285 SA-672 SA-675 50 B A50 55 … K02200 K02200 … 10 11 12 Carbon steel Carbon steel Carbon steel Plate Smls. & wld. pipe Smls. & wld. tube SA-285 SA-333 SA-334 C 1 1 13 14 15 Carbon steel Carbon steel Carbon steel Plate Wld. pipe Wld. pipe SA-516 SA-671 SA-671 16 17 18 19 Carbon steel Carbon steel Carbon steel Carbon steel Wld. pipe Wld. pipe Wld. pipe Wld. pipe 20 21 22 23 Carbon steel Carbon steel Carbon steel Carbon steel 24 25 26 27 268 Size/Thickness, mm 2011a SECTION II, PART D (METRIC) TABLE 2A SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa 1 2 3 4 5 310 310 330 330 330 165 165 205 205 205 6 7 8 9 345 345 345 380 10 11 12 External Pressure Chart No. Notes 371 371 371 (SPT) 371 (SPT) 371 CS-1 CS-1 CS-2 CS-2 CS-2 … G1, G4 E2 E2 E2 170 185 185 190 371 (SPT) 371 371 371 (SPT) CS-1 CS-1 CS-1 CS-1 … E2 E2, G1, G4 … 380 380 380 205 205 205 371 371 371 CS-2 CS-2 CS-2 … … … 13 14 15 380 380 380 205 205 205 371 371 371 CS-2 CS-2 CS-2 … G1, G4 G1, G4 16 17 18 19 380 380 380 380 205 205 205 205 371 371 371 371 CS-2 CS-2 CS-2 CS-2 G1, G4 G1, G4 G1, G4 G1, G4 20 21 22 23 400 415 415 415 250 205 205 205 371 (SPT) 371 371 371 CS-2 CS-2 CS-2 CS-2 E2 … … … 24 25 26 27 415 415 415 415 205 205 205 205 371 371 371 371 (SPT) CS-2 CS-2 CS-2 CS-2 … … … … 28 29 30 31 32 415 415 415 415 415 220 220 220 220 220 371 371 371 371 371 CS-2 CS-2 CS-2 CS-2 CS-2 … … G1, G4 G1, G4 G1, G4 33 34 35 415 415 415 220 220 220 371 371 371 CS-2 CS-2 CS-2 G1, G4 G1, G4 G1, G4 36 37 38 39 40 415 415 415 415 415 240 240 240 240 240 371 (SPT) 371 (SPT) 371 371 371 CS-2 CS-2 CS-2 CS-2 CS-2 E2 E2 E2 E2 E2 41 42 43 44 415 415 415 415 240 240 240 240 371 371 371 371 CS-2 CS-2 CS-2 CS-2 E2 E2 E2 E2 Max. Temp. Limit (SPT p Supports Only) 269 #† 2011a SECTION II, PART D (METRIC) TABLE 2A SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 500 1 2 3 4 5 103 103 110 110 110 103 103 110 110 110 101 101 110 110 110 99.4 99.4 110 110 110 97.8 97.8 110 110 110 94.8 94.8 110 110 110 90.5 90.5 110 110 110 86.2 86.2 108 108 108 83.9 83.9 104 104 104 81.4 81.4 100 100 100 78.9 78.9 99.1 99.1 99.1 … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 9 115 115 115 126 110 115 115 121 105 113 113 115 103 112 112 113 101 110 110 112 98.2 106 106 109 94.6 102 102 104 89.8 97.1 97.1 98.9 87.4 93.9 93.9 96.1 84.7 91.1 91.1 92.9 81.6 89.4 89.4 89.8 … … … … … … … … … … … … … … … … … … … … 10 11 12 126 126 126 126 126 126 126 126 126 124 124 124 122 122 122 118 118 118 114 114 114 107 107 107 104 104 104 101 101 101 98.1 98.1 98.1 … … … … … … … … … … … … … … … 13 14 15 126 126 126 126 126 126 126 126 126 124 124 124 122 122 122 118 118 118 114 114 114 107 107 107 104 104 104 101 101 101 98.1 98.1 98.1 … … … … … … … … … … … … … … … 16 17 18 19 126 126 126 126 126 126 126 126 126 126 126 126 124 124 124 124 122 122 122 122 118 118 118 118 114 114 114 114 107 107 107 107 104 104 104 104 101 101 101 101 98.1 98.1 98.1 98.1 … … … … … … … … … … … … … … … … … … … … 20 21 22 23 133 138 138 138 133 130 131 130 133 126 125 126 133 124 123 124 133 122 122 122 133 118 118 118 133 114 113 114 129 107 107 107 125 104 104 104 122 101 101 101 119 98.1 98.1 98.1 … … … … … … … … … … … … … … … … … … … … 24 25 26 27 138 138 138 138 130 131 131 131 126 125 125 125 124 123 123 123 122 122 122 122 118 118 118 118 114 113 113 113 107 107 107 107 104 104 104 104 101 101 101 101 98.1 98.1 98.1 98.1 … … … … … … … … … … … … … … … … … … … … 28 29 30 31 32 138 138 138 138 138 138 138 136 136 136 134 134 134 134 134 132 132 132 132 132 130 130 130 130 130 126 126 126 126 126 121 121 121 121 121 115 115 115 115 115 112 112 112 112 112 108 108 108 108 108 105 105 105 105 105 … … … … … … … … … … … … … … … … … … … … … … … … … 33 34 35 138 138 138 136 136 136 134 134 134 132 132 132 130 130 130 126 126 126 121 121 121 115 115 115 112 112 112 108 108 108 105 105 105 … … … … … … … … … … … … … … … 36 37 38 39 40 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 137 137 137 137 137 132 132 132 132 132 126 126 126 126 126 122 122 122 122 122 118 118 118 118 118 115 115 115 115 115 … … … … … … … … … … … … … … … … … … … … … … … … … 41 42 43 44 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 137 137 137 137 132 132 132 132 126 126 126 126 122 122 122 122 118 118 118 118 115 115 115 115 … … … … … … … … … … … … … … … … … … … … 270 INTENTIONALLY LEFT BLANK 271 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Line No. Alloy Designation/ UNS No. Class/ Condition/ Temper P-No. Group No. … … … … … 1 1 1 1 1 1 1 1 1 1 … … … … … … 1 1 1 1 1 1 K02800 K02403 K02800 K02403 K12437 K12437 … … … … 1 … … … … … 64 < t ≤ 100 64 < t ≤ 100 1 1 1 1 1 1 1 1 1 1 2 2 … … WCB K03504 K03502 J03002 … 70 … … … … 1 1 1 2 2 2 SA-266 SA-350 SA-508 SA-508 2 LF2 1 1A K03506 K03011 K13502 K13502 … … … … … … … … 1 1 1 1 2 2 2 2 Forgings Forgings Cast pipe SA-541 SA-541 SA-660 1 1A WCB K03506 K03020 J03003 … … … … … … 1 1 1 2 2 2 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Plate Plate Wld. pipe Wld. pipe Wld. pipe Wld. pipe SA-515 SA-516 SA-671 SA-671 SA-672 SA-672 70 70 CB70 CC70 B70 C70 K03101 K02700 K03101 K02700 K03101 K02700 … … … … … … … … … … … … 1 1 1 1 1 1 2 2 2 2 2 2 31 32 33 34 Carbon steel Carbon steel Carbon steel Carbon steel Smls. pipe Castings Fittings Wld. fittings SA-106 SA-216 SA-234 SA-234 C WCC WPC WPC K03501 K02503 K03501 K03501 … … … W … … … … 1 1 1 1 2 2 2 2 35 36 37 38 39 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Castings Castings Cast pipe Bar Bar SA-352 SA-487 SA-660 SA-695 SA-696 LCC 16 WCC B/40 C J02505 … J02505 K03504 K03200 … A … … … … … … … … 1 1 1 1 1 2 2 2 2 2 40 41 42 43 44 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Plate Plate Wld. pipe Wld. pipe Wld. pipe SA-537 SA-537 SA-671 SA-672 SA-691 … … CD70 D70 CMSH-70 K12437 K12437 K12437 K12437 K12437 2 1 … … … 100 < t ≤ 150 ≤ 64 ≤ 64 ≤ 64 ≤ 64 1 1 1 1 1 3 2 2 2 2 Nominal Composition Product Form Spec No. Type/Grade 1 2 3 4 5 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Bar Bar Forgings Wld. tube Smls. tube SA-695 SA-696 SA-727 SA-178 SA-210 B/35 B … C A-1 K03504 K03200 K02506 K03503 K02707 … … … … … 6 7 8 Carbon steel Carbon steel Carbon steel Castings Plate Plate SA-352 SA-515 SA-516 LCB 65 65 J03003 K02800 K02403 9 10 11 12 13 14 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Wld. pipe Wld. pipe Wld. pipe Wld. pipe Plate Wld. pipe SA-671 SA-671 SA-672 SA-672 SA-537 SA-691 CB65 CC65 B65 C65 … CMSH-70 15 16 17 Carbon steel Carbon steel Carbon steel Forgings Forgings Castings SA-105 SA-181 SA-216 18 19 20 21 Carbon steel Carbon steel Carbon steel Carbon steel Forgings Forgings Forgings Forgings 22 23 24 Carbon steel Carbon steel Carbon steel 25 26 27 28 29 30 272 Size/Thickness, mm 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa 1 2 3 4 5 415 415 415 415 415 240 240 250 255 255 6 7 8 450 450 450 9 10 11 12 13 14 External Pressure Chart No. Notes 371 371 371 (SPT) 371 371 CS-2 CS-2 CS-2 CS-2 CS-2 E2 E2 E2 E2 E2 240 240 240 371 371 371 CS-2 CS-2 CS-2 … … … 450 450 450 450 450 450 240 240 240 240 310 310 371 371 371 371 371 371 CS-2 CS-2 CS-2 CS-2 CS-2 CS-2 G1, G4 G1, G4 G1, G4 G1, G4 E2 E2, G1, G2 15 16 17 485 485 485 250 250 250 371 371 371 CS-2 CS-2 CS-2 … … … 18 19 20 21 485 485 485 485 250 250 250 250 371 371 371 371 CS-2 CS-2 CS-2 CS-2 … … … … 22 23 24 485 485 485 250 250 250 371 371 371 CS-2 CS-2 CS-2 … … … 25 26 27 28 29 30 485 485 485 485 485 485 260 260 260 260 260 260 371 371 371 371 371 371 CS-2 CS-2 CS-2 CS-2 CS-2 CS-2 … … G1, G3 G1, G4 G1, G3 G1, G4 31 32 33 34 485 485 485 485 275 275 275 275 371 371 371 371 CS-2 CS-2 CS-2 CS-2 E2 E2 E2 E2 35 36 37 38 39 485 485 485 485 485 275 275 275 275 275 371 371 371 371 371 CS-2 CS-2 CS-2 CS-2 CS-2 E2 E2 E2 E2 E2 40 41 42 43 44 485 485 485 485 485 315 345 345 345 345 371 371 371 371 371 CS-3 CS-3 CS-3 CS-3 CS-3 E2 E2 E2, G1, G4 E2, G1, G4 E2, G1, G4 Max. Temp. Limit (SPT p Supports Only) 273 #† 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 500 1 2 3 4 5 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 137 137 138 138 138 132 132 136 138 138 126 126 129 133 133 122 122 125 129 129 118 118 122 125 125 115 115 119 122 122 … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 150 150 150 150 150 150 147 147 147 144 144 144 142 142 142 138 138 138 132 132 132 126 126 126 122 122 122 118 118 118 115 115 115 … … … … … … … … … … … … … … … 9 10 11 12 13 14 150 150 150 150 150 150 149 149 149 149 150 150 147 147 147 147 150 150 145 145 145 145 150 150 142 142 142 142 150 150 138 138 138 138 150 150 132 132 132 132 150 150 126 126 126 126 150 150 122 122 122 122 148 148 118 118 118 118 140 140 115 115 115 115 134 134 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 15 16 17 161 161 161 156 156 156 151 151 151 148 148 148 146 146 146 142 142 142 136 136 136 129 129 129 125 125 125 122 122 122 118 118 118 … … … … … … … … … … … … … … … 18 19 20 21 161 161 161 161 156 156 156 156 151 151 151 151 148 148 148 148 146 146 146 146 142 142 142 142 136 136 136 136 129 129 129 129 125 125 125 125 122 122 122 122 118 118 118 118 … … … … … … … … … … … … … … … … … … … … 22 23 24 161 161 161 156 156 156 151 151 151 148 148 148 146 146 146 142 142 142 136 136 136 129 129 129 125 125 125 122 122 122 118 118 118 … … … … … … … … … … … … … … … 25 26 27 28 29 30 161 161 161 161 161 161 161 161 160 160 160 160 160 160 160 160 160 160 157 157 157 157 157 157 154 154 154 154 154 154 149 149 149 149 149 149 143 143 143 143 143 143 136 136 136 136 136 136 132 132 132 132 132 132 129 129 129 129 129 129 124 124 124 124 124 124 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 34 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 158 158 158 158 151 151 151 151 143 143 143 143 139 139 139 139 136 136 136 136 132 132 132 132 … … … … … … … … … … … … … … … … … … … … 35 36 37 38 39 161 161 161 161 161 161 160 161 161 161 161 159 161 161 161 161 155 161 161 161 161 151 161 161 161 158 146 158 158 158 151 142 151 151 151 143 137 143 143 143 139 134 139 139 139 136 131 136 136 136 132 128 132 132 132 … … … … … … … … … … … … … … … … … … … … … … … … … 40 41 42 43 44 161 161 161 161 161 161 161 161 161 161 161 160 160 160 160 161 159 159 159 159 161 157 157 157 157 161 156 156 156 156 161 157 157 157 157 160 156 156 156 156 159 153 153 153 153 153 150 150 150 150 141 147 147 147 147 … … … … … … … … … … … … … … … … … … … … … … … … … 274 INTENTIONALLY LEFT BLANK 275 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Line No. (a) Alloy Designation/ UNS No. Class/ Condition/ Temper P-No. Group No. … > 25 > 25 1 1 1 2 2 2 … … … … 2 … ≤ 25 ≤ 25 ≤ 25 ≤ 25 64 < t ≤ 100 64 < t ≤ 100 1 1 1 1 1 1 2 2 2 2 3 3 K12437 K12437 K12437 K12437 K12007 2 … … … … ≤ 64 ≤ 64 ≤ 64 ≤ 64 … 1 1 1 1 1 3 3 3 3 3 B C K12001 K12202 … … … … 1 1 2 3 SA-234 SA-234 SA-335 SA-369 WP1 WP1 P1 FP1 K12821 K12821 K11522 K11522 … W … … … … … … 3 3 3 3 1 1 1 1 Castings Castings Cast pipe SA-217 SA-352 SA-426 WC1 LC1 CP1 J12524 J12522 J12521 … … … … … … 3 3 3 1 1 1 C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo Plate Wld. pipe Wld. pipe SA-204 SA-672 SA-691 A L65 CM-65 K11820 K11820 K11820 … … … … … … 3 3 3 1 1 1 27 28 29 30 31 C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo Forgings Plate Forgings Wld. pipe Wld. pipe SA-182 SA-204 SA-336 SA-672 SA-691 F1 B F1 L70 CM-70 K12822 K12020 K12520 K12020 K12020 … … … … … … … … … … 3 3 3 3 3 2 2 2 2 2 32 33 34 C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo Plate Wld. pipe Wld. pipe SA-204 SA-672 SA-691 C L75 CM-75 K12320 K12320 K12320 … … … … … … 3 3 3 2 2 2 35 36 37 1 ⁄2Cr – 1⁄5Mo – V ⁄2Cr – 1⁄4Mo – Si 1 ⁄2Cr – 1⁄4Mo – Si Plate Forgings Plate SA-517 SA-592 SA-517 B A A K11630 K11856 K11856 … … … ≤ 32 64 < t ≤ 100 ≤ 32 11B 11B 11B 4 1 1 38 39 40 41 42 43 1 Smls. pipe Forged pipe Plate Wld. pipe Smls. tube Cast pipe SA-335 SA-369 SA-387 SA-691 SA-213 SA-426 P2 FP2 2 1 ⁄2CR T2 CP2 K11547 K11547 K12143 K12143 K11547 J11547 … … 1 … … … … … … … … … 3 3 3 3 3 3 1 1 1 1 1 1 Nominal Composition Product Form 1 2 3 Carbon steel Carbon steel Carbon steel Forgings Plate Wld. pipe SA-266 SA-299 SA-691 3 … CMS-75 K05001 K02803 K02803 … … … 4 5 6 7 8 9 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Plate Wld. pipe Wld. pipe Wld. pipe Plate Wld. pipe SA-299 SA-671 SA-672 SA-691 SA-537 SA-691 … CK75 N75 CMS-75 … CMSH-80 K02803 K02803 K02803 K02803 K12437 K12437 10 11 12 13 14 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Plate Wld. pipe Wld. pipe Wld. pipe Plate SA-537 SA-671 SA-672 SA-691 SA-738 … CD80 D80 CMSH-80 B 15 16 C – Mn – Si – Cb C – Mn – Si – V Plate Plate SA-737 SA-737 17 18 19 20 C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo Fittings Wld. fittings Smls. pipe Forged pipe 21 22 23 C – 1⁄2Mo C – 1⁄2Mo C – 1⁄2Mo 24 25 26 1 ⁄2Cr – 1⁄2Mo ⁄2Cr – 1⁄2Mo 1 ⁄2Cr – 1⁄2Mo 1 ⁄2Cr – 1⁄2Mo 1 ⁄2Cr – 1⁄2Mo 1 ⁄2Cr – 1⁄2Mo 1 Spec No. Type/Grade 276 Size/Thickness, mm 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa 1 2 3 515 515 515 260 275 275 4 5 6 7 8 9 515 515 515 515 515 515 10 11 12 13 14 External Pressure Chart No. Notes 371 371 371 CS-2 CS-2 CS-2 W1 … G1, G4 290 290 290 290 380 380 371 371 371 371 371 371 CS-2 CS-2 CS-2 CS-2 CS-5 CS-5 E2 E2, G1 E2, G1 E2, G1 E2 E2 550 550 550 550 585 415 415 415 415 415 371 371 371 371 350 CS-5 CS-5 CS-5 CS-5 CS-5 E1 E1, G1, G4 E1, G1, G4 E1, G1, G4 … 15 16 485 550 345 415 371 371 CS-3 CS-3 E2 E1 17 18 19 20 380 380 380 380 205 205 205 205 371 371 371 371 CS-2 CS-2 CS-2 CS-2 … … … … 21 22 23 450 450 450 240 240 240 371 371 371 CS-2 CS-2 CS-2 … … … 24 25 26 450 450 450 255 255 255 371 371 371 CS-2 CS-2 CS-2 … G1, G2 G1, G2 27 28 29 30 31 485 485 485 485 485 275 275 275 275 275 371 371 371 371 371 CS-2 CS-2 CS-2 CS-2 CS-2 … … … G1, G2 G1, G2 32 33 34 515 515 515 295 295 295 371 371 371 CS-2 CS-2 CS-2 … G1, G2 G1, G2 35 36 37 795 725 795 690 620 690 371 (SPT) 371 (SPT) 371 (SPT) HT-1 CS-5 HT-1 … … … 38 39 40 41 42 43 380 380 380 380 415 415 205 205 230 230 205 205 371 371 371 371 371 371 CS-2 CS-2 CS-2 CS-2 CS-2 CS-2 … … … G1, G2 … … Max. Temp. Limit (SPT p Supports Only) 277 #† (a) 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (a) Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 500 1 2 3 172 172 172 162 172 170 157 167 168 155 164 165 152 163 163 148 158 158 142 151 151 135 143 143 131 139 139 127 135 135 123 131 131 … … … … … … … … … … … … … … … 4 5 6 7 8 9 172 172 172 172 172 172 172 172 172 172 172 172 172 172 172 172 172 172 172 172 172 172 172 172 171 171 171 171 172 172 165 165 165 165 172 172 159 159 159 159 172 172 151 151 151 151 172 172 147 147 147 147 170 170 142 142 142 142 168 168 139 139 139 139 167 167 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 14 184 184 184 184 195 184 184 184 184 195 184 184 184 184 195 184 184 184 184 195 184 184 184 184 195 184 184 184 184 195 184 184 184 184 195 183 183 183 183 195 182 182 182 182 193 177 177 177 177 190 166 166 166 166 … … … … … … … … … … … … … … … … … … … … … … … … … … 15 16 161 184 161 184 161 184 161 184 161 184 161 184 161 184 157 184 155 183 153 180 152 178 … … … … … … … … … … 17 18 19 20 126 126 126 126 126 126 126 126 126 126 126 126 125 125 125 125 124 124 124 124 120 120 120 120 117 117 117 117 114 114 114 114 112 112 112 112 110 110 110 110 108 108 108 108 … … … … … … … … … … … … … … … … … … … … 21 22 23 150 150 150 150 150 150 149 149 149 147 147 147 145 145 145 140 140 140 137 137 137 133 133 133 131 131 131 128 128 128 127 127 127 … … … … … … … … … … … … … … … 24 25 26 150 150 150 150 150 150 150 150 150 150 150 150 150 150 150 148 148 148 144 144 144 141 141 141 138 138 138 136 136 136 133 133 133 … … … … … … … … … … … … … … … 27 28 29 30 31 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 160 160 160 160 160 156 156 156 156 156 152 152 152 152 152 149 149 149 149 149 147 147 147 147 147 144 144 144 144 144 … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 172 172 172 172 172 172 172 172 172 172 172 172 172 172 172 172 172 172 168 168 168 163 163 163 160 160 160 158 158 158 155 155 155 … … … … … … … … … … … … … … … 35 36 37 264 241 264 264 241 264 264 241 264 264 241 264 264 241 264 264 241 264 264 241 264 264 240 264 264 239 264 263 233 263 258 228 258 … … … … … … … … … … … … … … … 38 39 40 41 42 43 126 126 126 126 138 138 126 126 126 126 134 134 126 126 126 126 129 129 125 125 126 126 126 126 124 124 126 126 124 124 120 120 126 126 120 120 117 117 126 126 117 117 114 114 125 125 114 114 112 112 123 123 112 112 110 110 121 121 110 110 108 108 119 119 108 108 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 278 INTENTIONALLY LEFT BLANK 279 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Line No. Alloy Designation/ UNS No. Class/ Condition/ Temper P-No. Group No. … … … 4 4 4 1 1 1 … 1 … … … … … … 4 4 4 4 1 1 1 1 K11757 K11757 K11564 K11564 2 42 2 … … … … … 4 4 4 4 1 1 1 1 WC6 CP11 B11 J12072 J12072 K11797 … … … … … … 4 4 4 1 1 1 SA-213 SA-234 SA-234 T11 WP11 WP11 K11597 … … … 1 1/W … … … 4 4 4 1 1 1 Smls. pipe Forged pipe Plate Wld. pipe SA-335 SA-369 SA-387 SA-691 P11 FP11 11 11⁄4CR K11597 K11597 K11789 K11789 … … 1 … … … … … 4 4 4 4 1 1 1 1 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si Forgings Plate Wld. pipe SA-182 SA-387 SA-691 F11 11 11⁄4CR K11572 K11789 K11789 2 2 … … … … 4 4 4 1 1 1 25 26 27 13⁄4Cr – 1⁄2Mo – Cu 13⁄4Cr – 1⁄2Mo – Ti 13⁄4Cr – 1⁄2Mo – Ti Forgings Plate Plate SA-592 SA-517 SA-517 E E E K11695 K21604 K21604 … … … 64 < t ≤ 100 64 < t ≤ 150 ≤ 64 11B 11B 11B 2 2 2 28 29 30 31 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo Forgings Smls. tube Fittings Wld. fittings SA-182 SA-213 SA-234 SA-234 F22 T22 WP22 WP22 K21590 K21590 K21590 K21590 1 … 1 1/W … … … … 