N9000 PTFE Processing Guidelines
N9000 PTFE Substrates
Note: The following guidelines are provided to assist
The Park/Nelco (previously known as Metclad) NY,
Park/Nelco laminate and prepreg users with general
NX, and NH families of RF and Microwave materials
recommendations for successful processing during
are woven fiberglass/PTFE composites for use as
PWB fabrication. The recommendations are for general
printed-circuit substrates. The NY, NX, and NH
review purposes only and process adjustments may be
materials are used in high-frequency applications
required to achieve optimum results in your specific
where low loss and controlled dielectric constant and
manufacturing environment.
thickness (and thus impedance) are required. The
control of these parameters is particularly important
for applications such as antennas, filters, couplers, amplifiers, power dividers, and combiners. Using precise control of the
resin-to-glass Ratio, Park/Nelco is able to offer a range of materials from the lowest dielectric constant and dissipation
factor (the NY family) to more highly reinforced laminate (the NX family), and finally to the low cost, woven reinforced,
ceramic filled material (the NH family) with improved dimensional stability. The N9000 materials used in stripline or microstrip applications can be processed using conventional PTFE board fabrication processes and techniques. When a hybrid
or mixed material build is used, the NY, NX, and NH materials can also be processed using many typical glass-epoxy or
glass-thermoset (i.e., N4000-6, N4000-13, and N6000-21) process parameters with few in-line modifications.
Material Handling & Storage
Store laminate and bond ply material in a flat orientation and in a dry environment (<50% RH).
Do not bend, scratch, or dent laminate.
BONDING PTFE MULTILAYER PRINTED CIRCUITS
PTFE multilayer bonding is different than FR4 multilayer bonding. FR4 multilayer bonding utilizes laminate cores,
prepreg, and copper foil. PTFE multilayer bonding utilizes only laminate cores and bonding films. There is no
commercially available prepreg for PTFE. There are two types of PTFE multilayer printed circuit boards: all PTFE
and bonding film constructions and hybrid PTFE and FR4 constructions.
Hybrid PTFE and FR4 Construction:
There are two types of hybrid constructions: single layers of PTFE core bonded to one side or both sides of a FR4
printed circuit board. Hybrid constructions normally utilize a sequential lamination process. The FR4 multilayer
board and the PTFE multilayer board are processed separately. Utilize the bonding process for PTFE and bonding
film constructions listed below for the PTFE portion of the hybrid construction. The two assemblies are then bonded
together. The copper ground plane of the PTFE board is bonded to the FR4 board with FR4 prepreg.
PTFE and Bonding Film Construction:
The two most popular bonding films for PTFE multilayer constructions are thermoplastic FEP, type C, films
(fluorinated ethylene propylene) or thermoplastic chlorotrifluoroethylene films such as Neltec FV6700. FEP films are
recommended for any PTFE multilayer board that requires high temperature post processing such as plating reflow
and leveling. The melting point of FEP is higher than the tin/lead reflow or hot air leveling temperatures and therefore
circuit delamination due to heat should not happen. Also, FEP is recommended when bonding to metal ground
planes or layers that are mostly metal.
For More Information Contact One Of Our ISO 9002 Facilities or visit our web site at www.parknelco.com
Neltec (USA)
Neltec SA
Rev.C 06-02
Tempe, AZ
Lannemezan, France
(480) 967-5600
+33 (0) 5 62 98 52 90
N9000 PTFE Processing Guidelines
SURFACE PREPARATION:
Copper:
• A light micro-etch can be used to remove any residues of etch-resist from the copper circuitry and to provide a
greater surface area to which the bonding film will adhere.
• Mechanical cleaning should NOT be used.
• Alternative oxides should be used on large areas of copper, such as ground planes, to improve the bond.
• Brown oxide treatments can be used in lower temperature applications.
Substrate:
• All PTFE surfaces must be clean, dry and free of residues from the chemical processes.
• All PTFE surfaces must be activated prior to bonding. Use the plasma or sodium etch parameters
outlined in the plating section below.
• PTFE that has been soiled on previous runs must be chemically cleaned and re-activated.
Bonding Film:
• This requires no preparation, but lint-free gloves must be worn when handling the film to prevent contamination.
