Designation: A 537/A 537M – 95 (Reapproved 2000)
Standard Specification for
Pressure Vessel Plates, Heat-Treated, Carbon-ManganeseSilicon Steel1
This standard is issued under the fixed designation A 537/A 537M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope
1.1 This specification2 covers heat-treated carbonmanganese-silicon steel plates intended for fusion welded
pressure vessels and structures.
1.2 Material under this specification is available in the
following three classes:
Class
1
2
3
Heat
Treatment
Normalized
Quenched
and tempered
Quenched
and tempered
Thickness,
21⁄2 in. and
under
[65 mm and
under]
Over 21⁄2 to 4 in.
[Over 65 to 100
mm]
21⁄2 in. and
under
[65 mm and
under]
Over 21⁄2 to 4 in.
[Over 65 to 100
mm]
Over 4 to 6 in.
[Over 100 to 150
mm]
21⁄2 in. and
under
[65 mm and
under]
Over 21⁄2 to 4 in.
[Over 65 to 100
mm]
Over 4 to 6 in.
[Over 100 to 150
mm]
Yield
Strength,
min, ksi
[MPa]
Tensile
Strength,
min, ksi
[MPa]
50
70
[345]
[485]
45
[310]
65
[450]
60
80
[415]
[550]
55
[380]
75
[515]
46
[315]
70
[485]
55
80
[380]
[550]
50
[345]
75
[515]
40
[275]
70
[485]
1.3 The maximum thickness of plates furnished under this
specification is 4 in. [100 mm] for Class 1 and 6 in. [150 mm]
for Class 2 and Class 3.
1
This specification is under the jurisdiction of ASTM Committee A-1 on Steel,
Stainless Steel, and Related Alloys and is the direct responsibility of Subcommittee
A01.11 on Steel Plates for Boilers and Pressure Vessels.
Current edition approved June 15, 1995. Published August 1995. Originally
published as A 537 – 65. Last previous edition A 537/A 537M – 91.
2
For ASME Boiler and Pressure Vessel Code applications, see related Specification SA-537/SA-537M in Section II of that Code.
1.4 The values stated in either inch-pound units or SI units
are to be regarded separately as standard. Within the text, the
SI units are shown in brackets. The values stated in each
system are not exact equivalents; therefore, each system must
be used independently of the other. Combining values from the
two systems may result in nonconformance with the specification.
2. Referenced Documents
2.1 ASTM Standards:
A 20/A20M Specification for General Requirements for
Steel Plates for Pressure Vessels3
A 435/A435M Specification for Straight-Beam Ultrasonic
Examination of Steel Plates3
A 577/A577M Specification for Ultrasonic Angle-Beam
Examination of Steel Plates3
A 578/A578M Specification for Straight-Beam Ultrasonic
Examination of Plain and Clad Steel Plates for Special
Applications3
3. General Requirements and Ordering Information
3.1 Material supplied to this material specification shall
conform to Specification A 20/A 20M. These requirements
outline the testing and retesting methods and procedures,
permissible variations in dimensions, and mass, quality and
repair of defects, marking, loading, etc.
3.2 Specification A 20/A 20M also establishes the rules for
the ordering information which should be complied with when
purchasing material to this specification.
3.3 In addition to the basic requirements of this specification, certain supplementary requirements are available when
additional control, testing, or examination is required to meet
end use requirements. These include:
3.3.1 Vacuum treatment,
3.3.2 Additional or special tension testing,
3.3.3 Impact testing, and
3.3.4 Nondestructive examination.
3
Annual Book of ASTM Standards, Vol 01.04.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1
Copyright by ASTM Int'l (all rights reserved);
Reproduction authorized per License Agreement with Serkan Saygan (); Wed Aug 17 11:11:23 EDT 2005
A 537/A 537M – 95 (2000)
3.4 The purchaser is referred to the listed supplementary
requirements in this specification and to the detailed requirements in Specification A 20/A 20M.
3.5 If the requirements of this specification are in conflict
with the requirements of Specification A 20/A 20M, the requirements of this specification shall prevail.
4. Manufacture
4.1 Steelmaking Practice—The steel shall be killed and
shall conform to the fine austenitic grain size requirement of
Specification A 20/A 20M.
5. Heat Treatment
5.1 All plates shall be thermally treated as follows:
5.1.1 Class 1 plates shall be normalized.
5.1.2 Class 2 and Class 3 plates shall be quenched and
tempered. The tempering temperature for Class 2 plates shall
not be less than 1100°F [595°C] for not less than 1⁄2 h and
1150°F [620°C] for Class 3 plates for not less than 1⁄2 h.
6. Chemical Requirements
6.1 The steel shall conform to the chemical requirements
shown in Table 1 unless otherwise modified in accordance with
Supplementary Requirement S17, Vacuum Carbon-Deoxidized
Steel, in Specification A 20/A 20M.
7. Mechanical Requirements
7.1 Tension Tests:
7.1.1 Requirements—The material as represented by the
tension-test specimens shall conform to the requirements
shown in Table 2.