5A 5A 5A 5A 1 1 1 1 32 33 34 35 36 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo Smls. pipe Forgings Forged pipe Plate Wld. pipe SA-335 SA-336 SA-369 SA-387 SA-691 P22 F22 FP22 22 21⁄4CR K21590 K21590 K21590 K21590 K21590 … 1 … 1 … … … … … … 5A 5A 5A 5A 5A 1 1 1 1 1 37 38 39 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo Castings Castings Cast pipe SA-217 SA-217 SA-426 WC9 WC9 CP22 J21890 J21890 J21890 … … … … … … 5A 5A 5A 1 1 1 Nominal Composition Product Form Spec No. Type/Grade 1 2 3 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo Plate Wld. pipe Cast pipe SA-387 SA-691 SA-426 12 1CR CP12 K11757 K11757 J11562 1 22 … 4 5 6 7 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo Smls. tube Fittings Smls. pipe Forged pipe SA-213 SA-234 SA-335 SA-369 T12 WP12 P12 FP12 K11562 K12062 K11562 K11562 8 9 10 11 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo 1Cr – 1⁄2Mo Plate Wld. pipe Forgings Forgings SA-387 SA-691 SA-182 SA-336 12 1CR F12 F12 12 13 14 11⁄4Cr – 1⁄2Mo 11⁄4Cr – 1⁄2Mo 11⁄4Cr – 1⁄2Mo Castings Cast pipe Bar SA-217 SA-426 SA-739 15 16 17 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si Smls. tube Fittings Wld. fittings 18 19 20 21 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si 11⁄4Cr – 1⁄2Mo – Si 22 23 24 280 Size/Thickness, mm 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa 1 2 3 380 380 415 230 230 205 4 5 6 7 415 415 415 415 8 9 10 11 External Pressure Chart No. Notes 371 371 371 CS-2 CS-2 CS-2 … G15 … 220 220 220 220 371 371 371 371 CS-2 CS-2 CS-2 CS-2 … … … … 450 450 485 485 275 275 275 275 371 371 371 371 CS-2 CS-2 CS-2 CS-2 … G16, H2 … … 12 13 14 485 485 485 275 275 310 371 371 371 CS-2 CS-2 CS-3 … … … 15 16 17 415 415 415 205 205 205 371 371 371 CS-2 CS-2 CS-2 … … … 18 19 20 21 415 415 415 415 205 205 240 240 371 371 371 371 CS-2 CS-2 CS-2 CS-2 … … … G1, G2 22 23 24 485 515 515 275 310 310 371 371 371 CS-2 CS-3 CS-3 … … G1, G2, H2 25 26 27 725 725 795 620 620 690 371 (SPT) 371 (SPT) 371 (SPT) CS-5 CS-5 HT-1 S1 … … 28 29 30 31 415 415 415 415 205 205 205 205 371 371 371 371 CS-2 CS-2 CS-2 CS-2 … W2 W2 … 32 33 34 35 36 415 415 415 415 415 205 205 205 205 205 371 371 371 371 371 CS-2 CS-2 CS-2 CS-2 CS-2 W2 W2 W2 H1, W2 G1, G2 37 38 39 485 485 485 275 275 275 371 371 (SPT) 371 CS-2 CS-2 CS-2 W2 … … Max. Temp. Limit (SPT p Supports Only) 281 #† 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 500 1 2 3 126 126 138 125 125 131 124 124 124 122 122 120 121 121 117 121 121 112 119 119 109 117 117 106 115 115 104 113 113 103 112 112 102 … … … … … … … … … … … … … … … 4 5 6 7 138 138 138 138 136 136 136 136 132 132 132 132 128 128 128 128 125 125 125 125 120 120 120 120 116 116 116 116 113 113 113 113 112 112 112 112 110 110 110 110 109 109 109 109 … … … … … … … … … … … … … … … … … … … … 8 9 10 11 150 150 161 161 150 148 159 161 146 146 158 157 144 144 156 156 143 143 154 154 143 143 150 150 143 143 145 145 141 141 141 141 139 139 139 139 137 137 137 137 136 136 136 136 … … … … … … … … … … … … … … … … … … … … 12 13 14 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 156 156 161 151 151 161 146 146 161 143 143 160 141 141 159 138 138 155 … … … … … … … … … … … … … … … 15 16 17 138 138 138 132 132 132 127 127 127 124 124 124 121 121 121 116 116 116 112 112 112 109 109 109 108 108 108 106 106 106 104 104 104 … … … … … … … … … … … … … … … 18 19 20 21 138 138 138 138 132 132 138 138 127 127 138 138 124 124 138 138 121 121 138 138 116 116 135 135 112 112 131 131 109 109 127 127 108 108 126 126 106 106 123 123 104 104 121 121 … … … … … … … … … … … … … … … … … … … … 22 23 24 161 172 172 161 172 172 161 172 172 161 172 172 161 172 172 156 172 172 151 169 169 146 164 164 143 161 161 141 158 158 138 155 155 … … … … … … … … … … … … … … … 25 26 27 241 241 264 241 241 264 241 241 264 241 241 264 241 241 264 241 241 264 241 241 264 241 241 264 241 241 264 241 241 264 241 241 263 … … … … … … … … … … … … … … … 28 29 30 31 138 138 138 138 133 133 132 132 128 128 128 128 126 126 127 127 125 125 125 125 124 124 124 124 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 138 138 138 138 138 132 132 132 133 133 128 128 128 128 128 127 127 127 126 126 125 125 125 125 125 124 124 124 124 124 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 … … … … … … … … … … … … … … … … … … … … … … … … … 37 38 39 161 161 161 161 161 161 161 161 161 160 160 160 159 159 159 156 156 156 155 155 155 155 155 155 154 154 154 153 153 153 151 151 151 … … … … … … … … … … … … … … … 282 INTENTIONALLY LEFT BLANK 283 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Line No. Alloy Designation/ UNS No. Class/ Condition/ Temper P-No. Group No. … … … … … 5A 5A 5A 5A 5A 1 1 1 1 1 A 3 4 … … ≥6 5C 5C 5C 1 1 4 K31545 K31545 K31545 K31545 K31545 J31545 … … 1 … 1 … … … … … … … 5A 5A 5A 5A 5A 5A 1 1 1 1 1 1 F21 F21 21 K31545 K31545 K31545 … 3 2 … … … 5A 5A 5A 1 1 1 SA-213 SA-234 SA-234 T5 WP5 WP5 K41545 K41545 K41545 … … W … … … 5B 5B 5B 1 1 1 Smls. pipe Forged pipe Plate Wld. pipe SA-335 SA-369 SA-387 SA-691 P5 FP5 5 5CR K41545 K41545 K41545 K41545 … … 1 … … … … … 5B 5B 5B 5B 1 1 1 1 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo Forgings Plate Castings Cast pipe SA-182 SA-387 SA-217 SA-426 F5 5 C5 CP5 K41545 K41545 J42045 J42045 … 2 … … … … … … 5B 5B 5B 5B 1 1 1 1 29 30 31 32 33 9Cr – 1Mo 9Cr – 1Mo 9Cr – 1Mo 9Cr – 1Mo 9Cr – 1Mo Smls. tube Smls. pipe Forged pipe Castings Cast pipe SA-213 SA-335 SA-369 SA-217 SA-426 T9 P9 FP9 C12 CP9 K90941 K90941 K90941 J82090 J82090 … … … … … … … … … … 5B 5B 5B 5B 5B 1 1 1 1 1 34 35 36 37 9Cr – 1Mo – V 9Cr – 1Mo – V 9Cr – 1Mo – V 9Cr – 1Mo – V Forgings Smls. tube Smls. pipe Plate SA-182 SA-213 SA-335 SA-387 F91 T91 P91 91 K90901 K90901 K90901 K90901 … … … 2 … … … … 15E 15E 15E 15E 1 1 1 1 38 39 40 41 42 43 12Cr 12Cr 12Cr – Al 12Cr – Al 12Cr – Al 121⁄2Cr – 2Ni Bar Bar Bar Plate Bar Bar SA-479 SA-479 SA/JIS G4303 SA-240 SA-479 SA-479 403 403 SUS405 405 405 414 S40300 S40300 … S40500 S40500 S41400 A 1 … … … … … … … … … … 6 6 7 7 7 6 1 1 1 1 1 4 Nominal Composition Product Form Spec No. Type/Grade 1 2 3 4 5 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo Forgings Forgings Plate Wld. pipe Bar SA-182 SA-336 SA-387 SA-691 SA-739 F22 F22 22 21⁄4CR B22 K21590 K21590 K21590 K21590 K21390 3 3 2 … … 6 7 8 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo 21⁄4Cr – 1Mo Castings Forgings Forgings SA-487 SA-508 SA-541 8 22 22 J22091 K21590 K21390 9 10 11 12 13 14 3Cr – 1Mo 3Cr – 1Mo 3Cr – 1Mo 3Cr – 1Mo 3Cr – 1Mo 3Cr – 1Mo Smls. tube Smls. pipe Forgings Forged pipe Plate Cast pipe SA-213 SA-335 SA-336 SA-369 SA-387 SA-426 T21 P21 F21 FP21 21 CP21 15 16 17 3Cr – 1Mo 3Cr – 1Mo 3Cr – 1Mo Forgings Forgings Plate SA-182 SA-336 SA-387 18 19 20 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo Smls. tube Fittings Wld. fittings 21 22 23 24 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo 5Cr – 1⁄2Mo 25 26 27 28 284 Size/Thickness, mm 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa 1 2 3 4 5 515 515 515 515 515 310 310 310 310 310 6 7 8 585 585 725 9 10 11 12 13 14 External Pressure Chart No. Notes 371 371 371 371 371 CS-3 CS-3 CS-3 CS-3 CS-3 W2 W2 W2 G1, G2, H2 W2 380 380 585 371 371 371 CS-3 CS-2 CS-3 … … S3, W1 415 415 415 415 415 415 205 205 205 205 205 205 371 371 371 371 371 371 CS-2 CS-2 CS-2 CS-2 CS-2 CS-2 … … … … … … 15 16 17 515 515 515 310 310 310 371 371 371 CS-3 CS-3 CS-3 … … … 18 19 20 415 415 415 205 205 205 371 371 371 CS-2 CS-2 CS-2 … … … 21 22 23 24 415 415 415 415 205 205 205 205 371 371 371 371 CS-2 CS-2 CS-2 CS-2 … … … G1, G2 25 26 27 28 485 515 620 620 275 310 415 415 371 371 371 371 CS-2 CS-3 CS-3 CS-3 … … H2 … 29 30 31 32 33 415 415 415 620 620 205 205 205 415 415 371 371 371 371 (SPT) 371 CS-2 CS-2 CS-2 CS-3 CS-3 … … … H2 … 34 35 36 37 585 585 585 585 415 415 415 415 371 371 371 371 CS-3 CS-3 CS-3 CS-3 … … … … 38 39 40 41 42 43 485 485 410 415 415 795 275 275 174 170 170 620 371 371 371 371 371 371 … … CS-1 CS-1 CS-1 CS-3 … … G13 G13 G13 … Max. Temp. Limit (SPT p Supports Only) 285 #† 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 500 1 2 3 4 5 172 172 172 172 172 172 172 172 172 172 172 172 172 172 172 170 170 170 170 170 167 167 167 167 167 166 166 166 166 166 166 166 166 166 166 165 165 165 165 165 164 164 164 164 164 162 162 162 162 162 161 161 161 161 161 … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 195 195 241 195 195 241 195 195 241 193 193 241 191 191 241 189 189 241 189 189 240 188 188 238 187 187 236 186 186 234 184 184 231 … … … … … … … … … … … … … … … 9 10 11 12 13 14 138 138 138 138 138 138 133 133 132 133 133 133 128 128 128 128 128 128 126 126 127 126 126 126 125 125 125 125 125 125 124 124 124 124 124 124 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 123 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 15 16 17 172 172 172 172 172 172 172 172 172 170 170 170 167 167 167 166 166 166 166 166 166 165 165 165 164 164 164 162 162 162 161 161 161 … … … … … … … … … … … … … … … 18 19 20 138 138 138 131 131 131 124 124 124 121 121 121 120 120 120 119 119 119 118 118 118 117 117 117 115 115 115 114 114 114 112 112 112 … … … … … … … … … … … … … … … 21 22 23 24 138 138 138 138 131 131 131 131 124 124 124 124 121 121 121 121 120 120 120 120 119 119 119 119 118 118 118 118 117 117 117 117 115 115 115 115 114 114 114 114 112 112 112 112 … … … … … … … … … … … … … … … … … … … … 25 26 27 28 161 172 207 207 161 172 206 206 160 171 206 206 158 169 203 203 156 167 201 201 154 165 199 199 154 165 198 198 153 164 196 196 151 162 194 194 149 159 191 191 146 156 188 188 … … … … … … … … … … … … … … … … … … … … 29 30 31 32 33 138 138 138 207 207 131 131 131 206 206 124 124 124 206 206 121 121 121 203 203 120 120 120 201 201 119 119 119 199 199 118 118 118 198 198 117 117 117 196 196 115 115 115 194 194 114 114 114 191 191 112 112 112 188 188 … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 37 195 195 195 195 195 195 195 195 195 195 195 195 195 195 195 195 195 195 195 195 194 194 194 194 194 194 194 194 192 192 192 192 190 190 190 190 187 187 187 187 183 183 183 183 … … … … … … … … … … … … … … … … … … … … 38 39 40 41 42 43 161 161 115 115 115 264 161 161 110 110 110 264 160 160 105 105 105 264 159 159 103 103 103 262 158 158 102 102 102 260 155 155 100 100 100 254 153 153 98.9 98.9 98.9 249 150 150 97.2 97.2 97.2 244 148 148 96.1 96.1 96.1 241 145 145 94.7 94.7 94.7 237 141 141 92.7 92.7 92.7 232 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 286 INTENTIONALLY LEFT BLANK 287 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Line No. Alloy Designation/ UNS No. Class/ Condition/ Temper P-No. Group No. … … … … 7 6 6 6 1 1 1 1 2 … … … … … 6 6 6 3 3 3 J91540 S41500 S13800 A … … … … … 6 6 … 4 4 … 630 630 630 S17400 S17400 S17400 H1150 H1150 H1150 … … … … … … … … … SA-564 SA-693 SA-705 630 630 630 S17400 S17400 S17400 H1100 H1100 H1100 … … … … … … … … … Bar Plate Forgings SA-564 SA-693 SA-705 630 630 630 S17400 S17400 S17400 H1075 H1075 H1075 … … … … … … … … … 27Cr – 1Mo 27Cr – 1Mo 27Cr – 1Mo Plate Smls. & wld. tube Bar SA-240 SA-268 SA-479 XM-27 TPXM-27 XM-27 S44627 S44627 S44627 … … … … … … 10I 10I 10I 1 1 1 23 24 25 26 27 Mn – 1⁄4Mo – V Mn – 1⁄2Mo Mn – 1⁄2Mo Mn – 1⁄2Mo Mn – 1⁄2Mo Castings Plate Wld. pipe Plate Plate SA-487 SA-302 SA-672 SA-302 SA-533 2 A H75 B A J13005 K12021 K12021 K12022 K12521 A … … … 1 … … … … … 3 3 3 3 3 3 2 2 3 3 28 29 30 Mn – 1⁄2Mo Mn – 1⁄2Mo Mn – 1⁄2Mo Wld. pipe Plate Plate SA-672 SA-533 SA-533 H80 A A K12022 K12521 K12521 … 2 3 … … … 3 3 11A 3 3 4 31 32 33 Mn – 1⁄2Mo – 1⁄4Ni Mn – 1⁄2Mo – 1⁄4Ni Mn – 1⁄2Mo – 1⁄4Ni Plate Plate Plate SA-533 SA-533 SA-533 D D D K12529 K12529 K12529 1 2 3 … … … 3 3 11A 3 3 4 34 35 36 Mn – 1⁄2Mo – 1⁄2Ni Mn – 1⁄2Mo – 1⁄2Ni Mn – 1⁄2Mo – 1⁄2Ni Plate Plate Wld. pipe SA-302 SA-533 SA-672 C B J80 K12039 K12539 K12539 … 1 … … … … 3 3 3 3 3 3 37 38 39 40 Mn – 1⁄2Mo – 1⁄2Ni Mn – 1⁄2Mo – 1⁄2Ni Mn – 1⁄2Mo – 1⁄2Ni Mn – 1⁄2Mo – 1⁄2Ni Plate Wld. pipe Plate Wld. pipe SA-533 SA-672 SA-533 SA-672 B J90 B J100 K12539 K12539 K12539 K12539 2 … 3 … … … … … 3 3 11A 11A 3 3 4 4 Nominal Composition Product Form Spec No. Type/Grade 1 2 3 4 13Cr 13Cr 13Cr 13Cr Plate Forgings Bar Bar SA-240 SA-182 SA-479 SA-479 410S F6a 410 410 S41008 S41000 S41000 S41000 … 1 A 1 5 6 7 13Cr 13Cr 13Cr Forgings Castings Cast pipe SA-182 SA-217 SA-426 F6a CA15 CPCA15 S41000 J91150 J91150 8 9 10 13Cr – 4Ni 13Cr – 4Ni 13Cr – 8Ni – 2Mo Castings Forgings Forgings SA-487 SA-182 SA-705 CA6NM F6NM XM-13 (a) (a) (a) 11 12 13 17Cr – 4Ni – 4Cu 17Cr – 4Ni – 4Cu 17Cr – 4Ni – 4Cu Forgings, bar Plate Forgings SA-564 SA-693 SA-705 (a) (a) (a) 14 15 16 17Cr – 4Ni – 4Cu 17Cr – 4Ni – 4Cu 17Cr – 4Ni – 4Cu Bar Plate Forgings (a) (a) (a) 17 18 19 17Cr – 4Ni – 4Cu 17Cr – 4Ni – 4Cu 17Cr – 4Ni – 4Cu 20 21 22 288 Size/Thickness, mm 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa 1 2 3 4 415 485 485 485 205 275 275 275 5 6 7 585 620 620 8 9 10 #† External Pressure Chart No. Notes 371 371 371 371 CS-2 CS-2 CS-2 CS-2 … … … … 380 450 450 371 371 371 CS-3 CS-5 CS-5 … … … 760 795 1035 550 620 930 371 371 316 CS-5 CS-3 HA-7 … … W1 11 12 13 930 930 930 725 725 725 343 343 343 HT-1 HT-1 HT-1 G8, W1 G8, W1 G8, W1 (a) (a) (a) 14 15 16 965 965 965 795 795 795 343 343 343 HT-1 HT-1 HT-1 G8, W1 G8, W1 G8, W1 (a) (a) (a) 17 18 19 1000 1000 1000 860 860 860 343 343 343 HT-1 HT-1 HT-1 G8, W1 G8, W1 G8, W1 (a) (a) (a) 20 21 22 450 450 450 275 275 275 343 343 343 HA-2 HA-2 HA-2 G13 G13 G13 23 24 25 26 27 585 515 515 550 550 365 310 310 345 345 371 (SPT) 371 371 371 371 CS-3 CS-3 CS-3 CS-3 CS-5 … … G1, G2 … … 28 29 30 550 620 690 345 485 570 371 371 371 CS-3 CS-5 CS-5 G1, G2 … … 31 32 33 550 620 690 345 485 570 371 371 371 CS-5 CS-5 CS-5 … … … 34 35 36 550 550 550 345 345 345 371 371 371 CS-3 CS-5 CS-5 … … G1, G2 37 38 39 40 620 620 690 690 485 485 570 570 371 371 371 371 CS-5 CS-5 CS-5 CS-5 … G1, G2 … G1, G2 Max. Temp. Limit (SPT p Supports Only) 289 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 500 1 2 3 4 138 161 161 161 132 161 161 161 126 160 160 160 124 159 159 159 123 158 158 158 120 155 155 155 119 153 153 153 117 150 150 150 115 148 148 148 114 145 145 145 111 141 141 141 … … … … … … … … … … … … … … … … … … … … 5 6 7 195 207 207 195 207 207 195 207 207 194 205 205 192 203 203 188 199 199 186 197 197 182 193 193 180 190 190 176 186 186 172 182 182 … … … … … … … … … … … … … … … 8 9 10 253 264 345 253 264 345 253 264 345 250 264 345 248 264 345 242 262 341 238 254 331 233 244 319 231 240 313 227 235 … 224 229 … … … … … … … … … … … … … … … … (a) (a) (a) 11 12 13 310 310 310 310 310 310 310 310 310 310 310 310 310 310 310 302 302 302 296 296 296 292 292 292 290 290 290 288 288 288 … … … … … … … … … … … … … … … … … … (a) (a) (a) 14 15 16 322 322 322 322 322 322 322 322 322 322 322 322 322 322 322 314 314 314 308 308 308 303 303 303 301 301 301 299 299 299 … … … … … … … … … … … … … … … … … … (a) (a) (a) 17 18 19 333 333 333 333 333 333 333 333 333 333 333 333 333 333 333 325 325 325 319 319 319 314 314 314 312 312 312 309 309 309 … … … … … … … … … … … … … … … … … … 20 21 22 150 150 150 150 150 150 149 149 149 147 147 147 144 144 144 135 135 135 131 131 131 129 129 129 129 129 129 128 128 128 … … … … … … … … … … … … … … … … … … 23 24 25 26 27 195 172 172 184 184 195 172 172 184 184 195 172 172 184 184 195 172 172 184 184 195 172 172 184 184 194 172 172 184 184 194 172 172 184 184 190 172 172 184 184 187 172 172 184 184 185 171 171 184 184 182 168 168 184 184 … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 184 207 230 184 207 230 184 207 230 184 207 230 184 207 230 184 207 230 184 207 230 184 207 230 184 207 230 184 207 230 184 207 230 … … … … … … … … … … … … … … … 31 32 33 184 207 230 184 207 230 184 207 230 184 207 230 184 207 230 184 207 230 184 207 230 184 207 230 184 207 230 184 207 230 184 207 230 … … … … … … … … … … … … … … … 34 35 36 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 184 … … … … … … … … … … … … … … … 37 38 39 40 207 207 230 230 207 207 230 230 207 207 230 230 207 207 230 230 207 207 230 230 207 207 230 230 207 207 230 230 207 207 230 230 207 207 230 230 207 207 230 230 207 207 230 230 … … … … … … … … … … … … … … … … … … … … 290 INTENTIONALLY LEFT BLANK 291 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Line No. Alloy Designation/ UNS No. Class/ Condition/ Temper P-No. Group No. … … … … … 3 3 3 11A 10A 3 3 3 4 1 A 1 2 … … … 3 3 3 3 3 3 K11576 K11576 … … 64 < t ≤ 100 ≤ 64 11B 11B 3 3 2 2 2 2 K12766 K12765 K12766 K12765 1 1 2 2 … … … … 3 3 3 3 3 3 3 3 SA-508 SA-508 SA-217 3 3 WC5 K12042 K12042 J22000 1 2 … … … … 3 3 4 3 3 1 Castings Plate Plate SA-217 SA-517 SA-517 WC4 P P J12082 K21650 K21650 … … … … 64 < t ≤ 100 ≤ 64 4 11B 11B 1 8 8 2Ni – 11⁄2Cr – 1⁄4Mo – V 2Ni – 11⁄2Cr – 1⁄4Mo – V 2Ni – 11⁄2Cr – 1⁄4Mo – V 2Ni – 11⁄2Cr – 1⁄4Mo – V 2Ni – 11⁄2Cr – 1⁄4Mo – V Forgings Forgings Forgings Forgings Forgings SA-723 SA-723 SA-723 SA-723 SA-723 1 1 1 1 1 K23550 K23550 K23550 K23550 K23550 1 2 3 4 5 … … … … … … … … … … … … … … … 26 27 28 29 30 31 21⁄2Ni 23⁄4Ni – 11⁄2Cr – 1⁄2Mo – V 23⁄4Ni – 11⁄2Cr – 1⁄2Mo – V 23⁄4Ni – 11⁄2Cr – 1⁄2Mo – V 23⁄4Ni – 11⁄2Cr – 1⁄2Mo – V 23⁄4Ni – 11⁄2Cr – 1⁄2Mo – V Castings Forgings Forgings Forgings Forgings Forgings SA-352 SA-723 SA-723 SA-723 SA-723 SA-723 LC2 2 2 2 2 2 J22500 K34035 K34035 K34035 K34035 K34035 … 1 2 3 4 5 … … … … … … 9A … … … … … 1 … … … … … 32 33 34 35 36 3Ni – 13⁄4Cr – 1⁄2Mo 31⁄2Ni 31⁄2Ni 31⁄2Ni 31⁄2Ni Plate Forgings Plate Plate Castings SA-543 SA-350 SA-203 SA-203 SA-352 B LF3 E E LC3 K42339 K32025 K32018 K32018 J31550 1 … … … … … … … … … 11A 9B 9B 9B 9B 5 1 1 1 1 37 38 31⁄2Ni – 13⁄4Cr – 1⁄2Mo – V 31⁄2Ni – 13⁄4Cr – 1⁄2Mo – V Forgings