• After the above preparation, the materials must be stored in a clean area and should be used within 24 hours.
FV6700 BONDING:
Chlorotrifluoroethylene films such as Neltec FV6700 have been used to bond PTFE laminate cores together for over 25
years. This unreinforced film melts completely during the lamination process and care should be exercised to prevent
excess “squeeze out” due to over pressure. FV6700 would be considered a medium to high flow adhesive.
Surface Preparation:
• The copper and dielectric surfaces being bonded must be clean and dry.
• Inner layers should be handled with clean gloves along the periphery and should never be scrubbed. Only
chemical cleaning is recommended for inner layers. Organic cleaner is often used along with sulfuric acid and
DI water rinses.
• All PTFE layers should be treated to enhance adhesion. Plasma or sodium etch works well. (Both
processes are described below in the plating section).
• The copper ground planes should be oxide treated prior to bonding to increase surface roughness. As stated
above, alternative oxides work well. Red or brown oxide can be used in lower temperature applications.
Tooling:
Standard pin or slot tooling systems may be used. Tooling holes and slots on inner layers should be
surrounded by copper for strength. Stainless steel (304) caul plates are preferred to prevent distortion of
circuitry during bonding. Tooling plates must be flat and parallel. FV6700 is a medium to high flow adhesive.
Press platens and tooling plates must be flat and parallel to prevent excessive squeeze out and insure uniform
bond strength.
For More Information Contact One Of Our ISO 9002 Facilities or visit our web site at www.parknelco.com
Neltec (USA)
Neltec SA
Rev.C 06-02
Tempe, AZ
Lannemezan, France
(480) 967-5600
+33 (0) 5 62 98 52 90
N9000 PTFE Processing Guidelines
FV6700 Lay Up:
Lay up must be performed in a clean dust-free environment. FV6700 bond ply material is sold .0015” thick. One
layer of bond ply has been found to be adequate for filling up to one-ounce copper signal layers. Use of 2 layers
of FV6700 is not recommended due to “squeeze out” of the bond ply. FV6700 is a medium-to-high flow bond ply.
FV6700 Bonding Techniques
• Lay the bonding film between the laminate cores to be laminated.
• Insert a thermocouple into the laminate at the bond line.
• Load into a press pre-heated to 235°C.
• Apply pressure: 100-200 psi. (Use the minimum pressure possible to prevent excessive adhesive flow.)
• Hold in the press until the laminate reaches 220°C (This may require 20-30 minutes)
• Hold for an additional 15 minutes after the laminate has reached 220°C. (The final temperature at the bond line
will approach 235°C).
• Cool under pressure to less than 90°C before removing from the press.
FV6700 Bonding Film Lamination Parameters
FEP BONDING
Few adhesives can match the broad capabilities of FEP film. Its excellent resistance to both chemicals and high
temperatures makes possible bonded structures suitable for service in applications where ordinary adhesives may not be
equal to the task. FEP produces strong bonds between two surfaces of PTFE or between PTFE and other substrates that
can withstand temperatures greater than 332°C (630°F) above the PTFE melt temperature. FEP is highly viscous at its
melting point but it is considered a medium-to-high flow adhesive. Normally, FEP Type C films are used. The type C film
is primed to enhance adhesion.
For More Information Contact One Of Our ISO 9002 Facilities or visit our web site at www.parknelco.com
Neltec (USA)
Neltec SA
Rev.C 06-02
Tempe, AZ
Lannemezan, France
(480) 967-5600
+33 (0) 5 62 98 52 90
N9000 PTFE Processing Guidelines
Surface Preparation:
• The copper and dielectric surfaces being bonded must be clean and dry.
• Inner layers should be handled with clean gloves along the periphery and should never be scrubbed. Only
chemical cleaning is recommended for inner layers. Organic cleaner is often used along with sulfuric acid and
DI water rinses.
• All PTFE layers should be treated to enhance adhesion. Plasma or sodium etch works well. (Both
processes are described below in the plating section).
• The copper ground planes should be oxide treated prior to bonding to increase surface roughness. Alternative
oxides should be used. Red or brown oxide can be used in lower temperature applications.
