Shield Arc ® HYP+
High strength cellulosic electrode
Classification
AWS A5.5
ISO 2560-A
: E 7010-P1
: E 42 2 Mo C 25*
S M AW
General description
Cellulosic electrode for vertical do wn pipe welding
Suitable for pipe with strengths X52 trough X65
Cleaner weld puddle
Very low tendency to peel or flake off under high electrode pressure in tight joints
Low susceptibility to wagon tracks, windows and pinholes
Very low spatter and smoother arc action
Welding positions
Current type
DC +
ISO/ASME PG/5Gdown
Chemical composition (w%), typical, all weld metal
C
0.12
Mn
0.40
Si
0.15
Mo
0.50
V
0.01
Mechanical properties, all weld metal
Condition
Required: AWS A5.5
ISO 2560-A
Typical values
AW
0.2% Proof strength
(N/mm2)
min. 415
min. 420
450
Tensile strength
(N/mm2)
min. 480
500-640
540
Elongation
(%)
min. 22
min. 20
24
Impact ISO-V(J)
-20°C
-29°C
27
min. 47
65
45
Packaging and available sizes
Unit: Metal can
Identification
124
Diameter (mm)
Length (mm)
Pieces / unit
Net weight/unit (kg)
Imprint: 7010-G
3.2
350
210
5.4
4.0
350
135
5.4
4.8
350
89
5.1
Tip Color: none
Shield Arc® HYP+: rev. EN 02
Liability: All information in this data sheet is based on the best available knowledge, is subject to change without notice and can
only be considered as suitable for general guidance Fumes: Consult information on Welding Safety Sheet, available upon request
www.lincolnelectric.eu
Shield Arc ® HYP+
Materials to be welded
Steel grades/Code
Pipe material
EN 10208-2
EN 10216-1 / 10217-1
API 5LX
Gaz de France
Type
S M AW
L360, L415, L445
P 355
X52, X56, X60, X65
X52, X63
Calculation data
Sizes
Diam. x length
(mm)
Current
range
A)
Current
type
3.2x350
4.0x350
4.8x350
75-130
90-185
140-185
DC+
DC+
DC+
Arc time
Energy
Dep.rate
- per electrode at max. current (s)*
E(kJ)
H(kg/h)
Weight/
1000 pcs.
(kg)
Electrodes/
kg weldmetal
B
kg Electrodes/
kg weldmetal
1/N
25.8
39.5
57.1
Welding parameters, optimum fill passes
Welding positions
Diameter (mm)
3.2
4.0
4.8
PG/5G down
110A
150A
165A
Remarks/ Application advice
Preheating pipe material from L380 to L450 (X56 to X65) required (acc. EN 1011-1).
Pipeclamps to be removed after finishing root pass, start welding hot pass (within 5 min) after root pass
Use electrodes directly from metal cans
Use Fleetweld 5P+ for lower hardness in the root pass
125