Forgings SA-508 SA-508 4N 4N K22375 K22375 3 1 … … 3 11A 3 5 39 40 41 42 43 44 4Ni – 11⁄2Cr – 1⁄2Mo – V 4Ni – 11⁄2Cr – 1⁄2Mo – V 4Ni – 11⁄2Cr – 1⁄2Mo – V 4Ni – 11⁄2Cr – 1⁄2Mo – V 4Ni – 11⁄2Cr – 1⁄2Mo – V 25Ni – 15Cr – 2Ti Forgings Forgings Forgings Forgings Forgings Forgings, bar SA-723 SA-723 SA-723 SA-723 SA-723 SA-638 3 3 3 3 3 660 K44045 K44045 K44045 K44045 K44045 S66286 1 2 3 4 5 … … … … … … … … … … … … … … … … … … … Nominal Composition Product Form 1 2 3 4 5 Mn – 1⁄2Mo – 3⁄4Ni Mn – 1⁄2Mo – 3⁄4Ni Mn – 1⁄2Mo – 3⁄4Ni Mn – 1⁄2Mo – 3⁄4Ni Mn – V Plate Plate Plate Plate Castings SA-302 SA-533 SA-533 SA-533 SA-487 D C C C 1 K12054 K12554 K12554 K12554 J13002 … 1 2 3 A 6 7 8 1 ⁄2Ni – 1⁄2Cr – 1⁄4Mo – V ⁄2Ni – 1⁄2Mo – V 1 ⁄2Ni – 1⁄2Mo – V Castings Forgings Forgings SA-487 SA-541 SA-541 4 3 3 J13047 K12045 K12045 9 10 3 Forgings Plate SA-592 SA-517 F F 11 12 13 14 3 ⁄4Ni – 1⁄2Mo – 1⁄3Cr – V ⁄4Ni – 1⁄2Mo – 1⁄3Cr – V 3 ⁄4Ni – 1⁄2Mo – 1⁄3Cr – V 3 ⁄4Ni – 1⁄2Mo – 1⁄3Cr – V Forgings Forgings Forgings Forgings SA-508 SA-541 SA-508 SA-541 15 16 17 3 3 ⁄4Ni – 1⁄2Mo – Cr – V ⁄4Ni – 1⁄2Mo – Cr – V 3 ⁄4Ni – 1Mo – 3⁄4Cr Forgings Forgings Castings 18 19 20 1Ni – 1⁄2Cr – 1⁄2Mo 11⁄4Ni – 1Cr – 1⁄2Mo 11⁄4Ni – 1Cr – 1⁄2Mo 21 22 23 24 25 1 ⁄4Ni – 1⁄2Cr – 1⁄2Mo – V ⁄4Ni – 1⁄2Cr – 1⁄2Mo – V 3 3 Spec No. Type/Grade 292 Size/Thickness, mm 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa 1 2 3 4 5 550 550 620 690 585 345 345 485 570 380 6 7 8 620 550 620 9 10 External Pressure Chart No. Notes 371 371 371 371 371 (SPT) CS-3 CS-5 CS-5 CS-5 CS-3 … … … … H2 415 345 450 371 371 371 CS-3 CS-5 CS-5 H2 … … 725 795 620 690 371 (SPT) 371 (SPT) CS-5 HT-1 S1 … 11 12 13 14 550 550 620 620 345 345 450 450 371 371 371 371 CS-5 CS-5 CS-5 CS-5 … … … … 15 16 17 550 620 485 345 450 275 371 371 371 CS-5 CS-5 CS-2 … … … 18 19 20 485 725 795 275 620 690 371 (SPT) 371 (SPT) 371 (SPT) CS-2 CS-5 HT-1 … … … 21 22 23 24 25 795 930 1070 1205 1310 690 825 965 1105 1240 371 (SPT) 371 (SPT) 371 (SPT) 371 (SPT) 371 (SPT) HT-1 HT-1 HT-1 HT-1 HT-1 G14, W1 G6, W1 W1 W1 W1 26 27 28 29 30 31 485 795 930 1070 1205 1310 275 690 825 965 1105 1240 38 371 (SPT) 371 (SPT) 371 (SPT) 371 (SPT) 371 (SPT) CS-2 HT-1 HT-1 HT-1 HT-1 HT-1 … G14, W1 G6, W1 W1 W1 W1 32 33 34 35 36 725 485 485 485 485 585 260 275 275 275 343 371 149 (SPT) 260 38 CS-5 CS-2 CS-2 CS-2 CS-2 G5, H3, S4, W3 … … … … 37 38 620 725 485 585 343 343 CS-5 CS-5 … H3, S4, W3 39 40 41 42 43 44 795 930 1070 1205 1310 895 690 825 965 1105 1240 585 371 (SPT) 371 (SPT) 371 (SPT) 371 (SPT) 371 (SPT) 371 HT-1 HT-1 HT-1 HT-1 HT-1 HA-5 G14, W1 G6, W1 W1 W1 W1 W1 Max. Temp. Limit (SPT p Supports Only) 293 #† 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 500 1 2 3 4 5 184 184 207 230 196 184 184 207 230 190 184 184 207 230 184 184 184 207 230 181 184 184 207 230 180 184 184 207 230 180 184 184 207 230 180 184 184 207 230 178 184 184 207 230 175 184 184 207 230 172 184 184 207 230 168 … … … … … … … … … … … … … … … … … … … … … … … … … 6 7 8 207 184 207 207 184 207 207 184 207 207 184 207 207 184 207 207 184 207 207 184 207 207 184 207 207 184 207 207 184 207 207 184 207 … … … … … … … … … … … … … … … 9 10 241 264 241 264 241 264 241 264 241 264 241 264 241 264 241 264 241 264 240 263 236 258 … … … … … … … … … … 11 12 13 14 184 184 207 207 184 184 207 207 184 184 207 207 184 184 207 207 184 184 207 207 184 184 207 207 184 184 207 207 184 184 207 207 184 184 207 207 184 184 207 207 184 184 207 207 … … … … … … … … … … … … … … … … … … … … 15 16 17 184 207 161 184 207 161 184 207 161 184 207 161 184 207 161 184 207 161 184 207 159 184 207 156 184 207 154 184 207 152 184 207 149 … … … … … … … … … … … … … … … 18 19 20 161 241 264 161 241 264 161 241 264 161 241 264 161 241 264 161 241 264 159 241 264 156 241 264 154 241 264 152 240 263 149 236 258 … … … … … … … … … … … … … … … 21 22 23 24 25 264 310 356 402 436 264 310 356 402 436 264 310 356 402 436 264 310 356 402 436 264 310 356 402 436 264 310 356 402 436 264 310 356 402 436 264 310 356 402 436 263 309 355 401 435 259 304 349 394 428 253 297 341 386 418 … … … … … … … … … … … … … … … … … … … … … … … … … 26 27 28 29 30 31 161 264 310 356 402 436 … 264 310 356 402 436 … 264 310 356 402 436 … 264 310 356 402 436 … 264 310 356 402 436 … 264 310 356 402 436 … 264 310 356 402 436 … 264 310 356 402 436 … 263 309 355 401 435 … 259 304 349 394 428 … 253 297 341 386 418 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 241 161 161 161 161 241 160 161 161 … 241 157 161 161 … 241 155 161 161 … 241 152 161 161 … 239 148 … 158 … 237 142 … 151 … 236 133 … … … 233 128 … … … 230 122 … … … … 116 … … … … … … … … … … … … … … … … … … … … … … … … … … … … 37 38 207 241 207 241 207 241 207 241 207 241 205 239 204 237 202 236 200 233 197 230 … … … … … … … … … … … … 39 40 41 42 43 44 264 310 356 402 436 299 264 310 356 402 436 299 264 310 356 402 436 299 264 310 356 402 436 299 264 310 356 402 436 299 264 310 356 402 436 299 264 310 356 402 436 294 264 310 356 402 436 289 263 309 355 401 435 287 259 304 349 394 428 284 253 297 341 386 418 282 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 294 INTENTIONALLY LEFT BLANK 295 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Line No. Alloy Designation/ UNS No. Class/ Condition/ Temper P-No. Group No. > 125 … … 8 8 8 1 1 1 … … … … ≤ 125 … … … 8 8 8 8 1 1 1 1 S31603 S31603 S31603 S31603 … … … WP-W … … … … 8 8 8 8 1 1 1 1 316L TP316L TP316L TP316L S31603 S31603 S31603 S31603 … … … … … … … … 8 8 8 8 1 1 1 1 SA-351 SA-451 SA-351 SA-451 CF3M CPF3M CF8M CPF8M J92800 J92800 J92900 J92900 … … … … … … … … 8 8 8 8 1 1 1 1 Forgings Forgings Forgings Forgings SA-182 SA-965 SA-182 SA-965 F316 F316 F316H F316H S31600 S31600 S31609 S31609 … … … … > 125 … > 125 … 8 8 8 8 1 1 1 1 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Forgings Smls. tube Plate Wld. tube SA-182 SA-213 SA-240 SA-249 F316 TP316 316 TP316 S31600 S31600 S31600 S31600 … … … … ≤ 125 … … … 8 8 8 8 1 1 1 1 28 29 30 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Smls. & wld. pipe Wld. pipe Smls. pipe SA-312 SA-358 SA-376 TP316 316 TP316 S31600 S31600 S31600 … 1 … … … … 8 8 8 1 1 1 31 32 33 34 35 36 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Fittings Wld. fittings Bar Wld. tube Wld. pipe Wld. pipe SA-403 SA-403 SA-479 SA-688 SA-813 SA-814 316 316 316 TP316 TP316 TP316 S31600 S31600 S31600 S31600 S31600 S31600 … WP-W … … … … … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 37 38 39 40 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Forgings Smls. tube Plate Wld. tube SA-182 SA-213 SA-240 SA-249 F316H TP316H 316H TP316H S31609 S31609 S31609 S31609 … … … … ≤ 125 … … … 8 8 8 8 1 1 1 1 41 42 43 44 45 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Smls. & wld. pipe Wld. pipe Smls. pipe Fittings Wld. fittings SA-312 SA-358 SA-376 SA-403 SA-403 TP316H 316H TP316H 316H 316H S31609 S31609 S31609 S31609 S31609 … 1 … … WP-W … … … … … 8 8 8 8 8 1 1 1 1 1 Nominal Composition Product Form Spec No. Type/Grade 1 2 3 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Forgings Forgings Bar SA-182 SA-965 SA/JIS G4303 F316L F316L SUS316L S31603 S31603 … … … … 4 5 6 7 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Forgings Smls. tube Plate Wld. tube SA-182 SA-213 SA-240 SA-249 F316L TP316L 316L TP316L S31603 S31603 S31603 S31603 8 9 10 11 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Smls. & wld. pipe Wld. pipe Fittings Wld. fittings SA-312 SA-358 SA-403 SA-403 TP316L 316L 316L 316L 12 13 14 15 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Bar Wld. tube Wld. pipe Wld. pipe SA-479 SA-688 SA-813 SA-814 16 17 18 19 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Castings Cast pipe Castings Cast pipe 20 21 22 23 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 24 25 26 27 296 Size/Thickness, mm 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa 1 2 3 450 450 480 170 170 175 4 5 6 7 485 485 485 485 8 9 10 11 External Pressure Chart No. Notes 427 427 427 HA-4 HA-4 HA-4 G7 G7 G7 170 170 170 170 427 427 427 427 HA-4 HA-4 HA-4 HA-4 G7 G7 G7 G7 485 485 485 485 170 170 170 170 427 427 427 427 HA-4 HA-4 HA-4 HA-4 G7 G7 G7 G7 12 13 14 15 485 485 485 485 170 170 170 170 427 427 427 427 HA-4 HA-4 HA-4 HA-4 G7 G7 G7 G7 16 17 18 19 485 485 485 485 205 205 205 205 427 427 427 427 HA-4 HA-4 HA-2 HA-2 G7, G13 G7, G13 G7, G9, G10, G13 G7, G13 20 21 22 23 485 485 485 485 205 205 205 205 427 427 427 427 HA-2 HA-2 HA-2 HA-2 G7 G7, G9, G10 G7 G7 24 25 26 27 515 515 515 515 205 205 205 205 427 427 427 427 HA-2 HA-2 HA-2 HA-2 G7, G9 G7, G9 G7, G9, G10 G7 28 29 30 515 515 515 205 205 205 427 427 427 HA-2 HA-2 HA-2 G7, G9, G10 G7 G7, G9, G10 31 32 33 34 35 36 515 515 515 515 515 515 205 205 205 205 205 205 427 427 427 427 427 427 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 G7 G7 37 38 39 40 515 515 515 515 205 205 205 205 427 427 427 427 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 41 42 43 44 45 515 515 515 515 515 205 205 205 205 205 427 427 427 427 427 HA-2 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 G7 Max. Temp. Limit (SPT p Supports Only) 297 #† 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 500 1 2 3 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 109 109 109 103 103 103 98.0 98.0 98.0 95.7 95.7 95.7 94.1 94.1 94.1 92.8 92.8 92.8 90.9 90.9 90.9 89.0 89.0 89.0 87.8 87.8 87.8 … … … … … … 4 5 6 7 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 109 109 109 109 103 103 103 103 98.0 98.0 98.0 98.0 95.7 95.7 95.7 95.7 94.1 94.1 94.1 94.1 92.8 92.8 92.8 92.8 90.9 90.9 90.9 90.9 89.0 89.0 89.0 89.0 87.8 87.8 87.8 87.8 … … … … … … … … 8 9 10 11 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 109 109 109 109 103 103 103 103 98.0 98.0 98.0 98.0 95.7 95.7 95.7 95.7 94.1 94.1 94.1 94.1 92.8 92.8 92.8 92.8 90.9 90.9 90.9 90.9 89.0 89.0 89.0 89.0 87.8 87.8 87.8 87.8 … … … … … … … … 12 13 14 15 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 109 109 109 109 103 103 103 103 98.0 98.0 98.0 98.0 95.7 95.7 95.7 95.7 94.1 94.1 94.1 94.1 92.8 92.8 92.8 92.8 90.9 90.9 90.9 90.9 89.0 89.0 89.0 89.0 87.8 87.8 87.8 87.8 … … … … … … … … 16 17 18 19 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 133 133 133 133 125 125 125 125 119 119 119 119 116 116 116 116 114 114 114 114 112 112 112 112 110 110 110 110 109 109 109 109 108 108 108 108 … … … … … … … … 20 21 22 23 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 134 134 134 134 126 126 126 126 119 119 119 119 116 116 116 116 114 114 114 114 112 112 112 112 111 111 111 111 110 110 110 110 108 108 108 108 … … … … … … … … 24 25 26 27 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 134 134 134 134 126 126 126 126 119 119 119 119 116 116 116 116 114 114 114 114 112 112 112 112 111 111 111 111 110 110 110 110 108 108 108 108 … … … … … … … … 28 29 30 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 134 134 134 126 126 126 119 119 119 116 116 116 114 114 114 112 112 112 111 111 111 110 110 110 108 108 108 … … … … … … 31 32 33 34 35 36 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 134 134 134 134 134 134 126 126 126 126 126 126 119 119 119 119 119 119 116 116 116 116 116 116 114 114 114 114 114 114 112 112 112 112 112 112 111 111 111 111 111 111 110 110 110 110 110 110 108 108 108 108 108 108 … … … … … … … … … … … … 37 38 39 40 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 134 134 134 134 126 126 126 126 119 119 119 119 116 116 116 116 114 114 114 114 112 112 112 112 111 111 111 111 110 110 110 110 108 108 108 108 … … … … … … … … 41 42 43 44 45 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 134 134 134 134 134 126 126 126 126 126 119 119 119 119 119 116 116 116 116 116 114 114 114 114 114 112 112 112 112 112 111 111 111 111 111 110 110 110 110 110 108 108 108 108 108 … … … … … … … … … … 298 INTENTIONALLY LEFT BLANK 299 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Line No. Alloy Designation/ UNS No. Class/ Condition/ Temper P-No. Group No. … … … … 8 8 8 8 1 1 1 1 … … … … > 125 … ≤ 125 … 8 8 8 8 1 1 1 1 S31653 S31653 S31653 S31653 S31653 … … … … … … … … … … 8 8 8 8 8 1 1 1 1 1 316LN 316LN 316LN TP316LN TP316LN TP316LN S31653 S31653 S31653 S31653 S31653 S31653 … WP-W … … … … … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 SA-182 SA-213 SA-240 SA-312 F316N TP316N 316N TP316N S31651 S31651 S31651 S31651 … … … … ≤ 125 ≤ 125 ≤ 125 ≤ 125 8 8 8 8 1 1 1 1 Wld. pipe Smls. pipe Fittings Wld. fittings SA-358 SA-376 SA-403 SA-403 316N TP316N 316N 316N S31651 S31651 S31651 S31651 … … … WP-W ≤ 125 … … … 8 8 8 8 1 1 1 1 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N Bar Wld. tube Wld. pipe Wld. pipe Forgings SA-479 SA-688 SA-813 SA-814 SA-965 316N TP316N TP316N TP316N F316N S31651 S31651 S31651 S31651 S31651 … … … … … … … … … ≤ 125 8 8 8 8 8 1 1 1 1 1 33 34 35 36 37 38 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Forgings Bar Forgings Smls. tube Plate Wld. tube SA-182 SA/JIS G4303 SA-182 SA-213 SA-240 SA-249 F304L SUS304L F304L TP304L 304L TP304L S30403 … S30403 S30403 S30403 S30403 … … … … … … > 125 … ≤ 125 … … … 8 8 8 8 8 8 1 1 1 1 1 1 39 40 41 42 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Smls. & wld. pipe Wld. pipe Fittings Wld. fittings SA-312 SA-358 SA-403 SA-403 TP304L 304L 304L 304L S30403 S30403 S30403 S30403 … 1 … WP-W … … … … 8 8 8 8 1 1 1 1 Nominal Composition Product Form Spec No. Type/Grade 1 2 3 4 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Bar Wld. pipe Wld. pipe Bar SA-479 SA-813 SA-814 SA/JIS G4303 316H TP316H TP316H SUS316 S31609 S31609 S31609 … … … … … 5 6 7 8 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N Forgings Forgings Forgings Smls. tube SA-182 SA-965 SA-182 SA-213 F316LN F316LN F316LN TP316LN S31653 S31653 S31653 S31653 9 10 11 12 13 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N Plate Wld. tube Smls. & wld. pipe Wld. pipe Smls. pipe SA-240 SA-249 SA-312 SA-358 SA-376 316LN TP316LN TP316LN 316LN TP316LN 14 15 16 17 18 19 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N Fittings Wld. fittings Bar Wld. tube Wld. pipe Wld. pipe SA-403 SA-403 SA-479 SA-688 SA-813 SA-814 20 21 22 23 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N Forgings Smls. tube Plate Smls. & wld. pipe 24 25 26 27 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 16Cr – 12Ni – 2Mo – N 28 29 30 31 32 300 Size/Thickness, mm 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa 1 2 3 4 515 515 515 520 205 205 205 205 5 6 7 8 485 485 515 515 9 10 11 12 13 External Pressure Chart No. Notes 427 427 427 427 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 205 205 205 205 427 427 427 427 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 515 515 515 515 515 205 205 205 205 205 427 427 427 427 427 HA-2 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 G7 14 15 16 17 18 19 515 515 515 515 515 515 205 205 205 205 205 205 427 427 427 427 427 427 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 G7 G7 20 21 22 23 550 550 550 550 240 240 240 240 427 427 427 427 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 24 25 26 27 550 550 550 550 240 240 240 240 427 427 427 427 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 28 29 30 31 32 550 550 550 550 550 240 240 240 240 240 427 427 427 427 427 HA-2 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 G7 33 34 35 36 37 38 450 480 485 485 485 485 170 175 170 170 170 170 427 427 427 427 427 427 HA-3 HA-3 HA-3 HA-3 HA-3 HA-3 G7 G7 G7 G7 G7 G7 39 40 41 42 485 485 485 485 170 170 170 170 427 427 427 427 HA-3 HA-3 HA-3 HA-3 G7 G7 G7 G7 Max. Temp. Limit (SPT p Supports Only) 301 #† 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 500 1 2 3 4 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 134 134 134 134 126 126 126 126 119 119 119 119 116 116 116 116 114 114 114 114 112 112 112 112 111 111 111 111 110 110 110 110 108 108 108 108 … … … … … … … … 5 6 7 8 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 131 131 131 131 122 122 122 122 116 116 116 116 113 113 113 113 110 110 110 110 107 107 107 107 105 105 105 105 102 102 102 102 99.7 99.7 99.7 99.7 … … … … … … … … 9 10 11 12 13 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 131 131 131 131 131 122 122 122 122 122 116 116 116 116 116 113 113 113 113 113 110 110 110 110 110 107 107 107 107 107 105 105 105 105 105 102 102 102 102 102 99.7 99.7 99.7 99.7 99.7 … … … … … … … … … … 14 15 16 17 18 19 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 131 131 131 131 131 131 122 122 122 122 122 122 116 116 116 116 116 116 113 113 113 113 113 113 110 110 110 110 110 110 107 107 107 107 107 107 105 105 105 105 105 105 102 102 102 102 102 102 99.7 99.7 99.7 99.7 99.7 99.7 … … … … … … … … … … … … 20 21 22 23 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 155 155 155 155 147 147 147 147 144 144 144 144 140 140 140 140 137 137 137 137 135 135 135 135 133 133 133 133 130 130 130 130 … … … … … … … … 24 25 26 27 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 155 155 155 155 147 147 147 147 144 144 144 144 140 140 140 140 137 137 137 137 135 135 135 135 133 133 133 133 130 130 130 130 … … … … … … … … 28 29 30 31 32 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 155 155 155 155 155 147 147 147 147 147 144 144 144 144 144 140 140 140 140 140 137 137 137 137 137 135 135 135 135 135 133 133 133 133 133 130 130 130 130 130 … … … … … … … … … … 33 34 35 36 37 38 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 110 110 110 110 110 110 103 103 103 103 103 103 97.7 97.7 97.7 97.7 97.7 97.7 95.8 95.8 95.8 95.8 95.8 95.8 94.1 94.1 94.1 94.1 94.1 94.1 92.9 92.9 92.9 92.9 92.9 92.9 91.6 91.6 91.6 91.6 91.6 91.6 89.7 89.7 89.7 89.7 89.7 89.7 88.4 88.4 88.4 88.4 88.4 