Tooling:
Standard pin or slot tooling systems may be used. Tooling holes and slots on inner layers should be
surrounded by copper for strength. Stainless steel (304) caul plates are preferred to prevent distortion of
circuitry during bonding. Although FEP is a very low flow adhesive, press platens and tooling plates must be
flat and parallel to prevent excessive squeeze out and insure uniform bond strength.
FEP Lay-Up:
A solid copper border should be utilized on inner core layers to improve handling. For high layer count
applications, partial copper borders should be used and offset on adjacent layers so that total thicknesses
across the panel remain uniform to minimize circuit distortion after lamination. Due to its high viscosity, the
thickness of the FEP film must be adequate to fully encapsulate circuit features. .002-inch FEP film is required
to encapsulate 1 oz copper features and .001-inch film is required to encapsulate .5 oz copper features. During
lay-up, copper foils or thin aluminum foils (less than .003 inches) should be used as release materials.
FEP Bonding Techniques
• Lay the bonding film between the laminate cores to be laminated.
• Insert the thermocouple into the laminate at the bond line.
• Load into a press pre-heated to 296°C.
• Apply pressure: 100-200 psi.
• Hold in the press until the laminate reaches 271°C (This may require 30-40 minutes)
• Hold for an additional 40 minutes after the laminate has reached 271°C. (The final temperature at the bond line
will approach 296°C).
Cool under pressure to less than 90°C before removing from the press. The recommended bonding cycle shown in
the figure below has a 40 minute soak at 296°C (565°F) with 100 psi of pressure. The critical portions of the cycle
are those above 271°C (520°F), the melt point of FEP. Temperature ramp rates should be adjusted to insure good
temperature uniformity at temperatures above the melt point.
For More Information Contact One Of Our ISO 9002 Facilities or visit our web site at www.parknelco.com
Neltec (USA)
Neltec SA
Rev.C 06-02
Tempe, AZ
Lannemezan, France
(480) 967-5600
+33 (0) 5 62 98 52 90
N9000 PTFE Processing Guidelines
FEP Bonding Film Lamination Parameters
Drilling
Care must be taken when drilling PTFE materials. PTFE is chemically inert. There is no material available that can
chemically remove drill smear from a hole in a PTFE circuit board. The only way to remove the smear is to use a larger
drill bit and cut the smear out of the hole. The Neltec NY, NX and NH PTFE materials should be drilled using highly
polished carbide tools. The use of repointed tools is not recommended. Panels can be drilled in stacks based on total
thickness. The total stack height, including entry and backup materials, should not exceed 70% of the effective flute length
of the drill bit. The use of hard phenolic, rigid entry .020-.032” (0.5 mm - 0.8 mm) and backup .060-.080” (1.5 mm – 2.0
mm) material is recommended. PTFE laminates are much softer than FR4 laminates. The edges of the holes will be
distorted if entry and backup materials are not used during drilling. Aluminum or aluminum-clad materials entry and
backup materials are not recommended for any PTFE materials. Aluminum burrs have a tendency to damage the soft
PTFE during the machining process. The following feeds and speeds have been proven to work well in production
environments and are recommended as a beginning point to develop specific process parameters.
Drilling Parameters
To drill clean holes that do not contain drill smear, close attention must be placed on the drill speed and rate the drill
enters and exits the material. As stated above, polished carbide drill bits work best on PTFE. The following parameters
are basic recommendations for drilling PTFE. All fabricators should determine the optimal parameters for their equipment
and tooling. Remember: Use new, polished, carbide tooling to guarantee the highest hole quality.
Chip Load:
0.001” – 0.003” (0.025 mm – 0.076 mm) per revolution
Surface Speed: 200 - 400 sfm (1.0 – 2.0 m/s)
Retract Rate: 400 - 600 IPM (169 - 254 mm/s)
Tool Type:
Polished Carbide
Tool Life:
12-15 inches of dielectric (i.e. for 0.030”, approximately 400-500 hits)
depending on hole quality required.
