PANAVIA ETCHING AGENT V
Only for use on uncut enamel, for instance with
cementing of adhesion bridges.
ED PRIMER
A mild conditioner for enamel and dentine.
Enhances bond strength of PANAVIA 21 and accelerates
polymerization. Consists of Liquid A and liquid B.
PANAVIA 21 Paste
A radio-opaque composite, consisting of catalyst and
universal paste. It contains the adhesive monomer
MDP, which provides long term bond strength.
Available in three shades:
– PANAVIA 21 TC: Transparent paste for the cementing
of aesthetic restorations.
– PANAVIA 21 EX: A semi-transparent white paste.
– PANAVIA 21 OP: An opaque paste used for masking
metal.
OXYGUARD II
For application to the margin.
Easy to rinse off.
Contains a polymerization accelerator to promote setting.
PANAVIA 21
A cement meeting today’s highest standards as well as those of the 21st century!
Manufactured by KURARAY CO., LTD. 1-12-39 , Umeda, Kita-ku, Osaka 530-8611, JAPAN
Kuraray European Union Representative KURARAY EUROPE GmbH, Schiess Strasse 68, D-40549 Düsseldorf
NOTE: Please read PANAVIA 21 Instructions for Use thoroughly before using the product. PANAVIA 21 is a trade mark of Kuraray Co., Ltd. WARRANTY: All data herein are based on actual measurements performed by Kuraray Co., Ltd. All information contained herein is presented in good faith and without warranty.
Kuraray Co, Ltd. will replace any product that is proved to be defective. Neither Kuraray Co., Ltd. nor the distributor accepts liability for any loss or damage, direct, consequential or special, arising out of the application or use of or the inability to use these products. Before using, the user will determine the suitability of the products for the intended use and the user assumes all risk and liability whatsoever in connection therewith. 450 EUL-GB 01.99
Components
UNIVERSAL, SAFE AND SOLID
Panavia 21 enjoys worldwide fame as an
outstanding cement. The material bonds very good
to enamel and dentine as well as to composite,
porcelain and precious & base metals.
It is easy to use and preparation errors can be
eliminated.
Panavia 21, an incredibly reliable cement which
leads you securely into the 21st century.
21
P A N A V I A
21
P A N A V I A
www.kuraray.de
1 PANAVIA 21 paste: Catalyst and Universal paste
21
10
2 ED PRIMER Liquid A / Liquid B
3 OXYGUARD II
4 PANAVIA ETCHING AGENT V
6
5 Mixing pad
6 Mixing spatula
7 Mixing dish
8 Sponge pledget
9 Brush tips
P A N A V I A
10 Brush holder
1
3
Extensive range of indications
No etching required
8
5
PANAVIA 21 is specifically for the cementing
of adhesion bridges, splints and conventional
crown and bridge work, of metal, porcelain
and composite, of preformed posts and cast
post and core, and for bonded amalgam
restorations.
PANAVIA 21 is suited to all of these purposes,
offering valuable properties such as thin film
thickness, excellent pulp compatibility, availability in several colors, and superior bond.
9
Pre-treatment of the enamel and the dentine
involves application of ED PRIMER. Only unprepared enamel needs to be etched with PANAVIA
ETCHING AGENT V before ED PRIMER application.
4
2
Anaerobic curing
7
Easy processing
TC
(tooth color)
EX
(standard white)
OP
(opaque)
Anterior adhesion and splint
▲
●
■
Posterior adhesion bridge and splint
■
■
■
Metal inlay, onlay, crown and bridge
■
■
●
onlay and crown
■
▲
▲
■
First choice
Preformed post/Cast post and core
■
■
■
●
Adequate
Amalgam bonding
■
●
●
▲
Not recommended
Silanated porcelain or cured composite inlay,
Enhanced bond strength
Function of ED PRIMER
ED PRIMER improves the bonding to enamel,
dentine, metal and composite. In addition,
ED PRIMER also tightly seals the tubules and
the intertubular dentine, so ensuring reliable
use of the PANAVIA 21 system on vital teeth.
Furthermore, ED PRIMER contains a polymerization accelerator reducing PANAVIA 21
setting time, so that it attains its highest bond
strenght more quickly.
ED PRIMER dissolves the smear layer and penetrates
into the dentine
PANAVIA 21 is a paste-paste system. With a
simple turning motion, the practical dispenser
mixes both pastes at the correct ratio. After a
mixing period of 20 to 30 seconds, a smooth
paste is obtained: not too thick - which would
adversely affect the placement of the restoration - and thin enough to achieve an optimal
film thickness.
Superior peripheral sealing
PANAVIA 21 is a composite cement which has
an extremely high filler content of barium glass
particles, protecting PANAVIA 21 from abrasion
near the margins and preventing the development of a marginal gap. A benefit that may also
be attributed to the precisely tailored consistency of the material.
Dissolved smear layer
Dentinal tubules
Dentine
Adhesion of PANAVIA 21 to dentine
Dosage
Restoration
PANAVIA 21
Primer layer with smear layer ingredients
Hybrid, impregnated layer
Primer-link
Application of ED PRIMER on enamel and dentine.
PANAVIA 21 cures under anaerobic conditions,
a particularly favorable aspect for root canal
post cementing. If intra-oral cementing is
intended, PANAVIA 21 can be left to cure after
covering the margins with OXYGUARD II.
After the Panavia 21 setting time of 3 minutes,
OXYGUARD II is rinsed off.
Mixing for maximal 20 seconds
Ready for use