88.4 … … … … … … … … … … … … 39 40 41 42 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 110 110 110 110 103 103 103 103 97.7 97.7 97.7 97.7 95.8 95.8 95.8 95.8 94.1 94.1 94.1 94.1 92.9 92.9 92.9 92.9 91.6 91.6 91.6 91.6 89.7 89.7 89.7 89.7 88.4 88.4 88.4 88.4 … … … … … … … … 302 INTENTIONALLY LEFT BLANK 303 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Line No. Alloy Designation/ UNS No. Class/ Condition/ Temper P-No. Group No. … … … … 8 8 8 8 1 1 1 1 … … … … … … … … 8 8 8 8 1 1 1 1 S30400 S30400 S30400 S30409 S30409 … … … … … > 125 … … > 125 … 8 8 8 8 8 1 1 1 1 1 302 F304 TP304 304 TP304 S30200 S30400 S30400 S30400 S30400 … … … … … … ≤ 125 … … … 8 8 8 8 8 1 1 1 1 1 SA-312 SA-358 SA-376 TP304 304 TP304 S30400 S30400 S30400 … 1 … … … … 8 8 8 1 1 1 Fittings Wld. fittings Bar Wld. tube Wld. tube Wld. tube SA-403 SA-403 SA-479 SA-688 SA-813 SA-814 304 304 304 TP304 TP304 TP304 S30400 S30400 S30400 S30400 S30400 S30400 … WP-W … … … … … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Forgings Smls. tube Plate Wld. tube SA-182 SA-213 SA-240 SA-249 F304H TP304H 304H TP304H S30409 S30409 S30409 S30409 … … … … ≤ 125 … … … 8 8 8 8 1 1 1 1 32 33 34 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Smls. & wld. pipe Wld. pipe Smls. pipe SA-312 SA-358 SA-376 TP304H 304H TP304H S30409 S30409 S30409 … 1 … … … … 8 8 8 1 1 1 35 36 37 38 39 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Fittings Wld. fittings Bar Wld. tube Wld. tube SA-403 SA-403 SA-479 SA-813 SA-814 304H 304H 304H TP304H TP304H S30409 S30409 S30409 S30409 S30409 … WP-W … … … … … … … … 8 8 8 8 8 1 1 1 1 1 Nominal Composition Product Form Spec No. Type/Grade 1 2 3 4 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Bar Wld. tube Wld. pipe Wld. pipe SA-479 SA-688 SA-813 SA-814 304L TP304L TP304L TP304L S30403 S30403 S30403 S30403 … … … … 5 6 7 8 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Castings Cast pipe Castings Cast pipe SA-351 SA-451 SA-351 SA-451 CF3 CPF3 CF8 CPF8 J92500 J92500 J92600 J92600 9 10 11 12 13 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Forgings Smls. pipe Forgings Forgings Forgings SA-182 SA-376 SA-965 SA-182 SA-965 F304 TP304 F304 F304H F304H 14 15 16 17 18 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Bar Forgings Smls. tube Plate Wld. tube SA-479 SA-182 SA-213 SA-240 SA-249 19 20 21 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Smls. & wld. pipe Wld. pipe Smls. pipe 22 23 24 25 26 27 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 28 29 30 31 304 Size/Thickness, mm 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa 1 2 3 4 485 485 485 485 170 170 170 170 5 6 7 8 485 485 485 485 9 10 11 12 13 External Pressure Chart No. Notes 427 427 427 427 HA-3 HA-3 HA-3 HA-3 G7 G7 G7 G7 205 205 205 205 427 427 427 427 HA-3 HA-3 HA-1 HA-1 G7, G13 G7, G13 G7, G9, G10, G13 G7, G13 485 485 485 485 485 205 205 205 205 205 427 427 427 427 427 HA-1 HA-1 HA-1 HA-1 HA-1 G7, G9, G10 G7, G9, G10, S2 G7, G9, G10 G7 G7 14 15 16 17 18 515 515 515 515 515 205 205 205 205 205 427 427 427 427 427 HA-1 HA-1 HA-1 HA-1 HA-1 G7 G7, G9, G10 G7, G9 G7, G9, G10 G7 19 20 21 515 515 515 205 205 205 427 427 427 HA-1 HA-1 HA-1 G7, G9, G10 G7 G7, G9, G10, S2 22 23 24 25 26 27 515 515 515 515 515 515 205 205 205 205 205 205 427 427 427 427 427 427 HA-1 HA-1 HA-1 HA-1 HA-1 HA-1 G7 G7 G7 G7 G7 G7 28 29 30 31 515 515 515 515 205 205 205 205 427 427 427 427 HA-1 HA-1 HA-1 HA-1 G7 G7 G7 G7 32 33 34 515 515 515 205 205 205 427 427 427 HA-1 HA-1 HA-1 G7 G7 G7 35 36 37 38 39 515 515 515 515 515 205 205 205 205 205 427 427 427 427 427 HA-1 HA-1 HA-1 HA-1 HA-1 G7 G7 G7 G7 G7 Max. Temp. Limit (SPT p Supports Only) 305 #† 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 500 1 2 3 4 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 110 110 110 110 103 103 103 103 97.7 97.7 97.7 97.7 95.8 95.8 95.8 95.8 94.1 94.1 94.1 94.1 92.9 92.9 92.9 92.9 91.6 91.6 91.6 91.6 89.7 89.7 89.7 89.7 88.4 88.4 88.4 88.4 … … … … … … … … 5 6 7 8 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 129 129 129 129 122 122 122 122 116 116 116 116 114 114 114 114 111 111 111 111 109 109 109 109 107 107 107 107 105 105 105 105 103 103 103 103 … … … … … … … … 9 10 11 12 13 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 129 129 129 129 129 122 122 122 122 122 116 116 116 116 116 114 114 114 114 114 111 111 111 111 111 109 109 109 109 109 107 107 107 107 107 105 105 105 105 105 103 103 103 103 103 … … … … … … … … … … 14 15 16 17 18 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 129 129 129 129 129 122 122 122 122 122 116 116 116 116 116 114 114 114 114 114 111 111 111 111 111 109 109 109 109 109 107 107 107 107 107 105 105 105 105 105 103 103 103 103 103 … … … … … … … … … … 19 20 21 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 129 129 129 122 122 122 116 116 116 114 114 114 111 111 111 109 109 109 107 107 107 105 105 105 103 103 103 … … … … … … 22 23 24 25 26 27 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 129 129 129 129 129 129 122 122 122 122 122 122 116 116 116 116 116 116 114 114 114 114 114 114 111 111 111 111 111 111 109 109 109 109 109 109 107 107 107 107 107 107 105 105 105 105 105 105 103 103 103 103 103 103 … … … … … … … … … … … … 28 29 30 31 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 129 129 129 129 122 122 122 122 116 116 116 116 114 114 114 114 111 111 111 111 109 109 109 109 107 107 107 107 105 105 105 105 103 103 103 103 … … … … … … … … 32 33 34 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 129 129 129 122 122 122 116 116 116 114 114 114 111 111 111 109 109 109 107 107 107 105 105 105 103 103 103 … … … … … … 35 36 37 38 39 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 129 129 129 129 129 122 122 122 122 122 116 116 116 116 116 114 114 114 114 114 111 111 111 111 111 109 109 109 109 109 107 107 107 107 107 105 105 105 105 105 103 103 103 103 103 … … … … … … … … … … 306 INTENTIONALLY LEFT BLANK 307 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Line No. Alloy Designation/ UNS No. Class/ Condition/ Temper P-No. Group No. … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 … … … … … … > 125 … ≤ 125 … … … 8 8 8 8 8 8 1 1 1 1 1 1 S30453 S30453 S30453 S30453 S30453 … … … … WP-W … … … … … 8 8 8 8 8 1 1 1 1 1 304LN TP304LN TP304LN TP304LN S30453 S30453 S30453 S30453 … … … … … … … … 8 8 8 8 1 1 1 1 SA-182 SA-213 SA-240 F304N TP304N 304N S30451 S30451 S30451 … … … … … … 8 8 8 1 1 1 Smls. & wld. pipe Wld. pipe Smls. pipe Fittings Wld. fittings SA-312 SA-358 SA-376 SA-403 SA-403 TP304N 304N TP304N 304N 304N S30451 S30451 S30451 S30451 S30451 … 1 … … WP-W … … … … … 8 8 8 8 8 1 1 1 1 1 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – 4Si – N Bar Wld. tube Wld. pipe Wld. pipe Forgings Bar SA-479 SA-688 SA-813 SA-814 SA-965 SA-479 304N TP304N TP304N TP304N F304N … S30451 S30451 S30451 S30451 S30451 S21800 … … … … … … … … … … … … 8 8 8 8 8 8 1 1 1 1 1 3 36 37 38 39 40 41 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Castings Cast pipe Forgings Forgings Forgings Forgings SA-351 SA-451 SA-182 SA-965 SA-182 SA-965 CF8C CPF8C F347 F347 F347H F347H J92710 J92710 S34700 S34700 S34709 S34709 … … … … … … … … > 125 … > 125 … 8 8 8 8 8 8 1 1 1 1 1 1 42 43 44 45 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Forgings Smls. tube Plate Wld. tube SA-182 SA-213 SA-240 SA-249 F347 TP347 347 TP347 S34700 S34700 S34700 S34700 … … … … ≤ 125 … … … 8 8 8 8 1 1 1 1 Nominal Composition Product Form 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Bar Bar Castings Cast pipe Castings Cast pipe SA/JIS G4303 SA/JIS G4303 SA-351 SA-451 SA-351 SA-451 SUS302 SUS304 CF3A CPF3A CF8A CPF8A … … J92500 J92500 J92600 J92600 … … … … … … 7 8 9 10 11 12 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N Forgings Forgings Forgings Smls. tube Plate Wld. tube SA-182 SA-965 SA-182 SA-213 SA-240 SA-249 F304LN F304LN F304LN TP304LN 304LN TP304LN S30453 S30453 S30453 S30453 S30453 S30453 13 14 15 16 17 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N Smls. & wld. pipe Wld. pipe Smls. pipe Fittings Wld. fittings SA-312 SA-358 SA-376 SA-403 SA-403 TP304LN 304LN TP304LN 304LN 304LN 18 19 20 21 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N Bar Wld. tube Wld. tube Wld. tube SA-479 SA-688 SA-813 SA-814 22 23 24 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N Forgings Smls. tube Plate 25 26 27 28 29 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 18Cr – 8Ni – N 30 31 32 33 34 35 1 2 3 4 5 6 Spec No. Type/Grade 308 Size/Thickness, mm 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa 1 2 3 4 5 6 520 520 530 530 530 530 205 205 240 240 240 240 7 8 9 10 11 12 485 485 515 515 515 515 13 14 15 16 17 External Pressure Chart No. Notes 427 427 371 371 371 371 HA-1 HA-1 HA-3 HA-3 HA-1 HA-1 G7 G7 G7, G13 G7, G13 G7, G13 G7, G13 205 205 205 205 205 205 427 427 427 427 427 427 HA-1 HA-1 HA-1 HA-1 HA-1 HA-1 G7 G7 G7 G7 G7 G7 515 515 515 515 515 205 205 205 205 205 427 427 427 427 427 HA-1 HA-1 HA-1 HA-1 HA-1 G7 G7 G7 G7 G7 18 19 20 21 515 515 515 515 205 205 205 205 427 427 427 427 HA-1 HA-1 HA-1 HA-1 G7 G7 G7 G7 22 23 24 550 550 550 240 240 240 427 427 427 HA-1 HA-1 HA-1 G7 G7 G7 25 26 27 28 29 550 550 550 550 550 240 240 240 240 240 427 427 427 427 427 HA-1 HA-1 HA-1 HA-1 HA-1 G7 G7 G7 G7 G7 30 31 32 33 34 35 550 550 550 550 550 655 240 240 240 240 240 345 427 427 427 427 427 427 HA-1 HA-1 HA-1 HA-1 HA-1 HA-6 G7 G7 G7 G7 G7 … 36 37 38 39 40 41 485 485 485 485 485 485 205 205 205 205 205 205 427 427 427 427 427 427 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G7, G9, G13 G7, G13 G7, G9 G7, G9 G7 G7, G9 42 43 44 45 515 515 515 515 205 205 205 205 427 427 427 427 HA-2 HA-2 HA-2 HA-2 G7, G9 G7, G9 G7, G9 G7 Max. Temp. Limit (SPT p Supports Only) 309 #† 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 500 1 2 3 4 5 6 138 138 161 161 161 161 138 138 161 161 161 161 138 138 161 161 161 161 138 138 159 159 159 159 138 138 156 156 156 156 129 129 150 150 150 150 122 122 142 142 142 142 116 116 135 135 135 135 114 114 132 132 132 132 111 111 130 130 130 130 109 109 127 127 127 127 107 107 … … … … 105 105 … … … … 103 103 … … … … … … … … … … … … … … … … 7 8 9 10 11 12 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 129 129 129 129 129 129 122 122 122 122 122 122 116 116 116 116 116 116 114 114 114 114 114 114 111 111 111 111 111 111 109 109 109 109 109 109 107 107 107 107 107 107 105 105 105 105 105 105 103 103 103 103 103 103 … … … … … … … … … … … … 13 14 15 16 17 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 129 129 129 129 129 122 122 122 122 122 116 116 116 116 116 114 114 114 114 114 111 111 111 111 111 109 109 109 109 109 107 107 107 107 107 105 105 105 105 105 103 103 103 103 103 … … … … … … … … … … 18 19 20 21 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 129 129 129 129 122 122 122 122 116 116 116 116 114 114 114 114 111 111 111 111 109 109 109 109 107 107 107 107 105 105 105 105 103 103 103 103 … … … … … … … … 22 23 24 161 161 161 161 161 161 160 160 160 159 159 159 155 155 155 141 141 141 132 132 132 125 125 125 122 122 122 120 120 120 118 118 118 116 116 116 115 115 115 113 113 113 … … … … … … 25 26 27 28 29 161 161 161 161 161 161 161 161 161 161 160 160 160 160 160 159 159 159 159 159 155 155 155 155 155 141 141 141 141 141 132 132 132 132 132 125 125 125 125 125 122 122 122 122 122 120 120 120 120 120 118 118 118 118 118 116 116 116 116 116 115 115 115 115 115 113 113 113 113 113 … … … … … … … … … … 30 31 32 33 34 35 161 161 161 161 161 219 161 161 161 161 161 198 160 160 160 160 160 175 159 159 159 159 159 162 155 155 155 155 155 152 141 141 141 141 141 138 132 132 132 132 132 128 125 125 125 125 125 123 122 122 122 122 122 121 120 120 120 120 120 119 118 118 118 118 118 118 116 116 116 116 116 116 115 115 115 115 115 116 113 113 113 113 113 115 … … … … … … … … … … … … 36 37 38 39 40 41 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 134 134 134 134 134 134 129 129 129 129 129 129 127 127 127 127 127 127 127 127 127 127 127 127 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 126 … … … … … … … … … … … … 42 43 44 45 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 135 135 135 135 132 132 132 132 130 130 130 130 129 129 129 129 128 128 128 128 126 126 126 126 125 125 125 125 … … … … … … … … 310 INTENTIONALLY LEFT BLANK 311 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Line No. Alloy Designation/ UNS No. Class/ Condition/ Temper P-No. Group No. … … … 8 8 8 1 1 1 … WP-W … … … … … … … … 8 8 8 8 8 1 1 1 1 1 S34709 S34709 S34709 S34709 S34709 S34709 … … … … … … ≤ 125 … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 347H 347H 347H TP347H TP347H S34709 S34709 S34709 S34709 S34709 … WP-W … … … … … … … … 8 8 8 8 8 1 1 1 1 1 SA-182 SA-213 SA-240 SA-249 F348 TP348 348 TP348 S34800 S34800 S34800 S34800 … … … … ≤ 125 … … … 8 8 8 8 1 1 1 1 Smls. & wld. pipe Wld. pipe Smls. pipe SA-312 SA-358 SA-376 TP348 348 TP348 S34800 S34800 S34800 … 1 … … … … 8 8 8 1 1 1 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Fittings Wld. fittings Bar Wld. pipe Wld. pipe SA-403 SA-403 SA-479 SA-813 SA-814 348 348 348 TP348 TP348 S34800 S34800 S34800 S34800 S34800 … WP-W … … … … … … … … 8 8 8 8 8 1 1 1 1 1 32 33 34 35 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Forgings Smls. tube Plate Wld. tube SA-182 SA-213 SA-240 SA-249 F348H TP348H 348H TP348H S34809 S34809 S34809 S34809 … … … … ≤ 125 … … … 8 8 8 8 1 1 1 1 36 37 38 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Smls. & wld. pipe Fittings Wld. fittings SA-312 SA-403 SA-403 TP348H 348H 348H S34809 S34809 S34809 … … WP-W … … … 8 8 8 1 1 1 39 40 41 42 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Bar Wld. pipe Wld. pipe Bar SA-479 SA-813 SA-814 SA/JIS G4303 348H TP348H TP348H SUS347 S34809 S34809 S34809 … … … … … … … … … 8 8 8 8 1 1 1 1 Nominal Composition Product Form Spec No. Type/Grade 1 2 3 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Smls. & wld. pipe Wld. pipe Smls. pipe SA-312 SA-358 SA-376 TP347 347 TP347 S34700 S34700 S34700 … 1 … 4 5 6 7 8 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Fittings Wld. fittings Bar Wld. pipe Wld. pipe SA-403 SA-403 SA-479 SA-813 SA-814 347 347 347 TP347 TP347 S34700 S34700 S34700 S34700 S34700 9 10 11 12 13 14 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Forgings Smls. tube Plate Wld. tube Smls. & wld. pipe Smls. pipe SA-182 SA-213 SA-240 SA-249 SA-312 SA-376 F347H TP347H 347H TP347H TP347H TP347H 15 16 17 18 19 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Fittings Wld. fittings Bar Wld. pipe Wld. pipe SA-403 SA-403 SA-479 SA-813 SA-814 20 21 22 23 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Forgings Smls. tube Plate Wld. tube 24 25 26 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 27 28 29 30 31 312 Size/Thickness, mm 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa 1 2 3 515 515 515 205 205 205 4 5 6 7 8 515 515 515 515 515 9 10 11 12 13 14 External Pressure Chart No. Notes 427 427 427 HA-2 HA-2 HA-2 G7, G9 G7 G7, G9 205 205 205 205 205 427 427 427 427 427 HA-2 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 G7 515 515 515 515 515 515 205 205 205 205 205 205 427 427 427 427 427 427 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 G7 G7 15 16 17 18 19 515 515 515 515 515 205 205 205 205 205 427 427 427 427 427 HA-2 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 G7 20 21 22 23 515 515 515 515 205 205 205 205 427 427 427 427 HA-2 HA-2 HA-2 HA-2 G7, G9 G7, G9 G7, G9 G7 24 25 26 515 515 515 205 205 205 427 427 427 HA-2 HA-2 HA-2 G7, G9 G7 G7, G9 27 28 29 30 31 515 515 515 515 515 205 205 205 205 205 427 427 427 427 427 HA-2 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 G7 32 33 34 35 515 515 515 515 205 205 205 205 427 427 427 427 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 36 37 38 515 515 515 205 205 205 427 427 427 HA-2 HA-2 HA-2 G7 G7 G7 39 40 41 42 515 515 515 520 205 205 205 205 427 427 427 427 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 Max. Temp. Limit (SPT p Supports Only) 313 #† 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 500 1 2 3 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 135 135 135 132 132 132 130 130 130 129 129 129 128 128 128 126 126 126 125 125 125 … … … … … … 4 5 6 7 8 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 135 135 135 135 135 132 132 132 132 132 130 130 130 130 130 129 129 129 129 129 128 128 128 128 128 126 126 126 126 126 125 125 125 125 125 … … … … … … … … … … 9 10 11 12 13 14 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 135 135 135 135 135 135 132 132 132 132 132 132 130 130 130 130 130 130 129 129 129 129 129 129 128 128 128 128 128 128 126 126 126 126 126 126 125 125 125 125 125 125 … … … … … … … … … … … … 15 16 17 18 19 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 135 135 135 135 135 132 132 132 132 132 130 130 130 130 130 129 129 129 129 129 128 128 128 128 128 126 126 126 126 126 125 125 125 125 125 … … … … … … … … … … 20 21 22 23 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 135 135 135 135 132 132 132 132 130 130 130 130 129 129 129 129 128 128 128 128 126 126 126 126 125 125 125 125 … … … … … … … … 24 25 26 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 135 135 135 132 132 132 130 130 130 129 129 129 128 128 128 126 126 126 125 125 125 … … … … … … 27 28 29 30 31 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 135 135 135 135 135 132 132 132 132 132 130 130 130 130 130 129 129 129 129 129 128 128 128 128 128 126 126 126 126 126 125 125 125 125 125 … … … … … … … … … … 32 33 34 35 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 135 