For More Information Contact One Of Our ISO 9002 Facilities or visit our web site at www.parknelco.com
Neltec (USA)
Neltec SA
Rev.C 06-02
Tempe, AZ
Lannemezan, France
(480) 967-5600
+33 (0) 5 62 98 52 90
N9000 PTFE Processing Guidelines
Baseline Drilling Parameters
Hole Diameter
Inches (mm)
.020 (.50)
.030 (.75)
.040 (1.0)
.060 (1.5)
Surface Speed
SFM (mm/s)
200
200
200
200
Spindle Speed (min)
(RPM)
38,197
25,464
19,098
12,732
Feed Rate
Inches/min (mm/s)
38.2 (16.2)
25.5 (10.8)
19.1 (8.1)
19.1 (8.1)
Chip Load
Inches/rev (mm/rev)
.001
.001
.001
.0015
Hole Cleaning
Deburring: Use proper entry and exit materials to minimize burr formation. Hard phenolic entry and exit materials are
recommended for PTFE laminates. Aluminum or aluminum-clad materials can be used but “bird nesting” must be
eliminated or the dielectric will be damaged. The aluminum burrs have a tendency to damage the soft PTFE during drilling.
If copper burrs are observed after drilling, scrubbing with minimal force should be used to prevent deformations. Use a highpressure wash to remove debris from holes.
Desmear of Through Hole
For situations where FR4 or similar prepreg (i.e., N4000-6, -13, or N6000-21) is used in a hybrid PCB format, chemical
desmear can be used to desmear the non-PTFE layers. Use a recipe similar to the one shown below:
Typical Solvent Conditioner
Type
Butyl Carbitol @ 50 wt%
Temp
130° F ± 5 (54 °C ± 2.8)
Time
3 - 7 min.
Typical Oxidizer Parameters
Alkaline Permanganate
175° F ± 5 (79 °C ± 2.8)
8 - 15 min.
Plasma
For hybrid packages with thermoset bond plies, plasma desmear should be used before Sodium etch (see next section) to
get maximum adhesion of plating. If plasma is used for FR4 desmear and then for PTFE surface activation, the FR4 must
be desmeared prior to treating the PTFE. Desmear is not possible on PCBs using pure PTFE and thermoplastic
(i.e., FV6700 or FEP) bond-ply applications.
Plasma Process
The process below is a good starting point for FR4 and some other thermoset resin systems in a hybrid format.
Cycle A:
Step 1
Step 2
O2 50%; He 50%; power of 4300 watts RF and 250 psi for 10 Minutes
He 100%; power of 2575 watts; 250 psi for 15 minutes; final temperature, 175 °F (79 °C).
Cycle B:
Step 1
Step 2
Step 3
O2 90%; N2 10%; with final temperature of 135 °F (57 °C)
CF4 10-15%, O2 – balance; final temperature is 230 °F (110 °C)
O2 100%; One half the power used in Step 1
Cycle C:
Step 1
O2 50%; He 50%; power of 4300 watts RF; 250 psi for 10 Minutes
For More Information Contact One Of Our ISO 9002 Facilities or visit our web site at www.parknelco.com
Neltec (USA)
Neltec SA
Rev.C 06-02
Tempe, AZ
Lannemezan, France
(480) 967-5600
+33 (0) 5 62 98 52 90
N9000 PTFE Processing Guidelines
Step 2
He 100%; power of 2575 watts; 250 psi for 15 minutes; final temperature, 175 °F (79 °C).
PTFE THROUGH-HOLE PREPARATION:
Plasma:
Plasma processes typically used to desmear epoxy-based boards, (O2 / CF4 or O2 / NF3) appear to have limited
effectiveness when treating PTFE surfaces. However, other gasses such as NH3 or (70% H2 / 30% N2) blends
have been found to yield very good results with conventional production plasma equipment. The process
conditions outlined below have been found to increase the ability to plate as well the ability to bond as those
obtained by sodium etching. All loose debris in the holes should be removed prior to treatment.
Cycle 1:
Step 1
NH3 or (70% H2 / 30% N2) 100 mTorr Pump-down, 250 mTorr operating, power of 4000 watts;
frequency of 40 kHz; voltage of 500-600V; cycle time of 10-30 minutes
Contact your local Nelco representative for additional information.
