NILFLEX – Technical Sheet
Series:
NILFLEX SH - General purpose
High elasticity / Medium flow
Key Features :
Applications:
Availability:
o
Filled version (density from 0,98g/cm3 to 1,18g/cm3)
o
Automotive components
A = Low friction
o
Medium flow
o
Pipe
D = PE adhesion optimized
o
High elasticity
o
Wire and cable jacket
G = soap stabilized
o
Good compression set
o
Building
H = heat resistance improved
o
Good mechanical properties
o
Soft touch grips and handles
S = antimicrobical
o
Good adhesion to polyolefinic substrate (PP / PE)
o
Sealing and closures
T = copper / metal resistance
o
Good UV and ozone resistance
o
Sports equipment
U = UV resistance
o
Temperature range from –50°C to 100°C
o
Toys
V = low gloss
o
Injection moulding grade
o
Flexible connectors
o
Suitable for extrusion process
o
100% recyclable
Properties
GRADE
Hardness
sh A
Density
g/cm3
MFR
g/10min
Tensile Strength
Mpa
Elongation break
%
Tear Strength
N/mm
Compression set
%
Test
method
ASTM
D2240
ISO
1183
ISO
1133
ASTM
D412/C
ASTM
D412/C
ASTM
D624
IS0 815 - Type B
22h / 70°C
Nilflex SH A30 M021
30
0,89
10,0
5,0
980
15,9
32,0
Nilflex SH A40 M021
40
0,89
10,0
6,5
950
17,3
38,0
Nilflex SH A50 M021
50
0,89
10,0
7,5
950
24,0
40,0
Nilflex SH A60 M021
60
0,89
10,0
7,9
900
29,3
43,0
Nilflex SH A65 M021
65
0,89
10,0
8,5
900
31,5
46,0
Nilflex SH A70 M021
70
0,89
10,0
9,9
850
34,2
49,0
Nilflex SH A75 M021
75
0,89
10,0
10,5
850
37,0
53,0
Nilflex SH A80 M021
80
0,89
10,0
11,4
800
39,4
57,0
Nilflex SH A85 M021
85
0,89
10,0
12,5
770
47,0
59,0
Nilflex SH A90 M021
90
0,89
10,0
14,8
750
52,0
61,0
GRADE
Hardness
sh D
Density
g/cm3
MFR
g/10min
Tensile Strength
Mpa
Elongation break
%
Tear Strength
N/mm
Compression set
%
Test
method
ASTM
D2240
ISO
1183
ISO
1133
ASTM
D412/C
ASTM
D412/C
ASTM
D624
IS0 815 - Type B
22h / 70°C
40
0,89
10,0
17,0
750
78,0
-
Nilflex SH D40 M021
Properties
GRADE
Hardness
sh A
Density
g/cm3
MFR
g/10min
Tensile Strength
Mpa
Elongation break
%
Tear Strength
N/mm
Compression set
%
Test
method
ASTM
D2240
ISO
1183
ISO
1133
ASTM
D412/C
ASTM
D412/C
ASTM
D624
IS0 815 - Type B
22h / 70°C
Nilflex SH A20 M121
20
0,98
10,0
4,0
950
13,0
-
Nilflex SH A30 M121
30
0,98
10,0
4,9
950
15,9
-
Nilflex SH A40 M121
40
0,98
10,0
5,5
930
17,0
-
Nilflex SH A50 M121
50
0,98
10,0
6,2
930
24,0
-
Nilflex SH A60 M121
60
0,98
10,0
7,7
900
28,8
-
Nilflex SH A65 M121
65
0,98
10,0
8,1
900
31,0
-
Nilflex SH A70 M121
70
0,98
10,0
9,5
850
33,7
-
Nilflex SH A75 M121
75
0,98
10,0
10,0
850
36,8
-
Nilflex SH A80 M121
80
0,98
10,0
11,0
800
39,0
-
Nilflex SH A85 M121
85
0,98
10,0