135 135 135 132 132 132 132 130 130 130 130 129 129 129 129 128 128 128 128 126 126 126 126 125 125 125 125 … … … … … … … … 36 37 38 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 135 135 135 132 132 132 130 130 130 129 129 129 128 128 128 126 126 126 125 125 125 … … … … … … 39 40 41 42 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 135 135 135 135 132 132 132 132 130 130 130 130 129 129 129 129 128 128 128 128 126 126 126 126 125 125 125 125 … … … … … … … … 314 INTENTIONALLY LEFT BLANK 315 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Line No. Alloy Designation/ UNS No. Class/ Condition/ Temper P-No. Group No. > 10 > 10 > 125 … > 125 … 8 8 8 8 8 8 1 1 1 1 1 1 … … … … ≤ 125 … … … 8 8 8 8 1 1 1 1 S32100 S32100 S32100 … 1 … ≤ 10 … ≤ 10 8 8 8 1 1 1 321 321 321 TP321 TP321 S32100 S32100 S32100 S32100 S32100 … WP-W … … … … … … … … 8 8 8 8 8 1 1 1 1 1 SA-182 SA-213 SA-240 SA-249 SA-312 SA-376 F321H TP321H 321H TP321H TP321H TP321H S32109 S32109 S32109 S32109 S32109 S32109 … … … … … … ≤ 125 … … … ≤5 ≤ 10 8 8 8 8 8 8 1 1 1 1 1 1 Fittings Wld. fittings Bar Wld. pipe Wld. pipe Bar SA-403 SA-403 SA-479 SA-813 SA-814 SA/JIS G4303 321H 321H 321H TP321H TP321H SUS321 S32109 S32109 S32109 S32109 S32109 … … WP-W … … … … … … … … … … 8 8 8 8 8 8 1 1 1 1 1 1 18Cr – 11Ni 18Cr – 13Ni – 3Mo 18Cr – 13Ni – 3Mo 20Cr – 10Ni Plate Wld. tube Smls. & wld. pipe Bar SA-240 SA-249 SA-312 SA-479 305 TP317 TP317 ER308 S30500 S31700 S31700 S30880 … … … … … … … … 8 8 8 8 1 1 1 1 35 36 37 38 21Cr – 6Ni – 9Mn 21Cr – 6Ni – 9Mn 21Cr – 6Ni – 9Mn 21Cr – 6Ni – 9Mn Forgings Smls. & wld. pipe Plate Forgings SA-182 SA-312 SA-666 SA-965 FXM-11 TPXM-11 XM-11 FXM-11 S21904 S21904 S21904 S21904 … … … … … … … … 8 8 8 8 3 3 3 3 39 40 41 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn Forgings Plate Wld. tube SA-182 SA-240 SA-249 FXM-19 XM-19 TPXM-19 S20910 S20910 S20910 … … … … … … 8 8 8 3 3 3 42 43 44 45 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn Smls. & wld. pipe Wld. pipe Fittings Wld. fittings SA-312 SA-358 SA-403 SA-403 TPXM-19 XM-19 XM-19 XM-19 S20910 S20910 S20910 S20910 … 1 … WP-W … … … … 8 8 8 8 3 3 3 3 Nominal Composition Product Form Spec No. Type/Grade 1 2 3 4 5 6 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Smls. pipe Smls. pipe Forgings Forgings Forgings Forgings SA-376 SA-376 SA-182 SA-965 SA-182 SA-965 TP321 TP321H F321 F321 F321H F321H S32100 S32109 S32100 S32100 S32109 S32109 … … … … … … 7 8 9 10 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Forgings Smls. tube Plate Wld. tube SA-182 SA-213 SA-240 SA-249 F321 TP321 321 TP321 S32100 S32100 S32100 S32100 11 12 13 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Smls. & wld. pipe Wld. pipe Smls. pipe SA-312 SA-358 SA-376 TP321 321 TP321 14 15 16 17 18 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Fittings Wld. fittings Bar Wld. pipe Wld. pipe SA-403 SA-403 SA-479 SA-813 SA-814 19 20 21 22 23 24 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Forgings Smls. tube Plate Wld. tube Smls. & wld. pipe Smls. pipe 25 26 27 28 29 30 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 31 32 33 34 316 Size/Thickness, mm 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa 1 2 3 4 5 6 485 485 485 485 485 485 170 170 205 205 205 205 7 8 9 10 515 515 515 515 11 12 13 External Pressure Chart No. Notes 427 427 427 427 427 427 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G7, G9 G7 G7, G9 G7, G9 G7 G7, G9 205 205 205 205 427 427 427 427 HA-2 HA-2 HA-2 HA-2 G7, G9 G7, G9 G7, G9 G7 515 515 515 205 205 205 427 427 427 HA-2 HA-2 HA-2 G7, G9 G7 G7, G9 14 15 16 17 18 515 515 515 515 515 205 205 205 205 205 427 427 427 427 427 HA-2 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 G7 19 20 21 22 23 24 515 515 515 515 515 515 205 205 205 205 205 205 427 427 427 427 427 427 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 G7 G7 25 26 27 28 29 30 515 515 515 515 515 520 205 205 205 205 205 205 427 427 427 427 427 427 HA-2 HA-2 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 G7 G7 31 32 33 34 515 515 515 515 205 205 205 205 427 427 427 427 HA-1 HA-2 HA-2 HA-2 G7 G7 G7 G7 35 36 37 38 620 620 620 620 345 345 345 345 316 316 316 316 HA-6 HA-6 HA-6 HA-6 G7 G7 G7 G7 39 40 41 690 690 690 380 380 380 427 427 427 HA-6 HA-6 HA-6 G7 G7 G7 42 43 44 45 690 690 690 690 380 380 380 380 427 427 427 427 HA-6 HA-6 HA-6 HA-6 G7 G7 G7 G7 Max. Temp. Limit (SPT p Supports Only) 317 #† 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 500 1 2 3 4 5 6 115 115 138 138 138 138 115 115 138 138 138 138 115 115 138 138 138 138 115 115 138 138 138 138 115 115 138 138 138 138 115 115 138 138 138 138 112 112 134 134 134 134 106 106 128 128 128 128 104 104 125 125 125 125 102 102 123 123 123 123 100 100 120 120 120 120 98.5 98.5 119 119 119 119 97.3 97.3 117 117 117 117 96.0 96.0 115 115 115 115 … … … … … … … … … … … … 7 8 9 10 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 134 134 134 134 128 128 128 128 125 125 125 125 123 123 123 123 120 120 120 120 119 119 119 119 117 117 117 117 115 115 115 115 … … … … … … … … 11 12 13 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 134 134 134 128 128 128 125 125 125 123 123 123 120 120 120 119 119 119 117 117 117 115 115 115 … … … … … … 14 15 16 17 18 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 134 134 134 134 134 128 128 128 128 128 125 125 125 125 125 123 123 123 123 123 120 120 120 120 120 119 119 119 119 119 117 117 117 117 117 115 115 115 115 115 … … … … … … … … … … 19 20 21 22 23 24 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 134 134 134 134 134 134 128 128 128 128 128 128 125 125 125 125 125 125 123 123 123 123 123 123 120 120 120 120 120 120 119 119 119 119 119 119 117 117 117 117 117 117 115 115 115 115 115 115 … … … … … … … … … … … … 25 26 27 28 29 30 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 134 134 134 134 134 134 128 128 128 128 128 128 125 125 125 125 125 125 123 123 123 123 123 123 120 120 120 120 120 120 119 119 119 119 119 119 117 117 117 117 117 117 115 115 115 115 115 115 … … … … … … … … … … … … 31 32 33 34 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 129 134 134 129 122 126 126 122 116 119 119 116 114 116 116 114 111 114 114 111 109 112 112 109 107 111 111 107 105 110 110 105 103 108 108 103 … … … … … … … … 35 36 37 38 207 207 207 207 207 207 207 207 206 206 206 206 200 200 200 200 193 193 193 193 183 183 183 183 171 171 171 171 162 162 162 162 158 158 158 158 … … … … … … … … … … … … … … … … … … … … … … … … … … … … 39 40 41 230 230 230 229 229 229 228 228 228 222 222 222 216 216 216 210 210 210 206 206 206 202 202 202 201 201 201 200 200 200 198 198 198 196 196 196 195 195 195 194 194 194 … … … … … … 42 43 44 45 230 230 230 230 229 229 229 229 228 228 228 228 222 222 222 222 216 216 216 216 210 210 210 210 206 206 206 206 202 202 202 202 201 201 201 201 200 200 200 200 198 198 198 198 196 196 196 196 195 195 195 195 194 194 194 194 … … … … … … … … 318 INTENTIONALLY LEFT BLANK 319 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Line No. Spec No. Type/Grade Alloy Designation/ UNS No. Class/ Condition/ Temper P-No. Group No. … … … … 8 8 8 8 3 3 3 3 … WP-W … … … … … … … … 8 8 8 8 8 2 2 2 2 2 J93400 J93400 J93402 J93402 … … … … … … … … 8 8 8 8 2 2 2 2 J94202 J94202 S31000 S31008 S31008 S31008 … … … 1 … WP-W … … … … … … 8 8 8 8 8 8 2 2 2 2 2 2 Nominal Composition Product Form 1 2 3 4 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn Bar Wld. pipe Wld. pipe Forgings SA-479 SA-813 SA-814 SA-965 XM-19 TPXM-19 TPXM-19 FXM-19 S20910 S20910 S20910 S20910 … … … … 5 6 7 8 9 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni 23Cr – 12Ni Fittings Wld. fittings Wld. pipe Bar Bar SA-403 SA-403 SA-358 SA-479 SA/JIS G4303 309 309 309S 309S SUS309S S30900 S30900 S30908 S30908 … 10 11 12 13 25Cr – 12Ni 25Cr – 12Ni 25Cr – 12Ni 25Cr – 12Ni Castings Cast pipe Castings Cast pipe SA-351 SA-451 SA-351 SA-451 CH8 CPH8 CH20 CPH20 14 15 16 17 18 19 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni 25Cr – 20Ni Castings Cast pipe Forgings Wld. pipe Fittings Wld. fittings SA-351 SA-451 SA-965 SA-358 SA-403 SA-403 CK20 CPK20 F310 310S 310S 310S 320 Size/Thickness, mm 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa 1 2 3 4 690 690 690 690 380 380 380 380 5 6 7 8 9 515 515 515 515 520 10 11 12 13 14 15 16 17 18 19 External Pressure Chart No. Notes 427 427 427 427 HA-6 HA-6 HA-6 HA-6 G7 G7 G7 G7 205 205 205 205 205 427 427 427 427 427 HA-2 HA-2 HA-2 HA-2 HA-2 G7 G7 G7 G7 G7 450 450 485 485 195 195 205 205 427 427 427 427 HA-3 HA-3 HA-2 HA-2 G7, G9, G10, G13 G7, G13 G7 G7 450 450 515 515 515 515 195 195 205 205 205 205 427 427 427 427 427 427 HA-3 HA-3 HA-2 HA-2 HA-2 HA-2 G7 G7 G7, G9, G11, G12 G7 G7 G7 Max. Temp. Limit (SPT p Supports Only) 321 #† 2011a SECTION II, PART D (METRIC) TABLE 2A (CONT’D) SECTION III, DIVISION 1, CLASSES 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR FERROUS MATERIALS †# Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 200 250 300 325 350 375 400 425 450 475 500 1 2 3 4 230 230 230 230 229 229 229 229 228 228 228 228 222 222 222 222 216 216 216 216 210 210 210 210 206 206 206 206 202 202 202 202 201 201 201 201 200 200 200 200 198 198 198 198 196 196 196 196 195 195 195 195 194 194 194 194 … … … … … … … … 5 6 7 8 9 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 135 135 135 135 135 131 131 131 131 131 129 129 129 129 129 127 127 127 127 127 125 125 125 125 125 124 124 124 124 124 122 122 122 122 122 121 121 121 121 121 … … … … … … … … … … 10 11 12 13 129 129 138 138 129 129 138 138 129 129 138 138 128 128 138 138 127 127 137 137 124 124 134 134 122 122 131 131 119 119 128 128 117 117 125 125 114 114 123 123 112 112 120 120 110 110 117 117 106 106 114 114 103 103 111 111 … … … … … … … … 14 15 16 17 18 19 129 129 138 138 138 138 129 129 138 138 138 138 129 129 138 138 138 138 128 128 138 138 138 138 127 127 138 138 138 138 124 124 138 138 138 138 122 122 134 134 134 134 119 119 129 129 129 129 117 117 127 127 127 127 114 114 125 125 125 125 112 112 123 123 123 123 110 110 122 122 122 122 106 106 120 120 120 120 103 103 118 118 118 118 … … … … … … … … … … … … 322 2011a SECTION II, PART D (METRIC) NOTES TO TABLE 2A (10) GENERAL NOTES (a) The following abbreviations are used: Smls., Seamless; Temp., Temperature; and Wld., Welded. (b) An alternative typeface is used for stress values based on successful experience in service (see Notes E1 and E2). (c) Where specifications, grades, classes, and types are listed in this Table, and where the material specification in Section II, Part A or Part B is a dual-unit specification (e.g., SA-516/SA-516M), the values listed in this Table shall be applicable to either the customary U.S. version of the material specification or the SI units version of the material specification. For example, the values listed for SA-516 Grade 70 shall be used when SA-516M Grade 485 is used in construction. (d) The values in this Table may be interpolated to determine values for intermediate temperatures. The values at intermediate temperatures shall be rounded to the same number of decimal places as the value at the higher temperature between which values are being interpolated. The rounding rule is: when the next digit beyond the last place to be retained is less than 5, retain unchanged the digit in the last place retained; when the digit next beyond the last place to be retained is 5 or greater, increase by 1 the digit in the last place retained. (e) The properties of steels are influenced by the processing history, heat treatment, melting practice, and level of residual elements. See Nonmandatory Appendix A for more information. NOTES — EXPERIENCE CRITERION E1 For values at 350°C and above, the design stress intensity values are based on successful experience in service. E2 For values at 375°C and above, the design stress intensity values are based on successful experience in service. NOTES — GENERAL REQUIREMENTS G1 Material that conforms to Class 10, 13, 20, 23, 30, 33, 40, 43, 50, or 53 is not permitted. G2 Material that conforms to Class 11 or 12 is not permitted. G3 Material that conforms to Class 11 or 12 is not permitted when the nominal thickness of the material exceeds 19 mm. G4 Material that conforms to Class 11 or 12 is not permitted when the nominal thickness of the material exceeds 32 mm. G5 A product analysis is required on this material. G6 SA-723 shall not be used for minimum permissible temperature below +5°C. G7 Due to the relatively low yield strength of these materials, these higher stress values were established at temperatures where the shorttime tensile properties govern to permit the use of these alloys where slightly greater deformation is acceptable. The stress values in this range exceed 662⁄3% but do not exceed 90% of the yield strength at temperature. Use of these stresses may result in dimensional changes due to permanent strain. These stress values are not recommended for the flanges of gasketed joints or other applications where slight amounts of distortion can cause leakage or malfunction. Table Y-2 lists multiplying factors that, when applied to the yield strength values shown in Table Y-1, will give allowable stress values that will result in lower levels of permanent strain. G8 This material has reduced toughness at room temperature after exposure at high temperature. The degree of embrittlement depends on composition, heat treatment, time, and temperature. The lowest temperature of concern is about 250°C. See Appendix A, A-360. G9 At temperatures over 550°C, these stress intensity values apply only when the carbon is 0.04% or higher. This note is applicable only when stresses above 550°C are published. G10 For temperatures above 550°C, these stress intensity values may be used only if the material has been heat treated by heating to a minimum temperature of 1040°C and quenching in water or rapidly cooling by other means. This note is applicable only when stresses above 550°C are published. G11 These stress intensity values at temperatures of 575°C and above should be used only when assurance is provided that the steel has a predominant grain size not finer than ASTM No. 6. This note is applicable only when stresses above 550°C are published. G12 These stress intensity values shall be considered basic values to be used when no effort is made to control or check the grain size of the steel. G13 This steel may be expected to develop embrittlement after service at moderately elevated temperature; see Appendix A, A-340 and A-360. G14 All forgings shall have a maximum tensile strength not in excess of 175 MPa above the specified minimum. G15 Fabricated from SA-387 Grade 12 Class 1 plate. G16 Fabricated from SA-387 Grade 12 Class 2 plate. NOTES — HEAT TREATMENT REQUIREMENTS H1 Annealed. H2 Normalized and tempered. H3 Pieces that are formed (after quenching and tempering) at a temperature lower than 15°C below the final tempering temperature shall be heat treated after forming when the extreme fiber strain from forming exceeds 3%. Heat treatment shall be 580°C minimum, but not higher than 15°C below the final tempering temperature for a minimum time of 1 h per 25 mm of thickness. Pieces formed at temperatures within 15°C higher than the original tempering temperature shall be requenched and tempered, either before or after welding into the vessel. NOTES — SIZE REQUIREMENTS S1 The maximum thickness of forgings shall not exceed 95 mm (100 mm as heat treated). S2 Both DN 200 and larger, and schedule 140 and heavier. S3 The minimum thickness of pressure-retaining parts shall be 6 mm. S4 The minimum thickness of shells, heads, and other pressure-retaining parts shall be 6 mm. The maximum thickness shall be limited only by the ability to develop the specified mechanical properties. NOTES — WELDING REQUIREMENTS W1 Not for welded construction. W2 In welded construction, for temperatures above 450°C, the weld metal shall have a carbon content of greater than 0.05%. 