7.1.2 For Class 2 and Class 3 plates with a nominal
thickness of 3⁄4 in. [20 mm] and under, the 11⁄2 -in. [40-mm]
wide rectangular specimen may be used for the tension test,
and the elongation may be determined in a 2-in. [50-mm] gage
length that includes the fracture and that shows the greatest
elongation.
8. Keywords
8.1 carbon steel plate; pressure containing parts; pressure
vessel steels; steel plates for pressure vessel application
2
Copyright by ASTM Int'l (all rights reserved);
Reproduction authorized per License Agreement with Serkan Saygan (); Wed Aug 17 11:11:23 EDT 2005
A 537/A 537M – 95 (2000)
TABLE 1 Chemical Requirements
Element
Composition, %
Carbon, maxA
Manganese:
11⁄2 in. [40 mm] and under in thickness:B
Heat analysis
Product analysis
Over 11⁄2 in. [40 mm] in thickness:
Heat analysis
Product analysis
Phosphorus, maxA
Sulfur, maxA
Silicon:
Heat analysis
Product analysis
Copper, max:
Heat analysis
Product analysis
Nickel, max:B
Heat analysis
Product analysis
Chromium, max:
Heat analysis
Product analysis
Molybdenum, max:
Heat analysis
Product analysis
0.24
0.70–1.35
0.64–1.46
1.00–1.60
0.92–1.72
0.035
0.035
0.15–0.50
0.13–0.55
0.35
0.38
0.25
0.28
0.25
0.29
0.08
0.09
A
Applies to both heat and product analyses.
Manganese may exceed 1.35 % on heat analysis, up to a maximum of 1.60 %,
and nickel may exceed 0.25 % on heat analysis, up to a maximum of 0.50 %,
provided the heat analysis carbon equivalent does not exceed 0.57 % when based
upon the following equation:
Mn Cr 1 Mo 1 V Ni 1 Cu
1
CE 5 C 1 6 1
5
15
B
When this option is exercised, the manganese and nickel contents on product
analysis shall not exceed the heat analysis content by more than 0.12 % and
0.03 %, respectively.
TABLE 2 Tensile Requirements
Tensile strength:
21⁄2 in. and under
[65 mm and under]
Over 21⁄2 to 4 in., incl
[Over 65 to 100 mm, incl]
Over 4 to 6 in., incl
[Over 100 to 150 mm, incl]
Yield strength, min:
21⁄2 in. and under
[65 mm and under]
Over 21⁄2 to 4 in., incl
[Over 65 to 100 mm, incl]
Over 4 in. to 6 in., incl
[Over 100 to 150 mm, incl]
Elongation in 2 in.
[50 mm], min, %:B
4 in. [100 mm] and under
Over 4 in. [100 mm]
Elongation in 8 in.
[200 mm], min, %B
A
B
C
Class 1
Class 2
Class 3
ksi [MPa]
ksi [MPa]
ksi [MPa]
70–90
[485–620]
65–85
[450–585]
80–100
[550–690]
75–95
[515–655]
70–90
[485–620]
80–100
[550–690]
75–95
[515–655]
70–90
[485–620]
60
[415]
55
[380]
46
[315]
55
[380]
50
[345]
40
[275]
A
22
20
22
20
18
C
C
A
A
50
[345]
45
[310]
A
A
22
Product is not available in this size range.
See Specification A 20/A 20M for elongation adjustments.
There is no requirement for elongation in 8 in.
3
Copyright by ASTM Int'l (all rights reserved);
Reproduction authorized per License Agreement with Serkan Saygan (); Wed Aug 17 11:11:23 EDT 2005
A 537/A 537M – 95 (2000)
SUPPLEMENTARY REQUIREMENTS
Supplementary requirements shall not apply unless specified in the order.
A list of standardized supplementary requirements for use at the option of the purchaser are included
in Specification A 20/A 20M. Several of those considered suitable for use with this specification are
listed by title. Other tests may be performed by agreement between the supplier and the purchaser.
S1. Vacuum Treatment,
S2. Product Analysis,
S3. Simulated Post-Weld Heat Treatment of Mechanical
Test Coupons,
S4.1 Additional Tension Test,
S5. Charpy V-Notch Impact Test,
S6. Drop Weight Test,
S7. High-Temperature Tension Test,
S8. Ultrasonic Examination in accordance with Specification A 435/A 435M,
S9. Magnetic Particle Examination,
S11. Ultrasonic Examination in accordance with Specification A 577/A 577M,
S12. Ultrasonic Examination in accordance with Specification A 578/A 578M,
S14. Bend Test, and
S17. Vacuum Carbon-Deoxidized Steel.
ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned
in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk
of infringement of such rights, are entirely their own responsibility.
This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and
if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards
and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the
responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should
make your views known to the ASTM Committee on Standards, at the address shown below.
This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,
United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above
address or at 610-832-9585 (phone), 610-832-9555 (fax), or service@astm.org (e-mail); or through the ASTM website
(www.astm.org).
4
Copyright by ASTM Int'l (all rights reserved);