Park/Nelco materials should not need any baking prior to plasma. (Ceramic loaded PTFE materials from other
vendors do require a pre-bake of at least one hour). Plasma treated holes are more delicate than sodium etched
holes. Panels should not be exposed to any pressure wash or scrubbing process after plasma treatment prior
to metallization.
Sodium-Complex Etch:
Use the “Sodium Etch” process as an alternative to the plasma process (above). This etchant is actually Sodium
Napthalate complex in a glycol solution. Several commercial Sodium etchants are available in the market and
are commonly used. Contact your local Nelco representative for additional information.
Metallization:
Conventional plating may be used to plate PTFE. Electroless copper as well as the palladium catalyst direct
plating process such as Shipley’s Crimson™ process, work well on PTFE substrates after hole prep. All treated
PTFE should be processed within 24 hours. If not, retreat the holes prior to metalization. Once the electroless
copper or direct plating has been used, standard electrolytic copper can be used. Remember, the secret to
good plated through holes on PTFE substrates is a strong ductile cooper. The electrolytic copper should have a
tensile strength of at least 30,000 psi and copper elongation of at least 15%. Panels are often flash
electroplated 0.0001 - 0.0003 inch (2.5 - 7.6 µm) after electroless copper plating to reduce the risk of voiding
holes while preparing surfaces for photo resist.
Soldermask
PTFE and ceramic filled surfaces do not require pre-treatment or conditioning prior to solder-mask application. Baking is
desirable to drive out moisture prior to solder-mask treatment.
Reflow/HASL
Bake prior to re-flow or hot air solder leveling.
Imaging
The dimensional stability of Neltec’s PTFE material is excellent. The dimensional change should be <0.5 mils/inch (0.005
mm/cm), but does depend on the prepreg, construction, and process.
For More Information Contact One Of Our ISO 9002 Facilities or visit our web site at www.parknelco.com
Neltec (USA)
Neltec SA
Rev.C 06-02
Tempe, AZ
Lannemezan, France
(480) 967-5600
+33 (0) 5 62 98 52 90
N9000 PTFE Processing Guidelines
Developing/Etching/Stripping
Due the low modulus of the PTFE materials, frames and leaders may be required when processing thin laminates through
some conveyorized equipment. Standard etchants can be used.
Routing
Once circuits have been drilled and plated, the circuits must be removed from the master panel. Routing, steel rule die
cutting, waterjet cutting, and laser cutting can be used depending on required edge quality and cutting tolerances. In the
case of routing, standard carbide (helical two flute or four flute) routers are recommended. Copper foil should be etched
away from the routed edge to prevent burring. Tool life is approximately 2 to 5 feet of linear travel, depending on the
specifications for edge quality or edge plating. For edge plating, follow the hole plating recommendations above. All
fabricators should determine the optimal parameters for their equipment and tooling. Remember: Use new, polished,
carbide tooling to guarantee the highest edge quality.
Typical routing parameters for stack heights of 0.250” (6.35 mm):
Tool size:
Feed rate:
Speed:
0.093” (2.36 mm)
60 IPM
24k RPM
The above processing guides are recommendations only and intended for general review. Process adjustments may be
required to achieve optimum results.
For More Information Contact One Of Our ISO 9002 Facilities or visit our web site at www.parknelco.com
Neltec (USA)
Neltec SA
Rev.C 06-02
Tempe, AZ
Lannemezan, France
(480) 967-5600
+33 (0) 5 62 98 52 90
N9000 PTFE Processing Guidelines
Park/Nelco reserves the rights to make changes without further notice to any products herein to improve reliability,
function or design. Park/Nelco does not assume any reliability arising out of the application or use of any product
described herein; neither does it convey any license under its patent rights nor the rights of others. This disclaimer of
warranty is in lieu of all warranties whether expressed, implied or statutory, including implied warranties of merchantability
or fitness for a particular purpose. Park/Nelco is an Equal Opportunity / Affirmative Action Employer.
For More Information Contact One Of Our ISO 9002 Facilities or visit our web site at www.parknelco.com
Neltec (USA)
Neltec SA
Rev.C 06-02
Tempe, AZ
Lannemezan, France
(480) 967-5600
+33 (0) 5 62 98 52 90