323 2011a SECTION II, PART D (METRIC) NOTES TO TABLE 2A (CONT’D) NOTES — WELDING REQUIREMENTS (CONT’D) W3 The following, in addition to the variables in Section IX, QW-250, shall be considered as essential variables requiring requalification of the welding procedure. (a) An increase in the maximum or a decrease in the minimum specified preheat or interpass temperatures. The specified range of preheat temperatures shall not exceed 85°C. (b) A change in the thickness T of the welding procedure qualification test plate as follows: (1) For welded joints that are quenched and tempered after welding, any increase in thickness (the minimum thickness qualified in all cases is 6 mm). (2) For welded joints that are not quenched and tempered after welding, any change as follows: (a) for T less than 16 mm, any decrease in thickness (the maximum thickness qualified is 2T) (b) for T equal to 16 mm and over, any departure from the range of 16 mm to 2T 324 INTENTIONALLY LEFT BLANK 325 2011a SECTION II, PART D (METRIC) TABLE 2B SECTION III, DIVISION 1, CLASS 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR NONFERROUS MATERIALS # Nominal Composition Product Form Spec No. Alloy Designation/ UNS No. 1 2 3 4 … … … … Plate Plate Plate Plate SB-171 SB-171 SB-171 SB-171 C71500 C71500 C71500 C71500 M20 O25 M20 O25 64 < t ≤ 125 64 < t ≤ 125 ≤ 64 ≤ 64 34 34 34 34 5 6 7 … … … Smls. tube Smls. tube Castings SB-111 SB-111 SB-584 C71500 C71500 C93700 O61 HR50 M01 or M07 … … … 34 34 … 8 9 10 67Ni – 30Cu 67Ni – 30Cu 67Ni – 30Cu Bar, rod Smls. pipe & tube Forgings SB-164 SB-165 SB-564 N04400 N04400 N04400 Annealed Annealed Annealed … > 125 O.D. … 42 42 42 11 12 13 67Ni – 30Cu 67Ni – 30Cu 67Ni – 30Cu Plate Smls. tube Smls. pipe & tube SB-127 SB-163 SB-165 N04400 N04400 N04400 Annealed Annealed Annealed … … ≤ 125 O.D. 42 42 42 14 15 16 67Ni – 30Cu 67Ni – 30Cu 67Ni – 30Cu Bar, rod Plate Bar SB-164 SB-127 SB-164 N04400 N04400 N04400 Hot worked As rolled Hot worked … … … 42 42 42 17 18 19 20 67Ni – 30Cu 67Ni – 30Cu 67Ni – 30Cu – S 67Ni – 30Cu – S Smls. tube Smls. pipe & tube Bar, rod Bar, rod SB-163 SB-165 SB-164 SB-164 N04400 N04400 N04405 N04405 Stress rel. Stress rel. Annealed Hot worked … … … … 42 42 42 42 21 22 23 47Ni – 22Cr – 9Mo – 18Fe 47Ni – 22Cr – 9Mo – 18Fe 47Ni – 22Cr – 9Mo – 18Fe Plate Sheet Rod SB-435 SB-435 SB-572 N06002 N06002 N06002 Annealed Annealed Solution ann. 5 < t ≤ 64 1.5 < t ≤ 5 ≥5 43 43 43 24 25 26 47Ni – 22Cr – 9Mo – 18Fe 47Ni – 22Cr – 9Mo – 18Fe 47Ni – 22Cr – 9Mo – 18Fe Wld. pipe Smls. pipe & tube Wld. tube SB-619 SB-622 SB-626 N06002 N06002 N06002 Solution ann. Solution ann. Solution ann. … … … 43 43 43 27 28 29 30 31 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo Smls. & wld. fittings Forgings Forgings Rod Plate, sheet, strip SB-366 SB-462 SB-564 SB-574 SB-575 N06022 N06022 N06022 N06022 N06022 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. … … … … … 43 43 43 43 43 32 33 34 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo 55Ni – 21Cr – 13.5Mo Wld. pipe Smls. pipe & tube Wld. tube SB-619 SB-622 SB-626 N06022 N06022 N06022 Solution ann. Solution ann. Solution ann. … … … 43 43 43 35 36 37 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo Wld. fittings Smls. fittings Forgings SB-366 SB-366 SB-564 N06059 N06059 N06059 Solution ann. Solution ann. Solution ann. … … … 43 43 43 38 39 40 41 42 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo 59Ni – 23Cr – 16Mo Rod Plate, sheet, strip Wld. pipe Smls. pipe & tube Wld. tube SB-574 SB-575 SB-619 SB-622 SB-626 N06059 N06059 N06059 N06059 N06059 Solution ann. Solution ann. Solution ann. Solution ann. Solution ann. … … … … … 43 43 43 43 43 Line No. (10) 326 Class/Condition/ Temper Size/Thickness, mm P-No. 2011a SECTION II, PART D (METRIC) TABLE 2B SECTION III, DIVISION 1, CLASS 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR NONFERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Max. Temp. Limit (SPT p Supports Only) External Pressure Chart No. # Notes 1 2 3 4 310 310 345 345 125 125 140 140 260 260 260 260 NFC-4 NFC-4 NFC-4 NFC-4 G1, G4 G1, G4 G1, G4 G1, G4 5 6 7 360 495 205 125 345 83 260 260 204 (SPT) NFC-4 NFC-4 NFC-1 G1 G1 … 8 9 10 485 485 485 170 170 170 427 427 427 NFN-3 NFN-3 NFN-3 G1, G2, G4 G1, G4 G1, G2, G4 11 12 13 485 485 485 195 195 195 427 427 427 NFN-3 NFN-3 NFN-3 G1, G4 G1, G4 G1, G4 14 15 16 515 515 515 205 275 275 427 427 427 NFN-3 NFN-3 NFN-3 E2, G1 E2, G1, G4 E2, G1 17 18 19 20 585 585 485 515 380 380 170 240 260 260 427 427 NFN-3 NFN-3 NFN-3 NFN-3 G1, G4, W1 G1 G1, G2, G4 G1 21 22 23 655 655 655 240 240 240 427 427 427 NFN-15 NFN-15 NFN-15 G1, G4 G1, G4 G1, G2, G4 24 25 26 690 690 690 275 275 275 427 427 427 NFN-15 NFN-15 NFN-15 G1 G1, G4 G1 27 28 29 30 31 690 690 690 690 690 310 310 310 310 310 427 427 427 427 427 NFN-10 NFN-10 NFN-10 NFN-10 NFN-10 G1 G1 G1 G1 G1 32 33 34 690 690 690 310 310 310 427 427 427 NFN-10 NFN-10 NFN-10 G1 G1 G1 35 36 37 690 690 690 310 310 310 427 427 427 NFN-14 NFN-14 NFN-14 G1, G4 G1, G4 G1, G4 38 39 40 41 42 690 690 690 690 690 310 310 310 310 310 427 427 427 427 427 NFN-14 NFN-14 NFN-14 NFN-14 NFN-14 G1, G4 G1, G4 G1, G4 G1, G4 G1, G4 327 (10) 2011a SECTION II, PART D (METRIC) TABLE 2B SECTION III, DIVISION 1, CLASS 1 AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR NONFERROUS MATERIALS # Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding (10) Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 1 2 3 4 82.7 82.7 91.7 91.7 80.0 80.0 89.0 89.0 77.4 77.4 86.4 86.4 75.6 75.6 84.5 84.5 74.4 74.4 82.6 82.6 72.5 72.5 80.8 80.8 71.2 71.2 79.5 79.5 70.0 70.0 77.7 77.7 68.7 68.7 76.3 76.3 67.9 67.9 75.1 75.1 … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 82.7 165 55.2 80.0 165 51.1 77.4 165 47.3 75.6 165 46.8 74.4 165 45.5 72.5 162 44.8 71.2 159 44.2 70.0 156 43.6 68.7 153 … 67.9 150 … … … … … … … … … … … … … … … … … … … 8 9 10 115 115 115 106 106 106 99.7 99.7 99.7 96.1 96.1 96.1 93.7 93.7 93.7 91.8 91.8 91.8 91.1 91.1 91.1 90.4 90.4 90.4 90.3 90.3 90.3 90.3 90.3 90.3 90.3 90.3 90.3 90.3 90.3 90.3 90.2 90.2 90.2 89.5 89.5 89.5 88.9 88.9 88.9 87.7 87.7 87.7 11 12 13 129 129 129 119 119 119 112 112 112 108 108 108 105 105 105 103 103 103 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 101 99.9 99.9 99.9 98.7 98.7 98.7 14 15 16 138 172 172 136 172 172 133 172 172 131 172 172 128 171 171 126 168 168 124 165 165 122 164 164 122 162 162 121 161 161 120 160 160 119 159 159 118 158 158 117 156 156 116 144 144 106 140 140 17 18 19 20 195 195 115 161 195 195 106 151 195 195 99.7 140 195 195 96.1 136 195 195 93.7 132 195 195 91.8 129 195 195 91.1 128 195 195 90.4 128 195 195 90.3 128 195 195 90.3 128 … … 90.3 128 … … 90.3 128 … … 90.2 128 … … 89.5 127 … … 88.9 125 … … 87.7 122 21 22 23 161 161 161 151 151 151 143 143 143 138 138 138 132 132 132 127 127 127 123 123 123 119 119 119 115 115 115 112 112 112 110 110 110 107 107 107 105 105 105 104 104 104 103 103 103 101 101 101 24 25 26 184 184 184 173 173 173 164 164 164 157 157 157 151 151 151 146 146 146 141 141 141 136 136 136 132 132 132 128 128 128 125 125 125 122 122 122 120 120 120 118 118 118 117 117 117 116 116 116 27 28 29 30 31 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 … … … … … 207 207 207 207 207 … … … … … 207 207 207 207 207 … … … … … 202 202 202 202 202 … … … … … 193 193 193 193 193 189 189 189 189 189 185 185 185 185 185 182 182 182 182 182 180 180 180 180 180 177 177 177 177 177 32 33 34 176 207 176 176 207 176 176 207 176 … … … 176 207 176 … … … 176 207 176 … … … 172 202 172 … … … 164 193 164 160 189 160 157 185 157 155 182 155 153 180 153 151 177 151 35 36 37 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 202 202 202 197 197 197 192 192 192 187 187 187 183 183 183 178 178 178 38 39 40 41 42 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 207 202 202 202 202 202 197 197 197 197 197 192 192 192 192 192 187 187 187 187 187 183 183 183 183 183 178 178 178 178 178 328 INTENTIONALLY LEFT BLANK 329 2011a SECTION II, PART D (METRIC) TABLE 2B (CONT’D) SECTION III, DIVISION 1, CLASS 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR NONFERROUS MATERIALS # Nominal Composition Product Form Spec No. Alloy Designation/ UNS No. 1 2 3 4 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe Smls. pipe & tube Smls. pipe & tube Smls. tube Bar, rod SB-167 SB-167 SB-163 SB-166 N06600 N06600 N06600 N06600 Hot fin. Annealed Annealed Annealed > 125 O.D. > 125 O.D. … … 43 43 43 43 5 6 7 8 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe Smls. pipe & tube Plate Forgings Smls. tube SB-167 SB-168 SB-564 SB-163 N06600 N06600 N06600 N06600 Annealed Annealed Annealed Annealed ≤ 125 O.D. … … 6 < t ≤ 22 43 43 43 43 9 10 11 12 60Ni – 22Cr – 9Mo – 3.5Cb 60Ni – 22Cr – 9Mo – 3.5Cb 60Ni – 22Cr – 9Mo – 3.5Cb 60Ni – 22Cr – 9Mo – 3.5Cb Bar, rod Plate Smls. pipe & tube Bar, rod SB-446 SB-443 SB-444 SB-446 N06625 N06625 N06625 N06625 Annealed Annealed Annealed Annealed 100 < t ≤ 250 … … ≤ 100 43 43 43 43 13 14 15 16 58Ni – 29Cr – 9Fe 58Ni – 29Cr – 9Fe 58Ni – 29Cr – 9Fe 58Ni – 29Cr – 9Fe Smls. tube Smls. pipe & tube Plate Forgings SB-163 SB-167 SB-168 SB-564 N06690 N06690 N06690 N06690 Annealed Annealed Annealed Annealed … ≤ 125 O.D. … … 43 43 43 43 17 18 19 20 58Ni – 29Cr – 9Fe 58Ni – 29Cr – 9Fe 58Ni – 29Cr – 9Fe 58Ni – 29Cr – 9Fe Bar, rod Bar, rod Bar, rod Smls. tube SB-166 SB-166 SB-166 SB-163 N06690 N06690 N06690 N06690 Cold worked/ann. Hot worked Hot worked/ann. Annealed … … … 6 < t ≤ 22 43 43 43 43 21 22 23 42Fe – 33Ni – 21Cr 42Fe – 33Ni – 21Cr 42Fe – 33Ni – 21Cr Smls. tube Smls. pipe & tube Plate SB-163 SB-407 SB-409 N08800 N08800 N08800 Annealed Annealed Annealed … … … 45 45 45 24 25 26 27 42Fe – 33Ni – 21Cr 42Fe – 33Ni – 21Cr 42Fe – 33Ni – 21Cr 42Fe – 33Ni – 21Cr Forgings Bar, rod Smls. tube Smls. tube SB-564 SB-408 SB-163 SB-163 N08800 N08800 N08800 N08800 Annealed Hot fin. Annealed Cold worked … … 6 < t ≤ 22 … 45 45 45 45 28 29 30 31 32 42Fe – 33Ni – 21Cr 42Fe – 33Ni – 21Cr 42Fe – 33Ni – 21Cr 42Fe – 33Ni – 21Cr 42Fe – 33Ni – 21Cr Smls. tube Smls. pipe & tube Bar, rod Plate Forgings SB-163 SB-407 SB-408 SB-409 SB-564 N08810 N08810 N08810 N08810 N08810 Annealed Annealed Annealed Annealed Annealed … … … … … 45 45 45 45 45 33 34 42Ni – 21.5Cr – 5Mo – 2.3Cu 42Ni – 21.5Cr – 5Mo – 2.3Cu Smls. tube Bar, rod SB-163 SB-425 N08825 N08825 Annealed Annealed … … 45 45 35 36 37 Ti – 3Al – 2.5V Ti – 3Al – 2.5V Ti – 3Al – 2.5V Plate, sheet, strip Bar, billet Forgings SB-265 SB-348 SB-381 R56320 R56320 R56320 Annealed Annealed Annealed … … … 53 53 53 38 39 40 Ti – 3Al – 2.5V Ti – 3Al – 2.5V Ti – 3Al – 2.5V Smls. & wld. tube Wld. fittings Smls. pipe SB-338 SB-363 SB-861 R56320 R56320 R56320 Smls. ann. Smls. ann. Smls. ann. … … … 53 53 53 41 42 43 Ti – 3Al – 2.5V Ti – 3Al – 2.5V Ti – 3Al – 2.5V Smls. & wld. tube Wld. fittings Wld. pipe SB-338 SB-363 SB-862 R56320 R56320 R56320 Wld. ann. Wld. ann. Wld. ann. … … … 53 53 53 Line No. 330 Class/Condition/ Temper Size/Thickness, mm P-No. 2011a SECTION II, PART D (METRIC) TABLE 2B (CONT’D) SECTION III, DIVISION 1, CLASS 1 AND MC, AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR NONFERROUS MATERIALS Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Max. Temp. Limit (SPT p Supports Only) External Pressure Chart No. # Notes 1 2 3 4 515 550 550 550 170 205 240 240 427 427 427 427 NFN-4 NFN-4 NFN-4 NFN-4 G1 G1, G4 G1, G4 G1, G2, G4 5 6 7 8 550 550 550 550 240 240 240 275 427 427 427 427 NFN-4 NFN-4 NFN-4 NFN-21 G1, G4 G1, G4 G1, G2, G4 G1, G3, S1 9 10 11 12 760 760 825 825 345 380 415 415 427 427 427 427 NFN-17 NFN-17 NFN-17 NFN-17 … … … … 13 14 15 16 585 585 585 585 240 240 240 240 427 427 427 427 NFN-4 NFN-4 NFN-4 NFN-4 G1 G1 G1 G1 17 18 19 20 585 585 585 585 240 240 240 275 427 427 427 427 NFN-4 NFN-4 NFN-4 NFN-21 G1 G1 G1 G1, G3, S1 21 22 23 515 515 515 205 205 205 427 427 427 NFN-8 NFN-8 NFN-8 G1, G4 G1, G4 G1, G4 24 25 26 27 515 515 515 570 205 205 275 325 427 427 427 343 NFN-8 NFN-8 NFN-8 NFN-23 G1, G2, G4 G1, G2, G4 G1, G3, S1 G1 28 29 30 31 32 450 450 450 450 450 170 170 170 170 170 427 427 427 427 427 NFN-9 NFN-9 NFN-9 NFN-9 NFN-9 G1, G4 G1, G4 G1, G2, G4 G1, G4 G1, G2, G4 33 34 585 585 240 240 427 427 NFN-7 NFN-7 G1, G4 G2, G4 35 36 37 620 620 620 485 485 485 316 316 316 NFT-4 NFT-4 NFT-4 … … … 38 39 40 620 620 620 485 485 485 316 316 316 NFT-4 NFT-4 NFT-4 … … … 41 42 43 620 620 620 485 485 485 316 316 316 NFT-4 NFT-4 NFT-4 G5 G5 G5 331 2011a SECTION II, PART D (METRIC) TABLE 2B (CONT’D) SECTION III, DIVISION 1, CLASS 1 AND SECTION III, DIVISION 3, CLASSES TC AND SC DESIGN STRESS INTENSITY VALUES Sm FOR NONFERROUS MATERIALS # Design Stress Intensity, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 1 2 3 4 115 138 161 161 115 138 161 161 115 138 161 161 115 138 161 161 115 138 161 161 115 138 161 161 115 138 161 161 115 138 161 161 115 138 161 161 115 138 161 161 115 138 161 161 115 138 161 161 115 138 161 161 115 138 161 161 115 138 161 161 115 138 161 161 5 6 7 8 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 9 10 11 12 230 253 276 276 225 247 270 270 221 243 265 265 218 239 261 261 215 236 258 258 212 233 254 254 209 230 251 251 206 227 248 248 204 224 245 245 201 221 242 242 199 219 239 239 197 216 236 236 194 214 233 233 192 212 231 231 191 210 229 229 189 208 227 227 13 14 15 16 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 17 18 19 20 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 184 161 161 161 183 161 161 161 183 161 161 161 182 21 22 23 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 24 25 26 27 138 138 172 191 138 138 172 191 138 138 172 191 138 138 172 191 138 138 172 191 138 138 172 191 138 138 172 190 138 138 172 188 138 138 172 186 138 138 172 185 138 138 172 184 138 138 171 183 138 138 171 183 138 138 171 … 138 138 170 … 138 138 170 … 28 29 30 31 32 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 115 113 113 113 113 113 110 110 110 110 110 108 108 108 108 108 105 105 105 105 105 104 104 104 104 104 33 34 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 161 160 160 159 159 35 36 37 207 207 207 207 207 207 197 197 197 190 190 190 182 182 182 173 173 173 164 164 164 155 155 155 148 148 148 143 143 143 140 140 140 138 138 138 … … … … … … … … … … … … 38 39 40 207 207 207 207 207 207 197 197 197 190 190 190 182 182 182 173 173 173 164 164 164 155 155 155 148 148 148 143 143 143 140 140 140 138 138 138 … … … … … … … … … … … … 41 42 43 176 176 176 176 176 176 167 167 167 161 161 161 154 154 154 147 147 147 139 139 139 132 132 132 126 126 126 122 122 122 119 119 119 117 117 117 … … … … … … … … … … … … 332 2011a SECTION II, PART D (METRIC) NOTES TO TABLE 2B (10) (10) GENERAL NOTES (a) The following abbreviations are used: ann., annealed; fin., finished; rel., relieved; Smls., Seamless; and Wld., Welded. (b) An alternative typeface is used for stress values based on successful experience in service (see Notes E1 and E2). (c) Where specifications, grades, classes, and types are listed in this Table, and where the material specification in Section II, Part A or Part B is a dual-unit specification (e.g., SB-407/SB-407M), the values listed in this Table shall be applicable to either the customary U.S. version of the material specification or the SI units version of the material specification. For example, the values listed for SB-407 Grade N08800 shall be used when SB-407M Grade N08800 is used in construction. (d) The values in this Table may be interpolated to determine values for intermediate temperatures. The values at intermediate temperatures shall be rounded to the same number of decimal places as the value at the higher temperature between which values are being interpolated. The rounding rule is: when the next digit beyond the last place to be retained is less than 5, retain unchanged the digit in the last place retained; when the digit next beyond the last place to be retained is 5 or greater, increase by 1 the digit in the last place retained. (e) The properties of steels are influenced by the processing history, heat treatment, melting practice, and level of residual elements. See Nonmandatory Appendix A for more information. NOTES — EXPERIENCE CRITERION E1 DELETED. E2 For values at 425°C, the design stress intensity values are based on successful experience in service. NOTES — GENERAL REQUIREMENTS G1 Due to the relatively low yield strength of these materials, these higher stress values were established at temperatures where the shorttime tensile properties govern to permit the use of these alloys where slightly greater deformation is acceptable. The stress values in this range exceed 662⁄3% but do not exceed 90% of the yield strength at temperature. Use of these stresses may result in dimensional changes due to permanent strain. These stress values are not recommended for the flanges of gasketed joints or other applications where slight amounts of distortion can cause leakage or malfunction. Table Y-2 lists multiplying factors that, when applied to the yield strength values shown in Table Y-1, will give allowable stress values that will result in lower levels of permanent strain. G2 Use of external pressure charts for material in the form of bar stock is permitted for stiffening rings only. G3 SB-163 Supplementary Requirement S2 shall be met. G4 Design stress intensity values for 40°C may be used at temperatures down to −200°C without additional specification requirements. G5 A joint efficiency factor of 0.85 has been applied in arriving at the maximum allowable design stress intensity values for this material. NOTES — SIZE REQUIREMENTS S1 Thickness ≤ 2.5 mm. NOTES — WELDING REQUIREMENTS W1 Welding except for seal welds is not permitted. 333 2011a SECTION II, PART D (METRIC) TABLE 3 SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Line No. Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. Class/ Condition/ Temper Size/Thickness, mm Ferrous Materials (10) (10) (10) (10) (10) 1 2 3 4 5 6 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Bolting Bolting Bolting Bolting Bolting Bolting SA-307 SA-449 SA-325 SA-325 SA-449 SA-354 B 1 … 1 1 BC … K04200 … K02706 K04200 K04100 … … … … … … … 38 < t ≤ 75 … 32 < t ≤ 38 25 < t ≤ 38 64 < t ≤ 100 7 8 9 10 11 Carbon steel Carbon steel Carbon steel Carbon steel Carbon steel Bolting Bolting Bolting Bolting Bolting SA-325 SA-449 SA-354 SA-354 SA-354 1 1 BC BD BD K02706 K04200 K04100 K04100 K04100 … … … … … 13 < t ≤ 25 ≤ 25 6 < t ≤ 64 64 < t ≤ 100 6 < t ≤ 64 12 13 14 15 16 17 C – 1⁄4Mo C – 1⁄4Mo C – 1⁄4Mo C – 1⁄4Mo C – 1⁄4Mo … Bolting Bolting Bolting Bolting Bolting … SA-320 SA-574 SA-574 SA-574 SA-574 … L7A 4037 4042 4037 4042 … G40370 G40370 G40420 G40370 G40420 … … … … … … … ≤ 64 ≥ 16 ≥ 16 ≤ 13 ≤ 13 … 18 19 20 21 3 ⁄4Cr ⁄4Cr 3 ⁄4Cr 3 ⁄4Cr Bolting Bolting Bolting Bolting SA-574 SA-574 SA-574 SA-574 5137M 51B37M 5137M 51B37M … … … … … … … … ≥ 16 ≥ 16 ≤ 13 ≤ 13 22 23 24 25 26 27 1Cr – 1Mn – 1⁄4Mo 1Cr – 1Mn – 1⁄4Mo 1Cr – 1Mn – 1⁄4Mo 1Cr – 1Mn – 1⁄4Mo 1Cr – 1Mn – 1⁄4Mo 1Cr – 1Mn – 1⁄4Mo Bolting Bolting Bolting Bolting Bolting Bolting SA-540 SA-540 SA-540 SA-540 SA-540 SA-540 B22 B22 B22 B22 B22 B22 H41420 H41420 H41420 H41420 H41420 H41420 5 5 4 3 2 1 50 < t ≤ 100 ≤ 50 ≤ 100 ≤ 100 ≤ 75 ≤ 38 28 29 30 1Cr – 1⁄5Mo 1Cr – 1⁄5Mo 1Cr – 1⁄5Mo Bolting Bolting Bolting SA-193 SA-193 SA-320 B7 B7M L7M G41400 G41400 G41400 … … … 100 < t ≤ 175 ≤ 64 ≤ 64 31 32 33 1Cr – 1⁄5Mo 1Cr – 1⁄5Mo 1Cr – 1⁄5Mo Bolting Bolting Bolting SA-193 SA-193 SA-320 B7 B7 L7 G41400 G41400 G41400 … … … 64 < t ≤ 100 ≤ 64 ≤ 64 34 35 36 37 1Cr – 1⁄5Mo 1Cr – 1⁄5Mo 1Cr – 1⁄5Mo 1Cr – 1⁄5Mo Bolting Bolting Bolting Bolting SA-574 SA-574 SA-574 SA-574 4137 4140 4142 4145 G41370 G41400 G41420 G41450 … … … … ≥ 16 ≥ 16 ≥ 16 ≥ 16 3 334 2011a SECTION II, PART D (METRIC) TABLE 3 SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) III VIII-1 VIII-2 XII Notes Ferrous Materials 1 2 3 4 5 6 415 620 725 725 725 795 … 400 560 560 560 685 204 371 343 NP 371 343 232 343 343 343 371 343 NP 343 343 343 371 343 232 343 NP 343 343 343 … … … … … … 7 8 9 10 11 825 825 860 965 1035 635 635 750 795 895 NP 371 343 343 343 343 343 343 343 343 343 343 343 343 343 343 343 343 343 343 … … … … … 12 13 14 15 16 17 860 1170 1170 1240 1240 … 725 930 930 965 965 … NP 288 288 288 288 … 343 288 288 288 288 … 343 NP NP NP NP … 343 288 288 288 288 … W3 G7, G11, W1 G7, G11, W1 G7, G11, W1 G7, G11, W1 … 18 19 20 21 1170 1170 1240 1240 930 930 965 965 288 288 288 288 288 288 288 288 NP NP NP NP NP NP NP NP G7, G11, W1 G7, G11, W1 G7, G11, W1 G7, G11, W1 22 23 24 25 26 27 795 825 930 1000 1070 1140 690 725 825 895 965 1035 371 371 371 371 371 371 NP NP NP 371 NP NP NP NP NP NP NP NP NP NP NP 343 NP NP … … … … … … 28 29 30 690 690 690 515 550 550 427 NP NP 538 538 538 427 427 427 343 343 343 … … … 31 32 33 795 860 860 655 725 725 427 427 371 538 538 427 427 427 427 343 343 343 … … … 34 35 36 37 1170 1170 1170 1170 930 930 930 930 288 288 288 288 NP 288 NP NP NP NP NP NP NP 288 NP NP G7, G11, W1 G7, G11, W1 G7, G11, W1 G7, G11, W1 335 (10) (10) (10) (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 3 SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 Ferrous Materials (10) (10) (10) (10) (10) 1 2 3 4 5 6 48.3 100 139 139 139 159 48.3 100 139 139 139 159 48.3 100 139 139 139 159 48.3 100 139 139 139 159 48.3 100 139 139 139 159 48.3 100 139 139 139 159 48.3 100 139 139 139 159 48.3 100 139 139 139 159 48.3 100 139 139 139 159 … 100 139 139 139 159 … 100 139 139 139 159 … 100 139 139 139 159 … 100 139 139 139 159 … 100 … … 139 … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 10 11 159 159 172 193 207 159 159 172 193 207 159 159 172 193 207 159 159 172 193 207 159 159 172 193 207 159 159 172 193 207 159 159 172 193 207 159 159 172 193 207 159 159 172 193 207 159 159 172 193 207 159 159 172 193 207 159 159 172 193 207 159 159 172 193 207 … 159 … … … … … … … … … … … … … … … … … … … … … … … 12 13 14 15 16 17 172 233 233 241 241 … 172 233 233 241 241 … 172 233 233 241 241 … 172 233 233 241 241 … 172 233 233 241 241 … 172 233 233 241 241 … 172 233 233 241 241 … 172 233 233 241 241 … 172 233 233 241 241 … 172 233 233 241 241 … 172 233 233 241 241 … 172 … … … … … 172 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 18 19 20 21 233 233 241 241 233 233 241 241 233 233 241 241 233 233 241 241 233 233 241 241 233 233 241 241 233 233 241 241 233 233 241 241 233 233 241 241 233 233 241 241 233 233 241 241 … … … … … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 25 26 27 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 130 138 138 130 138 138 130 138 138 130 138 138 130 138 138 130 138 138 130 138 138 130 138 138 130 138 138 130 138 138 130 138 138 130 138 138 130 138 138 130 138 138 130 138 138 125 128 128 115 115 115 93.7 93.6 93.6 31 32 33 159 172 172 159 172 172 159 172 172 159 172 172 159 172 172 159 172 172 159 172 172 159 172 172 159 172 172 159 172 172 159 172 172 159 172 172 159 172 172 158 172 172 153 162 162 139 146 146 117 118 118 93.0 92.7 … 34 35 36 37 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 233 … … … … … … … … … … … … … … … … … … … … … … … … … … … … 336 2011a SECTION II, PART D (METRIC) TABLE 3 SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 Ferrous Materials 1 2 3 4 5 6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 10 11 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 12 13 14 15 16 17 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 18 19 20 21 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 22 23 24 25 26 27 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 28 29 30 68.4 68.4 68.4 43.8 43.7 43.7 18.9 18.9 18.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 68.6 68.8 … 43.7 43.6 … 18.9 18.9 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 34 35 36 37 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 337 (10) (10) (10) (10) (10) 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Line No. Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. Class/ Condition/ Temper Size/Thickness, mm Ferrous Materials (Cont’d) 1 2 3 4 1Cr – 1⁄5Mo 1Cr – 1⁄5Mo 1Cr – 1⁄5Mo 1Cr – 1⁄5Mo Bolting Bolting Bolting Bolting SA-574 SA-574 SA-574 SA-574 4137 4140 4142 4145 G41370 G41400 G41420 G41450 … … … … ≤ 13 ≤ 13 ≤ 13 ≤ 13 5 6 7 8 9 1Cr – 1⁄2Mo – V 1Cr – 1⁄2Mo – V 1Cr – 1⁄2Mo – V 1Cr – 1⁄2Mo – V 1Cr – 1⁄2Mo – V Bolting Bolting Bolting Bolting Bolting SA-193 SA-193 SA-540 SA-540 SA-193 B16 B16 B21 B21 B16 K14072 K14072 K14073 K14073 K14072 … … 5 5 … 100 < t ≤ 175 64 < t ≤ 100 50 < t ≤ 200 ≤ 50 ≤ 64 10 11 12 13 1Cr – 1⁄2Mo – V 1Cr – 1⁄2Mo – V 1Cr – 1⁄2Mo – V 1Cr – 1⁄2Mo – V Bolting Bolting Bolting Bolting SA-540 SA-540 SA-540 SA-540 B21 B21 B21 B21 K14073 K14073 K14073 K14073 4 3 2 1 ≤ 150 ≤ 150 ≤ 100 ≤ 100 14 15 16 5Cr – 1⁄2Mo 12Cr – 1Mo – V – W 12Cr – 1Mo – V – W Bolting Bolting Bolting SA-193 SA-437 SA-437 B5 B4C B4B K50100 K91352 K91352 … … … ≤ 100 … … 17 18 19 20 13Cr 17Cr – 4Ni – 4Cu 17Cr – 4Ni – 4Cu 17Cr – 4Ni – 4Cu Bolting Bolting Bolting Bolting SA-193 SA-564 SA-564 SA-705 B6 630 630 630 S41000 S17400 S17400 S17400 … H1150 H1100 H1100 ≤ 100 ≤ 200 ≤ 200 ≤ 200 21 22 23 24 25 1 ⁄2Ni – 1⁄2Cr – 1⁄4Mo ⁄2Ni – 1⁄2Cr – 1⁄4Mo 13⁄4Ni – 3⁄4Cr – 1⁄4Mo 13⁄4Ni – 3⁄4Cr – 1⁄4Mo 13⁄4Ni – 3⁄4Cr – 1⁄4Mo Bolting Bolting Bolting Bolting Bolting SA-574 SA-574 SA-320 SA-574 SA-574 8740 8740 L43 4340 4340 G87400 G87400 G43400 G43400 G43400 … … … … … ≥ 16 ≤ 13 ≤ 100 ≥ 16 ≤ 13 26 27 28 29 30 31 2Ni – 3⁄4Cr – 1⁄4Mo 2Ni – 3⁄4Cr – 1⁄4Mo 2Ni – 3⁄4Cr – 1⁄4Mo 2Ni – 3⁄4Cr – 1⁄4Mo 2Ni – 3⁄4Cr – 1⁄4Mo 2Ni – 3⁄4Cr – 1⁄4Mo Bolting Bolting Bolting Bolting Bolting Bolting SA-540 SA-540 SA-540 SA-540 SA-540 SA-540 B23 B23 B23 B23 B23 B23 H43400 H43400 H43400 H43400 H43400 H43400 5 5 4 3 2 1 … … … … … … 32 33 34 35 36 37 2Ni – 3⁄4Cr – 1⁄3Mo 2Ni – 3⁄4Cr – 1⁄3Mo 2Ni – 3⁄4Cr – 1⁄3Mo 2Ni – 3⁄4Cr – 1⁄3Mo 2Ni – 3⁄4Cr – 1⁄3Mo 2Ni – 3⁄4Cr – 1⁄3Mo Bolting Bolting Bolting Bolting Bolting Bolting SA-540 SA-540 SA-540 SA-540 SA-540 SA-540 B24 B24 B24 B24 B24 B24 K24064 K24064 K24064 K24064 K24064 K24064 5 5 4 3 2 1 … … … … … … 1 338 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) III VIII-1 VIII-2 XII Notes Ferrous Materials (Cont’d) 1 2 3 4 1240 1240 1240 1240 965 965 965 965 288 288 288 288 NP NP NP NP NP NP NP NP NP NP NP NP G7, G11, W1 G7, G11, W1 G7, G11, W1 G7, G11, W1 5 6 7 8 9 690 760 795 825 860 585 655 690 725 725 427 427 371 371 427 593 593 371 371 593 427 427 371 371 427 343 343 NP NP 343 … … … … … 10 11 12 13 930 1000 1070 1140 825 895 965 1035 371 371 371 371 371 371 371 371 371 371 371 371 343 343 343 343 … … … … 14 15 16 690 795 1000 550 585 725 427 371 371 649 371 371 427 371 371 343 343 343 … … … 17 18 19 20 760 930 965 965 585 725 795 795 427 NP 343 343 482 343 343 343 427 343 343 343 343 NP 343 343 … G4 G4 G4 21 22 23 24 25 1170 1240 860 1170 1240 930 965 725 930 965 288 288 204 288 288 NP NP 204 288 288 NP NP 371 NP NP NP NP 204 NP NP G7, G11, W1 G7, G11, W1 … G7, G11, W1 G7, G11, W1 26 27 28 29 30 31 795 825 930 1000 1070 1140 690 725 825 895 965 1035 371 371 371 371 371 371 371 371 371 371 371 371 371 371 371 371 371 371 343 343 343 343 343 343 … … … … … … 32 33 34 35 36 37 795 825 930 1000 1070 1140 690 725 825 895 965 1035 371 371 371 371 371 371 371 371 371 371 371 371 371 371 371 371 371 371 343 343 343 343 343 343 … … … … … … 339 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 Ferrous Materials (Cont’d) 1 2 3 4 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 241 … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 9 138 152 159 165 172 138 152 159 165 172 138 152 159 165 172 138 152 159 165 172 138 152 159 165 172 138 152 159 165 172 138 152 159 165 172 138 152 159 165 172 138 152 159 165 172 138 152 159 165 172 138 152 159 165 172 138 152 159 165 172 138 152 159 165 172 138 152 159 165 172 138 152 … … 172 138 152 … … 172 132 147 … … 164 119 133 … … 148 10 11 12 13 186 200 214 228 186 200 214 228 186 200 214 228 186 200 214 228 186 200 214 228 186 200 214 228 186 200 214 228 186 200 214 228 186 200 214 228 186 200 214 228 186 200 214 228 186 200 214 228 186 200 214 228 186 200 214 228 … … … … … … … … … … … … … … … … 14 15 16 138 147 181 138 147 181 138 147 181 138 147 181 138 147 181 138 147 181 138 147 181 138 147 181 138 147 181 138 147 181 138 147 181 138 147 181 138 147 181 138 147 181 138 … … 129 … … 105 … … 78.3 … … 17 18 19 20 147 181 193 193 147 181 193 193 147 181 193 193 147 181 193 193 147 181 193 193 147 181 193 193 147 181 193 193 147 181 193 193 147 181 193 193 147 181 193 193 147 181 193 193 147 181 193 193 147 181 193 193 147 … … … 147 … … … 147 … … … 125 … … … 92.4 … … … 21 22 23 24 25 233 241 172 233 241 233 241 172 233 241 233 241 172 233 241 233 241 172 233 241 233 241 172 233 241 233 241 172 233 241 233 241 172 233 241 233 241 172 233 241 233 241 172 233 241 233 241 172 233 241 233 241 172 233 241 … … 172 … … … … 172 … … … … 172 … … … … … … … … … … … … … … … … … … … … … … 26 27 28 29 30 31 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 37 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 159 165 186 200 214 228 … … … … … … … … … … … … … … … … … … … … … … … … 340 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 Ferrous Materials (Cont’d) 1 2 3 4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 9 105 114 … … 122 87.7 90.4 … … 91.8 61.7 61.1 … … 60.8 34.3 34.5 … … 34.6 13.8 13.7 … … 13.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 10 11 12 13 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 14 15 16 58.5 … … 44.4 … … 33.9 … … 26.3 … … 19.5 … … 13.0 … … 8.79 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 17 18 19 20 68.4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 24 25 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 26 27 28 29 30 31 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 36 37 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 341 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Line No. Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. Class/ Condition/ Temper Size/Thickness, mm Ferrous Materials (Cont’d) 1 2 3 4 2Ni – 3⁄4Cr – 1⁄3Mo – V 31⁄2Ni – 13⁄4Cr – 1⁄2Mo – V 25Ni – 15Cr – 2Ti 25Ni – 15Cr – 2Ti Bolting Forgings Bolting Bolting SA-540 SA-508 SA-453 SA-453 B24V 5 660 660 K24070 K42365 S66286 S66286 3 2 A B ≤ 275 … … … 5 6 7 8 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Bolting Bolting Bolting Bolting SA-193 SA-320 SA-320 SA-193 B8M B8M B8MA B8M2 S31600 S31600 S31600 S31600 1 1 1A … … … … 64 < t ≤ 75 9 10 11 12 13 14 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo Bolting Bolting Bolting Bolting Bolting Bolting SA-193 SA-320 SA-193 SA-193 SA-320 SA-193 B8M B8M B8M2 B8M B8M B8M2 S31600 S31600 S31600 S31600 S31600 S31600 2 2 … 2 2 … 32 < t ≤ 38 32 < t ≤ 38 50 < t ≤ 64 25 < t ≤ 32 25 < t ≤ 32 ≤ 50 15 16 17 18 19 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo 16Cr – 12Ni – 2Mo – N Bolting Bolting Bolting Bolting Bolting SA-193 SA-320 SA-193 SA-320 SA-193 B8M B8M B8M B8M B8MNA S31600 S31600 S31600 S31600 S31651 2 2 2 2 1A 19 < t ≤ 25 19 < t ≤ 25 ≤ 19 ≤ 19 … 20 21 22 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Bolting Bolting Bolting SA-193 SA-320 SA-320 B8 B8 B8A S30400 S30400 S30400 1 1 1A … … … 23 24 25 26 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Bolting Bolting Bolting Bolting SA-193 SA-320 SA-193 SA-320 B8 B8 B8 B8 S30400 S30400 S30400 S30400 2 2 2 2 32 < t ≤ 38 32 < t ≤ 38 25 < t ≤ 32 25 < t ≤ 32 27 28 29 30 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni 18Cr – 8Ni Bolting Bolting Bolting Bolting SA-193 SA-320 SA-193 SA-320 B8 B8 B8 B8 S30400 S30400 S30400 S30400 2 2 2 2 19 < t ≤ 25 19 < t ≤ 25 ≤ 19 ≤ 19 31 32 33 34 35 18Cr – 8Ni – N 18Cr – 8Ni – S 18Cr – 8Ni – S 18Cr – 8Ni – 4Si – N 18Cr – 8Ni – 4Si – N Bolting Bolting Bolting Bolting Bolting SA-193 SA-320 SA-320 SA-193 SA-193 B8NA B8F B8FA B8S B8SA S30451 S30323 S30323 S21800 S21800 1A 1 1A … … … … … … … 36 37 38 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Bolting Bolting Bolting SA-193 SA-320 SA-320 B8C B8C B8CA S34700 S34700 S34700 1 1 1A … … … 342 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) III VIII-1 VIII-2 XII Notes Ferrous Materials (Cont’d) 1 2 3 4 1000 795 895 895 895 690 585 585 371 NP 427 427 371 38 538 538 371 38 427 427 343 38 343 343 … … … … 5 6 7 8 515 515 515 550 205 205 205 380 427 204 NP NP 816 38 38 538 427 38 38 427 343 38 38 343 G5, G6 … … G9 9 10 11 12 13 14 620 620 620 655 655 655 345 345 450 450 450 515 427 NP NP 427 NP NP 427 38 538 427 38 538 NP 38 427 NP 38 427 343 38 343 343 38 343 G8 G8, G9 G9 G8 G8 G9 15 16 17 18 19 690 690 760 760 515 550 550 655 655 205 427 NP 427 NP 427 427 38 427 38 538 NP 38 NP 38 427 343 38 343 38 343 G8 G8 G8 G8 G5 20 21 22 515 515 515 205 205 205 427 204 NP 816 38 38 427 38 38 343 38 38 G5, G6 … … 23 24 25 26 690 690 725 725 345 345 450 450 NP NP NP NP 538 538 538 538 427 427 427 427 343 38 343 38 G8, G9 G8 G8, G9 G8 27 28 29 30 795 795 860 860 550 550 690 690 NP NP NP NP 538 538 538 538 427 427 427 427 343 38 343 38 G8, G9 G8 G8, G9 G8 31 32 33 34 35 515 515 515 655 655 205 205 205 345 345 427 204 NP NP NP 538 38 38 510 510 427 38 38 427 427 343 38 38 343 343 G5 … … … … 36 37 38 515 515 515 205 205 205 427 204 NP 816 38 38 427 38 38 343 38 38 G5, G6 … … 343 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 Ferrous Materials (Cont’d) 1 2 3 4 200 159 147 147 200 … 147 147 200 … 147 147 200 … 147 147 200 … 147 147 200 … 147 147 200 … 147 147 200 … 147 147 200 … 147 147 200 … 147 147 200 … 147 147 200 … 147 147 200 … 147 147 200 … 147 147 … … 147 147 … … 147 147 … … 147 147 … … 147 147 5 6 7 8 130 130 130 130 127 127 … 127 121 121 … 121 114 114 … 114 107 107 … 107 103 103 … 102 99.2 99.2 … 99.1 95.9 95.9 … 96.7 92.8 … … 95.4 90.2 … … 95.1 88.1 … … 95.1 86.1 … … 95.1 84.4 … … 95.1 83.2 … … 95.1 82.0 … … 95.1 80.7 … … 95.1 80.1 … … 95.1 79.5 … … 95.1 9 10 11 12 13 14 130 130 130 130 130 130 127 … 127 127 … 130 121 … 121 121 … 130 114 … 115 115 … 130 107 … 112 112 … 130 103 … 112 112 … 130 99.2 … 112 112 … 130 96.0 … 112 112 … 130 92.9 … 112 112 … 130 90.1 … 112 112 … 130 87.8 … 112 112 … 130 86.5 … 112 112 … 130 86.2 … 112 112 … 130 86.2 … 112 112 … 130 86.2 … 112 112 … 130 86.2 … 112 112 … 130 86.2 … 112 112 … 130 … … 112 … … 130 15 16 17 18 19 138 138 152 152 130 138 … 152 … 127 138 … 152 … 122 138 … 152 … 117 138 … 152 … 112 138 … 152 … 108 138 … 152 … 105 138 … 152 … 102 138 … 152 … 99.1 138 … 152 … 96.2 138 … 152 … 93.7 138 … 152 … 91.7 138 … 152 … 89.8 138 … 152 … 87.9 138 … 152 … 86.1 138 … 152 … 84.9 138 … 152 … 83.0 … … … … 81.7 20 21 22 130 130 130 122 122 … 114 114 … 108 108 … 103 103 … 99.1 99.1 … 95.7 95.7 … 92.8 92.8 … 90.1 … … 87.2 … … 84.5 … … 83.1 … … 82.5 … … 81.1 … … 79.2 … … 77.3 … … 76.0 … … 74.8 … … 23 24 25 26 130 130 130 130 122 122 121 121 114 114 115 115 108 108 114 114 103 103 112 112 99.2 99.2 112 112 95.7 95.7 112 112 92.6 92.6 112 112 89.9 89.9 112 112 87.8 87.8 112 112 86.5 86.5 112 112 86.2 86.2 112 112 86.2 86.2 112 112 86.2 86.2 112 112 86.2 86.2 112 112 86.2 86.2 112 112 86.2 86.2 112 112 86.2 86.2 112 112 27 28 29 30 138 138 172 172 138 138 172 172 138 138 172 172 138 138 172 172 138 138 172 172 138 138 172 172 138 138 172 172 138 138 172 172 138 138 172 172 138 138 172 172 138 138 172 172 138 138 172 172 138 138 172 172 138 138 172 172 138 138 172 172 138 138 172 172 138 138 172 172 138 138 172 172 31 32 33 34 35 130 130 130 164 164 122 115 … 163 163 112 101 … 160 160 105 96.6 … 156 156 99.0 93.6 … 150 150 93.8 90.6 … 143 143 89.6 87.4 … 137 137 86.3 84.3 … 132 132 83.7 … … 129 129 81.4 … … 126 126 79.6 … … 123 123 78.1 … … 121 121 76.9 … … 119 119 75.6 … … 118 118 74.4 … … 116 116 73.2 … … 115 115 71.9 … … 115 115 70.8 … … 115 115 36 37 38 130 130 130 127 127 … 122 122 … 118 118 … 113 113 … 109 109 … 107 107 … 106 106 … 104 … … 102 … … 99.7 … … 98.1 … … 96.7 … … 95.0 … … 94.4 … … 93.8 … … 93.1 … … 93.1 … … 344 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 Ferrous Materials (Cont’d) 1 2 3 4 … … 147 147 … … 147 147 … … 147 147 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 78.8 … … 95.1 78.2 … … 95.1 77.6 … … 95.1 77.1 … … … 74.7 … … … 65.5 … … … 50.4 … … … 38.6 … … … 29.6 … … … 23.0 … … … 17.7 … … … 13.4 … … … 10.4 … … … 8.05 … … … … … … … … … … … … … … … 9 10 11 12 13 14 … … 112 … … 130 … … 112 … … 130 … … 112 … … 130 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 15 16 17 18 19 … … … … 80.5 … … … … 79.2 … … … … 78.0 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 73.6 … … 72.4 … … 70.8 … … 68.9 … … 65.4 … … 51.0 … … 41.0 … … 32.9 … … 26.5 … … 21.3 … … 17.2 … … 13.9 … … 11.1 … … 8.73 … … … … … … … … … … … 23 24 25 26 86.2 86.2 112 112 86.2 86.2 112 112 86.2 86.2 112 112 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 27 28 29 30 138 138 172 172 138 138 169 169 138 138 164 164 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 31 32 33 34 35 69.0 … … 115 115 67.4 … … 115 115 66.3 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 36 37 38 92.6 … … 92.4 … … 90.3 … … 77.2 … … 57.3 … … 39.9 … … 30.0 … … 23.2 … … 16.3 … … 11.2 … … 8.93 … … 7.08 … … 5.77 … … 5.32 … … … … … … … … … … … 345 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Line No. Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. Class/ Condition/ Temper Size/Thickness, mm Ferrous Materials (Cont’d) 1 2 3 4 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Bolting Bolting Bolting Bolting SA-193 SA-320 SA-193 SA-320 B8C B8C B8C B8C S34700 S34700 S34700 S34700 2 2 2 2 32 < t ≤ 38 32 < t ≤ 38 25 < t ≤ 32 25 < t ≤ 32 5 6 7 8 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb 18Cr – 10Ni – Cb Bolting Bolting Bolting Bolting SA-193 SA-320 SA-193 SA-320 B8C B8C B8C B8C S34700 S34700 S34700 S34700 2 2 2 2 19 < t ≤ 25 19 < t ≤ 25 ≤ 19 ≤ 19 9 10 11 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Bolting Bolting Bolting SA-193 SA-320 SA-320 B8T B8T B8TA S32100 S32100 S32100 1 1 1A … … … 12 13 14 15 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Bolting Bolting Bolting Bolting SA-193 SA-320 SA-193 SA-320 B8T B8T B8T B8T S32100 S32100 S32100 S32100 2 2 2 2 32 < t ≤ 38 32 < t ≤ 38 25 < t ≤ 32 25 < t ≤ 32 16 17 18 19 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti 18Cr – 10Ni – Ti Bolting Bolting Bolting Bolting SA-193 SA-320 SA-193 SA-320 B8T B8T B8T B8T S32100 S32100 S32100 S32100 2 2 2 2 19 < t ≤ 25 19 < t ≤ 25 ≤ 19 ≤ 19 20 21 22 23 24 18Cr – 11Ni 18Cr – 11Ni 18Cr – 11Ni 18Cr – 11Ni 18Cr – 11Ni Bolting Bolting Bolting Bolting Bolting SA-193 SA-193 SA-193 SA-193 SA-193 B8P B8P B8P B8P B8P S30500 S30500 S30500 S30500 S30500 1 2 2 2 2 … 32 < t ≤ 38 25 < t ≤ 32 19 < t ≤ 25 ≤ 19 25 26 27 28 19Cr – 9Ni – Mo – W 19Cr – 9Ni – Mo – W 19Cr – 9Ni – Mo – W 19Cr – 9Ni – Mo – W Bolting Bolting Bolting Bolting SA-453 SA-453 SA-453 SA-453 651 651 651 651 S63198 S63198 S63198 S63198 B B B B > 75 > 75 ≤ 75 ≤ 75 29 30 31 32 19Cr – 9Ni – Mo – W 19Cr – 9Ni – Mo – W 19Cr – 9Ni – Mo – W 19Cr – 9Ni – Mo – W Bolting Bolting Bolting Bolting SA-453 SA-453 SA-453 SA-453 651 651 651 651 S63198 S63198 S63198 S63198 A A A A > 75 > 75 ≤ 75 ≤ 75 33 34 35 36 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn 22Cr – 13Ni – 5Mn Bolting Bolting Bolting Bolting SA-479 SA-479 SA-479 SA-479 XM-19 XM-19 XM-19 XM-19 S20910 S20910 S20910 S20910 Annealed Hot rolled Hot rolled Hot rolled … 75 < t ≤ 200 50 < t ≤ 75 ≤ 50 346 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) III VIII-1 VIII-2 XII Notes Ferrous Materials (Cont’d) 1 2 3 4 690 690 725 725 345 345 450 450 NP NP NP NP 38 38 38 38 38 38 38 38 38 38 38 38 G8 G8 G8 G8 5 6 7 8 795 795 860 860 550 550 690 690 NP NP NP NP 38 38 38 38 38 38 38 38 38 38 38 38 G8 G8 G8 G8 9 10 11 515 515 515 205 205 205 427 204 NP 816 38 38 427 38 38 343 38 38 G5, G6 … … 12 13 14 15 690 690 725 725 345 345 450 450 NP NP NP NP 538 38 538 38 427 38 427 38 343 38 343 38 G8 G8 G8 G8 16 17 18 19 795 795 860 860 550 550 690 690 NP NP NP NP 538 38 538 38 427 38 427 38 343 38 343 38 G8 G8 G8 G8 20 21 22 23 24 515 690 725 795 860 205 345 450 550 690 NP NP NP NP NP 816 538 538 538 538 427 427 427 427 427 343 343 343 343 343 … G8 G8 G8 G8 25 26 27 28 655 655 655 655 345 345 415 415 427 NP 427 NP NP 538 NP 538 NP 427 NP 427 NP 343 NP 343 … … … … 29 30 31 32 690 690 690 690 415 415 485 485 427 NP 427 NP NP 538 NP 538 NP 427 NP 427 NP 343 NP 343 … … … … 33 34 35 36 690 690 795 930 380 415 515 725 NP NP NP NP 621 621 621 621 427 427 427 427 343 343 343 343 … … … … 347 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 Ferrous Materials (Cont’d) 1 2 3 4 130 130 130 130 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 138 138 172 172 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 10 11 130 130 130 126 126 … 122 122 … 118 118 … 114 114 … 110 110 … 106 106 … 103 103 … 99.8 … … 96.8 … … 94.2 … … 92.7 … … 91.1 … … 88.7 … … 87.5 … … 86.3 … … 85.6 … … 85.1 … … 12 13 14 15 130 130 130 130 126 … 127 … 122 … 122 … 118 … 117 … 114 … 114 … 110 … 113 … 106 … 112 … 103 … 112 … 99.8 … 112 … 96.8 … 112 … 94.2 … 112 … 92.7 … 112 … 91.1 … 112 … 88.7 … 112 … 87.5 … 112 … 86.2 … 112 … 86.2 … 112 … 86.2 … 112 … 16 17 18 19 138 138 172 172 138 … 172 … 138 … 172 … 138 … 172 … 138 … 172 … 138 … 172 … 138 … 172 … 138 … 172 … 138 … 172 … 138 … 172 … 138 … 172 … 138 … 172 … 138 … 172 … 138 … 172 … 138 … 172 … 138 … 172 … 138 … 172 … 138 … 172 … 20 21 22 23 24 130 130 130 138 172 122 130 130 138 172 114 130 130 138 172 108 130 130 138 172 103 130 130 138 172 99.1 130 130 138 172 95.7 130 130 138 172 92.8 130 130 138 172 90.1 130 130 138 172 87.2 130 130 138 172 84.5 130 130 138 172 83.1 130 130 138 172 82.5 130 130 138 172 81.1 130 130 138 172 79.2 130 130 138 172 77.3 129 130 138 172 76.0 127 130 138 172 74.8 125 130 138 172 25 26 27 28 86.2 86.2 103 103 82.3 82.7 98.9 99.3 77.8 78.6 93.5 94.2 75.2 76.0 90.2 91.0 73.0 73.7 87.4 88.1 71.0 71.4 85.1 85.8 69.2 69.3 83.1 83.8 67.6 67.6 81.4 81.9 66.1 66.1 79.9 80.0 64.5 64.6 78.3 78.2 63.0 63.0 76.4 76.4 61.6 61.5 74.4 74.4 60.4 60.5 72.7 72.7 59.1 59.8 71.4 71.5 57.9 58.5 69.6 70.3 57.3 57.3 68.3 69.0 56.7 56.7 67.1 67.8 … 55.5 … 66.5 29 30 31 32 103 103 121 121 98.9 99.3 115 116 93.5 94.2 109 110 90.2 91.0 105 106 87.4 88.1 102 103 85.1 85.8 99.1 99.9 83.1 83.8 96.9 97.6 81.4 81.9 95.0 95.4 79.9 80.1 93.2 93.3 78.3 78.1 91.1 91.1 76.4 76.1 88.9 88.9 74.4 74.7 86.8 86.8 72.7 73.3 85.0 85.1 71.4 71.5 83.1 83.9 69.6 70.3 81.3 82.0 68.3 69.0 80.1 80.1 67.1 67.8 78.8 78.8 … 66.5 … 77.6 33 34 35 36 172 172 172 181 172 172 172 181 171 171 171 181 167 167 167 181 163 163 163 181 159 159 159 181 157 157 157 181 155 155 155 181 154 154 154 181 153 153 153 181 152 152 152 181 151 151 151 181 150 150 150 181 149 149 149 181 147 147 147 181 146 146 146 181 144 144 144 181 143 143 143 181 348 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 Ferrous Materials (Cont’d) 1 2 3 4 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 9 10 11 83.8 … … 83.0 … … 77.6 … … 59.2 … … 44.0 … … 33.0 … … 24.5 … … 17.6 … … 12.5 … … 8.45 … … 6.16 … … 4.38 … … 2.77 … … 1.62 … … … … … … … … … … … 12 13 14 15 86.2 … 112 … 86.2 … 112 … 86.2 … 112 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 16 17 18 19 138 … 172 … 138 … 172 … 138 … 172 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 20 21 22 23 24 73.6 123 130 138 172 72.4 121 130 138 169 70.8 118 130 138 164 68.9 … … … … 65.4 … … … … 51.0 … … … … 41.0 … … … … 32.9 … … … … 26.5 … … … … 21.3 … … … … 17.2 … … … … 13.9 … … … … 11.1 … … … … 8.73 … … … … … … … … … … … … … … … … … … … 25 26 27 28 … 54.7 … 65.3 … 53.8 … 64.1 … 52.5 … 62.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 30 31 32 … 65.3 … 76.4 … 64.1 … 74.8 … 62.8 … 72.8 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 33 34 35 36 141 141 141 181 139 139 139 181 134 134 134 165 121 121 121 114 80.1 80.1 80.1 81.8 53.1 53.1 53.1 52.7 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 349 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Line No. Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. Class/ Condition/ Temper Size/Thickness, mm Nonferrous Materials 1 2 3 4 5 6 … … … … … … Bolting Bolting Bolting Bolting Bolting Bolting SB-211 SB-211 SB-211 SB-211 SB-211 SB-211 2014 2014 2024 2024 2024 2024 A92014 A92014 A92024 A92024 A92024 A92024 T6 T651 T4 T4 T4 T4 3 – 200 3 – 200 3.18 – 12.69 12.70 – 114.30 114.31 – 165.10 165.11 – 203.2 7 8 9 10 … … … … Bolting Bolting Rod Rod SB-211 SB-211 SB-187 SB-187 6061 6061 … … A96061 A96061 C10200 C11000 T6 T651 O60 O60 3 – 200 3 – 200 … … 11 12 13 14 … … … … Bar, rod Bar, rod Bar, rod Bar, rod SB-150 SB-150 SB-150 SB-150 … … … … C61400 C61400 C61400 C61400 HR50 HR50 HR50 HR50 50 < t ≤ 75 25 < t ≤ 50 13 < t ≤ 25 ≤ 13 15 16 17 … … … Bar, rod Bar, rod Bar, rod SB-150 SB-150 SB-150 … … … C62300 C62300 C62300 HR50 M20 M30 > 75 > 75 > 75 18 19 20 … … … Bar, rod Bar, rod Bar, rod SB-150 SB-150 SB-150 … … … C62300 C62300 C62300 O20 O25 O30 > 75 > 75 > 75 21 22 23 24 … … … … Bar, rod Bar, rod Bar, rod Bar, rod SB-150 SB-150 SB-150 SB-150 … … … … C62300 C62300 C62300 C62300 HR50 HR50 HR50 HR50 50 < t ≤ 75 25 < t ≤ 50 13 < t ≤ 25 ≤ 13 25 26 27 28 … … … … Rod Bar Bar, rod Bar, rod SB-150 SB-150 SB-150 SB-150 … … … … C63000 C63000 C63000 C63000 HR50 M20 HR50 HR50 50 < t ≤ 75 50 < t ≤ 100 25 < t ≤ 50 13 < t ≤ 25 29 30 31 … … … Bar, rod Bar, rod Bar, rod SB-150 SB-150 SB-150 … … … C64200 C64200 C64200 M20 M30 M10 > 100 > 100 75 < t ≤ 100 32 33 34 35 … … … … Bar, rod Bar, rod Bar, rod Bar, rod SB-150 SB-150 SB-150 SB-150 … … … … C64200 C64200 C64200 C64200 HR50 HR50 HR50 HR50 50 < t ≤ 75 25 < t ≤ 50 13 < t ≤ 25 ≤ 13 350 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) III VIII-1 VIII-2 XII Notes Nonferrous Materials 1 2 3 4 5 6 450 450 425 425 425 400 380 380 310 290 275 260 204 (Cl. 3 only) NP 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 204 204 204 204 204 204 204 204 204 204 204 204 204 204 204 204 204 W4 G10, W4 W4 W4 W4 W4 7 8 9 10 290 290 205 205 240 240 69 69 204 (Cl. 3 only) NP NP NP 204 204 204 204 204 204 204 204 204 204 204 204 W4 G10, W4 … … 11 12 13 14 485 485 515 550 205 220 240 275 260 (Cl. 3 only) 260 (Cl. 3 only) 260 (Cl. 3 only) 260 (Cl. 3 only) 260 260 260 260 260 260 260 260 260 260 260 260 … … … … 15 16 17 515 515 515 205 205 205 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 316 316 316 204 204 204 316 316 316 W1 W1 W1 18 19 20 515 515 515 205 205 205 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 316 316 316 204 204 204 316 316 316 W1 W1 W1 21 22 23 24 525 580 605 620 255 275 305 345 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 204 (Cl. 3 only) 316 316 316 316 204 204 204 204 316 316 316 316 W1 W1 W1 W1 25 26 27 28 585 585 620 690 295 295 310 345 371 (Cl. 3 only) 371 (Cl. 3 only) 371 (Cl. 3 only) 371 (Cl. 3 only) 371 371 371 371 260 260 260 260 343 343 343 343 W4 W4 W4 W4 29 30 31 485 485 485 170 170 205 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 316 316 316 177 177 177 316 316 316 W1 W1 W4 32 33 34 35 515 550 585 620 240 290 310 310 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 316 316 316 316 177 177 177 177 316 316 316 316 W1 W1 W1 W1 351 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 Nonferrous Materials 1 2 3 4 5 6 89.6 89.6 77.9 72.4 68.9 65.5 89.6 89.6 77.9 72.4 68.9 65.5 89.6 89.6 77.9 72.4 68.9 65.5 89.3 89.3 77.2 72.3 68.9 65.5 77.6 77.6 71.1 71.3 68.6 65.2 48.6 48.6 46.1 46.4 46.3 43.5 29.6 29.6 33.2 32.6 32.7 30.5 12.4 12.4 20.8 21.2 21.2 19.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 10 57.9 57.9 46.2 46.2 57.9 57.9 40.1 40.1 57.9 57.9 37.4 37.4 57.9 57.9 35.7 35.7 57.7 57.7 35.1 35.1 44.5 44.5 28.1 28.1 32.2 32.2 21.7 21.7 20.8 20.8 15.6 15.6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 121 121 121 121 121 121 121 121 121 121 121 121 121 121 121 121 121 121 121 121 121 121 121 121 119 119 119 119 116 116 116 116 112 112 112 112 109 109 109 109 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 15 16 17 130 130 130 130 130 130 130 130 130 130 130 130 129 129 129 125 125 125 123 123 123 115 115 115 94.7 94.7 94.7 77.4 77.4 77.4 70.6 70.6 70.6 66.7 66.7 66.7 … … … … … … … … … … … … … … … … … … 18 19 20 130 130 130 130 130 130 130 130 130 130 130 130 129 129 129 125 125 125 123 123 123 115 115 115 94.7 94.7 94.7 77.4 77.4 77.4 70.6 70.6 70.6 66.7 66.7 66.7 … … … … … … … … … … … … … … … … … … 21 22 23 24 130 130 130 130 130 130 130 130 130 130 130 130 130 130 130 130 129 129 129 129 125 125 125 125 123 123 123 123 115 115 115 115 94.7 94.7 94.7 94.7 77.4 77.4 77.4 77.4 70.6 70.6 70.6 70.6 66.7 66.7 66.7 66.7 … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 28 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 138 137 137 137 137 125 125 125 125 99.9 99.9 99.9 99.9 73.5 73.5 73.5 73.5 54.1 54.1 54.1 54.1 39.0 39.0 39.0 39.0 … … … … … … … … … … … … … … … … 29 30 31 115 115 115 100 100 100 95.7 95.7 95.7 93.0 93.0 93.0 93.0 93.0 93.0 89.9 89.9 89.9 79.2 79.2 79.2 57.5 57.5 57.5 41.5 41.5 41.5 25.1 25.1 25.1 13.6 13.6 13.6 10.2 10.2 10.2 … … … … … … … … … … … … … … … … … … 32 33 34 35 115 115 115 115 100 100 100 100 95.7 95.7 95.7 95.7 93.0 93.0 93.0 93.0 93.0 93.0 93.0 93.0 89.9 89.9 89.9 89.9 79.2 79.2 79.2 79.2 57.5 57.5 57.5 57.5 41.5 41.5 41.5 41.5 25.1 25.1 25.1 25.1 13.6 13.6 13.6 13.6 10.2 10.2 10.2 10.2 … … … … … … … … … … … … … … … … … … … … … … … … 352 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. 500 525 550 575 600 625 650 675 700 725 750 775 800 825 850 875 900 Nonferrous Materials 1 2 3 4 5 6 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 7 8 9 10 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 15 16 17 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 18 19 20 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 21 22 23 24 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 25 26 27 28 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 29 30 31 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 32 33 34 35 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 353 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Line No. Nominal Composition Product Form Spec No. Type/Grade Alloy Designation/ UNS No. Class/ Condition/ Temper Size/Thickness, mm Nonferrous Materials (Cont’d) 1 2 3 4 … … … … Rod Rod Rod Rod SB-98 SB-98 SB-98 SB-98 … … … … C65100 C65100 C65100 C65100 O60 H06 H06 H06 … 25 < t ≤ 38 13 < t ≤ 25 ≤ 13 5 6 7 … … … Rod Rod Rod SB-98 SB-98 SB-98 … … … C65500 C65500 C65500 O60 H01 H02 … … … 8 9 10 … … … Rod Rod Rod SB-98 SB-98 SB-98 … … … C66100 C66100 C66100 O60 H01 H02 … … … 11 12 13 14 99Ni 99Ni 99Ni 99Ni – Low C Bolting Bolting Bolting Bolting SB-160 SB-160 SB-160 SB-160 … … … … N02200 N02200 N02200 N02201 Annealed Hot fin./ann. Cold drawn Hot fin./ann. … … … … 15 16 17 18 19 20 67Ni – 30Cu 67Ni – 30Cu 67Ni – 30Cu 67Ni – 30Cu 67Ni – 30Cu 67Ni – 30Cu Bolting Bolting Bolting Bolting Bolting Bolting SB-164 SB-164 SB-164 SB-164 SB-164 SB-164 … … … … … … N04400 N04400 N04400 N04400 N04400 N04400 Annealed Hot worked Hot worked CD-str. rel. Cold worked CD-str. rel. … … … … … … 21 22 23 24 25 67Ni – 30Cu – S 67Ni – 30Cu – S 67Ni – 30Cu – S 67Ni – 30Cu – S 67Ni – 30Cu – S Bolting Bolting Bolting Bolting Bolting SB-164 SB-164 SB-164 SB-164 SB-164 … … … … … N04405 N04405 N04405 N04405 N04405 Annealed Annealed Hot worked Hot worked Cold worked … … … … … 26 27 28 29 30 67Ni – 28Cu – 3Al 67Ni – 28Cu – 3Al 47Ni – 22Cr – 9Mo – 18Fe 47Ni – 22Cr – 19Fe – 6Mo 47Ni – 22Cr – 19Fe – 6Mo Bolting Bolting Bolting Bolting Bolting SF-468 SF-468 SB-572 SB-581 SB-581 … … … … … N05500 N05500 N06002 N06007 N06007 Ann./aged Ann./aged Annealed Solution ann. Solution ann. 25 – 38 6 – 16 … > 19 < 19 31 32 33 55Ni – 21Cr – 13.5Mo 40Ni – 29Cr – 15Fe – 5Mo 61Ni – 16Mo – 16Cr Bolting Bolting Bolting SB-574 SB-581 SB-574 … … … N06022 N06030 N06455 Solution ann. Solution ann. Solution ann. … … … 34 35 36 37 38 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe 72Ni – 15Cr – 8Fe Bolting Bolting Bolting Bolting Bolting SB-166 SB-166 SB-166 SB-166 SB-166 … … … … … N06600 N06600 N06600 N06600 N06600 Annealed Hot fin. Cold drawn Hot fin. Hot fin. … … … … … 354 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Line No. Min. Tensile Strength, MPa Min. Yield Strength, MPa Applicability and Max. Temperature Limits (NP p Not Permitted) III VIII-1 VIII-2 XII Notes Nonferrous Materials (Cont’d) 1 2 3 4 275 515 515 585 83 275 310 380 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 177 177 177 177 177 177 177 177 177 177 177 177 G2 G2, W2 G2, W2 G2, W2 5 6 7 360 380 485 100 165 260 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 177 NP NP 177 177 177 177 NP NP G2 G2, W2 G2, W2 8 9 10 360 380 485 100 165 260 177 (Cl. 3 only) 177 (Cl. 3 only) 177 (Cl. 3 only) 177 NP NP 177 177 177 177 NP NP G2 G2, W2 G2, W2 11 12 13 14 380 415 450 345 100 100 275 69 316 (Cl. 3 only) 316 (Cl. 3 only) 316 (Cl. 3 only) 316 (Cl. 3 only) 316 316 316 649 316 316 316 427 316 316 316 343 … … … … 15 16 17 18 19 20 485 515 550 580 585 600 170 205 275 345 380 415 427 427 427 260 260 NP 482 482 482 260 260 260 427 427 427 260 260 260 343 343 343 260 260 260 … … … G3 G3 G3 21 22 23 24 25 485 485 515 515 585 170 170 240 240 345 427 NP 427 NP 260 NP 482 NP 482 260 NP 427 NP 427 260 NP 343 NP 343 260 … … … … G3 26 27 28 29 30 895 895 655 585 620 585 620 240 205 240 NP NP NP NP NP 260 260 899 538 538 NP NP 427 427 427 NP NP 343 343 343 … … … … … 31 32 33 690 585 690 310 240 275 NP NP NP 427 427 427 427 427 427 343 343 343 … … … 34 35 36 37 38 550 585 620 620 620 240 240 275 275 275 427 427 NP 427 NP 649 649 260 NP 649 427 427 260 NP 427 343 343 260 NP 343 … … G3, H1 … … 355 2011a SECTION II, PART D (METRIC) TABLE 3 (CONT’D) SECTION III, CLASSES 2 AND 3;* SECTION VIII, DIVISIONS 1 and 2;‡ AND SECTION XII MAXIMUM ALLOWABLE STRESS VALUES S FOR BOLTING MATERIALS (*See Maximum Temperature Limits for Restrictions on Class) (‡Use with Part 4.16 of Section VIII, Division 2) Maximum Allowable Stress, MPa (Multiply by 1000 to Obtain kPa), for Metal Temperature, °C, Not Exceeding Line No. −30 to 40 65 100 125 150 175 200 225 250 275 300 325 350 375 400 425 450 475 Nonferrous Materials (Cont’d) 1 2 3 4 55.2 68.9 77.9 94.5 55.2 68.9 77.9 94.5 55.2 68.9 77.9 94.5 55.1 68.9 77.9 94.5 54.4 68.9 77.9 94.5 53.2 68.9 77.9 94.5 51.9 68.9 77.9 94.5 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 5 6 7 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 67.0 67.0 67.0 65.1 65.1 65.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 8 9 10 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 68.9 67.0 67.0 67.0 65.1 65.1 65.1 … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … … 11 12 13 14