Stainless 304 화학 성분표
Grade
C
304
304L
Mn
Si
P
S
- 0.08
- 2.0
- 0.75
- 0.045
- 0.030
- 0.030
- 2.0
- 0.75
- 0.045
- 0.030
- 2.0
- 0.75
- 0.045
- 0.030
0.04
304H
0.10
Cr
Mo
18.0
20.0
18.0
20.0
18.0
20.0
Ni
N
-
8.0 10.5
- 0.10
-
8.0 12.0
- 0.10
-
8.0 10.5
-
304L 과 304H 의 기계적 특성 비교표
Grade
Tensile Strength
Yield Strength
Elongation (%
Hardness
(MPa) min
0.2% Proof
in 50mm) min
Rockwell B (HR
Brinell (HB)
B) max
max
(MPa) min
304
515
205
40
92
201
304L
485
170
40
92
201
304H
515
205
40
92
201
304H also has a requirement for a grain size of ASTM No 7 or coarser.
Grade
304/L/H
Density
Elastic
Mean Coefficient of
Thermal
Specific
Electrical
(kg/m3)
Modulus
Thermal Expansion
Conductivity
Heat 0-
Resistivity
(GPa)
(mm/m/°C)
(W/m–K)
100°C
(nW–m)
(J/kg–K)
8000
Grade
UNS No.
193
0-
0-
0-
at
at
100°C
315°C
538°C
100°C
500°C
17.2
17.8
18.4
16.2
21.5
Old British
Euronorm
500
720
Swedish
Japanese
BS
En
No
Name
SS
JIS
304
S30400
304S31
58E
1.4301
X5CrNi18-10
2332
SUS 304
304L
S30403
304S11
-
1.4306
X2CrNi19-11
2352
SUS 304L
304H
S30409
304S51
-
1.4948
X6CrNi18-11
-
-
304 대체품
Grade
Why it might be chosen instead of 304
-1/4-
304 재질 대신하여 선택할 수 있는 이유
301L
A higher work hardening rate grade is required for certain roll formed or stretch formed
components.
특정 롤 성형 또는 연신 성형 부품에는 더 높은 가공 경화 속도 등급이 필요합니다.
302HQ Lower work hardening rate is needed for cold forging of screws, bolts and rivets.
나사, 볼트 및 리벳의 냉간 단조에는 낮은 가공 경화 속도가 필요합니다.
303
Higher machinability needed, and the lower corrosion resistance, formability and
weldability are acceptable.
더 높은 기계 가공성이 필요하고 더 낮은 내식성, 성형 성 및 용접성이 허용됩니다.
316
Higher resistance to pitting and crevice corrosion is required, in chloride environments
304 에 비해 내식성이 뛰어나다
염화물 환경에서는 공식 및 틈새 부식에 대한 더 높은 저항력이 필요합니다.
321
Better resistance to temperatures of around 600-900°C is needed…321 has higher hot
strength.
약 600 ~ 900 ° C 의 온도에 대한 더 나은 저항이 필요합니다. 321 은 고온 강도가 더 높습니다.
3CR12
A lower cost is required, and the reduced corrosion resistance and resulting discolouration
are acceptable.
더 낮은 비용이 요구되며 감소 된 내식성 및 결과적인 변색이 허용됩니다.
430
A lower cost is required, and the reduced corrosion resistance and fabrication
characteristics are acceptable.
더 낮은 비용이 필요하며 감소 된 내식성 및 제조 특성이 허용됩니다.
Stainless 316 특성
Grade
C
Mn
Si
P
S
Cr
Mo
Ni
N
316
Min
-
-
-
0
-
16.0
2.00
10.0
-
Max
0.08
2.0
0.75
0.045
0.03
18.0
3.00
14.0
0.10
Min
-
-
-
-
-
16.0
2.00
10.0
-
Max
0.03
2.0
0.75
0.045
0.03
18.0
3.00
14.0
0.10
Min
0.04
0.04
0
-
-
16.0
2.00
10.0
-
max
0.10
0.10
0.75
0.045
0.03
18.0
3.00
14.0
-
316L
316H
-2/4-
Grade
Tensile Strength
Yield Stress
Elongation (%
Hardness
(MPa) min
0.2% Proof
in 50 mm)
Rockwell B
Brinell (HB)
(MPa) min
min
(HR B) max
max
316
515
205
40
95
217
316L
485
170
40
95
217
316H
515
205
40
95
217
Grade
Density
Elastic
Mean Coefficient of
Thermal
Specific
Elec
(kg/m3)
Modulus
Thermal Expansion
Conductivity
Heat 0-
Resistivity
(GPa)
(µm/m/°C)
(W/m–K)
100°C
(nΩ–m)
316/L/H
8000
Grade
UNS No
316
S31600
193
0-
0-
0-
At
At
(J/kg–
100°C
315°C
538°C
100°C
500°C
K)
15.9
16.2
17.5
16.3
21.5
500
Old British
Euronorm
740
Swedish
Japanese
BS
En
No
Name
SS
JIS
316S31
58H,
1.4401
X5CrNiMo17-12-2
2347
SUS 316
1.4404
X2CrNiMo17-12-2
2348
SUS
58J
316L
S31603
316S11
-
316L
316H
S31609
316S51
-
-
-
Grade
Why it might be chosen instead of 316?
316Ti
Better resistance to temperatures of around 600-900°C is needed.
-
-
약 600-900 ° C 의 온도에 대한 더 나은 저항이 필요합니다.
316N
Higher strength than standard 316. 표준 316 보다 높은 강도.
317L
Higher resistance to chlorides than 316L, but with similar resistance to stress corrosion
cracking.
316L 보다 염화물에 대한 내성이 높지만 응력 부식 균열에 대한 내성은 비슷합니다.
904L
Much higher resistance to chlorides at elevated temperatures, with good formability
우수한 성형 성과 함께 고온에서 훨씬 더 높은 염화물 저항성
2205
Much higher resistance to chlorides at elevated temperatures, and higher strength than
316.
-3/4-
고온에서 염화물에 대한 저항성이 훨씬 높고 316 보다 강도가 높습니다.
-4/4-