13,5
770
47,0
-
Nilflex SH A90 M121
90
0,98
10,0
15,5
750
51,0
-
GRADE
Hardness
sh D
Density
g/cm3
MFR
g/10min
Tensile Strength
Mpa
Elongation break
%
Tear Strength
N/mm
Compression set
%
Test
method
ASTM
D2240
ISO
1183
ISO
1133
ASTM
D412/C
ASTM
D412/C
ASTM
D624
IS0 815 - Type B
22h / 70°C
40
0,98
10,0
18,0
750
77,0
-
Nilflex SH D40 M121
Properties
GRADE
Hardness
sh A
Density
g/cm3
MFR
g/10min
Tensile Strength
Mpa
Elongation break
%
Tear Strength
N/mm
Compression set
%
Test
method
ASTM
D2240
ISO
1183
ISO
1133
ASTM
D412/C
ASTM
D412/C
ASTM
D624
IS0 815 - Type B
22h / 70°C
Nilflex SH A20 M221
20
1,05
10,0
3,8
930
12,7
-
Nilflex SH A30 M221
30
1,05
10,0
4,5
930
15,4
-
Nilflex SH A40 M221
40
1,05
10,0
5,1
900
16,5
-
Nilflex SH A50 M221
50
1,05
10,0
6,0
900
23,0
-
Nilflex SH A60 M221
60
1,05
10,0
6,1
880
28,0
-
Nilflex SH A65 M221
65
1,05
10,0
6,8
880
29,2
-
Nilflex SH A70 M221
70
1,05
10,0
7,2
850
32,2
-
Nilflex SH A75 M221
75
1,05
10,0
8,7
850
36,5
-
Nilflex SH A80 M221
80
1,05
10,0
9,5
750
38,3
-
Nilflex SH A85 M221
85
1,05
10,0
12,0
750
46,2
-
Nilflex SH A90 M221
90
1,05
10,0
13,1
750
50,0
-
Properties
GRADE
Hardness
sh A
Density
g/cm3
MFR
g/10min
Tensile Strength
Mpa
Elongation break
%
Tear Strength
N/mm
Compression set
%
Test
method
ASTM
D2240
ISO
1183
ISO
1133
ASTM
D412/C
ASTM
D412/C
ASTM
D624
IS0 815 - Type B
22h / 70°C
Nilflex SH A30 M321
30
1,18
10,0
4,5
900
12,0
-
Nilflex SH A40 M321
40
1,18
10,0
5,1
850
13,5
-
Nilflex SH A50 M321
50
1,18
10,0
5,3
850
20,2
-
Nilflex SH A60 M321
60
1,18
10,0
6,0
800
25,0
-
Nilflex SH A65 M321
65
1,18
10,0
6,8
800
27,0
-
Nilflex SH A70 M321
70
1,18
10,0
7,3
750
30,2
-
Nilflex SH A75 M321
75
1,18
10,0
8,0
750
35,4
-
Nilflex SH A80 M321
80
1,18
10,0
10,0
700
37,5
-
Processing
Injection moulding:
Mould: 25 -50°C
Injection speed:
Injection pressure :
Back pressure:
Feed: 170 – 190°C
Rear: 180 – 200°C
Middle: 190 – 210°C
medium – fast
medium – fast
low – medium
Front: 200 – 220°C
Extrusion
Sh< A50
Die: 190°C
Sh> A50
Die: 200°C
Sh< A50
Feed: 150 – 170°C
Rear: 160 – 180°C Middle: 170 – 190°C Front: 180 – 200°C
Sh> A50
Feed: 160 – 180°C
Rear: 170 – 190°C Middle: 180 – 200°C Front: 190 – 210°C
L/D ratio:
Compression ratio (screw):
Screw speed:
min. 20:1
from 3,0:1 to 4,5:1
50-100 rpm
Taro Plast S.p.A.
Strada Diolo 57/A, 43019 Soragna
Italy
Phone: +39 0524 596711
Fax: +39 0524 596750
www.taroplast.com
CUSTOMER SERVICE ITALY
Phone: +39 0524 596727
Fax: +39 0524 596750
CUSTOMER SERVICE EUROPE
Phone: +39 0524 596723
Fax: +39 0524 596750
SALES CONTACT EMAIL
sales@taroplast.com